Abstract
Extracting the trapped oil into the pores is still a massive challenging. In this work, multiwalled carbon nanotubes were utilized to investigate the influence of the nanofluid’s flow rate on the oil recovery in enhanced oil recovery (EOR) stage. At the optimum conditions, comparative study was conducted to figure out the impact of EM waves on the recovery efficiency. The experimental study proved that 2 mL/min is the optimum flow rate for the utilized fluid. EM waves could enhance the recovered oil in EOR stage by 24.5% ROIP. The increment was ascribed to the extraordinary role of EM waves in increasing the viscosity of the nanofluid.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
Introduction
With the increase in the demand of crude oil and reduction in oil sources, extracting additional oil is becoming more challenging (Alnarabiji et al. 2014a, b, 2016, 2018; Shafie et al. 2014; Ahmed et al. 2018; Adil et al. 2018). Lately, nanosized materials have attracted wide attention due to their extraordinary characteristics (Ameen et al. 2019; Ghanem et al. 2018; Al-Swai et al. 2018; Alnarabiji et al. 2017, 2018; Ali et al. 2018; Chuah et al. 2016; Alqasem et al. 2017). Multiwalled carbon nanotube (MWCNT) as a type of nanomaterials has been implanted in enhanced oil recovery (EOR) and achieved remarkably high recovery (Alnarabiji et al. 2016). However, the previous study covered the influence of MWCNT concentration in the fluid on the recovery efficiency, whereas other parameters such as nanofluid flow rate as well as the effect of the electromagnetic (EM) waves on the recovery efficiency were not investigated.
In this work, the influence of the nanofluid’s flow rate on the oil recovery in EOR stage was investigated. At the optimum conditions, comparative study was conducted to figure out the impact of EM waves on the recovery efficiency.
Methodology
MWCNT fluid preparation
Since MWCNT (obtained from Cambridge, UK) is in powder form, it was suspended in distilled water in order to be injected into a porous medium. The suspended MWCNT was subjected to two main stages. In the first stage, MWCNT was dispersed in distilled water as a base fluid and stirred for 15 min using magnetic stirrer on hotplate, whereas in the second stage agitation conducted to the prepared suspension in an ultrasonic bath for approximately 2 min at room temperature to enhance the homogenous dispersion of the powder in the base fluid.
Experimental setup and procedure
Similar experimental setup in our previous study (Alnarabiji et al. 2018) was utilized to conduct this study. In the current study, study with varying the flow rate was conducted in order to figure out its influence on the hydrophobic MWCNT and observe the behavior of this material in the prepared porous medium and investigate its impact on nanofluid mobility and recovery efficiency. Practically, three different water flooding experiments were performed independently to investigate the impact of the three selected flow rates of nanofluid (0.05, 1.0, 2.0 mL/min) of 0.01 wt% on fluid mobility and the recovery efficiency. The optimum flow rate was selected by observing both recovery efficiency and fluid mobility via calculating the residual resistance factor (Rrf) using Eq. (1) (Shi et al. 2010).
where Ka is the obtained permeability of the porous medium before injecting the nanofluid, Kb is the resulted permeability of the porous medium after injecting the nanofluid, ΔP1 is the variation in the pressure at EOR stage, whereas ΔP2 is the difference in the calculated pressure before EOR stage. Noteworthy, If Rrf value is higher than one, this ascribes that the utilized nanofluid causes blocking to the channels and pores.
The combination between MWCNT and EM waves
The selected experiment of optimum flow rate in the absence of EM energy was considered as a reference experiment. Subsequently, the incremental recovery occurred from this experiment was considered as a baseline in the following experiment. The EM waves with 13.0 MHz square alternating current frequency was irradiated onto the studied porous medium in the EOR stage. The recovery efficiency and Rrf were computed and compared with the one in the absence of EM energy. Hence, Darcy’s equation was utilized to offer a better understanding of the recovery mechanism.
Results and discussion
It can be shown in Fig. 1 that the highest flow rate (F.R) of 2.0 mL/min gave the highest recovery efficiency 36.6% ROIP, while the rest of flow rates 0.5 and 1.0 mL/min gave 28.9 and 29.2% ROIP, respectively. The calculated mobility reduction factors for different flow rates (Fig. 2) are in good agreement with the recovery efficiency (Fig. 1). It can be concluded from the experimental results that the recovery of the MWCNT fluid increases with an increase in flow rate, which subsequently leads to an increase in capillary number and reduces the chance of MWCNT blocking the pore throat and channels.
It is demonstrated in Fig. 3 that the recovery efficiency of 61.1% ROIP was achieved by using MWCNT fluid in the presence of EM waves, while in the absence of EM waves it was only 36.6% ROIP. It can also be seen from Fig. 4 that the mobility reduction factor increased from 1.2 in the absence EM waves to 1.7 in the presence of EM waves. As long as flow rate, permeability, length and the cross-sectional area where the flow occurs are constant, the increase in pressure is attributed to the increase in the fluid’s viscosity. There are two main sources behind this increase in viscosity: Firstly, inducing the MWCNT by EM waves which increased the apparent viscosity. Since carbon nanotubes possess dielectric properties (Javey et al. 2002), the increment in the viscosity of the MWCNT fluid can be ascribed to the creation of negative and positive charges due to the polarization on the surface of MWCNT under EM waves. These electric dipoles will rearrange and align to create temporary chain-like structure which causes an increase in the viscosity of MWCNT fluid (Hao 2002), subsequently increasing the capillary number. In other words, more pressure is required to inject the fluid into the porous medium with the same flow rate (Fig. 4). Secondly, the electromagnetic waves emitted during the water flooding experiment had triggered the MWCNT in the porous medium to vibrate in a similar frequency and, therefore, form emulsion. More especially, it was found that CNT has the ability to form and stabilize Pickering emulsion. These results are in line with our previous study where EM waves assisted in enhancing the viscosity of the ZnO nanofluid (Alnarabiji et al. 2018).
On the other hand, previous studies proved that CNT with hydrophobic surface nature needs mechanical energy to form the emulsion (Wang and Hobbie 2003; Shen and Resasco 2009). It can be pustulated that EM waves provide the required mechanical energy to vibrate MWCNT. By increasing the pressure of the nanofluid injection, the viscosity of the formed emulsion can be remarkably higher than that of both water and oil. This might be attributed to the fact that the created emulsion exhibited non-Newtonian behavior (Schramm 1992). It is clear from Fig. 4 that the difference in the pressure in the presence of EM waves declines directly after injecting the brine into the medium. This is because brine possesses negative and positive ions attached to the surface of charged MWCNT to neutralize. In other words, even if electric dipoles are formed and charges are created on the surface of dielectric material, their effectiveness still depends on the ionic strength of the medium. For instance, brine ions are capable of neutralizing those polarized particles directly. Therefore, the neutralized particles will not be induced by the EM waves and no more emulsion will be formed under the influence of the vibration of dielectric nanoparticles induced by the frequency of EM waves. These results are in good agreement with previous study where it was found that the salinity of brine reduces emulsion stability (Zhang et al. 2009). It is clear from Fig. 4 that with the injection of brine into the porous medium, the pressure declines drastically to 6.2 psi and then gradually increases to 6.6 psi. The reason of this increment is that the salinity of brine works on increasing nanoparticles retention in the medium (Caldelas et al. 2011). This increment reached the maximum when 1 pore volume of brine was injected after the 2 pore volume of MWCNT fluid injected (Fig. 4). Later, the blockage was released gradually by injecting more pore volumes of brine till it stabilized at the end of the experiment.
It is expected that with increasing the concentration of MWCNT fluid, more number of nanoparticles will polarize under the impact of EM waves which will drive to create higher temporary viscosity and higher capillary number; as a result, MWCNT will contribute in forming stable emulsion (Zhang et al. 2009). However, this process might have negative impact on fluid mobility and recovery efficiency as a result. Therefore, further studies required to can be conducted to investigate the most suitable nanofluid conditions under EM field.
Conclusion
MWCNT has been utilized in EOR stage. It was found that 2 mL/min is the optimum flow rate of the prepared nanofluid. EM wave could enhance the recovery efficiency significantly where it was increased from 36.6 to 61.1% ROIP. The reason behind this increment was attributed to the increase in the MWCNT viscosity as well as the probable formation of emulsion.
Abbreviations
- MWCNT:
-
Multiwalled carbon nanotubes
- EOR:
-
Enhanced oil recovery
- EM:
-
Electromagnetic
- Rrf :
-
Residual resistance factor
- F.R:
-
Flow rate
- ROIP:
-
Residual oil in place
- CNT:
-
Carbon nanotubes
- ZnO:
-
Zinc oxide
References
Adil M, Lee K, Zaid HM, Latiff NRA, Alnarabiji MS (2018) Experimental study on electromagnetic-assisted ZnO nanofluid flooding for enhanced oil recovery (EOR). PLoS ONE 13:e0193518
Ahmed S, Elraies KA, Hashmet MR, Alnarabiji MS (2018) Empirical modeling of the viscosity of supercritical carbon dioxide foam fracturing fluid under different downhole conditions. Energies 11:782
Ali B, Yusup S, Quitain AT, Alnarabiji MS, Kamil RNM, Kida T (2018) Synthesis of novel graphene oxide/bentonite bi-functional heterogeneous catalyst for one-pot esterification and transesterification reactions. Energy Convers Manag 171:1801–1812
Alnarabiji MS, Yahya N, Hamid SBA, Azizi K, Kashif M, Qureshi S, Alqasem B (2014a) The role of surface area of ZnO nanoparticles as an agent for some chemical reactions. Defect Diffus Forum 354:201–213
Alnarabiji MS, Yahya N, Bee Abd Hamid S, Azizi K, Shafie A, Solemani H (2014b) Microwave synthesis of ZnO nanoparticles for enhanced oil recovery. Adv Mater Res 1024:83–86
Alnarabiji MS, Yahya N, Shafie A, Solemani H, Chandran K, Hamid SBA, Azizi K (2016) The influence of hydrophobic multiwall carbon nanotubes concentration on enhanced oil recovery. Proc Eng 148:1137–1140
Alnarabiji MS, Yahya N, Hamed Y, Ardakani SEM, Azizi K, Klemeš JJ, Abdullah B, Tasfy SFH, Hamid SBA, Nashed O (2017) Scalable bio-friendly method for production of homogeneous metal oxide nanoparticles using green bovine skin gelatin. J Clean Prod 162:186–194
Alnarabiji MS, Yahya N, Nadeem S, Adil M, Baig MK, Ghanem OB, Azizi K, Ahmed S, Maulianda B, Klemeš JJ (2018a) Nanofluid enhanced oil recovery using induced ZnO nanocrystals by electromagnetic energy: viscosity increment. Fuel 233:632–643
Alnarabiji M, Zabidi NAM, Ramli A, Ghanem OB, Abdullah B (2018b) Controllable green synthesis of supported hollow NiO crystals with shape evolution from octahedral to novel truncated octahedral. CrystEngComm 20:6662–6666
Alqasem B, Yahya N, Qureshi S, Irfan M, Rehman ZU, Soleimani H (2017) The enhancement of the magnetic properties of α-Fe2O3 nanocatalyst using an external magnetic field for the production of green ammonia. Mater Sci Eng, B 217:49–62
Al-Swai BM, Osman N, Alnarabiji MS, Adesina AA, Abdullah B (2018) Syngas production via methane dry reforming over ceria-magnesia mixed oxide supported nickel catalysts. Ind Eng Chem Res 58:539–552
Ameen M, Azizan MT, Ramli A, Yusup S, Alnarabiji MS (2019) Catalytic hydrodeoxygenation of rubber seed oil over sonochemically synthesized Ni–Mo/γ-Al2O3 catalyst for green diesel production. Ultrason Sonochem 51:90–102
Caldelas F, Murphy M, Huh C, Bryant S (2011) Factors governing distance of nanoparticle propagation in porous media. In: SPE production and operations symposium
Chuah LF, Amin MM, Yusup S, Bokhari A, Klemeš JJ, Alnarabiji MS (2016) Influence of green catalyst on transesterification process using ultrasonic-assisted. J Clean Prod 136:14–22
Ghanem OB, Shah SN, Lévêque J-M, Mutalib MA, El-Harbawi M, Khan AS, Alnarabiji MS, Al-Absi HR, Ullah Z (2018) Study of the antimicrobial activity of cyclic cation-based ionic liquids via experimental and group contribution QSAR model. Chemosphere 195:21–28
Hao T (2002) Electrorheological suspensions. Adv Coll Interface Sci 97:1–35
Javey A, Kim H, Brink M, Wang Q, Ural A, Guo J, McIntyre P, McEuen P, Lundstrom M, Dai H (2002) High-κ dielectrics for advanced carbon-nanotube transistors and logic gates. Nat Mater 1:241
Schramm LL (1992) Fundamental and applications in the petroleum industry. Adv Chem 231:3–24
Shafie A, Yahya N, Kashif M, Zaid HM, Soleimani H, Alnarabiji MS (2014) The band structures of single-walled carbon nanotubes and ZnO nanoparticles used for oil recovery in water flooding system. J Nano Res 26:101–110
Shen M, Resasco DE (2009) Emulsions stabilized by carbon nanotube-silica nanohybrids. Langmuir 25:10843–10851
Shi L, Ye Z, Zhang Z, Zhou C, Zhu S, Guo Z (2010) Necessity and feasibility of improving the residual resistance factor of polymer flooding in heavy oil reservoirs. Petrol Sci 7:251–256
Wang H, Hobbie EK (2003) Amphiphobic carbon nanotubes as macroemulsion surfactants. Langmuir 19:3091–3093
Zhang T, Roberts M, Bryant S, Huh C (2009) Foams and emulsions stabilized with nanoparticles for potential conformance control applications. In: SPE international symposium on oilfield chemistry
Acknowledgements
The authors would like to acknowledge Universiti Teknologi PETRONAS for facilitating the work and ministry of education.
Author information
Authors and Affiliations
Corresponding author
Additional information
Publisher’s Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Belhaj, A.F., Elraies, K.A., Janjuhah, H.T. et al. Electromagnetic waves-induced hydrophobic multiwalled carbon nanotubes for enhanced oil recovery. J Petrol Explor Prod Technol 9, 2667–2670 (2019). https://doi.org/10.1007/s13202-019-0653-6
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s13202-019-0653-6