Abstract
The recycling and recovery of precious metals from secondary materials, such as waste-printed circuit boards, are an important area of circular economy research due to the limited existing resources and increasing amount of e-waste produced by the rapid development of technology. In this study, the kinetic behavior of precious metals Au, Ag, Pt, and Pd between copper matte and iron-silicate slag was investigated at a typical flash smelting temperature of 1300 °C in both air and argon atmospheres. SEM–EDS, EPMA, and LA-ICP-MS-advanced analysis methods were used for sample characterization. The results indicate that precious metals favor the matte phase over slag, and the deportment to matte occurred swiftly within a short time after the system had reached the experimental temperature. With increasing contact times, the precious metals were distributed increasingly into the sulfide matte. The distribution coefficients, based on experimentally measured element concentrations, followed the order of palladium > platinum > gold > silver in both air and argon, and the matte acted as an efficient collector of these precious metals. The obtained results can be applied to industrial copper matte smelting processes, and they also help in upgrading CFD models to simulate the flash smelting process more precisely.
Graphical Abstract
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
Introduction
Due to technological advances and the improvement of economic and social conditions around the globe, the number of electronic devices in total and per capita is increasing. Meanwhile, the lifecycle of devices has become shorter as a result of rapid technology updates and increasing disposable income [1]. The United Nations University has estimated that, for example, in 2016, the global generation of WEEE (waste electrical and electronic equipment) was 44.7 million tons [2] and in 2018, 49.8 million tons [3], and it is expected to reach 52.2 million tons by 2021 [4]. WEEE consists of a wide range of materials, some of which have very high economic value. Due to the huge amounts produced every year, WEEE is considered as a valuable urban resource. Various methods, such as physical separation, electrostatic separation, pyrometallurgical, and hydrometallurgical processes have been investigated with the focus of recycling the valuable metals from these secondary resources [5, 6].
Reprocessing WEEE to recover the valuable metals is not a simple task. WEEE is a heterogeneous mixture of metallic and non-metallic fractions, where the components containing valuable metals are strongly bonded to other components that may have little or no value [7, 8]. Furthermore, common electronic devices may include lead, mercury, and arsenic, which are hazardous elements. Proper management of e-waste is, therefore, a must, as it can pollute ground water, acidify the soil, generate toxic fumes and gases in burning, accumulate in municipal disposal areas, and release carcinogenic substances [9].
Waste-printed circuit boards (WPCBs) are an important part of WEEE: they account for 2–3% of its total mass [4, 10]. WPCBs consist mostly of nonconductive insulator materials and several metals, such as copper and precious metals (PMs). The concentrations of PMs, specifically gold, silver, platinum, and palladium, in WPCBs can be considerably higher than in their primary sources [11]. Moreover, as primary precious metal resources are steadily depleting, the demand for these metals is growing in many sectors. Therefore, recycling of precious metals from WPCBs is of significant interest. The value of precious metals comprises 80% of the value of scrap electronic devices, despite their small quantities [12]. For these reasons, manufacturers, environmental agencies, and governments around the globe are attempting to find systematic and environmentally sustainable ways of recycling precious metals from WPCBs.
Pyrometallurgical processes are capable of dealing with complex e-waste streams [13,14,15,16]. WPCBs, in addition to their high precious metal content, also contain more than 20% copper [17]. Considering the economic and technical aspects, copper smelting is one of the predominant routes for WPCB and e-waste recycling [18]. Copper flash smelting is a mature technology that has been studied and employed by industry for decades [19,20,21], and the combustion reactions of chalcopyrite and other sulfides in it have also been widely investigated [22,23,24,25]. WPCBs can be processed along with the primary feed of copper concentrates. However, the elemental composition of WPCBs and other e-waste is often such that it can affect the processing conditions, for instance by changing the liquidus temperature or viscosity of the slag or by making the slag more corrosive towards refractories. Another issue related to WPCB smelting is that the mix of elements in WPCB does not match that in common primary mineral concentrates, for which the smelting technology has been optimized over many years and for which a large database of information has accumulated [7, 26,27,28].
To obtain the optimal process parameters for WPCB smelting and precious metals recovery, the thermodynamics and kinetic behavior of the valuable elements and their reaction mechanisms must be known. Equilibrium research regarding the precious metal distribution between matte and different slags has been intensively carried out during the past few decades. The investigated slag systems include, for example, FeOx–CaO [29], FeOx–SiO2 [30, 31], FeOx–SiO2–MgO [32], and SiO2–CaO–FeOx–MgO [33]. The distribution characteristics have also been studied as a function of matte grade with various sulfur and oxygen potentials [34,35,36]. However, studies on the kinetic behavior of precious metals in the matte-slag system are lacking [37], and more research is urgently needed to optimize the methods to recover precious metals from WPCBs through the copper smelting process.
The time dependency of precious metal (Au, Ag, Pt, and Pd) distribution was experimentally investigated in laboratory-scale copper matte smelting conditions. The results contribute to deeper understanding of PM distribution behavior during the settling process in the flash smelting furnace (FSF) and provide guidance in finding better strategies and methods for recovering the precious and platinum group metals from e-waste via pyrometallurgical routes.
Experimental
Materials
The raw materials used in this study were industrial chalcopyrite copper concentrate, synthetic iron oxide-silica slag, and PM (Ag, Au, Pt, Pd) powders. The concentrate was provided by Boliden Harjavalta, Finland. Its chemical composition was analyzed by X-ray fluorescence (XRF) spectrometry (Malvern Panalytical B.V., Almelo, The Netherlands) and is shown in Table 1.
The iron oxide-silica slag was prepared by mixing 65 wt% of hematite powder (Alfa Aesar, 99.99% purity) with 35 wt% of silica powder (Umicore, 99.99% purity). The preparation of the slag has been described in detail in a previous study [38]. Instead of real WPCB, pure Ag, Au, Pt, and Pd powders (Alfa Aesar, ≥ 99.9% purity) were used as sources of precious metals in the experiments.
Apparatus and Procedures
The experimental apparatus used in this study is shown in Fig. 1 and has been described in detail earlier [24]. The silica crucible, filled with sample material, was raised into the hot zone (temperature 1300 °C) with a Pt-hanging wire. After a preset time, the reactions were stopped by dropping the sample into a quenching vessel filled with ice water. For the experiments in an argon atmosphere, the work tube was sealed from the bottom, and a flow of 400–500 mL/min argon (AgA Linde, 99.999% purity) was used.
A slag to concentrate ratio of 1.116 was chosen in accordance with industrial operation practice [24]; this corresponds to a SiO2/Fe flux ratio of 0.53. Usually, the PM concentrations in real WPCBs are relatively low (varying from 80 to 3300 ppm) [39]. In this study, the amount of each metal (gold, silver, palladium, and platinum) was measured to be 2.5 wt% of the amount of concentrate (Table 2) considering the detection limitations of EPMA and LA-ICP-MS analyses [30, 34]. All the powders were ground together in a mortar to obtain a homogenous slag–concentrate-PM mixture. The mixture was then inserted into cone-shaped silica crucibles (Finnish Special Glass, Finland) with a mixture sample weight of 0.5236 g for each experiment, measured by an analytical balance (AB204, Mettler Toledo, USA).
The contact times were chosen to be 10, 20, 30, 60, 150, 300, and 600 s in air. For experiments in an argon atmosphere, 5, 10, 20, and 40 min were chosen. Each experiment was repeated at least twice, and a sufficient number of phase areas was analyzed in every polished section of the samples in order to ensure the reproducibility and reliability of the results.
Analyses
The samples were prepared with basic metallographic methods and first analyzed with a Mira 3 scanning electron microscope (SEM, Tescan, Brno, Czech Republic) equipped with an UltraDry silicon drift energy dispersive X-ray spectrometer (EDS, Thermo Fisher Scientific, Waltham, MA, USA) coupled to NSS microanalysis software (Thermo Fisher Scientific, Waltham, MA, USA). Considering the insufficient detection limits of EDS [40, 41] and PM concentration results from a previous equilibrium study, the chemical compositions of the matte phase were investigated by electron probe micro-analysis (EPMA) and the slag phase was analyzed by laser ablation-inductively coupled plasma-mass spectrometry (LA-ICP-MS). LA-ICP-MS was essential for the slag phase due to its very low PM concentrations.
The EPMA used in this work for matte phase analysis was a Cameca SX100 equipped with five wavelength dispersive spectrometers (Cameca SAS, Gennevilliers, France). The selected accelerating voltage was 20 kV, beam current 60 nA, and beam diameter 100 µm. The analyzed lines and standards (Astimex) used were as follows: Fe Kα and O Kα (hematite), Mg Kα (diopside), S Kα (pentlandite), Cu Kα (Cu), Zn Kα (sphalerite), Pb Lα (galena), Pd Lα (Pd), Ag Lα (Ag), Pt Lα (Pt), and Au Lα (Au).
The equipment used for slag trace element analysis was a Photon Machines Analyte Excite laser ablation system with a 193 nm wavelength 4 ns ArF excimer laser (Teledyne CETAC Technologies, Omaha, USA) coupled to an Nu AttoM single collector sector field ICP-MS (Nu Instruments Ltd., Wrexham, UK). The laser spot size was selected as 65 µm for the air-atmosphere experiments, and 40 µm for the argon-atmosphere samples, due to the limited size of slag areas available. The obtained detection limits of EPMA and LA-ICP-MS are shown in Table 3, and more detailed information about the technique adopted in our study can be found in the references [34, 40, 42,43,44].
Results and Discussion
Smelting Process and Sample Microstructures
In this study, copper concentrate, iron oxide–silica slag, and PMs (Au, Ag, Pt, and Pd) were pre-mixed and reacted at a typical copper smelting temperature of 1300 °C in both air and argon atmospheres. The purpose of the air-atmosphere experiments was to simulate the reaction shaft processes of the flash smelting furnace, while the argon atmosphere was used for simulating the reactions between matte and slag in low oxygen partial pressure (typically around 10−8 to 10−7 atm) on the slag–metal interface in the settler [45].
The SEM-backscattered electron micrographs of samples after different contact times in air are shown in Fig. 2. The reactions proceeded quickly, as the matte (A) and fayalite FeOx–SiO2 slag (B) phases already began to form after 10 s, which is consistent with the rapid reaction phenomena occurring in the flash smelting process [46]. The structure of the sample was first extremely heterogeneous and the interfaces between the matte and slag phases were not clear. Unreacted ferric oxide (D) was also detected. After 20 s, the fayalite slag areas had increased in size and started to segregate more clearly from the sulfide matte. The matte was rather randomly distributed, which showed that coalescence and settling had not taken place at this point. After 30 s of contact time, most of the remaining un-melted silica (C) had reacted and dissolved into the slag, and a clear interface between matte and slag was formed. With increasing contact time, phase coalescence and matte settling progressed further. Some areas were detected in the form of a PMs-Cu-Fe droplet clusters (E), and after 30 s, these droplets were found only in the matte phase. From the micrographs in Fig. 2e–f, platinum metal preferred to form these metallic droplets with copper and iron enclosed within the matte phase, while gold, silver, and palladium dispersed more evenly into the matte phase. However, a few Au-, Ag-, and Pd-containing clusters were also detected in the matte phase. In the sample at 150 s, a larger high-platinum content area was found. At 300 s, a large droplet with a platinum core surrounded by a shell formed of copper, iron, and small amounts of PMs was observed in the sample. However, these larger PM clusters and droplets were avoided in the EPMA analyses, which was used to detect the average concentrations of PMs in the matte.
Figure 3 shows the SEM micrographs of samples after different contact times in an argon atmosphere. As shown in Fig. 3a, the matte (A) and fayalite slag (B) phases had already formed and separated from each other after 5 min. PM-rich clusters (D) were detected with all contact times, and they were randomly distributed in the matte domains. Figure 3b–d illustrates the small change in the structure of the samples with increasing contact time from 10 to 40 min. At 40 min of contact time (Fig. 3d), the PM-rich clusters had coalesced into larger droplets and were specifically found near the slag–matte interfaces. As is to be expected with longer contact times, the PMs have more time to migrate and coalesce to form bigger droplets within the matte.
Behavior of Major Elements in Matte and Slag Phases
The concentrations of major elements in the matte (Cu–Fe–S) and slag (FeOx–SiO2) are shown in Figs. 4 (air atmosphere) and 5 (argon atmosphere) as a function of contact time. In air, the matte grade (wt% Cu) increased continuously, seen also as a decrease in its iron concentration. The sulfur concentration remained relatively stable with a minor decreasing trend as a function of increasing contact time. After 300 s, the reaction rate decreased, and the matte grade reached a value of approximately 50 wt% Cu at 600 s. In the slag phase shown in Fig. 4b, the silica concentration kept increasing until 60 s, after which the slag composition remained constant. Corresponding to the microstructures shown in Fig. 2, during the first 60 s, the primary silica crystals reacted and dissolved into the slag, and more silica was also dissolved from the crucible.
In the argon atmosphere, the concentrations of major elements in matte and slag phases remained relatively constant throughout the time series. The matte grade stabilized at a considerably lower level than in air, due to the absence of free oxygen. The slag composition was almost the same as that in air. These results were similar to the results of previous experiments conducted in the same conditions but with different trace elements [40].
Behavior of Precious Metals in Matte and Slag Phases
The concentrations of the PMs Au, Ag, Pt, and Pd in matte as a function of time are shown in Fig. 6. In air atmosphere (Fig. 6a), the Au, Ag, and Pd concentrations in matte consistently increased with longer contact times. The platinum concentration began to decrease after 150 s, which can be explained by the formation of large platinum-rich droplets in the matte, shown in Fig. 3e–f. In the argon atmosphere (Fig. 6b), the PM concentrations remained relatively constant as a function of time. After the longest contact times, all the PM concentrations in matte were lower in argon than in air. The sequence of concentration levels in both atmospheres was Ag > Pd > Au > Pt.
The concentrations of the PMs Au, Ag, Pt, and Pd in slag as a function of time are shown in Fig. 7. The slag chemistry plays an important role in the elimination of impurity elements and recovery of precious metals in copper smelting. In the FeOX–SiO2 slag used in this study, all precious metal concentrations initially decreased as a function of time and then stabilized at a constant level. The sequence of PM concentrations in the slag was Ag > Au > Pd > Pt in both air (Fig. 7a) and argon (Fig. 7b) atmospheres. However, the PM concentrations were higher in air than in the argon atmosphere after reaching stable concentration levels.
The distribution reaction for precious metal Me between matte and slag can be described using Eq. (1), when metals are deported into the slag phase due to the oxidation reaction:
Equation (1) can be presented using an equilibrium constant that consists of the activities of the species and the prevailing oxygen partial pressure, shown in Eq. (2). The activities can be expressed with the concentration of the species and its activity coefficient, as in Eqs. (3) and (4).
where K is the equilibrium constant, and αMe and αMeOx represent the activities of metal Me and metal oxide MeOx, respectively. γMe is the activity coefficient of Me and γMeO is the activity coefficient of MeOx. NMe is the molar fraction of metal Me, nT is the total number of moles of monocationic constituents in 100 g of each phase, Mme is the atomic mass of Me, and wt% Me is the weight percentage in matte and slag.
In the equilibrium studies, the distribution coefficient of a PM Me between copper matte and slag is defined by Eq. (5), where [Me wt%] refers to the equilibrium concentration of Me in copper matte and (Me wt %) is the equilibrium concentration in slag in weight percentage [30].
Combining Eqs. (1)–(4), Eq. (5) can be expressed as follows:
As shown by Eq. (6), the distribution coefficient is a practical and independent thermodynamic parameter of the matte–slag system (only influenced by the temperature, oxygen potential, etc.), so the concentrations of the initial precious metals will not influence the distribution results. Even though these noble metal concentrations in this study are higher than those in real WPCBs, the distribution ratios between the matte and slag should be thermodynamically independent. In that case, the distribution coefficients between matte and slag are essential parameters for evaluating the recycling efficiencies of the PMs during copper smelting, by utilizing copper matte as a medium for their collection. In this kinetic study, the distribution coefficients values of PMs were determined at selected times by Eq. (7), where t refers to the contact time after which the sample was quenched and the reactions stopped [45].
The logarithmic values of distribution coefficients Lm/s (Me) between matte and slag during the oxidation reactions in air are shown in Fig. 8. All PMs were found to deport strongly into the matte rather than into the slag, and with the increased contact time, their distribution coefficients followed a similar increasing tendency until 300 s, after which the values stabilized in the order of Pd > Pt > Au > Ag. At 20 s contact time, the average distribution coefficient values for Au, Ag, Pt, and Pd were 80, 70, 230, and 200, respectively, and at 300 s, these values surged to 600, 100, 1300, and 1200. During this time period, the matte grade also gradually increased. This also helped improve PM migration into the matte phase [36]. Tags a, b, c on the x-axis of Fig. 8 refer to the PM distribution results from equilibration studies between matte and iron-silicate slag where the temperature and matte grade were closest to the parameters in this work (a—Avarmaa et al. [30]; b—Chen et al. [34]; c—Shishin et al. [36]). The equilibration time in their studies was 3 h, 4 h, and 24 h, respectively. After 300–600 s, the distribution coefficients of the PMs obtained in this work agreed well with these recent equilibrium studies. Therefore, it seems that the equilibrium distribution coefficient values for PMs can be reached even in relatively short contact times.
The distribution coefficients of PMs in argon are shown in Fig. 9. The values are lower than those in air, but they still follow the same order of Pd > Pt > Au > Ag. As shown in Fig. 5a, the matte grade (wt% Cu) was relatively constant in the argon atmosphere; however, the distribution coefficients continued to increase as a function of time. This means that sufficient time is needed for the PMs to migrate to the matte phase in low oxygen partial pressures. In air, the obtained distribution coefficients stabilized after 300 s, while the values in argon continued to increase slightly until the longest investigated contact time of 40 min. The average distribution coefficients values after 40 min for Au, Ag, Pt, and Pd were approximately 200, 90, 710, and 750, respectively, i.e., somewhat lower than the corresponding results in air.
Conclusions
No previous data exist on the kinetic behavior of precious metals (PMs) in copper flash smelting conditions. In this study, the behavior of Au, Ag, Pt, and Pd was investigated in laboratory-scale experiments at a typical smelting temperature of 1300 °C in both air and argon atmospheres. The samples were analyzed by SEM–EDS for visual and preliminary compositional information, and by EPMA (matte) and LA-ICP-MS (slag) for more accurate phase composition data.
All the PMs studied in this work strongly preferred to deport into the matte rather than the slag phase. The novelty of the present research is the experimental proof that the studied PMs migrate to the matte phase almost instantly when the molten matte and slag begin to form. The PMs approached their reported equilibrium distribution coefficients after only 300 s contact time in the air atmosphere. However, it should be noted that the experimental conditions, mainly the gas atmospheres, in the earlier equilibrium studies did not fully correspond to those utilized in this work, and industrial copper concentrate was used in this study. In the argon atmosphere, the distribution coefficient values slightly increased during the entire contact time of 40 min. The calculated distribution coefficients Lm/s (Me), based on experimentally measured element concentrations, followed the order of Pd > Pt > Au > Ag in both air and argon atmospheres.
The distribution coefficients of PMs in air were higher than the results in argon, and PM concentrations in matte increased with longer contact time and higher matte grade. The oxygen potential had an impact on the PM migration rates and distribution coefficients. Based on the results in argon, considerably longer times are needed for the complete transfer of PMs to the matte at low oxygen potentials.
After reaching stable levels, the PM concentrations in the slag were relatively low, at approximately 408 ppm (Ag), 27 ppm (Au), 17 ppm (Pd), and 9 ppm (Pt) in air, and 346 ppm (Ag), 42 ppm (Au), 24 ppm (Pd), and 3 ppm (Pt) in argon. These low concentrations of chemically dissolved PMs in the slag indicated that copper matte can perform as an excellent collector to recover precious metals. This suggests that the highest PM losses in industrial operations most likely arise from mechanical matte entrainment.
These new experimental results regarding the effect of time on PM distribution behavior can be used for updating databases related to secondary raw materials processing via copper smelting and also for CFD models to simulate the behavior of precious metals in smelting processes more precisely.
References
Cayumil R, Khanna R, Rajarao R, Mukherjee P, Sahajwalla V (2016) Concentration of precious metals during their recovery from electronic waste. Waste Manag 57:121–130. https://doi.org/10.1016/j.wasman.2015.12.004
Baldé C, Forti V, Gray V, Kuehr R, Stegmann P (2017) The global E-waste monitor–2017, United Nations University (UNU), International Telecommunication Union (ITU) & International Solid Waste Association (ISWA), Bonn/Geneva/Vienna. Electronic Version. 978-992
Vegliò F, Birloaga I (eds) (2018) Waste electrical and electronic equipment recycling: aqueous recovery methods. 1st edition. Woodhead Publishing, United Kingdom. eBook ISBN: 9780081020586
Ilankoon I, Ghorbani Y, Chong MN, Herath G, Moyo T, Petersen J (2018) E-waste in the international context–A review of trade flows, regulations, hazards, waste management strategies and technologies for value recovery. Waste Manag 82:258–275. https://doi.org/10.1016/j.wasman.2018.10.018
Chagnes A, Cote G, Ekberg C, Nilsson M, Retegan T (2016) WEEE recycling: research, development, and policies. 1st edition. Elsevier. eBook ISBN: 9780128033647
Wan X, Taskinen P, Shi J, Jokilaakso A (2021) A potential industrial waste–waste co-treatment process of utilizing waste SO2 gas and residue heat to recover Co, Ni, and Cu from copper smelting slag. J Hazard Mater 414:125541. https://doi.org/10.1016/j.jhazmat.2021.125541
Anindya A (2012) Minor elements distribution during the smelting of WEEE with copper scrap. Doctoral thesis, RMIT university, Melbourne, Australia
Anindya A, Swinbourne D, Reuter M, Matusewicz R (2013) Distribution of elements between copper and FeOx–CaO–SiO2 slags during pyrometallurgical processing of WEEE: Part 1–Tin. Miner Process Extr Metall 122(3):165–173. https://doi.org/10.1179/1743285513Y.0000000043
Kaya M (2016) Recovery of metals and nonmetals from electronic waste by physical and chemical recycling processes. Waste Manag 57:64–90. https://doi.org/10.1016/j.wasman.2016.08.004
Hughes S, Jåfs M, Johto H, Stål J, Karonen J (2019) Outotec solutions for E-scrap processing, REWAS 2019. Springer, Berlin, pp 283–294. https://doi.org/10.1007/978-3-030-10386-6
Puca A, Carrano M, Liu G, Musella D, Ripa M, Viglia S, Ulgiati S (2017) Energy and exergy assessment of the production and operation of a personal computer. Resour Conserv Recycl 116:124–136. https://doi.org/10.1016/j.resconrec.2016.09.030
Chancerel P, Meskers CE, Hagelüken C, Rotter VS (2009) Assessment of precious metal flows during preprocessing of waste electrical and electronic equipment. J Ind Ecol 13(5):791–810. https://doi.org/10.1111/j.1530-9290.2009.00171.x
Cui J, Zhang L (2008) Metallurgical recovery of metals from electronic waste: a review. J Hazard Mater 158(2–3):228–256. https://doi.org/10.1016/j.jhazmat.2008.02.001
Ebin B, Isik MI (2016) Pyrometallurgical processes for the recovery of metals from WEEE. In: WEEE recycling. Elsevier, pp. 107–137. https://doi.org/10.1016/B978-0-12-803363-0.00005-5
Wang H, Zhang S, Li B, Pan DA, Wu Y, Zuo T (2017) Recovery of waste printed circuit boards through pyrometallurgical processing: a review. Resour Conserv Recycl 126:209–218. https://doi.org/10.1016/j.resconrec.2017.08.001
He W, Li G, Ma X, Wang H, Huang J, Xu M, Huang C (2006) WEEE recovery strategies and the WEEE treatment status in China. J Hazard Mater 136(3):502–512
Sum EY (1991) The recovery of metals from electronic scrap. JOM 43(4):53–61. https://doi.org/10.1007/BF03220549
Khaliq A, Rhamdhani MA, Brooks G, Masood S (2014) Metal extraction processes for electronic waste and existing industrial routes: a review and Australian perspective. Resource 3(1):152–179. https://doi.org/10.3390/resources3010152
Kojo IV, Jokilaakso A, Hanniala P (2000) Flash smelting and converting furnaces: a 50 year retrospect. JOM 52(2):57–61. https://doi.org/10.1007/s11837-000-0049-5
Taskinen P, Seppälä K, Laulumaa J, Poijärvi J (2001) Oxygen pressure in the Outokumpu flash smelting furnace—Part 1: copper flash smelting settler. Miner Process Extr Metall 110(2):94–100. https://doi.org/10.1179/mpm.2001.110.2.94
Taskinen P, Seppälä K, Laulumaa J, Poijärvi J (2001) Oxygen pressure in the Outokumpu flash smelting furnace—Part 2: the DON process. Miner Process Extr Metall 110(2):101–108. https://doi.org/10.1179/mpm.2001.110.2.101
Jorgensen FR (1983) Single-particle combustion of chalcopyrite. Proc Austral Inst Min Metall 288:37–46
Jokilaakso A, Suominen R, Taskinen P, Lilius K (1991) Oxidation of chalcopyrite in simulated suspension smelting. Trans Inst Min Metall (Sect C: Miner Process Extr Metall) 100:C79–C90
Wan X, Shen L, Jokilaakso A, Eriç H, Taskinen P (2020) Experimental approach to matte–slag reactions in the Flash Smelting Process. Miner Process Extr Metall Rev 42:231–241. https://doi.org/10.1080/08827508.2020.1737801
Guntoro PI, Jokilaakso A, Hellstén N, Taskinen P (2018) Copper matte-slag reaction sequences and separation processes in matte smelting. J Min Metall Sect B 54(3):301–311. https://doi.org/10.2298/jmmb180214021g
Ma E (2019) Recovery of waste printed circuit boards through pyrometallurgy. Electron Waste Manag Technol Treat Technol. https://doi.org/10.1016/B978-0-12-816190-6.00011-X
Sukhomlinov D, Avarmaa K, Virtanen O, Taskinen P, Jokilaakso A (2019) Slag–copper equilibria of selected trace elements in black copper smelting. Part I. Properties of the slag and chromium solubility. Miner Process Extr Metall Rev. https://doi.org/10.1080/08827508.2019.1575212
Sukhomlinov D, Avarmaa K, Virtanen O, Taskinen P, Jokilaakso A (2020) Slag-copper equilibria of selected trace elements in black-copper smelting. Part II. Trace element distributions. Miner Process Extr Metall Rev 41(3):171–177. https://doi.org/10.1080/08827508.2019.1634561
Roghani G, Font JC, Hino M, Itagaki K (1996) Distribution of minor elements between calcium ferrite slag and copper matte at 1523 K under high partial pressure of SO2. Mater Trans, JIM 37(10):1574–1579. https://doi.org/10.2320/matertrans1989.37.1574
Avarmaa K, O’Brien H, Johto H, Taskinen P (2015) Equilibrium distribution of precious metals between slag and copper matte at 1250–1350 & #xB0;C. J Sustain Metall 1(3):216–228. https://doi.org/10.1007/s11663-015-0498-4
Avarmaa K, Johto H, Taskinen P (2016) Distribution of precious metals (Ag, Au, Pd, Pt, and Rh) between copper matte and iron silicate slag. Metall Mater Trans B 47(1):244–255. https://doi.org/10.1007/s11663-015-0498-4
Roghani G, Takeda Y, Itagaki K (2000) Phase equilibrium and minor element distribution between FeOx-SiO2-MgO-based slag and Cu2S-FeS matte at 1573 K under high partial pressures of SO2. Min Metall Sect B. 31(4):705–712
Roghani G, Hino M, Itagaki K (1997) Phase equilibrium and minor elements distribution between SiO2–CaO–FeOx–MgO slag and copper matte at 1573 K under high partial pressures of SO2. Mater Trans, JIM 38(8):707–713. https://doi.org/10.2320/matertrans1989.38.707
Chen M, Avarmaa K, Klemettinen L, O’Brien H, Sukhomlinov D, Shi J, Taskinen P, Jokilaakso A (2020) Recovery of precious metals (Au, Ag, Pt, and Pd) from urban mining through copper smelting. Metall Mater Trans B 51:1495–1508. https://doi.org/10.1007/s11663-020-01861-5
Chen M, Avarmaa K, Klemettinen L, Shi J, Taskinen P, Jokilaakso A (2020) Experimental study on the phase equilibrium of copper matte and silica-saturated FeOx-SiO2-based slags in pyrometallurgical. WEEE Process Metall Mater Trans B 51:1552–1563. https://doi.org/10.1007/s11663-020-01874-0
Shishin D, Hidayat T, Chen J, Hayes PC, Jak E (2019) Experimental investigation and thermodynamic modeling of the distributions of Ag and Au between slag, matte, and metal in the Cu–Fe–O–S–Si system. J Sustain Metall 5(2):240–249. https://doi.org/10.1007/s40831-019-00218-w
Wan X, Fellman J, Jokilaakso A, Klemettinen L, Marjakoski M (2018) Behavior of waste printed circuit board (WPCB) materials in the copper matte smelting process. Metals 8(11):887. https://doi.org/10.3390/met8110887
Wan X, Jokilaakso A, Iduozee I, Eric H, Latostenmaa P (2019) Experimental research on the behavior of WEEE scrap in flash smelting settler with copper concentrate and synthetic slag. In: Proceedings of the EMC 2019, Düsseldorf, Germany, 23–26 June 2019, vol 3, pp 1137–1150. IASN 978-3-940276-89-6
Wu Z, Yuan W, Li J, Wang X, Liu L, Wang J (2017) A critical review on the recycling of copper and precious metals from waste printed circuit boards using hydrometallurgy. Front Environ Sci Eng 11(5):8. https://doi.org/10.1007/s11783-017-0995-6
Klemettinen L, Aromaa R, Dańczak A, O’Brien H, Taskinen P, Jokilaakso A (2020) Distribution kinetics of rare earth elements in copper smelting. Sustainability 12(1):208. https://doi.org/10.3390/su12010208
Wan X, Chen M, Qiu Y, Shi J, Li J, Liu C, Taskinen P, Jokilaakso A (2020) Influence of manganese oxide on the liquid-perovskite equilibrium in the CaO–SiO2–TiO2 system at 1400°C in air. Ceram Int. https://doi.org/10.1016/j.ceramint.2020.12.241
Klemettinen L, Taskinen P, O’Brien H, Jokilaakso A (2019) Equilibrium studies: experimental techniques and characterization methods at Aalto University, Finland. In Proceedings of international multidisciplinary geosciences conference—IMGC2019, University of Mitrovica, Republic of Kosovo, pp 93–103
Avarmaa K (2019) Thermodynamic properties of WEEE-based minor elements in copper smelting processes. PhD diss., Aalto University, Finland
Chen M, Avarmaa K, Klemettinen L, O’Brien H, Shi J, Taskinen P, Lindberg D, Jokilaakso A (2021) Precious metal distributions between copper matte and slag at high PSO2 in WEEE reprocessing. Metall Mater Trans B 52:871–882. https://doi.org/10.1007/s11663-021-02059-z
Wan X, Taskinen P, Shi J, Klemettinen L, Jokilaakso A (2021) Reaction mechanisms of waste printed circuit board recycling in copper smelting: the impurity elements. Miner Eng 160:106709. https://doi.org/10.1016/j.mineng.2020.106709
Asaki Z (1992) Kinetic studies of copper flash smelting furnace and improvements of its operation in the smelters in Japan. Miner Process Extr Metall Rev 11(3):163–185. https://doi.org/10.1080/08827509208914210
Acknowledgements
This work was financially supported by the Aalto University School of Chemical Engineering and the Business Finland financed SYMMET project [Grant number 3891/31/2018]. Thanks to Outotec Research Center (Pori, Finland) for their contribution. This study utilized the Academy of Finland’s RawMatTERS Finland Infrastructure (RAMI) based jointly at Aalto University, GTK, and VTT in Espoo. Xingbang Wan would also like to acknowledge the financial support from the China Scholarship Council [Grant Number 201706370096].
Funding
Open access funding provided by Aalto University.
Author information
Authors and Affiliations
Corresponding author
Ethics declarations
Conflict of interest
The authors report no conflicts of interest and the authors alone are responsible for the content and writing of the article.
Additional information
The contributing editor for this article was Yongxiang Yang.
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Wan, X., Kleemola, L., Klemettinen, L. et al. On the Kinetic Behavior of Recycling Precious Metals (Au, Ag, Pt, and Pd) Through Copper Smelting Process. J. Sustain. Metall. 7, 920–931 (2021). https://doi.org/10.1007/s40831-021-00388-6
Received:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s40831-021-00388-6