Abstract
Environmental concerns such as climate change due to rapid population growth are becoming increasingly serious and require amelioration. One solution is to create large capacity batteries that can be applied in electricity-based applications to lessen dependence on petroleum. Here, aluminum–air batteries are considered to be promising for next-generation energy storage applications due to a high theoretical energy density of 8.1 kWh kg−1 that is significantly larger than that of the current lithium-ion batteries. Based on this, this review will present the fundamentals and challenges involved in the fabrication of aluminum–air batteries in terms of individual components, including aluminum anodes, electrolytes and air cathodes. In addition, this review will discuss the possibility of creating rechargeable aluminum–air batteries.
Graphic Abstract
Similar content being viewed by others
Avoid common mistakes on your manuscript.
1 Introduction
Climate change has become an acute environmental problem, and one of the main causes is the tremendous amounts of CO2 gas emitted due to the explosion of human population and activity. One method to combat climate change is to suppress the consumption of petroleum as an energy and material resource through the development of renewable and sustainable energy sources for electric vehicles (EVs) and electrical energy storage systems. In terms of EVs, vital factors to assess market potential are the driving range as well as the vehicle price. Based on this, the development of low-cost batteries with high energy potential is a dominant research topic. Currently, the lithium-ion battery (LIB) is considered to be the most advanced and practical technology to be developed from small- to large-scale secondary batteries. However, the cost of LIBs is dependent on the cost of raw materials, including cathode and anode active materials, separators and electrolytes. In addition, the widespread adoption of LIBs in EVs is hindered by drawbacks such as safety concerns, limited driving ranges, slow charging times and heavy battery packs [1]. Moreover, the energy density of LIB cathodes ranges from ~ 140 to 350 mAh g−1 for oxide cathodes and 370 to over 2000 mAh g−1 for anodes depending on the material (i.e., graphite and silicon), leading to LIB cell capacities ranging from ~ 100 to 250 Wh kg−1, which are insufficient to meet the high energy and power density demands of modern EVs [2]. And although tremendous efforts have been undertaken to improve LIBs to provide greater energy capacity [3, 4], alternative strategies have also been proposed involving the creation of novel rechargeable batteries with sufficient theoretical energy densities for future applications [5]. Here, metal–air batteries have been intensively investigated over the last decade because of their high energy density and capacity as well as their relatively low costs in which the theoretical energy density of metal–air batteries can be 2- to 40-fold greater than that of LIBs. And of these different types of metal–air batteries, Li, Na, K, Zn, Mg, Fe, Si and Al air batteries have all been studied [6, 7] with each metal possessing advantages and drawbacks for use as anode electrodes. (Table 1 presents the voltage, theoretical specific capacity and energy density of typical metal–air batteries.) In general, metal–air batteries are composed of a metal anode, an air cathode and an appropriate electrolyte and possess high theoretical energy due to an open configuration in which oxygen can be directly absorbed from surrounding air. And among different types of metal–air batteries, Li–air batteries possess the highest theoretical energy density (11140 Wh kg−1) [8]. However, rechargeable Li–air batteries are difficult to obtain because of issues such as the blocking of air cathodes by discharge products as well as the instability of Li in humid environments that necessitates hermetical sealing in which Li metal is easily oxidized under ambient atmosphere. Alternatively, Al, Mg (2.20 Ah g−1) and Zn (0.82 Ah g−1) are all economically and environmentally friendly, abundant and relatively safe metals and in particular, Al is able to be recycled in large quantities in the modern world [9,10,11]. In addition, Al–air batteries possess a high theoretical voltage (2.7 V) and an energy density (8.1 kWh kg−1) that are second only to Li of the various metal–air batteries and are large enough to be considered for next-generation rechargeable batteries. The basic structure of primary Al–air batteries is composed of an Al anode, an air cathode and an appropriate electrolyte and in general; the electrolytes used for primary Al–air batteries are aqueous solutions of sodium hydroxide (NaOH), potassium hydroxide (KOH) or sodium chloride (NaCl) [12] in which electrochemical reactions in alkaline electrolytes at the electrodes can be expressed as follows [13]:
As for neutral pH electrolytes such as sodium chloride, the reaction of Al is not completely clear due to mixed species on the Al surface, which can combine metallic Al–Al2O3–Al(OH)3–H5AlO4, and other chlorinated complex species. And by taking the latter into account, the most extended and accepted reaction is described as follows [14]:
Al–air batteries were first proposed by Zaromb et al. [15, 16] in 1962. Following this, efforts have been undertaken to apply them to a variety of energy storage systems, including EV power sources, unmanned aerial (and underwater) vehicle applications and military communications [17,18,19,20]. And in 2016, researchers demonstrated that an EV can drive over 3000 km with the use of an Al–air battery that weighed ~ 100 kg. Despite this, Al–air batteries still possess many challenges prior to practical application, such as the accumulation of byproducts [Al(OH)3 and Al2O3] that can suppress Al–air battery electrochemical reactions. Based on all of this, this review will discuss the challenges associated with Al–air battery components including electrolytes, anodes and air cathodes to create better Al–air batteries. In addition, the possibility of rechargeable Al–air battery technologies will also be presented.
2 Electrolytes
The electrolyte is a main component of Al–air batteries, and the following section will present both aqueous and non-aqueous electrolytes used in these systems as well as additives that can influence battery properties. As for ionic liquid and deep eutectic solvent-based electrolytes for Al–air batteries, they are discussed in detail in the rechargeable Al–air battery section of this review.
2.1 Aqueous Electrolytes
Water-based aqueous electrolytes can be classified depending on their pH values as acidic (pH 2–7), neutral (pH 7) and alkaline (pH 7–13). Alkaline solutions such as potassium hydroxide (KOH) and sodium hydroxide (NaOH) solutions are the most common electrolytes developed for use in Al–air batteries, and KOH-based electrolytes are more preferable than NaOH because of their higher ionic conductivity, lower viscosity, higher oxygen diffusion coefficient and faster reaction kinetics [21] in which an Al–air battery using combination of the KOH alkaline electrolyte and the silver manganate nanoplate air cathode has recently been reported to be able to provide large specific cell capacities [22]. NaCl, a salt water electrolyte, has also been intensively studied for use as an Al–air battery electrolyte because of its abundance and safety in which if used, can provide a battery potential in the range of ~ 0.65–1.1 V for pure Al anodes. Previous studies have also noted the effects of NaCl concentration and battery operating temperature on the redox potential of Al anodes [23]. However, researchers have also reported that NaOH and KOH aqueous solutions can produce higher redox potentials in conjunction with Al anodes, which is one advantage of using alkaline solutions instead of salt water solutions (NaCl) [24]. Furthermore, researchers have demonstrated that dendrite formation on anodes and byproduct formation on cathodes can be suppressed through the use of acidic electrolytes such as hydrochloride acid and sulfuric acid [25]. Unfortunately, the use of acidic solutions can also result in corrosion issues for Al–air batteries.
2.2 Electrolyte Additives
Aqueous electrolytes face critical issues involving dendrite formation, electrode corrosion and hydrogen gas evolution. To address these issues, corrosion and hydrogen gas inhibitors can be used in which the basic mechanism of corrosion inhibitors is the adsorption of inhibitor molecules onto Al anode surfaces to suppress corrosion reactions. Based on this, various electrolyte additives have been actively studied. Here, Zn2+, Sn3+ and In3+ ions have been studied as additives for neutral salt water solutions [26,27,28], whereas polyethylene glycol and ZnO have been used as additives for alkaline conditions [29]. For example, Wang et al. [29] demonstrated that the corrosion rate of Al anodes can be suppressed by mixing polyethylene glycol and ZnO additives with KOH aqueous electrolytes and Liu et al. [30] reported that the addition of CMC (carboxymethyl cellulose) and ZnO can also suppress the corrosion rate of Al anodes in which the self-corrosion of Al anodes in a NaOH alkaline electrolyte solution can be delayed. Here, these researchers suggested that the carboxyl group of the CMC can bind to anode surfaces strongly and interact with Zn2+ ions to allow for the formation of a complex film on the anode surface, thus stabilizing it (Fig. 1). Researchers have further reported that some inorganic additives can effectively prevent Al anode corrosion, although other studies have shown that inorganic chemicals such as chromates, vanadates, borates and hexafluoride silicates do not have significant inhibitory effects [31]. Moreover, organic additives can also effectively prevent Al anode corrosion [24, 32]. For example, Zhang et al. [33] tested three dicarboxylic acids including succinic acid, adipic acid and sebacic acid as additives for alkaline electrolytes and found that these three acids lessened hydrogen evolution and confirmed that adipic acid is the most effective anode corrosion inhibitor. Researchers have also reported that some aromatic carboxylic acids can also be effective in the suppression of Al corrosion in alkaline solutions through the adsorption of carboxylic groups onto Al surfaces and that similar effects can be observed in other metals under acidic conditions [34]. Furthermore, Mahmoud et al. [32] reported the influence of imidazole derivatives on the inhibition of Al corrosion in a 0.5 M HCl solution and suggested that the N atoms of the imidazole group can bind to Al surfaces to suppress corrosion. Interestingly, Wang et al. [35] suggested that amino acid and rare-earth metal complexes such as l-cysteine and cerium nitrate can also suppress Al anode corrosion and hydrogen gas evolution by forming a complex film on anode surfaces in a 4 M NaOH alkaline solution and Wang et al. [36] applied a KOH solution in water with methanol as an electrolyte for comparison and found that the methanolic KOH solution delayed anode corrosion and that corrosion rates increased as the solution water content increased. Kang et al. [37] also reported that calcium oxide and l-aspartic can suppress the corrosion of Al anodes in NaOH alkaline media. Overall, all of these results suggest that various types of Al corrosion and hydrogen gas evolution inhibitors exist and can have practical use. More recently, Hopkins et al. [38] also created a new Al–air battery system using non-conducting oil instead of a liquid electrolyte during battery standby and reported significant Al anode corrosion suppression effects (Fig. 2).
2.3 Solid Electrolyte
Solid-state Al–air batteries are ideal because of their robustness, thermal stability and possible prevention of electrolyte leakage. Based on this, polymer-based electrolytes have been reviewed for their use in Al–air batteries [39, 40]. For example, Tan et al. [41] investigated acrylamide-based polymer gels (Fig. 3) and Ma et al. [42] applied a solid electrolyte composed of acryl resin containing inorganic materials including Sn, Zn and In in an Al–air battery combined with an air–cathode material composed of iron carbide. Di Palma et al. [43] also used xanthan and κ-carrageenan as hydrogel additives and found that these additives were conductive toward Al ions in which the performances of these additives were compared and their conductivities were in the order: the 1 M KOH liquid electrolyte < xanthan 8 M KOH < κ-carrageenan 8 M KOH. Furthermore, Peng et al. [44] studied a new type of all-solid-state fiber-shaped Al–air battery with high energy density and Mori et al. [45] prepared an all-solid-state Al–air battery with deep eutectic solvents. Despite these results, however, solid-state electrolytes can also increase battery resistances, which can result in lowered battery capacities as compared with those fabricated by using liquid-form electrolytes. Based on this, further studies need to be carried out to create high-performance solid-state Al–air batteries.
3 Anode Materials
Al anodes in Al–air batteries have been intensively studied because of their critical impact on performance in which main goals are to prevent corrosion and hydrogen evolution as well as to improve electrochemical properties such as electrolyte current density. Based on this, this section will describe the effects of pure Al anodes and alloy anodes of different metals with Al. In addition, this section will also discuss the influences of additives and coating materials on Al anodes.
3.1 Pure Al
In general, pure Al can exhibit better anodic performances than Al anodes with impurities. For example, Cho et al. [19] used 99.5% purity Al (2N5 commercial grade Al) as an Al anode in an Al–air battery with a NaOH alkaline electrolyte and found that the battery performance of 2N5 Al was inferior to that of 4 N high-purity Al (99.99%) because of the existence of a complex impurity layer that can reduce the discharge voltage. However, Wen et al. [46, 47] studied the effects of combining other metals with Al and found that Al–Mg–Ga–Sn–Mn anodes were more active than Al, Zn or Al–Mg–Ga–Sn anodes in which self-corrosion rates were found to be in the order: Al < Al–Mg–Ga–Sn–Mn < Al–Mg–Ga–Sn < Zn. In addition, these researchers also observed that Al–air batteries based on Al–Mg–Ga–Sn–Mn anodes can provide higher operating voltages and anodic utilization as compared with those using other anodic materials. In a further study, Pino et al. [48] compared commercial Al alloys including Al 2000, Al 2000 clad and Al 7000 as anodes in alkaline electrolytes and found that Al 2000 was ideal because it can exhibit higher open-circuit potentials, better anode efficiency and minimal corrosion rates. Furthermore, Mutlu et al. [49] investigated the effects of Al anodes treated with Cu through chemical and electrochemical processes on battery performance and found that Cu can improve anode efficiency by promoting the dissolution of Al according to battery reactions. Moreover, Ocon et al. [17] confirmed that carbon-treated commercial Al alloy anodes can achieve discharge rates up to three times higher than those without carbon on anode surfaces (Fig. 4).
For normal Al–air batteries, several issues exist, including: (1) the formation of byproducts such as Al2O3 and Al(OH)3 on electrode surfaces that can suppress Al–air battery electrochemical reactions, (2) hydrogen evolution resulting from parasitic corrosion reactions on Al surfaces and (3) the formation of corrosion products such as Al(OH) −4 and Al(OH)3 [50]. This parasitic chemical side reaction can be expressed as:
and can induce passivation and corrosion on Al anode surfaces to further suppress electrochemical reactions and often occurs in electrodes containing aqueous electrolytes. Furthermore, this passivation film is mainly composed of Al2O3 and Al(OH)3 and can induce positive shifts in the corrosion potential of Al electrodes, which can cause failure in corresponding Al–air batteries [17].
From a morphological point of view, Fan et al. [51, 52] studied the effects of grain size on Al anodes and found that the electrochemical properties of Al anodes are related to grain size in which finer grain-sized anodes demonstrated suppressed hydrogen evolution, improved electrochemical activity and increased anodic utilization in alkaline electrolytes. As for crystallinity, Fan et al. [53] also investigated the electrochemical properties of polycrystalline Al including Al (001), (110) and (111) single crystals and reported that the electrochemical properties of Al anodes were closely related to crystallographic orientation in alkaline electrolytes in which the (001) crystallographic plane demonstrated good corrosion resistance, but the (110) crystallographic plane was more sensitive. And as a result, Al (001) single crystals displayed higher anode efficiency and capacity density, proving that the control of the crystallographic orientation of Al anodes is a viable method to improve the performance of Al–air batteries using alkaline electrolytes (Fig. 5).
3.2 Al Alloys
Despite their promising characteristics, pure Al materials are unstable as anodes in Al–air batteries and a common method to improve electrochemical property involves the use of Al alloys. Based on this, numerous studies have been conducted to create better performance Al anodes by mixing Al with other metals such as Mn, Mg, Bi, In, Sn, Zn, Ga and Ti. And thus far, Al–Ga, Al–Sn, Al–Zn and Al–In alloys have been actively developed and have shown relatively high Al anode performances [23, 26, 54,55,56,57]. For example, Jingling et al. [58] investigated the electrochemical and corrosion performances of Al–0.5Mg–0.1Sn–0.02In–0.1Si and Al–0.5Mg–0.1Sn–0.02Ga–0.1Si alloys in both NaCl and NaOH electrolytes and found that the electrochemical properties of the Al–0.5Mg–0.1Sn–0.02Ga–0.1Si alloy were better in a 2 M NaCl solution, whereas the Al–0.5Mg–0.1Sn–0.02In–0.1Si alloy exhibited better performances in a 4 M NaOH solution. In another example, Ma et al. [59] reported that Si was effective at decreasing self-corrosion rates in which the anode properties of Al–Mg–Sn based alloys were examined. Here, these researchers reported that a Mg–6%–Al–3%–Zn–1.0%–In alloy was an optimal anode material for both cathodic protection and as a source of power.
In terms of the effects of individual elements, researchers have reported that Ga can suppress the formation of oxide film passivation in chloride solutions by becoming activated on Al surfaces and Sn can enhance Al anode dissolution rates and reduce corrosion rates [12]. Furthermore, Zn has been reported to be able to suppress hydrogen evolution on Al anodes by enhancing hydrogen evolution reaction (HER) potential and decreasing anode deterioration [60] and In can increase hydrogen evolution overpotential. For example, Sun et al. [61] reported that the addition of 0.5 wt% In to Al anodes can result in lowered corrosion rates and higher anodic efficiency as compared with pure Al. Here, this type of Al is referred to as a sacrificial anode, which can generally suppress the formation of passivating layers on Al surfaces. Furthermore, researchers have reported that further improvements in Al–air battery properties can be obtained by covering Al anodes with oxides or carbonaceous film layers [62,63,64,65,66,67].
4 Air Cathode
The properties of Al–air batteries are largely influenced by air–cathode catalytic materials, making air cathodes vital components. In general, an air cathode is composed of a current collector, a gas diffusion layer and a catalyst. Here, a current collector is normally composed of a stainless steel or Ni metal mesh and functions to transfer electrons and electricity and to connect to external electrical circuits [61, 68, 69]. Recently, Ti and Mo metals as well carbon meshes have also been used to prevent corrosion, especially from AlCl3-based electrolytes in rechargeable Al–air batteries. In terms of gas diffusion layers, they allow metal–air batteries to not only absorb air from ambient atmosphere but also seal batteries to prevent the leakage of liquid electrolytes, making their careful preparation a necessity. And in general, gas diffusion layers are usually composed of carbon or catalytic materials as well as hydrophobic binders such as polytetrafluoroethylene (PTFE) [70, 71]. As for catalytic materials in air cathodes, they can greatly influence the properties of corresponding metal–air batteries. And although carbon and manganese-based materials have often been applied as catalysts, many challenges associated with the use of other catalytic materials remain unresolved as described in the following section. Overall, however, catalytic materials are often mixed with binders and printed or placed onto current collectors in which the main chemical reaction catalyzed is the oxygen reduction reaction (ORR) [8, 10, 72]. Because air cathodes can greatly affect the properties of metal–air batteries, they must be optimized. This can be achieved by enhancing ORR, reducing carbonate and byproduct formation, preventing electrolyte evaporation and avoiding air–cathode flooding [21].
4.1 Al–Air Battery Electrochemical Reactions in Aqueous Electrolytes
The following reactions occur in the aqueous electrolyte of metal–air batteries during discharge [73]:
-
Anode:
$$ {\text{M }} \to {\text{ M}}^{ x+ } + x{\text{e}}^{ - } \quad \left( {{\text{M:}}\,{\text{metal}}} \right) $$(5) -
Air cathode:
$$ {\text{O}}_{2} + \, 2{\text{H}}_{2} {\text{O }} + \, 4{\text{e}}^{ - } \to \, 4{\text{OH}}^{ - } . $$(6)
The following reactions occur during charge:
-
Air cathode:
$$ 4{\text{OH}}^{ - } \to {\text{ O}}_{2} + \, 2{\text{H}}_{2} {\text{O }} + \, 4{\text{e}}^{ - } . $$(7)
Although metal reduction reaction is feasible in Zn–air batteries with KOH aqueous electrolytes, the reduction of Al3+ to Al is generally not possible in aqueous electrolytes in the case of Al–air batteries [24, 74]. However, if ionic liquid and deep eutectic solvent-based electrolytes are used in Al–air batteries, metal reduction reaction becomes possible. Rechargeable Al–air batteries are discussed in more detail in Sect. 5.
And based on Eq. (6), ORR is the critical cathodic reaction in Al–air batteries in which in aqueous electrolytes, ORR proceeds through a multi-electron chemical reaction that occurs at the cathode with two main possible pathways, including the transfer of 2e− to produce peroxide (H2O2) and the production of water through direct 4e− transfer as expressed by the following equations [75]:
-
Direct 4e− pathway:
$$ {\text{O}}_{2} + \, 4{\text{H}}^{ + } + \, 4{\text{e}}^{ - } \to \, 2{\text{H}}_{2} {\text{O}} $$(8) -
2e− pathway:
$$ {\text{O}}_{2} + \, 2{\text{H}}^{ + } + \, 2{\text{e}}^{ - } \to {\text{ H}}_{2} {\text{O}}_{2} $$(9)$$ {\text{H}}_{2} {\text{O}}_{2} + \, 2{\text{H}}^{ + } + \, 2{\text{e}}^{ - } \to \, 2{\text{H}}_{2} {\text{O}} $$(10)
Here, the 4e− pathway is preferable because the 2e− pathway produces H2O2, which is detrimental to air–cathode materials.
4.2 Catalysts
Because catalysts can greatly influence the properties of metal–air batteries, their improvement is of great interest. And because the reaction kinetics of ORR is often slow due to overpotentials [76], optimized catalysts that can reduce overpotentials and enhance ORR are vital for metal–air batteries and Al–air batteries. Based on this, numerous studies have been conducted to explore viable ORR catalysts, including precious metals and alloys, metal macrocyclic compounds, carbonaceous materials, transition metal oxides, chalcogenides, etc. (Fig. 6) [7, 13, 77,78,79].
4.3 Noble Metals and Alloys (Pt-Based Catalysts)
Nobel metals including Pt, Pd, Au and Ag have all been actively investigated because they can exhibit strong catalytic activities in metal–air batteries as well as in fuel cells due to the vacant state of the unoccupied d-orbitals, allowing them to be able to readily absorb reactant molecules [80,81,82,83]. And because activity is largely affected by the surface atomic configuration and the electron level state, the modification of electronic states can improve the catalytic activity of precious metal catalysts. Overall, Pt has been the most extensively studied noble metal catalyst in the past decades because of its excellent catalytic activity. Here, researchers have focused on catalytic activity and its dependence on Pt particle size and crystallographic facets [84, 85] in which the binding strength between Pt atoms and reactant species can determine ORR catalytic activity on different crystallographic facets in the order: Pt{100} < Pt{110} < Pt{111} [86, 87].
And although many challenges exist in the use of Pt catalysts, including the regulation of facet distribution and control of particle size, they are overshadowed by the essential problem arising from the high cost and scarcity of Pt as a limited natural resource. Therefore, the preparation of efficient Pt-based catalysts with minimal Pt loading is vital. One effective method is the deposition of Pt onto catalytic supports with large surface areas such as carbon (Fig. 7) [88,89,90]. In addition, Wang et al. [91] reported that the catalytic activity of Pt metal alloys can be higher than that of pure Pt as a result of an interesting phenomenon involving electronic ligands and compressive strain in which Pt lattices can be decreased and Pt d-orbital filling can be altered by incorporating transition metal atoms with different electronegativities into Pt lattice structures, allowing for higher catalytic activities than that of pure Pt. Furthermore, as other metals are mixed or doped with Pt metal catalysts, catalytic activities become dependent on the particle size, structure, chemical composition and electronic structure of these metals [92,93,94,95,96]. Based on this, researchers have incorporated Co, Fe, Ni, Ti and V into Pt structures to investigate their effects on Pt alloys. And in the case of a Pt–Ni alloy, a 9 nm octahedral Pt–Ni catalyst demonstrated optimal catalytic performances [97] and octahedral Pt–Ni nanoparticles possessed stronger ORR activities as compared with cubic structured Pt–Ni nanoparticles, suggesting that catalytic activity depends on both catalyst size and crystalline structure [98]. Despite these performances, however, catalytic activities can deteriorate during long-term ORR processes because of the weak durability of mixed transition metals. To address this, researchers have proposed core–shell-type catalysts to prevent damage to transition metals on catalyst surfaces and to reduce Pt consumption in which in this configuration, Pt can only be used at the surface of the catalyst [99,100,101,102,103,104,105,106].
4.4 Transition Metal Oxides
Although Pt and other metal-mixed or doped Pt alloy catalysts possess excellent ORR catalytic activities, their practical use in metal–air batteries and polymer electrolyte fuel cells is limited due to high costs and low natural abundance. As a result, tremendous efforts have been undertaken to explore alternative catalysts with high performance and low costs. Here, catalysts based on transition metal oxides are good options because of their high abundance and low costs. And based on this, early transition metal elements such as Fe, Mn, Co and Ni have been actively studied. For example, Mn-based oxides have been studied intensively as electrocatalyst materials because they possess relatively high ORR activities [107,108,109,110,111,112,113,114]. And because the valence states of Mn can exist as Mn(II), Mn(III) and Mn(IV), many manganese oxides can be obtained, including MnO, Mn3O4, Mn5O8, Mn2O3, MnOOH and MnO2 [115]. These multiple options for the valence and crystal structures of these transition metal oxides can provide great potential to create high-performance non-precious metal catalysts. And although the chemical composition of the various manganese oxides is identical to that of MnO2, different orientations can exhibit different catalytic activities because of differences in electrical conductivity and intrinsic tunnel size in the order: α-MnO2 > δ-MnO2 > γ-MnO2 > λ-MnO2 > β-MnO2 [116]. Researchers have also reported that the ORR activity of MnO2 can also differ based on morphology, including nanoflakes, nanowires and hollow spheres and attributed this to the differing amounts of Mn3+ on the surfaces of variable morphology [117, 118]. Other transition metal oxides, such as iron oxides [119], copper oxides [120], titanium oxides [121], cobalt oxides [122], nickel oxides [123] and cerium oxides [124], have also been studied in terms of their ORR activity, and researchers have reported that Co3O4 is a promising catalytic material among these transition metal oxides because of its high catalytic activity and low costs [125,126,127,128,129,130] in which the catalytic activity of Co3O4 depends on its corresponding crystalline facets and is in the order: (111) > (100) > (110) due to surface Co2+ ions [131]. Researchers have also reported that transition metal oxide catalysts possess low electrical conductivities, including Mn- and Co-based oxide catalysts and therefore, these catalysts are often combined with carbon-based support materials to enhance electrical conductivity for practical use [132,133,134,135,136,137,138,139,140].
Perovskite oxides (ABO3, A is a rare-earth metal and B is a transition metal) are a crystal structure of metal oxides that can exhibit bifunctional catalytic activity for both ORR and oxygen evolution reaction (OER) as catalysts. The ORR mechanism of perovskites is complex, and various factors such as surface absorption and electric conductivity can influence catalytic activity. Here, researchers have reported that ORR activities increased in the order of LaCoO3, LaMnO3, LaNiO3, LaFeO3 and LaCrO3 among LaMO3 (M = Ni, Co, Fe, Mn, and Cr) (Fig. 8) [141] and that a combination of individual perovskite catalysts such as LaNiO3 and LaMnO3 can produce synergetic effects to allow for good bifunctional catalysts by combining the high conductivity of LaNiO3 with the high ORR catalytic property of LaMnO3 [142]. Takeguchi et al. [143] also used a Ruddlesden–Popper-type layered perovskite (RP-LaSr3Fe3O10) as a reversible cathode catalyst for both ORR and OER and reported an equilibrium potential of 1.23 V with negligible overpotentials in which its ability to remove oxygen was suggested to be one of the reasons that both reversible ORR and OER were achieved with good efficiency.
Among transition metal oxide crystalline structures, spinel oxides (AB2O4) are also promising catalysts. Spinel oxides possess a cubic close-packed lattice structure with oxide anions in which one-eighth of the tetrahedral sites are occupied by A atoms and half of the octahedral sites are occupied by B atoms [144]. For example, CoMn2O4 has shown promise as a bifunctional catalyst for both ORR and OER in alkaline solutions [145]. And along with the above-mentioned perovskite catalysts and other transition metal oxides, spinel oxides also suffer from intrinsically low electrical conductivities and therefore are also commonly applied in combination with conductive carbon-based materials (Fig. 9) [146,147,148,149,150,151,152,153,154,155].
4.5 Carbonaceous Nanomaterials
Carbonaceous nanomaterials such as graphite, graphene and carbon nanotubes are promising metal-free ORR catalysts or supports because of their high electronic conductivity, large specific surface areas, environmental acceptability and corrosion resistance [156,157,158,159,160,161] and can be classified by their dimensional structure, including 0D fullerene, 1D carbon nanotubes, 2D graphene and various 3D nanostructured materials. As a result, carbon nanomaterials have been reviewed extensively and their catalytic activities have been studied in terms of the intermolecular charge-spin redistribution for ORR/OER/HER and in fuel cells [144].
4.6 Carbon Nanotube and Graphene-Based Nanocomposites
The structure of graphene involves one-atom-thick planar sheets composed of sp2-bonded carbon atoms that are densely packed in a honeycomb crystal lattice and recently; graphene has been intensively studied as an ORR catalyst in which significant catalytic activity improvements have been observed without the use of large quantities of Pt or noble metals [162,163,164,165,166,167]. In addition, Co3O4 and graphene composite catalysts have also shown high catalytic activities, demonstrating the possible synergetic chemical coupling effect between Co3O4, N and graphene toward enhanced ORR and OER [168, 169]. A combination of Mg and graphene has also been reported to be a promising material that can produce high performances in which Kosasang et al. [170] prepared a reduced graphene oxide and manganese oxide composite catalyst and reported a dominant 4e− pathway mechanism. As for carbon nanotubes (CNTs), they can be used as good support materials for catalysts because of their high specific surface areas, porous structure and high conductivity (Fig. 10) [171,172,173,174]. For example, Yoon et al. [134] applied a Co3O4 and CNT composite as a Li–air battery air cathode and reported high discharge capacities and low over-voltages, demonstrating the promising performance of the CNT/Co3O4 composite as a Li–air battery air electrode. In another study, Ni et al. [175] prepared a manganese oxide and CNT composite as a Li–air battery air cathode and reported enhanced catalytic activities and the formation of confined Li2O2 particles that can reduce the charge potential of Li-O2 batteries due to the synergistic effects of the intrinsic catalytic activity of MnO2 and the fewer oxygen functional groups on the catalyst surface.
4.7 Metal–Nitrogen–Carbon and Heteroatom-Doped Carbon
Metal–nitrogen–carbon materials are regarded as excellent low-cost ORR catalysts with high performances and generally involve metals such as Ni, Co, Fe, Mn, Cr and V. These materials are usually prepared by pyrolyzing N-rich metal complexes with carbon or by using metal salts, carbon and N-rich precursors as raw materials [176]. Here, the catalytic activity of these M–C–N catalysts is largely influenced by M and N precursors as well as pyrolysis temperatures in which appropriate pyrolysis temperatures are in the range of 700–900 °C. In alkaline media, the activity of M–C–N catalysts (M is V, Cr, Mn, Fe, Co or Ni) follows the order: Co > Ni > Mn > V > Cr, whereas in acidic media, the order follows: Fe > Co > Cr > Ni [177]. And although the mechanisms of active sites in M–N–C catalysts remain unknown, M–N moieties and N dopants that exist in carbonaceous materials are proposed to be the cause of high ORR catalytic activities [178].
Aside from N-doped carbon, the heteroatom-doping of carbon materials is another method to create carbonaceous catalytic materials with high efficiency in which B, S, P and F are generally used as dopants. In addition, the use of N as a mixed hetero-dopant is another method to create carbonaceous catalytic materials in which by introducing these dopants into carbon, resulting materials will possess large structural disorder and large amounts of heteroatom functionalities that can enhance ORR activity (Fig. 11) [179,180,181,182,183]. Furthermore, the introduction of heteroatoms into carbonaceous materials can allow for O–O bond breakage through the control of oxygen binding energy, which will result in the creation of carbon active sites adjacent to heteroatoms [184]. Based on all of this, Paraknowitsch et al. [185] and Cui et al. [186] provided excellent reviews on the recent progress made in the development of B-doped, P-doped and S-doped carbon materials for fuel cell applications. Moreover, Niu et al. [187] developed an easy preparation process to fabricate flexible, porous and well-dispersed metal-heteroatom-doped carbon nanofibers through the direct carbonization of electrospun Zn/Co-ZIFs/PAN nanofibers (Zn/Co-ZIFs/PAN). Here, the obtained Zn/Co and N co-doped porous carbon nanofibers as carbonized at 800 °C (Zn/Co–N@PCNFs-800) presented good flexibility, a continuous porous structure and an ORR catalytic activity superior to that of commercial 20 wt% Pt/C based on the onset potential (0.98 V vs. RHE), the half-wave potential (0.89 V vs. RHE) and limiting current density (−5.26 mA cm−2). Kim et al. [188] also incorporated various types of heteroatoms, including single dopants of N, B and P as well as multiple dopants involving B–N and P–N into a carbon matrix and reported that doping with N decreased the bonding between P and C in the matrix, whereas the use of multiple dopants induced the formation of additional active sites for ORR, which further enhanced both the ORR activity and stability of the resulting catalyst.
4.8 Carbon Quantum Dots
Carbon quantum dots and graphene quantum dots are small carbon nanoparticles (less than 10 nm in size) that possess various unique properties and can exhibit unusual chemical and physical properties due to their strong quantum confinement and edge effects [189]. As a result, these nanomaterials have found use in a growing number of fields over the last few years. However, the development and application of carbon-based quantum dots are not yet mature, especially in terms of electrocatalysis. Despite this, the numerous oxygen-rich functional groups on the surface of these carbon-based quantum dots can disrupt electroneutrality and produce abundant amounts of positively charged active sites that are useful for O2 surface adsorption. In addition, active sites on the edges of carbon-based quantum dots can enhance ORR. For example, Liu et al. [21] prepared surface-like multidimensional carbon-based quantum dots with O- and N-rich functional groups and reported that the resulting material possessed superior electrocatalytic activity for ORR and Zhang et al. [190] investigated the use of carbon-based quantum dots as ORR catalysts and suggested that the size of N-doped GQDs can affect ORR in which the adsorption strength of ORR intermediates, the reaction free energy of the rate-determining step and the overpotential can all increase with increasing N-doped GQD sizes. These researchers also reported that N-doped GQDs with the smallest size possessed the smallest overpotential and the highest ORR catalytic activity (Fig. 12), demonstrating the size effect of N-doped GQDs on ORR catalytic activity. In another study, Tam et al. [191] synthesized B-doped graphene quantum dots (BGQDs) through the hydrothermal treatment of glucose as the precursor in the presence of boric acid and investigated the effects of different types of B–C bond species on ORR catalytic activity to clarify the origin of the electrochemical reduction of O2. In addition, these researchers also prepared a composite of reduced graphene oxide and BGQDs (G-BGQDs) as a metal-free electrocatalyst for ORR and reported that the G-BGQD composite exhibited significantly enhanced electrocatalytic activities, including a positive onset potential and a high current density with a one-step, 4e− pathway toward ORR that were comparable to commercial Pt/C catalysts. Furthermore, these researchers reported that among various B–C bond structures in the BGQDs, the graphite-like BC3 structure was considered to be an important site for ORR because it improved the electric conductivity and electrocatalytic activity of the BGQDs as determined through DFT. Overall, these results demonstrated that both synthesized BGQDs and carbon-based quantum dots as metal-free catalysts are inexpensive, efficient electrocatalysts to replace Pt-based catalysts for ORR and other electrochemical applications.
4.9 Metal–Organic Frameworks
Metal–organic frameworks (MOFs) are synthesized by linking inorganic and organic units with strong bonds, and the corresponding flexibility with which the geometry, size and functionality of the constituents can be varied has led to more than 20000 different MOFs having been reported and studied within the past decade. In addition, organic units that are ditopic or polytopic organic carboxylates (and other similar negatively charged molecules) can be linked to metal-containing units to yield architecturally robust crystalline MOF structures with typical porosity 50% greater than that of MOF crystal volumes. Moreover, the surface areas of these MOFs typically range from 1000 to 10000 m2 g−1 and greatly exceed those of traditional porous materials such as zeolites and carbons. Furthermore, MOFs with permanent porosity are more extensive in their variety and multiplicity than any other classes of porous materials. And as a result of these aspects, MOFs are ideal candidates for the storage of fuels (hydrogen and methane), capture of carbon dioxide and catalysis applications as well as for use as electrodes in fuel cells and metal–air batteries [192] (an extensive review on the application of MOFs as ORR catalysts can be found in Ref. [193]). Despite these advantages, however, the low intrinsic electronic conductivity of MOFs remains an obstacle hindering utilization as electrodes. To address this, Gonen et al. [194] synthesized benzene tricarboxylic acid–based MOFs inside activated carbon (AC) with four different first-row transition metals, including Mn, Fe, Co and Cu and electrochemically analyzed the resulting MOFs@ACs based on their catalytic activity. Here, these researchers found that the MOFs@AC catalysts were conductive and active for ORR in alkaline environments and that Mn-MOF-based @AC exhibited the best performance with an onset potential of 0.9 V versus RHE and an almost 4e− mechanism. In another study, Zhao et al. [195] also prepared a newly designed mixed-node MOF catalyst CoxFe1−x-MOF-74 (0 < x ⩽ 1) as a highly efficient electrocatalyst for OER in alkaline media and reported a remarkably low overpotential (280 mV at a current density of 10 mA cm−2), a small Tafel slope (56 mV dec−1) and high faradic efficiency (91%) (Fig. 13), in which the catalyst delivered a current density of 20 mA cm−2 at 1.58 V for overall water-splitting reaction. These researchers also used aluminum terephthalate as an air cathode for an Al–air battery and again obtained promising results [196].
4.10 Single-Atom Catalysts
Single-atom catalysis has arguably become the most active frontier in heterogeneous catalysis. And with recent advances in practical synthetic methodologies, characterization techniques and computational modeling, numerous single-atom catalysts (SACs) have been studied that exhibit distinctive performances for a wide variety of chemical reactions. Because SACs possess well-defined active centers, unique opportunities exist for the rational design of novel catalysts with high activity and stability. And considering certain practical applications, researchers can often design suitable SACs. As a result, this field has developed rapidly and has produced promising catalyst leads [197]. For example, Zang et al. [198] prepared single Co atoms anchored on porous N-doped carbon nanoflake arrays from a Co-MOF precursor followed by the removal of unwanted Co clusters, which resulted in the attachment of well-dispersed Co single atoms to the carbon network through N–Co bonding and additional porosity and active surface areas as created by the removal of Co metal clusters. Here, these researchers reported that the single Co atom catalyst demonstrated lower OER overpotential and much higher ORR saturation current as compared with electrocatalysts containing excess Co nanoparticles, demonstrating that Co metal clusters were redundant in driving both OER and ORR (Fig. 14). And based on this bifunctional electrocatalytic activity and mechanical flexibility, these researchers assembled this electrocatalyst on carbon cloth as an air cathode in a solid-state Zn–air battery and obtained good cycling stability (2500 min, 125 cycles) as well as a high open-circuit potential (1.411 V). In another study, Jia et al. [199] synthesized N-doped porous carbon with atomic-level dispersion of Fe–Nx species and reported that the obtained Fe/N co-doped carbon nanocage ORR electrocatalyst exhibited a comparable half-wave potential (0.82 V) and higher limiting current density as compared with commercial Pt/C electrocatalysts. These researchers also used the obtained electrocatalyst in an air electrode of an assembled Zn–air battery and obtained a specific capacity of 705 mAh g−1 at 5 mA cm−2 and negligible voltage loss after continuous operation for 67 h. Here, these researchers attributed the superior performance of the Fe/N co-doped carbon nanocages to the porous structure and synergetic effects of the atomically dispersed Fe–Nx species and N-doping.
4.11 Nitrides and Carbides
Nanostructured metal carbides and nitrides have attracted much attention because of their active properties in various areas such as magnetism, biomedicine, electrocatalysis and environmental applications. In general, the intrinsically harsh characteristics of carbides and nitrides make their synthetic protocols difficult, especially at the nanoscale; however, they can usually result in improved performances in specific applications. For example, He et al. [200] used TiN as an ORR catalyst in a Li–air fuel cell with a non-aqueous/acidic aqueous hybrid electrolyte and extensively investigated the electrochemical properties of the TiN-based catalyst and the single cell and concluded that TiN possessed considerable electrochemical catalytic activity for Li–air fuel cells in weak acidic media. Lin et al. [201] also prepared a bifunctional electrocatalyst consisting of manganese iron binary carbide (MnxFe3−xC) nanoparticles anchored on N-doped graphitic carbon (MnxFe3−xC/NC) (Fig. 15) in which the synthesis involved the facile pyrolysis of a trimetallic (Fe, Mn, Zn) zeolitic imidazolate framework. Here, these researchers reported that the incorporation of Mn modulated the electronic properties of Fe3C and the surrounding carbon to enhance both ORR and OER activities. In addition, these researchers also suggested that MnxFe3−xC, which is well protected by carbon layers, can display high resistances to oxidation and corrosion. And as a result, the assembled Zn–air battery exhibited a large peak power density (160 mW cm−2 at 250 mA cm−2) with an energy density of up to 762 mWh gZn−1, a high open-circuit voltage of 1.5 V and an impressive long-term stability of over 1000 cycles. Lin et al. [201] also used TiN and TiC as active materials for air cathodes in rechargeable Al–air batteries with promising results.
5 Rechargeable Al–Air Batteries
Aside from the use of Al–air batteries as primary batteries, studies have also been conducted to explore the possibility of creating rechargeable Al–air batteries. In general, the creation of rechargeable Al–air batteries is challenging and can provide large breakthroughs in this field because Al possesses a large theoretical capacity. And although many researchers have reported the creation of rechargeable Al-ion batteries, few studies have reported rechargeable Al–air batteries. Despite this, researchers are actively researching rechargeable Al–air batteries, particularly using ionic liquid or deep eutectic solvents as electrolytes (Fig. 16) [13, 196, 202, 203]. Al–air batteries that use chloroaluminate ionic liquid as the electrolyte exhibit Lewis acid–base chemistry comparable to Brønsted acidity in water, and similar to the control that proton concentration exerts over chemistry and electrochemistry in aqueous solutions, chloroacidity is the major determinant of speciation, reactivity and electrochemistry in ionic liquids. As for Al–air batteries, the composition of the melt determines chloroacidity in which as the chloride donor undergoes stepwise Lewis acid-base reactions with acidic AlCl3, chloroaluminate anions form according to the following equilibrium reactions:
Here, at < 0.5 mol fraction of AlCl3 in the room temperature liquid melt, the only anions present in significant quantities are Lewis bases Cl− and AlCl4−, making the melt basic. And at AlCl3 mol fractions greater than 0.5, as was used in our study, the only anions present in appreciable amounts in the liquid were AlCl4− and Al2Cl7−. This is a crucial factor because the electrodeposition of Al can only occur from Al2Cl7− through the following reaction [204]:
Therefore, it is hypothesized that Al2Cl7− can function as a charge carrier in Al–air batteries. The overall electrochemical reactions in aqueous solution electrolytes are described in the above section and for rechargeable Al–air batteries, suitable ionic liquids must be applied as an electrolyte in the battery to permit the deposition of Al [205]. Overall, the theoretical voltage of Al–air batteries with an ionic liquid-based electrolyte can be speculated in which the following reactions occur upon discharge:
Anode:
And the following reactions may occur upon charge:
Anode:
Cathode:
Based on this, the theoretical voltage should be 3.24 V (cell potential = anodic potential + cathodic potential). However, the actual voltages of rechargeable Al–air batteries using ionic liquid-based electrolytes are lower than 3.24 V and detailed chemical reaction mechanisms remain to be determined in future studies to elucidate overpotentials as caused by electrolytes, electrode bulk resistances and interfacial resistances [202]. As for aqueous electrolytes and protic solvents, ORR proceeds through a multi-electron chemical reaction that occurs at the air cathode of Al–air batteries with two main possible pathways, including the transfer of 2e− to produce peroxide (H2O2) and the production of water through direct 4e− transfer as described in a previous section. In general, 1-ethyl-3-methylimidazolium chloride (EMImCl) has been used as an electrolyte for Al–air batteries. However, because EMImCl is an aprotic solvent, ORR is difficult to achieve due to the lack of protons in the solvent [206]. In addition, the effects of humidity (water) need to be considered with the use of EMImCl due to it being a hydrophilic ionic liquid, which can absorb humidity (water) from ambient atmosphere and cause water to be present in the electrolyte, leading to corresponding Al–air batteries absorbing water from surrounding ambient atmosphere and reactions 11 and 12 occurring at the air cathode.
In terms of electrocatalysts, bifunctional electrocatalysts are ideal for rechargeable Al–air batteries and various bifunctional electrocatalysts such as Pt, noble metal, metal nitride and carbide catalysts are active for ORR through the 4e− pathway. As for carbonaceous materials, they proceed through the 2e− pathway and therefore, corresponding air–cathode catalysts need to be carefully selected to prepare high-performance Al–air batteries. As examples, Sun et al. [207] prepared a gelled ionic liquid by complexing EMImCl with AlCl3 through Al electrodeposition in their Al-ion battery and reported promising results and aside from ionic liquid-based electrolytes, Nakayama et al. [208] managed to deposit and dissolve Al in non-corrosive sulfone-based electrolytes (Fig. 17). Furthermore, Gonzalo et al. [209] reported a stable electrogenerated superoxide ion in a phosphonium-based ionic liquid in the presence of water that led to a chemically reversible O2/O ·−2 redox couple instead of the usually observed disproportionation reaction and Gelman et al. [205] developed a primary Al–air cell based on an oxygen and water-stable 1-ethyl-3-methylimidazolium oligo-fluorohydrogenate electrolyte [EMIm(HF)2.3F] that delivered 140 mAh cm−2. Wang et al. [210] also reported a rechargeable Al–air battery based on 1-butyl-3-methylimidazolium chloride with aluminum triflate as a metal salt (Fig. 18). Moreover, Bogolowski et al. [206] recently used a Pt/C gas diffusion electrode (GDE) to show the feasibility of creating an electrically rechargeable Al–air battery at a 100 mA cm−2 current density for 15 cycles (200 h) in a 1:1.5 EMImCl/AlCl3 electrolyte. However, the charge/discharge cycle in this battery was limited to 3 h each, which represented a reversible capacity of 300 mAh cm−2 and is only 0.4% of the theoretical capacity for anode-normalized Al foil. Here, these researchers attributed the poor cell reversibility to trace amounts of residual water.
More recently, deep eutectic solvents such as acetamide- and urea-based eutectic solvents have also been investigated for use in Al–air batteries because of their cheaper material cost and ease of preparation (Fig. 19) [211, 212]. For example, some urea- and acetamide-based deep eutectic solvents developed by Abood et al. [213, 214] have shown appreciable reversible activities for Al deposition/stripping (Fig. 20) in which amide groups can react with AlCl3 and build positively charged complexes and negatively charged tetrachloroaluminate anions according to the following reaction:
And although the exact ion species or charge carriers for Al–air battery systems remain unclear, it is assumed that AlCl4− or Al2Cl7−is the charge carriers. In addition, Katayama et al. [215] suggested that in the case of Al–air batteries with an electrolyte composed of a mixture of AlCl3, 1-butyl-3-methylimidazolum chloride and bis(trifluoromethylsulfonyl)amide, the charge carriers should be either AlCl4− or Al2Cl7− and that as Al2Cl7− concentrations decrease, the concentration of AlCl4− increases as confirmed by Raman spectroscopy. Agiorgousis et al. [216] also excluded the possibility of Al3+ cations acting as charge carriers and instead suggested AlCl4− anions as possible charge carriers and Angell et al. [217] claimed that both Al2Cl7−and AlCl4− existed in the AlCl3− urea ionic liquid analog electrolyte. Anyway, the creation of efficient rechargeable Al–air batteries would be a great achievement and has large impacts because the theoretical capacity of Al–air batteries is much larger than that of Li-ion batteries.
6 Conclusion
Al–air batteries possess great potential for practical application due to their large energy capacity and in this review, Al–air batteries with Al anodes, electrolytes and air cathodes have been discussed and the possibility of creating rechargeable Al–air batteries has been presented. Overall, the focus of the development of pure Al and Al alloy anodes is the prevention of self-corrosion and byproduct formation. As for electrolytes, they are critical components determining the rechargeability potential of Al–air batteries. Electrolyte additives are also an important issue because they can suppress corrosion and hydrogen evolution to improve electrochemical properties. Furthermore, various solid electrolytes have been investigated despite poorer energy capacities as compared with liquid electrolytes due to bulk and interface impedance between electrodes and solid electrolytes. In terms of the ORR, this is the rate-determining critical process in Al–air batteries because of its sluggish reaction kinetics in comparison with electrochemical reactions at the anode. As a result, air–cathode materials are also critical components that can significantly influence overall battery properties. And although Pt-based catalysts are the most promising catalytic materials for ORR, their high cost and resource scarcity hinder application. Therefore, Pt alternatives have been extensively explored and involve the application of other transition metals to either fully or partially replace Pt. Furthermore, metal oxide catalysts including perovskites, spinel crystalline materials, metals and nitrogen as well as heteroatom-doped carbonaceous catalytic materials have also shown promise. Moreover, studies have shown that non-oxide materials such as metal nitrides, carbides, carbon-based quantum dots, MOFs and single-atom catalysts can also be used as next-generation catalytic materials that possess high ORR activity. Overall, because the theoretical capacity of Al–air batteries is much larger than that of Li-ion batteries, the creation of rechargeable Al–air batteries is of great importance and can be used in the design of smart grid energy systems. These rechargeable Al–air batteries can also potentially be applied in electricity-based vehicles to promote an environmentally friendly future.
References
Assat, G., Tarascon, J.M.: Fundamental understanding and practical challenges of anionic redoxactivity in Li-ion batteries. Nat. Energy 3, 373–386 (2018)
Erickson, E.M., Schipper, F., Penki, T.R., et al.: Review-recent advances and remaining challenges for lithium ion battery cathodes II. Lithium-rich, xLi2MnO3·(1 − x)LiNiaCobMncO2. J. Electrochem. Soc. 164, A6220–A6228 (2017)
Nitta, N., Wu, F., Lee, J.T., et al.: Li-ion battery materials: present and future. Mater. Today 18, 252–264 (2015)
Li, M., Lu, J., Chen, Z., et al.: 30 years of lithium-ion batteries. Adv. Mater. 30, 1800561–1800584 (2018)
Noori, A., El-Kady, M.F., Rahmanifar, M.S., et al.: Towards establishing standard performance metrics for batteries, supercapacitors and beyond. Chem. Soc. Rev. 48, 1272–1341 (2019)
Li, Y., Lu, J.: Metal–air batteries: will they be the future electrochemical energy storage device of choice? ACS Energy Lett. 26, 1370–1377 (2017)
Cheng, F., Chen, J.: Metal–air batteries: from oxygen reduction electrochemistry to cathode catalysts. Chem. Soc. Rev. 41, 2172–2192 (2012)
Jung, K.N., Kim, J., Yamauchi, Y., et al.: Rechargeable lithium–air batteries: a perspective on the development of oxygen electrodes. J. Mater. Chem. A 4, 14050–14068 (2016)
Peng, G.: Rechargeable zinc–air batteries: a promising way to green energy. J. Mater. Chem. A5, 7635–7650 (2017)
Zhang, T., Chen, J.: Magnesium–air batteries: from principle to application. Mater. Horiz. 1, 196–206 (2014)
Park, I.J., Seok, R.C., Kim, J.G.: Aluminum anode for aluminum–air battery—part II: influence of in addition on the electrochemical characteristics of Al–Zn alloy in alkaline solution. J. Power Sources 357, 47–55 (2017)
Zegao, S.: Performance of Al–air batteries based on Al–Ga, Al–In and Al–Sn alloy electrodes. J. Electrochem. Soc. 162, A2116–A2122 (2015)
Mori, R.: Rechargeable aluminum–air battery using various air-cathode materials and suppression of byproducts formation on both anode and air cathode. ECS Trans. 80, 377–393 (2017)
Xhanari, K., Finsgar, M.: Organic corrosion inhibitors for aluminum and its alloys in chloride and alkaline solutions: a review. Arab. J. Chem. 12, 4646–4663 (2016)
Zaromb, S.: The use and behavior of aluminum anodes in alkaline primary batteries. J. Electrochem. Soc. 109, 1125–1130 (1962)
Bockstie, L., Trevethan, D., Zaromb, S.: Control of Al corrosion in caustic solutions. J. Electrochem. Soc. 110, 267–271 (1963)
Pino, M., Herranz, D., Chacon, J., et al.: Carbon treated commercial aluminium alloys as anodes for aluminium–air batteries in sodium chloride electrolyte. J. Power Sources 326, 296–302 (2016)
Bernard, J., Chatenet, M., Dalard, F.: Understanding aluminum behaviour in aqueous alkaline solution using coupled techniques: part I. Rotating ring-disk study. Electrochim. Acta 52, 86–93 (2006)
Cho, Y.J., Park, I.J., Lee, H.J., et al.: Aluminum anode for aluminum–air battery—part I: influence of aluminum purity. J. Power Sources 277, 370–378 (2015)
Shkolnikov, E.I., Zhuk, A.Z., Vlaskin, M.S.: Aluminum as energy carrier: feasibility analysis and current technologies overview. Renew. Sustain. Energy Rev. 15, 4611–4623 (2011)
Liu, Y., Sun, Q., Li, W., et al.: A comprehensive review on recent progress in aluminum–air batteries. Green Energy Environ. 2, 246–277 (2017)
Ryu, J., Jang, H., Park, J., et al.: Seed-mediated atomic-scale reconstruction of silver manganate nanoplates for oxygen reduction towards high-energy aluminum–air flow batteries. Nat. Commun. 9, 3715–3724 (2018)
Abedin, S.Z.E., Endres, F.: Electrochemical behaviour of Al, Al–In and Al–Ga–In alloys in chloride solutions containing zinc ions. J. Appl. Electrochem. 34, 1071–1080 (2004)
Egan, D.R., Leon, P.D., Wood, R.J.K., et al.: Developments in electrode materials and electrolytes for aluminium–air batteries. J. Power Sources 236, 293–310 (2013)
Li, L., Manthiram, A.: Long-life, high-voltage acidic Zn–air batteries. Adv. Energy Mater. 6, 1502054 (2016)
Shayeb, H.A.E., Wahab, F.M.A.E., Abedin, S.Z.E.: Electrochemical behaviour of Al, Al–Sn, Al–Zn and Al–Zn–Sn alloys in chloride solutions containing indium ions. J. Appl. Electrochem. 29, 473–480 (1999)
Tang, Y., Lu, L., Roesky, H.W., et al.: The effect of zinc on the aluminum anode of the aluminum–air battery. J. Power Sources 138, 313–318 (2004)
Liu, Z., El Abedin, S.Z., Endres, F.: Electrochemical and spectroscopic study of Zn (II) coordination and Zn electrodeposition in three ionic liquids with the trifluoromethylsulfonate anion, different imidazolium ions and their mixtures with water. Phys. Chem. Chem. Phys. 17, 15945–15952 (2015)
Wang, X.Y., Wang, J.M., Wang, Q.L., et al.: The effects of polyethylene glycol (PEG) as an electrolyte additive on the corrosion behavior and electrochemical performances of pure aluminum in an alkaline zincate solution. Mater. Corros. 62, 1149–1152 (2011)
Liu, J., Wang, D., Zhang, D., et al.: Synergistic effects of carboxymethyl cellulose and ZnO as alkaline electrolyte additives for aluminium anodes with a view towards Al–air batteries. J. Power Sources 335, 1–11 (2016)
Yang, S., Knickle, K.: Design and analysis of aluminum/air battery system for electric vehicles. J. Power Sources 112, 162–173 (2002)
El-Haddad, M.N., Fouda, A.S.: Electroanalytical, quantum and surface characterization studies on imidazole derivatives as corrosion inhibitors for aluminum in acidic media. J. Mol. Liq. 209, 480–486 (2015)
Wang, D., Zhang, D., Lee, K., et al.: Performance of AA5052 alloy anode in alkaline ethylene glycol electrolyte with dicarboxylic acids additives for aluminium–air batteries. J. Power Sources 297, 464–471 (2015)
Madram, A.R., Shokri, F., Sovizi, M.R., et al.: Aromatic carboxylic acids as corrosion inhibitors for aluminium in alkaline solution. Port. Electrochim. Acta 34, 395–405 (2016)
Wang, D., Li, H., Liu, J., et al.: Evaluation of AA5052 alloy anode in alkaline electrolyte with organic rare-earth complex additives for aluminium–air batteries. J. Power Sources 293, 484–491 (2015)
Wang, J., Wang, J., Shao, H., et al.: The corrosion and electrochemical behaviour of pure aluminium in alkaline methanol solutions. J. Appl. Electrochem. 37, 753–758 (2007)
Kang, Q.X., Wang, Y., Zhang, X.Y.: Experimental and theoretical investigation on calcium oxide and L-aspartic as an effective hybrid inhibitor for aluminum–air batteries. J. Alloys Compd. 774, 1069–1080 (2019)
Hopkins, B.J., Horn, Y.S., Hart, D.P.: Suppressing corrosion in primary aluminum–air batteries via oil displacement. Science 362, 658–661 (2018)
Mokhtar, M., Zainal, M., Majlan, E.H., et al.: Recent developments in materials for aluminum–air batteries: a review. J. Ind. Eng. Chem. 32, 1–20 (2015)
Zhang, Z., Zuo, C., Liu, Z., et al.: All-solid-state Al–air batteries with polymer alkaline gel electrolyte. J. Power Sources 251, 470–0475 (2014)
Tan, M.J., Li, B., Chee, P., et al.: Acrylamide-derived freestanding polymer gel electrolyte for flexible metal–air batteries. J. Power Sources 400, 566–571 (2018)
Ma, Y., Sumboja, A., Zang, W., et al.: Flexible and wearable all-solid-state Al–air battery based on iron carbide encapsulated in electrospun porous carbon nanofibers. ACS Appl. Mater. Interfaces 11, 1988–1995 (2019)
Di Palma, T.M., Migliardini, F., Caputo, D., et al.: Xanthan and κ-carrageenan based alkaline hydrogels as electrolytes for Al/air batteries. Carbohydr. Polym. 157, 122–127 (2017)
Xu, Y., Zhao, Y., Ren, J., et al.: An all-solid-state fiber-shaped aluminum–air battery with flexibility, stretchability, and high electrochemical performance. Angew. Chem. Int. Ed. 55, 7979–7982 (2016)
Mori, R.: All solid state rechargeable aluminum–air battery with deep eutectic solvent based electrolyte and suppression of byproducts formation. RSC Adv. 9, 22220–22226 (2019)
Ma, J., Wen, J., Gao, J., et al.: Performance of Al–0.5Mg–0.02Ga–0.1Sn–0.5Mn as anode for Al–air battery in NaCl solutions. J. Power Sources 253, 419–423 (2014)
Ma, J., Wen, J., Gao, J., et al.: Performance of Al–1Mg–1Zn–0.1Ga–0.1Sn as anode for Al–air battery. Electrochem. Acta 129, 69–75 (2014)
Pino, M., Cuadrado, C., Chacon, J., et al.: The electrochemical characteristics of commercial aluminium alloy electrodes for Al/air batteries. J. Appl. Electrochem. 44, 1371–1380 (2014)
Mutlu, R.N., Yazici, B.: Copper-deposited aluminum anode for aluminum–air battery. J. Solid State Electrochem. 23, 529–541 (2019)
Doche, M.L., Rameau, J.J., Durand, R., et al.: Electrochemical behaviour of aluminium in concentrated NaOH solutions. Corros. Sci. 41, 805–826 (1999)
Fan, L., Lu, H.: The effect of grain size on aluminum anodes for Al–air batteries in alkaline electrolytes. J. Power Sources 284, 409–415 (2015)
Fan, L., Lu, H., Leng, J.: Performance of fine structured aluminum anodes in neutral and alkaline electrolytes for Al–air batteries. Electrochim. Acta 165, 22–28 (2015)
Fan, L., Lu, H., Leng, J., et al.: The effect of crystal orientation on the aluminum anodes of the aluminum–air batteries in alkaline electrolytes. J. Power Sources 299, 66–69 (2015)
Shayeb, H.A.E., Wahab, F.M.A.E., Abedin, S.Z.E.: Electrochemical behaviour of Al, Al–Sn, Al–Zn and Al–Zn–Sn alloys in chloride solutions containing stannous ions. Corros. Sci. 43, 655–669 (2001)
Saidman, S.B., Bessone, J.B.: Activation of aluminium by indium ions in chloride solutions. Electrochim. Acta 42, 413–420 (1997)
Wilhelmsen, W., Arnesen, T., Hasvold, Ø., et al.: The electrochemical behaviour of Al–In alloys in alkaline electrolytes. Electrochim. Acta 36, 79–85 (1991)
Smoljko, I., Gudić, S., Kuzmanić, N., et al.: Electrochemical properties of aluminium anodes for Al/air batteries with aqueous sodium chloride electrolyte. J. Appl. Electrochem. 42, 969–977 (2012)
Jingling, M., Jiuba, W., Hongxi, Z., et al.: Electrochemical performances of Al–0.5Mg–0.1Sn–0.02In alloy in different solutions for Al–air battery. J. Power Sources 293, 592–598 (2015)
Ma, J., Wen, J., Ren, F., et al.: Electrochemical performance of Al–Mg–Sn based alloys as anode for Al–air battery. J. Electrochem. Soc. 163, A1759–A1764 (2016)
Pino, M., Chacόn, J., Fatas, E., et al.: Performance of commercial aluminium alloys as anodes in gelled electrolyte aluminium–air batteries. J. Power Sources 299, 195–201 (2015)
Sun, Z., Lu, H.: Performance of Al–0.5In as anode for Al–air battery in inhibited alkaline solutions. J. Electrochem. Soc. 162, A1617–A1623 (2015)
Mori, R.: A new structured aluminium–Air secondary battery with a ceramic aluminium ion conductor. RSC Adv. 3, 11547–11551 (2013)
Mori, R.: A novel aluminium–air secondary battery with long-term stability. RSC Adv. 4, 1982–1987 (2014)
Mori, R.: A novel aluminium–air rechargeable battery with Al2O3 as the buffer to suppress byproduct accumulation directly onto an aluminium anode and air cathode. RSC Adv. 4, 30346–30351 (2014)
Mori, R.: Addition of ceramic barriers to aluminum–air batteries to suppress by-product formation on electrodes. J. Electrochem. Soc. 162, A288–A294 (2015)
Mori, R.: Capacity recovery of aluminium–air battery by refilling salty water with cell structure modification. J. Appl. Electrochem. 45, 821–829 (2015)
Mori, R.: Semi-rechargeable aluminum–Air battery with a TiO2 internal layer with plain salt water as an electrolyte. J. Electron. Mater. 45, 3375–3382 (2016)
Li, Y., Dai, H.: Recent advances in zinc–air batteries. Chem. Soc. Rev. 43, 5257–5275 (2014)
Gu, P., Zheng, M., Zhao, Q., et al.: Rechargeable zinc–air batteries: a promising way to green energy. J. Mater. Chem. A 5, 7651–7666 (2017)
Wang, K., Pei, P., Wang, Y., et al.: Advanced rechargeable zinc–air battery with parameter optimization. Appl. Energy 225, 848–856 (2018)
Quan, O., Hwang, H.J., Ji, Y., et al.: Transparent bendable secondary zinc–air batteries by controlled void ionic separators. Sci. Rep. 9, 3175–3183 (2019)
Li, C.S., Sun, Y.S., Gebert, F., et al.: Current progress on rechargeable magnesium–air battery. Adv. Energy Mater. 7, 1700869–1700879 (2017)
Li, P.C., Chi, C.H., Lee, T.H., et al.: Synthesis and characterization of carbon black/manganese oxide air cathodes for zinc–air batteries. J. Power Sources 269, 88–97 (2014)
Nestoridi, M., Pletcher, D., Wang, S., et al.: The study of aluminium anodes for high power density Al/air batteries with brine electrolytes. J. Power Sources 178, 445–455 (2008)
Poux, T., Napolskiy, F.S., Dintzer, D., et al.: Dual role of carbon in the catalytic layers of perovskite/carbon composites for the electrocatalytic oxygen reduction reaction. Catal. Today 189, 83–92 (2012)
Wu, G., Zelenay, P.: Nanostructured nonprecious metal catalysts for oxygen reduction reaction. Acc. Chem. Res. 46, 1878–1889 (2013)
Spendelow, J.S., Wieckowski, A.: Electrocatalysis of oxygen reduction and small alcohol oxidation in alkaline media. Phys. Chem. Chem. Phys. 9, 2654–2675 (2007)
Yejian, X., He, M., Shanshan, S., et al.: La1−xAgxMnO3 electrocatalyst with high catalytic activity for oxygen reduction reaction in aluminium air batteries. RSC Adv. 7, 5214–5221 (2017)
Leonard, N., Nallathambi, V., Barton, S.C.: Carbon supports for non-precious metal oxygen reducing catalysts. J. Electrochem. Soc. 160, F788–F792 (2013)
Wang, Z.L., Xu, D., Xua, J.J., et al.: Oxygen electrocatalysts in metal–air batteries: from aqueous to nonaqueous electrolytes. Chem. Soc. Rev. 43, 7746–7786 (2014)
Antolini, E.: Palladium in fuel cell catalysis. Energy Environ. Sci. 2, 915–931 (2009)
Jeong, Y.S.: Study on the catalytic activity of noble metal nanoparticles on reduced graphene oxide for oxygen evolution reactions in lithium–air batteries. Nano Lett. 15, 4261–4268 (2015)
Dong, Q., Wang, D.: Catalysts in metal–air batteries. MRS Comm. 8, 372–386 (2018)
Marković, N.M., Gasteiger, H.A., Ross, P.N.: Oxygen reduction on platinum low-index single-crystal surfaces in alkaline solution: rotating ring disk Pt (hkl) studies. J. Phys. Chem. 100, 6715–6721 (1996)
Nguyen, V.L., Ohtaki, M., Ngo, V.N., et al.: Structure and morphology of platinum nanoparticles with critical new issues of low-and high-index facets. Adv. Nat. Sci. Nanosci. Nanotechnol. 3, 025005–025008 (2012)
Shao, M., Chang, Q., Dodelet, J.P., et al.: Recent advances in electrocatalysts for oxygen reduction reaction. Chem. Rev. 116, 3594–3657 (2016)
Wang, J.X., Inada, H., Wu, L., et al.: Oxygen reduction on well-defined core-shell nanocatalysts: particle size, facet, and Pt shell thickness effects. J. Am. Chem. Soc. 131, 17298–17302 (2009)
Chitturi, V.R., Ara, M., Fawaz, W., et al.: Enhanced lithium-oxygen battery performances with Pt subnanocluster decorated N-doped single-walled carbon nanotube cathodes. ACS Catal. 6, 7088–7097 (2016)
Neburchilov, L., Wang, H., Martin, J.J., et al.: A review on air cathodes for zinc–air fuel cells. J. Power Sources 195, 1271–1291 (2010)
Rahman, M.A., Wang, X., Wenz, C.: High energy density metal–air batteries: a review. J. Electrochem. Soc. 160, A1759–A1771 (2013)
Wang, C., Daimon, H., Onodera, T., et al.: A general approach to the size-and shape-controlled synthesis of platinum nanoparticles and their catalytic reduction of oxygen. Angew. Chem. Int. Ed. Engl. 47, 3588–3591 (2008)
Yin, J., Fang, B., Luo, J., et al.: Nanoscale alloying effect of gold–platinum nanoparticles as cathode catalysts on the performance of a rechargeable lithium-oxygen battery. Nanotechnology 23, F305404 (2012)
Terashima, C., Iwai, Y., Cho, S.P., et al.: Solution plasma sputtering processes for the synthesis of PtAu/C catalysts for Li–air batteries. Int. J. Electrochem. Sci. 8, 5407–5420 (2013)
Moseley, P.T., Park, J.K., Kim, H.S., et al.: A study of PtxCoy alloy nanoparticles as cathode catalysts for lithium–air batteries with improved catalytic activity. J. Power Sources 244, 488–493 (2013)
Zhang, Y., Wu, X., Fu, Y., et al.: Carbon aerogel supported Pt–Zn catalyst and its oxygen reduction catalytic performance in magnesium–air batteries. J. Mater. Res. 29, 2863–2870 (2014)
Chen, W., Chen, S.: Iridium-platinum alloy nanoparticles: composition-dependent electrocatalytic activity for formic acid oxidation. J. Mater. Chem. 21, 9169–9178 (2011)
Xia, Y., Xiong, Y., Lim, B., et al.: Shape-controlled synthesis of metal nanocrystals: simple chemistry meets complex physics? Angew. Chem. Int. Ed. Engl. 48, 60–103 (2009)
Wu, J., Gross, A., Yang, H.: Shape and composition-controlled platinum alloy nanocrystals using carbon monoxide as reducing agent. Nano Lett. 11, 798–802 (2011)
Bae, S.J., Sung, J.Y., Yuntaek, L., et al.: Facile preparation of carbon-supported PtNi hollow nanoparticles with high electrochemical performance. J. Mater. Chem. 22, 8820–8825 (2012)
Hwang, S.J., Yoo, S.J., Shin, J., et al.: Supported core@shell electrocatalysts for fuel cells: close encounter with reality. Sci. Rep. 3, 1309 (2013)
Mazumder, V., Chi, M., More, K.L., et al.: Core/shell Pd/FePt nanoparticles as an active and durable catalyst for the oxygen reduction reaction. J. Am. Chem. Soc. 132, 7848–7849 (2010)
Kuttiyiel, K.A., Sasaki, K., Choi, Y.M., et al.: Nitride stabilized PtNi core–shell nanocatalyst for high oxygen reduction activity. Nano Lett. 12, 6266–6271 (2012)
Zhang, Y., Chao, M., Yimei, X., et al.: Hollow core supported Pt monolayer catalysts for oxygen reduction. Catal. Today 202, 50–54 (2013)
Tan, C., Sun, Y., Zheng, J., et al.: A self-supporting bimetallic Au@Pt core–shell nanoparticle electrocatalyst for the synergistic enhancement of methanol oxidation. Sci. Rep. 7, 6347 (2017)
Song, H.M., Anjum, D.H., Sougrat, R., et al.: Hollow Au@Pd and Au@Pt core–shell nanoparticles as electrocatalysts for ethanol oxidation reactions. J. Mater. Chem. 22, 25003–25010 (2012)
Xie, W., Herrmann, C., Kömpe, K., et al.: Synthesis of bifunctional Au/Pt/Au core/shell nanoraspberries for in situ SERS monitoring of platinum-catalyzed reactions. J. Am. Chem. Soc. 133, 19302–19305 (2011)
Jung, K.N., Hwang, S.M., Park, M.S., et al.: One-dimensional manganese–cobalt oxide nanofibres as bi-functional cathode catalysts for rechargeable metal–air batteries. Sci. Rep. 5, 7665 (2015)
Sumboja, A., Ge, X., Goh, F.W.P., et al.: Manganese oxide catalyst grown on carbon paper as an air cathode for high-performance rechargeable zinc–air batteries. ChemPlusChem 80, 1341–1346 (2015)
Post, J.E.: Manganese oxide minerals: crystal structures and economic and environmental significance. Proc. Natl. Acad. Sci. 96, 3447–3454 (1999)
Lima, F.H.B., Calegaro, M.L., Ticianelli, E.A.: Electrocatalytic activity of manganese oxides prepared by thermal decomposition for oxygen reduction. Electrochim. Acta 52, 3732–3738 (2007)
Cheng, F., Su, Y., Liang, J., et al.: MnO2-based nanostructures as catalysts for electrochemical oxygen reduction in alkaline media. Chem. Mater. 22, 898–905 (2010)
Morozan, A., Jousselme, B., Palacin, S.: Low-platinum and platinum-free catalysts for the oxygen reduction reaction at fuel cell cathodes. Energy Environ. Sci. 4, 1238–1254 (2011)
Mao, L., Zhang, D., Sotomura, T., et al.: Mechanistic study of the reduction of oxygen in air electrode with manganese oxides as electrocatalysts. Electrochim. Acta 48, 1015–1021 (2003)
Mainar, A.R., Colmenares, L.S., Leonet, O., et al.: Manganese oxide catalysts for secondary zinc air batteries: from electrocatalytic activity to bifunctional air electrode performance. Electrochim. Acta 217, 80–91 (2016)
Byon, H.R., Suntivich, J., Horn, Y.S.: Graphene-based non-noble-metal catalysts for oxygen reduction reaction in acid. Chem. Mater. 23, 3421–3428 (2011)
Mao, L., Sotomura, T., Nakatsu, K., et al.: Electrochemical characterization of catalytic activities of manganese oxides to oxygen reduction in alkaline aqueous solution. J. Electrochem. Soc. 149, A504–A507 (2002)
Xiao, J., Wan, L., Wang, X., et al.: Mesoporous Mn3O4–CoO core–shell spheres wrapped by carbon nanotubes: a high performance catalyst for the oxygen reduction reaction and CO oxidation. J. Mater. Chem. A 2, 3794–3800 (2014)
Cao, Y., Wei, Z., He, J., et al.: α-MnO2 nanorods grown in situ on graphene as catalysts for Li-O2 batteries with excellent electrochemical performance. Energy Environ. Sci. 5, 9765–9768 (2012)
Ye, Y., Kuai, L., Geng, B.: A template-free route to a Fe3O4–Co3O4 yolk–shell nanostructure as a noble-metal free electrocatalyst for ORR in alkaline media. J. Mater. Chem. 22, 19132–19138 (2012)
Ciston, J., Si, R., Rodríguez, J.A., et al.: Morphological and structural changes during the reduction and reoxidation of CuO/CeO2 and Ce1–xCuxO2 nanocatalysts: In situ studies with environmental TEM, XRD, and XAS. J. Phys. Chem. C 115, 13851–13859 (2011)
Liu, K., Song, Y., Chen, S.: Defective TiO2-supported Cu nanoparticles as efficient and stable electrocatalysts for oxygen reduction in alkaline media. Nanoscale 7, 1224–1232 (2015)
Lee, D.U., Scott, J., Park, H.W., et al.: Morphologically controlled Co3O4 nanodisks as practical Bi-functional catalyst for rechargeable zinc–air battery applications. Electrochem. Commun. 43, 109–112 (2014)
Landon, J., Demeter, E., İnoğlu, N., et al.: Spectroscopic characterization of mixed Fe–Ni oxide electrocatalysts for the oxygen evolution reaction in alkaline electrolytes. ACS Catal. 2, 1793–1801 (2012)
Li, X., Li, Z., Yang, X., et al.: First-principles study of the initial oxygen reduction reaction on stoichiometric and reduced CeO2 (111) surfaces as a cathode catalyst for lithium-oxygen batteries. Mater. Chem. A 5, 3320–3329 (2017)
Liu, P., Hao, Q., Xia, X., et al.: 3D hierarchical mesoporous flowerlike cobalt oxide nanomaterials: controllable synthesis and electrochemical properties. J. Phys. Chem. C 119, 8537–8546 (2015)
Biswas, S., Dutta, B., Kanakkithodi, A.M., et al.: Heterogeneous mesoporous manganese/cobalt oxide catalysts for selective oxidation of 5-hydroxymethylfurfural to 2,5-diformylfuran. Chem. Commun. 53, 11751–11754 (2017)
Melaet, G., Raiston, W.T., Li, C.S., et al.: Evidence of highly active cobalt oxide catalyst for the Fischer–Tropsch synthesis and CO2 hydrogenation, evidence of highly active cobalt oxide catalyst for the Fischer–Tropsch synthesis and CO2 hydrogenation. J. Am. Chem. Soc. 136, 2260–2263 (2014)
Chen, Z., Duan, Z., Wang, Z., et al.: Amorphous cobalt oxide nanoparticles as active water-oxidation catalysts. ChemCatChem 9, 3641–3645 (2017)
Zhao, J., He, Y., Chen, Z., et al.: Engineering the surface metal active sites of nickel cobalt oxide nanoplates toward enhanced oxygen electrocatalysis for Zn–air battery. ACS Appl. Mater. Interfaces. 11, 4915–4921 (2011)
Gwon, O., Kim, C., Kwon, O., et al.: An efficient oxygen evolution catalyst for hybrid lithium air batteries: almond stick type composite of perovskite and cobalt oxide. J. Electrochem. Soc. 163, A1893–A1897 (2016)
Xiao, J., Kuang, Q., Yang, S., et al.: Surface structure dependent electrocatalytic activity of Co3O4 anchored on graphene sheets toward oxygen reduction reaction. Sci. Rep. 3, 2300 (2013)
Cordoba, M., Miranda, C., Lederhos, C., et al.: Catalytic performance of Co3O4 on different activated carbon supports in the benzyl alcohol oxidation. Catalysts 7, 384–395 (2017)
Khan, M.A.N., Klu, P.K., Wang, C., et al.: Metal-organic framework-derived hollow Co3O4/carbon as efficient catalyst for peroxymonosulfate activation. Chem. Eng. J. 363, 234–246 (2019)
Yoon, T.H., Park, Y.J.: Carbon nanotube/Co3O4 composite for air electrode of lithium–air battery. Nanoscale Res. Lett. 7, 28–31 (2012)
Li, T., Lu, Y., Zhao, S., et al.: Co3O4-doped Co/CoFe nanoparticles encapsulated in carbon shells as bifunctional electrocatalysts for rechargeable Zn–air batteries. J. Mater. Chem. A 6, 3730–3737 (2018)
Lee, C.K., Park, Y.J.: Carbon and binder-free air electrodes composed of Co3O4 nanofibers for Li–air batteries with enhanced cyclic performance. Nanoscale Res. Lett. 10, 319–326 (2015)
Kim, J.Y., Park, Y.J.: Carbon nanotube/Co3O4 nanocomposites selectively coated by polyaniline for high performance air electrodes. Sci. Rep. 7, 8610–8620 (2015)
Liu, Q., Wang, L., Liu, X., et al.: N-doped carbon-coated Co3O4 nanosheet array/carbon cloth for stable rechargeable Zn–air batteries. Sci. China Mater. 62, 624–632 (2019)
Li, X., Xu, N., Li, H., et al.: 3D hollow sphere Co3O4/MnO2-CNTs: Its high-performance Bi-functional cathode catalysis and application in rechargeable zinc–air battery. Green Energy Environ. 2, 316–328 (2017)
Park, C.S., Kim, K.S., Park, Y.J.: Carbon-sphere/Co3O4 nanocomposite catalysts for effective air electrode in Li/air batteries. J. Powder Sources 244, 72–79 (2013)
Sunarso, J., Torriero, A.A.J., Zhou, W., et al.: Oxygen reduction reaction activity of La-based perovskite oxides in alkaline medium: a thin-film rotating ring-disk electrode study. J. Phys. Chem. C 116, 5827–5834 (2012)
Yuasa, M., Nishida, M., Kida, T., et al.: Bi-functional oxygen electrodes using LaMnO3/LaNiO3 for rechargeable metal–air batteries. J. Electrochem. Soc. 158, A605–A610 (2011)
Takeguchi, T., Yamanaka, T., Takahashi, H., et al.: Layered perovskite oxide: a reversible air electrode for oxygen evolution/reduction in rechargeable metal–air batteries. J. Am. Chem. Soc. 135, 11125–11130 (2013)
Dai, L., Xue, Y., Qu, L., et al.: Metal-free catalysts for oxygen reduction reaction. Chem. Rev. 115, 4823–4892 (2015)
Wang, D., Chen, X., Evans, D.G., et al.: Well-dispersed Co3O4/Co2MnO4 nanocomposites as a synergistic bifunctional catalyst for oxygen reduction and oxygen evolution reactions citation formats. Nanoscale 5, 5312–5315 (2013)
Li, C., Han, X., Cheng, F., et al.: Phase and composition controllable synthesis of cobalt manganese spinel nanoparticles towards efficient oxygen electrocatalysis. Nat. Comm. 6, 7345–7352 (2015)
Jadhav, H.S., Kalubarme, R.S., Roh, J.W., et al.: Facile and cost effective synthesized mesoporous spinel NiCo2O4 as catalyst for non-aqueous lithium–oxygen batteries. J. Electrochem. Soc. 161, A2188–A2196 (2014)
Maiyalagan, T., Jarvis, K.A., Therese, S., et al.: Spinel-type lithium cobalt oxide as a bifunctional electrocatalyst for the oxygen evolution and oxygen reduction reactions. Nat. Commun. 5, 3949–3955 (2014)
Liu, Y., Li, J., Li, W., et al.: Spinel LiMn2O4 nanoparticles dispersed on nitrogen-doped reduced graphene oxide nanosheets as an efficient electrocatalyst for aluminium–air battery. Int. J. Hydrog. Energy 40, 9225–9234 (2015)
Mohamed, S.G., Tsai, Y.Q., Chen, C.J., et al.: Ternary spinel MCo2O4 (M = Mn, Fe, Ni, and Zn) porous nanorods as bifunctional cathode materials for lithium-O2 batteries. ACS Appl. Mater. Interfaces 7, 12038–12046 (2015)
Ge, X., Liu, Y., Goh, F.W.T., et al.: Dual-phase spinel MnCo2O4 and spinel MnCo2O4/nanocarbon hybrids for electrocatalytic oxygen reduction and evolution. ACS Appl. Mater. Interfaces 6, 12684–12691 (2014)
Zhang, H., Li, H., Wang, H., et al.: NiCo2O4/N-doped graphene as an advanced electrocatalyst for oxygen reduction reaction. J. Power Sources 280, 640–648 (2015)
Ning, R., Tian, J., Asiri, A.M., et al.: Spinel CuCo2O4 nanoparticles supported on N-doped reduced graphene oxide: a highly active and stable hybrid electrocatalyst for the oxygen reduction reaction. Langmuir 29, 13146–13151 (2013)
Kargar, A., Yavuz, S., Kim, T.K., et al.: Solution-processed CoFe2O4 nanoparticles on 3D carbon fiber papers for durable oxygen evolution reaction. ACS Appl. Mater. Interfaces 7, 17851–17856 (2015)
Barros, W.R.P., Wei, Q., Zhang, G., et al.: Oxygen reduction to hydrogen peroxide on Fe3O4 nanoparticles supported on printex carbon and graphene. Electrochim. Acta 162, 263–270 (2015)
Ferreroa, G.A., Fuertes, A.B., Sevilla, M., et al.: Efficient metal-free N-doped mesoporous carbon catalysts for ORR by a template-free approach. Carbon 106, 179–187 (2016)
Niu, W., Li, L., Liu, X., et al.: Mesoporous N-doped carbons prepared with thermally removable nanoparticle templates: an efficient electrocatalyst for oxygen reduction reaction. J. Am. Chem. Soc. 137, 5555–5562 (2015)
Terrones, M., Botello, M.A.R., Delgado, J.C., et al.: Graphene and graphite nanoribbons: morphology, properties, synthesis, defects and applications. Nano Today 5, 351–372 (2010)
Zhang, Y., Ge, J., Wang, L., et al.: Manageable N-doped graphene for high performance oxygen reduction reaction. Sci. Rep. 3, 2771 (2013)
Zitolo, A., Goellner, V., Armel, V., et al.: Identification of catalytic sites for oxygen reduction in iron- and nitrogen-doped graphene materials. Nat. Mater. 14, 937–942 (2015)
Wan, K., Yu, Z.P., Li, X.H., et al.: Ph effect on electrochemistry of nitrogen-doped carbon catalyst for oxygen reduction reaction. ACS Catal. 5, 4325–4332 (2015)
Ganesan, P., Prabu, M., Sanetuntikul, J., et al.: Cobalt sulfide nanoparticles grown on nitrogen and sulfur codoped graphene oxide: an efficient electrocatalyst for oxygen reduction and evolution reactions. ACS Catal. 5, 3625–3637 (2015)
Hou, Y., Wen, Z., Cui, S., et al.: An advanced nitrogen-doped graphene/cobalt-embedded porous carbon polyhedron hybrid for efficient catalysis of oxygen reduction and water splitting. Adv. Funct. Mater. 25, 872–882 (2015)
Hou, Y., Yuan, H., Wen, Z., et al.: Nitrogen-doped graphene/CoNi alloy encased within bamboo-like carbon nanotube hybrids as cathode catalysts in microbial fuel cells. J. Power Sources 307, 561–568 (2016)
Chowdhury, C., Datta, A.: Silicon-doped nitrogen-coordinated graphene as electrocatalyst for oxygen reduction reaction. J. Phys. Chem. C 122, 27233–27240 (2018)
García, M.A.M., Rees, N.V.: “Metal-free” electrocatalysis: Quaternary-doped graphene and the alkaline oxygen reduction reaction. Appl. Catal. A Gen. 553, 107–116 (2018)
Peng, H., Mo, Z., Liao, S., et al.: High performance Fe- and N-doped carbon catalyst with graphene structure for oxygen reduction. Sci. Rep. 3, 1765 (2013)
Liang, Y., Li, Y., Wang, H., et al.: Co3O4 nanocrystals on graphene as a synergistic catalyst for oxygen reduction reaction. Nat. Mater. 10, 780–786 (2011)
Zhang, T., He, C., Sun, F., et al.: Co3O4 nanoparticles anchored on nitrogen-doped reduced graphene oxide as a multifunctional catalyst for H2O2 reduction, oxygen reduction and evolution reaction. Sci. Rep. 7, 43638 (2017)
Kosasang, S., Ma, N., Phattharasupakun, N., et al.: Manganese oxide/reduced graphene oxide nanocomposite for high-efficient electrocatalyst towards oxygen reduction reaction. ECS Trans. 85, 1265–1276 (2018)
Moniruzzaman, M., Winey, K.I.: Polymer nanocomposites containing carbon nanotubes. Macromolecules 39, 5194–5205 (2006)
Planeix, J., Coustel, B., Brotons, C.V., et al.: Application of carbon nanotubes as supports in heterogeneous catalysis. J. Am. Chem. Soc. 116, 7935–7936 (1994)
Xu, N., Nie, Q., Luo, L., et al.: Controllable hortensia-like MnO2 synergized with carbon nanotubes as an efficient electrocatalyst for long-term metal–air batteries. ACS Appl. Mater. Interfaces 11, 578–587 (2019)
Shen, Y., Sun, D., Yu, L., et al.: A high-capacity lithium–air battery with Pd modified carbon nanotube sponge cathode working in regular air. Carbon 62, 288–295 (2013)
Ni, W., Liu, S., Fei, Y., et al.: Preparation of carbon nanotubes/manganese dioxide composite catalyst with fewer oxygen-containing groups for Li-O2 batteries using polymerized ionic liquids as sacrifice agent. ACS Appl. Mater. Interfaces 9, 14749–14757 (2017)
Lv, Q., Si, W., He, J., et al.: Selectively nitrogen-doped carbon materials as superior metal-free catalysts for oxygen reduction. Nat. Commun. 9, 3376 (2018)
Easton, E.B., Yang, R., Bonakdarpour, A., et al.: Thermal evolution of the structure and activity of magnetron-sputtered TM–C–N (TM = Fe, Co) oxygen reduction catalysts. Electrochem. Solid State Lett. 10, B6–B10 (2007)
Carbonell, S.R., Santoro, C., Serov, A., et al.: Transition metal–nitrogen–carbon catalysts for oxygen reduction reaction in neutral electrolyte. Electrochem. Commun. 75, 38–42 (2017)
Zhang, P., Sun, F., Xiang, Z., et al.: ZIF-derived in situ nitrogen-doped porous carbons as efficient metal-free electrocatalysts for oxygen reduction reaction. Energy Environ. Sci. 7, 442–450 (2014)
Zhao, X., Zhao, H., Zhang, T., et al.: One-step synthesis of nitrogen-doped microporous carbon materials as metal-free electrocatalysts for oxygen reduction reaction. J. Mater. Chem. A 2, 11666–11671 (2014)
Wei, J., Hu, Y., Liang, Y., et al.: Nitrogen-doped nanoporous carbon/graphene nano-sandwiches: synthesis and application for efficient oxygen reduction. Adv. Funct. Mater. 25, 5768–5777 (2015)
Yan, X., Jia, Y., Yao, X.: Defects on carbons for electrocatalytic oxygen reduction. Chem. Soc. Rev. 47, 7628–7658 (2018)
Huang, B., Liu, Y., Huang, X., et al.: Multiple heteroatom-doped few-layer carbons for the electrochemical oxygen reduction reaction. J. Mater. Chem. A 6, 22277–22286 (2018)
Ikeda, T., Boero, M., Huang, S., et al.: Carbon alloy catalysts: active sites for oxygen reduction reaction. J. Phys. Chem. C 112, 14706–14709 (2008)
Paraknowitsch, J.P., Thomas, A.: Doping carbons beyond nitrogen: an overview of advanced heteroatom doped carbons with boron, sulfur and phosphorus for energy applications. Energy Environ. Sci. 6, 2839–2855 (2013)
Cui, H., Guo, Y., Guo, L., et al.: Heteroatom-doped carbon materials and their composites as electrocatalysts for CO2 reduction. J. Mater. Chem. A 6, 18782–18793 (2018)
Niu, Q., Chen, B., Guo, J., et al.: Flexible, porous, and metal–heteroatom-doped carbon nanofibers as efficient ORR electrocatalysts for Zn–air battery. Nano-Micro Lett. 11, 8 (2019)
Kim, D.W., Li, O.L., Saito, N.: Enhancement of ORR catalytic activity by multiple heteroatom-doped carbon materials. Phys. Chem. Chem. Phys. 17, 407–413 (2015)
Wang, Y., Hu, A.: Carbon quantum dots: synthesis, properties and applications. J. Mater. Chem. C 2, 6921–6939 (2014)
Zhang, P., Hu, Q., Yang, X., et al.: Size effect of oxygen reduction reaction on nitrogen-doped graphene quantum dots. RSC Adv. 8, 531–536 (2018)
Tam, T.V., Kang, S.G., Babu, K.F., et al.: Synthesis of B-doped graphene quantum dots as a metal-free electrocatalyst for the oxygen reduction reaction. J. Mater. Chem. A 5, 10537–10543 (2017)
Furukawa, H., Cordova, K.E., Keeffe, M.O., et al.: The chemistry and applications of metal-organic frameworks. Science 341, 1230444 (2013)
Li, L., He, J., Wang, Y., et al.: Metal-organic frameworks: a promising platform for constructing non-noble electrocatalysts for the oxygen-reduction reaction. J. Mater. Chem. A 7, 1964–1988 (2019)
Gonen, S., Lori, O., Tagurib, G.C., et al.: Metal organic frameworks as a catalyst for oxygen reduction: an unexpected outcome of a highly active Mn-MOF-based catalyst incorporated in activated carbon. Nanoscale 10, 9634–9641 (2018)
Zhao, X., Pattengale, B., Fan, D., et al.: Mixed-node metal-organic frameworks as efficient electrocatalysts for oxygen evolution reaction. ACS Energy Lett. 3, 2520–2526 (2018)
Mori, R.: Electrochemical properties of a rechargeable aluminum–air battery with a metal-organic framework as air cathode material. RSC Adv. 7, 6389–6395 (2017)
Wang, A., Li, J., Zhang, T.: Heterogeneous single-atom catalysis. Nat. Rev. Chem. 2, 65–81 (2018)
Zang, W., Sumboja, A., Ma, Y., et al.: Single Co atoms anchored in porous N-doped carbon for efficient zinc–air battery cathodes. ACS Catal. 8, 8961–8969 (2018)
Jia, N., Xu, Q., Zhao, F., et al.: Fe/N codoped carbon nanocages with single-atom feature as efficient oxygen reduction reaction electrocatalyst. ACS Appl. Energy Mater. 1, 4982–4990 (2018)
He, P., Yonggang, W., Zhou, H.: Titanium nitride catalyst cathode in a Li–air fuel cell with an acidic aqueous solution. Chem. Commun. 47, 10701–10703 (2011)
Lin, C., Li, X., Shinde, S.S., et al.: Long-life rechargeable Zn air battery based on binary metal carbide armored by nitrogen-doped carbon. ACS Appl. Energy Mater. 2, 1747–1755 (2019)
Mori, R.: Suppression of byproduct accumulation in rechargeable aluminum–air batteries using non-oxide ceramic materials as air cathode materials. Sustain. Energy Fuels 1, 1082–1089 (2017)
Mori, R.: Semi-solid-state aluminium–air batteries with electrolytes composed of aluminium chloride hydroxide with various hydrophobic additives. Phys. Chem. Chem. Phys. 20, 29983–29988 (2018)
Bakkar, A., Neuvert, V.: Electrodeposition and corrosion characterisation of micro- and nano-crystalline aluminium from AlCl3/1-ethyl-3-methylimidazolium chloride ionic liquid. Electrochim. Acta 103, 211–218 (2013)
Gelman, D., Shvartsev, D.B., Ein, E.Y.: Aluminum–air battery based on an ionic liquid electrolyte. J. Mater. Chem. A 2, 20237–20242 (2014)
Bogolowski, N., Drillet, J.F.: An electrically rechargeable Al–air battery with aprotic ionic liquid electrolyte. ECS Trans. 75, 85–92 (2017)
Sun, X.G., Fang, Y., Jiang, X., et al.: Polymer gel electrolytes for application in aluminum deposition and rechargeable aluminum ion batteries. Chem. Commun. 52, 292–295 (2016)
Nakayama, Y., Senda, Y., Kawasaki, H., et al.: Sulfone-based electrolytes for aluminium rechargeable batteries. Phys. Chem. Chem. Phys. 17, 5758–5766 (2015)
Gonzalo, C.P., Torriero, A.A.J., Forsyth, M., et al.: Redox chemistry of the superoxide ion in a phosphonium-based ionic liquid in the presence of water. J. Phys. Chem. Lett. 4, 1834–1837 (2013)
Wang, H., Gu, S., Bai, Y., et al.: High-voltage and noncorrosive ionic liquid electrolyte used in rechargeable aluminum battery. ACS Appl. Mater. Interfaces 8, 27444–27448 (2016)
Zein, S., Abedin, E.I., Giridhar, P., et al.: Electrodeposition of nanocrystalline aluminium from a chloroaluminate ionic liquid. Electrochem. Commun. 12, 1084–1086 (2014)
Eiden, P., Liu, Q., Sherif, Z.E.A., et al.: An experiment and theoretical study of the aluminium species present in mixtures of AlCl3 with the ionic liquids [BMP]Tf2N and [EMIm]Tf2N. Chem. Eur. J. 15, 3426–3434 (2009)
Abood, H.M.A., Abbott, A.P.A., Ballantyne, B.D., et al.: Do all ionic liquids need organic cations? Characterisation of [AlCl2n Amide] + AlCl4− and comparison with imidazolium based systems. Chem. Commun. 47, 3523–3525 (2011)
Bogolowski, N., Drillet, J.F.: Activity of different AlCl3-based electrolytes for the electrically rechargeable aluminium–air battery. Electrochim. Acta 274, 353–358 (2018)
Katayama, Y., Wakayama, T., Tachikawa, N., et al.: Electrochemical study on aluminum speciation in lewis acidic chloroaluminate-bis (trifluoromethylsulfonyl) amide mixed ionic liquids. Electrochemistry 86, 42–45 (2018)
Agiorgousis, M.L., Sun, Y.Y., Zhang, S.: The role of ionic liquid electrolyte in an aluminum-graphite electrochemical cell. ACS Energy Lett. 2, 689–693 (2017)
Angell, M., Pan, C.J., Rong, Y., et al.: High coulombic efficiency aluminum-ion battery using an AlCl3-urea ionic liquid analog electrolyte. Proc. Natl. Acad. Sci. USA 114, 834–839 (2017)
Acknowledgements
The author wishes to express thanks to Dr. Hideki Yoshioka and Mr. Kazuo Sakai for their helpful discussions.
Author information
Authors and Affiliations
Corresponding author
Ethics declarations
Conflict of interest
The author has no conflict of interest.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Mori, R. Recent Developments for Aluminum–Air Batteries. Electrochem. Energ. Rev. 3, 344–369 (2020). https://doi.org/10.1007/s41918-020-00065-4
Received:
Revised:
Accepted:
Published:
Issue Date:
DOI: https://doi.org/10.1007/s41918-020-00065-4