Highlights
-
A template approach for the synthesis of porous cobalt phosphide nanoarrays (Co2P/CoP NAs) is reported, which exhibits superior electrocatalytic activity and stability toward charge storage and hydrogen evolution.
-
Using Co2P/CoP NAs as a charge mediator, the H2 and O2 evolution of alkaline water electrolysis is separated effectively in time, thereby achieving a membrane-free pathway for H2 purification.
-
Introduction of easily oxidized chemicals to replace water oxidation triggers a low energy consumption path toward H2 purification.
Abstract
Electrochemical reduction of water to hydrogen (H2) offers a promising strategy for production of clean energy, but the design and optimization of electrochemical apparatus present challenges in terms of H2 recovery and energy consumption. Using cobalt phosphide nanoarrays (Co2P/CoP NAs) as a charge mediator, we effectively separated the H2 and O2 evolution of alkaline water electrolysis in time, thereby achieving a membrane-free pathway for H2 purification. The hierarchical array structure and synergistic optimization of the electronic configuration of metallic Co2P and metalloid CoP make the Co2P/CoP NAs high-efficiency bifunctional electrocatalysts for both charge storage and hydrogen evolution. Theoretical investigations revealed that the introduction of Co2P into CoP leads to a moderate hydrogen adsorption free energy and low water dissociation barrier, which are beneficial for boosting HER activity. Meanwhile, Co2P/CoP NAs with high capacitance could maintain a cathodic H2 evolution time of 1500 s at 10 mA cm−2 driven by a low average voltage of 1.38 V. Alternatively, the energy stored in the mediator could be exhausted via coupling with the anodic oxidation of ammonia, whereby only 0.21 V was required to hold the current for 1188 s. This membrane-free architecture demonstrates the potential for developing hydrogen purification technology at low cost.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
1 Introduction
Electrochemical water splitting to produce hydrogen (H2) has been considered to be a sustainable and environmentally friendly energy conversion technology [1,2,3]. Currently, state-of-the-art water electrolyzers are based on proton-exchange membranes (PEMs) that separate H2 production and O2 production, but large-scale practical application remains restricted by their high cost and insufficient durability (Fig. 1a) [4,5,6]. Tremendous efforts have been focused on improvement in water electrolyzer architecture [7,8,9,10]. Unfortunately, design of a cost-effective electrochemical energy recovery apparatus to harvest a high-purity H2 stream for wide application remains a great challenge. Thus, innovative breakthroughs to enable water splitting cells with economical and stable H2 recovery are urgently needed.
Recently, using nickel hydroxide as a solid-state redox mediator, Xia and his coworkers achieved an alternative method to split conventional water electrolysis into two independent steps [11]. The production of O2 and H2 at separate points in time potentially reduces cost by decreasing the stringent demands placed on PEM-based water electrolysis (Fig. 1b). The finding paves the way toward an important pathway for separating H2 and O2 production in water electrolysis. Nevertheless, for the following two reasons, there is still great room for improvement in terms of the performance of the system. Firstly, the anodic reaction for oxygen evolution reaction (OER) in the counterpart cell requires a large overpotential on account of the intrinsically formidable kinetics, resulting in relatively low overall efficiency [12, 13]. Previous works have reported that more easily oxidized chemicals could be used as sacrificial agents for electrochemical oxidation to replace the OER, complementing the advancement of overall energy conversion efficiency during the electrolysis process [14,15,16,17]. Among these energy-saving electrolysis techniques, ammonia (NH3) electrolysis (2NH3 → 3H2 + N2) is attracting extensive attention due to the capability of simultaneous H2 production and ammonia-rich wastewater purification [18, 19]. Secondly, the charge storage capacity needed for the redox mediator was underestimated, and the H2 evolution period in the cathodic cell was thus not long enough, which complicated the operating conditions.
This issue motivates us to seek out a high-capacity redox system that could persistently and efficiently mediate the ion exchange between anode and cathode during the gas evolution process. In view of their high power density, fast charge–discharge rate and long cycling life, pseudocapacitors as electrochemical energy storage media have great application as mediators for decoupling water electrolysis [20, 21]. Besides, the alkaline hydrogen evolution reaction (HER), which involves the dissociation of water molecules with the generation of H* (H2O + e− = H* + OH−), has a high activation barrier due to the sluggish reaction kinetics [22, 23]. Thus, the development of dual functional catalysts that exhibit highly efficient HER and superior capacity is of key interest and a significant innovation.
Transition metal phosphides (TMPs), with high thermal stability and a broad array of chemical structures, have been identified as potential catalysts for electrocatalysis and energy storage [24, 25]. Specifically, modderite structure CoP, with a stable orthorhombic crystal structure (space group: Pnma) where Co3+ is bonded to six equivalent P3− atoms to form corner-sharing CoP6 octahedra, possesses high reactivity but inferior electronic conductivity [26, 27]. To solve the problem, it is widely accepted that hybridization with highly conductive species is a feasible strategy to tune the valence electron state, thereby benefiting the electrical conductivity and electrochemical reaction kinetics [28, 29]. Based on the above considerations, we herein successfully developed a doping-assisted approach to obtain metallic Co2P/metalloid CoP nanoarrays (denoted as Co2P/CoP NAs) as bifunctional electrocatalysts for charge storage and hydrogen generation. Hierarchical array structures were designed with increased surface area to facilitate diffusion of electrolyte into the electrode during the electrocatalytic process. The as-prepared Co2P/CoP NAs electrode could deliver a large specific areal capacitance of 10.52 F cm−2 and low HER overpotential of 40 mV at a current density of 10 mA cm−2 in an alkaline electrolyte. Theoretical calculations were carried out to better understand the effect of Co2P incorporation on the enhancement of electrocatalytic activity. In the water electrolyzer, the high capacitance of the Co2P/CoP NAs mediator supported persistent H2 separation, where the H2 production period lasted for 1500 s at a current density of 10 mA cm−2, almost 3.1 times longer than that for pure CoP (480 s). Alternatively, the energy stored in the mediator could be exhausted via coupling with the oxidation of ammonia, with NiSe as the anode (Fig. 1c). The shortened oxidation path at the anode was responsible for enhanced charge transfer, whereby a total driving voltage of 1.55 V was required to support a current density of 10 mA cm−2 in the ammonia-containing solution, ~ 0.14 V lower than that under alkaline conditions.
2 Experimental Section
2.1 Reagents and Materials
Cobalt acetate tetrahydrate (Co(CH3COO)2·4H2O), ammonium fluoride (NH4F), urea (CO(NH2)2), selenium (Se) and dimethylformamide (C3H7NO) were purchased from Sinopharm Chemical Reagents Beijing Co., Ltd (China). Zinc nitrate hexahydrate (Zn(NO3)2·6H2O), sodium hypophosphite monohydrate (NaH2PO2·H2O), potassium hydroxide (KOH) were purchased from Sigma-Aldrich. Milli-Q ultrapure water was used for all experiments. All of the reagents were analytical grade and used without further purification.
2.2 Synthesis of Zn–Co Hydroxide Nanoarrays
Cobalt foam (CF) was cleaned in acetone (15 min), 0.1 M hydrochloric acid (15 min) and ethanol (15 min) by sequential ultrasonication. Zn–Co hydroxide arrays were prepared on CFs via a hydrothermal method. 4 mmol Zn(NO3)2·6H2O and Co(CH3COO)2·4H2O with molar ratio of 1:2 were dissolved in 40 mL of distilled water at room temperature. Then, 8 mmol of NH4F and 10 mmol of CO(NH2)2 were added into the mixture under vigorous stirring to form a clear solution. After immersing the cleaned CF (1 × 4 cm2) in the homogeneous solution, the autoclave was sealed and maintained at 100 °C for 6 h and then cooled down to room temperature naturally.
2.3 Phosphorization of Zn–Co Hydroxide Nanoarrays
The Zn–Co hydroxide nanoarray-loaded electrode and NaH2PO2 were located in different positions in a quartz boat, with NaH2PO2 at the upstream side of the furnace. Subsequently, the sample was heated to 400 °C at a ramp rate of 10 °C min−1 and maintained for 120 min in an Ar atmosphere. The furnace was naturally cooled down to room temperature under Ar atmosphere.
2.4 Acid Etching of Phosphorized Zn–Co Nanoarrays
The phosphorized Zn–Co nanoarrays were immersed into a 0.1 M HCl solution and stirred for 6 h. After that, the sample was taken out and washed, which was denoted as Co2P/CoP NAs. For comparison, pure CoP on CF was prepared without the addition of Zn(NO3)2·6H2O.
2.5 Preparation of NiSe Electrode
Nickel foam (NF) was sequentially washed using acetone, 2.0 M HCl, and a mixture of deionized water and absolute ethanol for 10 min under ultrasonication, respectively. After that, 2.5 mmol Se, 7.5 mmol NaOH, 0.14 mL hydrazine and 25 mL dimethylformamide (DMF) were dissolved in 40 mL deionized water under vigorous stirring. The NF was immersed in the solution and transferred into a 50-mL Teflon-lined stainless steel autoclave at 180 °C for 1 h. The as-obtained NiSe/NF was washed with deionized water several times.
2.6 Structural Characterization
The crystal structure of the samples was characterized by powder X-ray diffraction (XRD) (PANalytical Inc.) using Cu Kα radiation with a fixed slit. The morphology and information on the lattice spacing of the materials were obtained using a field emission scanning electron microscope (FE-SEM, Hitachi, Japan) and high-resolution transmission electron microscope (HRTEM) equipped with an X-ray energy-dispersive spectrometer (EDS) (JEM-2100F, JEOL, Japan). X-ray photoelectron spectroscopy (XPS) analyses were carried out with a PHI5000 Versa Probe system. All the spectra were referenced to the C 1 s binding energy (BE) of 284.8 eV. The specific surface area was measured by N2 adsorption–desorption isotherms at 77 K using the Brunauer–Emmett–Teller (BET, ASAP2460, Micromeritics) method. Raman spectra were obtained using a confocal Raman microscope (Renishaw, England). In situ X-ray absorption spectra (XAS) at the Co K-edge were recorded at beam line BL14W1 of Shanghai Synchrotron Radiation Facility (SSRF), China.
2.7 Electrochemical Characterization
Electrochemical measurements were carried out with an electrochemical workstation (Gamry) using a standard three-electrode setup in 1.0 M KOH electrolytes. The as-synthesized catalytic electrodes were used as working electrodes and a graphite rod and Ag/AgCl as counter electrode and reference electrode, respectively. The electrochemical profiles of electrodes were investigated using linear sweep voltammetry (LSV), cyclic voltammetry (CV) and galvanostatic charge–discharge measurements, respectively. All potentials were quoted with respect to the reversible hydrogen electrode (RHE) according to equation: ERHE = EAg/AgCl + 0.059 × pH + 0.2. Unless specifically noted, all of the potentials are given without iR compensation. Cyclic voltammetry (CV) measurements were applied to probe the electrochemical double-layer capacitance (Cdl) in the non-Faradaic region for estimating the effective electrochemical surface area (ECSA). Electrochemical impedance spectroscopy (EIS) measurements were carried out using this apparatus over a frequency range of 100 kHz to 0.01 Hz with AC amplitude of 5 mV. The areal capacitance C (F cm−2) of the electrode can be calculated from the galvanostatic charge–discharge curves based on the following equation: C = (I × ∆t)/(A × ∆V), where I is the discharge current (A), Δt is the discharge time (s), A is the area of electrode (cm2) and ΔV is potential change during discharge (V).
2.8 Water Electrolysis Investigation
A water electrolysis system was constructed with NiSe/NF, Co2P/CoP NAs and a Co-based mediator electrode as the anode, cathode and mediator, respectively. Water electrolysis was investigated using chronopotentiometry measurements with applied currents of 10 and 20 mA cm−2. Step 1 was performed in 1.0 M KOH electrolyte, where the HER electrode and Co2P/CoP NAs electrode were connected to the cathode and anode of a DC power supply. Step 2 was started after finishing the charging process of the redox mediator. In Step 2, the high-valent cobalt electrode and NiSe/NF electrode were connected to the cathode and anode of the DC power supply for electrolysis. Step 2 automatically stopped when the discharge of the Co-based electrode finished. Cell voltages (voltage vs. time) of Steps 1 and 2 were recorded to characterize the electrolysis profile. With the use of an additional Ag/AgCl reference electrode, the chronopotentiometry data (potential vs. time) of the Co-based mediator electrode were recorded in Steps 1 and 2.
2.9 Density Functional Theory Calculation
The CoP (111) and CoP(111)/Co2P(111) interface were built, and the vacuum space along the z direction was set to be 15 Å, which is enough to avoid interaction between two neighboring images. H, H2O and H–OH groups were absorbed on the surface of these materials. First principles calculations were carried out in the framework of density functional theory, including structural and electronic aspects, based on the Cambridge Sequential Total Energy Package known as CASTEP [30]. The exchange–correlation functional under the generalized gradient approximation (GGA) with norm-conserving pseudopotentials and Perdew–Burke–Ernzerhof functional were adopted to describe the electron–electron interaction [31]. An energy cutoff of 750 eV was used, and a k-point sampling set of 5 × 5 × 1 was tested to convergence. A force tolerance of 0.01 eV Å−1, energy tolerance of 5.0 × 10−7eV per atom and maximum displacement of 5.0 × 10−4 Å were considered. Each atom in the storage models was allowed to relax to the minimum enthalpy without any constraints. The transition state of the H2O → H–OH process was calculated. Additionally, the complete linear synchronous transit (LST)/quadratic synchronous transit (QST) search protocol was used, and the root mean square (RMS) convergence of 0.05 eV Å was set for transition states (TS). The adsorption energy ΔE of A groups on the surface of substrates was defined as: ΔE = E*A − (E* + EA), where *A and * denote the adsorption of A groups on substrates and the bare substrates and EA denotes the energy of A groups. The free energy change ΔG of the reaction was calculated as the difference between the free energies of the initial and final states as shown below: ΔG = ΔE + ΔZPE − TΔS, where E is the energy calculated by DFT, ZPE is the zero point energy and S denotes the entropy.
3 Results and Discussion
3.1 Synthesis and Characterization of Co2P/CoP NAs
Figure 1d shows the fabrication procedure of Co2P/CoP NAs on Co foam (CF). By using a bottom-up hydrothermal process, a Zn–Co hydroxide arrayed structure was first synthesized on macroporous CF (Fig. S1). Briefly, Zn2+ with lower solubility preferentially precipitated in solution compared with Co hydroxide [32, 33]. Thus, in the competitive co-precipitation process, Zn hydroxides were first formed as the “trunk” on the CF. As the Zn2+ concentration decreased, Co hydroxide nanosheets successively precipitated on the Zn-rich trunks, resulting in a Zn–Co hierarchical structure (Fig. S2a). After phosphorization, the Zn–Co hydroxide was transformed into phosphide, while the arrayed structure was well preserved (Fig. S2b). The hierarchical Co2P/CoP NAs could be finally achieved by an etching approach using 0.1 M HCl solution.
The crystal structures of the as-prepared products were subsequently investigated by XRD. In the absence of zinc, the orthorhombic crystal structure of CoP was well indexed to a reference XRD pattern (ICDD PDF: 65-1474), whereas mixed crystals were achieved with Zn addition, exhibiting orthorhombic CoP and Co2P structures (ICDD PDF: 65-2381) (Fig. 2a). As shown by SEM in Fig. 2b, c, the hierarchical Co2P/CoP NAs were composed of numerous fuzzy flakes, which was in sharp contrast to the irregular morphology observed in the absence of Zn2+ (Fig. S3a, b). A two-dimensional nanoflake morphology with a thickness of several layers, which was beneficial for the exposure of catalytically active sites, was further confirmed by TEM images (Fig. 2d). Meanwhile, EDX elemental mapping revealed that Co and P were homogeneously distributed on the surface of the nanosheets (Fig. 2e). In good agreement with the XRD analysis, the high-resolution TEM (HRTEM) image showed that the Co2P phase was well preserved in the CoP nanosheets (Fig. 2f). The lattice spacing of 0.247 nm was assigned to the (111) plane of orthorhombic CoP, while lattice distances of 0.208 and 0.220 nm corresponded to the (211) and (201) planes of Co2P, respectively. Analogously, the pure CoP exhibited the crystal phase of CoP under HRTEM observation (Fig. S3c–e). Additionally, the Brunauer–Emmett–Teller (BET) surface area of porous Co2P/CoP NAs (20.25 m2 g−1) was 4 times higher than that for CoP (5.4 m2 g−1) (Fig. S4). To probe the formation mechanism of the Co2P/CoP structure, various Zn amount and annealing temperatures were investigated. As shown in Fig. S5, the Co2P phase could be observed in the presence of Zn and the corresponding peaks became narrow and sharp with the increase in the amount of Zn. Notably, only CoP could be synthesized under 300 °C pyrolysis conditions in the presence of Zn (Fig. S6). The control of the amount of Zn and the annealing temperature suggested the critical roles of Zn content and phosphorization temperature in adjusting the Co2P/CoP hierarchical structure (Figs. S5, S6). XPS measurements were employed to probe the surface chemistry of the fabricated phosphides. The XPS survey scan spectrum of Co2P/CoP NAs implied the presence of Zn, Co and P elements (Fig. S7). In the high-resolution Co 2p region, the peak area at the position of 779.0 eV assigned to Co 2p3/2 was rapidly decreased after incorporation of Co2P, suggesting the increased electron density of partial positively charged Co species (Coδ+) in the mixed crystal phase (Fig. 2g) [34]. It was noted that the incorporation of Co2P led to a shift of Coδ+ to higher energy levels by 0.3 eV and a negative shift of P 2p3/2 by 0.2 eV, indicating strong electronic interactions between Co and P (Figs. 2g and S7c) [35].
3.2 Investigation of Electrochemical Charge Storage and HER Activities
The capacitive behavior of the hierarchical Co2P/CoP NAs material was investigated in a three-electrode cell using cyclic voltammetry (CV) measurements. Figure 3a presents the typical CV curves of as-prepared catalysts in 1.0 M KOH electrolyte at different scan rates between 0.5 and 1.6 V versus RHE. A redox peak can be clearly observed from the CV curves of the Co-based materials, which is ascribed to the reversible Faradaic process of interconversion of Co(II)/Co(III) and Co(III)/Co(IV) couples. The similarity of the Co 2p spectrum with that of standard Co3O4 and the disappearance of metal phosphide after long-term tests suggested the oxidization of Co atoms to form CoOx species (Fig. S8a, b). The oxidation phenomenon was also revealed by the increased O amount, probably implying that the essential active sites of Co2P/CoP NAs for the electrochemical energy storage were metal oxide/hydroxides formed on the surface (Fig. S8c, d). For Co2P/CoP electrode materials, surface Faradaic reactions could thus be proposed in alkaline medium as follows [36, 37]:
Meanwhile, symmetric peaks can be observed for both anodic and cathodic currents, implying the reversibility of the Co2P/CoP-loaded electrode. However, due to the internal resistance, the anodic and cathodic peaks shifted with increasing scan rate. The CV curves of Co foam demonstrated that the current was much lower than that for the Co2P/CoP NAs-loaded electrode, indicating that capacitive effects arising from the Co foam substrate can be neglected (Fig. 3a). The CV curve of the Co2P/CoP NAs exhibited remarkably higher current in comparison with pure CoP, suggesting that the incorporation of Co2P could enhance the charge storage capacity (Fig. 3a).
To further estimate the stable potential window of the as-synthesized catalysts, galvanostatic charging and discharging of the samples were performed in 1 M KOH solution using a saturated Ag/AgCl reference electrode and a graphite rod counter electrode. Figure 3b depicts the charge–discharge curves of Co2P/CoP NAs at different current densities (5–50 mA cm−2) in the range of − 0.2 and 0.4 V versus Ag/AgCl. In agreement with the CV results, the lack of defined voltage plateaus in the charge/discharge curves suggested the presence of pseudo-capacitive behavior. The areal capacitance of the Co2P/CoP NAs electrode slowly decreased as current density increased from 5 to 50 mA cm−2. The discharge time for Co2P/CoP NAs reached 2,000 s at a current density of 5 mA cm−2, resulting in a high areal capacitance of 12.95 F cm−2, ~ 4.5 times higher than that for the pure CoP-loaded electrode (2.86 F cm−2) (Fig. S9a). The Co2P/CoP NAs electrode also exhibited excellent rate capability performance, with 61% capacitance retained at the high current density of 50 mA cm−2 (7.9 F cm−2) in comparison with 5 mA cm−2 (Fig. S9b). The capacitive performance of the Co2P/CoP NAs regulated by the Zn content, and annealing temperature was also evaluated and is shown in Fig. S10. As expected, the sample obtained with the molar ratio of Co to Zn (2 to 1) and annealing temperature of 400 °C possessed the optimal capacitance activity. The extremely low amount of Zn identified by EDX spectroscopy, and inductively coupled plasma mass spectrometry (ICP–MS) suggested its insufficiency to alter the capacitance activity (Fig. S11). To provide further insights into the superior charge storage, the physical origins of the electrode kinetics were further examined via electrochemical impedance spectroscopy (EIS). A small semicircle in the high-frequency region reflects low charge transfer resistance [38, 39]. The Co2P/CoP NAs electrode exhibits a smaller semicircle diameter than that of pure CoP, suggesting that the introduction of Co2P could lower charge transfer resistance and accelerate electron transport across the interface between Co2P/CoP NAs and electrolytes (Fig. 3c). The synergistic effect between Co2P and CoP, where the CoP is responsible for high reactivity while Co2P accounts for electronic conductivity, as well as the porous arrayed structure that benefits the high diffusivity of ions in the electrolyte, could play a vital role in boosting the charge storage.
To construct an electrolyzer for electrocatalytic H2 evolution, an active HER catalyst was simultaneously needed. Fortunately, the developed Co2P/CoP NAs also exhibited the highest catalytic activity toward HER, with low overpotential of 160 mV at 100 mA cm−2 and Tafel slope of 57 mV dec−1 (Figs. 3d and S12). The electrocatalytic performance of Co2P/CoP NAs is comparable to those of other highly efficient HER electrocatalysts reported recently (Table S1). To reach the same current density, an overpotential of 296 mV was needed for the pure CoP electrode. In the meantime, the HER polarization curves of the Co-based sample obtained with the addition of chemicals were at similar levels to that obtained in basic conditions, indicating the presence of robust catalytic activity under different conditions. We next investigated the effect of the electrochemically active surface area (ECSA) on HER performance, which was estimated by measuring the electrochemical double-layer capacitance (Cdl). The Cdl value of Co2P/CoP NAs was evaluated by CVs to be 8.1 mF cm−2, which is larger than that of CoP (3.7 mF cm−2), demonstrating the greater exposure of catalytically active sites (Fig. S13). The EIS results suggested superior charge transfer performance between the surface of the Co2P/CoP NAs electrode and the electrolyte (Fig. S14). The long-term stability of the electrode was also investigated at current densities of 10 and 20 mA cm−2 (Fig. S15a). The Co2P/CoP NAs electrode retained steady activity, and no noticeable overpotential augment was observed after more than 28 h of H2 release. Moreover, the LSV curve recorded after 2000 cycles almost overlapped the initial one (Fig. S15b). After durability tests, the electrode was subjected to post-characterizations to investigate the changes in the morphology and chemical structure of the Co2P/CoP NAs electrocatalyst. The electronic patterns directly show that the structure of vertically aligned nanorod arrays and the clear lattice spacing were well maintained after the HER stability test (Fig. S16d–f). Meanwhile, XRD and XPS results demonstrated that the crystal structure and chemical composition remain nearly unchanged after HER, exhibiting the structural robustness of the catalysts (Fig. S16a–c).
To understand the origin of the high HER activity of Co2P/CoP NAs, theoretical investigations were conducted based on DFT calculations. Figure S17 exhibits the schematic models of the matched Co2P(111)/CoP(111) heterostructure and pure CoP(111), respectively. The H2O molecule has a lower adsorption energy of − 1.76 eV on Co2P(111)/CoP(111) than that on CoP(111) (− 1.68 eV), indicating more favorable H2O adsorption for Co2P(111)/CoP(111) (Fig. S18). Importantly, the water dissociation on Co2P(111)/CoP(111) experiences a quite low barrier of 0.57 eV, more promising than that on CoP(111) (1.29 eV), which is even comparable to that of the Pt (111) (0.563 eV) (Fig. 3e) [40]. Meanwhile, the lower absolute values of ΔGH* enable a suitable H* adsorption strength [41]. Figure 3f presents that the CoP (111) surface has a ΔGH* value of − 0.28 eV on the Co site. After the incorporation of Co2P, the ΔGH* increased to − 0.12 eV on the Co–Co bridge site, which is more thermo-neutral than that of pure CoP and close to that of the Pt (111) (− 0.08 eV) (Figs. 3f and S19) [40, 42]. Additionally, a reduced valance charge for Co near the Co2P(111)/CoP(111) interface can be clearly observed, consistent with the above XPS results, which is beneficial for hydrogen desorption from Co sites (Co2P(111)/CoP(111)) (Fig. S20 and Table S2). From the above analysis, it was deduced that the Co sites near Co2P/CoP interfaces served as the actual active sites for HER.
3.3 Performance of the Two-Step Alkaline Water Electrolysis
In the meantime, a NiII → NiIV earth-abundant catalyst was applied as the catalyst for the anodic reaction, aiming for a low bias voltage to achieve high H2 production efficiency. Based on the combined results of XRD, TEM-EDS, and XPS analysis, nickel selenide (NiSe) was shown to form a good coating on the Ni foam (NF) (Fig. S21). As observed from the polarization curve, the NiSe/NF electrode can support a current density of 50 mA cm−2 at a potential of 1.65 V for OER (Fig. S22). For better implementation, a batch-type reactor for decoupling the conventional water electrolytic process was constructed using NiSe electrodes as anode, Co2P/CoP NAs-loaded electrodes as cathode and Co-based electrodes as redox mediator. Water electrolysis in the cell was investigated by chronopotentiometry measurements with a current density of 10 mA cm−2. As depicted in Fig. 4a, the chronopotentiometry data of the anode (anodic potential vs. time) and cathode (cathodic potential vs. time) were investigated during the electrolysis process using pure CoP as the redox mediator. Two steps (Steps 1 and 2) with different cell voltages were involved in the electrolysis process. In the hydrogen cell (Step 1), HER occurs at the cathode, and OH− ions are consumed by the mediator, transforming Co(II) to Co(IV). Step 1 exhibits a cell voltage of ~ 1.45 V, which is derived from the difference between the anodic potential of Co oxidation and cathodic potential of H2O reduction (Fig. S23a). In the oxygen cell (Step 2), OER occurs at the anode, while the NiSe/NF electrode interacts with OH− to evolve O2, and the cathodic reaction synchronously occurring in the counter compartment involves reduction of Co(IV) to Co(II), thus accomplishing the whole regeneration cycle. In the O2-production process, the cell voltage is ~ 0.25 V, which is calculated from the potential difference between the anodic oxidation of OH− and the cathodic reduction of Co(IV) to Co(II) (Fig. S23a). In this configuration, the cell voltage for step 1 markedly increases after 480 s, suggesting that Co(II) has been completely converted to Co(IV). Subsequently, the electrolysis in step 2 was automatically completed after 357 s.
It should be noted that the hierarchical Co2P/CoP NAs material, as a well-engineered electrode, exhibited much higher energy storage efficiency and longer cycle life than pure CoP. These characteristics are of great importance to prolong the electrolysis time in each step. To demonstrate this, a batch-type reactor was reconstructed using the hierarchical Co2P/CoP NAs material as redox mediator. Under a current density of 10 mA cm−2, the H2 production time in this alkaline electrolytic cell could be increased to ~ 1500 s, ~ 3.1 times longer than that using the pure CoP electrode (Fig. 4b). At the same time, an unequal electrolysis time (1290 s) for O2 production was observed in step 2, which resulted from the rapid release of energy storage capacity in the arrayed nanostructure. Photographic profiles of the H2 generation in Step 1 and O2 generation in Step 2 are shown in Fig. S24 to further characterize the separated steps. Moreover, the electrolysis process was also investigated at a current density of 20 mA cm−2. As depicted in Fig. S25, the stable H2 production indicated the flexibility of the system.
3.4 Evaluation of the Two-Step Alkaline Ammonia Electrolysis
Furthermore, the total driving voltage of the two-step alkaline water electrolysis process (Step 1 + Step 2) was calculated according to a previous method [43]. A total driving voltage of 1.69 V could support a current density of 10 mA cm−2 in two-step water electrolysis, which was mainly restricted by the sluggish kinetics of anodic OER (Fig. S23b). The question arises, how to strengthen the charge transfer efficiency at the anode in order to decrease the total driving voltage? It has been revealed that the charge transfer at the anode can be efficiently intensified by substitution of reactions of easily oxidized contaminants for OER. As a typical pollutant present in landfill leachate worldwide, aqueous ammonia nitrogen conversion into nitrogen gas should be an environmentally friendly pathway [44, 45]. Thus, a platform for the anodic conversion of ammonia was herein constructed to decrease the total driving voltage via enhancing the anodic charge transfer.
As shown in Fig. 5a, NiSe exhibited exceptional ammonia conversion performance, with a potential of only 1.52 V required to drive a current density of 100 mA cm−2, much lower than the value of 1.79 V for OER. The multistep chronopotentiometric curve of NiSe demonstrated that the potential of the NiSe-based electrode maintained stability at various current densities, indicating outstanding mass transfer properties and mechanical robustness in the ammonia alkaline electrolyte (inset of Fig. 5a). According to the in situ Raman results, the pair of bands at 481 and 561 cm−1 at potentials above 0.40 V was attributed to Ni–O vibrations in NiOOH, whereas the peak for NiOOH disappeared after the introduction of ammonia (Fig. 5b) [46, 47]. This strongly implied that NiIIIOOH as a reactive species was rapidly consumed in the ammonia oxidation process, whereby anodic charge transfer can be intensified by minimizing the energy consumption required for Ni conversion. The phenomenon could also be revealed by the high-resolution XPS spectra of Ni and Se, and EDX element mapping after long-term activation (Fig. S26). By contrast, Raman results for the Co-based electrodes after reaction indicated that the CoIII = O vibrational mode could be preserved in the two electrolytes (Fig. S27) [48, 49]. Furthermore, Co K-edge peaks obtained by in situ XANES measurements of the Co2P/CoP NAs electrode after applying a potential of 0.45 V versus Ag/AgCl were almost at the same energy in the two electrolytes, implying that the oxidized proportion of Co could be well maintained (Fig. 5c). These results suggested that the ammonia had only a slight effect on the high specific capacity of the electrode. Correspondingly, in the presence of ammonia, similar areal capacitance was observed via comparison of the integrated CV area and calculated charge–discharge curves obtained in basic conditions (Fig. S28). Notably, the Co2P/CoP NAs electrode exhibited weaker oxidation ability toward ammonia in comparison with that of the NiSe electrode (Fig. S29). Thus, the NiSe electrode was chosen as the anode to oxidize ammonia.
After the addition of ammonia to the working chamber, the total driving voltage of the two-step electrolysis cell decreased by 0.14 V under the same current density of 10 mA cm−2 (Fig. S30). The calculated voltage of 1.55 V at 10 mA cm−2 is comparable with that of other landmark reports on redox mediator systems (Table S3). In addition, owing to the negligible effect of ammonia, the vast majority of high-valent Co on the Co2P/CoP NAs surface could be preserved in the separate working step, whereby H2 production time in the ammonia-containing electrolytic cell still maintained a level of ~ 1400 s (Fig. 5d). This electrolytic cell exhibited stable H2 generation for 20 consecutive cycles at the current density of 20 mA cm−2 (Fig. 5e). Furthermore, over 200 consecutive cycles of the Co2P/CoP NAs electrode at 50 mA cm−2 are shown in Fig. S31 to demonstrate the stability of the charge storage.
4 Conclusions
In summary, we report that the bifunctional Co2P/CoP NAs electrode can act as a robust and low-cost charge mediator for decoupled water electrolysis under alkaline conditions. Theoretical calculations demonstrated that the incorporation of Co2P optimizes the hydrogen adsorption free energy and reduces the water dissociation barrier in an alkaline medium, thereby leading to the outstanding HER performance of Co2P/CoP NAs. Importantly, the Co2P/CoP NAs electrode also exhibited superior charge storage capability, which could prolong the H2 evolution time to 1500 s under a current density of 10 mA cm−2. To decrease the energy cost, the energy stored in hierarchical Co2P/CoP NAs was selectively coupled with the oxidation of ammonia with NiSe as anode, whereby only 0.21 V was required to maintain the current for 1188 s. The work demonstrates the design of cobalt phosphide nanoarrays with ultrahigh capacitance for use as a charge reservoir for persistent hydrogen liberation from contaminant decomposition, thereby achieving an economical and environmentally friendly route to acquiring high-purity H2. More importantly, the configuration presented herein may also be applied as a high-performance device for electrocatalytic gas separation in fields including seawater electrolysis or the chlor-alkali process.
References
X. Yu, Z.Y. Yu, X.L. Zhang, Y.R. Zheng, Y. Duan et al., “Superaerophobic” nickel phosphide nanoarray catalyst for efficient hydrogen evolution at ultrahigh current densities. J. Am. Chem. Soc. 141, 7537–7543 (2019). https://doi.org/10.1021/jacs.9b02527
Z. Pu, I.S. Amiinu, R. Cheng, P. Wang, C. Zhang et al., Single-atom catalysts for electrochemical hydrogen evolution reaction: recent advances and future perspectives. Nano-Micro Lett. 12, 21 (2020). https://doi.org/10.1007/s40820-019-0349-y
C.T. Dinh, A. Jain, F.P.G. de Arquer, P. De Luna et al., Multi-site electrocatalysts for hydrogen evolution in neutral media by destabilization of water molecules. Nat. Energy 4, 107–114 (2018). https://doi.org/10.1038/s41560-018-0296-8
S. Deng, K. Zhang, D. Xie, Y. Zhang, Y. Zhang et al., High-index-faceted Ni3S2 branch arrays as bifunctional electrocatalysts for efficient water splitting. Nano-Micro Lett. 11, 12 (2019). https://doi.org/10.1007/s40820-019-0242-8
J. Li, W. Xu, J. Luo, D. Zhou, D. Zhang, L. Wei, P. Xu, D. Yuan, Synthesis of 3D hexagram-like cobalt-manganese sulfides nanosheets grown on nickel foam: a bifunctional electrocatalyst for overall water splitting. Nano-Micro Lett. 10, 6 (2018). https://doi.org/10.1007/s40820-017-0160-6
K. Zeng, D. Zhang, Recent progress in alkaline water electrolysis for hydrogen production and applications. Prog. Energy Combust. Sci. 36, 307–326 (2010). https://doi.org/10.1016/j.pecs.2009.11.002
X. Han, X. Ling, D. Yu, D. Xie, L. Li et al., Atomically dispersed binary Co–Ni sites in nitrogen-doped hollow carbon nanocubes for reversible oxygen reduction and evolution. Adv. Mater. 31, 1905622 (2019). https://doi.org/10.1002/adma.201905622
S. Giancola, M. Zatoń, Á. Reyes-Carmona, M. Dupont, A. Donnadio, S. Cavaliere, J. Rozière, D.J. Jones, Composite short side chain PFSA membranes for PEM water electrolysis. J. Membr. Sci. 570, 69–76 (2019). https://doi.org/10.1016/j.memsci.2018.09.063
X. Han, W. Zhang, X. Ma, C. Zhong, N. Zhao, W. Hu, Y. Deng, Identifying the activation of bimetallic sites in NiCo2S4@g–C3N4–CNT hybrid electrocatalysts for synergistic oxygen reduction and evolution. Adv. Mater. 31, 1808281 (2019). https://doi.org/10.1002/adma.201808281
Z. Kang, G. Yang, J. Mo, Y. Li, S. Yu et al., Novel thin/tunable gas diffusion electrodes with ultra-low catalyst loading for hydrogen evolution reactions in proton exchange membrane electrolyzer cells. Nano Energy 47, 434–441 (2018). https://doi.org/10.1016/j.nanoen.2018.03.015
L. Chen, X. Dong, Y. Wang, Y. Xia, Separating hydrogen and oxygen evolution in alkaline water electrolysis using nickel hydroxide. Nat. Commun. 7, 11741 (2016). https://doi.org/10.1038/ncomms11741
T. Wu, S. Sun, J. Song, S. Xi, Y. Du et al., Iron-facilitated dynamic active-site generation on spinel CoAl2O4 with self-termination of surface reconstruction for water oxidation. Nat. Catal. 2, 763–772 (2019). https://doi.org/10.1038/s41929-019-0325-4
Z. Zhang, X. Li, C. Zhong, N. Zhao, Y. Deng, X. Han, W. Hu, Spontaneous synthesis of silver-nanoparticle-decorated transition-metal hydroxides for enhanced oxygen evolution reaction. Angew. Chem. Int. Ed. 59, 7245–7250 (2020). https://doi.org/10.1002/anie.202001703
Y. Liu, J. Zhang, Y. Li, Q. Qian, Z. Li, Y. Zhu, G. Zhang, Manipulating dehydrogenation kinetics through dual-doping Co3N electrode enables highly efficient hydrazine oxidation assisting self-powered H2 production. Nat. Commun. 11, 1853 (2020). https://doi.org/10.1038/s41467-020-15563-8
K. Zhang, G. Zhang, J. Qu, H. Liu, Intensification of anodic charge transfer by contaminant degradation for efficient H2 production. J. Mater. Chem. A 6, 10297–10303 (2018). https://doi.org/10.1039/C8TA01849A
Y. Li, X. Wei, L. Chen, J. Shi, M. He, Nickel-molybdenum nitride nanoplate electrocatalysts for concurrent electrolytic hydrogen and formate productions. Nat. Commun. 10, 5335 (2019). https://doi.org/10.1038/s41467-019-13375-z
X. Liu, J. He, S. Zhao, Y. Liu, Z. Zhao, J. Luo, G. Hu, X. Sun, Y. Ding, Self-powered H2 production with bifunctional hydrazine as sole consumable. Nat. Commun. 9, 4365 (2018). https://doi.org/10.1038/s41467-018-06815-9
W. Xu, D. Du, R. Lan, J. Humphreys, D.N. Miller, M. Walker, Z. Wu, J.T.S. Irvine, S. Tao, Electrodeposited NiCu bimetal on carbon paper as stable non-noble anode for efficient electrooxidation of ammonia. Appl. Catal. B Environ. 237, 1101–1109 (2018). https://doi.org/10.1016/j.apcatb.2016.11.003
A. Estejab, D.A. Daramola, G.G. Botte, Mathematical model of a parallel plate ammonia electrolyzer for combined wastewater remediation and hydrogen production. Water Res. 77, 133–145 (2015). https://doi.org/10.1016/j.watres.2015.03.013
H. Dotan, A. Landman, S.W. Sheehan, K.D. Malviya, G.E. Shter et al., Decoupled hydrogen and oxygen evolution by a two-step electrochemical-chemical cycle for efficient overall water splitting. Nat. Energy 4, 786–795 (2019). https://doi.org/10.1038/s41560-019-0462-7
Y. Ma, Z. Guo, X. Dong, Y. Wang, Y. Xia, Organic proton-buffer electrode to separate hydrogen and oxygen evolution in acid water electrolysis. Angew. Chem. Int. Ed. 58, 4622–4626 (2019). https://doi.org/10.1002/anie.201814625
J. Wei, M. Zhou, A. Long, Y. Xue, H. Liao, C. Wei, Z.J. Xu, Heterostructured electrocatalysts for hydrogen evolution reaction under alkaline conditions. Nano-Micro Lett. 10, 75 (2018). https://doi.org/10.1007/s40820-018-0229-x
L. Cao, Q. Luo, W. Liu, Y. Lin, X. Liu et al., Identification of single-atom active sites in carbon-based cobalt catalysts during electrocatalytic hydrogen evolution. Nat. Catal. 2, 134–141 (2018). https://doi.org/10.1038/s41929-018-0203-5
Y. Li, Z. Dong, L. Jiao, Multifunctional transition metal-based phosphides in energy-related electrocatalysis. Adv. Energy Mater. 10, 1902104 (2019). https://doi.org/10.1002/aenm.201902104
K.U.D. Calvinho, A.B. Laursen, K.M.K. Yap, T.A. Goetjen, S. Hwang et al., Selective CO2 reduction to C3 and C4 oxyhydrocarbons on nickel phosphides at overpotentials as low as 10 mV. Energy Environ. Sci. 11, 2550–2559 (2018). https://doi.org/10.1039/C8EE00936H
H. Li, Q. Li, P. Wen, T.B. Williams, S. Adhikari et al., Colloidal cobalt phosphide nanocrystals as trifunctional electrocatalysts for overall water splitting powered by a zinc-air battery. Adv. Mater. 30, 1705796 (2018). https://doi.org/10.1002/adma.201705796
X. Liu, W. Li, X. Zhao, Y. Liu, C.W. Nan, L.Z. Fan, Two birds with one stone: metal–organic framework derived micro-/nanostructured Ni2P/Ni hybrids embedded in porous carbon for electrocatalysis and energy storage. Adv. Funct. Mater. 29, 1901510 (2019). https://doi.org/10.1002/adfm.201901510
T. Liu, A. Li, C. Wang, W. Zhou, S. Liu, L. Guo, Interfacial electron transfer of Ni2P–NiP2 polymorphs inducing enhanced electrochemical properties. Adv. Mater. 30, 1803590 (2018). https://doi.org/10.1002/adma.201803590
Z.H. Xue, H. Su, Q.Y. Yu, B. Zhang, H.H. Wang, X.H. Li, J.S. Chen, Janus Co/CoP nanoparticles as efficient Mott–Schottky electrocatalysts for overall water splitting in wide pH range. Adv. Energy Mater. 7, 1602355 (2017). https://doi.org/10.1002/aenm.201602355
M.D. Segall, P.J.D. Lindan, M.J. Probert, C.J. Pickard, P.J. Hasnip, S.J. Clark, M.C. Payne, First-principles simulation: ideas, illustrations and the CASTEP code. J. Phys.: Condens. Matter 14, 2717 (2002). https://doi.org/10.1088/0953-8984/14/11/301
J.P. Perdew, K. Burke, M. Ernzerhof, Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865 (1996). https://doi.org/10.1103/PhysRevLett.77.3865
K. Zhang, G. Zhang, J. Qu, H. Liu, Zinc substitution-induced subtle lattice distortion mediates the active center of cobalt diselenide electrocatalysts for enhanced oxygen evolution. Small 16, 1907001 (2020). https://doi.org/10.1002/smll.201907001
X. Liu, Z. Chang, L. Luo, T. Xu, X. Lei, J. Liu, X. Sun, Hierarchical ZnxCo3−xO4 nanoarrays with high activity for electrocatalytic oxygen evolution. Chem. Mater. 26, 1889–1895 (2014). https://doi.org/10.1021/cm4040903
W. Gao, M. Yan, H.Y. Cheung, Z. Xia, X. Zhou et al., Modulating electronic structure of CoP electrocatalysts towards enhanced hydrogen evolution by Ce chemical doping in both acidic and basic media. Nano Energy 38, 290–296 (2017). https://doi.org/10.1016/j.nanoen.2017.06.002
L. Zhou, M. Shao, J. Li, S. Jiang, M. Wei, X. Duan, Two-dimensional ultrathin arrays of CoP: electronic modulation toward high performance overall water splitting. Nano Energy 41, 583–590 (2017). https://doi.org/10.1016/j.nanoen.2017.10.009
J. Wen, B. Xu, J. Zhou, Toward flexible and wearable embroidered supercapacitors from cobalt phosphides-decorated conductive fibers. Nano-Micro Lett. 11, 89 (2019). https://doi.org/10.1007/s40820-019-0321-x
H. Liang, C. Xia, Q. Jiang, A.N. Gandi, U. Schwingenschlögl, H.N. Alshareef, Low temperature synthesis of ternary metal phosphides using plasma for asymmetric supercapacitors. Nano Energy 35, 331–340 (2017). https://doi.org/10.1016/j.nanoen.2017.04.007
F. Ning, M. Shao, C. Zhang, S. Xu, M. Wei, X. Duan, Co3O4@layered double hydroxide core/shell hierarchical nanowire arrays for enhanced supercapacitance performance. Nano Energy 7, 134–142 (2014). https://doi.org/10.1016/j.nanoen.2014.05.002
T. Liu, L. Zhang, W. You, J. Yu, Core–shell nitrogen-doped carbon hollow spheres/Co3O4 nanosheets as advanced electrode for high-performance supercapacitor. Small 14, 1702407 (2018). https://doi.org/10.1002/smll.201702407
K. Jiang, B. Liu, M. Luo, S. Ning, M. Peng et al., Single platinum atoms embedded in nanoporous cobalt selenide as electrocatalyst for accelerating hydrogen evolution reaction. Nat. Commun. 10, 1743 (2019). https://doi.org/10.1038/s41467-019-09765-y
J. Yang, A.R. Mohmad, Y. Wang, R. Fullon, X. Song et al., Ultrahigh-current-density niobium disulfide catalysts for hydrogen evolution. Nat. Mater. 18, 1309–1314 (2019). https://doi.org/10.1038/s41563-019-0463-8
J. Zhang, Y. Zhao, X. Guo, C. Chen, C.L. Dong et al., Single platinum atoms immobilized on an MXene as an efficient catalyst for the hydrogen evolution reaction. Nat. Catal. 1, 985–992 (2018). https://doi.org/10.1038/s41929-018-0195-1
M. Hou, L. Chen, Z. Guo, X. Dong, Y. Wang, Y. Xia, A clean and membrane-free chlor-alkali process with decoupled Cl2 and H2/NaOH production. Nat. Commun. 9, 438 (2018). https://doi.org/10.1038/s41467-018-02877-x
A. Valera-Medina, H. Xiao, M. Owen-Jones, W.I.F. David, P.J. Bowen, Ammonia for power. Prog. Energy Combust. Sci. 69, 63–102 (2018). https://doi.org/10.1016/j.pecs.2018.07.001
D.R. MacFarlane, P.V. Cherepanov, J. Choi, B.H.R. Suryanto, R.Y. Hodgetts, J.M. Bakker, F.M. FerreroVallana, A.N. Simonov, A roadmap to the ammonia economy. Joule 4, 1–20 (2020). https://doi.org/10.1016/j.joule.2020.04.004
X. Liu, K. Ni, B. Wen, R. Guo, C. Niu et al., Deep reconstruction of nickel-based precatalysts for water oxidation catalysis. ACS Energy Lett. 4, 2585–2592 (2019). https://doi.org/10.1021/acsenergylett.9b01922
H. Sun, X. Xu, Z. Yan, X. Chen, F. Cheng, P.S. Weiss, J. Chen, Porous multishelled Ni2P hollow microspheres as an active electrocatalyst for hydrogen and oxygen evolution. Chem. Mater. 29, 8539–8547 (2017). https://doi.org/10.1021/acs.chemmater.7b03627
T. Liu, D. Liu, F. Qu, D. Wang, L. Zhang et al., Enhanced electrocatalysis for energy-efficient hydrogen production over CoP catalyst with nonelectroactive Zn as a promoter. Adv. Energy Mater. 7, 1700020 (2017). https://doi.org/10.1002/aenm.201700020
H.Y. Wang, S.F. Hung, Y.Y. Hsu, L. Zhang, J. Miao, T.S. Chan, Q. Xiong, B. Liu, In situ spectroscopic identification of μ-OO bridging on spinel Co3O4 water oxidation electrocatalyst. J. Phys. Chem. Lett. 7, 4847–4853 (2016). https://doi.org/10.1021/acs.jpclett.6b02147
Acknowledgements
This work was financially supported by the National Natural Science Foundation of China (Nos. 51708543, 51438011 and 51722811) and Water Pollution Control and Treatment National Science and Technology Major Project (Nos. 2017ZX07402001 and 2018ZX07110-007).
Author information
Authors and Affiliations
Corresponding author
Electronic supplementary material
Below is the link to the electronic supplementary material.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Zhang, K., Zhang, G., Ji, Q. et al. Arrayed Cobalt Phosphide Electrocatalyst Achieves Low Energy Consumption and Persistent H2 Liberation from Anodic Chemical Conversion. Nano-Micro Lett. 12, 154 (2020). https://doi.org/10.1007/s40820-020-00486-2
Received:
Accepted:
Published:
DOI: https://doi.org/10.1007/s40820-020-00486-2