Highlights
-
Fe single atoms supported on porous carbon nanofiber are prepared by spatial confinement.
-
The iron single atoms supported on porous nitrogen-doped carbon nanofibers (FeSAs-NCF) can promote the reversible conversion between aluminum polysulfides.
-
The FeSAs-NCF can chemically anchor the polysulfides to suppress shuttle effect.
Abstract
Rechargeable aluminum–sulfur (Al–S) batteries have been considered as a highly potential energy storage system owing to the high theoretical capacity, good safety, abundant natural reserves, and low cost of Al and S. However, the research progress of Al–S batteries is limited by the slow kinetics and shuttle effect of soluble polysulfides intermediates. Herein, an interconnected free-standing interlayer of iron single atoms supported on porous nitrogen-doped carbon nanofibers (FeSAs-NCF) on the separator is developed and used as both catalyst and chemical barrier for Al–S batteries. The atomically dispersed iron active sites (Fe–N4) are clearly identified by aberration-corrected high-angle annular dark-field scanning transmission electron microscopy and X-ray absorption near-edge structure. The Al–S battery with the FeSAs-NCF shows an improved specific capacity of 780 mAh g−1 and enhanced cycle stability. As evidenced by experimental and theoretical results, the atomically dispersed iron active centers on the separator can chemically adsorb the polysulfides and accelerate reaction kinetics to inhibit the shuttle effect and promote the reversible conversion between aluminum polysulfides, thus improving the electrochemical performance of the Al–S battery. This work provides a new way that can not only promote the conversion of aluminum sulfides but also suppress the shuttle effect in Al–S batteries.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
1 Introduction
Metal–sulfur batteries, using sulfur as a cathode material coupled with metal anodes, have become one of the most highly potential energy storage systems due to the high energy density, rich raw materials, low cost and environmental-friendliness [1]. Currently, various metal–sulfur batteries have been reported, and lithium–sulfur batteries are the most extensively studied. Although lithium–sulfur battery can offer a high theoretical capacity, the high cost of lithium anode arose from the finite lithium resource and the safety issue arose from lithium dendrite formation hindering the practical application [2,3,4]. Aluminum as the most abundant metal element in the crust can couple with sulfur to fabricate rechargeable aluminum–sulfur (Al–S) batteries, in which both aluminum and sulfur are cheap and environmentally friendly materials with good air stability and safety. More importantly, both Al and S electrodes have high theoretical specific capacities of 2976 and 1672 mAh g−1, respectively [5,6,7]. A rechargeable Al–S battery can deliver a theoretical cell capacity of 1072 mAh g−1 based on total electrode mass and operate at a voltage of 1.25 V, resulting in a theoretical energy density of 1340 Wh kg−1 [8]. Therefore, Al–S batteries are promising for large-scale energy storage.
Rechargeable Al–S battery was first proposed in 2015, and a high specific capacity was delivered; however it could only run a few cycles [9]. Since then, various electrode materials and electrolytes were explored to boost electrochemical performances of Al–S batteries [8, 10,11,12,13,14,15,16,17,18,19]. Currently, the main problems of Al–S batteries are slow kinetic response and short cycle life. The slow kinetics is mainly caused by the charge transfer reaction between sulfur and Al and the dissociation barrier of the aluminum species [6, 11, 20]. The short cycle life is caused by the following reasons: (1) the aluminum polysulfides intermediate products can dissolve in the electrolyte and shuttle to the Al anode, leading to the loss of active sulfur; (2) the slow kinetic response of reversible conversion between Al2S3 and S causes gradual sulfur loss, further leading to poor life-span; (3) the strong bond energy of Al–S may cause incomplete reaction of Al2S3, which also shortens the cycle life [8, 9, 21]. At present, different strategies have been proposed to address the above problems. One is using other halogen anions to replace chloride ions in electrolytes to lower the dissociation barrier of aluminum ion clusters. For example, the brominated electrolyte could increase the reaction kinetics, because the energy barrier of releasing Al3+ was lower than that of Al2Cl7− [11]. The second is introducing catalysts to promote the conversion of aluminum polysulfides during charge/discharge processes. Wan and co-workers fabricated a Cu/Co-porous carbon composite, in which Cu and Co species as active centers promoted the conversion of aluminum polysulfides during the charge–discharge processes. Specifically, the Cu formed an ionic cluster with polysulfide to facilitate the reversibility of S, while the Co contributed to form cobalt sulfides, and the assembled Al–S battery showed an enhanced cycle performance [22, 23]. The third is adding chemical or physical barriers to suppress the dissolution of aluminum polysulfides [24]. The strong interactions between lithium polysulfides and heteroatoms doped carbon or polymeric carbon nitride have been discussed and confirmed in order to anchor polysulfides [25,26,27]. Stimulated by these research approaches of covalent binding and ionic association in lithium–sulfur batteries [28,29,30], similar approaches can also be learned to effectively capture polysulfides and inhibit shuttle effect for Al–S batteries. However, it is difficult to solve the issues of slow kinetics and short cycle life concurrently through the above approaches. Therefore, it is necessary to find a way that can not only reduce the dissociation barrier of aluminum ion clusters and promote the conversion of aluminum sulfides but also suppress the shuttle effect, simultaneously.
Recently, isolated single atoms supported on carbon matrix have been regarded as efficient catalysts for electrocatalysis (e.g., oxygen reduction reaction) due to the unique structure, highly dispersed active sites and the maximum atomic utilization [31, 32]. Organic metallic materials with isolated metal sites are also promising for batteries, and the organic aluminum compound with Al–O coordination can modulate the deposition of lithium [33]. Single atom catalysts (SACs) were employed in lithium–sulfur batteries for enhancing electrochemical performance through the strong interaction between single atoms and lithium polysulfides [34, 35]. Inspired by this, it is expected that an interconnected free-standing interlayer composed of SACs with distinctive electronic structure on the separator may not only accelerate the charge transfer between aluminum and sulfur but also chemically interact with aluminum polysulfides and physically block soluble aluminum polysulfides to suppress the shuttle effect [32].
Herein, iron single atoms supported on porous nitrogen-doped carbon nanofibers (FeSAs-NCF) with free-standing network are fabricated and directly coated onto the separator to form the interlayer of Al–S batteries. The iron single atoms are clearly identified by HAADF-STEM and XANES. The Al–S battery with the FeSAs-NCF shows an improved specific capacity and enhanced cycle stability, as the specific capacity remains 320 mAh g−1 at a current density of 1000 mA g−1 after 500 cycles. The improved electrochemical performance is explained that the atomically dispersed iron active centers can promote the reversible conversion between aluminum polysulfides to accelerate reaction kinetics, stabilize aluminum anode, chemically anchor the polysulfides and physically block soluble aluminum polysulfides to suppress the shuttle effect, which are evidenced by the experimental and theoretical results.
2 Experimental and Calculation
2.1 Synthesis of FeSAs-NCF
The precursor of FeSAs-CNF was first prepared (see Supporting Information). The obtained nanofibers were pre-oxidized at 250 °C with a heating rate of 1 °C min−1 in air for 2 h. The samples were then carbonized by utilizing a plasma enhanced chemical vapor deposition (PECVD) system. The obtained samples were treated by N2 plasma (plasma power of 300 W) at 500 °C (2 °C min−1) for 5 min a pressure of 12.9 Pa and then calcinated at 920 °C (2 °C min−1) for 2 h under N2 atmosphere.
2.2 Preparation of S Cathodes
First, the composite of S and carbon nanofibers (S@CNF) was obtained by heating the mixture of the both at 155 °C for 12 h, and the content of sulfur is 69%. The as-prepared S@CNF was mixed with carbon black and polyvinylidene fluoride (PVDF), in methylpyrrolidone (NMP). Then, the S@CNF slurry was casted onto Mo foil, which was used as the current collector due to the high corrosion resistance to ionic liquids.
2.3 Modification of Separator
The sheet shape of FeSAs-NCF (Fig. S1) was directly coated onto the Whatman GF/D glass fiber separator and then punched into the disks with a diameter of 14 mm.
2.4 Electrochemical Measurements
The Al–S batteries were assembled in Swagelok-type cells. Al foil was used as the anode, the separator was Whatman GF/D, and the electrolyte was [EMIM]Cl/AlCl3 (mole ratio: 1:1.3); the cells were assembled in glovebox (O2, H2O < 1 ppm). Galvanostatic charge/discharge was performed within the voltage range between 0.01 and 1.8 V. The cells were measured using a LAND battery system under different current densities. Before long-term cycling, the assembled battery firstly was run for two cycles. Electrochemical impedance spectroscopy (EIS) was performed within the frequency range from 1 MHz to 0.01 Hz (Gamry REF 600).
2.5 Calculation
All theoretical calculations were carried out in the Vienna ab-initio simulation package (VASP) using projector augmented wave (PAW) method to gain the system energy and structural information. The generalized gradient approximation (GGA) with the Perdew–Burke–Ernzerhof (PBE) functional was adopted in all calculations. A supercell of graphene containing 6 × 6 × 1 unit cells was used in all graphene-based systems. In the vertical direction, a vacuum layer of about 15 Å in thickness was introduced in the surfaces for all composite systems (polysulfide and graphene-based systems). The cutoff energy was set at 520 eV, and total energy convergence was set to be lower than 1 × 10−5 eV. The first Brillouin zone was sampled with a k-points mesh of 3 × 3 × 3 Gamma-centered grids for the structural relaxation.
3 Results and Discussion
The synthesis of the FeSAs-NCF is shown schematically in Fig. 1a. First, polyacrylonitrile (PAN), iron phenanthroline (Fe-Phen), and zinc oxide nanoparticles were dispersed in dimethylformamide and electrospun to obtain a piece of PAN-based cloth, and then it was pyrolyzed with the aid of N2 plasma. During the plasma-assisted pyrolysis, the PAN was converted to porous nitrogen-doped carbon nanofibers, and all the Fe-Phen was converted to Fe single atoms coordinated with nitrogen atoms. Meanwhile, the zinc oxide nanoparticles were reduced and volatilized to leave a large number of pores in the nanofibers. As a result, a sheet of FeSAs-NCF was successfully obtained (Fig. S1) and FeSAs-NCF coating on the separator can form the physical barrier to alleviate the shuttle effect. To further analyze the FeSAs-NCF, it displays nanofiber structure and there are abundant pores inside the nanofibers (Fig. 1b-c) through the scanning electron microscopy images (SEM). The one-dimensional porous nanofiber structure can facilitate to expose more active sites, shorten ion diffusion path and accelerate electron transfer to enhance electrochemical performance. The porous structure with a pore size of approximately 250 nm is further confirmed by the representative transmission electron microscopy (TEM) image in Fig. 1d. Additionally, there are no particles observed in the SEM or TEM images, suggesting the possible formation of Fe single atoms. The corresponding selected area electron diffraction (SAED) also suggests the absence of Fe-related crystal phase (Fig. S2), further confirming the formation of Fe single atoms. HAADF-STEM images display the homogeneously distributed Fe single atoms (Fig. 1e-f), which are clearly identified throughout the carbon nanofibers in the enlarged image (marked in yellow circles in Fig. 1f). Additionally, the elemental mappings of the FeSAs-NCF evidence the homogeneous distribution of Fe, C and N in the nanofibers (Fig. 1g). The mass loading of iron single atoms was determined to be 2.94 wt% by inductively coupled plasma-mass spectrometry. These a large number of iron atoms with highly dispersed state can maximize atomic utilization and act as active sites to improve the electrochemical performance.
The FeSAs-NCF displays the identical XRD pattern of the NCF, and the two diffraction peaks of graphitic carbon are assigned to the (002) and (101) crystal planes (Fig. 2a) [36]. The absence of any Fe-related phase confirms the atomic dispersion of Fe in the N-doped carbon nanofibers, which is in good accordance with the STEM observation. The specific surface area of the FeSAs-NCF is 227.8 m2 g−1 estimated from nitrogen adsorption–desorption isotherm (Fig. S3), and the mesopores with the main pore size of ~ 30 nm mainly exist in the FeSAs-NCF (Fig. S4). Furthermore, the FeSAs-NCF displays a larger ID/IG value (1.00) than that of the NCF (0.91), demonstrating that the defective degree is enhanced by introducing the iron single atoms (Fig. 2b). The result of X-ray photoelectron spectroscopy (XPS) could confirm iron, nitrogen, and carbon elements in the FeSAs-NCF (Fig. S5). The N 1s XPS of the NCF is divided into four component peaks at 398.1, 399.8, 401.2, and 402.4 eV, which are assigned to pyridinic N, pyrrolic N, graphitic N, and oxidized N, respectively (Fig. 2c) [37, 38]. Compared with the NCF, an additional peak of N 1s of the FeSAs-NCF appears at 398.8 eV, which is identified as Fe–N bond [37, 38]. XANES was used to further identify the electronic structure and coordination of the FeSAs-NCF. Figure 2d shows the Fe K-edge XANES spectra of the FeSAs-NCF, Fe foil, and FePc. The near-edge absorption energy of Fe in the FeSAs-NCF is close to that of FePc but totally different from that of Fe foil, demonstrating that the Fe is atomically dispersed and coordinated with N as Fe–N4 [39, 40]. The small peak at ~ 7113.5 eV is associated with the transition from 1s to 4pz, implying the existence of Fe–N4 configuration [41, 42]. The Fourier transformed (FT) k2-weighted-EXAFS spectra of FeSAs-NCF, Fe foil, and FePc are displayed in Fig. 2e, and the main peak at 1.6 Å of the FeSAs-NCF is attributed to the Fe–N coordination [41, 42]. The obtained Fourier transformed (FT) k2-weighted-EXAFS spectrum was fitted to identify the coordination number of Fe in the FeSAs-NCF. The calculated coordination number of Fe–N is ~ 3.52 in the first shell of Fe atoms for FeSAs-NCF (Fig. S6 and Table S1). The wavelet transform-EXAFS (WT-EXAFS) of Fe k-edge was performed to further distinguish the dispersion of Fe in the FeSAs-NCF. The WT contour plot of the FeSAs-NCF only shows the maximum intensity peak at 5 Å−1 (Fig. 2f), and this maximum intensity peak is similar to that of FePc but different from that of Fe foil (Fig. S7), further confirming the Fe–N coordination. The results clearly evidence the Fe sites are atomically dispersed with the coordination of Fe–N4 in the FeSAs-NCF.
Al–S batteries with various modified separators were assembled and evaluated to verify the catalysis and anchor roles of FeSAs-NCF. The thickness of the FeSAs-NCF layer on the separator is ~ 30 μm (Fig. S8). The representative cyclic voltammetry (CV) curves clearly demonstrate the reversible redox reactions between aluminum and sulfur in the Al–S batteries (Fig. 3a) [23]. Meanwhile, the Al–S battery with the FeSAs-NCF displays larger redox peak current densities and a smaller peak potential separation than the cell with NCF and the blank cell, demonstrating the FeSAs-NCF can facilitate the redox reaction between Al and S and accelerate the redox kinetics of converting sulfur into aluminum sulfides. Additionally, the larger peak current densities of the Al–S battery with FeSAs-NCF indicate a higher conversion efficiency between sulfur and aluminum sulfides, which can boost the utilization of S and retard the shuttle effect of soluble aluminum polysulfides. The role of FeSAs-NCF in promoting charge transfer capability was evaluated by electrochemical impedance spectroscopy (EIS). The fitted Nyquist plots clearly indicate that the charge transfer resistance (Rct) of the Al–S battery with FeSAs-NCF is much smaller than that with the NCF and that of the blank one (Fig. 3b and Table S2), revealing the FeSAs-NCF can boost charge transfer capability of the Al–S battery. Then, the diffusion coefficients were calculated from the Nyquist plots in Fig. 3b to further evaluate reaction kinetics, and the diffusion coefficients of cells with FeSAs-NCF, NCF and blank separators are 9.63 × 10–15, 2.70 × 10–15, and 7.43 × 10–16 cm2 s−1 (see details in Supporting Information). Meanwhile, the ion diffusion coefficient was also studied by galvanostatic intermittent titration technique (Fig. S9), and the results display that the ratio of D1 (the cell with FeSAs-NCF) to D2 (the blank cell) is greater than 1, further revealing that the FeSAs-NCF can accelerate the ion diffusion to contribute to fast reaction kinetic.
The typical galvanostatic charge/discharge curves display that the cell with FeSAs-NCF shows a higher discharge voltage and delivers a larger discharge capacity than the cell with NCF and the blank cell (Fig. 3c). Furthermore, the cell with FeSAs-NCF displays the highest discharge voltage of 0.75 V, and this high discharge voltage plateau can still retain after 100 cycles (Fig. S10). Moreover, the cell with FeSAs-NCF obviously possesses a lower electrochemical polarization than the cell with NCF and blank cell, indicating the lowest energy barrier of the conversion reaction between charge and discharge products. Figure 3d shows that the cell with FeSAs-NCF delivers an initial capacity of 1130 mAh g−1 at 100 mA g−1 and remains a stable capacity of 780 mAh g−1 after 100 cycles. However, the battery with NCF and blank cell only remain the specific capacities of 280 and 70 mAh g−1 after 100 cycles, respectively. Furthermore, the battery with FeSAs-NCF demonstrates good cycling stability and the specific capacity reaches 320 mAh g−1 at a high current density of 1000 mA g−1 after 500 cycles (Fig. 3e). The Coulombic efficiency is approximately 90% upon cycling, and the possible reasons can be explained that: (1) the dissolution of discharge product polysulfides may not be completely suppressed, and there is still a small number of polysulfides migrating to the negative electrode side; (2) the discharge product Al2S3 is not fully oxidized due to the non-conducive nature. Additionally, the Al–S battery performances were compared with others reported in recent literature (Table S3), and the results display that combination of specific capacity and cycling stability in this work surpasses most of others. The enhanced electrochemical performance is explained that the FeSAs-NCF can accelerate reaction kinetics and chemically adsorb the polysulfides to promote the reversible conversion between aluminum polysulfides and inhibit the shuttle effect.
The roles of FeSAs-NCF in catalyzing aluminum polysulfides and suppressing shuttle effect of the Al–S batteries were further investigated. Firstly, the morphologies of the anodes after cycling were analyzed. In the cells without FeSAs-NCF, the surfaces of the Al anodes after cycling are uneven and dark (Fig. S11), which is ascribed to the uneven dissolution and deposition of aluminum and the irreversible reactions of the soluble aluminum polysulfides caused by the shuttle effect. Meanwhile, in the Al–S cell with FeSAs-NCF, there is no obvious change of the Al anode surface after cycling, revealing that the shuttle effect is suppressed by the FeSAs-NCF, and the FeSAs interlayer contributes to the homogenization of aluminum deposition. A close observation displays that there are a large number of irregular holes in the Al anodes from the cell with NCF and the blank cell (Fig. S12), which is caused by the uneven dissolution and deposition of aluminum during charge–discharge process. The difference in the surface morphologies reveals that the FeSAs-NCF can induce well-distributed deposition of aluminum. The EDS mappings reveal that the sulfur-containing species were deposited on the Al anode without the addition of FeSAs-NCF (Fig. S13), inferring that the soluble aluminum polysulfides shuttled to the Al anode. To further verify the adsorption capacity of FeSAs-NCF on polysulfides, the permeation test was conducted for visualization using H-type cell. When the blank separator was used, the color of the solution in right chamber gradually gets darker (Fig. S14). However, there is no noticeable color change in right chamber after 48 h when the FeSAs-NCF was used, revealing the strong adsorption capacity of FeSAs-NCF on polysulfides. The results confirm that the strong barrier effect of the FeSAs-NCF to chemically anchor the soluble aluminum polysulfides. Subsequently, the electrolytes in Al–S batteries with and without FeSAs-NCF layer after cycling were collected and measured by ultraviolet spectrophotometer (UV–Vis). The UV–Vis spectra of the electrolytes in the cells with and without FeSAs-NCF collected at 1.8 V appear the same absorption peak at ~ 290 nm, which is assigned to the absorption peak of \({\mathrm{S}}_{6}^{2-}\)(Fig. 4a) [22, 23, 43]. The difference is that the electrolyte in the cell with FeSAs-NCF shows another absorption peak at ~ 465 nm, corresponding to \({\mathrm{S}}_{4}^{2-}\) polysulfide in the electrolyte [22, 23, 43]. The high yield of \({\mathrm{S}}_{4}^{2-}\) polysulfide is possibly because the Fe–N4 active centers are more beneficial to catalyze \({\mathrm{S}}_{8}\) into \({\mathrm{S}}_{4}^{2-}\) than \({\mathrm{S}}_{8}\) into \({\mathrm{S}}_{6}^{2-}\) [22, 23, 43]. Additionally, compared with the pristine FeSAs-NCF, the Raman spectrum of the FeSAs-NCF collected at 1.8 V displays two additional light peaks within the range of 250–600 cm−1, which is ascribed to the chemically adsorbed polysulfides (\({\mathrm{S}}_{\mathrm{n}}^{2-}\)). The result clearly confirms the adsorption of polysulfides on the FeSAs-NCF [44]. Then, the aluminum polysulfide (\({\mathrm{S}}_{6}^{2-}\)) was prepared and employed to assemble symmetric cells to further evaluate the catalytic role of the FeSAs-NCF (Fig. S15). The CV curve of the FeSAs-NCF symmetric cell shows two obvious reduction peaks at −0.25 V and −0.90 V compared with that in the electrolyte without \({\mathrm{S}}_{6}^{2-}\), which are identified as the reduction of \({\mathrm{S}}_{6}^{2-}\) to Al2S3 (Fig. 4c). However, there are almost no such reduction peaks in the CV curve of the symmetric cell with NCF. The result further confirms that the FeSAs-NCF can catalytic the reduction of \({\mathrm{S}}_{6}^{2-}\). Another symmetric cell with FeSAs-NCF/Al2S3 as both anode and cathode was also studied. The corresponding CV curve displays that the peak current densities of the FeSAs-NCF/Al2S3 symmetric cell are much larger than that of the NCF/Al2S3 cell, indicating that the FeSAs-NCF can obviously accelerate the reaction rate of the Al2S3 (Fig. 4d). Moreover, compared with the NCF/Al2S3 symmetric cell, the FeSAs-NCF/Al2S3 symmetric cell shows the smallest voltage hysteresis between the oxidation and reduction peaks, confirming the atomically dispersed Fe active centers are more favorable to promote the kinetic conversion of Al2S3 (Fig. 4d). All the above results experimentally verify that the FeSAs-NCF can not only suppress the shuttle effect but also catalyze the redox reactions of aluminum polysulfides for the Al–S battery. Based on the above analysis and discussion, the mechanism of the FeSAs-NCF inhibiting shuttle effect and catalyzing aluminum polysulfides is illustrated in Fig. 4e, and the discharge reactions on cathode side is expressed as follows:
The overall reaction on cathode side:
Meanwhile, the reaction on anode side can be written below:
Accordingly, the overall reaction is given below:
The first-principle calculations were performed to further reveal the improved reaction kinetics of the aluminum polysulfides. The optimized structure models of NCF and FeSAs-NCF are displayed in Fig. 5a. The overall reduction from S8 to Al2S3 involved in multiple intermediates including Al2S18, Al2S12, and Al2S6 during the discharge was considered [6, 45]. The optimized adsorption conformations of various polysulfide intermediates on the NCF and FeSAs-NCF substrates are shown in Fig. 5b. The Gibbs free energies were calculated of each reaction on both the NCF and FeSAs-NCF substrates, and the corresponding Gibbs free energy profiles are shown in Fig. 5b. After the spontaneous exothermic process of converting S8 to Al2S18, where the steps of the formation of Al2S12, Al2S6 and Al2S3 are either endothermic or nearly thermoneutral, the largest positive Gibbs free energy of the formation of Al2S3 from Al2S6 reveals that this process is the rate-determining step in the entire discharge reaction. The Gibbs free energy on the FeSAs-NCF (2.65 eV) is lower than that of on the NCF (3.20 eV) for the reduction of Al2S6, demonstrating the reduction of S is thermodynamically more favorable on the FeSAs-NCF than on the NCF substrate.
4 Conclusions
In summary, iron single atoms dispersed in nitrogen-doped carbon nanofibers have been successfully prepared and used as a unique interlayer to modify the separator for Al–S batteries. The HAADF-STEM and XANES characterizations confirm the iron is atomically dispersed with the coordination of Fe–N4. The Al–S battery with the FeSAs-NCF demonstrates significantly enhanced electrochemical performance, and the Al–S battery with FeSAs-NCF delivers a specific capacity of 780 mAh g−1. The enhanced performance is ascribed to the unique spatial configuration and chemical properties of FeSAs-NCF. Specifically, the FeSAs-NCF is functioned as a chemical and physical barrier to hinder the shuttle effect of soluble aluminum polysulfides. More importantly, the Fe single atoms can catalyze the conversion of aluminum polysulfides to promote the kinetics of the charge/discharge processes.
References
S.H. Chung, A. Manthiram, Current status and future prospects of metal-sulfur batteries. Adv. Mater. 31(27), 1125–1175 (2019). https://doi.org/10.1002/adma.201901125
M. Zhao, B.Q. Li, X.Q. Zhang, J.Q. Huang, Q. Zhang, A perspective toward practical lithium-sulfur batteries. ACS. Cent. Sci. 6(7), 1095–1104 (2020). https://doi.org/10.1021/acscentsci.0c00449
X. Zhang, Y. Yang, Z. Zhou, Towards practical lithium-metal anodes. Chem. Soc. Rev. 49, 3040–3071 (2020). https://doi.org/10.1039/C9CS00838A
X. Yu, M.J. Boyer, G.S. Hwang, A. Manthiram, Room-temperature aluminum-sulfur batteries with a lithium-ion-mediated ionic liquid electrolyte. Chem 4, 586–598 (2018). https://doi.org/10.1016/j.chempr.2017.12.029
S. He, D. Zhang, X. Zhang, S. Liu, W. Chu et al., Rechargeable Al-chalcogen batteries: status, challenges, and perspectives. Adv. Energy Mater. 11(29), 769–783 (2021). https://doi.org/10.1002/aenm.202100769
X. Yu, A. Manthiram, Electrochemical energy storage with a reversible nonaqueous room-temperature aluminum-sulfur chemistry. Adv. Energy Mater. 7(18), 561–570 (2017). https://doi.org/10.1002/aenm.201700561
H. Yang, H. Li, J. Li, Z. Sun, K. He et al., The rechargeable aluminum battery: opportunities and challenges. Angew. Chem. Int. Ed. 58(35), 978–996 (2019). https://doi.org/10.1002/anie.201814031
T. Gao, X. Li, X. Wang, J. Hu, F. Han et al., A rechargeable Al/S battery with an ionic-liquid electrolyte. Angew. Chem. Int. Ed. 128(34), 10052–10055 (2016). https://doi.org/10.1002/ange.201603531
G. Cohn, L. Ma, L.A. Archer, A novel non-aqueous aluminum sulfur battery. J. Power Sources 283, 416–422 (2015). https://doi.org/10.1016/j.jpowsour.2015.02.131
G.A. Elia, K.V. Kravchyk, M.V. Kovalenko, J. Chacón, A. Holland et al., An overview and prospective on Al and Al-ion battery technologies. J. Power Sources 481, 870–892 (2021). https://doi.org/10.1016/j.jpowsour.2020.228870
H. Yang, L. Yin, J. Liang, Z. Sun, Y. Wang et al., An aluminum-sulfur battery with a fast kinetic response. Angew. Chem. Int. Ed. 130(7), 1916–1920 (2018). https://doi.org/10.1002/ange.201711328
Y. Bian, Y. Li, Z. Yu, H. Chen, K. Du et al., Using an AlCl3/urea ionic liquid analog electrolyte for improving the lifetime of aluminum-sulfur batteries. ChemElectroChem 5, 3607–3611 (2018). https://doi.org/10.1002/celc.201801198
W. Chu, X. Zhang, J. Wang, S. Zhao, S. Liu et al., A low-cost deep eutectic solvent electrolyte for rechargeable aluminum-sulfur battery. Energy Storage Mater. 22, 418–423 (2019). https://doi.org/10.1016/j.ensm.2019.01.025
Y. Zhang, L. Ma, R. Tang, X. Zheng, X. Wang et al., The host hollow carbon nanospheres as cathode material for nonaqueous room-temperature Al–S batteries. Int. J. Hydro. Energy 46, 4936–4946 (2021). https://doi.org/10.1016/j.ijhydene.2020.11.076
J. Smajic, S. Wee, F.R. Simoes, M.N. Hedhili, N. Wehbe et al., Capacity retention analysis in aluminum-sulfur batteries. ACS Appl. Energy Mater. 3(7), 6805–6814 (2020). https://doi.org/10.1021/acsaem.0c00921
K.V. Kravchyk, M.V. Kovalenko, Aluminum electrolytes for Al dual-ion batteries. Commun. Chem. 3, 120–129 (2020). https://doi.org/10.1038/s42004-020-00365-2
H. Zhao, J. Xu, D. Yin, Y. Du, Electrolytes for batteries with earth-abundant metal anodes. Chem 24, 18220–18234 (2018). https://doi.org/10.1002/chem.201802438
X. Qu, Y. Tang, A. Du, S. Dong, G. Cui, Polymer electrolytes-new opportunities for the development of multivalent ion batteries. Chem. Asian J. 16, 3272–3280 (2021). https://doi.org/10.1002/asia.202100882
W. Zhou, M. Zhang, X. Kong, W. Huang, Q. Zhang, Recent advance in ionic-liquid-based electrolytes for rechargeable metal-ion batteries. Adv. Sci. 8(13), 4490–4511 (2021). https://doi.org/10.1002/advs.202004490
B. Akgenc, S. Sarikurt, M. Yagmurcukardes, F. Ersan, Aluminum and lithium sulfur batteries: a review of recent progress and future directions. J. Phys. Condens. Matter 33, 253002–253018 (2021). https://doi.org/10.1088/1361-648X/abfa5e
S. Xia, X.M. Zhang, K. Huang, Y.L. Chen, Y.T. Wu, Ionic liquid electrolytes for aluminium secondary battery: influence of organic solvents. J. Electroanal. Chem. 757, 167–175 (2015). https://doi.org/10.1016/j.jelechem.2015.09.022
Y. Guo, H. Jin, Z. Qi, Z. Hu, H. Ji et al., Carbonized-MOF as a sulfur host for aluminum-sulfur batteries with enhanced capacity and cycling life. Adv. Funct. Mater. 29(7), 7676–7682 (2019). https://doi.org/10.1002/adfm.201807676
Y. Guo, Z. Hu, J. Wang, Z. Peng, J. Zhu et al., Rechargeable aluminium-sulfur battery with improved electrochemical performance by cobalt-containing electrocatalyst. Angew. Chem. Int. Ed. 132(51), 22963–22967 (2020). https://doi.org/10.1002/ange.202008481
X. Zheng, R. Tang, Y. Zhang, L. Ma, X. Wang et al., Design of a composite cathode and a graphene coated separator for a stable room-temperature aluminum-sulfur battery. Sustain. Energy Fuels 4, 1630–1641 (2020). https://doi.org/10.1039/C9SE00762H
L.C. Yin, J. Liang, G.M. Zhou, F. Li, R. Saito et al., Understanding the interactions between lithium polysulfides and N-doped graphene using density functional theory calculations. Nano Energy 25, 203–210 (2016). https://doi.org/10.1016/j.nanoen.2016.04.053
J. Liang, L. Yin, X. Tang, H. Yang, W. Yan et al., Kinetically enhanced electrochemical redox of polysulfides on polymeric carbon nitrides for improved lithium–sulfur batteries. ACS Appl. Mater. Interfaces 8(38), 25193–25201 (2016). https://doi.org/10.1021/acsami.6b05647
X. Hong, R. Wang, Y. Liu, J. Fu, J. Liang et al., Recent advances in chemical adsorption and catalytic conversion materials for Li–S batteries. J. Energy Chem. 42, 144–168 (2019). https://doi.org/10.1016/j.jechem.2019.07.001
M. Ling, L. Zhang, T. Zheng, J. Feng, J. Guo et al., Nucleophilic substitution between polysulfides and binders unexpectedly stabilizing lithium sulfur battery. Nano Energy 38, 82–90 (2017). https://doi.org/10.1016/j.nanoen.2017.05.020
M. Ling, W. Yan, A. Kawase, H. Zhao, Y.B. Fu et al., Electrostatic polysulfides confinement to inhibit redox shuttle process in the lithium sulfur batteries. ACS Appl. Mater. Interf. 9(37), 31741–31745 (2017). https://doi.org/10.1021/acsami.7b06485
X. Hong, J. Mei, L. Wen, Y. Tong, A.J. Vasileff et al., Nonlithium metal–sulfur batteries: steps toward a leap. Adv. Mater. 31(5), 1802822 (2019). https://doi.org/10.1002/adma.201802822
C.C. Hou, H.F. Wang, C. Li, Q. Xu, From metal-organic frameworks to single/dual-atom and cluster metal catalysts for energy applications. Energy Environ. Sci. 13, 1658–1693 (2020). https://doi.org/10.1039/C9EE04040D
Y. Peng, B. Lu, S. Chen, Carbon-supported single atom catalysts for electrochemical energy conversion and storage. Adv. Mater. 30(48), 1995–2020 (2018). https://doi.org/10.1002/adma.201801995
H. Zhong, Y. Zhao, T. Zhang, G. Liu, Controlled lithium deposition on Alq3 coated substrate. Batteries Supercaps 4(1), 98–105 (2021). https://doi.org/10.1002/batt.202000126
C. Zhao, G.L. Xu, Z. Yu, L. Zhang, I.H. Wang et al., A high-energy and long-cycling lithium-sulfur pouch cell via a macroporous catalytic cathode with double-end binding sites. Nat. Nanotechnol. 16, 166–173 (2021). https://doi.org/10.1038/s41565-020-00797-w
Z. Du, X. Chen, W. Hu, C. Chuang, S. Xie et al., Cobalt in nitrogen-doped graphene as single-atom catalyst for high-sulfur content lithium-sulfur batteries. J. Am. Chem. Soc. 141, 3977–3985 (2019). https://doi.org/10.1021/jacs.8b12973
L.F. Chen, Y. Lu, L. Yu, X.W. Lou, Designed formation of hollow particle-based nitrogen-doped carbon nanofibers for high-performance supercapacitors. Energy Environ. Sci. 10, 1777–1783 (2017). https://doi.org/10.1039/C7EE00488E
Y. Wang, D. Adekoya, J. Sun, T. Tang, H. Qiu et al., Manipulation of edge-site Fe–N2 moiety on holey Fe, N codoped graphene to promote the cycle stability and rate capacity of Li–S batteries. Adv. Funct. Mater. 29(5), 7485–7494 (2018). https://doi.org/10.1002/adfm.201807485
Z. Zhang, J. Sun, F. Wang, L.M. Dai, Efficient oxygen reduction reaction (ORR) catalysts based on single iron atoms dispersed on a hierarchically structured porous carbon framework. Angew. Chem. Int. Ed. 130(29), 9038–9043 (2018). https://doi.org/10.1002/ange.201804958
P. Peng, L. Shi, F. Huo, C. Mi, X. Wu et al., A pyrolysis-free path toward superiorly catalytic nitrogen-coordinated single atom. Sci. Adv. 5, 2322–2329 (2019). https://doi.org/10.1126/sciadv.aaw2322
Y. Wang, M. Wang, Z. Zhang, Q. Wang, Z. Jiang et al., Phthalocyanine precursors to construct atomically dispersed iron electrocatalysts. ACS Catal. 9(7), 6252–6261 (2019). https://doi.org/10.1021/acscatal.9b01617
H.B. Yang, S.F. Hung, S. Liu, K. Yuan, S. Miao et al., Atomically dispersed Ni(I) as the active site for electrochemical CO2 reduction. Nat. Energy 3, 140–147 (2018). https://doi.org/10.1038/s41560-017-0078-8
T. Yamamoto, Assignment of pre-edge peaks in K-edge X-ray absorption spectra of 3D transition metal compounds: electric dipole or quadrupole? X-Ray Spectrom. 37, 572–584 (2008). https://doi.org/10.1002/xrs.1103
N.S. Manan, L. Aldous, Y. Alias, P. Murray, L.J. Yellowlees et al., Electrochemistry of sulfur and polysulfides in ionic liquids. J. Phys. Chem. B 115, 13873–13882 (2011). https://doi.org/10.1021/jp208159v
V.A. Matamoros, O. Cespedes, B.R.G. Johnson, T.M. Stawski, U. Terranova et al., A highly reactive precursor in the iron sulfide system. Nat. Commun. 9, 3125–3132 (2018). https://doi.org/10.1038/s41467-018-05493-x
X. Xiao, J. Tu, Z. Huang, S.Q. Jiao, A cobalt-based metal-organic framework and its derived material as sulfur hosts for aluminum-sulfur batteries with the chemical anchoring effect. Phys. Chem. Chem. Phys. 23(17), 10326–10334 (2021). https://doi.org/10.1039/D1CP01232K
Acknowledgements
This work is financially supported by the National Natural Science Foundation of China (No. 51874197) and Natural Science Foundation of Shanghai (Nos. 21ZR1429400, 22ZR1429700). The authors appreciate the BL14W1 in the Shanghai Synchrotron Radiation Facility (SSRF) for help with characterization.
Funding
Open access funding provided by Shanghai Jiao Tong University.
Author information
Authors and Affiliations
Corresponding author
Supplementary Information
Below is the link to the electronic supplementary material.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Wang, F., Jiang, M., Zhao, T. et al. Atomically Dispersed Iron Active Sites Promoting Reversible Redox Kinetics and Suppressing Shuttle Effect in Aluminum–Sulfur Batteries. Nano-Micro Lett. 14, 169 (2022). https://doi.org/10.1007/s40820-022-00915-4
Received:
Accepted:
Published:
DOI: https://doi.org/10.1007/s40820-022-00915-4