Highlights
-
Core–shell structured SnS2@C hollow nanospheres were synthesized.
-
The uniform carbon coating and hollow structure can alleviate the mechanical strain and therefore electrochemical performance.
Abstract
Constructing unique and highly stable structures with plenty of electroactive sites in sodium storage materials is a key factor for achieving improved electrochemical properties through favorable sodium ion diffusion kinetics. An SnS2@carbon hollow nanospheres (SnS2@C) has been designed and fabricated via a facile solvothermal route, followed by an annealing treatment. The SnS2@C hybrid possesses an ideal hollow structure, rich active sites, a large electrode/electrolyte interface, a shortened ion transport pathway, and, importantly, a buffer space for volume change, generated from the repeated insertion/extraction of sodium ions. These merits lead to the significant reinforcement of structural integrity during electrochemical reactions and the improvement in sodium storage properties, with a high specific reversible capacity of 626.8 mAh g−1 after 200 cycles at a current density of 0.2 A g−1 and superior high-rate performance (304.4 mAh g−1 at 5 A g−1).
Similar content being viewed by others
Avoid common mistakes on your manuscript.
1 Introduction
Over-engineering and usage of lithium ion batteries have caused a sudden reduction in lithium sources on earth, along with soaring lithium prices, compared with the previous two decades [1,2,3,4,5,6]. On the contrary, sodium resources are abundant and even unlimited, accounting for the fourth largest abundance of all elements on a global scale [7]. The advantages of low-cost and similarity in physicochemical properties make sodium ion batteries a promising and reasonable alternative to lithium ion batteries [8,9,10]. As a result, there is urgency in exploring optimized and high-performance electrode materials for sodium ion batteries [11, 12].
Among the anode materials that have been reportedly applied to sodium ion batteries [13,14,15,16,17,18,19], tin and tin-based compounds have attracted intensive attention as sodium storage materials, based on the alloying formation of Na15Sn4. The high theoretical capacity of 1136 mAh g−1 enables SnS2 to stand out from the list of tin-based anode materials (847 mAh g−1 for metallic tin, 1022 mAh g−1 for SnS) because of the additional capacity contribution of the conversion reaction [20]. Like most alloying materials, poor cycling stability is the most serious obstacle of SnS2 to achieve decent electrochemical performance, which is due to the greatly destructive volume expansion and extraction during the sodiation and de-sodiation processes, resulting in the loss of contact between electrode materials and current collectors.
Up to now, reported structural designs of SnS2 have mostly been focused on two-dimensional (2D) structures as electrode materials for sodium ion batteries [13, 15, 20,21,22,23,24,25,26,27,28,29], because of its own Cdl2-type hexagonal layer nature [20]. Graphene is regarded as the most favorable substrate to be composited with SnS2, considering the structural compatibility of two-layered materials, which act to restrain the volume variation in the electrochemical reactions. For example, Zhang et al. [24] reported a hybrid consisting of few-layered SnS2 on reduced graphene oxide nanosheets. Qu et al. [21] integrated SnS2 with reduced graphene oxide via a hydrothermal reaction. Liu et al. [13] restacked exfoliated SnS2 on graphene sheets by the hydrolysis of lithiated SnS2. Tu et al. [28] fabricated a sandwich composite combining few-layered SnS2 nanosheets with reduced graphene oxide nanosheets. However, there are few reports on three-dimensional (3D) nanostructured SnS2 anode materials for sodium ion batteries, in part owing to the difficulties encountered in the multi-step and time-consuming synthesis procedure or the post-removal of the employed templates or substrates.
Here, a facile template-free hydrothermal reaction followed by an annealing approach has been applied to synthesize 3D SnS2@carbon hollow nanospheres (SnS2@C). The hollow structure could grant free interior space to accommodate volume expansion and, thus, alleviate mechanical stress. The structure also produces a high surface area to facilitate the presence of more electroactive sites for reactions and facile permeation of electrolyte in electrode materials, as well as a shortened diffusion path for ions and electrons. To reinforce structural stability, a uniform carbon shell was adopted to cover the surface of the hollow nanospheres to suppress the volume variation during electrochemical reactions. Combining the virtues of the core–shell and hollow structures, the as-prepared SnS2@C hollow nanospheres exhibited decent cycling performance with a high reversible specific capacity of 626.8 mAh g−1 after 200 cycles at a current density of 0.2 A g−1, and high-rate capability with a capacity of 304.4 mAh g−1 at 5 A g−1.
2 Experimental
2.1 Sample Preparation
2.1.1 Synthesis of SnO2 Hollow Nanospheres
SnO2 hollow spheres were synthesized by a facile one-pot template-free approach [30]. In a typical synthesis, 0.24 g of urea was added to a mixture of 15 mL of deionized water and 25 mL of ethanol, with stirring for 15 min. Then, 0.195 g of potassium stannate trihydrate (K2SnO3·3H2O) was added to the as-obtained solution, which was vigorously stirred at 25 °C for another 1 h. Afterward, the resultant mixture was transferred to a Teflon-lined stainless steel autoclave and then heated at 220 °C for 24 h in an electric oven. After the reaction, the as-obtained SnO2 hollow spheres were centrifugally separated from the suspension and washed with deionized water several times before being dried in a vacuum oven at 70 °C overnight.
2.1.2 Synthesis of SnO2@C Hollow Nanospheres
First, 150 mg of the as-obtained SnO2 hollow nanospheres was dispersed in 100 mL of Tris buffer solution that was stirred for 30 min. Then, 100 mg of dopamine-HCl was added to the solution with vigorous stirring for 12 h. The resultant precipitate was collected by centrifugation and dried at 70 °C for 6 h. Then, the sample was placed in an alumina crucible in the tube furnace, which was heated to 500 °C at a speed of 5 °C min−1 under flowing argon gas. After 2 h of reaction, the furnace was left to cool down to 25 °C before the samples were removed from the tube furnace.
2.1.3 Synthesis of SnS2@C Hollow Nanospheres
The as-prepared SnO2@C hollow nanospheres was loaded in an alumina boat, which was placed in a larger, covered alumina boat containing excess thioacetamide outside the inner alumina boat. Then, the alumina boats were transferred to a tube furnace under vacuum and annealed at 300 °C for 2 h at a heating speed of 5 °C min−1.
2.1.4 Synthesis of SnS2/C Bulks
SnS2/C bulks were synthesized under identical synthesis conditions as those for SnS2@C hollow nanospheres, except, the rapid heating speed was 30 °C min−1 during the sulfidation procedure.
2.1.5 Synthesis of Bare SnS2
Bare SnS2 was synthesized under identical synthesis conditions as those for SnS2@C hollow nanospheres through the sulfidation of SnO2 hollow nanospheres without the carbon coating procedure.
2.2 Material Characterization
The morphologies of samples were characterized by field-emission scanning electron microscopy (FE-SEM, JSM-7500F, JEOL) and transmission electron microscopy (TEM, JEM-2100F, JEOL). X-ray powder diffraction (XRD) was carried out with Cu-Kα radiation (λ = 1.5406 Å) over the range of 2θ = 5°–90°. In situ X-ray diffraction (XRD) measurements were performed on a D8 Advance X-ray diffractometer with Cu-Kα X-ray radiation (λ = 1.5406 Å) scanned in the range of 10°–49°. An in situ battery was designed with a Be window for X-ray penetration. The in situ XRD data were recorded upon initial discharging. The (001), (100), (101), and (102) crystal planes of SnS2 were chosen for in situ monitoring during the discharge/charge processes at 0.15 A g−1. The Raman spectra of the samples were measured using a LabRAM HR Evolution Raman spectrometer. X-ray photoelectron spectroscopy (XPS) experiments were conducted on an ESCALAB 250Xi X-ray photoelectron spectrometer.
2.3 Electrochemical Measurements
Electrochemical measurements were carried out with coin cells, which were assembled in a glove box filled with argon atmosphere. The electrode slurries of the obtained materials were prepared by thoroughly mixing the active material, poly(vinylidene difluoride) (PVDF), and acetylene black in a weight ratio of 8:1:1 in N-methyl pyrrolidone (NMP). The cells were constructed with sodium foil as the anode, prepared active material as the cathode, glass microfiber as the separator, and 1-M NaClO4 in a mixture of ethylene carbonate (EC) and propylene carbonate (PC) (1:1 by volume), with 5 wt% fluoroethylene carbonate (FEC) additive as the electrolyte. The average mass of active materials loading per plate was 0.9 mg cm−1. The charge/discharge cycling was performed using a battery tester (LANHE CT2001A) with a voltage range between 0.01 and 3.0 V. An electrochemistry workstation (CHI660E) was utilized to conduct measurements in cyclic voltammetry (CV) and electrochemical impedance spectroscopy (EIS). EIS was conducted over the frequency range from 100 kHz to 0.01 Hz at an open circuit voltage. The SnS2@C electrodes were first sodiated and then de-sodiated in the cells by discharging to 0.01 V and charging to 3.0 V at a constant current of 0.20 mA g−1, respectively. Then, the electrodes were disassembled in a glove box filled with argon atmosphere for ex situ TEM measurements.
3 Results and Discussion
The SnO2 precursor was prepared via a facile one-pot template-free approach through the hydrolysis of K2SnO3·3H2O under hydrothermal conditions. The scanning electron microscopy (SEM) images reveal the obtained SnO2 to exhibit high monodispersity and a uniform spherical morphology, 250–350 nm in size, as shown in Fig. 1a, b. The distinct contrast difference between the center and edge, shown in the TEM image in Fig. 1c, indicates the hollow feature of the obtained monodispersed SnO2 nanospheres with a shell thickness of about 80 nm. After carbon coating by the thermal decomposition of dopamine, the SnO2 nanospheres are well encapsulated in the uniform carbon shells, with a thickness of ~ 30 nm, to form intermediate SnO2@C. The final product of SnS2@C was obtained after sulfidation using thioacetamide as a sulfur source, which inherited the structure and morphology of the SnO2@C hollow nanospheres, as shown in Fig. 1g–i. The elemental mapping images in Fig. 1k further indicates the hollow character of SnS2@C and the distributions of tin and sulfur in the carbon shells.
As evidenced by the X-ray diffraction (XRD) pattern shown in Fig. 2a, all the diffraction peaks are well indexed to the hexagonal phase SnS2 (JCPDS card no. 23-0677), indicating the complete sulfidation of SnO2@C. No carbon peak can be detected in the XRD pattern, suggesting the low content or amorphous nature of the carbon layer. The carbon content in the SnS2@C sample was determined through CHNS elemental analysis, with a value of 17.6 wt%. Considering the XRD result, the thermal decomposition of dopamine generated disordered carbon shells on the hollow spheres, which can be further supported by the Raman spectrum, showing a higher intensity for the disorder-induced D band than that for the graphitic G band. The sharp peak, located at 312 cm−1, can be ascribed to in-plane vibrational modes in the S–Sn–S plane of hexagonal SnS2 [24]. The surface feature and element states of the SnS2@C were validated using XPS. The survey spectrum (Fig. 2c) indicates that the composite is composed of Sn, S, and C elements. The Sn 3d high-resolution XPS spectrum shows two peaks, located at 486.5 and 494.9 eV, corresponding to Sn 3d5/2 and Sn 3d3/2 of Sn4+, respectively [31]. The S 1s peak can be fitted to peaks at 162.1 and 163.3 eV, which can be ascribed to S2− in SnS2, and to a peak at 164.2 eV, corresponding to elemental S [11]. For the C 1s spectrum, the XPS peak can be de-convolved into three components of carbon species at 284.7, 286.0, and 288.9 eV, indicating the existence of non-oxygenated carbon, carbon in C–N bonds, and C=N bonds, respectively [24, 32, 33]. The Brunauer–Emmett–Teller surface area of SnS2@C was measured to be 93.1 m2 g−1, which is higher than that of SnS2/C, with a value of 75.3 m2 g−1, as shown in Fig. S12.
CV was conducted to evaluate the sodiation/de-sodiation reactions of the SnS2@C hollow nanospheres at a scan rate of 0.1 mV s−1, as shown in Fig. 3a. The distinct peaks in the initial cathodic scan, located at 1.76 and 1.18 V, can be attributed to the Na+ intercalation into SnS2 to form NaxSnS2 [13, 32]. The broad peak, ranging from 0.59 to 0.3 V, is related to the conversion reaction of NaxSnS2 to form Na2S and metallic Sn and, subsequently, the alloying reaction between the formed Sn and Na+ as well as the formation of solid electrolyte interphase film. In the anodic scan, the peak at 0.25 V corresponds to the extraction of Na+ from NaxSn. Meanwhile, the peak at 1.14 V can be assigned to the reformation of NaxSnS2 [34].
To elucidate the structural virtue, SnS2/C bulks were prepared to provide a comparison under the identical synthesis conditions as those for SnS2@C hollow nanospheres except a rapid heating rate of 30 °C min−1 in the sulfidation procedure. The carbon content of SnS2/C bulks is 15.6 wt% by CHNS elemental analysis. Figure 3b presents the comparison of the rate capabilities of SnS2@C hollow nanospheres and SnS2/C bulks. The average specific capacities of SnS2@C are 695.5, 604.1, 507.6, 427.2, and 350.8 mAh g−1 at current densities of 0.1, 1, 2, 3, and 4 A g−1, respectively. Remarkably, SnS2@C delivered a high capacity of 304.4 mAh g−1 at a relatively large current density of 5 A g−1. When the current density returned to 0.1 A g−1, the specific capacity recovered to 665.5 mAh g−1, showing good reversibility. By contrast, the SnS2/C shows lower capacities at various current densities (only 34.8 mAh g−1 at 5 A g−1). Figure 3c presents the representative discharge/charge profiles of SnS2@C under different current densities, corresponding to Fig. 3b. In terms of cyclic stability, SnS2@C exhibits superior capacity retention compared with SnS2/C, delivering a specific capacity of 626.8 mAh g−1 at the 200th cycle under 0.2 A g−1, which is much larger than that of SnS2/C bulks with a value of 110.5 mAh g−1, as shown in Fig. 3d. EIS measurements were conducted to reveal the difference in electrochemical behavior between SnS2/C and SnS2@C. The Nyquist plots and resistance values simulated from modeling the experimental impedance spectra are shown in Figs. 3e, S14, and Table S1, which show the lower charge transfer resistance of SnS2@C hollow nanospheres as compared with that of SnS2/C bulks.
To clarify the reaction kinetics underlying the superior sodium storage of SnS2@C, CV tests at various scan rates of 0.2, 0.4, 0.6, 0.8, and 1 mV s−1 were conducted to investigate the sodiation and de-sodiation processes. As shown in Fig. 3f, the cathodic and anodic peak current responses increase with increasing scan rate, with a gradual broadening of the peaks. The relationship between the peak current and scan rate was calculated based on the equation of log i = b·logv + log a, where a and b are two variables, and the b-value determines the sodiation and de-sodiation types, which is between 0.5 and 1.0. The b-value approaching 1.0 refers to a capacitive-dominated process, while b-values close to 0.5 indicate that the electrochemical reactions are under the control of ion diffusion. The b-values are calculated to be 0.7 and 0.75 for the anodic and cathodic peaks, respectively, indicating a combined effect between capacitive and ion diffusion processes on sodium storage. The capacitive contribution can be further quantitatively determined based on the equation i = k1·v + k2·v1/2, which includes the capacitive effect (k1·v) and diffusion-controlled reaction (k2·v1/2). The capacitive contributions are calculated to be 32.07%, 45.89%, 49.40%, and 52.44% at the scan rates of 0.2, 0.4, 0.6, and 0.8 mV s−1, respectively, as shown in Fig. 3h. Compared with SnS2/C, the large values of the capacitive contribution ratios of SnS2@C can be attributed to the high surface area stemming from the hollow structure. Figure 3i displays the ratio of the capacitive contribution to the total capacity for the SnS2@C hollow nanospheres, with a value of 53.27% at a scan rate of 1.0 mV s−1.
Compared with the SnS2/C bulks and reported tin sulfides materials, 3D SnS2@C hollow nanospheres exhibit outstanding electrochemical performance compared with 0D SnS2/C composites, 2D SnS2/graphene composites, and SnS2-based hybrids, as anode materials for sodium ion batteries, as summarized in Table S2 in Supporting Information. This performance could be attributed to the following characteristics: (1) the hollow structure facilitates high surface permeability because of the large electrolyte/electrode interfaces and more reactive sites for sodium ions. More importantly, the inner hollow space can accommodate the large volume expansion (324%) and, therefore, absorb the stress generated in the reaction processes; (2) the uniform carbon shells efficiently buffer the volume variation during the sodiation and de-sodiation processes, maintaining the mechanical stability and structural integrity of SnS2 hollow nanospheres. Moreover, the connected carbon shells provide a conductive framework to promote electron transfer and enhance the electrical conductivity of the composite; (3) the annealed hollow structure and large surface area are favorable to the capacitive contribution during the charge and discharge processes, producing a preferred effect on rate capability.
To uncover the underlying reaction mechanism of SnS2@C hollow nanospheres, a combined study of in situ XRD and HRTEM images was conducted for further analysis, as shown in Fig. 4a–c. The 2D view of in situ XRD patterns displays the gradual disappearance of the main peaks of SnS2 at 15.3°, 28.2°, 32.1° and 41.9° during the initial discharge process, indicating the participation of SnS2 by Na+ intercalation. As the reaction progresses, no new peaks, corresponding to Na2S nor NaxSn, can be discerned in the XRD patterns, which may be due to the low crystallinity [20]. Meanwhile, the HRTEM image (Fig. 4b) provides clear evidence of the existence of Na2S and sodiated Sn, Na15Sn4, at the fully discharged state, verifying the occurrence of the alloying reaction between Na+ and the formed Sn. When de-sodiation proceeds to 3.0 V (Fig. 4c), the detection of SnS and SnS2 demonstrates the partial irreversible recovery of SnS2 from metallic Sn, which can be ascribed to sluggish reaction kinetics [20]. Figure 4d–f shows the TEM images of the SnS2@C electrode after 100 cycles at the current density of 0.5 A g−1, demonstrating the structural stability. It is found that SnS2@C hollow nanospheres are amorphous to some extent, and the structural integrity is well maintained after cycling.
4 Conclusion
In summary, SnS2@C hollow nanospheres were synthesized via a facile solvothermal route, followed by an annealing treatment. Standing out from the various widely reported 2D structured SnS2 electrode materials for sodium ion batteries, the obtained SnS2@C hollow nanospheres possess multiple merits, including many active sites, high surface permeability, desirable void space for volume expansion, and favorable kinetics by the virtue of a high face-to-volume ratio. Combined with the effective buffering effects of the carbon coating strategy, the mechanical stability is considerably improved to withstand repeated charging/discharge processes, showing decent sodium storage performance. The resultant SnS2@C hollow nanospheres exhibit high specific capacity and superior rate capability, in part owing to the capacitive contribution for fast sodiation/de-sodiation reaction kinetics, based on the quantitative capacitive analysis. The facile synthesis and satisfied electrochemical properties enable SnS2@C hollow nanospheres to be a promising high-performance electrode material for energy storage and conversion.
References
C.X. Zu, H. Li, Thermodynamic analysis on energy densities of batteries. Energy Environ. Sci. 4(8), 2614–2624 (2011). https://doi.org/10.1039/c0ee00777c
D. Li, H. Wang, T. Zhou, W. Zhang, H.K. Liu, Z. Guo, Unique structural design and strategies for germanium-based anode materials toward enhanced lithium storage. Adv. Energy Mater. 7(23), 1700488 (2017). https://doi.org/10.1002/aenm.201700488
S. Zhao, Z. Wang, Y. He, B. Jiang, Y. Harn et al., Interconnected Ni(HCO3)2 hollow spheres enabled by self-sacrificial templating with enhanced lithium storage properties. ACS Energy Lett. 2(1), 111–116 (2017). https://doi.org/10.1021/acsenergylett.6b00582
B. Jiang, C. Han, B. Li, Y. He, Z. Lin, In-situ crafting of ZnFe2O4 nanoparticles impregnated within continuous carbon network as advanced anode materials. ACS Nano 10(2), 2728–2735 (2016). https://doi.org/10.1021/acsnano.5b07806
Y. Liu, N. Zhang, L. Jiao, J. Chen, Tin nanodots encapsulated in porous nitrogen-doped carbon nanofibers as a free-standing anode for advanced sodium-ion batteries. Adv. Mater. 27(42), 6702–6707 (2015). https://doi.org/10.1002/adma.201503015
B. Jiang, Y. He, B. Li, S. Zhao, S. Wang, Y.B. He, Z. Lin, Polymer-templated formation of polydopamine-coated SnO2 nanocrystals: anodes for cyclable lithium-ion batteries. Angew. Chem. Int. Ed. 56(7), 1869–1872 (2017). https://doi.org/10.1002/anie.201611160
E. de la Llave, V. Borgel, K.J. Park, J.Y. Hwang, Y.K. Sun et al., Comparison between Na-ion and Li-ion cells: understanding the critical role of the cathodes stability and the anodes pretreatment on the cells behavior. ACS Appl. Mater. Interfaces 8(3), 1867–1875 (2016). https://doi.org/10.1021/acsami.5b09835
M.D. Slater, D. Kim, E. Lee, C.S. Johnson, Sodium-ion batteries. Adv. Funct. Mater. 23(8), 947–958 (2013). https://doi.org/10.1002/adfm.201200691
V. Palomares, P. Serras, I. Villaluenga, K.B. Hueso, J. Carretero-Gonzalez, T. Rojo, Na-ion batteries, recent advances and present challenges to become low cost energy storage systems. Energy Environ. Sci. 5(3), 5884–5901 (2012). https://doi.org/10.1039/c2ee02781j
H. Pan, Y.S. Hu, L. Chen, Room-temperature stationary sodium-ion batteries for large-scale electric energy storage. Energy Environ. Sci. 6(8), 2338–2360 (2013). https://doi.org/10.1039/c3ee40847g
P.V. Prikhodchenko, D.Y.W. Yu, S.K. Batabyal, V. Uvarov, J. Gun et al., Nanocrystalline tin disulfide coating of reduced graphene oxide produced by the peroxostannate deposition route for sodium ion battery anodes. J. Mater. Chem. A 2(22), 8431–8437 (2014). https://doi.org/10.1039/c3ta15248k
T. Jin, Q. Han, Y. Wang, L. Jiao, 1D nanomaterials: design, synthesis, and applications in sodium–ion batteries. Small 14(2), 1703086 (2018). https://doi.org/10.1002/smll.201703086
Y. Liu, H. Kang, L. Jiao, C. Chen, K. Cao, Y. Wang, H. Yuan, Exfoliated-SnS2 restacked on graphene as a high-capacity, high-rate, and long-cycle life anode for sodium ion batteries. Nanoscale 7(4), 1325–1332 (2015). https://doi.org/10.1039/C4NR05106H
L. Wu, X. Hu, J. Qian, F. Pei, F. Wu et al., A Sn–SnS–C nanocomposite as anode host materials for Na-ion batteries. J. Mater. Chem. A 1(24), 7181–7184 (2013). https://doi.org/10.1039/c3ta10920h
T. Zhou, W.K. Pang, C. Zhang, J. Yang, Z. Chen, H.K. Liu, Z. Guo, Enhanced sodium-ion battery performance by structural phase transition from two-dimensional hexagonal-SnS2 to orthorhombic-SnS. ACS Nano 8(8), 8323–8333 (2014). https://doi.org/10.1021/nn503582c
Y. Zheng, T. Zhou, C. Zhang, J. Mao, H. Liu, Z. Guo, Boosted charge transfer in SnS/SnO2 heterostructures: toward high rate capability for sodium-ion batteries. Angew. Chem. Int. Ed. 55(10), 3408–3413 (2016). https://doi.org/10.1002/anie.201510978
Y. Jiang, Y. Guo, W. Lu, Z. Feng, B. Xi et al., Rationally incorporated MoS2/SnS2 nanoparticles on graphene sheets for lithium-ion and sodium-ion batteries. ACS Appl. Mater. Interfaces 9(33), 27697–27706 (2017). https://doi.org/10.1021/acsami.7b06572
D. Ma, Y. Li, H. Mi, S. Luo, P. Zhang, Z. Lin, J. Li, H. Zhang, Robust SnO2−x nanoparticle-impregnated carbon nanofibers with outstanding electrochemical performance for advanced sodium-ion batteries. Angew. Chem. Int. Ed. 57(29), 8901–8905 (2018). https://doi.org/10.1002/anie.201802672
X. Wang, X. Li, Q. Li, H. Li, J. Xu et al., Improved electrochemical performance based on nanostructured SnS2@CoS2–rGO composite anode for sodium-ion batteries. Nano-Micro Lett. 10, 46 (2018). https://doi.org/10.1007/s40820-018-0200-x
W. Sun, X. Rui, D. Yang, Z. Sun, B. Li et al., Two-dimensional tin disulfide nanosheets for enhanced sodium storage. ACS Nano 9(11), 11371–11381 (2015). https://doi.org/10.1021/acsnano.5b05229
B. Qu, C. Ma, G. Ji, C. Xu, J. Xu et al., Layered SnS2-reduced graphene oxide composite—a high-capacity, high-rate, and long-cycle life sodium-ion battery anode material. Adv. Mater. 26(23), 3854–3859 (2014). https://doi.org/10.1002/adma.201306314
D. Chao, P. Liang, Z. Chen, L. Bai, H. Shen et al., Pseudocapacitive Na-ion storage boosts high rate and areal capacity of self-branched 2D layered metal chalcogenide nanoarrays. ACS Nano 10(11), 10211–10219 (2016). https://doi.org/10.1021/acsnano.6b05566
R. Thangavel, A. Samuthira Pandian, H.V. Ramasamy, Y.S. Lee, Rapidly synthesized, few-layered pseudocapacitive SnS2 anode for high-power sodium ion batteries. ACS Appl. Mater. Interfaces 9(46), 40187–40196 (2017). https://doi.org/10.1021/acsami.7b11040
Y. Zhang, P. Zhu, L. Huang, J. Xie, S. Zhang, G. Cao, X. Zhao, Few-layered SnS2 on few-layered reduced graphene oxide as Na-ion battery anode with ultralong cycle life and superior rate capability. Adv. Funct. Mater. 25(3), 481–489 (2015). https://doi.org/10.1002/adfm.201402833
X. Xie, D. Su, S. Chen, J. Zhang, S. Dou, G. Wang, SnS2 nanoplatelet@graphene nanocomposites as high-capacity anode materials for sodium-ion batteries. Chem-Asian J. 9(6), 1611–1617 (2014). https://doi.org/10.1002/asia.201400018
P. Zhou, X. Wang, W. Guan, D. Zhang, L. Fang, Y. Jiang, SnS2 nanowall arrays toward high-performance sodium storage. ACS Appl. Mater. Interfaces 9(8), 6979–6987 (2017). https://doi.org/10.1021/acsami.6b13613
Y. Wang, J. Zhou, J. Wu, F. Chen, P. Li et al., Engineering SnS2 nanosheet assemblies for enhanced electrochemical lithium and sodium ion storage. J. Mater. Chem. A 5(48), 25618–25624 (2017). https://doi.org/10.1039/C7TA08056E
F. Tu, X. Xu, P. Wang, L. Si, X. Zhou, J. Bao, A few-layer SnS2/reduced graphene oxide sandwich hybrid for efficient sodium storage. J. Phys. Chem. C 121(6), 3261–3269 (2017). https://doi.org/10.1021/acs.jpcc.6b12692
P. Zheng, Z. Dai, Y. Zhang, K.N. Dinh, Y. Zheng et al., Scalable synthesis of SnS2/S-doped graphene composites for superior Li/Na-ion batteries. Nanoscale 9(39), 14820–14825 (2017). https://doi.org/10.1039/C7NR06044K
X.W. Lou, Y. Wang, C. Yuan, J.Y. Lee, L.A. Archer, Template-free synthesis of SnO2 hollow nanostructures with high lithium storage capacity. Adv. Mater. 18(17), 2325–2329 (2006). https://doi.org/10.1002/adma.200600733
Y. Lei, S. Song, W. Fan, Y. Xing, H. Zhang, Facile synthesis and assemblies of flowerlike SnS2 and In3+-doped SnS2: hierarchical structures and their enhanced photocatalytic property. J. Phys. Chem. C 113(4), 1280–1285 (2009). https://doi.org/10.1021/jp8079974
L. Fan, X. Li, X. Song, N. Hu, D. Xiong, A. Koo, X. Sun, Promising dual-doped graphene aerogel/SnS2 nanocrystal building high performance sodium ion batteries. ACS Appl. Mater. Interfaces 10(3), 2637–2648 (2018). https://doi.org/10.1021/acsami.7b18195
Z. Chen, R. Wu, M. Liu, H. Wang, H. Xu et al., General synthesis of dual carbon-confined metal sulfides quantum dots toward high-performance anodes for sodium-ion batteries. Adv. Funct. Mater. 27(38), 1702046 (2017). https://doi.org/10.1002/adfm.201702046
J. Wang, C. Luo, J. Mao, Y. Zhu, X. Fan, T. Gao, A.C. Mignerey, C. Wang, Solid-state fabrication of SnS2/C nanospheres for high-performance sodium ion battery anode. ACS Appl. Mater. Interfaces 7(21), 11476–11481 (2015). https://doi.org/10.1021/acsami.5b02413
Acknowledgements
Financial support provided by the National Natural Science Foundation of China (Grant No. 21701144), the China Postdoctoral Science Foundation (Grant Nos. 2016M592303 and 2017T100536) are gratefully acknowledged.
Author information
Authors and Affiliations
Corresponding authors
Electronic supplementary material
Below is the link to the electronic supplementary material.
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Li, S., Zhao, Z., Li, C. et al. SnS2@C Hollow Nanospheres with Robust Structural Stability as High-Performance Anodes for Sodium Ion Batteries. Nano-Micro Lett. 11, 14 (2019). https://doi.org/10.1007/s40820-019-0243-7
Received:
Accepted:
Published:
DOI: https://doi.org/10.1007/s40820-019-0243-7