Highlights
-
The development of transition metal compounds-carbon hybrid electrodes for high energy/power supercapacitors is summarized.
-
Effects of the conductive carbon skeleton, interfacial engineering, and electronic structure for transition metal compounds-carbon hybrid are discussed.
-
Some perspectives and issues in the future are provided.
Abstract
Due to their rapid power delivery, fast charging, and long cycle life, supercapacitors have become an important energy storage technology recently. However, to meet the continuously increasing demands in the fields of portable electronics, transportation, and future robotic technologies, supercapacitors with higher energy densities without sacrificing high power densities and cycle stabilities are still challenged. Transition metal compounds (TMCs) possessing high theoretical capacitance are always used as electrode materials to improve the energy densities of supercapacitors. However, the power densities and cycle lives of such TMCs-based electrodes are still inferior due to their low intrinsic conductivity and large volume expansion during the charge/discharge process, which greatly impede their large-scale applications. Most recently, the ideal integrating of TMCs and conductive carbon skeletons is considered as an effective solution to solve the above challenges. Herein, we summarize the recent developments of TMCs/carbon hybrid electrodes which exhibit both high energy/power densities from the aspects of structural design strategies, including conductive carbon skeleton, interface engineering, and electronic structure. Furthermore, the remaining challenges and future perspectives are also highlighted so as to provide strategies for the high energy/power TMCs/carbon-based supercapacitors.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
1 Introduction
In recent years, the intense consumption of fossil energy and environmental pollution has brought great challenges to the survival and development of human beings. Therefore, searching for clean and sustainable energy sources has become one of the most important topics [1,2,3,4]. Especially for intermittent energy storage, such as wind energy, tidal energy, and solar energy, new technologies suited for both high energy density and power density are urgently needed [4,5,6]. Electrochemical capacitors commonly refer to as supercapacitors, which offer high power density, superior rate performance, and excellent cycle stability [7], have become a prime candidate for the high power applications that require fast on–off response such as hybrid electric vehicles, grid stabilization systems, forklifts, load cranes, aerospace equipment, and military weapons [6, 8]. Current commercial supercapacitors are mainly based on carbon materials, which store/release electrical charges through the physical adsorption/desorption of charges or electrolyte ions on the electrode surface, also called electrochemical double layer capacitors (EDLCs) [9]. Compared with commercial batteries (> 100 Wh kg−1), the energy densities of EDLCs (less than 10 Wh kg−1) are still low, which have become a great challenge for the large-scale application and further popularization of supercapacitors [10, 11]. To address the issue, the development of alternative electrode materials with higher specific capacitance is extremely urgent.
Transition metal compounds (TMCs), such as metal oxides, hydroxides, sulfides, and phosphides, have attracted great attention due to their high theoretical capacitance [12, 13], abundant sources, and low cost, etc. [14,15,16]. In this case, the studies of TMC-based supercapacitors are rising up due to their obviously enlarged energy densities (approaching 102 Wh kg−1) [3]. The energy storage mechanisms of TMC-based electrodes primarily involve the electron transfer in the process of redox reactions and valence state changes of transition metal ions, indicating that the ion diffusion rate and phase transformation due to the change of valence state are important for electrochemical properties. Such transformation generally leads to the sluggish bulk phase reaction and dramatic volumetric expansion/shrinkage during the energy storage process and finally resulting in the low chemical reaction kinetics and inferior cycle stabilities of TMC-based supercapacitors. Since rapid charge/discharge capability and long cycling stability of minimum 10,000 cycles are key criteria for supercapacitors, the poor electrical conductivity, low power density, unsatisfactory mechanical/electrochemical stability, and some other problems, still limit their prospects of TMCs for large-scaled applications [17].
Due to the superior electric conductivity, large specific surface area, low cost, and structural controllability, carbon materials, such as graphene quantum dots, carbon nanotubes, graphene, porous carbon, etc., have been widely researched for energy storage and conversion [7, 18, 19]. Therefore, combining with various dimensional carbon skeletons can not only improve the intrinsic low conductivity, but also modify the morphology of transition metal crystals, which is beneficial for the enhancement of reaction kinetics, fast charging/discharging rate, and cycling stability of TMCs/carbon composites [20]. Although a large number of studies have been done for TMCs/carbon composites, the physical mixture or simple combination of transition metal derivative particles with carbon skeletons still faces some inevitable challenges, such as huge volume expansion/shrinkage during ultra-long charge/discharge process, or even breaking down of electrochemically active materials from carbon surface due to the vulnerable TMCs/carbon interfaces.
Recently, TMCs with nanoscale dimensions, especially quantum dot morphology, have aroused enormous attention in various applications because of their attractive intrinsic characteristics, such as small size effect, quantum tunneling effect, coulomb blockade effect, and surface effect [21,22,23]. Compared with bulk materials, the combination of nanoscale TMCs and carbon skeletons can provide improved electrochemical performance, which is beneficial for the construction of fast ions transport [24, 25]. In addition to nano-crystallization, the rational modification of TMCs crystals, such as the introduction of lattice defects, heterostructure, metal heteroatoms, etc., can also certainly enhance the redox reaction kinetics through decreasing reaction energy or shortening the ions diffusion paths [16]. However, nanoscale TMCs, which show high surface area/energy and large amounts of surface electrons, unavoidably aggregate during the long-times charge/discharge process. Therefore, how to keep the uniform dispersion and stable presence of nanoscale TMCs is another vital challenge that needs to be urgently solved. The construction of interfacial adhesion between TMCs and carbon skeletons may be an effective strategy to promote the uniform and stable dispersion of nanoscale-TMCs on the carbon surface. While it is crucial to systematically understand the design principles from the aspects of carbon skeletons, TMC’s electronic structure, and interfaces for TMCs/carbon composites, there is a lack of review that dedicates to the up-to-date reports for boosting the power/energy densities and cycling stabilities of TMCs/carbon-based supercapacitors.
Though TMCs/carbon composites have drawn tremendous attention for supercapacitors, the deeper research about the energy storage process and attenuation mechanisms has not yet been clearly understood. In addition, the systematic discussion about the relationship between structural design strategies, high power/energy densities, and fast pseudocapacitive reaction kinetics is critical for the practical and large-scale application of TMCs/carbon hybrid electrodes. In this review, we mainly focus on the latest advances in the field of TMCs/carbon hybrid electrodes for supercapacitors, including the construction of conductive carbon skeletons, modification of TMCs/carbon interface engineering, and regulation of electronic structures of TMCs (Fig. 1). More importantly, we propose the challenges and perspectives of developing such TMCs/carbon composites, along with the possible strategies and research directions in the future.
2 Conductive Carbon Skeletons
The high power densities of TMC-based electrodes are commonly restricted due to their poor intrinsic conductivity and sluggish redox reaction kinetics. To solve these challenges, TMCs are usually composited with carbon skeletons, which can not only construct effective electrons/ions transfer channels, but also sustain the structural stability of the entire electrode. In recent years, carbon skeletons with various dimensions (0, 1, 2, or 3 D) have been successfully designed and introduced into the TMCs composite [23, 26,27,28] (Fig. 2). In this section, we will discuss the application of carbon materials as conductive skeletons in designing and fabricating TMCs/carbon hybrid electrodes from the aspect of carbon structures with different dimensions. Table 1 summarizes the electrochemical performance of TMCs/carbon hybrid electrodes for supercapacitors in recent years.
2.1 0D Carbons (Carbon or Graphene Quantum Dots)
0D carbon materials, such as carbon quantum dots (CQDs) or graphene quantum dots (GQDs), have been diffusely studied in supercapacitors due to their small size effect, quantum tunneling effect, coulomb blockade effect, and surface effect, endowing such carbons with high electrons mobility, huge specific surface area, etc. [26, 46, 47]. In this case, TMCs combined with 0D carbon materials have emerged as promising materials for supercapacitors. For example, the reduced carbon quantum dots (RCQDs) were successfully embedded into the RuO2 nanoparticles (RCQDs/RuO2) through a facile impregnation method (As shown in Fig. 3a) [48]. The hybrid network constructed by RCQDs/RuO2 can provide rapid electronic transport and ionic migration paths. The RCQDs incorporated into the integral structure can effectively prevent the further agglomeration of RuO2 nanoparticles and vastly facilitate the fast ions/electrons transfer during charge–discharge processes (Fig. 3a), and keep the structural stability. As a result, the RCQDs/RuO2 electrode exhibited high specific capacitance (594 F g−1) and superior rate capability (77.4% capacity retention at 50 A g−1 compared to that at 1 A g−1). Moreover, the capacitance of RCQDs/RuO2 remained 96.9% after 5000 cycles at 5 A g−1, which was much higher than the RuO2 electrode (the rate capability and capacity retention of corresponding was only 58.3% and 73.9%, respectively).
GQDs were also introduced into the MnO2 nanoparticles (GQDs/MnO2) through the hydrothermal and plasma-enhanced chemical vapor deposition process [32]. By controlling the deposition time, a series of GQDs/MnO2 composites were obtained, and the GQDs (the size of 2–3 nm) were well dispersed on the surfaces of MnO2 sheets. Benefiting from the high conductivity and rich active sites of GQDs (Fig. 3b), the maximum specific capacitance of GQDs/MnO2-3 (3 represents the mass ratio of MnO2/GQDs) can reach to 1170 F g−1 at 5 mV s−1 and excellent cycle performance can be achieved (92.7% retention after 10,000 cycles). More importantly, as demonstrated in asymmetric supercapacitors (ASCs) using GQDs/MnO2-3 and nitrogen-doped graphene as anode and cathode, respectively, the superior energy density of 79 Wh kg−1 at an ultrahigh power density of 12,351 W kg−1 can be obtained in an aqueous electrolyte with ultrawide voltage window (2.3 V). In addition, the GQDs embed to V2O5 interlayer, constructing VNS-GQDs positive electrode composite material was recently reported by Ganganboina and co-workers via a solvothermal treatment process [33]. Due to the high conductivity of graphene quantum dots, the VNS-GQDs exhibited an ultra-high specific capacitance of 572 F g−1 at 1 A g−1, which could keep 92% retention after 10,000 charge–discharge cycles, much higher than that of VNS (227 F g−1). Due to the synergistic effect of GQDs and VNS nanosheets, the assembled asymmetric device (VNS-GQDs//MCS) demonstrated a superior energy density of 20.62 Wh kg−1 at the superhigh power density of 14.86 kW kg−1.
In addition to the metal oxides, other transition metal derivatives, such as metal hydroxides/sulfides, can also be decorated by GQDs. For example, the CQDs/Ni(OH)2 with a lamellar structure was prepared by Wei and co-workers through a facile hydrothermal method [31]. The introduction of CQDs greatly improved the rate performance and specific capacitance of the overall electrode. As a result, the CQDs/Ni(OH)2 electrode exhibited a high specific capacitance of 2900 F g−1 at 1 A g−1, and the capacitance still remained at 2051 F g−1 even at a high current density of 10 A g−1. Furthermore, Huang et al. fabricated GQDs/NiCo2S4 composite that GQDs decorated hierarchical-like hollow NiCo2S4 nanostructures by simple two-step hydrothermal reactions [49]. The introduction of the GQDs can change the surface morphology and internal structure of NiCo2S4 nanowires, indicating the unique nanostructures result in low impedance, large specific surface area, and more redox active sites, more interspaces and pathways for ion diffusion. As a result, the prepared GQDs/NiCo2S4 electrode exhibited high specific capacitance (678.22 F g−1 at 0.2 A g−1) and superior cycling stability (94% retention after 5000 cycles).
The greatly improved electrochemical performance of the 0D carbons decorated TMCs electrode could be attributed to two reasons: (1) the CQDs or GQDs incorporated in the composite can provide additional capacitance and construct highly conductive networks inside the micro-nano-scaled regions, which promotes the rapid charge transport and ionic diffusion, boosts the fast redox reactions, ensuring the excellent rate performance; (2) a small number of oxygen-containing functional groups (mainly carboxyl) at the edges of CQDs or GQDs can form strong and stable chemical interactions between the 0D carbon and TMCs through the formation of C–O–M covalent bonds (M represents metal atoms), which is beneficial for improving the rate and cycling performance. However, though the 0D carbons generally have been used to enhance some pseudocapacitive materials conductivity, the relative lower specific capacitance and easy agglomeration of such carbons still need to be solved.
2.2 1D Carbons (Nanotubes or Nanofibers)
Owing to the high conductivity, good flexibility, and superior functionality, 1D carbon materials, such as carbon nanofibers (CNF) and carbon nanotubes (CNTs), have been widely used as individual electrode materials or conductive substrates for supercapacitors [50, 51]. In the process, the TMCs are commonly in situ introduced into the surface of 1D CNTs through physical or chemical methods. Such a strategy can not only effectively control the morphology of TMCs, but also greatly improve the overall electrical conductivity of 1D TMCs/carbon composites, which is beneficial for the improvement of both power and energy densities. For example, the Ni(OH)2 could be irreversibly transformed into NiOx during the energy storage process and commonly resulted in the poor rate capability and cycle stability of such hydroxide. To address the issue, Tang et al. [35] have prepared the Ni(OH)2/CNTs/NF electrode through the CVD and chemical bath deposition (CBD) process. After the introduction of high conductivity CNTs, the intrinsic drawbacks of Ni(OH)2 could be effectively exempted. The electrochemical testing showed that the Ni(OH)2/CNTs/NF electrode exhibited both high rate capacity (3300 F g−1 at 0.5 A g−1, 2211 F g−1 at 10 A g−1) and excellent cycling stability (87% retention after 3000 cycles). In addition, when assembled as asymmetric supercapacitors using Ni(OH)2/CNTs/NF and AC as anode and cathode, respectively, the device indicated an ultra-high energy density of 32.5 Wh kg−1 at a power density of 1800 W kg−1. Such an obvious improvement can be attributed to the elaborate design of a composite structure, in which the active Ni(OH)2 nanoparticles are effectively anchored on the surface of highly conductive CNTs/NF current collectors and dramatically impeded the phase transformation of Ni(OH)2.
Besides the 1D carbon skeleton surface, the TMCs can also be confined into the cavities of carbon nanofibers [52]. The interspace provided by the 1D carbon skeleton can effectively prevent the aggregation and phase transformation of TMC-based electrodes. For example, the P-doped Co3O4 ultrafine nanoparticles have been successfully encapsulated into P, N co-doped carbon nanowires (P-Co3O4@P, N–C) by a pyrolysis-oxidation-phosphorization method [53]. Because of the strong fastened effect of electroactive Co3O4 into the conductive carbon substrate, the agglomeration of active materials was prevented. Moreover, the good keeping of 1D oriented arrangement hybrid composites can provide a huge accessible surface area and hierarchically porous characteristic, which are beneficial for the sufficient permeation and migration of electrolyte ions. When assembled with Co@P/N–C, the P-Co3O4@P/N–C//Co@P/N–C asymmetric supercapacitor could achieve an outstanding energy density of 47.6 Wh kg−1 at the high power density of 750 W kg−1, indicating the impressive supercapacitor possessing an enormous potential in the practical applications. In addition, a NiO nanoparticle-dispersed electrospun N-doped porous CNF (NiO/PCNF) free-standing film electrode was fabricated using dicyandiamide(DCDA) and PAN as CNF precursors and nickel acetylacetone as Ni sources by Li et al. (Fig. 4a) [36]. The NiO nanoparticles were uniformly dispersed in the framework of N-doped porous CNF (Fig. 4b). Such a 1D fibrous feature and the interwoven conductive skeleton are beneficial for the fast transfer of electrolyte ions/electrons through the in-plane direction. The NiO/PCNF-0.75 (0.75 represents the weight ratio of DCDA and nickel acetylacetone) showed the maximum specific capacitance of 850 F g−1 at 1 A g−1, and high specific capacitance was retained 748 F g−1 even at 10 A g−1, meaning outstanding rate capability (Fig. 4c, d).
Owing to the high electrical conductivity, superior mechanical strength, and flexible capability, such 1D TMCs/carbon composites have also been widely researched in wearable device applications [50]. For example, Hu et al. [34] developed a MnO2-CNT-textile electrode through the electrodeposit method of MnO2 onto the highly conductive CNT with polyester coatings, which exhibited a large mass loading (8.3 mg cm−2) and high areal capacitance (2.8 F cm−2) in a wearable device. The textile fibers wattled by CNT with high conductivity could largely promote the electrolyte ions/electrons transfer through the in-plane direction, and the MnO2-CNT-textile electrode exhibited a high energy density of 5–20 Wh kg−1 at the high power density of 13 kW kg−1. In another article, Salman and co-workers successfully integrated tungsten nitride (WN) with reduced graphene oxide fibers (rGOF) to obtain a WN-rGOF hybrid by a simple hydrothermal method [54]. Owing to the high tensile strength, excellent flexibility and high electrical conductivity of rGOF, large capacitance and high chemical stability of WN electrode can be obtained. The energy density of WN-rGOF-based hybrid supercapacitors showed a great energy density of 1.448 mWh cm−3. More importantly, the WN-rGOF electrode showed high capacitance retention of 84.7% after 10,000 cycles even under severe mechanical deformation conditions, exhibiting a fascinating advantage for wearable device applications in the future.
1D carbons showed great potential for supercapacitors application, especially flexible wearable devices. However, higher demands have been made for flexible energy-storage systems along with the rapid development of the society, which needs to improve the areal/volumetric performances of 1D carbon. Notably, the form of free-standing TMCs/carbon films attracted more and more attention owing to no additional binders, conductors, or collectors. Compared with TMCs/carbon powders, it can increase the mass loading of active materials, simplify the electrode preparation process, and avoid uncontrollable side reactions, but it needs more advanced technologies. Therefore, the development and application of free-standing film electrodes may be an important development direction of the energy storage industry.
2.3 2D Carbons
Due to the ultra-high specific surface area (2630 m2 g−1) and excellent conductivity, studies about the 2D graphene-based materials applied in energy storage and conversion have sprung up since its first report in 2004 by Novoselov and Geim [55, 56]. More specially, graphene also has been widely studied as a conductive substrate and flexible host in the synthesis of graphene/TMCs composites [15, 57, 58]. The continuously conjugated sp2-C skeleton of graphene can provide efficient ions/electrons transfer channels, which is not only beneficial for the improvement of rate performance of TMCs, but also significant for the long charge/discharge cycling stability. For example, our group previously prepared Ni(OH)2/graphene hybrid material via the microwave heating method [38]. Structural characterization demonstrated that the as-prepared Ni(OH)2 with hierarchical flowerlike morphology were homogeneously decorated on the graphene nanosheets. Compared with pure Ni(OH)2, the hybrid material showed higher specific capacitance and more superior rate capability (As shown in Fig. 5a). Moreover, the Ni(OH)2/graphene//porous graphene-based asymmetric supercapacitor exhibited a high energy density of 77.8 Wh kg−1 at 174.7 W kg−1, which could still retain 13.5 Wh kg−1 at an ultrahigh power density of 15.2 kW kg−1. The superior performance mainly attributes to high conductivity and specific surface area of graphene-based conductive skeleton and high theoretical specific capacitance of Ni(OH)2.
A class of hybrid Fe2O3 nanoclusters/rGO papers (Fe2O3/ rGO)-based negative electrodes were also prepared by Hu and co-workers through a facile hydrothermal method and followed by an electrochemical reduction strategy [39]. When tested in 3 M KOH aqueous electrolyte, the hybrid Fe2O3/rGO electrode obtained both high volumetric energy and power density (0.056 Wh cm−3 and 6.21 W cm−3). Such excellent electrochemical performance can be attributed to the conductive skeleton and flexible host of rGO nanosheets, and the high pseudocapacitance provided by Fe2O3 nanoparticles. As shown in Fig. 5b, Jiang et al. developed a simple, productive, and economical one-pot ball-milling manner to produce a series of graphene/Co3O4 composites [41]. SEM image indicated that the Co3O4 nanoparticles were uniformly anchored on the graphene surface. Graphene as a conductive skeleton can offer fast ion transport pathway. Compared with other composites, the as-prepared graphene/Co3O4-2 (2 represents the graphene content) displayed the most distinguished specific capacitance of 530 F g−1 at 20 A g−1 (Fig. 5b). When assembled as asymmetric supercapacitors using graphene as anode and graphene/Co3O4-2 as a cathode, the energy density of such ASCs could reach 67.5 W h kg−1 at the high power density of 0.8 kW kg−1.
Though the graphene in the construction of TMC-based composite electrodes has been widely employed, the serious agglomeration and restacking issues due to the interplanar π–π interaction and Van der Waals forces always impede its practical popularization, which is urgent to be solved [59]. Moreover, graphene have outstanding electronic conductivity on the horizontal plane; however, its vertical conductivity is low and usually does not achieve ion cross-layer transmission. To address these problems, some methods have been developed, such as pores-creation using KOH/H2O2 treatment, lead-in spacer, and design of ribbons [60, 61].
2.4 3D Carbons
To address the above aggregation issue of graphene, reasonably constructing 3D carbon frameworks, such as 3D porous carbon, 3D graphene building, or 3D cross-linked carbon network, etc., as highly conductive substrates have been raised [62,63,64,65,66,67,68]. These carbon skeletons with unique 3D morphology usually exhibit hierarchical porous structure and ultra-high surface area, which can provide abundant electrolyte ions/electrons transfer channels and sufficient growing space for TMCs. In this context, Bao et al. prepared 3D graphene frameworks/Co3O4 composites via a thermal explosion method [42]. As depicted in Fig. 6a, 3D graphene frameworks with macropores acting as the conductive skeleton can facilitate the rapid transfer of electrolyte ions/electrons. In addition, the Co3O4 nanoparticles with about 4.6–9.4 nm diameters were uniformly and densely distributed on the 3D carbon frameworks. When 3D graphene/Co3O4 composites were used as electrode material for supercapacitors, high specific capacitance (≈ 1765 F g−1 at a current density of 1 A g−1) could be observed, and retention kept 93% even after 5000 cycles at a highly constant current density of 10 A g−1. Moreover, Xu et al. successfully prepared a hybrid material that VN nanoparticles incorporated into a 3D carbon matrix (3D VN/C) through the multi-phase polymeric strategy (Fig. 6b) [43]. The VN nanoparticles are uniformly distributed among the 3D carbon networks, in which the carbon matrix can not only serve as a 3D conductive network but also prevent the VN aggregation. As a result, the 3D VN/C membranes electrode showed excellent electrochemical performance, including high energy density (43.0 Wh kg−1 at a power density of 800 W kg−1) and good cycling stability (82.9% at 1.0 A g−1 after 8000 cycles). More importantly, when the power density reached 4 kW kg−1, the device still performed a high energy density of 32.3 Wh kg−1.
Apart from the usage of single carbon to build 3D conductive carbon skeletons, the substrates can also be constructed by two or more kinds of carbon units. For example, Qing et al. [69] embedded highly crystallized GQDs onto activated carbons (AC) to construct 3D overall conductive networks, which could greatly improve the capacity and rate performances in contrast to pure ACs. The small-sized GQDs are more beneficial to establish evenly distributed conductive networks, which can accelerate the electron/ion transport kinetics in carbon frameworks. Liu et al. [45] designed and prepared MOFs-derived ZnCoNiS nanosheet arrays based on a 3D rGO/CNTs conductive substrate (CoZnNiS/CNTs/rGO) (As depicted in Fig. 6c). The 3D rGO/CNTs network endowed high conductivity of the whole electrode and greatly promoted the electrons transfer kinetics while shortened the electrolyte ions diffusion paths. Moreover, the rough surface of CoZnNiS nanosheets could provide abundant exposing surfaces and active sites, enhancing the redox reaction rate. As a result, the composite film electrode displayed a maximum specific capacitance and high volumetric specific capacitance (1349.2 F g−1 and 1727.0 F cm−3 at 1 A g−1, respectively). When used CoZnNiS/CNTs/rGO and carbon sphere/rGO electrode to assemble hybrid supercapacitor, the device showed a superior energy density of 60.4 Wh kg−1 at an ultrahigh power density of 1200 W kg−1.
To sum up, regardless of the 0D, 1D, 2D, or 3D carbon skeletons, the reasonable design of carbon structures with high conductivity and large specific surface areas to satisfy the high mass loading of TMCs is quietly important. Moreover, how to design ideal carbon skeletons, which exhibit both high bulk densities and porous structure, seems a big challenge. Particularly, the relationships between the holistic devices’ energy density and the ratio of TMCs to carbon-based host have not been reported so far, the content of porous carbon host affects the conductivity and capacitance of the whole electrode that the content of porous carbon host too high to achieve high volume density leading higher electrolyte consumption, too low causing of high charge resistance. In the practical application of TMCs, the fast reaction kinetics of the pseudocapacitive energy storage process commonly need the synergistic effect of conductivity, ions transfer channels, interface stability, etc. Therefore, the systematic design of carbon skeletons for the TMCs/carbon based supercapacitors with high energy/power densities may be the research direction in the future.
3 Interface Engineering
Besides the construction of conductive carbon skeletons, the well-designed interface engineering between carbon networks and TMCs is another indispensable role for TMC-based electrodes which exhibit improved energy density and cycle life [70]. Due to the nano-size effect, TMCs nanoparticles with high surface energy are easy to aggregate during the energy storage process, which can directly lead to the capacity fading, resulting in the hindrance of scaled application of TMCs/carbon-based supercapacitors [71, 72]. Moreover, the roughly physical combination of TMCs and carbon skeletons usually causes high interface impedance and cuts off the electron transfer channels across the heterogeneous interfaces. Therefore, the ideal design of carbon/TMCs interfaces is vitally important for the further enhancement of electrochemical performance. In this section, we will summarize the recent progress of the interface engineering between carbon and TMCs from the aspects of heteroatom-doping, functional group modification, organic interlayer, and spatial confinement (Table 2).
3.1 Heteroatom-Doped Carbon Skeletons
Heteroatoms doping (such as B, N, P, and S) of carbon skeleton is an effective way to construct strong TMCs–carbon interfaces [80]. Density functional theory (DFT) calculations verified that the density of states and charge population of carbon materials have been dramatically altered after the heteroatoms doping [81]. Previous works demonstrated that the electrochemical conductivity and wettability of carbon materials were remarkably improved by the heteroatoms doping, which was beneficial for the enhancement of the electrochemical activity of TMCs/carbon-based electrodes (Fig. 7a–c) [81,83,84]. For example, Dubal and Abdel-Azeim et al. [85] confirmed that the introduction of heteroatoms in carbon matrix could enhance the binding energy between TMCs and carbon (Fig. 7d). In this case, Yang et al. [86] successfully using urea as N source manufactured ultrasmall MnO nanoparticles inserted into N-rich carbon nanosheets (MnO@NCs) hybrid by a facile tactic (Fig. 8a). As shown in Fig. 8b, XPS confirmed that N atoms were successfully introduced into the carbon skeleton, and the ultrasmall MnO nanoparticles (around 2–4 nm) were uniformly anchored on the N-rich carbon nanosheets. Moreover, the copious nitrogen species doped in the carbon skeletons altered the local electron distribution, and the nanoparticles were preferentially in situ nucleated at the N-rich sites, which was beneficial for the uniform dispersion of MnO nanoparticles and offered powerful support for the large mass loading of MnO nanoparticles. Consequently, as assembled in an asymmetric device, the MnO@NCs//AC demonstrated a striking energy density of 21.6 Wh kg−1 at a high power density of 12.4 kW kg−1.
In another report, the composite electrode of Fe2O3 nanodots supported by nitrogen-doped graphene sheets (Fe2O3 ND@NG) was prepared through a facile one-pot method [73]. At a current density of 1 A g−1, the Fe2O3 ND@NG-0.75 (0.75 represents mass ratios of precursor) with the highest N content electrode exhibited the highest specific capacitance of 274 F g−1, which could still arrive to 140 F g−1 even at a high current density of 50 A g−1, indicating a superior rate performance. The excellent electrochemical performance may be attributed to that the nitrogen doping in graphene not only endows graphene with a high charge mobility rate and extra capacitance, but also increases the binding energy between Fe2O3 NDs and NG to build a stable heterogeneous interface. In addition, Miao et al. selected MOFs as precursors to obtain a series of CoSe2/NC hybrid materials with abundant N content [87]. N doping not only enhanced the electric conductivity and wettability of carbon skeletons, but also contributed additional pseudocapacitance. Compared with other hybrids, the CoSe2/NC-400 electrode presented superior electrochemical performance, including high capacity (120.2 mAh g−1 at 1 A g−1), good rate capability (61.2% from 1 to 20 A g−1), and remarkable cyclic ability (retaining 92% after 10,000 cycles). Furthermore, the CoSe2/NC-400//AC-based asymmetric device showed an outstanding energy density of 40.9 Wh kg−1 at a high power density of 980 W kg−1.
Besides single atom doping, co-doping of multiple atoms is also widely investigated [82]. As reported, various heteroatoms co-dopped in the carbon matrix could play specific roles, such as N atom boosting capacitance [88], P atom operating potential window in aqueous electrolyte [89, 90], O atom promoting the electrode–electrolyte interaction [91, 92], and so on [93]. Moreover, the multiple atoms co-doped in the carbon skeleton can play a synergistic coupling effect and effectively improve the electrochemical activities of TMCs/carbon-based electrodes [94]. For example, Hou et al. [17] synthesized Ni/Co-OOH nanosheets decorated with N, S co-doped carbon fragments (NSCF) through an in situ electrochemical self-reconstruction method (Fig. 8d). Even at a high mass loading, the Ni/Co-OOH/NSCF electrode still delivered an ultrahigh capacity and excellent rate capability. Furthermore, as depicted in Fig. 8e, f, an outstanding energy density of 94.3 Wh kg−1 at an ultrahigh power density of 3.6 kW kg−1 could be observed based on the assembled asymmetric supercapacitor of Ni/Co-OOH/NSCF//Fe@N-doped carbon. In another article, Zhao and co-workers successfully fabricated MoS2/nitrogen-phosphorus co-doped graphene composite (MoS2/NPG) via a one-pot hydrothermal strategy [95]. The introduction of N and P atoms could greatly enhance the conductivity and wettability of graphene. After N and P doping, the intimate contact between MoS2 and graphene was largely improved, which could efficiently reduce the electrolyte ions/electrons transfer impedance inside the whole electrode, even across the electrode/electrolyte interfaces. Owing to the synergistic effect of N and P doping, the MoS2/NPG composite showed an outstanding specific capacitance (588 F g−1) in 1 M Na2SO4 aqueous solution. Moreover, the MoS2/NPG electrode-based symmetric supercapacitor device presented a high energy density of 24.34 Wh kg−1 at 300 W kg−1. Even at an ultrahigh power density of 5994 W kg−1, the energy density still remained 6.66 Wh kg−1.
Despite the heteroatoms-doping carbon displayed improved electrochemical performance in aqueous electrolytes, it may be counterproductive in organic electrolytes. Therefore, systematic study of influence of heteroatom doping on the surface chemistry of carbon materials will be a focus of future research. Moreover, reasonable doping amount and doping type also have a great influence on the electrochemical properties of carbon materials. The amount of dopants in carbon is too low to provide more faradaic pseudocapacitances, too high will sacrifice high conductivity, and different doping types perform various functions such as the forms of nitrogen atoms doped including pyridine N, pyrrolic N, graphitic N, etc.
3.2 Covalently Heterogeneous Interface
Be similar to the heteroatoms doping, the introduction of functional groups onto carbon skeleton surface is another necessary strategy to ensure the formation of efficient covalent grafting between TMCs and carbon skeleton through the construction of M–O/N/P/S-C bonds, in which the M represents TMCs, the O/N/P/S represents functional groups, and C represents carbon skeletons. Using strong oxidizing acids (such as nitric and sulfuric acid) to functionalize the carbon surface is the most common method, which can introduce functional groups like amino, carboxyl, hydroxyl, phosphate, or thiol [70]. These superficial functional groups can not only control the loading amount of TMCs but also increase the infiltration of electrode materials in the electrolyte. More importantly, the covalent interfaces between TMCs and carbon are beneficial for the improvement of structural stability during the long charge/discharge process.
For example, Ko et al. [74] prepared layer-by-layer assembly films consisting of amine-functionalized carbon nanotubes (CNTs) and oleic acid-stabilized transition metal oxide nanoparticles (OA-TMO NPs) via the direct construction of covalent-bonding interfaces. The covalent interfaces between CNTs and TMO NPs can reduce the internal interfacial resistance and promote fast electron/ions transfer. Therefore, the CNTs/OA-TMO NPs electrode showed excellent electrochemical performance, including high specific capacitance and excellent cycling stability (e.g., the CNTs/OA-MnO NPs performed the capacity of 305 F cm−3 at 5 mV s−1 and capacitance retention of 106% after 10,000 cycles). In another report, Ni(OH)2/amino-functionalized graphene quantum dots (Ni(OH)2/af-GQDs) composite was fabricated by Zheng and his co-workers via a facile mixture stirring method [96]. Obviously, the introduction of amino-groups on graphene surfaces could remarkably promote the ions transport and enhance anchor forces for Ni2+, which were beneficial for the improvement of electrochemical capacitance. The asymmetric supercapacitor with the Ni(OH)2/af-GQDs as a positive electrode and electrochemical-exfoliated graphene as negative electrode showed a high energy density of 46.5 Wh kg−1 at 1 kW kg−1, which still remained at 16.8 Wh kg−1 even at a high power density of 9 kW kg−1.
In addition, Jia et al. [75] encapsulated the Mn3O4 hollow spheres with modified multi-shell numbers onto the reduced graphene oxide (rGO) surface to obtain the Mn3O4-rGO hybrid materials through oxygen vacancy-assisted hydroxyl modifying method (Fig. 9a). The rGO and multi-shelled Mn3O4 hollow spheres could form Mn-C-O bond with strong binding forces, which could be identified by the XPS O 1 s spectrum with the existence of Mn–O-C specific peak (Fig. 9b). As shown in Fig. 9c, d, the Mn3O4-rGO-2 (2 represents different rGO weights) with large Mn–O–C content (42.1%) exhibited a much higher specific capacitance (561.5 C g−1 at 1 A g−1) and more excellent cycling stability (98% retention after 10,000 cycles). In comparison to the other two hybrid materials, the improved electrochemical performance can be attributed to the construction of covalent heterogeneous interfaces which can ensure the fast charge/discharge reaction kinetics and ultra-long cycling stabilities [75]. Therefore, to ensure fast and reversible Faradaic redox reactions, the design of strong covalent grafting between carbons and TMCs is a promising strategy that reduces the charge transfer resistance at the interface.
3.3 Organic Interlayer
In order to improve the interface stability between TMCs and carbon skeleton, the covalent introduction of organic interlayers onto carbon surface to form the ternary composite is also an efficient method. The organic interlayer between carbon skeleton and TMCs can construct a firm adhesive layer, like glue, connecting the conductive carbon skeleton and pseudocapacitive TMCs. Nowadays, many conductive polymers as carbon coatings have been widely researched, like polyaniline (PANI), polypyrrole (PPy), polythiophene (PTh), etc. [96,98,99].
Taking polyaniline as an example, Zhu et al. [76] fabricated CuO-PANI-rGO ternary hybrid via an in situ polymerization method followed by hydrothermal treatment (Fig. 10a, b). The introduction of PANI can not only maintain the strong attachment between CuO nanorods and rGO surface, but also construct penetrating channels between CuO and rGO for rapid charge transfer. As a result, the CuO-PANI-rGO ternary hybrid displayed a high specific capacitance of 634.4 F g−1 at 1 A g−1 in an aqueous solution, and the self-assembled typical ternary hybrid device exhibited a high energy density of 126.8 Wh kg−1 at a striking power density of 114.2 kW kg−1. Besides, after 10,000 cycles, the specific capacitance lost only remained 2.6%, indicating an outstanding cycle life. In another article, a novel 3D porous graphene/polyaniline/Co3O4 ternary hybrid aerogel (3D GPC) was obtained by Lin and co-workers through a similar hydrothermal method [100]. The 3D GPC possessed an excellent electrochemical performance, including high specific capacitance (1247 F g−1 at 1 A g−1) and superior rate capability (755 F g−1 even at a current density of 20 A g−1). The energy density of 54.5 Wh kg−1 could be achieved at an ultrahigh power density of 3.8 kW kg−1 by calculation. The extraordinary capacitive properties of the 3D GPC hybrid can be explained by the following reasons: (1) the high pseudocapacitance contributed by the PANI and Co3O4; (2) the synergistic effect provided by the uniformly dispersed PANI/Co3O4 NPs onto graphene surface; (3) the effective diffusion paths constructed by the 3D porous structure. Zhang et al. prepared a series of ternary composites through the incorporation of NiO nanocrystals into PAN-based activated carbon nanofibers (ACNF/PANI/NiO) by the combination of multiple methods [77]. Due to the synergistic effect of NiO nanocrystals and PANI modified carbon substrates, the ACNF/PANI/NiO-0.3 (0.3 represents the mass of NiO) composite showed the highest specific capacitance 1157 F g−1 at a current density of 1 A g−1 in 6 M KOH electrolyte and still remained 720 F g−1 even at a high current density of 10 A g−1. Moreover, the ACNF/PANI/NiO-0.3 electrode-based asymmetric supercapacitor exhibited a superior energy density of 14.47 Wh kg−1 at a high power density of 651 W kg−1. Organic interlayer introduced between the carbon skeleton and TMCs that not only serves as a “bridge” for accelerating ion transfer in the interface but also provides a high pseudocapacitance, resulting in high capacitance and rate performance.
3.4 Spatial Confinement
Besides, in order to construct an efficient binding interface between carbon skeletons and TMCs, the in situ spatial confinement effect also is a useful strategy in the preparation of TMCs/carbon composites [52, 101]. TMCs nanocrystals can be strongly confined in the pore or interlamination of carbon skeletons owing to the physical interaction between TMCs and carbon surface. The spatial confinement effect can not only prevent the emergence of direct detaching of TMCs from carbon surface during the long-term charge/discharge process, but also benefit the fast redox reaction kinetics based on the construction of electron transfer channels. Benefiting from the carbon skeletons with superior conductivity and mechanical strength, the charge transfer properties of TMCs/carbon composites can be largely improved, and the structural stabilities can also be correspondingly preserved, which exhibit great advantageous for the power/energy densities and long cycle life.
For example, Cao et al. fabricated a porous rGO/MoO3 composite that the MoO3 particles were strongly wrapped by reduced graphene oxide (rGO) nanosheets through a simple mixture of Mo-MOFs and rGO sheets followed by an annealing process (Fig. 11a) [102]. As shown in Fig. 11b the conductivity of rGO/MoO3 composite was greatly improved in comparison to pristine MoO3, which mainly attributed to the unique structure and synergetic effect of rGO/MoO3 composite. The rGO network greatly reduced the impedance by providing a highly conductive and porous pathway for allowing fast electrons and ions transfer, which was beneficial for the improvement of rate performance. Moreover, the rGO film wrapping around MoO3 prevented the detaching and aggregation of MoO3 nanomaterials, greatly improving the superior cycling capability. Therefore, an all-solid-state flexible supercapacitor device based on rGO/MoO3 composite delivered a good energy density of 14 Wh kg−1 at a high power density of 500 W kg−1 and excellent capacitance retention of ≈ 80% after 5000 cycles at 2 A g−1.
Carbon nanosheets/VN nanodots (VNNDs/CNSs) hybrid electrode material was prepared by Li and co-workers via a facile spatially confined strategy that the VN nanodots (VNNDs) were intercalated into carbon nanosheets (CNSs) (Fig. 11c) [78]. The strategy can well disperse the VNNDs along with the formation of the pillared lamellar structure of CNSs and provide abundant active sites and enhance fast electrolyte ions/electrons diffusion kinetics. The VNNDs encapsulated in CNSs layers could effectively impede the electrochemical oxidation of VN and maintain a more stable structure during the longtime charge/discharge process. Compared with VNND or CNSs, the VNNDs/CNSs hybrid electrode exhibited an ultrahigh specific capacitance (573.1 F g−1 at 0.5 A g−1) and an excellent rate capability (the capacity retention of 58.4% at 100 A g−1 compared with that at 0.5 A g−1) (Fig. 11d). Moreover, the symmetric all solid-state flexible supercapacitors assembled by VNNDs/CNSs electrodes and KOH/PVA gel electrolyte showed an outstanding volumetric energy density of 16.1 Wh L−1 at an ultrahigh volumetric power density of 64,500 W L−1, proving a large potential in the next-generation energy storage devices high energy density.
Yang and his co-works successfully obtained Co3O4/P, N co-doped carbon composites (Co3O4@PNC) through confining the growth of Co3O4 nanoparticles within the nanopores of P, N co-doped carbon material [103]. Compared with Co3O4 (about 320 F g−1), the Co3O4@PNC-2 (2 represents mass loadings of Co3O4) composite showed a higher specific capacitance of 1310 F g−1 at 0.5 A g−1, which still remained at 655 F g−1 even at a high current density of 20 A g−1, indicating an excellent rate capability. This obvious improvement was mainly attributed that the introduction of carbon can not only enhance the conductivity of composite but also keep the uniform distribution of Co3O4 nanoparticles with ultrasmall size (2–5 nm). As a result, the asymmetric supercapacitor based on Co3O4@PNC-2//AC exhibited an ultra-high energy density of 47.18 Wh kg−1 at 375 W kg−1 and maintained at 34.22 Wh kg−1 even at an ultra-high power density of 7.5 kW kg−1.
As a kind method of spatial constraint, the design of core–shell structure also plays a crucial role in improving the electrochemical performance of TMCs [104]. Carbon shell with high mechanical strength not only could enhance the electrical conductivity of composite, but also protect against the degradation and aggregation of TMCs nanoparticles. In this case, Yoon et al. [79] designed and developed a novel millerite core-nitrogen-doped carbon hollow shell (NiS–NC HS) structure by using PD-derived carbon as coated and NiS as the core. Compared with pristine Ni3S2 (828.21 F g−1), the maximum specific capacitance of NiS–NC HS was 1170.72 F g−1 at 0.5 A g−1, and 90.71% of its initial capacitance could be maintained at 6 A g−1 after 4000 charge–discharge cycles. Moreover, the electrode still could retain 72.1% of its maximum capacitance even through the current density increasing to 10 A g−1, displaying a twofold higher rate capability compared with the pristine Ni3S2 (34.56%). In another article, a T-Nb2O5@carbon hollow core–shell nanostructures are constructed by Zhang et al. via using silica as a template [105]. The T-Nb2O5@carbon hollow core–shell nanostructures showed significant improvement in the rate capability (from 34 to 59%) compared to the T-Nb2O5 nanoparticles. More interestingly, hybrid supercapacitors based on the composite exhibited a stable cycle performance (85% capacitance retention after 10,000 cycles) and still processed an energy density of 12 Wh kg−1 at 16 kW kg−1. These results indicated that design of core–shell structure processed great constraining force for TMCs, in which carbon shell could not only enhance the whole conductivity for facilitating the electron transport, but also relieve the volume expansion of TMCs during the charge–discharge process, thereby ensuring the high rate capability and superior cycle stability.
Till now, despite the interface design of TMCs/carbon has already done a lot of research, achieving both outstanding energy density and superior power density of electrode materials is still a huge challenge, and the crucial challenge is to build up stable interface incorporation between carbon and TMCs. The combination of physical spatial constraints and chemical bonding may be a more efficient manner for achieving rapid electrons transfer at the interface of TMCs/carbon-based electrodes in the future.
4 Regulation of TMC’s Electronic Structure
For most of TMCs, the regulation of electronic structure plays a crucial role in enhancing the electrochemical performance of supercapacitors [16, 106, 107]. For example, owing to the different interlink manners, manganese oxides exhibited abundant crystalline structures (including α, β, γ, δ, and λ forms), leading to different electronic structure [108]. Particularly, when the crystal size of TMCs is decreased to nanometer scale or quantum dots, the physical and chemical properties of such materials can make significant changes owing to some special effects such as small size effect, quantum tunneling effect, and surface effect. Moreover, doping heterogeneous atoms to adjust the crystal electronic structure followed by the synergistic effect of multi-metal can also further enhance the electrochemical performance [109, 110]. In recent years, the adjustment of TMC’s electronic structure to optimize TMCs/carbon electrodes has been investigated extensively for supercapacitors [16, 111, 112]. In this section, we will summarize the recent progress from the aspects of the effect of nano-crystallization or quantum dots construction, heterogeneous atoms doping, defects, and construction of heterogeneous interfaces in the regulation of TMC's electronic structure for TMCs/carbon-based supercapacitors with both high energy/power densities.
4.1 Nano-Crystallization or Quantum Dots
Due to the sluggish reaction kinetics, poor electrical conductivity, and volumetric expansion effect, the high power densities and long cycle lives of TMC-based electrodes are greatly prevented in the practical application of supercapacitors. To solve the above challenges, the design of TMCs with nano-crystallization or quantum dots size is considered as an effective strategy [46]. Specifically, nano-structured TMCs can provide larger electrochemical active surfaces owing to surface effect, which shortens the ion diffusion distances and increases the contact areas with electrolytes [113, 114]. For example, Wang et al. [115] synthesized sub-nanometer, ultrafine a-Fe2O3 sheets loading on graphene (SU-Fe2O3-rGO) by controlling the crystallization kinetics (As shown in Fig. 11a). Compared with the NP-Fe2O3-rGO microparticles, the SU-Fe2O3-rGO with the ultrathin thickness (only about 0.9 nm) and smaller lateral size (about 14.5 nm) can avoid the slow ion diffusion kinetics in the bulk phase of Fe2O3 and greatly facilitate the ion/electron transport during electrochemical reactions (Fig. 12b). As a result, the SU-Fe2O3-rGO electrode exhibited a superior specific capacitance of 1575 F g−1 at 1.25 A g−1 and remained at 955 F g−1 even at a high current density of 25 A g−1, indicating a superior rate performance. When assembled as asymmetric supercapacitor using SU-Fe2O3-rGO as anode and NiCo2O4 hybrid as cathode, a high energy density of 43.6 Wh kg−1 could be achieved at a power density 844 W kg−1 (Fig. 12c) and the device possessed excellent cycle life with a capacitance retention of 106.4% after 30,000 cycles at 5 A g−1.
In a similar case, the GCFS-0.33 electrode with high specific capacitance (310.2 C g−1 at 2 mV s−1) was obtained in which the ternary Co0.33Fe0.67S2 nanoparticles (10–60 nm) were embedded between the graphene nanosheets through a facile one-step hydrothermal method [116]. When the GCFS-0.33 composites and sulfurized graphene/CoNiAl-layered double hydroxides were used as the negative and positive electrode, respectively, the as-fabricated ASCs exhibited a high energy density of 66.8 Wh kg−1 at a power density of 300.5 W kg−1 and still retained a high energy density of 13.1 Wh kg−1 even at an ultrahigh power density of 29.4 kW kg−1. Such a robust sandwich-like structure with superior mechanical integration and high electrical conductivity can provide unobstructed pathways for the fast diffusion/transportation of electrolyte ions/electrons during rapid charge/discharge processes, which is beneficial to improve the rate capability. Wang et al. [117] have synthesized a Ni3S2@Co9S8/N-HPC composite in which the Ni3S2 attaching Co9S8 nanocrystal was encapsulated into a 3D N-doped hierarchical porous carbon (N-HPC). The strawberry-like Ni3S2@Co9S8 nanoparticles (average diameter of 900 nm) confined in the carbon skeleton can provide high theoretical specific capacitance, and 3D interconnected hierarchical porous carbon framework can construct fast electrolyte ions/electrons transfer channels. Benefiting from the synergistic effect, the Ni3S2@Co9S8/N-HPC composite showed an ultrahigh specific capacitance and excellent cycling stability. In addition, the Ni3S2@Co9S8/N-HPC//HPC was assembled into an ASCs in a 6 M KOH electrolyte. The ASCs delivered a high energy density of 77.1 W h kg−1 at 263.3 W kg−1 and still remained as high as 36.1 Wh kg−1 even at an ultrahigh power density of 25.9 kW kg−1.
Quantum dots (QDs) have presented an exponential growth of research in various potential applications in the last decades, especially in supercapacitors [117,119,120,121]. Due to the quantum effect, TMCs-QDs as electrode materials for supercapacitors have received extensive attention [122]. For example, Xia et al. synthesized Fe2O3/FGS hybrid materials that Fe2O3 quantum dots (QDs) (about 2 nm) were uniformly decorated on the functionalized graphene sheets (FGS) through a thermal decomposition method (Fig. 12d) [24]. The Fe2O3 QDs can be evenly dispersed on the surface of FGS with a proper mass ratio of Fe2O3/FGS (2:1), and the high conductivity and large surface area of FGS efficiently suppress the agglomeration of Fe2O3 QDs. As a result, the asymmetrical supercapacitor based on Fe2O3/FGS exhibited a high energy density of 50.7 Wh kg−1 at a power density of 100 W kg−1 and cycling stability of 95% after 5000 cycles in a voltage window of 2 V. Moreover, a Nb2O5 QD-NC hybrid material was prepared by Liu et al. that Nb2O5 quantum dots (about 5 nm) were successfully embedded into the nitrogen-doped porous carbon (NC) derived from ZIF-8 dodecahedrons [123]. When assembled with commercial activated carbon cathode, the hybrid supercapacitors (HSCs) showed a high energy density of 76.9 Wh kg−1 at an ultrahigh power density of 11,250 W kg−1 and superior cycling stability (about capacity retention of 85%) in an organic condition. The excellent performance of Nb2O5 QD-NC can be ascribed to the following reasons: (1) the high surface area and highly porous structure of NC can provide more ion attachment site which is beneficial for the fast electrolyte ions/electrons transfer; (2) ultrasmall size (ca. 5 nm) may shorten the ion diffusion and electron transportation distance; (3) the uniform distribution of Nb2O5 QDs and strongly interfacial binding between Nb2O5 QDs and NC can prevent the volume change upon cycling; (4) N doping may boost the electronic properties and provide additional charge-storage sites.
In contrast to conventional bulk materials, TMCs with nanoscale size can greatly improve ionic and electronic transport, which may be a promising solution for the achievement of both high energy and power densities for TMCs/carbon-based supercapacitors [124]. Consequently, nanoscale TMCs crystals supported by the conductive carbon skeletons can not only avoid the deficiency of single material, but also greatly boost the practical application of TMCs/carbon electrodes in energy storage devices.
4.2 Heterogeneous Atoms Doping
Heterogeneous atoms doping is another effective strategy, which can fundamentally regulate the electronic structure and alter the electron distribution to further improve the reaction activity and the electrochemical performance of TMCs/carbon based supercapacitors [125, 126]. According to the doping type, heterogeneous atoms doping can be divided into cation doping (heterogeneous metal atoms, e.g., Ni and Co, Co and W, Mn and Fe, even more, metal atoms, etc.) and anion doping (e.g., N, P, or F). Owing to the synergistic effect of the multiple transition metal atoms, combination of various TMCs can provide highly electrochemical conductivity and abundant redox activity, which is beneficial for the electrochemical performance [127, 128, 129]. For example, Liu’s group systematically studied the influence of cobalt and manganese atoms (Co, Mn) on the single doping or co-doping of Ni(OH)2 crystals by DFT calculations [130]. The Mn doping could increase the capacity owing to the lower deprotonation energy and facile electron transfer path, while the Co doping could improve the structural stability of the entire electrode (Fig. 13e–g) [130]. As shown in Fig. 13b-d, the Ni–Co–Mn–OH/rGO//PPD/rGO hybrid capacitor demonstrated remarkable energy densities of 74.7 and 49.9 W kg−1 at the power densities of 1.68 and 18.5 kW kg−1, respectively. Moreover, 91% of its initial capacity could be retained after 10,000 cycles at 20 A g−1, showing super-fast energy storage capacity and long cycle life. In another article, Mohamed et al. [131] fabricated Co-W-S composites in an N, S co-doped porous carbon matrix (Co-W-S@N, S-PC) using PTA@ZIF-67 as a precursor via a simple carbonization method. Compared with the Co1−xS@N, S-PC, the introduction of W atom could not only increase the redox activity of transition metal redox centers, but also provide additional faradaic pseudocapacitance. As a result, the Co-W-S@N, S-PC electrode demonstrated an ultrahigh specific capacitance (1929 F g−1 at 5 mV s−1). Furthermore, the asymmetric supercapacitor device based on Co-W-S@N, S-PC//AC delivered a superior energy density of 32.9 Wh kg−1 at the high power density of 700.2 W kg−1 and good cyclic stability with capacitance retention of 77% after 5000 cycles at 10 A g−1.
In contrast to cation doping, the anion doping of TMCs based electrodes is rarely reported. The experimental results and DFT calculations have confirmed that the anion-doping in TMCs could act as an effective approach to enhance the electrochemical conductivity and improve the reaction kinetics [53, 132]. For example, Liu et al. developed a P-CoS2@P, S, N–C hybrid of P-doped CoS2 (P-CoS2) nanoparticles confined in highly conductive P, S, N tri-doped carbon skeleton (P, S, N–C) [133]. The P-CoS2@P, S, N–C hybrid delivered a high specific capacity of 689 C g−1 at 2 A g−1, and still possessed capacitance retention of 77.5% even at a high current density of 30 A g−1. This was mainly because the introduction of P atom could enhance the covalency and decrease the migration energy of electrons, which largely boosted the electrochemical conductivity. In addition, ultrafine P-Co3O4 nanoparticles embedded into P, N–C nanowires (P-Co3O4@P, N–C) were also prepared via an in situ structural reconstruction strategy [53]. The theoretical calculation and experimental results showed that P doping could improve the electrochemical reactivity and facilitate the electrons/ions transport. Therefore, the appropriate incorporation of a small number of heterogeneous atoms into TMCs can not only provide additional capacity but also improve its electrical conductivity, which provides a helpful way to regulate the electronic structure of the TMCs.
4.3 Defects
Defects, such as vacancies, edges, grain boundaries, substitutional impurities, and so on, always play significant roles in improving geometric and electronic structures of TMCs [134]. Different defects often play different functions in improving the electrochemical performance of TMCs, such as vacancies increasing more active sites and enhancing conductivity [135, 136], substitutional impurities providing additional capacitances and so on [131, 137]. Specifically, the vacancies including metal vacancies and nonmetallic vacancies have been extensively explored to accelerate the intrinsic conductivity and redox activity of TMCs for supercapacitors [136, 138, 139]. In this part, taking oxygen vacancies, for example, we will mainly discuss the effect of oxygen vacancies on the electrochemical performance of transition metal oxides (TMOs) based supercapacitors.
Kim et al. have confirmed that the presence of oxygen vacancies in α-MoO3 can greatly improve the electrical conductivity (electrical conductivity from 10–5 S cm−1 increasing to 10–4 S cm−1) and broaden the interlayer spacing. The experimental results showed that MoO3–x had higher capacity (∼ 550 C g−1) and better cycling stability (76% after 10,000 cycles) compared with MoO3 (< 400 C g−1, 50% after 50 cycles) at a sweep rate of 100 mV s−1 [140]. The incorporation of oxygen vacancies could act as electron donors and consequently increase the free carrier concentration as well as provide more exposed electrochemical active sites, resulting in improved electrochemical properties [141]. To gain abundant oxygen vacancies, Yang and co-workers firstly prepared ultrafine Co3O4 nanoparticles/graphene (UCNG) composites with abundant oxygen-vacancy via a new-type one-step laser irradiation strategy [142]. The theoretical calculations demonstrated that the surface oxygen vacancies could promote the electrons transfer by creating midgap electronic states. As a result, the UCNG electrode achieved a high specific capacitance of 978.1 F g−1 at 1 A g−1 and more than capacitance retention of 93.7% even at a high current density of 10 A g−1. Moreover, based on the fluorine-doped, Liu et al. [125] successfully fabricated F-Co2MnO4-x/CF composite by introducing oxygen vacancies into Co2MnO4 (Fig. 14a). As advanced electrode materials for supercapacitor, the F-Co2MnO4−x/CF exhibited a higher specific capacity of 269 mAh g−1 and more superior cyclic stability (93.3% of the initial specific capacity after 5000 cycles) in comparison to the F-Co2MnO4/CF (204 mAh g−1, 90.9%) and Co2MnO4/CF (165 mAh g−1, 85.8%), principally demonstrating that the introduction of F dopants and oxygen vacancies could synergistically increase the electrical conductivity and reactivity of electrochemically active sites (Fig. 14b). Moreover, the ASCs of F-Co2MnO4−x /CF//Fe2O3/CF exhibited high energy density of 64.4 Wh kg−1 at a power density of 800 W kg−1 (Fig. 14c).
In short, the introduction of oxygen vacancies into TMOs can tremendously improve the electrochemical performance for supercapacitors, e g., greater electrical conductivity, more prominent specific capacitance, rate performance, and cyclic stability. Besides, the distribution of the defects is also a critical factor of the electrochemical performance enhancement, oxygen vacancies with uniform distribution in TMCs are beneficial to improve the cycle stability [143]. Therefore, defects reasonably introduced into electrode materials can not only contribute to improving the physicochemical properties but also adjust the performance of materials.
4.4 Heterogeneous Interface
In the past few years, the construction of heterogeneous interfaces during the synthesis of TMCs crystals has aroused extensive research interests due to its improved high ion carrier mobility and broad electrode potential, mainly because the unique structure can decrease the activity of hydrogen evolution reaction (HER) and oxygen evolution reaction (OER) at high voltage window [142,144,145,146,147]. For example, the NiFeP@NiCo2S4/carbon cloth (NiFeP@NiCo2S4/CC) hybrid electrode with NiFeP@NiCo2S4 heterostructure was successfully manufactured by using a novel combination of hydrothermal reaction, phosphorization treatment, and electrodeposition technique strategy (Fig. 15a) [148]. Compared with NiFeP/CC and NiCo2S4/CC, the NiFeP@NiCo2S4/CC hybrid electrode demonstrated higher specific capacitance (Fig. 15c), better rate capability, and more excellent cycling stability. In an asymmetric supercapacitor of NiFeP@NiCo2S4/CC//porous carbon OPC-850, the device obtained a superior energy density of 32.1 Wh kg−1 at an ultrahigh power density of 18,034.2 W kg−1 (Fig. 15d). The distinguished electrochemical performance can be attributed that the unique heterostructure not only provides abundant open channels to achieve rapid electronic transport, but also enlarge accessible 2D surface to offer more active sites for absorbing electrolyte ions (Fig. 15b).
In addition, bimetallic MOF-derived NiCo2S4-Ni9S8-C double-layered yolk–shell microspheres were synthesized by Yan et al. [149]. Owing to the existence of NiCo2S4-Ni9S8 hetero-interface, the composite materials exhibited superior specific capacity (293.6 mAh g−1 at 1 A g−1) and good rate ability (capacitance retained 81.1% as current densities increased from 1 to 20 A g−1). Based on DFT calculations, the authors also confirmed that the hetero-interfaces of NiCo2S4-Ni9S8 changed the electronic distribution, thus strengthening the electrochemical conductivity of the entire electrode. Moreover, the hybrid supercapacitors assembled by NiCo2S4-Ni9S8-C DYMs and graphene hydrogel showed an excellent energy density of 51 Wh kg−1 at a superhigh power density of 1399.4 W kg−1. In another article, Dang and his co-workers fabricated a 3D NiCoP/CoP hetero-nanosheets network supported by N-CNTs (N-CTs@NiCoP/CoP) via one-step phosphorization of nickel/cobalt hydroxide [150]. The hybrid supercapacitor of N-CNTs@NiCoP/CoP//ZIF-67-derived porous carbon demonstrated an outstanding energy density of 45.5 Wh kg−1 at 784 W kg−1 and great stability of 87% retention (after 10,000 cycles at 12 A g−1). The superior electrochemical performance can be mainly ascribed to the strong synergistic effect of NiCoP/CoP heterojunctions, the large surface area of N-CNTs skeletons, and 3D conductive networks.
In conclusion, a heterogeneous interface consisting of two or more types of TMCs materials not only enhances the structural stability, but also provides fast pathways for electrolyte ion/electrons transfer, leading to the improved electrochemical performance of the whole electrode, which could offer a good thought of a structural design for TMCs/carbon based supercapacitors.
5 Summary and Outlook
TMCs/carbon-based supercapacitors with the potential high energy densities represent the application tendency of next-generation energy storage systems. However, as for the practical and large-scale applications, the poor power density and inferior cycle stability derived from the low intrinsic conductivity and structural instability of TMCs are critical constraints. In this review, focusing on the current fundamental understanding, challenges, and opportunities, we systematically discuss the possible design strategies for the TMCs/carbon-based supercapacitors from the aspects of conductive carbon substrates, interface engineering, and modification of electronic structures for the first time. Firstly, we present the structural design strategies for the carbon skeletons with different dimensions. As the electrode supports and conductive skeletons, carbon substrates with high electron conductivities to guarantee the rapid charge transfer, abundant pore channels to promote the electrolyte ions migration, large specific surface area to load more amounts of TMCs, even superior mechanical stability/flexibility to support long cycle life, etc., are greatly needed. Secondly, we point out that the strong interfaces between carbon skeletons and TMCs play a crucial role in achieving high power density and long cycle stability of TMCs/carbon-based supercapacitors. Specifically, we describe four feasible manners for the construction of steady interfaces between carbon skeletons and TMCs by the modification of carbon surface or physical interaction, including heteroatom-doping, functional groups modification, organic interlayer introduction, and spatial confinement. Lastly, the modification of TMCs (including TMCs-QDs) crystals with nanoscale dimensions can reduce the electron/ion diffusion distance, increase the electrode/electrolyte contact surface, improve the intrinsic conductivity/redox activity, etc., and also have been presented as one guarantee role to realize both high power/energy densities of TMCs/carbon based supercapacitors.
Despite large amounts of research that have been done to study the assemble strategies, electrochemical performance, and energy storage mechanism of TMCs/carbon based supercapacitors, some critical challenges still need to be considered: (1) How to achieve the high-efficiency utilization of carbon as conductive support plays a pretty important role. Although large specific surface area and porous structure of carbon substrate can provide high conductivity and abundant electrons/electrolyte ions transfer channels, carbon materials with low specific capacitance restrict its development. Therefore, the high-efficiency utilization of carbon as conductive substrate needs to be considered on basis of appropriate mass ratio between carbon and TMCs, achieving high energy density as well as high power density. (2) The trade-off between high mass loading and agglomeration of nanoscale TMCs crystals also is a challenge. TMCs with nanostructure can achieve high mass loading and efficient utilization ratio, which possess much higher faradaic pseudocapacitive reaction kinetics. However, in a real scenario, the high surface energy of TMCs with ultra-small sizes is easy to be agglomerated, resulting in sluggish reaction kinetics as same as bulk materials. (3) New techniques and methods are urgently needed to construct steady composite interfaces. For composite materials, the fast transfer of electrolyte ions/electrons across the heterogeneous interfaces plays an important role in achieving ultra-high charge/discharge rates. However, how to build a steady composite interface is still a problem that needs deep thinking. (4) Besides, the choices of electrolyte, current collector, separator, and other components are also equally important. Notably, the form of free-standing film electrodes attracted more and more attention owing to no additional binders, conductors, or collectors. Compared with powder electrodes, it can increase mass loading of active materials, simplify the electrode preparation process, and avoid uncontrollable side reactions, which may be an important development direction of energy storage industry in the future.
This review provides a comprehensive and in-depth discussion about the structural design strategies for the high power TMCs/carbon-based supercapacitors. We try to present the classic and latest research findings and propose progressive perspectives towards the critical challenges that are relevant to the practical and large-scale application of TMCs/carbon-based supercapacitors. Overall, it is highly expected that more novel design strategies and efficient TMCs/carbon-based supercapacitors could come into the picture and further revolutionize the way we live in the future.
References
P. Simon, Y. Gogotsi, Materials for electrochemical capacitors. Nat. Mater. 7(11), 845–854 (2008). https://doi.org/10.1038/nmat2297
Y. Wang, L. Zhang, H. Hou, W. Xu, G. Duan et al., Recent progress in carbon-based materials for supercapacitor electrodes: a review. J. Mater. Sci. 56(1), 173–200 (2021). https://doi.org/10.1007/s10853-020-05157-6
Y. Shao, M.F. El-Kady, J. Sun, Y. Li, Q. Zhang et al., Design and mechanisms of asymmetric supercapacitors. Chem. Rev. 118(18), 9233–9280 (2018). https://doi.org/10.1021/acs.chemrev.8b00252
H. Wang, H. Dai, Strongly coupled inorganic-nano-carbon hybrid materials for energy storage. Chem. Soc. Rev. 42(7), 3088–3113 (2013). https://doi.org/10.1039/c2cs35307e
Z. Yang, J. Zhang, M.C.W. Kintner-Meyer, X. Lu, D. Choi et al., Electrochemical energy storage for green grid. Chem. Rev. 111(5), 3577–3613 (2011). https://doi.org/10.1021/cr100290v
J.R. Miller, P. Simon, Materials science—electrochemical capacitors for energy management. Science 321(5889), 651–652 (2008). https://doi.org/10.1126/science.1158736
F. Beguin, V. Presser, A. Balducci, E. Frackowiak, Carbons and electrolytes for advanced supercapacitors. Adv. Mater. 26(14), 2219–2251 (2014). https://doi.org/10.1002/adma.201304137
A. Berrueta, A. Ursua, I. San Martin, A. Eftekhari, P. Sanchis, Supercapacitors: electrical characteristics, modeling, applications, and future trends. IEEE Access 7, 50869–50896 (2019). https://doi.org/10.1109/access.2019.2908558
X. Zhao, B.M. Sanchez, P.J. Dobson, P.S. Grant, The role of nanomaterials in redox-based supercapacitors for next generation energy storage devices. Nanoscale 3(3), 839–855 (2011). https://doi.org/10.1039/c0nr00594k
Y. Wang, Y. Xia, Recent progress in supercapacitors: from materials design to system construction. Adv. Mater. 25(37), 5336–5342 (2013). https://doi.org/10.1002/adma.201301932
J. Yan, Q. Wang, T. Wei, Z. Fan, Recent advances in design and fabrication of electrochemical supercapacitors with high energy densities. Adv. Energy Mater. 4(4), 14264 (2014). https://doi.org/10.1002/aenm.201300816
P. Veerakumar, A. Sangili, S. Manavalan, P. Thanasekaran, K.-C. Lin, Research progress on porous carbon supported metal/metal oxide nanomaterials for supercapacitor electrode applications. Ind. Eng. Chem. Res. 59(14), 6347–6374 (2020). https://doi.org/10.1021/acs.iecr.9b06010
K.A. Owusu, L. Qu, J. Li, Z. Wang, K. Zhao et al., Low-crystalline iron oxide hydroxide nanoparticle anode for high-performance supercapacitors. Nat. Commun. 8, 14264 (2017). https://doi.org/10.1038/ncomms14264
L. Zheng, J. Song, X. Ye, Y. Wang, X. Shi et al., Construction of self-supported hierarchical nico-s nanosheet arrays for supercapacitors with ultrahigh specific capacitance. Nanoscale 12(25), 13811–13821 (2020). https://doi.org/10.1039/d0nr02976a
P. Geng, S. Zheng, H. Tang, R. Zhu, L. Zhang et al., Transition metal sulfides based on graphene for electrochemical energy storage. Adv. Energy Mater. 8(15), 1703259 (2018). https://doi.org/10.1002/aenm.201703259
T. Wang, H.C. Chen, F. Yu, X.S. Zhao, H. Wang, Boosting the cycling stability of transition metal compounds-based supercapacitors. Energy Storage Mater. 16, 545–573 (2019). https://doi.org/10.1016/j.ensm.2018.09.007
L. Hou, W. Yang, R. Li, X. Xu, P. Wang et al., Self-reconstruction strategy to synthesis of Ni/Co–OOH nanoflowers decorated with N, S co-doped carbon for high-performance energy storage. Chem. Eng. J. 396, 125323 (2020). https://doi.org/10.1016/j.cej.2020.125323
Y. Jiang, J. Liu, Definitions of pseudocapacitive materials: a brief review. Energy Environ. Mater. 2(1), 30–37 (2019). https://doi.org/10.1002/eem2.12028
Z. Qiu, Y. Wang, X. Bi, T. Zhou, J. Zhou et al., Biochar-based carbons with hierarchical micro-meso-macro porosity for high rate and long cycle life supercapacitors. J. Power Sources 376, 82–90 (2018). https://doi.org/10.1016/j.jpowsour.2017.11.077
S. Kumar, G. Saeed, L. Zhu, K.N. Hui, N.H. Kim et al., 0d to 3d carbon-based networks combined with pseudocapacitive electrode material for high energy density supercapacitor: a review. Chem. Eng. J. 403, 126352 (2021). https://doi.org/10.1016/j.cej.2020.126352
P. Balaya, Size effects and nanostructured materials for energy applications. Energy Environ. Sci. 1(6), 645–654 (2008). https://doi.org/10.1039/b809078p
Y. Son, M. Park, Y. Son, J.-S. Lee, J.-H. Jang et al., Quantum confinement and its related effects on the critical size of GeO2 nanoparticles anodes for lithium batteries. Nano Lett. 14(2), 1005–1010 (2014). https://doi.org/10.1021/nl404466v
R.W. Mo, Z.Y. Lei, K.N. Sun, D. Rooney, Facile synthesis of anatase tio2 quantum-dot/graphenenanosheet composites with enhanced electrochemical performance for lithium-ion batteries. Adv. Mater. 26(13), 2084–2088 (2014). https://doi.org/10.1002/adma.201304338
H. Xia, C. Hong, B. Li, B. Zhao, Z. Lin et al., Facile synthesis of hematite quantum-dot/functionalized graphene-sheet composites as advanced anode materials for asymmetric supercapacitors. Adv. Funct. Mater. 25(4), 627–635 (2015). https://doi.org/10.1002/adfm.201403554
H.M. Jeong, K.M. Choi, T. Cheng, D.K. Lee, R. Zhou et al., Rescaling of metal oxide nanocrystals for energy storage having high capacitance and energy density with robust cycle life. Proc. Natl. Acad. Sci. USA 112(26), 7914–7919 (2015). https://doi.org/10.1073/pnas.1503546112
V.C. Hoang, K. Dave, V.G. Gomes, Carbon quantum dot-based composites for energy storage and electrocatalysis: mechanism, applications and future prospects. Nano Energy 66, 104093 (2019). https://doi.org/10.1016/j.nanoen.2019.104093
X. Yang, C. Cai, Y. Zou, C. Xiang, H. Chu et al., Co3O4-doped two-dimensional carbon nanosheet as an electrode material for high-performance asymmetric supercapacitors. Electrochim. Acta 335, 135611 (2020). https://doi.org/10.1016/j.electacta.2020.135611
X.-M. Han, Y.-B. Wu, H.-Y. Zhao, J. Bi, B.-B. Wei, Preparation and supercapacitor properties of carbon-coated SnO2 hollow fibers. Acta Phys. Chim. Sin. 31(11), 2220–2228 (2015). https://doi.org/10.3866/pku.whxb201510131
Y. Zhu, Z. Wu, M. Jing, H. Hou, Y. Yang et al., Porous NiCo2O4 spheres tuned through carbon quantum dots utilised as advanced materials for an asymmetric supercapacitor. J. Mater. Chem. A 3(2), 866–877 (2015). https://doi.org/10.1039/c4ta05507a
H. Lv, X. Gao, Q. Xu, H. Liu, Y.-G. Wang et al., Carbon quantum dot-induced MnO2 nanowire formation and construction of a binder-free flexible membrane with excellent superhydrophilicity and enhanced supercapacitor performance. ACS Appl. Mater. Interfaces 9(46), 40394–40403 (2017). https://doi.org/10.1021/acsami.7b14761
G. Wei, X. Xu, J. Liu, K. Du, J. Du et al., Carbon quantum dots decorated hierarchical Ni(OH)(2) with lamellar structure for outstanding supercapacitor. Mater. Lett. 186, 131–134 (2017). https://doi.org/10.1016/j.matlet.2016.09.126
H. Jia, Y. Cai, J. Lin, H. Liang, J. Qi et al., Heterostructural graphene quantum dot/MnO2 nanosheets toward high-potential window electrodes for high-performance supercapacitors. Adv. Sci. 5(5), 1700887 (2018). https://doi.org/10.1002/advs.201700887
A.B. Ganganboina, E.Y. Park, R.-A. Doong, Boosting the energy storage performance of V(2)O(5)nanosheets by intercalating conductive graphene quantum dots. Nanoscale 12(32), 16944–16955 (2020). https://doi.org/10.1039/d0nr04362a
L. Hu, W. Chen, X. Xie, N. Liu, Y. Yang et al., Symmetrical MnO2-carbon nanotube-textile nanostructures for wearable pseudocapacitors with high mass loading. ACS Nano 5(11), 8904–8913 (2011). https://doi.org/10.1021/nn203085j
Z. Tang, C.-H. Tang, H. Gong, A high energy density asymmetric supercapacitor from nano-architectured Ni(OH)2/carbon nanotube electrodes. Adv. Funct. Mater. 22(6), 1272–1278 (2012). https://doi.org/10.1002/adfm.201102796
Q. Li, J. Guo, D. Xu, J. Guo, X. Ou et al., Electrospun N-doped porous carbon nanofibers incorporated with nio nanoparticles as free-standing film electrodes for high-performance supercapacitors and CO2 capture. Small 14(15), 1704203 (2018). https://doi.org/10.1002/smll.201704203
A. Meng, X. Yuan, T. Shen, J. Zhao, G. Song et al., Amorphous nickel sulfide nanoparticles anchored on N-doped graphene nanotubes with superior properties for high-performance supercapacitors and efficient oxygen evolution reaction. Nanoscale 12(7), 4655–4666 (2020). https://doi.org/10.1039/c9nr09654j
J. Yan, Z. Fan, W. Sun, G. Ning, T. Wei et al., Advanced asymmetric supercapacitors based on Ni(OH)2/graphene and porous graphene electrodes with high energy density. Adv. Funct. Mater. 22(12), 2632–2641 (2012). https://doi.org/10.1002/adfm.201102839
Y. Hu, C. Guan, Q. Ke, Z.F. Yow, C. Cheng et al., Hybrid Fe2O3 nanoparticle clusters/RGO paper as an effective negative electrode for flexible supercapacitors. Chem. Mater. 28(20), 7296–7303 (2016). https://doi.org/10.1021/acs.chemmater.6b02585
T. Xiong, W.S.V. Lee, X. Huang, J.M. Xue, Mn3O4/reduced graphene oxide based supercapacitor with ultra-long cycling performance. J. Mater. Chem. A 5(25), 12762–12768 (2017). https://doi.org/10.1039/c7ta03319b
Y. Jiang, C. He, S. Qiu, J. Zhang, X. Wang et al., Scalable mechanochemical coupling of homogeneous Co3O4 nanocrystals onto in -situ exfoliated graphene sheets for asymmetric supercapacitors. Chem. Eng. J. 397, 125503 (2020). https://doi.org/10.1016/j.cej.2020.125503
L. Bao, T. Li, S. Chen, C. Peng, L. Li et al., 3d graphene frameworks/Co3O4 composites electrode for high-performance supercapacitor and enzymeless glucose detection. Small 13(5), 1602077 (2017). https://doi.org/10.1002/smll.201602077
Y. Wu, Y. Yang, X. Zhao, Y. Tan, Y. Liu et al., A novel hierarchical porous 3d structured vanadium nitride/carbon membranes for high-performance supercapacitor negative electrodes. Nano-Micro Lett. 10(4), 63 (2018). https://doi.org/10.1007/s40820-018-0217-1
S. Li, K. Yang, P. Ya, K. Ma, Z. Zhang et al., Three-dimensional porous carbon/Co3O4 composites derived from graphene/Co-MOF for high performance supercapacitor electrodes. Appl. Surf. Sci. 503, 144090 (2020). https://doi.org/10.1016/j.apsusc.2019.144090
Y. Liu, N. Xin, Q. Yang, W. Shi, 3d cnts/graphene network conductive substrate supported mofs-derived CoZnNiS nanosheet arrays for ultra-high volumetric/gravimetric energy density hybrid supercapacitor. J. Colloid Interface Sci. 583, 288–298 (2020). https://doi.org/10.1016/j.jcis.2020.08.128
T. Shen, L. Yang, M.E. Pam, Y. Shi, H.Y. Yang, Quantum dot-carbonaceous nanohybrid composites: preparation and application in electrochemical energy storage. J. Mater. Chem. A 8(43), 22488–22506 (2020). https://doi.org/10.1039/d0ta07674k
Z. Zhang, J. Zhang, N. Chen, L. Qu, Graphene quantum dots: An emerging material for energy-related applications and beyond. Energy Environ. Sci. 5(10), 8869–8890 (2012). https://doi.org/10.1039/c2ee22982j
Y. Zhu, X. Ji, C. Pan, Q. Sun, W. Song et al., A carbon quantum dot decorated RuO2 network: outstanding supercapacitances under ultrafast charge and discharge. Energy Environ. Sci. 6(12), 3665–3675 (2013). https://doi.org/10.1039/c3ee41776j
Y. Huang, T. Shi, Y. Zhong, S. Cheng, S. Jiang et al., Graphene-quantum-dots induced NiCo2S4 with hierarchical-like hollow nanostructure for supercapacitors with enhanced electrochemical performance. Electrochim. Acta 269, 45–54 (2018). https://doi.org/10.1016/j.electacta.2018.02.145
L. Liu, Z. Niu, J. Chen, Flexible supercapacitors based on carbon nanotubes. Chin. Chem. Lett. 29(4), 571–581 (2018). https://doi.org/10.1016/j.cclet.2018.01.013
G. Nie, X. Zhao, Y. Luan, J. Jiang, Z. Kou et al., Key issues facing electrospun carbon nanofibers in energy applications: On-going approaches and challenges. Nanoscale 12(25), 13225–13248 (2020). https://doi.org/10.1039/d0nr03425h
L. Jiang, Y. Qiu, P. Luo, Y. Yu, Nickel hydroxide-impregnated and -coated carbon nanotubes using an easily manipulated solvothermal route for supercapacitors. Ceram. Int. 42(10), 11634–11639 (2016). https://doi.org/10.1016/j.ceramint.2016.04.064
S. Liu, Y. Yin, Y. Shen, K.S. Hui, Y.T. Chun et al., Phosphorus regulated cobalt oxide@nitrogen-doped carbon nanowires for flexible quasi-solid-state supercapacitors. Small 16(4), 1906458 (2020). https://doi.org/10.1002/smll.201906458
A. Salman, S. Padmajan Sasikala, I.H. Kim, J.T. Kim, G.S. Lee et al., Tungsten nitride-coated graphene fibers for high-performance wearable supercapacitors. Nanoscale 12(39), 20239–20249 (2020). https://doi.org/10.1039/d0nr06636b
B. Wang, T. Ruan, Y. Chen, F. Jin, L. Peng et al., Graphene-based composites for electrochemical energy storage. Energy Storage Mater. 24, 22–51 (2020). https://doi.org/10.1016/j.ensm.2019.08.004
S. Korkmaz, I.A. Kariper, Graphene and graphene oxide based aerogels: synthesis, characteristics and supercapacitor applications. J. Energy Storage 27, 101038 (2020). https://doi.org/10.1016/j.est.2019.101038
T. Palaniselvam, J.-B. Baek, Graphene based 2d-materials for supercapacitors. 2d Mater 2(3), 032002 (2015). https://doi.org/10.1088/2053-1583/2/3/032002
M.S. Rahmanifar, M. Hemmati, A. Noori, M.F. El-Kady, M.F. Mousavi et al., Asymmetric supercapacitors: an alternative to activated carbon negative electrodes based on earth abundant elements. Mater. Today Energy 12, 26–36 (2019). https://doi.org/10.1016/j.mtener.2018.12.006
X. Yang, C. Cheng, Y. Wang, L. Qiu, D. Li, Liquid-mediated dense integration of graphene materials for compact capacitive energy storage. Science 341(6145), 534–537 (2013). https://doi.org/10.1126/science.1239089
Z. Tang, X. Li, T. Sun, S. Shen, H. Xiu et al., Porous crumpled graphene with hierarchical pore structure and high surface utilization efficiency for supercapacitor. Microporous Mesoporous Mat. 272, 40–43 (2018). https://doi.org/10.1016/j.micromeso.2018.06.020
Y. Xu, Z. Lin, X. Zhong, X. Huang, N.O. Weiss et al., Holey graphene frameworks for highly efficient capacitive energy storage. Nat. Commun. 5, 4554 (2014). https://doi.org/10.1038/ncomms5554
A.R. Thiruppathi, B. Sidhureddy, E. Boateng, D.V. Soldatov, A. Chen, Synthesis and electrochemical study of three-dimensional graphene-based nanomaterials for energy applications. Nanomaterials 10(7), 1295 (2020). https://doi.org/10.3390/nano10071295
R.R. Salunkhe, Y.V. Kaneti, J. Kim, J.H. Kim, Y. Yamauchi, Nanoarchitectures for metal-organic framework-derived nanoporous carbons toward supercapacitor applications. Acc. Chem. Res. 49(12), 2796–2806 (2016). https://doi.org/10.1021/acs.accounts.6b00460
H. Jiang, P.S. Lee, C. Li, 3d carbon based nanostructures for advanced supercapacitors. Energy Environ. Sci. 6(1), 41–53 (2013). https://doi.org/10.1039/c2ee23284g
J. Xu, Z. Tan, W. Zeng, G. Chen, S. Wu et al., A hierarchical carbon derived from sponge-templated activation of graphene oxide for high-performance supercapacitor electrodes. Adv. Mater. 28(26), 5222 (2016). https://doi.org/10.1002/adma.201600586
J. Chen, J. Xu, S. Zhou, N. Zhao, C.-P. Wong, Nitrogen-doped hierarchically porous carbon foam: a free-standing electrode and mechanical support for high-performance supercapacitors. Nano Energy 25, 193–202 (2016). https://doi.org/10.1016/j.nanoen.2016.04.037
J. Luo, H. Zhang, Z. Zhang, J. Yu, Z. Yang, In-built template synthesis of hierarchical porous carbon microcubes from biomass toward electrochemical energy storage. Carbon 155, 1–8 (2019). https://doi.org/10.1016/j.carbon.2019.08.044
C. Leng, Z. Zhao, Y. Song, L. Sun, Z. Fan et al., 3D carbon frameworks for ultrafast charge/discharge rate supercapacitors with high energy-power density. Nano-Micro Lett. 13, 8 (2021). https://doi.org/10.1007/s40820-020-00535-w
Y. Qing, Y. Jiang, H. Lin, L. Wang, A. Liu et al., Boosting the supercapacitor performance of activated carbon by constructing overall conductive networks using graphene quantum dots. J. Mater. Chem. A 7(11), 6021–6027 (2019). https://doi.org/10.1039/c8ta11620b
G.M. Tomboc, B. Tesfaye Gadisa, M. Jun, N.K. Chaudhari, H. Kim et al., Carbon transition-metal oxide electrodes: understanding the role of surface engineering for high energy density supercapacitors. Chem. Asian J. 15(11), 1628–1647 (2020). https://doi.org/10.1002/asia.202000324
B. Qu, C. Ma, G. Ji, C. Xu, J. Xu et al., Layered SnS2-reduced graphene oxide composite—a high-capacity, high-rate, and long-cycle life sodium-ion battery anode material. Adv. Mater. 26(23), 3854–3859 (2014). https://doi.org/10.1002/adma.201306314
X. Zhou, Z. Zhang, X. Lu, X. Lv, G. Ma et al., Sb2O3 nanoparticles anchored on graphene sheets via alcohol dissolution-reprecipitation method for excellent lithium-storage properties. ACS Appl. Mater. Interfaces 9(40), 34927–34936 (2017). https://doi.org/10.1021/acsami.7b10107
L. Liu, J. Lang, P. Zhang, B. Hu, X. Yan, Facile synthesis of Fe2O3 nano-dots@nitrogen-doped graphene for supercapacitor electrode with ultralong cycle life in koh electrolyte. ACS Appl. Mater. Interfaces 8(14), 9335–9344 (2016). https://doi.org/10.1021/acsami.6b00225
Y. Ko, D. Shin, B. Koo, S.W. Lee, W.-S. Yoon et al., Ultrathin supercapacitor electrodes with high volumetric capacitance and stability using direct covalent-bonding between pseudocapacitive nanoparticles and conducting materials. Nano Energy 12, 612–625 (2015). https://doi.org/10.1016/j.nanoen.2015.01.002
H. Jia, Z. Wang, C. Li, X. Si, X. Zheng et al., Designing oxygen bonding between reduced graphene oxide and multishelled Mn3O4 hollow spheres for enhanced performance of supercapacitors. J. Mater. Chem. A 7(12), 6686–6694 (2019). https://doi.org/10.1039/c8ta11482j
S. Zhu, M. Wu, M.-H. Ge, H. Zhang, S.-K. Li et al., Design and construction of three-dimensional CuO/polyaniline/RGO ternary hierarchical architectures for high performance supercapacitors. J. Power Sources 306, 593–601 (2016). https://doi.org/10.1016/j.jpowsour.2015.12.059
J. Zhang, L. Su, L. Ma, D. Zhao, C. Qin et al., Preparation of inflorescence-like acnf/pani/nio composite with three-dimension nanostructure for high performance supercapacitors. J. Electroanal. Chem. 790, 40–49 (2017). https://doi.org/10.1016/j.jelechem.2017.02.047
Q. Li, Y. Chen, J. Zhang, W. Tian, L. Wang et al., Spatially confined synthesis of vanadium nitride nanodots intercalated carbon nanosheets with ultrahigh volumetric capacitance and long life for flexible supercapacitors. Nano Energy 51, 128–136 (2018). https://doi.org/10.1016/j.nanoen.2018.06.053
S.N. Tiruneh, B.K. Kang, H.W. Choi, S.B. Kwon, M.S. Kim et al., Millerite core-nitrogen-doped carbon hollow shell structure for electrochemical energy storage. Small 14(41), 1802933 (2018). https://doi.org/10.1002/smll.201802933
F. Lai, J. Feng, R. Yan, G.-C. Wang, M. Antonietti et al., Breaking the limits of ionic liquid-based supercapacitors: mesoporous carbon electrodes functionalized with manganese oxide nanosplotches for dense, stable, and wide-temperature energy storage. Adv. Funct. Mater. 28(36), 1801298 (2018). https://doi.org/10.1002/adfm.201801298
R. Paul, F. Du, L. Dai, Y. Ding, Z.L. Wang et al., 3d heteroatom-doped carbon nanomaterials as multifunctional metal-free catalysts for integrated energy devices. Adv. Mater. 31(13), 1805598 (2019). https://doi.org/10.1002/adma.201805598
A. Gopalakrishnan, S. Badhulika, Effect of self-doped heteroatoms on the performance of biomass-derived carbon for supercapacitor applications. J. Power Sources 480, 228830 (2020). https://doi.org/10.1016/j.jpowsour.2020.228830
X. Wang, C. Yang, J. Li, X.A. Chen, K. Yang et al., Insights of heteroatoms doping-enhanced bifunctionalities on carbon based energy storage and conversion. Adv. Funct. Mater. 31(11), 2009109 (2020). https://doi.org/10.1002/adfm.202009109
K. Xiao, L.-X. Ding, G. Liu, H. Chen, S. Wang et al., Freestanding, hydrophilic nitrogen-doped carbon foams for highly compressible all solid-state supercapacitors. Adv. Mater. 28(28), 5997 (2016). https://doi.org/10.1002/adma.201601125
D.P. Dubal, S. Abdel-Azeim, N.R. Chodankar, Y.-K. Han, Molybdenum nitride nanocrystals anchored on phosphorus-incorporated carbon fabric as a negative electrode for high-performance asymmetric pseudocapacitor. Iscience 16, 50 (2019). https://doi.org/10.1016/j.isci.2019.05.018
M. Yang, Y. Zhong, X. Zhou, J. Ren, L. Su et al., Ultrasmall MnO@N-rich carbon nanosheets for high-power asymmetric supercapacitors. J. Mater. Chem. A 2(31), 12519–12525 (2014). https://doi.org/10.1039/c4ta02055c
C. Miao, X. Xiao, Y. Gong, K. Zhu, K. Cheng et al., Facile synthesis of metal-organic framework-derived CoSe2 nanoparticles embedded in the N-doped carbon nanosheet array and application for supercapacitors. ACS Appl. Mater. Interfaces 12(8), 9365–9375 (2020). https://doi.org/10.1021/acsami.9b22606
H.M. Jeong, J.W. Lee, W.H. Shin, Y.J. Choi, H.J. Shin et al., Nitrogen-doped graphene for high-performance ultracapacitors and the importance of nitrogen-doped sites at basal planes. Nano Lett. 11(6), 2472–2477 (2011). https://doi.org/10.1021/nl2009058
Y. Wen, B. Wang, C. Huang, L. Wang, D. Hulicova-Jurcakova, Synthesis of phosphorus-doped graphene and its wide potential window in aqueous supercapacitors. Chem. Eur. J. 21(1), 80–85 (2015). https://doi.org/10.1002/chem.201404779
J. Zhang, S. Ali, F. Liu, A. Ali, K. Wang et al., Phosphorus-doped carbon composites with rich graphene derived from phenol resin as supercapacitor electrode materials with high window potential and energy density. J. Electron. Mater. 48(7), 4196–4206 (2019). https://doi.org/10.1007/s11664-019-07188-5
J. Li, W. Liu, D. Xiao, X. Wang, Oxygen-rich hierarchical porous carbon made from pomelo peel fiber as electrode material for supercapacitor. Appl. Surface Sci. 416, 918–924 (2017). https://doi.org/10.1016/j.apsusc.2017.04.162
M. Krishnamoorthy, N. Jha, Oxygen-rich hierarchical porous graphene as an excellent electrode for supercapacitors, aqueous Al-ion battery, and capacitive deionization. ACS Sustain. Chem. Eng. 7(9), 8475–8489 (2019). https://doi.org/10.1021/acssuschemeng.9b00233
S. Ghosh, S. Barg, S.M. Jeong, K. Ostrikov, Heteroatom-doped and oxygen-functionalized nanocarbons for high-performance supercapacitors. Adv. Energy Mater. 10(32), 2001239 (2020). https://doi.org/10.1002/aenm.202001239
Z. Liu, S. Zhang, L. Wang, T. Wei, Z. Qiu et al., High-efficiency utilization of carbon materials for supercapacitors. Nano Select. 1(2), 244–262 (2020). https://doi.org/10.1002/nano.202000011
S. Zhao, W. Xu, Z. Yang, X. Zhang, Q. Zhang, One-pot hydrothermal synthesis of nitrogen and phosphorus co-doped graphene decorated with flower-like molybdenum sulfide for enhanced supercapacitor performance. Electrochim. Acta 331, 135265 (2020). https://doi.org/10.1016/j.electacta.2019.135265
L. Zheng, L. Guan, J. Song, H. Zheng, Rational design of a sandwiched structure Ni(OH)(2) nanohybrid sustained by amino-functionalized graphene quantum dots for outstanding capacitance. Appl. Surface Sci. 480, 727–737 (2019). https://doi.org/10.1016/j.apsusc.2019.02.243
L.-L. Jiang, X. Lu, C.-M. Xie, G.-J. Wan, H.-P. Zhang et al., Flexible, free-standing TiO2-graphene-polypyrrole composite films as electrodes for supercapacitors. J. Phys. Chem. C 119(8), 3903–3910 (2015). https://doi.org/10.1021/jp511022z
A. Ehsani, A.A. Heidari, H.M. Shiri, Electrochemical pseudocapacitors based on ternary nanocomposite of conductive polymer/graphene/metal oxide: an introduction and review to it in recent studies. Chem. Record 19(5), 908–926 (2019). https://doi.org/10.1002/tcr.201800112
Z. Xu, Z. Zhang, H. Yin, S. Hou, H. Lin et al., Investigation on the role of different conductive polymers in supercapacitors based on a zinc sulfide/reduced graphene oxide/conductive polymer ternary composite electrode. RSC Adv. 10(6), 3122–3129 (2020). https://doi.org/10.1039/c9ra07842h
H. Lin, Q. Huang, J. Wang, J. Jiang, F. Liu et al., Self-assembled graphene/polyaniline/Co3O4 ternary hybrid aerogels for supercapacitors. Electrochim. Acta 191, 444–451 (2016). https://doi.org/10.1016/j.electacta.2015.12.143
S.M. Zhu, H.A. Zhou, M. Hibino, I. Honma, M. Ichihara, Synthesis of MnO2 nanoparticles confined in ordered mesoporous carbon using a sonochemical method. Adv. Funct. Mater. 15(3), 381–386 (2005). https://doi.org/10.1002/adfm.200400222
X. Cao, B. Zheng, W. Shi, J. Yang, Z. Fan et al., Reduced graphene oxide-wrapped MoO3 composites prepared by using metal-organic frameworks as precursor for all-solid-state flexible supercapacitors. Adv. Mater. 27(32), 4695–4701 (2015). https://doi.org/10.1002/adma.201501310
J. Yang, X. Xu, X. Zhou, S. Jiang, W. Chen et al., Ultrasmall Co3O4 nanoparticles confined in P, N-doped carbon matrices for high-performance supercapacitors. J. Phys. Chem. C 124(17), 9225–9232 (2020). https://doi.org/10.1021/acs.jpcc.0c01539
X. Lu, T. Liu, T. Zhai, G. Wang, M. Yu et al., Improving the cycling stability of metal-nitride supercapacitor electrodes with a thin carbon shell. Adv. Energy Mater. 4(4), 1300994 (2014). https://doi.org/10.1002/aenm.201300994
S. Zhang, J. Wu, J. Wang, W. Qiao, D. Long et al., Constructing t-Nb2O5@carbon hollow core-shell nanostructures for high-rate hybrid supercapacitor. J. Power Sources 396, 88–94 (2018). https://doi.org/10.1016/j.jpowsour.2018.06.007
M. Pan, W. Zeng, H. Quan, J. Cui, Y. Guo et al., Low-crystalline Ni/Co-oxyhydroxides nanoarrays on carbon cloth with high mass loading and hierarchical structure as cathode for supercapacitors. Electrochim. Acta 357, 136886 (2020). https://doi.org/10.1016/j.electacta.2020.136886
J. Theerthagiri, R.A. Senthil, P. Nithyadharseni, S.J. Lee, G. Durai et al., Recent progress and emerging challenges of transition metal sulfides based composite electrodes for electrochemical supercapacitive energy storage. Ceram. Int. 46(10), 14317–14345 (2020). https://doi.org/10.1016/j.ceramint.2020.02.270
M. Sun, B. Lan, L. Yu, F. Ye, W. Song et al., Manganese oxides with different crystalline structures: Facile hydrothermal synthesis and catalytic activities. Mater. Lett. 86, 18–20 (2012). https://doi.org/10.1016/j.matlet.2012.07.011
X. Ma, P. Zhang, Y. Zhao, Y. Liu, J. Li et al., Role of n doping on the electrochemical performances of ZnCo2O4 quantum dots/reduced graphene oxide composite nanosheets. Chem. Eng. J. 327, 1000–1010 (2017). https://doi.org/10.1016/j.cej.2017.06.084
I. Shakir, A. Rasheed, S. Haider, M.F.A. Aboud, The impact of Cu2+ and Mg2+ onto the electrochemical energy storage properties of nanocrystalline Co0.8Ni0.2Fe2O4 particles and their hybrids with graphene. Ceram. Int. 45(14), 18099–18105 (2019). https://doi.org/10.1016/j.ceramint.2019.05.066
D. Majumdar, Review on current progress of MnO2-based ternary nanocomposites for supercapacitor applications. ChemElectroChem 8(2), 291–336 (2020). https://doi.org/10.1002/celc.202001371
J.H. Zhong, A.L. Wang, G.R. Li, J.W. Wang, Y.N. Ou et al., Co3O4/Ni(OH)(2) composite mesoporous nanosheet networks as a promising electrode for supercapacitor applications. J. Mater. Chem. 22(12), 5656–5665 (2012). https://doi.org/10.1039/c2jm15863a
C. Xu, Z. Li, C. Yang, P. Zou, B. Xie et al., An ultralong, highly oriented nickel-nanowire-array electrode scaffold for high-performance compressible pseudocapacitors. Adv. Mater. 28(21), 4105–4110 (2016). https://doi.org/10.1002/adma.201505644
X. Zang, C. Shen, E. Kao, R. Warren, R. Zhang et al., Titanium disulfide coated carbon nanotube hybrid electrodes enable high energy density symmetric pseudocapacitors. Adv. Mater. 30(5), 1704754 (2018). https://doi.org/10.1002/adma.201704754
C. Wang, L. Zhang, M. Li, J. Zhang, Y. Chen et al., Sub-nanometer, ultrafine alpha-Fe2O3 sheets realized by controlled crystallization kinetics for stable, high-performance energy storage. Chem. Eur. J. 25(19), 5005–5013 (2019). https://doi.org/10.1002/chem.201805593
W. Liu, H. Niu, J. Yang, K. Cheng, K. Ye et al., Ternary transition metal sulfides embedded in graphene nanosheets as both the anode and cathode for high-performance asymmetric supercapacitors. Chem. Mater. 30(3), 1055–1068 (2018). https://doi.org/10.1021/acs.chemmater.7b04976
S. Wang, Z. Xiao, S. Zhai, H. Wang, W. Cai et al., Construction of strawberry-like Ni3S2@Co9S8 heteronanoparticle-embedded biomass-derived 3d n-doped hierarchical porous carbon for ultrahigh energy density supercapacitors. J. Mater. Chem. A 7(29), 17345–17356 (2019). https://doi.org/10.1039/c9ta05145g
Y. Yang, Y. Zheng, W. Cao, A. Titov, J. Hyvonen et al., High-efficiency light-emitting devices based on quantum dots with tailored nanostructures. Nat. Photonics 9(4), 259–266 (2015). https://doi.org/10.1038/nphoton.2015.36
T. Shen, J. Yuan, X. Zhong, J. Tian, Dip-coated colloidal quantum-dot films for high-performance broadband photodetectors. J. Mater. Chem. C 7(21), 6266–6272 (2019). https://doi.org/10.1039/c9tc00079h
H. Moon, C. Lee, W. Lee, J. Kim, H. Chae, Stability of quantum dots, quantum dot films, and quantum dot light-emitting diodes for display applications. Adv. Mater. 31(34), 1804294 (2019). https://doi.org/10.1002/adma.201804294
J. Zhou, Y. Yang, C.-Y. Zhang, Toward biocompatible semiconductor quantum dots: from biosynthesis and bioconjugation to biomedical application. Chem. Rev. 115(21), 11669–11717 (2015). https://doi.org/10.1021/acs.chemrev.5b00049
P. Wu, Y. Xu, J. Zhan, Y. Li, H. Xue et al., The research development of quantum dots in electrochemical energy storage. Small 14(42), 1801479 (2018). https://doi.org/10.1002/smll.201801479
S. Liu, J. Zhou, Z. Cai, G. Fang, Y. Cai et al., Nb2O5 quantum dots embedded in mof derived nitrogen-doped porous carbon for advanced hybrid supercapacitor applications. J. Mater. Chem. A 4(45), 17838–17847 (2016). https://doi.org/10.1039/c6ta07856g
E. Pomerantseva, F. Bonaccorso, X. Feng, Y. Cui, Y. Gogotsi, Energy storage: The future enabled by nanomaterials. Science 366(6468), 969 (2019). https://doi.org/10.1126/science.aan8285
S. Liu, Y. Yin, D. Ni, K.S. Hui, M. Ma et al., New insight into the effect of fluorine doping and oxygen vacancies on electrochemical performance of Co2MnO4 for flexible quasi-solid-state asymmetric supercapacitors. Energy Storage Mater. 22, 384–396 (2019). https://doi.org/10.1016/j.ensm.2019.02.014
Q. Chen, J. Jin, Z. Kou, J. Jiang, Y. Fu et al., Cobalt-doping in hierarchical Ni(3)S(2)nanorod arrays enables high areal capacitance. J. Mater. Chem. A 8(26), 13114–13120 (2020). https://doi.org/10.1039/d0ta04483k
J. Zhang, Y. Wang, H.-J. Liao, T.-Y. Yang, Z. Chen et al., Hierarchical mn-doped Fe2O3@RGO hollow core-shell spheres for high-performance hybrid capacitor. Mater. Today Energy 17, 100388 (2020). https://doi.org/10.1016/j.mtener.2020.100388
S. Pang, L. Gong, N. Du, H. Luo, K. Yu et al., Formation of high-performance Cu-WOx@C tribasic composite electrode for aqueous symmetric supercapacitor. Mater. Today Energy 13, 239–248 (2019). https://doi.org/10.1016/j.mtener.2019.05.016
W. Liu, Z. Zhang, Y. Zhang, Y. Zheng, N. Liu et al., Interior and exterior decoration of transition metal oxide through Cu0/Cu+ Co-doping strategy for high-performance supercapacitor. Nano-Micro Lett. 13, 61 (2021). https://doi.org/10.1007/s40820-021-00590-x
B. Zhao, L. Zhang, Q. Zhang, D. Chen, Y. Cheng et al., Rational design of nickel hydroxide-based nanocrystals on graphene for ultrafast energy storage. Adv. Energy Mater. 8(9), 1702247 (2018). https://doi.org/10.1002/aenm.201702247
A.M. Mohamed, A.O.A. El Naga, T. Zaki, H.B. Hassan, N.K. Allam, Bimetallic co-w-s chalcogenides confined in n, s-codoped porous carbon matrix derived from metal-organic frameworks for highly stable electrochemical supercapacitors. ACS Appl. Energy Mater. 3(8), 8064–8074 (2020). https://doi.org/10.1021/acsaem.0c01513
M. Yu, Z. Wang, C. Hou, Z. Wang, C. Liang et al., Nitrogen-doped Co3O4 mesoporous nanowire arrays as an additive-free air-cathode for flexible solid-state zinc-air batteries. Adv. Mater. 29(15), 1602868 (2017). https://doi.org/10.1002/adma.201602868
S. Liu, D. Gao, J. Li, K. San Hui, Y. Yin et al., Phosphorus dual-site driven Cos2@S, N co-doped porous carbon nanosheets for flexible quasi-solid-state supercapacitors. J. Mater. Chem. A 7(46), 26618–26630 (2019). https://doi.org/10.1039/c9ta09646a
Z. Hu, Z. Wu, C. Han, J. He, Z. Ni et al., Two-dimensional transition metal dichalcogenides: Interface and defect engineering. Chem. Soc. Rev. 47(9), 3100–3128 (2018). https://doi.org/10.1039/c8cs00024g
X. Zhang, X. Liu, Y. Zeng, Y. Tong, X. Lu, Oxygen defects in promoting the electrochemical performance of metal oxides for supercapacitors: Recent advances and challenges. Small Methods 4(6), 1900823 (2020). https://doi.org/10.1002/smtd.201900823
D. Yao, F. Wang, W. Lei, Y. Hua, X. Xia et al., Oxygen vacancies boosting ultra-stability of mesoporous ZnO-CoO@n-doped carbon microspheres for asymmetric supercapacitors. Sci. China Mater. 63(10), 2013–2027 (2020). https://doi.org/10.1007/s40843-020-1357-9
L. Su, S. Lei, L. Liu, L. Liu, Y. Zhang et al., Sprinkling MnFe2O4 quantum dots on nitrogen-doped graphene sheets: The formation mechanism and application for high-performance supercapacitor electrodes. J. Mater. Chem. A 6(21), 9997–10007 (2018). https://doi.org/10.1039/c8ta02982b
H. Zeng, M.H. Oubla, X. Zhong, N. Alonso-Vante, F. Du et al., Rational defect and anion chemistries in Co3O4 for enhanced oxygen evolution reaction. Appl. Catal. B-Environ. 281, 119535 (2021). https://doi.org/10.1016/j.apcatb.2020.119535
C. Ren, X. Jia, W. Zhang, D. Hou, Z. Xia et al., Hierarchical porous integrated Co1-xS/CoFe2O4@RGO nanoflowers fabricated via temperature-controlled in situ calcining sulfurization of multivariate CoFe-MOF-74@RGO for high-performance supercapacitor. Adv. Funct. Mater. 30(45), 2004519 (2020). https://doi.org/10.1002/adfm.202004519
H.-S. Kim, J.B. Cook, H. Lin, J.S. Ko, S.H. Tolbert et al., Oxygen vacancies enhance pseudocapacitive charge storage properties of MoO3-x. Nat. Mater. 16(4), 454 (2017). https://doi.org/10.1038/nmat4810
J. Yang, X. Xiao, P. Chen, K. Zhu, K. Cheng et al., Creating oxygen-vacancies in MoO3-x nanobelts toward high volumetric energy-density asymmetric supercapacitors with long lifespan. Nano Energy 58, 455–465 (2019). https://doi.org/10.1016/j.nanoen.2019.01.071
S. Yang, Y. Liu, Y. Hao, X. Yang, W.A. Goddard et al., Oxygen-vacancy abundant ultrafine Co3O4/graphene composites for high-rate supercapacitor electrodes. Adv. Sci. 5(4), 1700659 (2018). https://doi.org/10.1002/advs.201700659
Q.-L. Wu, S.-X. Zhao, L. Yu, X.-X. Zheng, Y.-F. Wang et al., Oxygen vacancy-enriched MoO3-x nanobelts for asymmetric supercapacitors with excellent room/low temperature performance. J. Mater. Chem. A 7(21), 13205–13214 (2019). https://doi.org/10.1039/c9ta03471d
X. Zheng, G. Wang, F. Huang, H. Liu, C. Gong et al., Liquid phase exfoliated hexagonal boron nitride/graphene heterostructure based electrode toward asymmetric supercapacitor application. Front. Chem. 7, 00544 (2019). https://doi.org/10.3389/fchem.2019.00544
Z. Gao, C. Chen, J. Chang, L. Chen, P. Wang et al., Porous Co3S4@Ni3S4 heterostructure arrays electrode with vertical electrons and ions channels for efficient hybrid supercapacitor. Chem. Eng. J. 343, 572–582 (2018). https://doi.org/10.1016/j.cej.2018.03.042
S. Saha, P. Samanta, N.C. Murmu, T. Kuila, A review on the heterostructure nanomaterials for supercapacitor application. J. Energy Storage 17, 181–202 (2018). https://doi.org/10.1016/j.est.2018.03.006
J.-C. Liu, Z.-H. Huang, T.-Y. Ma, Aqueous supercapacitor with ultrahigh voltage window beyond 2.0 volt. Small Struct. 1(1), 2000020 (2020). https://doi.org/10.1002/sstr.202000020
L. Wan, C. He, D. Chen, J. Liu, Y. Zhang et al., In situ grown NiFeP@NiCo2S4 nanosheet arrays on carbon cloth for asymmetric supercapacitors. Chem. Eng. J. 399, 125778 (2020). https://doi.org/10.1016/j.cej.2020.125778
Y. Yan, A. Li, C. Lu, T. Zhai, S. Lu et al., Double-layered yolk-shell microspheres with NiCo2S4-Ni9S8-C hetero-interfaces as advanced battery-type electrode for hybrid supercapacitors. Chem. Eng. J. 396, 125316 (2020). https://doi.org/10.1016/j.cej.2020.125316
T. Dang, D. Wei, G. Zhang, L. Wang, Q. Li et al., Homologous NiCoP/CoP hetero-nanosheets supported on N-doped carbon nanotubes for high-rate hybrid supercapacitors. Electrochim. Acta 341, 135988 (2020). https://doi.org/10.1016/j.electacta.2020.135988
Acknowledgements
This work was supported by the National Natural Science Foundation of China (Nos. 51972342, and 51872056), Taishan Scholar Project of Shandong Province (ts20190922), Key Basic Research Project of Natural Science Foundation of Shandong Province (ZR2019ZD51), Project funded by China Postdoctoral Science Foundation (2019TQ0353 and 2020M672165), Fundamental Research Funds for the Central Universities (20CX06024A), Shandong Provincial Natural Science Foundation, China (ZR201911040344).
Author information
Authors and Affiliations
Corresponding authors
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Ren, K., Liu, Z., Wei, T. et al. Recent Developments of Transition Metal Compounds-Carbon Hybrid Electrodes for High Energy/Power Supercapacitors. Nano-Micro Lett. 13, 129 (2021). https://doi.org/10.1007/s40820-021-00642-2
Received:
Accepted:
Published:
DOI: https://doi.org/10.1007/s40820-021-00642-2