Highlights
-
The Mo2C modified carbon nanosheets produce a graphene wave structure to form localized charges and further enhance the N-doping effect.
-
The optimal sample shows a Tafel slope as low as 60.6 mV dec−1 and high durability up to 10 h in acidic media.
Abstract
Charge engineering of carbon materials with many defects shows great potential in electrocatalysis, and molybdenum carbide (Mo2C) is one of the noble-metal-free electrocatalysts with the most potential. Herein, we study the Mo2C on pyridinic nitrogen-doped defective carbon sheets (MoNCs) as catalysts for the hydrogen evolution reaction. Theoretical calculations imply that the introduction of Mo2C produces a graphene wave structure, which in some senses behaves like N doping to form localized charges. Being an active electrocatalyst, MoNCs demonstrate a Tafel slope as low as 60.6 mV dec−1 and high durability of up to 10 h in acidic media. Besides charge engineering, plentiful defects and hierarchical morphology also contribute to good performance. This work underlines the importance of charge engineering to boost catalytic performance.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
1 Introduction
With the intensification of global energy consumption and severe environmental deterioration, sustainable and environmentally friendly approaches have aroused increasing interest [1]. Among ongoing attempts to produce clean fuels, the electrolysis of water to produce H2 is attractive [2,3,4,5,6]. The key to this problem is to seek an effective electrocatalyst to minimize the overpotential for hydrogen evolution reaction (HER). To replace Pt-based noble metals, abundant earth catalysts have received great attention [7,8,9,10,11]. Because of their similar electronic structure and catalytic behaviors to Pt [12], Mo-based compounds [13, 14], especially molybdenum carbide [15], have drawn tremendous fascination. On the other hand, the electronic structure significantly affects the interaction between the catalyst surface and reactants [4, 16,17,18,19,20]. Charge engineering is an important strategy to regulate the surface/interface behaviors involved in catalysis. For example, Sasaki et al. [21] found that carbide ligand changed the d-electron configuration of Mo2C to moderate Mo–H binding energy, leading to enhanced-HER activity.
Recently, researchers have paid great attention to nitrogen-doped defective carbon materials for electrocatalysis [22,23,24,25,26]. The defects not only play an important role in the adsorption/desorption during reaction, but also change the electrical conductivity of the catalysts to regulate the electronic structure [27]. However, related work on the application of MO2C to pyridinic N-doped carbon is limited. Furthermore, for gas-involving electrocatalysis, the hierarchical morphology is also important to optimize the gas/mass transport [16].
Considering the above-mentioned observations, Mo2C@ defect-rich N-doped carbon nanosheets (MoNCs) were developed. The theoretical results imply that the introduction of Mo2C produces a graphene wave structure, which to a degree behaves like N doping to form localized charges. As expected, the catalyst shows high-electrocatalytic HER activity with a Tafel slope as low as 60.6 mV dec−1 and stability up to 10 h in acidic media, making it one of the best Mo2C electrocatalysts. The multifold design, including charge engineering and nanoarchitecture construction, contributes to the HER performance.
2 Experimental Section
2.1 Materials
Ammonium heptamolybdate ((NH4)6Mo7O24·4H2O), melamine (C3H6N6), sucrose, and sulfuric acid (H2SO4, 98%) were bought from Tianjin Kaida Chemical Factory, Tianjin Kermel Chemical Factory, Sinopharm Chemical Reagent Co., Ltd., and Beijing Chemical Factory, respectively. Nafion solution (5 wt.%, Dupont D520) and Pt/C (20 wt.%, JM) were bought from Shanghai Hesen Electric Co., Ltd.
2.2 Synthesis
Graphitic carbon nitride (g-C3N4) was prepared by simple calcination. A certain quantity of melamine was placed in an alumina crucible (100 mL) with a cover and then heated at 550 °C for 4 h in a muffle furnace (2.3 °C min−1). Subsequently, the obtained light-yellow solid product was milled into a powder state and sealed for later use. Next, ammonium heptamolybdate, sucrose, and g-C3N4 were mixed together (1:2:2, mass ratio). The homogeneous mixture was placed in an alumina crucible and then transferred to the center of the tube furnace. After pumping and purging the system three times with N2 flow, it was heated to 800 °C (3 °C min−1) and maintained at 800 °C for 6 h under flowing N2. The obtained black sample, called MoNCs (Mo2C@N-doped carbon sheets; the mass ratio of g-C3N4 and ammonium heptamolybdate is 2), was then ground to a fine powder without further treatment. For comparison, MoNCs-0, MoNCs-1, and MoNCs-5 (the mass ratio of g-C3N4 and ammonium heptamolybdate is 0, 1, 5), as counterparts, were also prepared in the same way.
2.3 Materials Characterization
X-ray diffraction (XRD) was applied on Siemens D-5005 with Cu Kα radiation (2θ = 0.02° per step). X-ray photoelectron spectra (XPS) were performed with an Al Kα source (Thermo Scientific ESCALAB Ka+). The transmission electron microscope (TEM) operated on JEM-2100 at 200 kV. The nitrogen adsorption isotherm (ASAP 2020 at 77 K, USA) was recorded by the Brunauer–Emmett–Teller (BET) equation and Barrett–Joyner–Halenda (BJH) model. The Raman spectrum was measured on LabRAM HR800. Thermogravimetric analysis (TGA) was carried out on an SDT Q600 (TA) instrument under air flow (10 °C min−1) up to 700 °C. The product transformed according to the following reaction: Mo2C + 4O2 = 2MoO3 + CO2 [28].
2.4 Computational Details
In this work, nanosheets with Mo2C nanoparticles have been modeled as single-layer graphene in a 6 × 6 × 1 supercell, and Mo2C in a 5 × 5 × 2 supercell. The cell and atomic coordinates are fully relaxed based on the density functional theory implemented in the Vienna Ab-initio Simulation Package (VASP) v5.3.5 [29,30,31] with grimme-D2 correction [32], where the PBE functional [33] and PAW pseudopotential [34, 35] have been used. The criteria of convergence of energy and force have been taken as 1 × 10−6 eV and 0.01 eV Å−1, respectively, the energy cutoff is set to 450 eV, and a 3 × 3×1 k-mesh is used to sample the Brillouin zone [36, 37]. The parameters are comparable to those in Refs. [36, 37]. In the core-level shift (CLS) calculation, the final state approximation has been adopted.
2.5 Electrochemical Measurements
The HER measurements were performed in a typical three-electrode cell in 0.5 M H2SO4 using a CHI 660e electrochemical station (Shanghai Chenhua Co., China) at room temperature. A glassy carbon electrode (GCE) 8 mm in diameter, a saturated calomel electrode (SCE), and a graphite rod electrode were used as the working electrode, reference electrode, and counter electrode, respectively. All of the potentials were converted to the potential versus the reversible hydrogen electrode (RHE) according to E (RHE) = E (SCE) + 0.241 + 0.059 pH. The working electrode was fabricated as follows: A catalyst ink was prepared by dispersing 6 mg of catalyst into a mixed solution including 40 μL Nafion solution and 1 mL of 3:1 v/v water/isopropanol via sonication for at least 1 h to form a homogeneous ink. Then, 20 μL of well-dispersed catalyst ink was drop-casted on the glassy carbon electrode, producing a ~ 0.23 mg cm−2 loading for all samples, and the modified GC electrode was then dried at 50 °C in a drying oven for the following test. Before data collection, all working electrodes were pretreated by cyclic voltammetric scanning in 0.5 M H2SO4 solution to activate the electrodes. The electrochemical impedance spectroscopy (EIS) measurements were tested in 0.5 M H2SO4 solution with open-circuit voltage at a frequency from 10 mHz to 100 kHz at an amplitude of 5 mV.
3 Results and Discussion
We combined Mo2C and N-doped graphene and theoretically simulated its atomic structure with first-principles calculation. Due to the limitation of computations, we used a slab of Mo2C covered with one layer of graphene to simulate part of the interface region of Mo2C and graphene. The vacuum was added in the direction perpendicular to the graphene plane, and periodicity was kept in the other two directions. According to the literature [37, 38], the β-Mo2C is a meta-stable structure at high temperature, where the Mo atoms are packed in a hexagonal close-packed structure, and the C atoms randomly occupy half of the octahedral interstitial sites (Fig. 1). As noted, the Mo2C@N-doped graphene has two types of structures: The Mo-terminated surface adhered to the graphene, and the C-terminated surface adhered to the graphene. We found that in Mo-terminated Mo2C@N-doped graphene, the graphene was approximately 2.22 Å above the Mo2C (Fig. 1b). Interestingly, the phenomenon of a graphene wave was observed, which should be attributed to the mismatch of the graphene and Mo2C unit cell. We have reason to believe that the graphene wave could introduce more localized charge density on some C sites, as indicated by the yellow circles (Fig. 1f), leading to the redistribution of electrons on the graphene and formation of a gradient of charge density to increase active sites. For C-terminated Mo2C@N-doped graphene, the graphene is found to be self-reorganized in the bulk defect region and approximately 3.96 Å above Mo2C (Fig. 1d).
Here, a Mo2C slab covered with one layer of graphene was used to simulate the real case, in which Mo2C nanoparticles are enclosed in nanosheets. Given that the nanoparticles have various shapes and sizes, the structural change and charge localization on the graphene should be more significant, as the nanoparticles have curved and highly indexed surfaces. On the other hand, with the increase in the number of nanosheets, the effect weakens. However, for a nanoparticle with two or three layers of nanosheets, the predicted phenomena should occur and contribute to the catalysis. Moreover, to clarify the influence of Mo2C on N-doped carbon sheets (NCS) further, we computed the N1s CLS within pyridinic N-doped graphene and Mo2C@N-doped graphene. For Mo-terminated Mo2C@N-doped graphene, the CLS moves forward to a higher energy (Figs. 1e, f and S1). The N1s core level deepens, which means that N achieved more electrons localized on the N atom. This will strengthen the N-doping effect and further promote the HER activity. Apart from these, we also calculated three more types of N doping in the Mo2C region within Mo2C@N-doped graphene, as shown in Fig. S1b–d. All three types of structures yield rather smaller binding energies for N1s core electrons.
The synthesis route of MoNCs is shown in Fig. 2a. The carbonization of sucrose and the decomposition of ammonium heptamolybdate and g-C3N4 were integrated, rendering the simultaneous formation of uniformly dispersed Mo2C and N-doped carbon nanosheets. The synthesis avoids sophisticated or hazardous processes and expensive precursors. Figure 2b clearly displays the diffraction peaks at 34.4°, 38.0°, and 39.4°, attributed to the (100), (002), and (101) plane of hexagonal β-Mo2C (PDF# 35-0787), respectively [40]. No additional peaks were observed except for the (002) diffraction peak of graphite at ~ 26° [41]. Then, the N2 adsorption–desorption measurement (Fig. 2c) was carried out to investigate the specific surface area and pore structure. The typical type-IV isotherm curve is noted according to the Brunauer–Deming–Deming–Teller classification [42], verifying the presence of mesopores [43]. The BET surface area (SBET) is evaluated as 216.4 m2 g−1. The pore size distribution curve indicates the presence of micropores and mesopores, which are probably caused by the released molecules (H2O, CO2, C2N2+, C3N2+, C3N3+, etc.) during the carbonization of sucrose [44, 45] and the decomposition of g-C3N4 [46]. There is no doubt that the hierarchically porous structure will supply adequate diffusion passageways to strengthen the mass transfer [47].
In Fig. 3a, b, the typical TEM and HRTEM images reveal that MoNCs mainly consisted of a large amount of 1–3-nm Mo2C (inset in Fig. 3b) particles wrapped in thin carbon nanosheets. The lattice spacing is ~ 0.23 nm, corresponding to the distance between the (101) crystal planes of β-Mo2C. The thin carbon nanosheets (3–5 graphene layers) with lattice spacing of ~ 0.34 nm not only inhibit the agglomeration of Mo2C, but also guarantee the fast electron transfer and effective exposure of active phases. Massive defects were also noted (white arrows). The elemental mapping (Fig. 3c–f) result indicates that the Mo, N, and C atoms were homogeneously distributed. The Raman spectrum (Fig. 3g) also displays the typical D-band and G-band at 1341 and 1583 cm−1, respectively. The D1, D3, D4, and G peaks were fitted [48]. The high value (2.16) of ID1/IG implies abundant defects, which are believed to enhance the electrocatalytic activity [49]. The Mo2C content in MoNCs determined by TGA is ~ 50.0 wt.% (Fig. S2). X-ray photoelectron spectroscopy (XPS) was used to further characterize the composition and chemical state of each element. As seen in Fig. S3, the survey XPS spectrum of the MoNCs shows obvious signals of elemental Mo, C, and N, which is consistent with the elemental mapping result above. The Mo 3d XPS spectrum (Fig. 3h) was deconvoluted into six peaks, corresponding to Mo2+ (228.6 and 232.4 eV), Mo4+ (229.3 and 232.8 eV), and Mo6+ (233.2 and 235.9 eV) species [50]. Mo2+ comes from Mo2C, which serves as the active sites for HER [51, 52]. In Fig. S4, the main peak at 284.6 eV in the deconvoluted C1s spectrum implies that graphite carbon is the majority species [53]. The N1s XPS spectrum was deconvoluted into two peaks at 401.3 and 398.6 eV (Fig. 3i), corresponding to the quaternary N (20%) and pyridinic N (80%), respectively. The high pyridinic N content will be favorable for HER [54]. Moreover, the element contents in the MoNCs were calculated and summarized in Table S2.
The electrocatalytic HER performance was investigated. For comparison, control samples synthesized with different mass ratios of starting materials were also tested. In Fig. 4a, the MoNCs show a low onset overpotential of 83 mV and the lowest overpotential of 157 mV @ 10 mA cm−2, exhibiting the best HER activity among the four control samples. In addition, the influence of loading mass on the HER activity was also studied (Fig. S5). The linear sweep voltammetry (LSV) curves of the MoNCs are also provided when the loading mass increased from 0.115 to 0.460 mg cm−2, indicating the enhanced-HER performance with more loadings. To demonstrate the HER mechanism, the linear sections of the Tafel plots were fitted to the Tafel equation (η = a + b log (j), where a is the intercept, b is the Tafel slope, and j is the current density), as shown in Fig. 4b. The MoNCs achieve the smallest Tafel slope of 60.6 mV dec−1 among the four samples (Table S3), suggesting that HER can likely proceed through the Volmer–Heyrovsky mechanism [55]. Remarkably, the exchange current density (j0) for MoNCs, calculated by extrapolating the Tafel plot to an overpotential of 0 mV (Fig. S6), was also the highest (2.65 × 10−2 mA cm−2). Compared to the previously reported Mo2C-based non-precious-metal catalysts, the excellent HER performance makes our sample one of the most promising electrocatalysts (Fig. 4c, Table S3). MoNCs show almost no current loss after 1000 CV cycles (Fig. 4e). Furthermore, the current density exhibits a negligible degeneration at a static overpotential of 157 mV after 10 h of constant operation, verifying the high durability.
The effective electrochemical surface area (ECSA) was evaluated by the electrochemical double-layer capacitance (EDLC, Cdl) (Figs. 4d, 5). The Cdl measured at 0.10 V for MoNCs was the highest (14.31 mF cm−2), indicating more active sites. The EIS was also tested (Fig. S7). The Nyquist plot of the MoNCs displays a small semicircle among them, suggesting lower impedance to accelerate the charge transfer during HER. Furthermore, the turnover frequency (TOF) of MoNCs was estimated [56] (see more details from supporting information). In Fig. S8, the MoNCs achieved a TOF of 0.07 and 1.12 s−1 at overpotential of 150 and 250 mV, respectively. The values were much higher than those of other catalysts, indicating more active sites.
4 Conclusion
In summary, we illustrate charge engineering of Mo2C@ defect-rich N-doped carbon nanosheets for electrocatalytic H2 evolution. The calculation result indicates that the introduction of Mo2C induces a graphene wave structure, which behaves like N doping to form localized charges for the first time. The thin carbon nanosheets, combined with plentiful defects, facilitate the fast electron transfer and effective exposure of active phases. As a result, the sample displays a Tafel slope as low as 60.6 mV dec−1 and high durability up to 10 h in acidic media, featuring excellent HER catalytic activity and stability. Our work emphasizes the importance of charge engineering in electrocatalysis.
References
Z. Shi, K. Nie, Z.J. Shao, B. Gao, H. Lin et al., Phosphorus-Mo2C@carbon nanowires toward efficient electrochemical hydrogen evolution: composition, structural and electronic regulation. Energy Environ. Sci. 10, 1262–1271 (2017). https://doi.org/10.1039/C7EE00388A
C. Tang, N. Cheng, Z. Pu, W. Xing, X. Sun, NiSe nanowire film supported on nickel foam: An efficient and stable 3D bifunctional electrode for full water splitting. Angew. Chem. Int. Ed. 54, 9351–9355 (2015). https://doi.org/10.1002/anie.201503407
Y. Fang, H. Zhou, Y. Huang, J. Sun, F. Qin, J. Bao, W.A. Goddardlll, S. Chen, Z. Ren, High-performance bifunctional porous non-noble metal phosphide catalyst for overall water splitting. Nat. Commun. 9, 2551 (2018). https://doi.org/10.1038/s41467-018-04746-z
Z.L. Chen, H. Yuan, Y. Liu, H. Wang, H.Y. Yang, H.B. Xu, Y.J. Li, R.B. Wu, In situ formation of cobalt nitrides/graphitic carbon composites as efficient bifunctional electrocatalysts for overall water splitting. ACS Appl. Mater. Interfaces. 10, 7134–7144 (2018). https://doi.org/10.1021/acsami.7b18858
W. Ma, R. Ma, J. Wu, P. Sun, X. Liu, K. Zhou, T. Sasaki, Development of efficient electrocatalysts via molecular hybridization of NiMn layered double hydroxide nanosheets and graphene. Nanoscale 8, 10425–10432 (2016). https://doi.org/10.1039/C6NR00988C
G. Fang, Q. Wang, J. Zhou, Y. Lei, Z. Chen, B. Wu, A. Pan, S. Liang, Metal organic framework-templated synthesis of bimetallic selenides with rich phase boundaries for sodium-ion storage and oxygen evolution reaction. ACS Nano 9b00816 (2019). https://doi.org/10.1021/acsnano.9b00816
T. He, H. Xue, X. Wang, S. He, Y. Lei et al., Architecture of CoNx single clusters on nanocarbon as excellent oxygen reduction catalysts with high-efficient atomic utilization. Nanoscale 9, 8341–8348 (2017). https://doi.org/10.1039/C7NR02165H
H. Zhang, H. Qiao, H. Wang, N. Zhou, J. Chen, Y. Tang, J. Li, C. Huang, Nickel cobalt oxide/carbon nanotubes hybrid as a high-performance electrocatalyst for metal/air battery. Nanoscale 6, 10235–10242 (2014). https://doi.org/10.1039/C4NR02125H
M. Wang, Z. Fang, K. Zhang, J. Fang, F. Qin, Z. Zhang, J. Li, Y. Liu, Y. Lai, Synergistically enhanced activity of graphene quantum dots/graphene hydrogel composites: A novel all-carbon hybrid electrocatalyst for metal/air batteries. Nanoscale 8, 11398–11402 (2016). https://doi.org/10.1039/C6NR02622B
T. Sun, L. Xu, D. Wang, Y. Li, Metal organic frameworks derived single atom catalysts for electrocatalytic energy conversion. Nano Res. (2019). https://doi.org/10.1007/s12274-019-2345-4
F. Yu, L. Yu, I.K. Mishra, Y. Yu, Z. Ren, H. Zhou, Recent developments in earth-abundant and non-noble electrocatalysts for water electrolysis. Mater. Today Phys. 7, 121–138 (2018). https://doi.org/10.1016/j.mtphys.2018.11.007
R.B. Levy, M. Boudart, Platinum-like behavior of tungsten carbide in surface catalysis. Science 181, 547–549 (1973). https://doi.org/10.1126/science.181.4099.547
Y. Zhu, G. Chen, X. Xu, G. Yang, M. Liu, Z. Shao, Enhancing electrocatalytic activity for hydrogen evolution by strongly coupled molybdenum nitride@nitrogen-doped carbon porous nano-octahedrons. ACS Catal. 7, 3540–3547 (2017). https://doi.org/10.1021/acscatal.7b00120
J. Wang, W. Chen, T. Wang, N. Bate, C. Wang, E. Wang, A strategy for highly dispersed Mo2C/MoN hybrid nitrogen-doped graphene via ion-exchange resin synthesis for efficient electrocatalytic hydrogen reduction. Nano Res. 11, 4535–4548 (2018). https://doi.org/10.1007/s12274-018-2034-8
L. Chen, H. Jiang, H. Jiang, H. Zhang, S. Guo, Y. Hu, C. Li, Mo-based ultrasmall nanoparticles on hierarchical carbon nanosheets for superior lithium ion storage and hydrogen generation catalysis. Adv. Energy Mater. 7, 1602782 (2017). https://doi.org/10.1002/aenm.201602782
L. Zhao, Q. Wang, X. Zhang, C. Deng, Z. Li, Y. Lei, M. Zhu, Combined electron and structure manipulation on Fe containing N-doped CNTs to boost bifunctional oxygen electrocatalysis. ACS Appl. Mater. Interfaces 10, 35888–35895 (2018). https://doi.org/10.1021/acsami.8b09197
Y. Dong, B. Zeng, J. Xiao, X. Zhang, D. Li, M. Li, J. He, M. Long, Effect of sulphur vacancy and interlayer interaction on the electronic structure and spin splitting of bilayer MoS2. J. Phys. Condens. Mat. 30, 125302 (2018). https://doi.org/10.1088/1361-648X/aaad3b
Y.Y. Chen, Y. Zhang, W.J. Jiang, X. Zhang, Z. Dai, L.J. Wan, J.S. Hu, Pomegranate-like N, P-doped Mo2C@C nanospheres as highly active electrocatalysts for alkaline hydrogen evolution. ACS Nano 10, 8851–8860 (2016). https://doi.org/10.1021/acsnano.6b04725
N. Han, K.R. Yang, Z. Lu, W. Xu, T. Gao et al., Nitrogen-doped tungsten carbide nanoarray as an efficient bifunctional electrocatalyst for water splitting. Nat. Commun. 9, 924 (2018). https://doi.org/10.1038/s41467-018-03429-z
Y. Bai, H. Huang, C. Wang, R. Long, Y. Xiong, Engineering the surface charge states of nanostructures for enhanced catalytic performance. Mater. Chem. Front. 1, 1951–1964 (2017). https://doi.org/10.1039/C7QM00020K
W.F. Chen, C.H. Wang, K. Sasaki, N. Marinkovic, W. Xu, J.T. Muckerman, Y. Zhu, R.R. Adzic, Highly active and durable nanostructured molybdenum carbide electrocatalysts for hydrogen production. Energy Environ. Sci. 6, 943–951 (2013). https://doi.org/10.1039/c2ee23891h
Y. Lei, Q. Shi, C. Han, B. Wang, N. Wu, H. Wang, Y. Wang, N-doped graphene grown on silk cocoon-derived interconnected carbon fibers for oxygen reduction reaction and photocatalytic hydrogen production. Nano Res. 9, 2498–2509 (2016). https://doi.org/10.1007/s12274-016-1136-4
Q. Wang, Y. Lei, D. Wang, Y. Li, Defect engineering in earth-abundant electrocatalysts for CO2 and N2 reduction. Energy Environ. Sci. (Advance Article, 2019). https://doi.org/10.1039/C8EE03781G
L. Zhang, Y. Jia, G. Gao, X. Yan, N. Chen et al., Graphene defects trap atomic Ni species for hydrogen and oxygen evolution reactions. Chem 4, 285–297 (2018). https://doi.org/10.1016/j.chempr.2017.12.005
Y. Wei, X. Zhang, Z. Luo, D. Tang, C. Chen, T. Zhang, Z. Xie, Nitrogen-doped carbon nanotube supported Pd catalyst for improved electrocatalytic performance towards ethanol electrooxidation. Nano-Micro Lett. 9, 28 (2017). https://doi.org/10.1007/s40820-017-0129-5
J. Liu, T. He, Q. Wang, Z. Zhou, Y. Zhang et al., Confining ultrasmall bimetal alloys in porous N-Carbon as scalable and sustainable electrocatalysts for rechargeable Zn-air batteries. J. Mater. Chem. A (Advance Article, 2019). https://doi.org/10.1039/C9TA02264C
Q. Wang, Y. Lei, Y. Zhu, H. Wang, J. Feng et al., Edge defect engineering of nitrogen-doped carbon for oxygen electrocatalysts in Zn-air batteries. ACS Appl. Mater. Interfaces 10, 29448–29456 (2018). https://doi.org/10.1021/acsami.8b07863
W. Gao, Y. Shi, Y. Zhang, L. Zuo, H. Lu, Y. Huang, W. Fan, T. Liu, Molybdenum carbide anchored on graphene nanoribbons as highly efficient all-pH hydrogen evolution reaction electrocatalyst. ACS Sustain. Chem. Eng. 4, 6313–6321 (2016). https://doi.org/10.1021/acssuschemeng.6b00859
G. Kresse, J. Hafner, Ab initiomolecular dynamics for liquid metals. Phys. Rev. B 47, 558–561 (1993). https://doi.org/10.1103/PhysRevB.47.558
G. Kresse, J. Hafner, Ab initiomolecular-dynamics simulation of the liquid-metal–amorphous-semiconductor transition in germanium. Phys. Rev. B 49, 14251–14269 (1994). https://doi.org/10.1103/PhysRevB.49.14251
G. Kresse, J. Furthmüller, Efficiency of Ab-initio total energy calculations for metals and semiconductors using a plane-wave basis set. Comput. Mater. Sci. 6, 15–50 (1996). https://doi.org/10.1016/0927-0256(96)00008-0
S. Grimme, Semiempirical GGA-type density functional constructed with a long-range dispersion correction. J. Comput. Chem. 27, 1787–1799 (2006). https://doi.org/10.1002/jcc.20495
J.P. Perdew, K. Burke, M. Ernzerhof, Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865–3868 (1996). https://doi.org/10.1103/PhysRevLett.77.3865
P.E. Blöchl, Projector augmented-wave method. Phys. Rev. B 50, 17953–17979 (1994). https://doi.org/10.1103/PhysRevB.50.17953
G. Kresse, D. Joubert, From ultrasoft pseudopotentials to the projector augmented-wave method. Phys. Rev. B 59, 1758–1775 (1999). https://doi.org/10.1103/PhysRevB.59.1758
J. Jia, W. Zhou, Z. Wei, T. Xiong, G. Li et al., Molybdenum carbide on hierarchical porous carbon synthesized from Cu–MoO2 as efficient electrocatalysts for electrochemical hydrogen generation. Nano Energy 41, 749–757 (2017). https://doi.org/10.1016/j.nanoen.2017.10.030
J.R. Dos Santos Politi, F. Viñes, J.A. Rodriguez, F. Illas, Atomic and electronic structure of molybdenum carbide phases: bulk and low Miller-index surfaces. Phys. Chem. Chem. Phys. 15, 12617–12625 (2013). https://doi.org/10.1039/c3cp51389k
J. Jia, T. Xiong, L. Zhao, F. Wang, H. Liu, R. Hu, J. Zhou, W. Zhou, S. Chen, Ultrathin N-doped Mo2C nanosheets with exposed active sites as efficient electrocatalyst for hydrogen evolution reactions. ACS Nano 11, 12509–12518 (2017). https://doi.org/10.1021/acsnano.7b06607
K. Momma, F. Izumi, VESTA 3 for three-dimensional visualization of crystal, volumetric and morphology data. J. Appl. Cryst. 44, 1272–1276 (2011). https://doi.org/10.1107/S0021889811038970
F.X. Ma, H.B. Wu, B.Y. Xia, C.Y. Xu, X.W.D. Lou, Hierarchical β-Mo2C nanotubes organized by ultrathin nanosheets as a highly efficient electrocatalyst for hydrogen production. Angew. Chem. Int. Ed. 54, 15395–15399 (2015). https://doi.org/10.1002/anie.201508715
S. Zhou, G. Zhou, S. Jiang, P. Fan, H. Hou, Flexible and refractory tantalum carbide-carbon electrospun nanofibers with high modulus and electric conductivity. Mater. Lett. 200, 97–100 (2017). https://doi.org/10.1016/j.matlet.2017.04.115
M. Thommes, K. Kaneko, A.V. Neimark, J.P. Olivier, F. Rodriguez-Reinoso, J. Rouquerol, K.S.W. Sing, Physisorption of gases, with special reference to the evaluation of surface area and pore size distribution (IUPAC Technical Report). Pure Appl. Chem. 87, 1051–1069 (2015). https://doi.org/10.1515/pac-2014-1117
Q. Wang, Y. Ji, Y. Lei, Y. Wang, Y. Wang, Y. Li, S. Wang, Pyridinic-N-dominated doped defective graphene as a superior oxygen electrocatalyst for ultrahigh-energy-density Zn-air batteries. ACS Energy Lett. 3, 1183–1191 (2018). https://doi.org/10.1021/acsenergylett.8b00303
C. Liu, F. Wang, J. Zhang, K. Wang, Y. Qiu, Q. Liang, Z. Chen, Efficient photoelectrochemical water splitting by g-C3N4/TiO2 nanotube array heterostructures. Nano-Micro Lett. 10, 37 (2018). https://doi.org/10.1007/s40820-018-0192-6
J. Liang, Y. Zheng, J. Chen, J. Liu, D. Hulicova-Jurcakova, M. Jaroniec, S.Z. Qiao, Facile oxygen reduction on a three-dimensionally ordered macroporous graphitic C3N4/carbon composite electrocatalyst. Angew. Chem. Int. Ed. 51, 3892–3896 (2012). https://doi.org/10.1002/anie.201107981
Q. Wang, Y. Lei, Z. Chen, N. Wu, Y. Wang, B. Wang, Y. Wang, Fe/Fe3C@C nanoparticles encapsulated in N-doped graphene-CNTs framework as an efficient bifunctional oxygen electrocatalyst for robust rechargeable Zn-air batteries. J. Mater. Chem. A 6, 516–526 (2018). https://doi.org/10.1039/C7TA08423D
N. Wang, T. Hang, D. Chu, M. Li, Three dimensional hierarchical nanostructured Cu/Ni-Co coating electrode for hydrogen evolution reaction in alkaline media. Nano-Micro Lett. 7, 347–352 (2015). https://doi.org/10.1007/s40820-015-0049-1
Z. Chen, Q. Wang, X. Zhang, Y. Lei, W. Hu, Y. Luo, Y. Wang, N-doped defective carbon with trace Co for efficient rechargeable liquid electrolyte-/all-solid-state Zn-air batteries. Sci. Bull. 63, 548–555 (2018). https://doi.org/10.1016/j.scib.2018.04.003
G. Duan, H. Fang, C. Huang, S. Jiang, H. Hou, Microstructures and mechanical properties of aligned electrospun carbon nanofibers from binary composites of polyacrylonitrile and polyamic acid. J. Mater. Sci. 53, 15096–15106 (2018). https://doi.org/10.1007/s10853-018-2700-y
P. Xiao, Y. Yan, X. Ge, Z. Liu, J.Y. Wang, X. Wang, Investigation of molybdenum carbide nano-rod as an efficient and durable electrocatalyst for hydrogen evolution in acidic and alkaline media. Appl. Catal. B Environ. 154–155, 232–237 (2014). https://doi.org/10.1016/j.apcatb.2014.02.020
Y.J. Tang, M.R. Gao, C.H. Liu, S.L. Li, H.L. Jiang, Y.Q. Lan, M. Han, S.H. Yu, Porous molybdenum-based hybrid catalysts for highly efficient hydrogen evolution. Angew. Chem. Int. Ed. 54, 12928–12932 (2015). https://doi.org/10.1002/anie.201505691
Y. Zhao, K. Kamiya, K. Hashimoto, S. Nakanishi, In situ CO2-emission assisted synthesis of molybdenum carbonitride nanomaterial as hydrogen evolution electrocatalyst. J. Am. Chem. Soc. 137, 110–113 (2014). https://doi.org/10.1021/ja5114529
Y. Liu, G. Yu, G.D. Li, Y. Sun, T. Asefa, W. Chen, X. Zou, Coupling Mo2C with nitrogen-rich nanocarbon leads to efficient hydrogen-evolution electrocatalytic sites. Angew. Chem. Int. Ed. 54, 10752–10757 (2015). https://doi.org/10.1002/anie.201504376
C. Lu, D. Tranca, J. Zhang, F.N. Rodrı́guez Hernández, Y. Su, X. Zhuang, F. Zhang, G. Seifert, X. Feng, Molybdenum carbide-embedded nitrogen-doped porous carbon nanosheets as electrocatalysts for water splitting in alkaline media. ACS Nano 11, 3933–3942 (2017). https://doi.org/10.1021/acsnano.7b00365
W.F. Chen, J.T. Muckerman, E. Fujita, Recent developments in transition metal carbides and nitrides as hydrogen evolution electrocatalysts. Chem. Commun. 49, 8896–8909 (2013). https://doi.org/10.1039/c3cc44076a
C. Tang, W. Wang, A. Sun, C. Qi, D. Zhang, Z. Wu, D. Wang, Sulfur-decorated molybdenum carbide catalysts for enhanced hydrogen evolution. ACS Catal. 5, 6956–6963 (2015). https://doi.org/10.1021/acscatal.5b01803
Acknowledgements
Y. Lei thanks the financial support from Changsha Science and Technology Plan (kq1801065), Hunan Provincial Science and Technology Plan Project (No. 2017TP1001), and State Key Laboratory Fund and the National Key R&D Program of China (2018YFB0704100). Q. Feng acknowledges the NSFC grant (No. 11627901), the Scientific Challenge Project of China (No. TZ2018001), and the visit at the National Joint Engineering Laboratory of Power Grid with Electric Vehicles (Shandong University). The computations are supported by the IMD supercomputing center.
Author information
Authors and Affiliations
Corresponding author
Electronic supplementary material
Below is the link to the electronic supplementary material.
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Lei, C., Zhou, W., Feng, Q. et al. Charge Engineering of Mo2C@Defect-Rich N-Doped Carbon Nanosheets for Efficient Electrocatalytic H2 Evolution. Nano-Micro Lett. 11, 45 (2019). https://doi.org/10.1007/s40820-019-0279-8
Received:
Accepted:
Published:
DOI: https://doi.org/10.1007/s40820-019-0279-8