Highlights
-
Atomically substitutional engineering in binary transition metal dichalcogenides (TMDs) enables the facile production of ternary or quaternary TMDs with tunable (opto)electronic properties spanning the entire compositional spectrum.
-
A comprehensive overview is provided on multinary TMDs, including Janus-type structures, aiming to elaborate on their theoretical foundations, synthetic strategies, tailored properties, and superior applications.
-
The challenges and opportunities faced in accelerating the exploitation of multinary TMDs as highly promising nanomaterials are discussed.
Abstract
Transition metal dichalcogenides (TMDs) are a promising class of layered materials in the post-graphene era, with extensive research attention due to their diverse alternative elements and fascinating semiconductor behavior. Binary MX2 layers with different metal and/or chalcogen elements have similar structural parameters but varied optoelectronic properties, providing opportunities for atomically substitutional engineering via partial alteration of metal or/and chalcogenide atoms to produce ternary or quaternary TMDs. The resulting multinary TMD layers still maintain structural integrity and homogeneity while achieving tunable (opto)electronic properties across a full range of composition with arbitrary ratios of introduced metal or chalcogen to original counterparts (0–100%). Atomic substitution in TMD layers offers new adjustable degrees of freedom for tailoring crystal phase, band alignment/structure, carrier density, and surface reactive activity, enabling novel and promising applications. This review comprehensively elaborates on atomically substitutional engineering in TMD layers, including theoretical foundations, synthetic strategies, tailored properties, and superior applications. The emerging type of ternary TMDs, Janus TMDs, is presented specifically to highlight their typical compounds, fabrication methods, and potential applications. Finally, opportunities and challenges for further development of multinary TMDs are envisioned to expedite the evolution of this pivotal field.
Similar content being viewed by others
Avoid common mistakes on your manuscript.
1 Introduction
The discovery and in-depth investigation of graphene have led to considerable attention toward two-dimensional (2D) nanomaterials as a new family in the materials world, with potential applications in medical treatment, environmental detections, energy exploitation, and photoelectric devices [1,2,3,4,5,6,7,8]. Numerous 2D members have emerged in the post-graphene era, including transition metal dichalcogenides (TMDs), black phosphorus, hexagonal boron nitride, graphitic carbon nitride, and more [9,10,11,12,13,14]. With the comprehensive exploitation of diverse 2D nanomaterials, finding and tuning their novel features has become a goal to broaden and facilitate their utilization. However, 2D nanomaterials with fixed properties are incapable of satisfying the advanced application scenarios in efficiency, stability, specificity, and operability [15,16,17,18,19]. To improve their performance, elemental doping and other nanomaterials-involved hybridization have been greatly developed [20,21,22,23]. Elemental doping is a tried-and-tested strategy to modulate the band structure of 2D nanomaterials and endows tailored properties toward varied (opto)electronic devices, although the doping rate is usually restricted to < 10%, leading to a limited ability for modulating properties by introducing defects or other elements [10, 24, 25]. Alternatively, nanostructured hybridization is realized via surface adsorption of 2D nanomaterials or covalent linkage with other nanostructures to form heterojunction for more or better functionalities [19, 26, 27]. However, it is challenging to intrinsically modulate the nature of 2D nanomaterials via external contact, and the formed interface between two hybrid species exhibits a high transfer barrier for carriers, compromising the responsiveness and reaction rate of the hybridized compounds [28,29,30,31].
TMD monolayers consist of three layers of atoms with a transition metal layer sandwiched between two chalcogen layers (i.e., X–M–X), as shown in Fig. 1a. The transition metal typically ranges from Group IVB to VIIB, while the chalcogen is S, Se, or Te in Group VIA. Many types of binary compounds with a chemical formula of MX2 are included in 2D TMDs, such as MoS2, WS2, MoSe2, and MoTe2. These TMD materials exhibit diverse optoelectronic properties from semiconductivity, semi-metallicity, metallicity to superconductivity, depending on their chemical composition and/or crystal phase, despite similar structural parameters [32,33,34,35,36,37]. Recently, the evolution in properties for these binary TMDs has inspired scientists to develop new degrees of freedom for tuning/optimizing the properties of 2D TMDs “from the inside out” by partly substituting the transition metal with ones from the same or adjacent group and/or the chalcogens with another type of chalcogen atom, ultimately forming ternary or quaternary TMD layers (Fig. 1b, c).
With good miscibility, atoms from the same or adjacent group can be introduced in binary TMDs at any percentage, and the resulting ternary or quaternary TMD layers maintain their structural integrity and homogeneity to easily obtain a series of fully composition-tunable structural and (opto)electronic properties between the two end-TMDs (Fig. 1d) [38,39,40,41,42,43]. For instance, the optical bandgap of MoS2xSe2(1−x) monolayers can be continuously tuned from 1.557 to 1.856 eV as the S composition increases [44]. In monolayer MoxRe1−xS2, the strong band bowing effect extends the photoresponse wavelength from visible light (633 nm) to NIR light (1,550 nm) [45]. After combining two TMDs with different carrier types in WS2xSe2−2x monolayers, the conductive behavior is gradually regulated from p-type to weak bipolar and then to n-type with increasing S composition [46]. As the filling of d orbitals in multinary TMDs changes continuously with the composition, phase engineering of 2D TMDs can be readily achieved via atomic substitution (e.g., WSe2(1−x)Te2x exhibits tunable crystal phases from semiconducting 2H phase to metallic 1T’ phase as x increases) [47, 48]. Recently, Liu’s team even observed superconductivity and Weyl semi-metallic features in Mo-rich Mo0.8W0.2Te2 and W-rich Mo0.2W0.8Te2 layers, respectively [49]. Meanwhile, ternary Janus TMD monolayers with different chalcogens on the top and bottom side of the transition metal break the crystal mirror symmetry to generate permanent built-in vertical dipole moments [50, 51].
Ternary or quaternary TMD layers have emerged as a promising upgraded material compared to pristine binary TMDs, offering significantly improved performance and exotic behaviors due to their tunable and tailored properties. For example, MoS2-based photodetectors show excellent photoresponsivity with a relatively long response time, while the introduction of tin to form Mo1−xSnxS2 layers can modulate the defect-induced trap states to tremendously shorten the photoresponse time [52]. Atomically substitutional engineering can also enhance the catalytic activity in hydrogen evolution reaction (HER) by decreasing the adsorption-free energy of TMDs toward hydrogen, and the relatively big lattice mismatch can form vacancies on the basal plane to provide more catalytic active sites [53,54,55]. Recently, more and more multinary TMDs with controlled composition in special crystalline structures have been successfully fabricated to exhibit unique and excellent properties for better applications, fuel immense interest, and further research in the interdisciplinary realm of materials, physics, chemistry, and electronics. This review provides a systematic overview of recent advancements in burgeoning ternary and quaternary TMD layers. It begins with the concept of atomically substitutional engineering, classification of TMDs, substituting principles/rules, and synthetic strategies. The paper then elaborates on various tunable properties and exotic behaviors of multinary TMD layers, followed by recent exploitation on novel/enhanced applications of multinary TMDs. As an emerging ternary TMD, Janus TMDs are also presented, from their theoretical foundation to fabrication approaches and potential applications. Finally, the challenges facing TMDs are discussed in detail, and opportunities in this pivotal field are envisioned to navigate further exploration and investigation of multinary TMDs in the future.
2 Concepts and Rules for Atomic Substitution in TMDs
Various functionalization strategies have been developed to construct novel 2D nanosystems for next-generation high-performance devices, including elemental doping, hybridization with other nanomaterials, and atomic substitution in TMDs (also known as alloyed TMDs and abbreviated as ATMDs). Table 1 summarizes their individual characteristics and main advantages. Elemental doping allows for a wide variety of available elements, but the proportion of introduced atoms is typically restricted to less than 10% due to lattice mismatch [10, 24, 25]. Heterojunctions are established via surface adsorption or covalent linkage in hybrids of TMDs with diversified nanostructures, allowing for new carrier separation and transfer channels that enhance the application of 2D TMDs in catalysis [19, 27]. However, the heterogeneous interface can present a high transfer barrier for carriers, compromising hybrid compound responsiveness and reaction rate. In comparison, atomic substitution in TMDs offers the ability to form random solid solutions with different transition metals from the same or adjacent group and/or different chalcogens. This form of substitution can easily regulate the properties of 2D TMDs “from the inside out” via the creation of ternary or quaternary TMDs. The resulting multinary TMDs introduce a full range of compositions in TMDs while maintaining crystal integrity and homogeneity so that crystal phase, bandgap, band alignment/structure, carrier type/density, basal-plane activity, and electroconductibility (metallicity, semiconductivity, or Wyle semi-metallicity) can be flexibly tuned [41, 45, 46, 48, 56,57,58,59]. The multinary atomic layers of TMDs not only expand the family of 2D nanomaterials, but also unlock the exotic physical and chemical properties of TMDs for greatly improved performance in optoelectronic applications.
To achieve atomic substitution in binary TMD layers (MX2, Fig. 1a), an additional transition metal element and/or a different chalcogen element is introduced into a TMD layer at any proportion while maintaining the layered structure. This results in ternary or quaternary TMDs. In contrast to the case of binary TMDs with the chemical formula MX2, ternary TMDs can be classified as M1−xNxX2 (MNX type) and MX2(1−x)Y2x (MXY type), where M/N represents different transition metal elements from Group IVB, VB, VIB, or VIIB, and X/Y represents different chalcogen elements (Fig. 1c). Additionally, there are emerging MXY-type TMDs with a highly ordered Janus structure of TMDs. These Janus TMDs contain different chalcogen elements on the top and bottom of the middle metal layer, such as S–Mo–Se [50]. This unique configuration breaks the out-of-plane structural symmetry, generating permanent built-in vertical dipole moments (see the detailed demonstration in Sect. 6) [50, 60]. It is worth noting that Sn-based metal dichalcogenides (for example, SnS2) have a similar layered crystal structure as TMDs, making Sn a promising candidate for atomic substitution in binary TMDs with outstanding optoelectronic performance, as reported previously [52, 57, 61,62,63,64].
Before designing and fabricating multinary TMD layers, it is crucial to assess the possibility of atomic substitution theoretically with considering a wide range of atomic incorporation from 0 to 100% in experiments. In evaluating the feasibility, parameters such as lattice constant and bandgap of the two types of TMDs for the final ternary or quaternary atomic layers, also known as end-TMDs, must be taken into account. For instance, MoS2 (x = 0) and WS2 (x = 1) serve as the end-materials of Mo1−xWxS2 layers. Yakobson’s group provided a set of rules to choose possible candidates for end-materials, which includes: (1) |a1 − a2|/max{a1, a2} < 0.034, (2) ΔdM–X < 0.1 Å, (3) (Eg1 > 0) or (Eg2 > 0) [65]. Here, a1 and a2 represent the lattice constants of the two end-materials, ΔdM–X is the difference in bond length between metal−chalcogen, Eg1 and Eg2 are the bandgaps of the two end-TMDs, respectively. The first and second rules require a good match in lattice constants and metal–chalcogen bond distances between the two end-materials. Ternary TMDs that consist of two end-materials with large lattice mismatches and even different crystal structures often exhibit poor miscibility and a tendency to separate or segregate into distinct phases. This phase separation has detrimental consequences for their intrinsic properties and their applications in devices. To address this issue, it is necessary to elevate the temperature sufficiently to improve the miscibility or solubility of the ternary TMDs [66, 67]. Meanwhile, the third rule guarantees that at least one of the end-materials is semiconducting for tunable bandgap achievement. Based on these rules, the pairs of end-materials are summarized in Fig. 2a according to the differences in theoretical bandgap and lattice constant [65]. The data points on the left side correspond to relatively small lattice mismatch, making them promising candidates for multinary TMDs. Additionally, the data points located in the top left (blue shade) signify that the two end-TMDs are metallic and semiconducting, respectively, leading to a fascinating metal–semiconductor phase transition as x changes.
To assess the thermodynamic stability of miscible ternary TMD layers, the mixing enthalpy (ΔHmix) can be used as an important reference for variable lattice matching degrees (ΔdM–X) [66, 67]. Over the past few years, the cluster expansion (CE) method has been used to calculate the mixing enthalpies of diverse ternary TMDs, allowing for an assessment of their thermodynamic stability through the full microscopic description of atomic configurations in a crystal [42, 65, 66]. Studies from first-principles simulation together with the CE method have calculated the ΔHmix of 2H-phase Mo- and W-based MXY-type TMD monolayers with different compositions and configurations [66]. As seen in Fig. 2b, the ΔHmix of the MoS2(1−x)Se2x random alloys at all compositions are almost negative (red dashed line), indicating that the ternary TMDs are stable and that random solid solutions are favored at 0 K. This phenomenon can be attributed to the small lattice mismatch between the two end-materials and the energy gain induced by the large additional charge exchange in such alloys [66, 67, 69, 70]. Similar calculations showed that the ΔHmix of WS2(1−x)Se2x and Mo1−xWxS2 random alloys at all compositions were also confirmed to be negative [65, 66]. This makes it easy to synthesize and preserve such ternary TMDs with complete miscibility in some practical experiments [42, 59, 66, 68, 71,72,73]. On the other hand, the ΔHmix of MoSe2(1−x)Te2x, WSe2(1−x)Te2x, MoS2(1−x)Te2x (Fig. 2c), and WS2(1−x)Te2x random alloys are all positive due to relatively large lattice mismatch and different crystal phases between the two end-materials [66]. Thus, these ternary TMDs have no energetically favorable configuration/structure at 0 K and will undergo phase separation/segregation, requiring higher temperatures to improve their miscibility/solubility [48, 67, 74, 75].
It has been found that single-phase random solid solutions can also be obtained for ternary TMDs with positive ΔHmix at sufficiently high temperatures due to the large entropic energy gain [66, 69]. Indeed, the stability of ternary TMDs depends on the change in Gibbs free energy of mixing (ΔGmix), which can be expressed by ΔGmix(x; T) = ΔHmix(x) − TΔS(x) [68]. When ΔHmix is greater than zero, ΔGmix can be reduced to a negative value by increasing temperature because the entropy (ΔS) is positive [66, 68, 75]. Therefore, the calculation and evaluation of enthalpy and entropy are crucial prerequisites for obtaining stable and single-phase uniform ATMDs. For example, Amin and his colleagues used density functional theory (DFT) to calculate the ΔHmix and the temperature-dependent − TΔS of the random 2H-phase W1−xNbxS2 monolayer (Fig. 2d–e) [68]. Their results showed that as the temperature increases, the entropy term gradually dominates to reduce the ΔGmix, making the W1−xNbxS2 random alloys more stable. Based on the analysis of temperature-dependent stability (equilibrium phase diagram), the composition of an ATMD at a given finite temperature can be divided into three regions: stable, metastable, and unstable (Fig. 2f). At 640 K, the three regions meet, indicating that single-phase W1−xNbxS2 random solid solutions are stabilized at arbitrary composition (i.e., the miscibility temperature). As summarized in Fig. 2g, the miscibility temperatures of 20 MNX-type and 5 MXY-type 2H-phase ATMDs were systematically calculated using first-principles DFT modeling and were further confirmed by experimental synthesis. These findings and discussions indicate that the theoretical work provides valuable guidance for producing random and uniform/homogeneous ATMDs.
In the fabrication of 2D ATMDs, high temperature is generally required and atomic substitution in TMDs can induce lattice distortion to increase their configurational entropies. This often results in the production of ATMDs in a random phase rather than a separated phase [76]. Meanwhile, the degree of alloying/uniformity of the synthesized ATMDs varies depending on the used precursors, synthetic strategies, and experimental conditions [45, 55, 65, 68, 77, 78]. In addition to thermodynamic stability, atomic distribution and electronic properties are also significant factors that influence the crystal phase of 2D ATMDs due to their different filling of the d orbitals [39, 45, 47, 77]. Dynamic stability should also be considered during the fabrication and utilization of 2D ATMDs. Through molecular dynamics (MD) simulations, Ajayan and his colleagues investigated the effect of composition (x) of MoxW1−xS2 alloys on their mechanical stability and found that the alloying of MoS2 can withstand higher stress values but reduces its failure strain [79].
3 Strategies and Approaches for Atomic Substitution in TMD Layers
Once the feasibility of multinary TMDs has been ensured using the aforementioned rules, atomic substitution in binary TMD layers can be achieved through two approaches: top–down and bottom–up. In the top–down approach, massive layered ATMD bulky crystals are first synthesized and then exfoliated into atomically thin layers [48, 80, 81]. This approach includes mechanical exfoliation and liquid exfoliation. In contrast, the bottom–up approach involves synthesizing single-/few-layer ATMD nanosheets directly from appropriate precursors. This approach includes hydro/solvothermal reaction, chemical vapor deposition, pulsed laser deposition, and so on [52, 82,83,84,85,86]. The synthesis of parent bulky crystals in the top–down approach typically requires high temperatures and a lengthy chemical vapor transport (CVT) process (~ 1 week). Although the resulting bulk ATMDs have high crystal quality, to obtain atomically thin (monolayer or few-layer) ATMDs requires an additional manual micromechanical or liquid exfoliation process, which introduces randomness in the layer number, morphology, and size of exfoliated ATMD layers, limiting their scaling-up applications [3, 78, 87,88,89]. To achieve highly controllable synthesis of various 2D ATMDs, bottom–up approaches can utilize diversified chemical precursors and precisely adjustable experimental conditions to fabricate numerous 2D ATMDs with high quality and excellent performance. In this discussion, we will mainly focus on the bottom–up approaches after briefly describing liquid exfoliation.
3.1 Liquid Exfoliation
Both sonication-assisted and ion intercalation-assisted methods of liquid exfoliation are capable of producing dispersive nanosheets in liquid with high yield, while also meeting the requirements of low cost and simple operation [90, 91]. During sonication-assisted liquid exfoliation, ultrasonic waves induce bubbles between layers of bulk crystals, and the micromechanical forces generated by the bursting of these bubbles drive the materials to be exfoliated into monolayers [3, 92]. By contrast, the ion intercalation-assisted liquid exfoliation method involves the insertion of small metal ions (such as Li+ or Na+) into the layered crystals to expand the interlayer spacing, which weakens the van der Waals interaction between adjacent layers and facilitates the separation of ATMD layers [3, 53, 90]. Interestingly, the introduction of small metal ions into ATMD layers can increase the electron density of the d orbitals of transition metals, leading to a phase transformation from 2H to 1T [39, 53]. As illustrated in Fig. 3, a Li-ion intercalation-assisted liquid exfoliation method was developed using LiPF6 as the electrolyte, which allowed for the preparation of a high concentration (~ 66%) of metallic 1T-phase MoS2xSe2(1−x) and MoxW1−xS2 nanosheets from their 2H-phase bulk crystals [80].
3.2 Hydrothermal and Solvothermal Reaction
Hydro/solvothermal reactions involve mixing preselected precursors (such as metal salts and chalcogens) and appropriate solvents in a closed reactor, under specific experimental conditions. By manipulating the relative amounts of reactants and controlling various experimental factors such as temperature, precursor state, and surfactant, ATMDs can be fabricated with adjustable compositions (ranging from 0 to 1), tunable sizes, and multifarious morphologies. For instance, Kang’s team utilized chloride (MoCl5 and NbCl5) or sodium salts (Na2MoO4 and NaReO4) as metal precursors to synthesize a series of ATMD nanosheets with fully tunable compositions via hydro/solvothermal reactions, including Re1−xMoxSe2, Re1−xMoxS2, and Mo1−xNbxSe2 (as illustrated in Fig. 4) [55, 93, 94]. The reactions were conducted at relatively low temperatures of ~ 300 °C, which resulted in such ATMDs being prone to phase segregation and domain separation, and annealing treatments were required to ameliorate their miscibility. Interestingly, both experimental results and theoretical simulations demonstrated that a certain degree of phase separation can promote the formation of atomic vacancies, significantly enhancing their electrocatalytic activity [93].
3.3 Chemical Vapor Deposition
The chemical vapor deposition (CVD) process is commonly executed in a tubular furnace divided into multiple temperature zones. Diverse precursors and substrates, such as SiO2/Si, mica or Al2O3, are positioned in different temperature zones. The high-temperature vaporized precursors are transported to a specific location using a carrier gas to initiate the growth of 2D ATMDs via reaction/deposition. The excess carrier gas and precursors are subsequently discharged out of the tube, as illustrated in Fig. 5a [95,96,97]. By adjusting key growth parameters like precursors (type, state, and pretreatment mode), promoters/additives, substrates, and gas flow, precisely controlled growth of various ATMD layers can be achieved with fully tunable compositions, high quality, and adjustable size/morphology/layer number [4, 96, 98,99,100]. The high-temperature deposition and 2D growth of CVD-fabricated ATMDs (> 700 °C) result in excellent crystallinity and uniformity/homogeneity, and the directly grown ATMDs on SiO2/Si substrates ensure good contact, facilitating the fabrication of high-performance (opto)electronic devices. Additionally, modified CVD methods such as additive-assisted CVD, confined-space CVD, and inductively coupled plasma-CVD have been recently developed to fabricate ATMD layers with well-crystalline quality and tailored properties [4, 33, 52, 101, 102]. In a more inspiring development, a novel technique called modularized local-precursor-supply CVD has successfully enabled the batch manufacturing of wafer-scale homogeneous multinary TMDs by supplying uniform precursors to wafers face-to-face in designed modules, providing a powerful path for the industrialized application of ATMDs, especially in (opto)electronics [103,104,105].
Liu’s team developed a molten-salt-assisted CVD method that has been shown to lower the melting point of metal precursors, promote the formation of intermediates, and improve the quality of ATMD monolayers by modulating the reaction rate [33]. This method was used to synthesize various high-quality ATMD monolayers, which proved to be a powerful strategy for investigating the fundamental properties of ATMDs and fabricating high-performance devices (Fig. 5b). Lee and co-workers selectively synthesized ATMD monolayers and their lateral heterostructures by combining the CVD method with a solution-processed precursor deposition [106]. By precisely controlling the timing and supersaturation degree of liquid-phase precursors, many types of lateral heterostructures were reliably grown (Fig. 5c). This work has opened up new avenues for the manufacture of advanced heterojunction devices, thanks to the tunable structural and electronic properties of ATMD layers. Xiao’s work demonstrated the synthesis of multifarious high-quality ATMD monolayers with large lateral size via a confined-space CVD method [52, 107,108,109]. By introducing an assistant substrate, contaminants and by-products were blocked, thereby significantly increasing the size and crystal uniformity of ATMD monolayers. To accelerate the industrialized application (such as in integrated circuits) of ATMDs, Xue et al. developed a CVD-based modularized strategy for the wafer-scale batch production of multinary TMDs, including the Janus type [103]. This strategy enables vertical stacking of multiple modules and localizes precursor within each module, allowing for the batch fabrication of multinary TMDs on wafer sizes up to 12 inches.
3.4 Physical Vapor Deposition and Other Strategies
Physical vapor deposition (PVD) is a direct method for synthesizing ATMDs from TMDs that can be easily vaporized [46, 84, 110]. For instance, MoS2xSe2(1−x) (x = 0–0.40) monolayers were synthesized successfully by using MoS2 and MoSe2 powders as precursors. The precise tuning of the alloy composition (x) was achieved by controlling the temperature of MoSe2 powders [84]. In another study, the same group introduced Se vapor during the PVD process to prevent the decomposition of MoSe2 to Mo3Se4 at high temperatures. This approach resulted in the successful fabrication of selenium-rich MoS2(1−x)Se2x alloys with x ranging from 0.41 to 1.00 [110]. The lateral size and morphology of MoS2(1−x)Se2x domains can be controlled effectively by tuning the temperature and its gradient in the deposition zone.
In addition to the typical strategies described above, several emerging and advanced approaches have demonstrated great potential for fabricating high-quality ATMDs. One such approach to achieve atomic substitution is through low-energy ion implantation or beam-mediated ion irradiation of pre-existing binary TMDs, such as CVD-grown MX2, allowing for highly controllable fabrication of ATMDs [111,112,113,114,115]. For example, Bartels and co-workers utilized an Ar+-ion beam to remove sulfur atoms from MoS2 monolayers grown on SiO2/Si substrates via CVD and then controlled the insertion cycles of Se precursor to produce MoS2(1−x)Se2x, achieving precise bandgap tuning [113]. Other powerful techniques such as pulsed laser deposition (PLD) and molecular beam epitaxy (MBE) have also been extended to produce high-quality multinary TMDs. For example, Yao and co-workers pioneered the fabrication of centimeter-scale and high-quality Mo0.5W0.5S2 alloy films using PLD for the first time [116]. This approach utilized highly pure Mo, W, and S elements as precursors and resulted in low defect density and unique alloying effects. The Mo0.5W0.5S2-based photodetector exhibited outstanding photoresponse performance. Song et al. reported a novel strategy for synthesizing Mo1−xWxS2 alloys by sulfurizing super-cycle atomic layer deposition (ALD) of Mo1−xWxOy films [117]. The resulting Mo1−xWxS2 alloys exhibited high crystal quality and composition/layer number-dependent bandgaps. Furthermore, a vertically composition-controlled (VCC) Mo1−xWxS2 multilayer was fabricated using multiple continuous super-cycles. The resulting Mo1−xWxS2 multilayer-based photodetector demonstrated much higher photocurrent than MoS2- and WS2-based photodetectors. More recently, Zhang et al. synthesized VxMo1−xSe2 monolayers using a MBE method and systematically investigated the evolution of thermal stability, electronic structure, and magnetism of monolayer VxMo1−xSe2 as a function of V concentration (x) [86]. The results showed that x = 0.44 was a critical value: The alloys at x < 0.44 underwent semiconductor–metal phase separation, but the alloys at x > 0.44 preferred to form stable and homogeneous metallic phases. For better understanding of the different bottom–up methods, their strength and weakness are summarized in Table 2.
4 Diverse Characteristics of Multinary TMDs
In contrast to binary TMDs, multinary TMD layers are created through atomically substitutional engineering that introduces a large number of heteroatoms. This results in substantially modulated properties, such as phase evolution from 2H to 1T/1T’, fully tunable bandgaps, and unique Raman shifts [44, 49, 55]. In this section, we provide an overview of the typical characteristics of multinary TMD layers, their composition-dependent features, and their great potential for various applications.
4.1 Varied Crystal Structures of Multinary TMDs
According to reports, phase transitions in binary TMDs can be achieved through various methods such as high pressure, thermal annealing, and laser/electron-beam irradiation [39, 118]. Similarly, atomic substitution has been found to be a more mild and efficient strategy to induce phase transition/evolution from 2H to 1T/1T’ in TMD layers for enhancing the performance of 2D TMDs. Under harsh conditions, the lattice structures of binary TMDs undergo physical alterations and lattice reconstruction, leading to phase transitions. However, the resulting 1T/1T’-phase TMDs are usually metastable and tend to revert back to the thermodynamically stable 2H phase [39, 118]. In contrast, atomic substitution in TMDs allows for continuous changes in the electron filling within the d orbitals of ATMDs as the composition varies. This leads to the formation of stabilized 1T/1T’-phase ATMDs with homogeneous and integrated crystal structures, providing exciting opportunities for investigating exotic physical phenomena and developing futuristic devices [47, 119,120,121].
As is well-known, the two most common crystal phases in binary TMDs are the 2H phase with trigonal prismatic coordination (D3h symmetry) and the 1T-phase with octahedral coordination (D3d symmetry) [32, 82]. Due to the different filling in the d orbitals of transition metals, TMD nanomaterials exhibit different thermodynamically stable crystal phases and diversified conductive properties, such as semiconductivity, metallicity, and semi-metallicity [39, 119]. Group IVB (d0) and Group VIB (d2) TMDs show stable octahedral structure (1T phase) and trigonal prismatic structure (2H phase), respectively. Group VB (d1) TMDs have both 1T and 2H phases, while Group VIIB (d3) TMDs exhibit a distorted octahedral structure due to the distortion or/and dimerization of metal atoms (i.e., 1T’ phase) [39, 119]. Therefore, ATMD layers composed of two end-materials with different crystal phases will undergo phase transition during the continuous change of electron filling of d orbitals [47, 65]. For instance, Mo1−xRexSe2 alloys will undergo a phase transition from 2H to 1T’ as x increases, with a turning point at x = 0.42 [47]. The phase structure of WTe2xS2(1−x) alloys will transform from 2H to 1T’ at x = 0.45, accompanied by a transition of conductivity from semiconducting to metallic. Interestingly, Group VIB (d2) ATMDs with thermodynamically stable 2H phase still retain the intriguing metastable metallic 1T-phase [80, 122]. In recent research, alloying of TMDs was found to reduce the energy barriers for the phase transition from 2H to 1T, thus facilitating the formation of 1T-phase in Mo1−xWxS2 monolayer via a rapid cooling CVD process [123]. Similarly, Yang et al. synthesized Mo1−xWxS2 nanosheets with 1T/2H phase heterostructures via a one-step liquid-phase reaction, and the 1T/2H phase ratio can be adjusted by tuning the reaction temperature [122].
In addition to thermodynamics, lithium-ion intercalation has also been shown to effectively obtain 1T-phase ATMD monolayers [53, 80]. During lithiation treatment, the transition metal d orbitals’ electron density increases to destabilize the original 2H phase and increase the 1T phase’s stability, leading to a phase transition from 2H to 1T [119]. Zhang’s group, for example, prepared single-layer MoxW1−xS2 and MoS2xSe2(1−x) alloys with a high concentration of metallic 1T-phase from their 2H-phase parent bulk crystals through lithium-ion intercalation [80]. Instead of external approaches, such as those mentioned above, alloying two end-TMDs with different crystal phases can intrinsically change their thermodynamically stable crystal phase by continuously tuning the d-orbital filling, providing composition-dependent tunable crystal phases and extra fascinating properties [47]. In M1−xRexX2 (M = Mo, W; X = S, Se) systems, the insertion and substitution of Re atoms introduce additional electrons into the lattice to fill the higher energy levels of MX2, which destabilizes the triangular prismatic 2H phase. At the same time, it increases the stability of the octahedral 1T/1T’ phase, inducing a phase transformation from 2H to 1T/1T’ [45, 47, 120, 124]. In Yang’s work, the 2H-to-1T’ phase transition was successfully achieved in RexMo1−xS2 monolayers as x increased, and the experimental results and DFT calculations confirmed that the phase transition occurred at approximately x = 0.5 (Fig. 6a–c) [120]. Similarly, Liu’s team achieved phase transitions from 2H to 1T’ in WSe2(1−x)Te2x monolayers at x = 0.5–0.6 (Fig. 6d–f) [48]. This semiconductor-to-metal transition in 2D ATMDs provides an inspiring option for designing innovative functional devices with accessional fantastic properties and novel physical effects [39, 125].
Recently, the M1−xRexX2 systems have demonstrated a reverse transition from 1T’ to 2H due to the significant differences in structural and electronic properties between the two end-materials. For example, Re1−xMoxSe2 alloy nanosheets exhibit a phase transition from 1T’ to 2H with increasing x, and theoretical calculations show that alloying promotes the formation of atomic vacancies on the surface of alloy nanosheets, further improving HER performance [55]. Interestingly, since ReS2 and MoS2 are two semiconductors with completely different phase structures, MoxRe1−xS2 alloys exhibit a much stronger bandgap bowing effect compared to Mo1−xWxS2 and MoS2(1−x)Se2x, significantly expanding the tunable bandgap and spectral response range in such alloys [45]. Overall, the diverse 2D TMDs with varying structural and electronic properties provide numerous choices for designing diversified 2D ATMDs with promising applications in various advanced fields. Atomically substitutional engineering in TMDs will induce lattice strain and even phase transition/evolution of ATMD layers, benefiting from their different structural properties like lattice constant and crystal phase. Table 3 summarizes the atomic substitution-induced phase transitions in specific ternary TMDs, providing inspiration for designing novel ATMD layers. In particular, the 2H-to-1T/1T’ phase transition can increase the metallicity of 2D ATMDs and introduce more active sites on their basal plane, making them irreplaceable in the realms of catalysis and gas-sensing [47, 53, 80, 120, 127]. Moreover, the tunable crystal phase feature enables ATMDs to perform better in HER and provides an inspiring opportunity for investigating new functional devices [54, 55, 120].
4.2 Fully Tunable Bandgaps of Multinary TMDs
Atomically substitutional engineering enables the alteration of bandgaps, band alignment/structure, and ultimately the optical and electronic properties of ATMD layers by exploiting the different electronic properties of multifarious TMDs. The introduction of an arbitrary number of heteroatoms can allow for fully tunable bandgap and tailored spectral response to be achieved across ATMD layers, making them ideal for next-generation electronic and optoelectronic devices. In 2014, Duan and his team synthesized high-quality and uniform MoS2xSe2(1−x) nanosheets with fully tunable compositions via an improved CVD process [44]. The optical bandgap of MoS2xSe2(1−x) can be continuously tuned from 1.557 eV (795 nm) to 1.856 eV (668 nm), as shown in Fig. 7a, b. This demonstrates the potential of atomically substitutional engineering for achieving tailored bandgap and spectral response in ATMD layers. The relationship between bandgap energy and composition x can be expressed as follows:
This equation, shown in Fig. 7c, describes the bandgap bowing effect in ATMDs, where the bowing parameter “b” is equal to 0.05 eV [44, 110, 128,129,130]. In another study, WS2xSe2(1−x) nanosheets were fabricated to display a continuously tunable bandgap energy ranging from 1.649 eV (752 nm) to 1.979 eV (627 nm) [46]. Additionally, Mo1−xWxS2 alloy monolayers demonstrate composition-dependent bandgap and bowing effects, as shown in Fig. 7d, e. The bandgap is tunable from approximately 1.87 to 2.02 eV and has a larger bowing parameter of 0.24 ± 0.05 eV, serving as a typical example [131].
The differences in the bowing parameters of various ATMDs can be attributed to the diversity in electron filling of the d orbitals and lattice matching degrees between the two end-materials [41, 45, 66, 132,133,134]. MNX-type ATMDs, which involve two transition metal elements, generally have larger bowing parameters than MXY-type ATMDs [128, 129]. Additionally, the bandgap properties of ATMDs have been shown to be strongly dependent on layer number, temperature, and strain [135,136,137]. Interestingly, alloying of TMDs can modify their band edge positions (i.e., CBM and VBM), and the composition-dependent positions exhibit a similar bowing effect, as shown in Fig. 7f [132]. Furthermore, atomic substitution can alter the type of band alignment in material systems. For example, Zheng et al. developed PbI/WS2(1−x)Se2x heterostructures via two-step CVD and discovered that increasing Se content in the alloys gradually alters their interfacial band alignments from type-I to type-II, accompanied by a change in PL emission from original enhancement (WS2) to final quenching (WSe2) [138]. In conclusion, atomically substitutional engineering can achieve a wide range and precise tuning of the bandgap and band alignment/structure, enabling the creation of novel optoelectronic and photovoltaic devices with tailored spectral response.
4.3 Composition-dependent Raman Scattering of Multinary TMDs
Raman spectroscopy is a nondestructive and rapid tool used to investigate lattice vibrations and phonon dispersion of 2D nanomaterials. Researchers can use information such as peak frequency, peak intensity, and full width at half maxima (FWHM) in Raman spectroscopy to analyze the layer number, lattice orientation, strain, and other structural characteristics of 2D TMDs [139, 140]. Atomic substitution of TMDs changes their crystalline and electronic structures, which also alters their Raman scattering. As a result, researchers can creatively use Raman spectroscopy to characterize the composition and structure of ATMDs [139,140,141].
Studies have revealed that there are nine normal vibrational modes at the Γ point in the Brillouin zone for 2D (A)TMDs, among which the A1’ mode (out-of-plane) and E’ mode (in-plane) are Raman active [140]. For Mo1−xWxS2 monolayers, three characteristic peaks can be observed, assigned to the WS2-like E’, MoS2-like E’, and A1’ modes, respectively (Fig. 8a, b) [142]. Notably, the A1’ and E’ modes of Mo1−xWxS2 monolayers exhibit one-mode and two-mode composition-dependent behaviors, respectively. The FWHM of most peaks from Mo1−xWxS2 monolayers is larger than that of MoS2 and WS2 monolayers, indicating wider mode dispersion caused by well-blended and random alloys [142, 143]. In addition, a composition-insensitive disorder-related mode at ~ 360 cm−1 can only be observed in alloyed TMDs, implying the formation of disordered/random alloys instead of phase separation [142]. Similar behaviors have been found in other MNX-type ATMDs, such as Mo1−xWxSe2 and Mo1−xWxTe2 [49, 129, 144]. Distinctively, both the A1’ and E’ modes of most Re-based ATMDs (e.g., Mo1−xRexS2, W1−xRexS2) exhibit two-mode behavior, which is attributed to their tanglesome anisotropic crystal structure and the relatively large lattice mismatch between ReS2 and MoS2/WS2 [45, 124].
Figure 8c–e summarizes the Raman spectra and peak shift tendency of MoS2xSe2(1−x) alloys with different S compositions [44]. The A1g and E2g peaks correspond to the branch of A1’ and E’ modes, respectively, and both modes exhibit two-mode behavior, as also demonstrated in WS2xSe2(1−x) and HfS2(1−x)Se2x alloys [46, 145]. It is worth noting that Se- and Te-based ATMDs often exhibit strong A1’ modes, making it challenging to observe the E’ characteristic peak, which can be studied using polarization Raman spectroscopy [46, 74, 108, 110, 142, 146, 147]. The atomic displacement for the E’ and A1’ modes in ATMDs, as illustrated in Fig. 8f, suggests that the E’ mode involves vibrations of both transition metal and chalcogen atoms, while the A1’ mode is only affected by chalcogen atom vibrations, revealing different behaviors in peak shift for different types of ATMDs [142]. These behaviors in Raman spectra imply the vibration and strain of the lattice in ATMDs, enhancing the surface activity of ATMD layers, ultimately enhancing the HER and gas-sensing performance [59, 127, 148].
The modified random-element-isodisplacement (MREI) model has been developed to simulate the lattice vibration behaviors of various TMD alloys. This model is based on two basal assumptions: (1) Atoms of the same kind vibrate with the same amplitude and phase, and (2) substituted atoms are randomly distributed [142, 149,150,151]. Through the MREI model, Xie’s group simulated the mode behaviors and fitted the composition-dependent Raman frequencies of A1’ and E’ modes in Mo1−xWxS2 monolayers, as outlined in Fig. 8f–g [142]. The fitting results are in good agreement with the experimental data, and the composition-dependent Raman frequency of the A1’ mode in Mo1−xWxS2 monolayer can be expressed as follows:
By utilizing the MREI model combined with Raman spectroscopy, the aforementioned equation can be effectively employed to quantify the composition of Mo1−xWxS2 alloys.
5 Improved Performances of Multinary TMDs
Atomically substitutional engineering allows for the creation of multinary TMDs with unique tunable properties such as a tunable bandgap, band alignment/structure, and crystal phase. These multinary TMDs often exhibit superior performance compared to binary TMDs. In this context, it is important to highlight the various advantages of multinary TMDs in a range of applications, including electronic and optoelectronic devices, as well as electrocatalysis, and more.
5.1 Electronic Devices
Semiconducting binary TMDs have garnered widespread interest as field-effect transistors (FETs) due to their intriguing structural properties and exceptionally high electronic performance, including a high on/off ratio and carrier mobility in monolayer structures [152]. To further enhance the electrical performance of TMDs and explore their potential for nano-microdevices, heteroatom doping has been extensively studied to achieve p-/n-type modulation in TMDs [24, 25]. However, unlike conventional bulk 3D semiconductors, doping in atomically thin TMDs presents challenges in effectively modulating carrier density. The doping concentration in TMDs is often limited to less than 10% due to stringent lattice constant requirements, which obstructs the controllable synthesis and systematic investigation of doped TMDs [20, 28]. Interestingly, atomically substituted ternary TMDs not only inherit the unique layered structure of TMDs but also exhibit fascinating and full-composition-tunable electronic properties that can greatly improve their FET performance. This includes the ability to regulate carrier type, increase interface flexibility, and improve structural stability, which surpasses most hybridization strategies using external contacts [46, 58, 65, 66, 153].
5.1.1 Regulated Carriers in Type and Density
Different binary TMDs generally exhibit different conductive types. For instance, MoS2 and WS2 grown on SiO2/Si substrates generally exhibit n-type conduction, while WSe2 exhibits p-type conduction [152, 154,155,156]. By alloying two kinds of TMDs with different conductive types, we can achieve fully adjustable instinctive electrical transport properties in a full range of compositions. Some Mo- and W-based ATMD layers exhibit a high degree of miscibility, resulting in their stability being even better than pristine TMDs [66]. As an example, Duan et al. fabricated WS2xSe2−2x alloys with fully tunable compositions (x = 0–1) and carefully investigated their electrical transport properties through WS2xSe2−2x-based FETs with different compositions (Fig. 9a) [46]. As shown in Fig. 9b, Se-rich WS2xSe2−2x alloys exhibit p-type conduction behavior, whereas S-rich WS2xSe2−2x alloys demonstrate n-type conduction behavior. Additionally, weak bipolar behavior is observed in WS2xSe2−2x alloys at the intermediate alloy region (0.4–0.65 S ratio). With an increase in the S ratio, the carrier types in WS2xSe2−2x-based transistors gradually change from hole to electron, indicating that the valence band and conduction band shift as the composition changes (Fig. 9c). Similar conduction behavior evolution has also been observed in ReS2xSe2−2x and Mo1−xWxSe2 alloys [58, 130]. The tunable conduction behavior of ATMDs from p-type to bipolar and then to n-type can be attributed to the majority carriers of their two end-materials (i.e., x = 0 or 1) being holes and electrons, respectively, and their valence band or/and conduction band shifting as the alloy composition changes [41, 58, 132]. In another interesting study, the MoxRe1−xS2-based FETs not only exhibited tunable conduction behavior dependent on composition but also had a novel “bipolar-like” electron behavior due to the formation of individual “sub-gap” in the conduction band. This could be used as a real bipolar FET to construct logic inverter devices (Fig. 9d) [45].
Yu et al. recently synthesized WSe2(1−x)Te2x (x = 0–1) alloys that exhibit a metal–semiconductor phase transition, with Se-rich alloys demonstrating semiconducting 2H phase and Te-rich alloys showing metallic 1 T’ phase. Remarkably, Se-rich WSe2(1−x)Te2x-based FETs showed exceptional electronic performance with a maximum hole mobility of 46 cm2 V−1 s−1 and a high on/off ratio of 106 at x = 0.3, while Te-rich WSe2(1−x)Te2x exhibited metallic conductivity due to the rare Wyle semi-metallicity [48]. Moreover, monolayer alloys with a lateral core/shell structure, WSe2−2xTe2x/WSe2−2yTe2y (x > y), were synthesized using a one-step CVD method with rapid cooling [157]. Differential band alignment was generated due to different Te concentrations in the core and shell regions, forming different Schottky barrier heights of electrons and holes in each region. This led to diverse conductive behaviors in the core and shell regions, with shell-based FETs (WSe2−2yTe2y, Te poor) exhibiting p-type conduction behavior with an excellent on/off ratio of 106 and a high mobility of 30 cm2 V−1 s−1, while core-based FETs (WSe2−2xTe2x, Te rich) showed bipolar conductive behavior. The process is depicted in Fig. 9e–h. These findings demonstrate that ternary materials can exhibit different crystal phases and conductive properties at different compositions, providing a novel strategy for developing advanced exotic electronic devices with homo/heterojunctions. The current application of ternary TMDs in integrated electronic devices is at an early stage, primarily due to limitations caused by Coulomb impurity scattering resulting from the low dielectric constant of SiO2/Si substrates, as well as alloy scattering in ternary TMDs, which restricts carrier mobility. To overcome these limitations and enhance device performance, it is crucial to employ high-k dielectrics and optimize device structures [28, 46].
5.1.2 Enhanced Electronic Performances
Ternary TMDs have recently emerged as innovative van der Waals (vdW) interfacial layers for the fabrication of advanced electronic devices with enhanced performance. For example, Chen et al. developed top-gate transistors using monolayer MoS2 on three-layer MoxW1−xS2 alloys, where enhanced electronic performance was achieved through atomic substitution-modified defect states and strains (Fig. 10a. b) [158]. Vu et al. employed a liquid-phase one-step CVD strategy to produce NbSe2/WxNb1−xSe2 metal–semiconductor vdW heterostructures with precise control over atomic substitution ratios [159]. These vdW heterostructure-based FETs exhibited significantly superior electrical performance compared to pristine WSe2, including a raised carrier mobility of 27.24 cm2 V−1 s−1 (1,238 times improvement) and an on/off ratio of 2.2 × 107 (4.400 times improvement), attributed to the substitution-modulated/optimized contacts and Schottky barrier heights between the channel and electrodes. In another study, Kim et al. designed a unique FET with semiconducting WSe2 channel and metallic NbSe2 electrodes, introducing an interfacial transition region (WxNb1−xSe2) to boost charge transport between the metallic–semiconducting TMD interface and improve carrier mobility [153]. Compared to traditional FETs, this vdW stack structure-based FET showed increased charge injection efficiency and reduced Schottky barrier heights at the channel–electrode interfaces through quantum–mechanical tunneling (Fig. 10c, d). Therefore, optimizing contact resistance and Schottky barriers at the channel–electrode interfaces is important considerations in the design of ATMD-based FETs for advanced electronic devices with high performance.
5.2 Optoelectronic Devices
5.2.1 Modulated Defect/Trap Levels
Conventional binary TMDs often have high concentrations of chalcogen vacancies due to high-temperature synthesis, which severely limits their photoresponsivity and response time [116, 160,161,162]. To improve optoelectronic performance, atomic substitution of TMDs can be used to tailor their energy band structures and further to modulate their energy levels of defect state. In Lim’s work, a large-area and continuous uniform MoS1.15Se0.85 film was produced on a 4-inch quartz wafer and utilized to fabricate photodetectors (Fig. 11a, b) [163]. The band structure and defect states were modulated to optimize the absorption process for light and improve photoresponsivity. In particular, due to the band bowing effect caused by atomic substitution, the defect level of VS (S vacancy) in MoS1.15Se0.85 is very close to its CBM, making it unlikely to be a recombination center and allowing captured electrons to be re-emitted into the conduction band as free carriers again (Fig. 11c). In other words, atomic substitution results in MoS1.15Se0.85 presenting a shallower energy level of defect state compared to MoS2 and MoSe2, making it emerge more photogenerated carriers. This transition of defect states from deep to shallow led to much-enhanced photoresponsivity compared to MoS2, MoSe2 (Fig. 11d), and other typical semiconductors (e.g., WS2, WSe2, Bi2Se3, and GaAs) [163]. Multiple devices with photoresponsive activity were used to characterize the uniformity of the alloy film, which is a significant step toward the industrialized manufacture and application of ATMD-based optoelectronic devices (Fig. 11e). Therefore, ternary TMDs hold great potential for improving optoelectronic performance by tailoring their energy band structures, which can pave the way for the development of advanced electronic devices.
The modulation mechanism for defect states in MNX-type TMDs can also be employed to enhance the photoresponsivity and accelerate the photoresponse rate. For instance, a high-performance photodetector was fabricated using PLD-grown Mo0.5W0.5S2 thin film with modulated band alignment and less defect concentration (i.e., S vacancy), which reduced photocarriers to be captured by the defect/trap states and shorten the response time to 150 ms [116]. Additionally, the relatively low defect concentration and shallower defect level enabled the Mo0.5W0.5S2-based photodetector to exhibit a superior responsivity of 5.8 A W−1 compared with pristine MoS2 and WS2 under Vds of 2.2 V. Similarly, a ternary Mo0.5W0.5Se2-based photodetector was fabricated using the same synthetic method and physical mechanism, which showed much higher device performance compared to the binary MoSe2 and WSe2, including a photoresponsivity of 77.1 A W−1 and a response time of 8.3 ms [85]. Moreover, improved optoelectronic performance has been achieved in other ternary TMDs, such as Mo1−xSnxS2 (a response time of 20 ms with comparison of 2.12 s for MoS2), WS2(1−x)Se2x (a response time of 20 ms with comparison of 6.86 s for WS2 and 30 ms for WSe2), and ReS2(1−x)Se2x (a response time of 15 ms with comparison of 60 ms for ReS2 and 20 ms for ReSe2), by suppressing deep-level defect states [52, 108, 109]. Overall, atomically substitutional engineering plays a significant role in modulating the energy levels of the defect/trap states and significantly improving the performance of ATMD-based optoelectronic devices.
The band engineering in ternary TMDs has inspired the fabrication of self-powered photodetectors using ternary TMDs with spatial composition gradients. For example, Xu et al. synthesized vertically stacked MoS2(1−x)Se2x alloys with a spatially graded bandgap (induced by spatially graded composition x) using a liquid precursor-based CVD method, which exhibited a built-in electric field and can be utilized for self-powered photodetection [164]. In experiments, the self-powered phototransistors showed a sensitive gate-tuned photovoltaic effect and presented a photoresponsivity of 311 mA W−1 with an excellent detectivity of ~ 1011 Jones at 0 bias. Additionally, the biased devices delivered a remarkable photoresponsivity of 191.5 A W−1, a fast response time of 50 ms, and a photoconductive gain of 106–107 under light ranging from 405 to 808 nm, which demonstrated superior photoelectronic performance and photoresponse time in comparison with the photodetectors based on binary TMDs and even their heterostructures. This exciting work demonstrated promising prospects in structural design and bandgap engineering of 2D ATMDs for developing photoelectronic/photovoltaic devices.
5.2.2 Anisotropic and Broadening Photoresponse
Re-involved ATMDs with anisotropic 1T’-phase crystal structures exhibit intriguing anisotropic photoresponses in optoelectronic devices, which depend on the polarization angle of the incident light [130, 165]. For example, in ReS2xSe2(1−x)-based optoelectronic devices, the photocurrent reaches the maximum and minimum values when the incident light is polarized along and perpendicular to the b-axis, respectively (Fig. 12a–d) [130]. Moreover, strong band bowing can be observed in MoxRe1−xS2 alloys due to the large lattice mismatch and completely different crystal phase between MoS2 and ReS2, providing an exceedingly broadened spectral response range from visible to near-infrared light (Fig. 12e–h) [45]. Hence, Re-involved ATMDs play a vital role in designing futuristic anisotropy-based and specially tailored devices. Additionally, it was discovered that as the Te content in HfS2(1−x)Te2x alloys increases from 0 (HfS2) to 0.19 (HfS1.81Te0.19), the bandgap decreases from 1.7 to 0.88 eV with significant band bowing. Consequently, the photoresponse wavelength of HfS2(1−x)Te2x-based photodetectors can be tremendously extended from visible to infrared light (1,310 nm) [166]. Benefiting from the strong band bowing effect, the specific atomic substitution in TMDs can greatly broaden their spectral response range, which provides a vital strategy for the development of high-performance TMD-based infrared photodetectors.
5.3 Electrocatalytic Hydrogen Evolution Reaction
In today’s highly industrialized era, hydrogen is being considered as a potential sustainable and renewable substitute for fossil fuels. Electrocatalytic water splitting is one of the most effective and eco-friendly approaches for hydrogen production. Over the past decade, binary TMDs have been shown to be promising alternatives to noble metal-based electrocatalysts (such as Pt and Ir) for HER due to their unique layered structure, high specific surface area, and excellent stability [148]. However, the HER catalytically active sites in most binary TMDs are only located at the layer edges, with their basal planes being catalytically inert [148, 167, 168]. In contrast, ternary TMDs can introduce appropriate defects, induce lattice strain, facilitate phase transition, and even modify electronic structure to optimize the ΔGH, which greatly enhances the HER performance.
5.3.1 Enhanced Catalytic Activity by 2H-Phase Ternary TMDs
Gan et al. embedded MoxW1−xS2 alloys onto flexible conductive carbon substrates (MoxW1−xS2/C) to serve as HER electrocatalysts [143]. The local strain and grain boundaries induced by the alloying process resulted in a reduction of the energy barrier of hydrogen formation, leading to improved HER performance. In fact, the Mo0.37W0.63S2/C sample exhibited an impressively low overpotential of 0.137 V at jgeo = 10 mA cm−2 and a remarkable Tafel slope of 53 mV dec−1, better than that of the MoS2/C and WS2/C alternatives. Alternatively, CVD-grown WS2(1−x)Se2x monolayers were also used as catalysts for HER. These monolayers presented a lower overpotential of 80 mV (jgeo = 10 mA cm−2) and a smaller Tafel slope of 85 mV dec−1 compared to WS2 and WSe2 [59]. The slight crystal distortion on the basal plane caused by lattice mismatch led to the formation of a polarized electric field in the plane, which contributed to the bond fracture of molecules adsorbed on the basal plane and thus enhanced the HER performance.
5.3.2 Enhanced Catalytic Activity by 1T/1T’-Phase Ternary TMDs
Research has shown that ternary TMDs with 1 T/1 T’ phase are more advantageous for HER than the 2H phase, due to their comparatively high-density exposed active sites and metallic conductivity [148]. Zhang et al. employed a ball milling and Li-ion intercalation method to synthesize high-percentage metallic 1T-phase MoSSe nanodots from corresponding 2H-phase bulk crystals [53]. These nanodots exhibited high-density catalytically active edge sites and Se vacancies (Fig. 13a–c), and first-principle calculations revealed that alloying of 2D TMDs reduces the Gibbs free energy for atomic hydrogen adsorption (ΔGH). Furthermore, experimental characterization confirmed that the Se vacancy (VSe) in MoSSe nanodots further reduces the ΔGH to enhance HER catalytic activity (Fig. 13d, e). The combined effect of high-density exposed catalytic active sites, high conductivity of metallic 1T phase, and the reduced ΔGH led to significantly improved HER performance compared to MoS2 and MoSe2 nanodots (Fig. 13f, g). Similarly, ReSSe nanodots with intrinsic distorted 1T’ structure were fabricated and demonstrated greatly modified HER performance compared to ReS2 and ReSe2 nanodots due to the alloying effect and the asymmetric S vacancies [169].
In addition to the 1T/1T’ phase induced by Li-ion intercalation and the inherent one in binary TMDs, the substitution-induced phase transition from 2H to 1T/1T’ also exhibits improved performances in HER application. Kang et al. synthesized Mo1−xVxSe2 nanosheets with fully tunable composition (x = 0–1) via a colloidal reaction, which showed a tunable phase from 2H to 1T with increasing x [54]. The two end-materials possess completely different crystalline phases (i.e., 2H phase for MoSe2, 1T-phase for VSe2), leading to the induction of a mass of multifarious atomic vacancies (such as Se monovacancy, Se divacancy, V vacancy) in their ternary nanosheets. These abundant vacancies act as catalytically active sites for the HER reaction (Fig. 14a). Computational studies verified that alloying can significantly reduce the formation energy of atomic vacancies, and both the alloying itself and the atomic vacancies can reduce ΔGH to enhance the catalytic activity of HER (Fig. 14b). The HER performance of Mo1−xVxSe2 alloys with different compositions was systematically investigated in Kang’s work, and it was found that the best performance was achieved at x = 0.3 due to the existence of the most abundant atomic vacancies (Fig. 14c, d). The same research group performed another important work to produce Mo1−xNbxSe2 (x = 0–1) ternary nanosheets with varying compositions in a full range through a solvothermal reaction [93]. These nanosheets had large lattice mismatches and were comprehensively investigated for their potential in HER. HAADF-STEM revealed the presence of diverse atomic defects, including Se and Nb vacancies, concurrent vacancies, and even adatom defects. DFT calculations confirmed that the ternary nanosheets had obviously lower formation energies for vacancies compared to the binary counterparts. As a consequence, abundant defect sites and substitution-reduced ΔGH synergistically enhanced the HER performance of the ternary TMD nanosheets. Furthermore, more phase transition alloy nanosheets, including Re1−xMoxS2, Re1−xMoxSe2, W1−xVxSe2, and Nb1−xVxSe2, were fabricated to exploit the best HER performance by the alloying formation of 1T/1T’ phase and introduction of atomic vacancies [55, 94, 121, 126]. The enhanced HER performance provided by a variety of ternary TMDs is summarized in Table 4.
5.4 Other Applications
In addition to their achievements in various applications including HER, ternary TMDs are promising materials for gas-sensing and photoelectrocatalysis, although related research is in its early stages. For example, Ko et al. fabricated large-area and uniform WS2xSe2−2x alloy films via a sulfurization process based on CVD (Fig. 15a, b) [127]. Through electronic sensitization and surface modification, the WS0.96Se1.04-based gas sensor exhibited a 2.4 times enhanced response compared to WSe2 when exposed to 500 ppm NO2 (Fig. 15c). Furthermore, the WS0.96Se1.04-based gas sensor demonstrated good flexibility and outstanding long-term stability. In Xu’s work, MoSeS alloy monolayers were produced by a novel liquid–liquid interface-mediated strategy and employed in electroreduction of CO2 into syngas (i.e., CO and H2) [171]. Remarkably, the MoSeS monolayers showed a current density of 43 mA cm−2 at − 1.15 V vs. RHE, which was 2.7 and 1.3 times higher than that of MoS2 and MoSe2 monolayers, respectively. Moreover, the MoSeS monolayers exhibited a much higher Faradaic efficiency (FE) of 45.2% for CO production at − 1.15 V compared to MoS2 (16.6%) and MoSe2 (30.5%) monolayers. DFT calculations indicated that the eccentric charge around Mo atoms in MoSeS alloys not only stabilizes the COOH* intermediate but also promotes the rate-limiting step of CO desorption, greatly enhancing electrocatalytic performance. More recently, Shao et al. fabricated lateral epitaxial metal–semiconductor SnxMo1−xS2/MoS2 heterostructures via a one-step CVD method, in which the edge of MoS2 is modified with Sn atoms in situ to form metallic SnxMo1−xS2 alloys, resulting in seamless splicing of metallic SnxMo1−xS2 at semiconducting MoS2 edge (Fig. 15d, e) [172]. As a result, due to efficient electron–hole separation and fast charge transfer, the heterostructures showed improved performance in photoelectrocatalytic oxygen evolution, including a lower onset potential of 0.15 V and a higher current density of > 0.8 mA cm−2 at 1.23 V vs. RHE, which was 2.5 times higher than that of pristine MoS2 (Fig. 15f).
6 Emerging Janus Ternary TMD Monolayers
Similar to the gold Janus in Roman mythology, a unique type of MXY-type ATMD layer can be found, where a chalcogen element (X) is present on the upper side of the transition metal, while another chalcogen element (Y) is located on the lower side of the transition metal. The highly ordered ternary structure of Janus TMD monolayers (JTMDs) breaks the out-of-plane symmetry, generating spontaneous vertical dipole moments [50, 60]. Since the fabrication of Janus SMoSe in 2017, JTMDs have received considerable attention, and their fascinating and unique properties have been predicted theoretically and investigated experimentally, such as Zeeman- and Rashba-type spin splitting, rapid exciton formation, tribological piezoelectricity, intrinsic ferroelasticity, and large valley polarization [50, 60, 173,174,175,176,177].
Approaches for Synthesizing Janus Ternary TMDs: Researchers from Thygesen’s group evaluated the thermodynamic stability of 216 Janus monolayers in both H-phase and T-phase using calculated energy above the convex hull (Ehull), which represents the energy of the most stable phase (possibly mixed) as a function of stoichiometry [178]. As shown in Fig. 16a, the H-phase JTMDs of Group VB or VIB transition metals and T-phase JTMDs of Group IVB or VB transition metals have relatively high thermodynamic stability and are expected to be successfully synthesized. Additionally, the researchers assessed the dynamic stability of all 216 Janus monolayers and computed the magnetic, elastic, electronic, and optical properties of the 70 most stable Janus monolayers. These results were uploaded to the Computational 2D Materials Database, providing a powerful guide for the fabrication and preservation of Janus monolayers [179, 180]. Moreover, the atomically thin nature of Janus XMY monolayers endows their (opto)electronic properties highly sensitive to various structural defects. Therefore, it is crucial to have a comprehensive understanding of the formation and influences of different types of defects on the (opto)electronic properties of Janus monolayers before their fabrication and application. Zhang et al. conducted first-principles calculations to evaluate the thermodynamic stability of different defects in Janus SMoSe and their impact on its electronic properties [181]. The results revealed that point vacancies of S and Se atoms were the most thermodynamically favorable compared to line defects and 60° grain boundaries. Additionally, polar-discontinuous 60° grain boundaries tend to exhibit characteristics of 1D metallic quantum wires.
Due to its unique structure, the synthesis of JTMDs requires precise reaction conditions. Currently, JTMDs are fabricated using CVD-grown binary TMD monolayers [50, 51, 101, 182, 183]. The simplest method involves sulfurizing CVD-grown MoSe2 at high temperatures to produce Janus SMoSe [51]. An alternative method involves stripping the top-layer S atoms of CVD-grown MoS2 and replacing them with H atoms via hydrogen plasma treatment, followed by selenization of the intermediate Janus SMoH to form Janus SMoSe (Fig. 16b) [50, 183]. In both methods, the temperature and carrier gas flow rate must be precisely controlled to prevent further sulfurization/selenization or the formation of ATMDs with random atomic arrangements. To simplify the process, Lin and his colleagues developed a pulsed laser deposition (PLD)-based strategy to form Janus SWSe by implanting Se clusters into CVD-grown WS2 at 300 °C (Fig. 16c) [182]. The kinetic energy (KE) of Se species can be controlled by adjusting the background Ar pressure, which allows for the controlled conversion of WS2 into Janus SWSe, WS2(1−x)Se2x random alloys, and even WSe2 by precisely altering the KE during the process of repeated Se implantation and recrystallization (Fig. 16d, e). Recently, Trivedi et al. demonstrated a selective epitaxy atomic replacement (SEAR) method for preparing JTMDs and their heterostructures at room temperature (Fig. 16f–h) [101]. Janus SWSe was used as an example, where the H radicals combined with the Se atoms at the top of CVD-grown WSe2 to form intermediates that were then bombarded and split with high-energy H+ ions to generate Se vacancies. The introduction of sulfur during the SEAR process is essential to fabricate Janus SWSe, where H radicals react with sulfur to form H2S vapor that is transported toward the samples by the carrier gas and dissociated into S and H radicals. Ultimately, the S radicals incorporate into chemically active Se vacancies to form stable Janus SWSe (Fig. 16g). Importantly, this process is performed at room temperature and driven by kinetics rather than thermodynamics.
Unique Properties and Promising Application of JTMDs: The in-plane symmetry breaking of Janus XMY and the different electronegativities of the X and Y atoms result in a built-in vertical dipole moment in 2D JTMDs, providing an important platform for fabricating next-generation high-performance devices with applications in exciton dynamics, dipole interaction, spintronics, and piezoelectricity [50, 174]. Figure 17a shows that angle-dependent optical second harmonic generation (SHG) characterization of Janus SMoSe and random MoSSe alloy confirms the breaking of mirror symmetry and the existence of vertical dipoles in Janus SMoSe monolayers [50]. Interestingly, the wave functions of electrons and holes are separated under the built-in dipole moment in 2D JTMDs (Fig. 17b), which prolongs the exciton radiative recombination lifetime compared with binary TMDs and improves the efficiency and performance of JTMDs-based photovoltaic and photoelectric devices [174].
The presence of built-in dipole moments in JTMDs enhances electronic interactions between JTMDs and organic molecules. In Yeh’s study, the gas sensitivity of 2D TMDs and JTMDs to various volatile organic compounds (such as acetone, methanol, and formyl aldehyde) was investigated through DFT calculations [184]. The results showed that the adsorption of acetone molecules significantly altered the bandgaps of JTMDs compared to binary TMDs, resulting in a conspicuous change in conductivity for the ultrasensitive detection of acetone gas (Fig. 17c). This modulation/optimization of the electron transfer process can be attributed to the dipole interaction between the internal dipole moment of JTMDs and the polarized gas molecules. In another study, CVD-fabricated Janus SMoSe monolayers were utilized to detect various biomolecules (glucose and dopamine) via surface-enhanced Raman scattering (SERS) (Fig. 17d) [185]. The dipole moments provided by Janus SMoSe polarize dipoles in glucose and redistribute abundant charge to significantly enhance the Raman vibrational intensity of glucose (Fig. 17e, f). As a result, Janus SMoSe demonstrated a Raman enhancement factor of up to 105 for glucose with a good linear detection relationship within a concentration of 1–10 mM (Fig. 17g).
In addition to the inherent vertical dipole moments present in JTMDs, the formation of the Janus structure in 2D TMDs changes their crystal and band structures. First-principles calculations suggest that the Janus SMoSe monolayer has an electron carrier mobility of 73.8 cm2 V−1 s−1 and a hole carrier mobility of 157.2 cm2 V−1 s−1 [186]. However, layer-stacked Janus SMoSe exhibits an electron carrier mobility of 1,194 cm2 V−1 s−1 in bilayer SMoSe structures and an extremely high hole carrier mobility of 5,894 cm2 V−1 s−1 in trilayer SMoSe structures. This layer-dependent enhanced carrier mobility can be explained by changes in deformation potential and elastic modulus. Lu’s work computationally and experimentally demonstrated that Janus SMoSe has much lower overpotential and hydrogen adsorption-free energy in HER compared to MoS2 and MoSe2 [51]. Additionally, Idrees et al. investigated the optical and electronic properties of JTMD monolayers and their heterostructures through hybrid DFT calculations [187]. The results indicated that these monolayers and heterostructures have strong optical absorption in the visible to ultraviolet regions, with SeWTe, SMoTe, and SWTe monolayers achieving an absorption efficiency of ~ 80% in the visible, infrared, and ultraviolet regions. It was also revealed that the water reduction and oxidation potentials for all JTMD monolayers at pH = 0 are located between their valence and conduction band edges, making them promising candidates for water splitting.
7 Summary and Outlooks
The extensive research and exploitation of binary TMDs have made it increasingly important to tune and improve their properties for potential applications in modern realms. Atomically substitutional engineering is an exclusive strategy for TMDs that combines diverse TMDs with different structural and electronic properties to form ternary or quaternary uniform solid solutions with special crystal phases, continuously tunable bandgaps, tailored band alignment/structure, and exotic physical phenomena (such as superconductivity and Weyl semi-metallicity). The good miscibility of TMDs allows for arbitrary mixing percentages in ATMDs and forms an internal contact in monolayers, making atomic substitution clearly superior to elemental doping and hybridization with other nanomaterials. Compared to binary TMDs, ATMDs can achieve enhanced/improved performances in a wide range of advanced applications such as electronic devices, photoelectronic sensing, electrocatalysis, and photoelectronic conversion. The emergence of 2D ATMDs has introduced a range of new members to the family of 2D nanomaterials, offering a highly competitive and flexible platform for numerous contemporary industrial applications.
In recent years, rapid progress has been witnessed in the facile synthesis, outstanding properties, and novel applications of ATMD layers. However, there are still some challenges in their exploitation and investigation. For instance, most current studies focus on the fabrication of ternary TMDs, with only a few quaternary TMDs reported [33, 75, 188]. Generally, 2D ATMDs containing more elements should exhibit a wider range of property modulation, more functions, and even unprecedented properties compared to ternary TMDs [189]. To advance in this direction, more research efforts are directed toward the synthesis of high-quality quaternary TMDs. They refer to not only MNXY-type TMDs mentioned earlier but also quaternary TMDs with additional cationic or anionic substitutions. Examples of these emerging materials include MXYZ-type MoS2(1−x−y)Se2xTe2y and MNOX-type Mo1−x−yWxVySe2 [104, 190]. These TMDs offer more flexibility in tuning their properties and demonstrate superior performance for various applications. Furthermore, recently discovered multinary TMDs with non/sub-stoichiometric phases, obtained through tailored experimental conditions, demonstrate unique physical properties and impressive performance [191, 192]. For instance, LixMoS2 exhibits superior thermal conductivity, while FexNbS2 displays an induced antiferromagnetic order [192]. These materials hold great promise and should be extensively studied and appreciated in future research. In terms of synthetic methods, CVD and hydro/solvothermal methods have proven to be the most effective for fabricating high-quality 2D ATMDs, but the quality of products is critically dependent on the types/states of the precursors, experimental conditions, and even the reaction apparatus. In the future, more attempts should be made to simplify the synthesis of 2D ATMDs and obtain high-quality products under mild conditions. One can realize the production of highly uniform ATMDs in CVD by spin-coating liquid precursors onto substrates [193, 194]. The large-scale manufacturing of ATMDs on wafers can be accomplished by designing wafer modules within CVD furnaces and establishing pathways for precursor supply [103, 104]. The crystalline quality of these materials can be improved by carefully selecting specific substrates. For example, it has been demonstrated that Re-based TMDs exhibit an improved lattice matching with mica compared to SiO2/Si substrates, leading to a better crystalline quality [195, 196]. Regarding the synthesis of Janus ATMDs, only Janus SMoSe and SWSe have been successfully fabricated, although various 2D JTMDs have been theoretically simulated to exhibit good thermodynamic stability. Further research is needed to develop effective strategies to synthesize a broader range of Janus ATMDs with tailored properties for various applications.
The utilization of 2D ATMDs is still in the initial stages, leaving ample room to explore their enhanced/novel applications. Atomic substitution of binary TMDs has proven effective in modulating the internal lattices to achieve tunable Raman scattering and inducing lattice disorder and phase transitions through the creation of atomic vacancies. Therefore, atomically substitutional engineering is a promising strategy to enhance the SERS performance of 2D ATMDs [197]. Additionally, multinary TMDs can alter the band alignment/structure, defect state energy level, carrier density/type, and broaden spectral response, making ATMD layers desirable channel materials for developing advanced FETs and photodetectors. Moving forward, it is crucial to direct the rapid development of 2D ATMDs for use in logic devices, photovoltaic cells, light-emitting diodes, and other related areas [42, 198, 199]. Specifically, there should be a widespread promotion of ATMDs with tailored spectral response ranges and band alignments in the fields of photodetection, photocatalysis, and self-powered optoelectronic devices [42, 164, 200]. Additionally, emphasis should be placed on ATMDs with crystalline phase transition capabilities for highly sensitive sensing and detection of multifarious trace molecules [3, 197]. Furthermore, recent studies have demonstrated that specific atomic substitution in binary TMDs, such as VxMo1−xSe2 and RexMo1−xSe2, can induce magnetism, thereby broadening the avenues for fundamental physics research and the exploitation of intriguing spintronic devices [47, 86]. This requires further optimization of device structure, fabrication of more 2D ATMDs with new/multi-components, and even hybridization/coupling of them with various nanostructures beyond 2D ATMDs. Ongoing research in these areas will lead to the practical realization of advanced applications of ATMDs.
References
K.S. Novoselov, A.K. Geim, S.V. Morozov, D. Jiang, Y. Zhang et al., Electric field effect in atomically thin carbon films. Science 306, 666–669 (2004). https://doi.org/10.1126/science.1102896
Y. Gao, J. Chen, G. Chen, C. Fan, X. Liu, Recent progress in the transfer of graphene films and nanostructures. Small Methods 5, e2100771 (2021). https://doi.org/10.1002/smtd.202100771
C. Tan, X. Cao, X.-J. Wu, Q. He, J. Yang et al., Recent advances in ultrathin two-dimensional nanomaterials. Chem. Rev. 117, 6225–6331 (2017). https://doi.org/10.1021/acs.chemrev.6b00558a
Q. Zhang, X. Xiao, L. Li, D. Geng, W. Chen et al., Additive-assisted growth of scaled and quality 2D materials. Small 18, e2107241 (2022). https://doi.org/10.1002/smll.202107241
W. Qian, S. Xu, X. Zhang, C. Li, W. Yang et al., Differences and similarities of photocatalysis and electrocatalysis in two-dimensional nanomaterials: strategies, traps, applications and challenges. Nano-Micro Lett. 13, 156 (2021). https://doi.org/10.1007/s40820-021-00681-9
Z. Lyu, S. Ding, D. Du, K. Qiu, J. Liu et al., Recent advances in biomedical applications of 2D nanomaterials with peroxidase-like properties. Adv. Drug Deliv. Rev. 185, 114269 (2022). https://doi.org/10.1016/j.addr.2022.114269
L. Cheng, X. Wang, F. Gong, T. Liu, Z. Liu, 2D nanomaterials for cancer theranostic applications. Adv. Mater. 32, e1902333 (2020). https://doi.org/10.1002/adma.201902333
Y. Zhang, J. Mei, C. Yan, T. Liao, J. Bell et al., Bioinspired 2D nanomaterials for sustainable applications. Adv. Mater. 32, e1902806 (2020). https://doi.org/10.1002/adma.201902806
M. Wang, J. Zhu, Y. Zi, Z.-G. Wu, H. Hu et al., Functional two-dimensional black phosphorus nanostructures towards next-generation devices. J. Mater. Chem. A 9, 12433–12473 (2021). https://doi.org/10.1039/D1TA02027G
Z. Wei, B. Li, C. Xia, Y. Cui, J. He et al., Various structures of 2D transition-metal dichalcogenides and their applications. Small Method 2, 1800094 (2018). https://doi.org/10.1002/smtd.201800094
S. Roy, X. Zhang, A.B. Puthirath, A. Meiyazhagan, S. Bhattacharyya et al., Structure, properties and applications of two-dimensional hexagonal boron nitride. Adv. Mater. 33, e2101589 (2021). https://doi.org/10.1002/adma.202101589
H.Y. Hoh, Y. Zhang, Y.L. Zhong, Q. Bao, Harnessing the potential of graphitic carbon nitride for optoelectronic applications. Adv. Opt. Mater. 9, 2100146 (2021). https://doi.org/10.1002/adom.202100146
W. Yu, K. Gong, Y. Li, B. Ding, L. Li et al., Flexible 2D materials beyond graphene: synthesis, properties, and applications. Small 18, e2105383 (2022). https://doi.org/10.1002/smll.202105383
H. Tian, J. Tice, R. Fei, V. Tran, X. Yan et al., Low-symmetry two-dimensional materials for electronic and photonic applications. Nano Today 11, 763–777 (2016). https://doi.org/10.1016/j.nantod.2016.10.003
R. Rajendran, L.K. Shrestha, K. Minami, M. Subramanian, R. Jayavel et al., Dimensionally integrated nanoarchitectonics for a novel composite from 0D, 1D, and 2D nanomaterials: RGO/CNT/CeO2 ternary nanocomposites with electrochemical performance. J. Mater. Chem. A 2, 18480–18487 (2014). https://doi.org/10.1039/C4TA03996C
J. Mei, Y. Zhang, T. Liao, Z. Sun, S.X. Dou, Strategies for improving the lithium-storage performance of 2D nanomaterials. Natl. Sci. Rev. 5, 389–416 (2018). https://doi.org/10.1093/nsr/nwx077
C. Murugan, V. Sharma, R.K. Murugan, G. Malaimegu, A. Sundaramurthy, Two-dimensional cancer theranostic nanomaterials: synthesis, surface functionalization and applications in photothermal therapy. J. Control. Release 299, 1–20 (2019). https://doi.org/10.1016/j.jconrel.2019.02.015
W. Wen, Y. Song, X. Yan, C. Zhu, D. Du et al., Recent advances in emerging 2D nanomaterials for biosensing and bioimaging applications. Mater. Today 21, 164–177 (2018). https://doi.org/10.1016/j.mattod.2017.09.001
G. Guan, M.-Y. Han, Functionalized hybridization of 2D nanomaterials. Adv. Sci. 6, 1901837 (2019). https://doi.org/10.1002/advs.201901837
Y.-C. Lin, R. Torsi, D.B. Geohegan, J.A. Robinson, K. Xiao, Controllable thin-film approaches for doping and alloying transition metal dichalcogenides monolayers. Adv. Sci. 8, 2004249 (2021). https://doi.org/10.1002/advs.202004249
R. Wang, Y. Yu, S. Zhou, H. Li, H. Wong et al., Strategies on phase control in transition metal dichalcogenides. Adv. Funct. Mater. 28, 1802473 (2018). https://doi.org/10.1002/adfm.201802473
G. Guan, S. Zhang, S. Liu, Y. Cai, M. Low et al., Protein induces layer-by-layer exfoliation of transition metal dichalcogenides. J. Am. Chem. Soc. 137, 6152–6155 (2015). https://doi.org/10.1021/jacs.5b02780
G. Guan, J. Xia, S. Liu, Y. Cheng, S. Bai et al., Electrostatic-driven exfoliation and hybridization of 2D nanomaterials. Adv. Mater. 29, 1700326 (2017). https://doi.org/10.1002/adma.201700326
S. Li, Y. Ma, N.A.N. Ouedraogo, F. Liu, C. You et al., P-/n-Type modulation of 2D transition metal dichalcogenides for electronic and optoelectronic devices. Nano Res. 15, 123–144 (2022). https://doi.org/10.1007/s12274-021-3500-2
L. Loh, Z. Zhang, M. Bosman, G. Eda, Substitutional doping in 2D transition metal dichalcogenides. Nano Res. 14, 1668–1681 (2021). https://doi.org/10.1007/s12274-020-3013-4
Q. Lu, Y. Yu, Q. Ma, B. Chen, H. Zhang, 2D transition-metal-dichalcogenide-nanosheet-based composites for photocatalytic and electrocatalytic hydrogen evolution reactions. Adv. Mater. 28, 1917–1933 (2016). https://doi.org/10.1002/adma.201503270
X. Huang, C. Tan, Z. Yin, H. Zhang, 25th anniversary article: hybrid nanostructures based on two-dimensional nanomaterials. Adv. Mater. 26, 2185–2204 (2014). https://doi.org/10.1002/adma.201304964
Y. Zhao, K. Xu, F. Pan, C. Zhou, F. Zhou et al., Doping, contact and interface engineering of two-dimensional layered transition metal dichalcogenides transistors. Adv. Funct. Mater. 27, 1603484 (2017). https://doi.org/10.1002/adfm.201603484
Q. Wang, Y. Lei, Y. Wang, Y. Liu, C. Song et al., Atomic-scale engineering of chemical-vapor-deposition-grown 2D transition metal dichalcogenides for electrocatalysis. Energy Environ. Sci. 13, 1593–1616 (2020). https://doi.org/10.1039/D0EE00450B
S. Chen, D. Huang, M. Cheng, L. Lei, Y. Chen et al., Surface and interface engineering of two-dimensional bismuth-based photocatalysts for ambient molecule activation. J. Mater. Chem. A 9, 196–233 (2021). https://doi.org/10.1039/D0TA08165E
X. Gan, D. Lei, R. Ye, H. Zhao, K.-Y. Wong, Transition metal dichalcogenide-based mixed-dimensional heterostructures for visible-light-driven photocatalysis: dimensionality and interface engineering. Nano Res. 14, 2003–2022 (2021). https://doi.org/10.1007/s12274-020-2955-x
W. Choi, N. Choudhary, G.H. Han, J. Park, D. Akinwande et al., Recent development of two-dimensional transition metal dichalcogenides and their applications. Mater. Today 20, 116–130 (2017). https://doi.org/10.1016/j.mattod.2016.10.002
J. Zhou, J. Lin, X. Huang, Y. Zhou, Y. Chen et al., A library of atomically thin metal chalcogenides. Nature 556, 355–359 (2018). https://doi.org/10.1038/s41586-018-0008-3
X. Xi, Z. Wang, W. Zhao, J.-H. Park, K.T. Law et al., Ising pairing in superconducting NbSe2 atomiclayers. Nat. Phys. 12, 139–143 (2016). https://doi.org/10.1038/nphys3538
Y. Qi, P.G. Naumov, M.N. Ali, C.R. Rajamathi, W. Schnelle et al., Superconductivity in weyl semimetal candidate MoTe2. Nat. Commun. 7, 11038 (2016). https://doi.org/10.1038/ncomms11038
E. Navarro-Moratalla, J.O. Island, S. Mañas-Valero, E. Pinilla-Cienfuegos, A. Castellanos-Gomez et al., Enhanced superconductivity in atomically thin TaS2. Nat. Commun. 7, 11043 (2016). https://doi.org/10.1038/ncomms11043
X. Qian, J. Liu, L. Fu, J. Li, Quantum spin Hall effect in two-dimensional transition metal dichalcogenides. Science 346, 1344–1347 (2014). https://doi.org/10.1126/science.1256815
Q.H. Wang, K. Kalantar-Zadeh, A. Kis, J.N. Coleman, M.S. Strano, Electronics and optoelectronics of two-dimensional transition metal dichalcogenides. Nat. Nanotechnol. 7, 699–712 (2012). https://doi.org/10.1038/nnano.2012.193
Y. Xiao, M. Zhou, J. Liu, J. Xu, L. Fu, Phase engineering of two-dimensional transition metal dichalcogenides. Sci. China Mater. 62, 759–775 (2019). https://doi.org/10.1007/s40843-018-9398-1
X. Yuan, M. Yang, L. Wang, Y. Li, Structural stability and intriguing electronic properties of two-dimensional transition metal dichalcogenide alloys. Phys. Chem. Chem. Phys. 19, 13846–13854 (2017). https://doi.org/10.1039/C7CP01727H
C. Gao, X. Yang, M. Jiang, L. Chen, Z. Chen et al., Machine learning-enabled band gap prediction of monolayer transition metal chalcogenide alloys. Phys. Chem. Chem. Phys. 24, 4653–4665 (2022). https://doi.org/10.1039/d1cp05847a
Z. Shi, Q. Zhang, U. Schwingenschlögl, Alloying as a route to monolayer transition metal dichalcogenides with improved optoelectronic performance: Mo(S1–xSex)2 and Mo1–yWyS2. ACS Appl. Energy Mater. 1, 2208–2214 (2018). https://doi.org/10.1021/acsaem.8b00288
M. Chen, L. Zhu, Q. Chen, N. Miao, C. Si et al., Quantifying the composition dependency of the ground-state structure, electronic property and phase-transition dynamics in ternary transition-metal-dichalcogenide monolayers. J. Mater. Chem. C 8, 721–733 (2020). https://doi.org/10.1039/C9TC05487A
H. Li, X. Duan, X. Wu, X. Zhuang, H. Zhou et al., Growth of alloy MoS2xSe2(1–x) nanosheets with fully tunable chemical compositions and optical properties. J. Am. Chem. Soc. 136, 3756–3759 (2014). https://doi.org/10.1021/ja500069b
Q. Deng, X. Li, H. Si, J. Hong, S. Wang et al., Strong band bowing effects and distinctive optoelectronic properties of 2H and 1T’ phase-tunable MoxRe1–xS2 alloys. Adv. Funct. Mater. 30, 2003264 (2020). https://doi.org/10.1002/adfm.202003264
X. Duan, C. Wang, Z. Fan, G. Hao, L. Kou et al., Synthesis of WS2xSe2-2x alloy nanosheets with composition-tunable electronic properties. Nano Lett. 16, 264–269 (2016). https://doi.org/10.1021/acs.nanolett.5b03662
V. Kochat, A. Apte, J.A. Hachtel, H. Kumazoe, A. Krishnamoorthy et al., Re doping in 2D transition metal dichalcogenides as a new route to tailor structural phases and induced magnetism. Adv. Mater. 29, 1703754 (2017). https://doi.org/10.1002/adma.201703754
P. Yu, J. Lin, L. Sun, Q.L. Le, X. Yu et al., Metal-semiconductor phase-transition in WSe2(1–x)Te2x monolayer. Adv. Mater. 29, 1603991 (2017). https://doi.org/10.1002/adma.201603991
Y. Deng, P. Li, C. Zhu, J. Zhou, X. Wang et al., Controlled synthesis of MoxW1−xTe2 atomic layers with emergent quantum states. ACS Nano 15, 11526–11534 (2021). https://doi.org/10.1021/acsnano.1c01441
A.-Y. Lu, H. Zhu, J. Xiao, C.-P. Chuu, Y. Han et al., Janus monolayers of transition metal dichalcogenides. Nat. Nanotechnol. 12, 744–749 (2017). https://doi.org/10.1038/nnano.2017.100
J. Zhang, S. Jia, I. Kholmanov, L. Dong, D. Er et al., Janus monolayer transition-metal dichalcogenides. ACS Nano 11, 8192–8198 (2017). https://doi.org/10.1021/acsnano.7b03186
H. Mo, X. Zhang, Y. Liu, P. Kang, H. Nan et al., Two-dimensional alloying molybdenum tin disulfide monolayers with fast photoresponse. ACS Appl. Mater. Interfaces 11, 39077–39087 (2019). https://doi.org/10.1021/acsami.9b13645
C. Tan, Z. Luo, A. Chaturvedi, Y. Cai, Y. Du et al., Preparation of high-percentage 1T-phase transition metal dichalcogenide nanodots for electrochemical hydrogen evolution. Adv. Mater. 30, 1705509 (2018). https://doi.org/10.1002/adma.201705509
I.S. Kwon, I.H. Kwak, T.T. Debela, J.Y. Kim, S.J. Yoo et al., Phase-transition Mo1−xVxSe2 alloy nanosheets with rich V-Se vacancies and their enhanced catalytic performance of hydrogen evolution reaction. ACS Nano 15, 14672–14682 (2021). https://doi.org/10.1021/acsnano.1c04453
I.H. Kwak, I.S. Kwon, T.T. Debela, H.G. Abbas, Y.C. Park et al., Phase evolution of Re1−xMoxSe2 alloy nanosheets and their enhanced catalytic activity toward hydrogen evolution reaction. ACS Nano 14, 11995–12005 (2020). https://doi.org/10.1021/acsnano.0c05159
X. Liu, J. Wu, W. Yu, L. Chen, Z. Huang et al., Monolayer WxMo1−xS2 grown by atmospheric pressure chemical vapor deposition: bandgap engineering and field effect transistors. Adv. Funct. Mater. 27, 1606469 (2017). https://doi.org/10.1002/adfm.201606469
G. Shao, X.-X. Xue, B. Wu, Y.-C. Lin, M. Ouzounian et al., Template-assisted synthesis of metallic 1T’-Sn0.3W0.7S2 nanosheets for hydrogen evolution reaction. Adv. Funct. Mater. 30, 1906069 (2020). https://doi.org/10.1002/adfm.201906069
X. Li, M.-W. Lin, L. Basile, S.M. Hus, A.A. Puretzky et al., Isoelectronic tungsten doping in monolayer MoSe2 for carrier type modulation. Adv. Mater. 28, 8240–8247 (2016). https://doi.org/10.1002/adma.201601991
Q. Fu, L. Yang, W. Wang, A. Han, J. Huang et al., Synthesis and enhanced electrochemical catalytic performance of monolayer WS2(1−x)Se2x with a tunable band gap. Adv. Mater. 27, 4732–4738 (2015). https://doi.org/10.1002/adma.201500368
W.-J. Yin, H.-J. Tan, P.-J. Ding, B. Wen, X.-B. Li et al., Recent advances in low-dimensional Janus materials: theoretical and simulation perspectives. Mater. Adv. 2, 7543–7558 (2021). https://doi.org/10.1039/D1MA00660F
F. Raffone, C. Ataca, J.C. Grossman, G. Cicero, MoS2 enhanced T-phase stabilization and tunability through alloying. J. Phys. Chem. Lett. 7, 2304–2309 (2016). https://doi.org/10.1021/acs.jpclett.6b00794
X. Zhou, L. Gan, W. Tian, Q. Zhang, S. Jin et al., Ultrathin SnSe2 flakes grown by chemical vapor deposition for high-performance photodetectors. Adv. Mater. 27, 8035–8041 (2015). https://doi.org/10.1002/adma.201503873
Y. Huang, H.-X. Deng, K. Xu, Z.-X. Wang, Q.-S. Wang et al., Highly sensitive and fast phototransistor based on large size CVD-grown SnS2 nanosheets. Nanoscale 7, 14093–14099 (2015). https://doi.org/10.1039/C5NR04174K
P. Perumal, R.K. Ulaganathan, R. Sankar, Y.-M. Liao, T.-M. Sun et al., Ultra-thin layered ternary single crystals [Sn(SxSe1–x)2] with bandgap engineering for high performance phototransistors on versatile substrates. Adv. Funct. Mater. 26, 3630–3638 (2016). https://doi.org/10.1002/adfm.201600081
A. Kutana, E.S. Penev, B.I. Yakobson, Engineering electronic properties of layered transition-metal dichalcogenide compounds through alloying. Nanoscale 6, 5820–5825 (2014). https://doi.org/10.1039/C4NR00177J
J. Kang, S. Tongay, J. Li, J. Wu, Monolayer semiconducting transition metal dichalcogenide alloys: stability and band bowing. J. Appl. Phys. 113, 143703 (2013). https://doi.org/10.1063/1.4799126
H.-P. Komsa, A.V. Krasheninnikov, Two-dimensional transition metal dichalcogenide alloys: stability and electronic properties. J. Phys. Chem. Lett. 3, 3652–3656 (2012). https://doi.org/10.1021/jz301673x
Z. Hemmat, J. Cavin, A. Ahmadiparidari, A. Ruckel, S. Rastegar et al., Quasi-binary transition metal dichalcogenide alloys: thermodynamic stability prediction, scalable synthesis, and application. Adv. Mater. 32, e1907041 (2020). https://doi.org/10.1002/adma.201907041
J.-H. Yang, B.I. Yakobson, Unusual negative formation enthalpies and atomic ordering in isovalent alloys of transition metal dichalcogenide monolayers. Chem. Mater. 30, 1547–1555 (2018). https://doi.org/10.1021/acs.chemmater.7b04527
M.C. Troparevsky, J.R. Morris, M. Daene, Y. Wang, A.R. Lupini et al., Beyond atomic sizes and hume-rothery rules: understanding and predicting high-entropy alloys. JOM 67, 2350–2363 (2015). https://doi.org/10.1007/s11837-015-1594-2
H. Taghinejad, D.A. Rehn, C. Muccianti, A.A. Eftekhar, M. Tian et al., Defect-mediated alloying of monolayer transition-metal dichalcogenides. ACS Nano 12, 12795–12804 (2018). https://doi.org/10.1021/acsnano.8b07920
W. Yao, Z. Kang, J. Deng, Y. Chen, Q. Song et al., Synthesis of 2D MoS2(1–x)Se2x semiconductor alloy by chemical vapor deposition. RSC Adv. 10, 42172–42177 (2020). https://doi.org/10.1039/d0ra07776c
Y. Tsai, Z. Chu, Y. Han, C.-P. Chuu, D. Wu et al., Tailoring semiconductor lateral multijunctions for giant photoconductivity enhancement. Adv. Mater. 29, 1703680 (2017). https://doi.org/10.1002/adma.201703680
B. Tang, J. Zhou, P. Sun, X. Wang, L. Bai et al., Phase-controlled synthesis of monolayer ternary telluride with a random local displacement of tellurium atoms. Adv. Mater. 31, e1900862 (2019). https://doi.org/10.1002/adma.201900862
J. Cavin, A. Ahmadiparidari, L. Majidi, A.S. Thind, S.N. Misal et al., 2D high-entropy transition metal dichalcogenides for carbon dioxide electrocatalysis. Adv. Mater. 33, e2100347 (2021). https://doi.org/10.1002/adma.202100347
Y. Chen, Z. Tian, X. Wang, N. Ran, C. Wang et al., 2D transition metal dichalcogenide with increased entropy for piezoelectric electronics. Adv. Mater. 34, e2201630 (2022). https://doi.org/10.1002/adma.202201630
J. Lin, J. Zhou, S. Zuluaga, P. Yu, M. Gu et al., Anisotropic ordering in 1T’ molybdenum and tungsten ditelluride layers alloyed with sulfur and selenium. ACS Nano 12, 894–901 (2018). https://doi.org/10.1021/acsnano.7b08782
D.O. Dumcenco, H. Kobayashi, Z. Liu, Y.-S. Huang, K. Suenaga, Visualization and quantification of transition metal atomic mixing in Mo1−xWxS2 single layers. Nat. Commun. 4, 1351 (2013). https://doi.org/10.1038/ncomms2351
S. Susarla, P. Manimunda, Y.M. Jaques, J.A. Hachtel, J.C. Idrobo et al., Strain-induced structural deformation study of 2D MoxW(1–x)S2. Adv. Mater. Interfaces 6, 1801262 (2019). https://doi.org/10.1002/admi.201801262
C. Tan, W. Zhao, A. Chaturvedi, Z. Fei, Z. Zeng et al., Preparation of single-layer MoS2xSe2(1–x) and MoxW1-xS2 nanosheets with high-concentration metallic 1T phase. Small 12, 1866–1874 (2016). https://doi.org/10.1002/smll.201600014
D. Hu, G. Xu, L. Xing, X. Yan, J. Wang et al., Two-dimensional semiconductors grown by chemical vapor transport. Angew. Chem. Int. Ed. 56, 3611–3615 (2017). https://doi.org/10.1002/anie.201700439
G.H. Han, D.L. Duong, D.H. Keum, S.J. Yun, Y.H. Lee, Van der waals metallic transition metal dichalcogenides. Chem. Rev. 118, 6297–6336 (2018). https://doi.org/10.1021/acs.chemrev.7b00618
Q. Gong, L. Cheng, C. Liu, M. Zhang, Q. Feng et al., Ultrathin MoS2(1–x)Se2x alloy nanoflakes for electrocatalytic hydrogen evolution reaction. ACS Catal. 5, 2213–2219 (2015). https://doi.org/10.1021/cs501970w
Q. Feng, Y. Zhu, J. Hong, M. Zhang, W. Duan et al., Growth of large-area 2D MoS2(1–x)Se2x semiconductor alloys. Adv. Mater. 26, 2648–2653 (2014). https://doi.org/10.1002/adma.201306095
Z. Zheng, J. Yao, G. Yang, Centimeter-scale deposition of Mo0.5W0.5Se2 alloy film for high-performance photodetectors on versatile substrates. ACS Appl. Mater. Interfaces 9, 14920–14928 (2017). https://doi.org/10.1021/acsami.7b02166
L. Zhang, T. Yang, X. He, W. Zhang, G. Vinai et al., Molecular beam epitaxy of two-dimensional vanadium-molybdenum diselenide alloys. ACS Nano 14, 11140–11149 (2020). https://doi.org/10.1021/acsnano.0c02124
X. Hu, Z. Hemmat, L. Majidi, J. Cavin, R. Mishra et al., Controlling nanoscale thermal expansion of monolayer transition metal dichalcogenides by alloy engineering. Small 16, e1905892 (2020). https://doi.org/10.1002/smll.201905892
G.K. Solanki, D.N. Gujarathi, M.P. Deshpande, D. Lakshminarayana, M.K. Agarwal, Transport property measurements in tungsten sulphoselenide single crystals grown by a CVT technique. Cryst. Res. Technol. 43, 179–185 (2008). https://doi.org/10.1002/crat.200711060
S.D. Karande, N. Kaushik, D.S. Narang, D. Late, S. Lodha, Thickness tunable transport in alloyed WSSe field effect transistors. Appl. Phys. Lett. 109, 142101 (2016). https://doi.org/10.1063/1.4964289
F.I. Alzakia, S.C. Tan, Liquid-exfoliated 2D materials for optoelectronic applications. Adv. Sci. 8, e2003864 (2021). https://doi.org/10.1002/advs.202003864
S. Witomska, T. Leydecker, A. Ciesielski, P. Samorì, Production and patterning of liquid phase–exfoliated 2D sheets for applications in optoelectronics. Adv. Funct. Mater. 29, 1901126 (2019). https://doi.org/10.1002/adfm.201901126
Z. Yang, H. Liang, X. Wang, X. Ma, T. Zhang et al., Atom-thin SnS2-xSex with adjustable compositions by direct liquid exfoliation from single crystals. ACS Nano 10, 755–762 (2016). https://doi.org/10.1021/acsnano.5b05823
I.S. Kwon, I.H. Kwak, J.Y. Kim, T.T. Debela, Y.C. Park et al., Concurrent vacancy and adatom defects of Mo1-xNbxSe2 alloy nanosheets enhance electrochemical performance of hydrogen evolution reaction. ACS Nano 15, 5467–5477 (2021). https://doi.org/10.1021/acsnano.1c00171
I.H. Kwak, T.T. Debela, I.S. Kwon, J. Seo, S.J. Yoo et al., Anisotropic alloying of Re1−xMoxS2 nanosheets to boost the electrochemical hydrogen evolution reaction. J. Mater. Chem. A 8, 25131–25141 (2020). https://doi.org/10.1039/D0TA09299A
W. Zhang, X. Li, T. Jiang, J. Song, Y. Lin et al., CVD synthesis of Mo(1–x)WxS2 and MoS2(1–x)Se2x alloy monolayers aimed at tuning the bandgap of molybdenum disulfide. Nanoscale 7, 13554–13560 (2015). https://doi.org/10.1039/c5nr02515j
Z. Cai, B. Liu, X. Zou, H.-M. Cheng, Chemical vapor deposition growth and applications of two-dimensional materials and their heterostructures. Chem. Rev. 118, 6091–6133 (2018). https://doi.org/10.1021/acs.chemrev.7b00536
L. Tang, J. Tan, H. Nong, B. Liu, H.-M. Cheng, Chemical vapor deposition growth of two-dimensional compound materials: controllability, material quality, and growth mechanism. Acc. Mater. Res. 2, 36–47 (2021). https://doi.org/10.1021/accountsmr.0c00063
L. Fang, S. Tao, Z. Tian, K. Liu, X. Li et al., Controlled growth of transition metal dichalcogenide via thermogravimetric prediction of precursors vapor concentration. Nano Res. 14, 2867–2874 (2021). https://doi.org/10.1007/s12274-021-3347-6
F. Chen, L. Wang, X. Ji, Q. Zhang, Temperature-dependent two-dimensional transition metal dichalcogenide heterostructures: controlled synthesis and their properties. ACS Appl. Mater. Interfaces 9, 30821–30831 (2017). https://doi.org/10.1021/acsami.7b08313
S. Susarla, V. Kochat, A. Kutana, J.A. Hachtel, J.C. Idrobo et al., Phase segregation behavior of two-dimensional transition metal dichalcogenide binary alloys induced by dissimilar substitution. Chem. Mater. 29, 7431–7439 (2017). https://doi.org/10.1021/acs.chemmater.7b02407
D.B. Trivedi, G. Turgut, Y. Qin, M.Y. Sayyad, D. Hajra et al., Room-temperature synthesis of 2D Janus crystals and their heterostructures. Adv. Mater. 32, e2006320 (2020). https://doi.org/10.1002/adma.202006320
S.J. Yun, G.H. Han, H. Kim, D.L. Duong, B.G. Shin et al., Telluriding monolayer MoS2 and WS2 via alkali metal scooter. Nat. Commun. 8, 2163 (2017). https://doi.org/10.1038/s41467-017-02238-0
G. Xue, X. Sui, P. Yin, Z. Zhou, X. Li et al., Modularized batch production of 12-inch transition metal dichalcogenides by local element supply. Sci. Bull. 68, 1514–1521 (2023). https://doi.org/10.1016/j.scib.2023.06.037
Y. Zuo, C. Liu, L. Ding, R. Qiao, J. Tian et al., Robust growth of two-dimensional metal dichalcogenides and their alloys by active chalcogen monomer supply. Nat. Commun. 13, 1007 (2022). https://doi.org/10.1038/s41467-022-28628-7
Z. Ye, C. Tan, X. Huang, Y. Ouyang, L. Yang et al., Emerging MoS2 wafer-scale technique for integrated circuits. Nano-Micro Lett. 15, 38 (2023). https://doi.org/10.1007/s40820-022-01010-4
J. Lee, S. Pak, Y.W. Lee, Y. Park, A.R. Jang et al., Direct epitaxial synthesis of selective two-dimensional lateral heterostructures. ACS Nano 13, 13047–13055 (2019). https://doi.org/10.1021/acsnano.9b05722
X. Zhang, S. Xiao, L. Shi, H. Nan, X. Wan et al., Large-size Mo1-xWxS2 and W1-xMoxS2 (x = 0–0.5) monolayers by confined-space chemical vapor deposition. Appl. Surf. Sci. 457, 591–597 (2018). https://doi.org/10.1016/j.apsusc.2018.06.299
K. Ding, Q. Fu, H. Nan, X. Gu, K. Ostrikov et al., Controllable synthesis of WS2(1–x)Se2x monolayers with fast photoresponse by a facile chemical vapor deposition strategy. Mater. Sci. Eng. B 269, 115176 (2021). https://doi.org/10.1016/j.mseb.2021.115176
P. Kang, H. Nan, X. Zhang, H. Mo, Z. Ni et al., Controllable synthesis of crystalline ReS2(1–x)Se2x monolayers on amorphous SiO2/Si substrates with fast photoresponse. Adv. Opt. Mater. 8, 1901415 (2020). https://doi.org/10.1002/adom.201901415
Q. Feng, N. Mao, J. Wu, H. Xu, C. Wang et al., Growth of MoS2(1–x)Se2x (x = 0.41–1.00) monolayer alloys with controlled morphology by physical vapor deposition. ACS Nano 9, 7450–7455 (2015). https://doi.org/10.1021/acsnano.5b02506
M.N. Bui, S. Rost, M. Auge, J.-S. Tu, L. Zhou et al., Low-energy Se ion implantation in MoS2 monolayers. NPJ 2D Mater. Appl. 6, 42 (2022). https://doi.org/10.1038/s41699-022-00318-4
S. Prucnal, A. Hashemi, M. Ghorbani-Asl, R. Hübner, J. Duan et al., Chlorine doping of MoSe2 flakes by ion implantation. Nanoscale 13, 5834–5846 (2021). https://doi.org/10.1039/D0NR08935D
Q. Ma, M. Isarraraz, C.S. Wang, E. Preciado, V. Klee et al., Postgrowth tuning of the bandgap of single-layer molybdenum disulfide films by sulfur/selenium exchange. ACS Nano 8, 4672–4677 (2014). https://doi.org/10.1021/nn5004327
M. Ghorbani-Asl, S. Kretschmer, D.E. Spearot, A.V. Krasheninnikov, Two-dimensional MoS2 under ion irradiation: from controlled defect production to electronic structure engineering. 2D Mater. 4, 025078 (2017). https://doi.org/10.1088/2053-1583/aa6b17
X. Kong, L. Liang, Floquet band engineering and topological phase transitions in 1T’ transition metal dichalcogenides. 2D Mater. 9, 025005 (2022). https://doi.org/10.1088/2053-1583/ac4957
J. Yao, Z. Zheng, G. Yang, Promoting the performance of layered-material photodetectors by alloy engineering. ACS Appl. Mater. Interfaces 8, 12915–12924 (2016). https://doi.org/10.1021/acsami.6b03691
J.G. Song, G.H. Ryu, S.J. Lee, S. Sim, C.W. Lee et al., Controllable synthesis of molybdenum tungsten disulfide alloy for vertically composition-controlled multilayer. Nat. Commun. 6, 7817 (2015). https://doi.org/10.1038/ncomms8817
H.H. Huang, X. Fan, D.J. Singh, W.T. Zheng, Recent progress of TMD nanomaterials: phase transitions and applications. Nanoscale 12, 1247–1268 (2020). https://doi.org/10.1039/c9nr08313h
D. Voiry, A. Mohite, M. Chhowalla, Phase engineering of transition metal dichalcogenides. Chem. Soc. Rev. 44, 2702–2712 (2015). https://doi.org/10.1039/c5cs00151j
S.-Z. Yang, Y. Gong, P. Manchanda, Y.-Y. Zhang, G. Ye et al., Rhenium-doped and stabilized MoS2 atomic layers with basal-plane catalytic activity. Adv. Mater. 30, e1803477 (2018). https://doi.org/10.1002/adma.201803477
I.S. Kwon, I.H. Kwak, G.M. Zewdie, S.J. Lee, J.Y. Kim et al., WSe2-VSe2 alloyed nanosheets to enhance the catalytic performance of hydrogen evolution reaction. ACS Nano 16, 12569–12579 (2022). https://doi.org/10.1021/acsnano.2c04113
K. Yang, X. Wang, H. Li, B. Chen, X. Zhang et al., Composition- and phase-controlled synthesis and applications of alloyed phase heterostructures of transition metal disulphides. Nanoscale 9, 5102–5109 (2017). https://doi.org/10.1039/c7nr01015j
Z. Wang, Y. Shen, Y. Ito, Y. Zhang, J. Du et al., Synthesizing 1T–1H two-phase Mo1-xWxS2 monolayers by chemical vapor deposition. ACS Nano 12, 1571–1579 (2018). https://doi.org/10.1021/acsnano.7b08149
Z. Wang, X. Zhao, Y. Yang, L. Qiao, L. Lv et al., Phase-controlled synthesis of monolayer W1–xRexS2 alloy with improved photoresponse performance. Small 16, e2000852 (2020). https://doi.org/10.1002/smll.202000852
Y.-C. Lin, D.O. Dumcenco, Y.-S. Huang, K. Suenaga, Atomic mechanism of the semiconducting-to-metallic phase transition in single-layered MoS2. Nat. Nanotechnol. 9, 391–396 (2014). https://doi.org/10.1038/nnano.2014.64
I.H. Kwak, I.S. Kwon, G.M. Zewdie, T.T. Debela, S.J. Lee et al., Polytypic phase transition of Nb1- xVxSe2 via colloidal synthesis and their catalytic activity toward hydrogen evolution reaction. ACS Nano 16, 4278–4288 (2022). https://doi.org/10.1021/acsnano.1c10301
K.Y. Ko, S. Lee, K. Park, Y. Kim, W.J. Woo et al., High-performance gas sensor using a large-area WS2xSe2-2x alloy for low-power operation wearable applications. ACS Appl. Mater. Interfaces 10, 34163–34171 (2018). https://doi.org/10.1021/acsami.8b10455
Y. Chen, J. Xi, D.O. Dumcenco, Z. Liu, K. Suenaga et al., Tunable band gap photoluminescence from atomically thin transition-metal dichalcogenide alloys. ACS Nano 7, 4610–4616 (2013). https://doi.org/10.1021/nn401420h
M. Zhang, J. Wu, Y. Zhu, D.O. Dumcenco, J. Hong et al., Two-dimensional molybdenum tungsten diselenide alloys: photoluminescence, Raman scattering, and electrical transport. ACS Nano 8, 7130–7137 (2014). https://doi.org/10.1021/nn5020566
F. Cui, Q. Feng, J. Hong, R. Wang, Y. Bai et al., Synthesis of large-size 1T’ ReS2xSe2(1–x) alloy monolayer with tunable bandgap and carrier type. Adv. Mater. 29, 1705015 (2017). https://doi.org/10.1002/adma.201705015
J. Kim, H. Seung, D. Kang, J. Kim, H. Bae et al., Wafer-scale production of transition metal dichalcogenides and alloy monolayers by nanocrystal conversion for large-scale ultrathin flexible electronics. Nano Lett. 21, 9153–9163 (2021). https://doi.org/10.1021/acs.nanolett.1c02991
Y.-R. Lin, W.-H. Cheng, M.H. Richter, J.S. DuChene, E.A. Peterson et al., Band edge tailoring in few-layer two-dimensional molybdenum sulfide/selenide alloys. J. Phys. Chem. C 124, 22893–22902 (2020). https://doi.org/10.1021/acs.jpcc.0c04719
N. Tit, I.M. Obaidat, H. Alawadhi, Origins of bandgap bowing in compound-semiconductor common-cation ternary alloys. J. Phys. Condens. Matter 21, 075802 (2009). https://doi.org/10.1088/0953-8984/21/7/075802
L. Yang, Q. Fu, W. Wang, J. Huang, J. Huang et al., Large-area synthesis of monolayered MoS2(1–x)Se2x with a tunable band gap and its enhanced electrochemical catalytic activity. Nanoscale 7, 10490–10497 (2015). https://doi.org/10.1039/c5nr02652k
F. Liang, H. Xu, Z. Dong, Y. Xie, C. Luo et al., Substrates and interlayer coupling effects on Mo1–xWxSe2 alloys. J. Semicond. 40, 062005 (2019). https://doi.org/10.1088/1674-4926/40/6/062005
H. Masenda, L.M. Schneider, M. Adel Aly, S.J. Machchhar, A. Usman et al., Energy scaling of compositional disorder in ternary transition-metal dichalcogenide monolayers. Adv. Electron. Mater. 7, 2100196 (2021). https://doi.org/10.1002/aelm.202100196
B. Aslan, I.M. Datye, M.J. Mleczko, K. Sze Cheung, S. Krylyuk et al., Probing the optical properties and strain-tuning of ultrathin Mo1−xWxTe2. Nano Lett. 18, 2485–2491 (2018). https://doi.org/10.1021/acs.nanolett.8b00049
W. Zheng, B. Zheng, C. Yan, Y. Liu, X. Sun et al., Direct vapor growth of 2D vertical heterostructures with tunable band alignments and interfacial charge transfer behaviors. Adv. Sci. 6, 1802204 (2019). https://doi.org/10.1002/advs.201802204
J. Wu, L. Xie, Structural quantification for graphene and related two-dimensional materials by Raman spectroscopy. Anal. Chem. 91, 468–481 (2019). https://doi.org/10.1021/acs.analchem.8b04991
X. Zhang, X.-F. Qiao, W. Shi, J.-B. Wu, D.-S. Jiang et al., Phonon and Raman scattering of two-dimensional transition metal dichalcogenides from monolayer, multilayer to bulk material. Chem. Soc. Rev. 44, 2757–2785 (2015). https://doi.org/10.1039/c4cs00282b
C. Ramkumar, K.P. Jain, S.C. Abbi, Resonant Raman scattering probe of alloying effect in GaAs1-xPx ternary alloy semiconductors. Phys. Rev. B Condens. Matter 54, 7921–7928 (1996). https://doi.org/10.1103/physrevb.54.7921
Y. Chen, D.O. Dumcenco, Y. Zhu, X. Zhang, N. Mao et al., Composition-dependent Raman modes of Mo1−xWxS2 monolayer alloys. Nanoscale 6, 2833–2839 (2014). https://doi.org/10.1039/C3NR05630A
X. Gan, R. Lv, X. Wang, Z. Zhang, K. Fujisawa et al., Pyrolytic carbon supported alloying metal dichalcogenides as free-standing electrodes for efficient hydrogen evolution. Carbon 132, 512–519 (2018). https://doi.org/10.1016/j.carbon.2018.02.025
Y. Sun, K. Fujisawa, Z. Lin, Y. Lei, J.S. Mondschein et al., Low-temperature solution synthesis of transition metal dichalcogenide alloys with tunable optical properties. J. Am. Chem. Soc. 139, 11096–11105 (2017). https://doi.org/10.1021/jacs.7b04443
D. Wang, X. Zhang, G. Guo, S. Gao, X. Li et al., Large-area synthesis of layered HfS2(1–x)Se2x alloys with fully tunable chemical compositions and bandgaps. Adv. Mater. 30, e1803285 (2018). https://doi.org/10.1002/adma.201803285
A. Apte, A. Krishnamoorthy, J.A. Hachtel, S. Susarla, J.C. Idrobo et al., Telluride-based atomically thin layers of ternary two-dimensional transition metal dichalcogenide alloys. Chem. Mater. 30, 7262–7268 (2018). https://doi.org/10.1021/acs.chemmater.8b03444
A.T. Barton, R. Yue, L.A. Walsh, G. Zhou, C. Cormier et al., WSe(2–x)Tex alloys grown by molecular beam epitaxy. 2D Mater. 6, 045027 (2019). https://doi.org/10.1088/2053-1583/ab334d
Q. Fu, J. Han, X. Wang, P. Xu, T. Yao et al., 2D transition metal dichalcogenides: design, modulation, and challenges in electrocatalysis. Adv. Mater. 33, e1907818 (2021). https://doi.org/10.1002/adma.201907818
A.K. Chanchal, Garg, MREI-model calculations of optical phonons in layered mixed crystals of 2H-polytype of the series SnS2–xSex (0⩽x⩽2). Phys. B Condens. Matter 383, 188–193 (2006). https://doi.org/10.1016/j.physb.2006.03.009
Y. Chen, W. Shockley, G.L. Pearson, Lattice vibration spectra of GaAsxP1-x single crystals. Phys. Rev. 151, 648–656 (1966). https://doi.org/10.1103/PhysRev.151.648
I.F. Chang, S.S. Mitra, Application of a modified random-element-isodisplacement model to long-wavelength optic phonons of mixed crystals. Phys. Rev. 172, 924–933 (1968). https://doi.org/10.1103/physrev.172.924
B. Radisavljevic, A. Radenovic, J. Brivio, V. Giacometti, A. Kis, Single-layer MoS2 transistors. Nat. Nanotechnol. 6, 147–150 (2011). https://doi.org/10.1038/nnano.2010.279
A.R. Kim, Y. Kim, J. Nam, H.S. Chung, D.J. Kim et al., Alloyed 2D metal-semiconductor atomic layer junctions. Nano Lett. 16, 1890–1895 (2016). https://doi.org/10.1021/acs.nanolett.5b05036
A. Sebastian, R. Pendurthi, T.H. Choudhury, J.M. Redwing, S. Das, Benchmarking monolayer MoS2 and WS2 field-effect transistors. Nat. Commun. 12, 693 (2021). https://doi.org/10.1038/s41467-020-20732-w
B. Liu, Y. Ma, A. Zhang, L. Chen, A.N. Abbas et al., High-performance WSe2 field-effect transistors via controlled formation of In-plane heterojunctions. ACS Nano 10, 5153–5160 (2016). https://doi.org/10.1021/acsnano.6b00527
H. Zhou, C. Wang, J.C. Shaw, R. Cheng, Y. Chen et al., Large area growth and electrical properties of p-type WSe2 atomic layers. Nano Lett. 15, 709–713 (2015). https://doi.org/10.1021/nl504256y
K. Xu, A. Sharma, S. Kang, J. Kang, X. Hu et al., Heterogeneous electronic and photonic devices based on monolayer ternary telluride core/shell structures. Adv. Mater. 33, e2100343 (2021). https://doi.org/10.1002/adma.202100343
K.-C. Chen, C.-Y. Jian, Y.-J. Chen, S.-C. Lee, S.-W. Chang et al., Current enhancement and bipolar current modulation of top-gate transistors based on monolayer MoS2 on three-layer WxMo1−xS2. ACS Appl. Mater. Interfaces 10, 24733–24738 (2018). https://doi.org/10.1021/acsami.8b06327
V.T. Vu, T.T.H. Vu, T.L. Phan, W.T. Kang, Y.R. Kim et al., One-step synthesis of NbSe2/Nb-doped-WSe2 metal/doped-semiconductor van der waals heterostructures for doping controlled ohmic contact. ACS Nano 15, 13031–13040 (2021). https://doi.org/10.1021/acsnano.1c02038
W. Zhou, X. Zou, S. Najmaei, Z. Liu, Y. Shi et al., Intrinsic structural defects in monolayer molybdenum disulfide. Nano Lett. 13, 2615–2622 (2013). https://doi.org/10.1021/nl4007479
H. Tian, M.L. Chin, S. Najmaei, Q. Guo, F. Xia et al., Optoelectronic devices based on two-dimensional transition metal dichalcogenides. Nano Res. 9, 1543–1560 (2016). https://doi.org/10.1007/s12274-016-1034-9
H. Qiu, T. Xu, Z. Wang, W. Ren, H. Nan et al., Hopping transport through defect-induced localized states in molybdenum disulphide. Nat. Commun. 4, 2642 (2013). https://doi.org/10.1038/ncomms3642
Y.R. Lim, J.K. Han, Y. Yoon, J.B. Lee, C. Jeon et al., Atomic-level customization of 4 in transition metal dichalcogenide multilayer alloys for industrial applications. Adv. Mater. 31, e1901405 (2019). https://doi.org/10.1002/adma.201901405
H. Xu, J. Zhu, G. Zou, W. Liu, X. Li et al., Spatially bandgap-graded MoS2(1–x)Se2x homojunctions for self-powered visible-near-infrared phototransistors. Nano-Micro Lett. 12, 26 (2020). https://doi.org/10.1007/s40820-019-0361-2
P. Chauhan, G.K. Solanki, A.B. Patel, K. Patel, P. Pataniya et al., Tunable and anisotropic photoresponse of layered Re0.2Sn0.8Se2 ternary alloy. Sol. Energy Mater. Sol. Cells 200, 109936 (2019). https://doi.org/10.1016/j.solmat.2019.109936
J. Ye, K. Liao, X. Ge, Z. Wang, Y. Wang et al., Narrowing bandgap of HfS2 by Te substitution for short-wavelength infrared photodetection. Adv. Opt. Mater. 9, 2002248 (2021). https://doi.org/10.1002/adom.202002248
T.F. Jaramillo, K.P. Jørgensen, J. Bonde, J.H. Nielsen, S. Horch et al., Identification of active edge sites for electrochemical H2 evolution from MoS2 nanocatalysts. Science 317, 100–102 (2007). https://doi.org/10.1126/science.1141483
W. Xu, S. Li, S. Zhou, J.K. Lee, S. Wang et al., Large dendritic monolayer MoS2 grown by atmospheric pressure chemical vapor deposition for electrocatalysis. ACS Appl. Mater. Interfaces 10, 4630–4639 (2018). https://doi.org/10.1021/acsami.7b14861
Z. Lai, A. Chaturvedi, Y. Wang, T.H. Tran, X. Liu et al., Preparation of 1T’-phase ReS2xSe2(1–x) (x = 0–1) nanodots for highly efficient electrocatalytic hydrogen evolution reaction. J. Am. Chem. Soc. 140, 8563–8568 (2018). https://doi.org/10.1021/jacs.8b04513
Y. Lei, S. Pakhira, K. Fujisawa, X. Wang, O.O. Iyiola et al., Low-temperature synthesis of heterostructures of transition metal dichalcogenide alloys (WxMo1-xS2) and graphene with superior catalytic performance for hydrogen evolution. ACS Nano 11, 5103–5112 (2017). https://doi.org/10.1021/acsnano.7b02060
J. Xu, X. Li, W. Liu, Y. Sun, Z. Ju et al., Carbon dioxide electroreduction into syngas boosted by a partially delocalized charge in molybdenum sulfide selenide alloy monolayers. Angew. Chem. Int. Ed. 56, 9121–9125 (2017). https://doi.org/10.1002/anie.201704928
G. Shao, Y. Lu, J. Hong, X.-X. Xue, J. Huang et al., Seamlessly splicing metallic SnxMo1−xS2 at MoS2 edge for enhanced photoelectrocatalytic performance in microreactor. Adv. Sci. 7, 2002172 (2020). https://doi.org/10.1002/advs.202002172
F. Li, W. Wei, H. Wang, B. Huang, Y. Dai et al., Intrinsic electric field-induced properties in Janus MoSSe van der waals structures. J. Phys. Chem. Lett. 10, 559–565 (2019). https://doi.org/10.1021/acs.jpclett.8b03463
T. Zheng, Y.-C. Lin, Y. Yu, P. Valencia-Acuna, A.A. Puretzky et al., Excitonic dynamics in Janus MoSSe and WSSe monolayers. Nano Lett. 21, 931–937 (2021). https://doi.org/10.1021/acs.nanolett.0c03412
H. Cai, Y. Guo, H. Gao, W. Guo, Tribo-piezoelectricity in Janus transition metal dichalcogenide bilayers: a first-principles study. Nano Energy 56, 33–39 (2019). https://doi.org/10.1016/j.nanoen.2018.11.027
C. Zhang, Y. Nie, S. Sanvito, A. Du, First-principles prediction of a room-temperature ferromagnetic Janus VSSe monolayer with piezoelectricity, ferroelasticity, and large valley polarization. Nano Lett. 19, 1366–1370 (2019). https://doi.org/10.1021/acs.nanolett.8b05050
J. Liang, W. Wang, H. Du, A. Hallal, K. Garcia et al., Very large Dzyaloshinskii-Moriya interaction in two-dimensional Janus manganese dichalcogenides and its application to realize skyrmion states. Phys. Rev. B 101, 184401 (2020). https://doi.org/10.1103/physrevb.101.184401
A.C. Riis-Jensen, T. Deilmann, T. Olsen, K.S. Thygesen, Classifying the electronic and optical properties of Janus monolayers. ACS Nano 13, 13354–13364 (2019). https://doi.org/10.1021/acsnano.9b06698
S. Haastrup, M. Strange, M. Pandey, T. Deilmann, P.S. Schmidt et al., The computational 2D materials database: high-throughput modeling and discovery of atomically thin crystals. 2D Mater. 5, 042002 (2018). https://doi.org/10.1088/2053-1583/aacfc1
M.N. Gjerding, A. Taghizadeh, A. Rasmussen, S. Ali, F. Bertoldo et al., Recent progress of the computational 2D materials database (C2DB). 2D Mater. 8, 044002 (2021). https://doi.org/10.1088/2053-1583/ac1059
S. Zhang, X. Wang, Y. Wang, H. Zhang, B. Huang et al., Electronic properties of defective Janus MoSSe monolayer. J. Phys. Chem. Lett. 13, 4807–4814 (2022). https://doi.org/10.1021/acs.jpclett.2c01195
Y.-C. Lin, C. Liu, Y. Yu, E. Zarkadoula, M. Yoon et al., Low energy implantation into transition-metal dichalcogenide monolayers to form Janus structures. ACS Nano 14, 3896–3906 (2020). https://doi.org/10.1021/acsnano.9b10196
X. Wan, E. Chen, J. Yao, M. Gao, X. Miao et al., Synthesis and characterization of metallic Janus MoSH monolayer. ACS Nano 15, 20319–20331 (2021). https://doi.org/10.1021/acsnano.1c08531
C.-H. Yeh, Computational study of Janus transition metal dichalcogenide monolayers for acetone gas sensing. ACS Omega 5, 31398–31406 (2020). https://doi.org/10.1021/acsomega.0c04938
S. Jia, A. Bandyopadhyay, H. Kumar, J. Zhang, W. Wang et al., Biomolecular sensing by surface-enhanced Raman scattering of monolayer Janus transition metal dichalcogenide. Nanoscale 12, 10723–10729 (2020). https://doi.org/10.1039/D0NR00300J
W.-J. Yin, B. Wen, G.-Z. Nie, X.-L. Wei, L.-M. Liu, Tunable dipole and carrier mobility for a few layer Janus MoSSe structure. J. Mater. Chem. C 6, 1693–1700 (2018). https://doi.org/10.1039/C7TC05225A
M. Idrees, H.U. Din, R. Ali, G. Rehman, T. Hussain et al., Optoelectronic and solar cell applications of Janus monolayers and their van der Waals heterostructures. Phys. Chem. Chem. Phys. 21, 18612–18621 (2019). https://doi.org/10.1039/C9CP02648G
S. Susarla, A. Kutana, J.A. Hachtel, V. Kochat, A. Apte et al., Quaternary 2D transition metal dichalcogenides (TMDs) with tunable bandgap. Adv. Mater. 29, 1702457 (2017). https://doi.org/10.1002/adma.201702457
C.-Z. Ning, L. Dou, P. Yang, Bandgap engineering in semiconductor alloy nanomaterials with widely tunable compositions. Nat. Rev. Mater. 2, 17070 (2017). https://doi.org/10.1038/natrevmats.2017.70
I.S. Kwon, S.J. Lee, J.Y. Kim, I.H. Kwak, G.M. Zewdie et al., Composition-tuned (MoWV)Se2 ternary alloy nanosheets as excellent hydrogen evolution reaction electrocatalysts. ACS Nano 17, 2968–2979 (2023). https://doi.org/10.1021/acsnano.2c11528
T. Joseph, M. Ghorbani-Asl, A.G. Kvashnin, K.V. Larionov, Z.I. Popov et al., Nonstoichiometric phases of two-dimensional transition-metal dichalcogenides: from chalcogen vacancies to pure metal membranes. J. Phys. Chem. Lett. 10, 6492–6498 (2019). https://doi.org/10.1021/acs.jpclett.9b02529
Z. Wang, R. Li, C. Su, K.P. Loh, Intercalated phases of transition metal dichalcogenides. SmartMat 1, e1013 (2020). https://doi.org/10.1002/smm2.1013
B. An, Y. Ma, F. Chu, X. Li, Y. Wu et al., Growth of centimeter scale Nb1−xWxSe2 monolayer film by promoter assisted liquid phase chemical vapor deposition. Nano Res. 15, 2608–2615 (2022). https://doi.org/10.1007/s12274-021-3825-x
S. Park, S.J. Yun, Y.I. Kim, J.H. Kim, Y.M. Kim et al., Tailoring domain morphology in monolayer NbSe2 and WxNb1−xSe2 heterostructure. ACS Nano 14, 8784–8792 (2020). https://doi.org/10.1021/acsnano.0c03382
X. Li, F. Cui, Q. Feng, G. Wang, X. Xu et al., Controlled growth of large-area anisotropic ReS2 atomic layer and its photodetector application. Nanoscale 8, 18956–18962 (2016). https://doi.org/10.1039/C6NR07233J
F. Cui, X. Li, Q. Feng, J. Yin, L. Zhou et al., Epitaxial growth of large-area and highly crystalline anisotropic ReSe2 atomic layer. Nano Res. 10, 2732–2742 (2017). https://doi.org/10.1007/s12274-017-1477-7
G. Song, S. Cong, Z. Zhao, Defect engineering in semiconductor-based SERS. Chem. Sci. 13, 1210–1224 (2021). https://doi.org/10.1039/d1sc05940h
S.G. Yi, S.H. Kim, S. Park, D. Oh, H.Y. Choi et al., Mo1-xWxSe2-based Schottky junction photovoltaic cells. ACS Appl. Mater. Interfaces 8, 33811–33820 (2016). https://doi.org/10.1021/acsami.6b11768
K.C. Kwon, T.H. Lee, S. Choi, K.S. Choi, S.O. Gim et al., Synthesis of atomically thin alloyed molybdenum-tungsten disulfides thin films as hole transport layers in organic light-emitting diodes. Appl. Surf. Sci. 541, 148529 (2021). https://doi.org/10.1016/j.apsusc.2020.148529
R. Yang, L. Liu, S. Feng, Y. Liu, S. Li et al., One-step growth of spatially graded Mo1−xWxS2 monolayers with a wide span in composition (from x = 0 to 1) at a large scale. ACS Appl. Mater. Interfaces 11, 20979–20986 (2019). https://doi.org/10.1021/acsami.9b03608
Acknowledgements
This work was supported by National Key R&D Program of China (2021YFF1200200) and Peiyang Talents Project of Tianjin University.
Author information
Authors and Affiliations
Contributions
ZL helped in visualization, writing—original draft. SYT was involved in figure design, language editing. GG contributed to conceptualization, supervision, writing—review and editing. M-YH helped in project administration, supervision, writing—review and editing.
Corresponding authors
Ethics declarations
Conflict of interest
The authors declare no interest conflict. They have no known competing financial interests or personal relationships that could have appeared to influence the work reported in this paper.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Liu, Z., Tee, S.Y., Guan, G. et al. Atomically Substitutional Engineering of Transition Metal Dichalcogenide Layers for Enhancing Tailored Properties and Superior Applications. Nano-Micro Lett. 16, 95 (2024). https://doi.org/10.1007/s40820-023-01315-y
Received:
Accepted:
Published:
DOI: https://doi.org/10.1007/s40820-023-01315-y