Highlights
-
Novel double-network (DN) ion-conducting hydrogel (ICH) based on a poly(ionic liquid)/MXene/poly(vinyl alcohol) system (named PMP DN ICH) was synthesized using freeze–thawing and ionizing radiation technology.
-
The PMP DN ICH possesses a multiple cross-linking mechanism and exhibits outstanding ionic conductivity (63.89 mS cm−1), excellent temperature resistance (−60–80 °C) and decent mechanical performance.
-
The well-designed PMP DN ICH shows considerable potential in wearable sensing, energy storage, and energy harvesting.
Abstract
High-performance ion-conducting hydrogels (ICHs) are vital for developing flexible electronic devices. However, the robustness and ion-conducting behavior of ICHs deteriorate at extreme temperatures, hampering their use in soft electronics. To resolve these issues, a method involving freeze–thawing and ionizing radiation technology is reported herein for synthesizing a novel double-network (DN) ICH based on a poly(ionic liquid)/MXene/poly(vinyl alcohol) (PMP DN ICH) system. The well-designed ICH exhibits outstanding ionic conductivity (63.89 mS cm−1 at 25 °C), excellent temperature resistance (− 60–80 °C), prolonged stability (30 d at ambient temperature), high oxidation resistance, remarkable antibacterial activity, decent mechanical performance, and adhesion. Additionally, the ICH performs effectively in a flexible wireless strain sensor, thermal sensor, all-solid-state supercapacitor, and single-electrode triboelectric nanogenerator, thereby highlighting its viability in constructing soft electronic devices. The highly integrated gel structure endows these flexible electronic devices with stable, reliable signal output performance. In particular, the all-solid-state supercapacitor containing the PMP DN ICH electrolyte exhibits a high areal specific capacitance of 253.38 mF cm−2 (current density, 1 mA cm−2) and excellent environmental adaptability. This study paves the way for the design and fabrication of high-performance multifunctional/flexible ICHs for wearable sensing, energy-storage, and energy-harvesting applications.
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
1 Introduction
Ion-conducting hydrogels (ICHs) have been extensively used to develop electronic skin (e-skin), wearable sensors, supercapacitors (SCs), and triboelectric nanogenerators (TENGs) owing to their inherent properties such as flexibility, biocompatibility, and high conductivity [1,2,3]. However, conventional conductive hydrogels contain substantial amounts of absorbed water, which inevitably freezes or evaporates at cold or high temperatures, respectively. The flexibility and conductivity deteriorate significantly, which severely inhibits their performance in practical applications [4, 5]. Additionally, they tend to exhibit inferior mechanical properties [6, 7]. Therefore, designing new ICHs with high environmental tolerance and decent mechanical stability without sacrificing ionic conductivity is challenging but crucial.
Several attempts have been made to address these problems. On the one hand, ICHs with excellent temperature resistance and water retention have been obtained by utilizing organic solvents [8], inorganic salts [9], or ionic liquids (ILs) [10] as cryoprotectants/humectants. Unfortunately, organic solvents such as ethylene glycol and glycerol hinder ion migration, resulting in ICHs with poor ionic conductivity [7, 9]. Alternatively, ICHs containing a large amount of inorganic salts exhibit a salting-out effect, which increases their cross-linking degree while restricting ion migration [11]. ILs which are organic molten salts comprising organic cations and organic/inorganic anions have drawn considerable interest in the development of electronic devices owing to their benefits including high ionic conductivity, high thermal/chemical stability, nonvolatile behavior, and wide electrochemical window [12, 13]. Furthermore, the chemical structure and performance of ILs can be tuned by changing the anion–cation pairs [1, 14]. However, ILs are unable to maintain a stable shape owing to their viscous flow characteristics, and leakage problems occur when they are doped into polymer matrices [15]. Therefore, by polymerizing IL monomers into poly(ionic liquid)s (PILs), the inherent properties of the ILs can be transferred to the polymer chain and the potential leakage problem of the ILs can be eliminated, thereby obtaining ICHs with excellent temperature resistance and ionic conductivity [16, 17].
On the other hand, strategies have been reported for synthesizing diverse strong and tough hydrogels such as double-network (DN) hydrogels [18] and nanocomposite hydrogels [19, 20]. Among these, DN hydrogels can effectively disperse stress and dissipate energy by introducing sacrificial bonds such as hydrogen bonds and ionic bonds into the network, which improve flexibility [18, 21].
Poly(vinyl alcohol (PVA) has been widely used as a hydrogel polymer matrix because of its excellent biocompatibility, water-retaining ability, nontoxicity, and low cost [22, 23]. Several PVA-based DN hydrogels with excellent mechanical properties and freezing resistance have recently been reported [24, 25]. However, these hydrogels must exhibit sufficient conductivity to be applicable as flexible electronic materials. Therefore, a novel strategy was devised in the present study to construct a multifunctional PIL/MXene/PVA (PMP)-based DN ICH (denoted as PMP DN ICH) with excellent temperature tolerance, mechanical flexibility, and superior ionic conductivity by combining freeze–thawing and ionizing radiation methods (Fig. 1a). The freeze-thawing process enabled in situ crystallization of PVA, which facilitated the formation of a physically cross-linked network [26], whereas the subsequent ionizing radiation process allowed the formation of a chemically cross-linked PIL–PVA network. The large amount of the PIL and its network helped eliminate the potential leakage problem of ILs and improve the temperature resistance of the PVA-based hydrogel while endowing it with excellent ionic conductivity. Moreover, nanosheets of a two-dimensional (2D) transition metal carbide/nitride (Ti3C2Tx MXene) with abundant surface hydrophilic groups (such as –F, –OH, and =O) were introduced as physical cross-linkers to further enhance the mechanical properties of PMP DN ICH by forming noncovalent interactions, such as hydrogen bonding, with the polymer network [27].
Finally, the DN structure formed through a multiple cross-linking mechanism enabled PMP DN ICH to exhibit outstanding ionic conductivity, wide-ranging temperature resistance, and decent mechanical properties. More importantly, PMP DN ICH was used to construct a flexible strain sensor, a thermal sensor, an all-solid-state SC, and a single-electrode TENG that exhibited reliable properties. Overall, the comprehensive performance of PMP DN ICH makes it a versatile candidate material for fabricating flexible electronic devices intended for wearable sensing, energy-storage, and energy-harvesting applications.
2 Experimental Section
2.1 Materials
1-Vinyl-3-butylimidazolium bromide (VBImBr, 99%) was purchased from the Lanzhou Institute of Chemical Physics (China). 1-vinylimidazole (≥ 99%), 2,6-ditert-butyl-4-methylphenol (BHT, 99%), and 1,3,5-tris(bromomethyl)benzene (98%) were purchased from Sigma-Aldrich. PVA was purchased from Sinopharm Chemical Reagent Co., Ltd. (China), with an average degree of polymerization (DP) of 1750 ± 50. Activated carbon (YP–50F) and carbon black were purchased from Kuraray Co., Ltd and 9 Ding Chemistry Co., Ltd, respectively. Ecoflex 00–50 silicone rubber was purchased from Smooth-On Company, USA. All other chemicals (analytical grade) were purchased from Sinopharm Chemical Reagent Co., Ltd. (China), and used without further purification.
2.2 Preparation of Ti3C2Tx MXene Nanosheets
Ti3C2Tx MXene (MXene) was synthesized according to the following process. First, 1 g LiF was added to 40 mL HCl solution (9 mol L−1) and stirred for 30 min. Secondly, 1 g Ti3AlC2 powder was slowly added to the above solution and stirred at 35 °C for 48 h. Finally, the reaction solution was washed by centrifugation with water until the pH of the solution was ≥ 6, and the precipitate was collected. Subsequently, the precipitate was sonicated with ethanol and water, and was centrifuged at 3500 r min−1 for 25 min; the upper dark green liquid was the delaminated MXene nanosheet aqueous solution.
2.3 Synthesis of Ph–3MVIm–Br
1,3,5-tris (1′-methylene-3′-vinylimidazolium bromide) benzene (termed Ph–3MVIm–Br; Ph = phenyl, 3 denotes the number of branched polymerizable ion pairs, MVIm = 1-methylene-3-vinylimidazolium cation, Br = bromide anion) was synthesized according to Ref. [28]; the detailed synthesis process was shown in the supporting information.
2.4 Radiation Synthesis of PMP DN ICH
Firstly, 1 g PVA power was added to 9 g deionized water under stirring at 90 °C for 4 h until PVA was completely dissolved to form 10 wt% PVA solution. Then, VBImBr (1.848 g, 8 mol L−1), Ph–3MVIm–Br (12.77 mg, 0.02 mol L−1), MXene (27.72 mg, 1.5 wt%, relative to monomer), and 10% PVA aqueous solution (1 mL) were added into an irradiation flask and ultrasonic dispersed. Subsequently, the solution was bubbled by N2 for 10 min. The above solution was placed at − 25 °C for 12 h and then thawing 6 h to forming physical cross-linked gel. Finally, the above physical cross-linked gel was irradiated under an electron-beam (EB) accelerator (10 MeV, EL PONT Co., Ltd. China) with the dose rate of 10 kGy pass−1 to obtain PMP DN ICH.
2.5 General Characterization Techniques
The chemical structure of the Ph–3MVIm–Br was analyzed by 1H nuclear magnetic resonance (1H NMR) using D2O as the solvent. Fourier-transform infrared (FTIR, Tensor 27, Bruker) spectrometry and scanning electron microscope (SEM, SU8000, Hitachi, Japan) were used to confirm the structure and composition of the freeze-dried PMP DN ICH. The thermal stability of the PMP DN ICH was carried on a thermogravimetric analysis (TGA) (Q600 SDT) under N2 gas atmosphere with a heating rate of 10 °C min−1. Differential scanning calorimetry (DSC) was performed using a TA Q200 instrument. X-ray diffraction (XRD) was tested by Rigaku corporation (Japan) diffractometer. Cyclic voltammetry (CV), electrochemical impedance spectroscopy (EIS), galvanostatic charge/discharge (GCD) were measured by an electrochemical workstation (CHI660E, Chenhua, Shanghai). The cycling stability was tested with a LANBTS electrochemical instrument. The open-circuit voltage, short-circuit current, and transferred charge amount were recorded by a Keithley 6514 electrometer.
2.6 Conductivity Tests
The ionic conductivity of the PMP DN ICH was measured on the electrochemical workstation. The PMP DN ICH (diameter of 13 mm, thickness of approximately 8 mm) was sandwiched between two sheet metal electrodes. Next the electrochemical impedance spectroscopy (EIS) was measured at different temperatures (− 60, − 25, 0, 25, 40, 60, and 80 °C). It was calculated by Eq. (1):
where l (mm) represents the thickness of the PMP DN ICH, R (Ω) represents the bulk resistance, and S (mm2) represents the contact area of the PMP DN ICH. The samples were tested in parallel in three groups.
2.7 Measurement of Adhesive Strength and Mechanical Properties
The adhesive strength and mechanical properties of the PMP DN ICH were measured by using the tensile testing machine (CMT–4104, Shenzhen sans testing machine Co., Ltd.). The adhesive strength testing method of the PMP DN ICH is shown in Fig. S12c. Cut the PMP DN ICH into regular-shaped samples (30 mm × 20 mm × 3 mm), and sandwich them between two substrates. Next, the tensile testing machine with a 100 N load cell broken the PMP DN ICH at a rate of 50 mm min−1. The experimental results of the adhesive strength were based on the results of at least 3 samples. Besides, the cyclic tensile tests of the PMP DN ICH (40 mm × 10 mm × 3 mm) were also carried out on the tensile testing machine under the rate of 200 mm min−1.
2.8 Electrical Sensing Properties of the PMP DN ICH-Based Strain Sensor
The sensing properties of the PMP DN ICH-based strain sensor were evaluated by the relative changes of the resistance. By loading the PMP DN ICH onto the tensile testing machine and connecting it to the electrochemical workstation with copper wires, the strain-induced resistance change of the PMP DN ICH can be monitored in real time. The relative rate of change of the resistance was calculated by Eq. (2):
where R and R0 are the resistance without and with stretching, respectively.
2.9 Human Motion Detection of the PMP DN ICH-Based Strain Sensor
The PMP DN ICH was cut into a cuboid shape (40 mm × 10 mm × 3 mm) and adhered to the various joints of the human body (finger, wrist, neck, belly, and knee) to detect the human motion. Then, the two ends of the PMP DN ICH were connected to an electrochemical workstation or a small portable wireless transmission device. This experiment was completed with the assistance of a volunteer, and informed written consent was obtained for publishing the images and data. The gel was not harmful to humans.
2.10 Thermal Detection
The resistance of the sensor at various temperatures was measured by the electrochemical workstation. The temperature coefficient of resistance (TCR) was calculated via Eq. 3:
where R0 (Ω): the initial resistance of the PMP DN ICH at 25 °C; ΔR (Ω): the relative change of resistance; and ΔT (°C): the relative change of temperature.
2.11 Fabrication and Electrochemical Measurement of the Flexible All-Solid-State Supercapacitor
An appropriate amount of NMP solution was added dropwise to the mixture of activated carbon, carbon black, and PVDF powder with a mass ratio of 85:5:10. After fully grinding and uniform, the mixed slurry was applied to the cleaned rectangle nickel foam (1 × 2 cm2) and dried in vacuum at 50 °C for 48 h. The total mass load of electrode material was about 3.0 mg. Then, the activated carbon electrode was performed by a powder tablet press (YP–40 T, Tianjin Jinfulun technology Co., Ltd) under a pressure of 10 MPa. The SCs was assembled by the activated carbon electrodes and the PMP DN ICH with a sandwich structure. Finally, two titanium foils as current collector and conductive wire were placed on both sides of the sample and sealed with PDMS. Electrochemical performance was tested after standing 1 h.
2.12 Fabrication of the Single-Electrode PMP DN ICH–TENG
The PMP DN ICH–TENG was fabricated by sandwiching the PMP DN ICH with commercial kapton film and ecoflex, where PMP DN ICH, kapton film, and ecoflex classed as the electrode, the negative and positive electrification layer, respectively. And the Ag wire was attached to PMP DN ICH for electrical output measurements.
3 Results and Discussion
3.1 Design and Preparation of PMP DN ICH
MXene nanosheets were synthesized according to our previously reported method [29]. The IL 1,3,5-tris(1′-methylene-3′-vinylimidazolium bromide) benzene (Ph–3MVIm–Br) was used as a cross-linker after being synthesized by alkylation. The chemical structure of Ph–3MVIm–Br was determined by 1H nuclear magnetic resonance spectroscopy (Fig. S1). PMP DN ICH was prepared using a two-step method (Fig. 1a) that involved dissolving the IL monomer 1-vinyl-3-butylimidazolium bromide (VBImBr) and IL cross-linker Ph–3MVIm–Br in a 10% aqueous PVA solution, and then ultrasonically dispersing a certain amount of the MXene into the preceding solution. A physically cross-linked network was readily obtained from the resulting black precursor solution by freeze–thawing. Subsequently, a chemically cross-linked PIL–PVA network was constructed by the in situ polymerization/cross-linking driven by the ionizing radiation technique. Finally, black-colored PMP DN ICH with abundant covalent and noncovalent cross-linked networks was successfully obtained (Fig. 1b). The radiation-associated conditions for synthesizing PMP DN ICH were comprehensively optimized (Figs. S2 and S3) and determined to be as follows: absorbed dose, 20 kGy; monomer concentration, 8 mol L−1; cross-linker concentration, 0.02 mol L−1; and MXene content, 1.5 wt%. The gel synthesized under these conditions was used in the subsequent experiments.
Fourier-transform infrared (FTIR) spectra of VBImBr, Ph–3MVIm–Br, the MXene, PVA, and PMP DN ICH were acquired (Fig. 1c). The imidazolium-associated peaks at 1157 and ~ 3000 cm−1 appeared in the spectrum of PMP DN ICH after the irradiation step, indicating that the imidazole ring structure was not damaged by irradiation. Moreover, the characteristic –C=C– peaks at 924–981 and 1648 cm−1 almost disappeared after the irradiation, indicating successful polymerization/cross-linking of PMP DN ICH [30]. Additionally, peaks appeared at 3296 and 1086 cm−1, presumably owing to the stretching vibrations of –OH groups in the PVA chains [31]; these peaks shifted to 3367 and 1093 cm−1, respectively, in the spectrum of PMP DN ICH, suggesting hydrogen bond formation [32]. X-ray diffractometry (XRD) analysis of PVA, the MXene, and PMP DN ICH (Fig. 1d) indicated that the typical PVA crystalline peaks corresponding to the (101), (200), and (102) lattice planes almost completely receded in the pattern of PMP DN ICH, suggesting that the PVA in PMP DN ICH could be chemically cross-linked [33]. Additionally, the intensity of the (002) peak of the MXene in PMP DN ICH decreased and shifted to a lower 2θ value, implying that the d-spacing of the MXene could have increased slightly, possibly owing to hydrogen bonding between the MXene and the other components [34, 35]. Scanning electron microscopy (SEM) revealed the highly porous nature of PMP DN ICH (Fig. 1e), and energy-dispersive X-ray spectroscopy (EDS) mapping confirmed the uniform distribution of Ti in PMP DN ICH, suggesting a regular distribution of the MXene (Fig. S4). Overall, these findings validated the synthesis of PMP DN ICH with a homogeneously cross-linked network featuring abundant covalent and noncovalent interactions using the aforementioned meticulous design approach.
3.2 Mechanical Properties, Environmental Tolerance, and Conductivity of PMP DN ICH
The mechanical performance, environmental tolerance, and conductivity of PMP DN ICH were explored to determine its applicability in flexible electronic devices. Moreover, when the PMP DN ICH was attached on the skin surface as a wearable material to detect human movement, adhesion was also key influencing factors. As shown in Fig. S5, PMP DN ICH exhibited enhanced mechanical performance owing to its chemically cross-linked structure that was generated by ionizing radiation. Moreover, it showed remarkable mechanical elasticity and shape recovery, given its ability to undergo large stretching and compression without any evident structural deformation and then quickly return to its initial shape after stress removal (Fig. 2a, b). PMP DN ICH was subjected to 10 successive tensile–relaxation cycles (ε = 100%) and compression–relaxation cycles (ε = 70%) to quantitatively examine its fatigue resistance and cycling stability (Fig. 2c, d). After displaying hysteresis in the first loading–unloading cycle, the stress–strain curves of PMP DN ICH in the subsequent cycles almost overlapped, indicating decent elastic behavior and fatigue resistance [36, 37]. In contrast, the hydrogel precursor Pre-PMP DN ICH exhibited inferior fatigue resistance and cycling stability (Fig. S6a–d).
To achieve practical viability, ICHs must exhibit acceptable performance under extreme conditions in terms of aspects such as temperature resistance, long-term stability, and anti-drying properties. To that end, the temperature resistance of Pre-PMP DN ICH and PMP DN ICH was analyzed under extreme storage conditions (Figs. 2e and S6e). The results indicated that both materials exhibited outstanding flexibility in terms of being effortlessly twisted/compressed and being bent at − 60 °C. However, Pre-PMP DN ICH which had a physically cross-linked structure could not be used at high temperatures because its structure was destroyed after only 10 min at 80 °C (Fig. S7). Temperature-dependent tensile and compressive stress–strain curves of Pre-PMP DN ICH (Fig. S6f, g) and PMP DN ICH (Fig. 2f, g) suggested that the mechanical strength increased and the ductility decreased with decreasing temperature. Notably, PMP DN ICH exhibited satisfactory tensile stress–strain and compressive stress–strain characteristics at − 60 °C (98.6 kPa–195% and 559.4 kPa–78.3%, respectively) in terms of meeting practical application requirements. This level of mechanical flexibility of PMP DN ICH at extreme temperatures can be leveraged to significantly broaden its applicability.
The conductivities of Pre-PMP and PMP DN ICH at different temperatures were investigated by electrochemical impedance spectroscopy (EIS) (Figs. 2h and S8). The conductivity of Pre-PMP DN ICH increased from 70.26 mS cm−1 at − 60 °C to 141.08 mS cm−1 at 60 °C, whereas that of PMP DN ICH increased from 37.65 mS cm−1 at − 60 °C to 139.21 mS cm−1 at 80 °C. The results indicate the stable ion-transporting tendency of the DN ICH at extreme temperatures. The excellent conductivity of PMP DN ICH in harsh environments was corroborated by comparison with those of previously reported temperature-tolerant hydrogels (Fig. S9). Additionally, PMP DN ICH was used as a wire in a circuit to illuminate a light-emitting diode (LED) using a 3 V power source (Fig. S10 and Movies S1, S2). Stretching or compressing PMP DN ICH led to commensurate changes in the brightness of the LED lamp.
The long-term stability and anti-drying property of the DN ICH were also explored (Figs. 2i, j and S11–S13). After storage for 30 d in an ambient environment, Pre-PMP DN ICH showed significant volume shrinkage owing to water evaporation (Fig. S11), with its weight and conductivity decreasing to 58.19% and 49.92%, respectively. In contrast, PMP DN ICH exhibited relatively higher final weight and conductivity values (81.20% and 66.66%, respectively). The excellent long-term stability and moisture retention of PMP DN ICH were evidently due to the abundant hydrogen bonds in the formed three-dimensional network, which effectively reduced the evaporation rate of internal water [38, 39]. Furthermore, the MXene in PMP DN ICH also exhibited excellent oxidation resistance (Fig. S14) [40]. More importantly, PMP DN ICH could be functioned as an effective adhesive material (Fig. S15).
To sum up, the outstanding mechanical performance, environmental resistance, long-term moisture retention ability, conductivity, and oxidation resistance of PMP DN ICH underscore its application potential in flexible wearable electronic device fabrication.
3.3 Antibacterial Performance of PMP DN ICH
Antibacterial performance plays a critical role to wearable material. Many studies have proved that imidazole-based ILs and MXene possessed outstanding antibacterial performance [41, 42]. Therefore, the antibacterial activities of the fabricated PMP DN ICH were verified by using Gram-negative Escherichia coli (E. coli) and Gram-positive Staphylococcus aureus (S. aureus). Figure 3a–c depicts the antibacterial mechanism of the PMP DN ICH. For PIL, the positively charged imidazole rings interacts with the negatively charged phospholipid bilayer of bacterial cell membrane through electrostatic interaction, thus providing an opportunity for imidazole side chain alkyl to insert into the phospholipid bilayer, resulting in the rupture of bacterial cell membrane and the leakage of cytoplasm, thereby killing the bacteria (Fig. 3b) [42, 43]. Furthermore, studies have shown that oxygen-containing groups of MXene nanosheets can form hydrogen bonds with lipopolysaccharide chains of the bacterial cell membranes, prevent bacteria from ingesting nutrients, inducing bacteria to produce active oxygen components and cell inactivation, thus inhibiting bacterial growth. In addition, the sharp edges of the MXene nanosheets could also enter the cytoplasmic region by cutting the bacterial cell wall, causing the release of bacterial DNA and eventually disintegrate of the bacteria (Fig. 3c) [44].
The antibacterial ability of the PMP DN ICH is shown in Fig. 3d–f. The sizes of the inhibition zones of the PMP DN ICH against E. coli and S. aureus were found to be 24 and 24 mm (Fig. 3d), respectively, indicating the desirable antibacterial activity of the PMP DN ICH. In addition, E. coli and S. aureus were incubated with the PMP DN ICH at 37 °C for 18 h. The active colonies of all the investigated microbes were almost vanished (Fig. 3e), and the corresponding antibacterial rates of E. coli and S. aureus were found to be 99.91% and 99.98%, respectively (Fig. 3f), further displaying the excellent antibacterial property.
3.4 Electrical Sensing Properties of a PMP DN ICH-Based Strain Sensor
To evaluate the potential applicability of the developed ICH in wearable strain sensing, its electrical sensing properties were comprehensively explored by constructing and assessing a PMP DN ICH-based strain sensor. No obvious signal fluctuations were observed at tensile rates ranging from 50 to 300 mm min−1 and over a tensile strain range of 25%–200%, which demonstrated the reversible and stable signal output ability of the devised strain sensor (Fig. 4a, b). Moreover, the responsive resistance variation waveforms were consistent with the tensile strain (50%), indicating negligible electromechanical hysteresis (Fig. S16) [45]. The stability of the PMP DN ICH-based strain sensor was tested at a tensile strain of 25% over approximately 300 loading–unloading cycles (Fig. 4c). The relative resistance variation was generally consistent, indicating excellent repeatability and stability of the PMP DN ICH-based strain sensor.
Subsequently, the PMP DN ICH-based strain sensor was attached to different parts of the human body to detect human movement (Fig. 4d). Interestingly, when the sensor was mounted on the belly and knee, it readily detected and distinguished between different breathing and motion states (Fig. 4e, f). Furthermore, to achieve remote monitoring of human movement, a wireless sensing system was constructed by connecting a small portable wireless transmission device to PMP DN ICH (Fig. 4g) [8]. The PMP DN ICH-based strain sensor adhered to the neck or wrist could effectively detect neck nodding, looking up movements, and repetitive wrist motion (Fig. 4h, j and Movie S3). More importantly, the relative resistance increased as the bending angle of the finger increased from 30° to 90°, indicating a high sensitivity (Fig. 4i and Movie S4). Additionally, the ability of the wireless sensing system to convey information using Morse codes was explored (Fig. 4g, k) [46]. Distress signals of “GO,” “SOS,” and “HELP” were encrypted and translated by briefly and extensively stretching the PMP DN ICH-based strain sensor in an alternating manner (Fig. 4l–n and Movies S5, S6, S7). The demonstrations of the PMP DN ICH-based wireless strain sensor present the possibility to use PMP DN ICH as wearable devices for human health monitoring, encrypted transmission of information, and human–machine interfaces.
3.5 Thermal Sensing Properties of a PMP DN ICH-Based Thermistor
The outstanding temperature resistance of PMP DN ICH was leveraged to use it as a thermosensitive material to explore its viability as a temperature sensor. The thermal sensitivity of a thermistor is commonly evaluated using the temperature coefficient of resistance (TCR), which is estimated using the slope of the fit resistance curves [47]. Therefore, the changes in relative resistance of a PMP DN ICH-based thermistor were monitored with step increases in temperature from 30 to 100 °C (Fig. 5a, b). The obtained TCR values of − 1.96% °C−1 (30–60 °C) and − 0.62% °C−1 (60–100 °C) (Fig. 5b) are superior to most previously reported TCR data (Table S1), demonstrating the outstanding temperature sensitivity of the PMP DN ICH-based thermistor. Furthermore, the PMP DN ICH-based thermistor demonstrated excellent repeatability of the thermal response over relatively small and large temperature ranges (Fig. 5c, d). These results indicated that the PMP DN ICH-based thermistor had excellent thermal sensitivity and could be applied as a thermal sensor for monitoring environmental temperature changes. More importantly, the fabricated thermistor showed remarkable potential in quantitatively monitoring the human body temperature (Fig. 5e, f). For example, the thermistor was fixed onto a mask to detect normal breathing by monitoring the temperature changes during exhalation and inhalation (Fig. 5e). Additionally, when an external heat source was used to simulate the temperature of human fever (Fig. 5f), the thermistor effectively responded to changes in the body temperature through variations in its relative resistance. The above results indicate that the PMP DN ICH-based thermistor is suitable for monitoring the changes in ambient and body temperatures.
3.6 Electrochemical Properties of a Flexible PMP DN ICH-Based All-Solid-State Supercapacitor
To certify the ability of PMP DN ICH to effectively function as an electrolyte, given its unique advantages, a flexible all-solid-state SC was assembled by combining the PMP DN ICH electrolyte exhibiting adhesive properties with an activated carbon electrode (Fig. 6a). The electrochemical performance of the flexible PMP DN ICH-based SC was evaluated by cyclic voltammetry (CV), galvanostatic charge–discharge (GCD) analysis, and EIS. The optimal working potential window of the fabricated SC was determined to be 1.3 V (Fig. S17). As shown in Fig. 6b, the shapes of CV curves were close to rectangle as the scan rate increased from 5 to 100 mV s−1 over the working potential window of 0–1.3 V, exemplifying the typical electronic double layer capacitive performance and excellent rate capability [24, 48]. GCD curves of the SC obtained at various current densities (1–8 mA cm−2) displayed symmetric triangular shapes and featured a small IR drop even at a high current density of 8.0 mA cm−2, indicating that the SC exhibited nearly ideal charge–discharge ability and decent capacitive behavior (Fig. 6c) [49]. Notably, even at the highest imposed current density of 8 mA cm−2, the areal capacitance and coulombic efficiency of the SC were maintained at 143.38 mF cm−2 and 96.68%, respectively (Fig. 6d). These values are considerably higher than those obtained in previous hydrogel-based studies (Table S2). In addition, the PMP DN ICH-based SC possesses a wide electrochemical window and a range of operating temperatures, which ensure that the SC can be used normally in harsh environments. The EIS curve and the corresponding equivalent circuit of the SC (Fig. 6e) were used to determine its equivalent series resistance (Rs) and charge-transfer resistance (Rct) from the intercepts of the approximate semicircular area in the high-frequency region of the Nyquist plot [25, 30]. The low Rs (5.6 Ω) and Rct (9.3 Ω) values indicate good electrode–electrolyte contact and the occurrence of efficient charge transfer. Moreover, the data in the low-frequency region were almost parallel to the Z′′-axis, demonstrating the excellent capacitive behavior of the fabricated SC [50]. The Ragone plot suggests that the maximum energy and power densities of the devised SC (55.25 μWh cm−2 and 5200 μWh cm−2, respectively) are superior to those of most reported hydrogel-based SCs (Fig. 6f) [2, 10, 24, 48, 51,52,53,54,55,56,57]. Furthermore, the fabricated SC retained an initial areal capacitance of 77.08% and an almost unchanged coulombic efficiency of 99.15%, indicating its decent long-term stability (Fig. 6g) [58]. The practical viability of the fabricated SC was assessed by using it to power small electronic devices (Fig. 6h). The SC with a volume of 2 × 1 × 0.3 cm3 was able to drive an electronic meter for 3 min (Movie S8), whereas two SCs connected in series could illuminate an LED bulb for 47 s (Movie S9). These electrochemical results highlight the broad application prospects of the PMP DN ICH-based SC in developing flexible energy-storage systems for wearable electronics.
3.7 Electrochemical Performance of the PMP DN ICH-Based SC Under Different Conditions
PMP DN ICH was found to exhibit outstanding mechanical performance, excellent temperature resistance, and long-term stability. Therefore, the electrochemical performance of the PMP DN ICH-based SC was meticulously probed under various conditions (Figs. 7 and S18). The CV curves nearly overlapped as the storage duration increased to 30 d (Fig. 7a). Moreover, the final capacitance retention and coulombic efficiency were 79.93% and 92.78%, respectively (Figs. 7b and S18a), and the Nyquist plots shifted slightly to the right (Fig. 7c), demonstrating the remarkable long-term stability of the SC. The temperature resistance of the SC was investigated by increasing the temperature from − 60 to 80 °C. The CV integration area increased compared to that of the initial state (Fig. 7d), and the Rs value from the Nyquist plots decreased (Fig. 7f) owing to the enhanced ionic diffusion efficiency of the SC at elevated temperatures. Furthermore, the capacitance retention increased gradually from 78.09% to 103.93%, and the coulombic efficiency decreased from 88.79% to 55.56% as the temperature increased from − 60 to 80 °C (Figs. 7e and S18b). The possible reason for this behavior is that with the increasing temperature, the reaction kinetics of some side reactions in the charging process of the supercapacitor accelerated, and the side reaction was prompted to occur at a high temperature, thus extending the charging time of the supercapacitor, resulting in the reduction of its coulombic efficiency [59]. Subsequently, the electrochemical stability of PMP DN ICH under different mechanical stimuli was studied (Figs. 7g–l and S18c, d). Interestingly, the CV curves and Nyquist plots nearly overlapped for different loadings as well as bending angles (Fig. 7g, i, j, l). Moreover, the capacitance retention and coulombic efficiency remained almost unchanged (Figs. 7h, k and S18c, d), indicating the stable energy-storage characteristics of the SC. Overall, the excellent environmental stability, temperature tolerance, and mechanical flexibility of the SC enabled it function as a reliable power source at different temperatures and under varying mechanical conditions. This high-performance PMP DN ICH electrolyte paves a new way for flexible and wearable SCs and could have a wide range of applications in advanced energy-storage devices.
3.8 Electrical Output Properties of a PMP DN ICH-Based Triboelectric Nanogenerator
PMP DN ICH was subsequently used as a current collector to assemble a single-electrode-mode TENG (Fig. 8a). An elastomeric silicone rubber substrate (Ecoflex 00–50) was employed as the positive friction layer, a commercial Kapton film was used as the negative-contact triboelectric material layer, and Ag wire was adopted as the electrode [3]. The operating mechanism of the PMP DN ICH-based TENG is illustrated in Fig. 8b. When the Kapton film is separated from the silicone rubber layer, no electric potential is present between the films. However, when the Kapton film touches the TENG, electrons are transferred from the silicone rubber layer to the Kapton film, yielding a positively and negatively charged silicone rubber layer and Kapton film, respectively (Fig. 8b(i)). When the Kapton film is separated and removed, PMP DN ICH provides a negative charge to compensate for the positive charge on the surface of the silicone rubber layer, leading to electron flow from the external circuit to PMP DN ICH (Fig. 8b(ii)). Subsequently, an electrostatic equilibrium is achieved when the Kapton film and silicone rubber layers are completely detached (Fig. 8b(iii)). Once the Kapton film is reconnected to the TENG, electrons are repelled from the PMP DN ICH electrode to ground (Fig. 8b(iv)). Finally, an alternating current (AC) electric signal is generated through continuous contact-separation events.
Typical electrical output measurements of a standard PMP DN ICH-based TENG (40 × 40 mm2; frequency, 2 Hz) were performed under a force load of 2 N. The open-circuit voltage (Voc), short-circuit current (Isc), and transferred short-circuit charge (Qsc) of the devised TENG were 66.0 V, 0.18 μA, and 20.6 nC, respectively (Fig. 8c). The electrical output performance of the PMP DN ICH-based TENG under various frequencies (1–3 Hz) was measured under a force load of 2 N (Fig. 8d). It was found that the Voc remained relatively stable and reached 67.6 V. Moreover, the TENG could drive loads under different external resistances of 105–1010 Ω (Fig. 8e), with the optimal output power density being 77.3 mW m−2 at a load resistance of 2 × 108 Ω. The output voltage stability of the TENG was then monitored for 10,000 contact-separation cycles at a frequency of 2 Hz (Fig. 8f). The superior electrical output reliability indicated that the TENG could satisfy practical application requirements. Subsequently, the TENG was connected to external capacitive loads and LEDs in a commercial rectifier circuit (Fig. 8g). Furthermore, the ability of the TENG to be continuously charged was analyzed at different capacitances (Fig. 8h). Notably, the charging speed accelerated with decreasing capacitance, with the 4.7 and 22 µF capacitors achieving voltages of 5.2 and 1.6 V, respectively, by tapping the device for 200 s at a frequency of 2 Hz. Additionally, the charging ability of the TENG as a power source for real-time practical applications was further assessed by illuminating 68 green commercial LEDs (Fig. 8i and Movie S10), underscoring the significant application potential of the devised TENG for low-frequency mechanical energy harvesting.
4 Conclusion
A PMP-based DN ICH with excellent temperature resistance, acceptable mechanical properties, outstanding conductivity, long-term stability, high oxidation resistance, and antibacterial activity was successfully prepared using freeze–thawing and ionizing radiation technology. Experimental results demonstrated the high sensitivity, fast response ability, and excellent sensing stability of PMP DN ICH; consequently, the ICH was applied to human motion monitoring and thermal sensing to probe environmental temperature changes. The all-solid-state SC based on PMP DN ICH operated adequately during prolonged storage as well as at various temperatures and under different mechanical stimuli. More importantly, the single-electrode PMP DN ICH-based TENG exhibited favorable energy-harvesting performance as a self-charging power system. These applications illuminate that this work provides an important approach to construct high-performance ICH for multifunctional/flexible wearable sensing, energy-storage, and energy-harvesting technologies. In addition, the PMP DN ICH may have broad application prospects in smart wearable devices, human–machine, and advanced energy-storage devices.
References
X. Yao, S. Zhang, L. Qian, N. Wei, V. Nica et al., Super stretchable, self-healing, adhesive ionic conductive hydrogels based on tailor-made ionic liquid for high-performance strain sensors. Adv. Funct. Mater. 32, 2204565 (2022). https://doi.org/10.1002/adfm.202204565
S. Wang, D. Zhang, X. He, J. Zhou, Y. Zhou et al., Anti-swelling zwitterionic hydrogels as multi-modal underwater sensors and all-in-one supercapacitors. ACS Appl. Polym. Mater. 4, 7498–7507 (2022). https://doi.org/10.1021/acsapm.2c01202
X. Luo, L. Zhu, Y.-C. Wang, J. Li, J. Nie et al., A flexible multifunctional triboelectric nanogenerator based on MXene/PVA hydrogel. Adv. Funct. Mater. 31, 2104928 (2021). https://doi.org/10.1002/adfm.202104928
J. Xu, R. Jin, X. Ren, G. Gao, A wide temperature-tolerant hydrogel electrolyte mediated by phosphoric acid towards flexible supercapacitors. Chem. Eng. J. 413, 127446 (2021). https://doi.org/10.1016/j.cej.2020.127446
W. Peng, L. Han, Y. Gao, Z. Gong, T. Lu et al., Flexible organohydrogel ionic skin with ultra-low temperature freezing resistance and ultra-durable moisture retention. J. Colloid Interface Sci. 608, 396–404 (2022). https://doi.org/10.1016/j.jcis.2021.09.125
C. Ge, Y. Ling, S. Yan, S. Luan, H. Zhang et al., Preparation and mechanical properties of strong and tough poly (vinyl alcohol)-polypeptide double-network hydrogels. Eur. Polym. J. 99, 504–510 (2018). https://doi.org/10.1016/j.eurpolymj.2018.01.005
Y. Ye, Y. Zhang, Y. Chen, X. Han, F. Jiang, Cellulose nanofibrils enhanced, strong, stretchable, freezing-tolerant ionic conductive organohydrogel for multi-functional sensors. Adv. Funct. Mater. 30, 2003430 (2020). https://doi.org/10.1002/adfm.202003430
H. Zhou, J. Lai, B. Zheng, X. Jin, G. Zhao et al., From glutinous-rice-inspired adhesive organohydrogels to flexible electronic devices toward wearable sensing, power supply, and energy storage. Adv. Funct. Mater. 32, 2108423 (2022). https://doi.org/10.1002/adfm.202108423
J. Yin, K. Wei, J. Zhang, S. Liu, X. Wang et al., MXene-based film electrode and all-round hydrogel electrolyte for flexible all-solid supercapacitor with extremely low working temperature. Cell Rep. Phys. Sci. 3, 100893 (2022). https://doi.org/10.1016/j.xcrp.2022.100893
J. Liu, J. Huang, Q. Cai, Y. Yang, W. Luo et al., Design of slidable polymer networks: a rational strategy to stretchable, rapid self-healing hydrogel electrolytes for flexible supercapacitors. ACS Appl. Mater. Interfaces 12, 20479–20489 (2020). https://doi.org/10.1021/acsami.0c03224
Y. Zhou, C. Wan, Y. Yang, H. Yang, S. Wang et al., Highly stretchable, elastic, and ionic conductive hydrogel for artificial soft electronics. Adv. Funct. Mater. 29, 1806220 (2019). https://doi.org/10.1002/adfm.201806220
J. Le Bideau, L. Viau, A. Vioux, Ionogels, ionic liquid based hybrid materials. Chem. Soc. Rev. 40, 907–925 (2011). https://doi.org/10.1039/c0cs00059k
Y.-R. Gao, J.-F. Cao, Y. Shu, J.-H. Wang, Research progress of ionic liquids-based gels in energy storage, sensors and antibacterial. Green Chem. Eng. 2, 368–383 (2021). https://doi.org/10.1016/j.gce.2021.07.012
S. Zheng, W. Li, Y. Ren, Z. Liu, X. Zou et al., Moisture-wicking, breathable, and intrinsically antibacterial electronic skin based on dual-gradient poly(ionic liquid) nanofiber membranes. Adv. Mater. 34, e2106570 (2022). https://doi.org/10.1002/adma.202106570
H. Lee, A. Erwin, M.L. Buxton, M. Kim, A.V. Stryutsky et al., Shape persistent, highly conductive ionogels from ionic liquids reinforced with cellulose nanocrystal network. Adv. Funct. Mater. 31, 2103083 (2021). https://doi.org/10.1002/adfm.202103083
W. Qian, J. Texter, F. Yan, Frontiers in poly(ionic liquid)s: syntheses and applications. Chem. Soc. Rev. 46, 1124–1159 (2017). https://doi.org/10.1039/c6cs00620e
F. Xie, X. Gao, Y. Yu, F. Lu, L. Zheng, Dually cross-linked single network poly(ionic liquid)/ionic liquid ionogels for a flexible strain-humidity bimodal sensor. Soft Matter 17, 10918–10925 (2021). https://doi.org/10.1039/d1sm01453f
T. Lin, S. Li, Y. Hu, L. Sheng, X. Chen et al., Ultrastretchable and adhesive agarose/Ti3C2Tx-crosslinked-polyacrylamide double-network hydrogel for strain sensor. Carbohydr. Polym. 290, 119506 (2022). https://doi.org/10.1016/j.carbpol.2022.119506
L.-W. Xia, R. Xie, X.-J. Ju, W. Wang, Q. Chen et al., Nano-structured smart hydrogels with rapid response and high elasticity. Nat. Commun. 4, 2226 (2013). https://doi.org/10.1038/ncomms3226
Z. Wang, H. Zhou, D. Liu, X. Chen, D. Wang et al., A structural gel composite enabled robust underwater mechanosensing strategy with high sensitivity. Adv. Funct. Mater. 32, 2201396 (2022). https://doi.org/10.1002/adfm.202201396
J.P. Gong, Why are double network hydrogels so tough? Soft Matter 6, 2583–2590 (2010). https://doi.org/10.1039/B924290B
J.-N. Liu, Q. He, M.-Y. Pan, K. Du, C.-B. Gong et al., An energy-saving, bending sensitive, and self-healing PVA-borax-IL ternary hydrogel electrolyte for visual flexible electrochromic strain sensors. J. Mater. Chem. A 10, 25118–25128 (2022). https://doi.org/10.1039/D2TA06667J
J.J. Paik, B. Jang, S. Nam, L.J. Guo, A transparent poly(vinyl alcohol) ion-conducting organohydrogel for skin-based strain-sensing applications. Adv. Healthc. Mater. 12, e2300076 (2023). https://doi.org/10.1002/adhm.202300076
S. Wu, L. Tang, Y. Xu, J. Yao, G. Tang et al., A self-powered flexible sensing system based on a super-tough, high ionic conductivity supercapacitor and a rapid self-recovering fully physically crosslinked double network hydrogel. J. Mater. Chem. C 10, 3027–3035 (2022). https://doi.org/10.1039/D1TC04514H
J. Huang, S. Han, J. Zhu, Q. Wu, H. Chen et al., Mechanically stable all flexible supercapacitors with fracture and fatigue resistance under harsh temperatures. Adv. Funct. Mater. 32, 2270200 (2022). https://doi.org/10.1002/adfm.202270200
H. Fang, J. Wang, L. Li, L. Xu, Y. Wu et al., A novel high-strength poly(ionic liquid)/PVA hydrogel dressing for antibacterial applications. Chem. Eng. J. 365, 153–164 (2019). https://doi.org/10.1016/j.cej.2019.02.030
Y. Li, J. Yan, Y. Liu, X.-M. Xie, Super tough and intelligent multibond network physical hydrogels facilitated by Ti3C2Tx MXene nanosheets. ACS Nano 16, 1567–1577 (2022). https://doi.org/10.1021/acsnano.1c10151
X. Suo, X. Cui, L. Yang, N. Xu, Y. Huang et al., Synthesis of ionic ultramicroporous polymers for selective separation of acetylene from ethylene. Adv. Mater. 32, e1907601 (2020). https://doi.org/10.1002/adma.201907601
W. Zhao, J. Jiang, W. Chen, Y. He, T. Lin et al., Radiation synthesis of rapidly self-healing, durable, and flexible poly(ionic liquid)/MXene gels with anti-freezing property for multi-functional strain sensors. Chem. Eng. J. 468, 143660 (2023). https://doi.org/10.1016/j.cej.2023.143660
M. Shi, T. Lin, Y. Wang, Y. Hu, J. Peng et al., One-step radiation synthesis of novel star-shaped polymeric ionic liquid–POSS gel electrolytes with high ionic conductivity and mechanical properties for supercapacitor. J. Mater. Sci. 55, 16347–16359 (2020). https://doi.org/10.1007/s10853-020-05162-9
S. Zhang, Y. Zhang, B. Li, P. Zhang, L. Kan et al., One-step preparation of a highly stretchable, conductive, and transparent poly(vinyl alcohol)-phytic acid hydrogel for casual writing circuits. ACS Appl. Mater. Interfaces 11, 32441–32448 (2019). https://doi.org/10.1021/acsami.9b12626
O. Hu, J. Lu, G. Chen, K. Chen, J. Gu et al., An antifreezing, tough, rehydratable, and thermoplastic poly(vinyl alcohol)/sodium alginate/poly(ethylene glycol) organohydrogel electrolyte for flexible supercapacitors. ACS Sustainable Chem. Eng. 9, 9833–9845 (2021). https://doi.org/10.1021/acssuschemeng.1c02464
X. Liu, J. Qin, J. Wang, Y. Chen, G. Miao et al., Robust conductive organohydrogel strain sensors with wide range linear sensing, UV filtering, anti-freezing and water-retention properties. Colloids Surf. A 632, 127823 (2022). https://doi.org/10.1016/j.colsurfa.2021.127823
L. Mao, S. Hu, Y. Gao, L. Wang, W. Zhao et al., Biodegradable and electroactive regenerated bacterial cellulose/MXene (Ti3C2tx) composite hydrogel as wound dressing for accelerating skin wound healing under electrical stimulation. Adv. Healthc. Mater. 9, e2000872 (2020). https://doi.org/10.1002/adhm.202000872
Y. Zhu, J. Liu, T. Guo, J.J. Wang, X. Tang et al., Multifunctional Ti3C2Tx MXene composite hydrogels with strain sensitivity toward absorption-dominated electromagnetic-interference shielding. ACS Nano 15, 1465–1474 (2021). https://doi.org/10.1021/acsnano.0c08830
H. Qiao, P. Qi, X. Zhang, L. Wang, Y. Tan et al., Multiple weak H-bonds lead to highly sensitive, stretchable, self-adhesive, and self-healing ionic sensors. ACS Appl. Mater. Interfaces 11, 7755–7763 (2019). https://doi.org/10.1021/acsami.8b20380
T. Li, Y. Wang, S. Li, X. Liu, J. Sun, Mechanically robust, elastic, and healable ionogels for highly sensitive ultra-durable ionic skins. Adv. Mater. 32, e2002706 (2020). https://doi.org/10.1002/adma.202002706
Y. Yu, P. Yi, W. Xu, X. Sun, G. Deng et al., Environmentally tough and stretchable MXene organohydrogel with exceptionally enhanced electromagnetic interference shielding performances. Nano-Micro Lett. 14, 77 (2022). https://doi.org/10.1007/s40820-022-00819-3
H. Sun, Y. Zhao, S. Jiao, C. Wang, Y. Jia et al., Environment tolerant conductive nanocomposite organohydrogels as flexible strain sensors and power sources for sustainable electronics. Adv. Funct. Mater. 31, 2101696 (2021). https://doi.org/10.1002/adfm.202101696
A. Chae, G. Murali, S.-Y. Lee, J. Gwak, S.J. Kim et al., Highly oxidation-resistant and self-healable MXene-based hydrogels for wearable strain sensor. Adv. Funct. Mater. 33, 2370144 (2023). https://doi.org/10.1002/adfm.202370144
J. Qin, J. Guo, Q. Xu, Z. Zheng, H. Mao et al., Synthesis of pyrrolidinium-type poly(ionic liquid) membranes for antibacterial applications. ACS Appl. Mater. Interfaces 9, 10504–10511 (2017). https://doi.org/10.1021/acsami.7b00387
X. Liu, L. Chang, L. Peng, R. Bai, Y. Wei et al., Poly(ionic liquid)-based efficient and robust antiseptic spray. ACS Appl. Mater. Interfaces 13, 48358–48364 (2021). https://doi.org/10.1021/acsami.1c11481
H. Wang, J. Xu, K. Li, Y. Dong, Z. Du et al., Highly stretchable, self-healable, and self-adhesive ionogels with efficient antibacterial performances for a highly sensitive wearable strain sensor. J. Mater. Chem. B 10, 1301–1307 (2022). https://doi.org/10.1039/d2tb00041e
A. Arabi Shamsabadi, M. Sharifian Gh, B. Anasori, M. Soroush, Antimicrobial mode-of-action of colloidal Ti3C2Tx MXene nanosheets. ACS Sustainable Chem. Eng. 6, 16586–16596 (2018). https://doi.org/10.1021/acssuschemeng.8b03823
J. Zhang, W. Xue, Y. Dai, L. Wu, B. Liao et al., Double network hydrogel sensors with high sensitivity in large strain range. Macromol. Mater. Eng. 306(12), 2100486 (2021). https://doi.org/10.1002/mame.202100486
M. Pi, S. Qin, S. Wen, Z. Wang, X. Wang et al., Rapid gelation of tough and anti-swelling hydrogels under mild conditions for underwater communication. Adv. Funct. Mater. 33, 2210188 (2023). https://doi.org/10.1002/adfm.202210188
J. Liu, H. Wang, T. Liu, Q. Wu, Y. Ding et al., Multimodal hydrogel-based respiratory monitoring system for diagnosing obstructive sleep apnea syndrome. Adv. Funct. Mater. 32, 2204686 (2022). https://doi.org/10.1002/adfm.202204686
J. Huang, S. Peng, J. Gu, G. Chen, J. Gao et al., Self-powered integrated system of a strain sensor and flexible all-solid-state supercapacitor by using a high performance ionic organohydrogel. Mater. Horiz. 7, 2085–2096 (2020). https://doi.org/10.1039/D0MH00100G
S. Long, Y. Feng, F. He, J. Zhao, T. Bai et al., Biomass-derived, multifunctional and wave-layered carbon aerogels toward wearable pressure sensors, supercapacitors and triboelectric nanogenerators. Nano Energy 85, 105973 (2021). https://doi.org/10.1016/j.nanoen.2021.105973
M.Y. Bhat, N. Yadav, S.A. Hashmi, A high performance flexible gel polymer electrolyte incorporated with suberonitrile as additive for quasi-solid carbon supercapacitor. Mater. Sci. Eng. B 262, 114721 (2020). https://doi.org/10.1016/j.mseb.2020.114721
Q. Hu, S. Cui, K. Sun, X. Shi, M. Zhang et al., An antifreezing and thermally stable hydrogel electrolyte for high-performance all-in-one flexible supercapacitor. J. Energy Storage 50, 104231 (2022). https://doi.org/10.1016/j.est.2022.104231
H. Peng, X. Gao, K. Sun, X. Xie, G. Ma et al., Physically cross-linked dual-network hydrogel electrolyte with high self-healing behavior and mechanical strength for wide-temperature tolerant flexible supercapacitor. Chem. Eng. J. 422, 130353 (2021). https://doi.org/10.1016/j.cej.2021.130353
Y. Zhao, B. Zhang, B. Yao, Y. Qiu, Z. Peng et al., Hierarchically structured stretchable conductive hydrogels for high-performance wearable strain sensors and supercapacitors. Matter 3, 1196–1210 (2020). https://doi.org/10.1016/j.matt.2020.08.024
Y. Guo, K. Zheng, P. Wan, A flexible stretchable hydrogel electrolyte for healable all-in-one configured supercapacitors. Small 14, e1704497 (2018). https://doi.org/10.1002/smll.201704497
J. Lu, J. Gu, O. Hu, Y. Fu, D. Ye et al., Highly tough, freezing-tolerant, healable and thermoplastic starch/poly(vinyl alcohol) organohydrogels for flexible electronic devices. J. Mater. Chem. A 9, 18406–18420 (2021). https://doi.org/10.1039/D1TA04336F
C. Cai, W. Zhou, Y. Fu, Bioinspired MXene nacre with mechanical robustness for highly flexible all-solid-state photothermo-supercapacitor. Chem. Eng. J. 418, 129275 (2021). https://doi.org/10.1016/j.cej.2021.129275
Q. Liu, J. Zhou, C. Song, X. Li, Z. Wang et al., 2.2V high performance symmetrical fiber-shaped aqueous supercapacitors enabled by “water-in-salt” gel electrolyte and N-doped graphene fiber. Energy Storage Mater. 24, 495–503 (2020). https://doi.org/10.1016/j.ensm.2019.07.008
C. Ma, D. Hou, J. Jiang, Y. Fan, X. Li et al., Elucidating the synergic effect in nanoscale MoS2/TiO2 heterointerface for Na-ion storage. Adv. Sci. 9, e2204837 (2022). https://doi.org/10.1002/advs.202204837
E. Cevik, S.T. Gunday, A. Bozkurt, R. Amine, K. Amine, Bio-inspired redox mediated electrolyte for high performance flexible supercapacitor applications over broad temperature domain. J. Power. Sources 474, 228544 (2020). https://doi.org/10.1016/j.jpowsour.2020.228544
Acknowledgements
The authors would like to thank the National Natural Science Foundation of China (11875138, 52077095) and the Analysis and Testing Center of Huazhong University of Science and Technology for providing the experimental measurements. The authors thank the Accelerator and Radiation Processing Research Division of Huazhong University of Science and Technology for its technical support. The authors thank Professor Fei Song and Dr. Bo Tang from State Key Laboratory of Polymer Materials Engineering, National Engineering Laboratory of Eco-Friendly Polymeric Materials (Sichuan), Sichuan University, for its technical support.
Author information
Authors and Affiliations
Corresponding author
Ethics declarations
Conflict of interest
The authors declare no interest conflict. They have no known competing financial interests or personal relationships that could have appeared to influence the work reported in this paper.
Supplementary Information
Below is the link to the electronic supplementary material.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Zhao, W., Zhou, H., Li, W. et al. An Environment-Tolerant Ion-Conducting Double-Network Composite Hydrogel for High-Performance Flexible Electronic Devices. Nano-Micro Lett. 16, 99 (2024). https://doi.org/10.1007/s40820-023-01311-2
Received:
Accepted:
Published:
DOI: https://doi.org/10.1007/s40820-023-01311-2