Abstract
Due to the significant friction-reduction and anti-wear properties of nano particle, nano copper oxide (CuO) particle decorating on boron nitride nanosheets (BNNS) nanocomposites are fabricated with polydopamine (PDA) as the linking agent. The structural and morphological characteristics of the CuO@BNNS composite are characterized by scanning electron microscopy (SEM), X-ray diffraction patterns, fourier transform infrared spectroscopy and thermogravimetric analysis. The synergistic effect of CuO and BNNS on extreme pressure of lubrication oil are investigated. A four-ball tribometer is adopted to investigate the tribological behaviors of the as-prepared oil with different additives. Optical microscope and SEM are used to analyze the topography of worn surface. Energy dispersive spectroscopy is adopted to investigate the element distribution on worn surface. The results demonstrate that the CuO@BNNS nanoparticle could effectively improve the friction-reduction and anti-wear properties of the paraffin liquid, compared to paraffin liquid containing modified CuO (f-CuO) or PDA-BNNS respectively. The worn surface of steel ball presents smooth morphology for oil containing CuO@BNNS, contrast to oil containing f-CuO or PDA-BNNS respectively. With the tribo-film formation on the worn surface, the elements distribute uniformly on the worn surface for oil containing CuO@BNNS. Compared to lower load, the effect of load-carrying capacity and easy-shear property of CuO@BNNS outstand under 392 N, which results in the smooth worn surface compared to oil containing other additives.
Article Highlights
CuO@BNNS hybrid nanoparticle was prepared with a simple and mild method.
CuO@BNNS presents superior anti-friction and anti-wear properties due to the synergistic effect of nanoparticle.
The result obtained in the paper promotes the application of h-BN based nanocomposites in tribology.
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Avoid common mistakes on your manuscript.
1 Introduction
In recent years, scientist has focused on the uses of hybrid nanocomposites as lubricant additives, such as composites based on graphene, MoS2, WS2 and h-BN, which can play a great role on friction-reduction and anti-wear properties [1,2,3,4]. In modern equipment and manufacturing industry field, to some extent, production cost and service life of equipment are restricted by lubricant system. As the critical component in lubricant oil, additive plays an important role on the tribological performance under the complex conditions. It is worthwhile exploring the tribological properties of different combinations with various nano particles. In the past few years, lots of researches have carried out on preparation of two-dimensional (2D) layered materials for the friction-reduction and anti-wear property in fluid lubricants [5,6,7]. The excellent tribological properties can be attributed to the weak Vander Waals force among layers and the formation of a robust tribo-film on friction pairs.
With the similar layered structure to graphene, h-BN maintaining lots of excellent properties, such as hear-resistant property, electrical insulation and low interlaminar shear stress, has been studied on tribological properties in different areas [8,9,10,11,12,13,14,15,16,17,18]. As the traditional lubricant additive, h-BN can improve the tribological properties of lubricant composites [8,9,10,11,12,13] or oil [14,15,16,17,18]. Based on the results [14,15,16,17,18], the functionalized h-BN presents obviously friction-reduction and wear-resistance compared to the h-BN without any surface treatment. And the similar result also confirms the excellent lubrication and anti-wear properties of alkyl-functionalized h-BN, compared with MoS2 [15, 21]. Bondarev found that the h-BN with different morphologies presented different tribological performance. And the correlation between mechanical properties and the friction behavior was proposed through TEM [19].
However, as the elevation of the synthesis tactics for nanocomposites, many researches have demonstrated hybrid nano-material can effectively enhance the lubrication properties, due to the synergistic effect [3, 4, 19,20,21,22,23,24,25]. The decoration of Fe3O4 on h-BN can promote the dispersion of Fe3O4 in oil. And this can effectively improve the lubricant effect of nano particle and facilitate the formation of tribo-film on the worn surface [21]. During the friction, Fe3O4 on h-BN surface can act a part in roll lubrication and formation of tribo-film as molecular bear and active substance. Sahoo [23] investigated the tribological properties of h-BN modified with GO through covalent interaction. Similar results showed that the covalent modification endowed h-BN superior dispersion in oil, which resulted in the excellent tribological performance. Apart from nano particle, the synergetic effect between ionic liquid and BN as oil additive is also explored by Lopez’s group [24]. Clearly, the cooperation with nano particle is an effective way to enhance the tribological performance of h-BN based composites. The synergetic effect between h-BN and nanoparticle can be achieved through the combination of nano particles with different dimensions.
Nano Cu or CuO has been adopted as lubricant additive in many studies. Researches have demonstrated that Cu or CuO on lamellar structure can markedly enhance the wear-resistance of lubricant oil or self-lubricant composites [2, 25,26,27,28,29,30]. Due to the good dispersion ability of Cu@WS2 in polyalkylene glycol (PAG), the PAG oil showed better friction-reduction and anti-wear properties than WS2 and Cu nanoparticles. The uniform distribution of Cu on the WS2 endowed the good adsorption on the friction pairs, which promoted the tribo-chemical reaction and formation of tribo-film [2]. And this is also be confirmed in the lubricant oil system containing Cu@GO [26, 27]. Similarly, the polyimide composite reinforced with CuO@g-C3N4 presents superior wear-resistance capacity due to the combination with CuO@g-C3N4 hybrid composite [31]. As the combination with CuO, the anti-wear property of mineral oil containing CuO and h-BN as additives is greatly improved. Result showed that with the sliding process, the steel-steel contact at the beginning was protected by the formation of cooper tribo-film on the friction pairs [7, 28]. With the collaboration of CuO nano particle, tribological properties of nano diamond also performs well as oil additive [7]. For recent years, the effect of exfoliated h-BN nano sheets (BNNS) decorating with CuO were examined at catalytic degradation [32] and electrochemical detection [33]. The CuO@BNNS composite presents better catalytic activity for bisphenol A removal and electrochemical detection for L-cysteine. However, there are few studies on effect of combinated CuO@BNNS on tribological properties as lubricant oil.
During the traditional preparation tactics of CuO@h-BN, the calcination or hydro-thermal will inevitably result in the agglomeration of the nano h-BN, which is not desired for tribological application. Therefore, an intermediate that connect layered material and nano particle is necessary. As a neurotransmitter secreted by human being, dopamine plays an important role in the preparation of biomimetic materials. Apart from that, polydopamine (PDA) can spread on the surface of h-BN during polymerization due to the weak electrostatic interaction with the heteroatom [34]. Then the polydopamine uncovered on the h-BN surface becomes the gathering center of meatal ion or compound. And this will strength the interaction between CuO and h-BN. However, the tribological properties of BNNS decorated with CuO has not been repored.
Based on the above result, in this paper, CuO@BNNS composite was fabricated with a simple and mild method firstly. Then, suspension abilities of the obtained lubricant oil containing CuO, BNNS and CuO@BNNS were explored. In Sect. 3, the tribological properties of as-obtained paraffin liquid lubricant oil with different additives were investigated on a four-ball tribometer. After that, the element distribution of hybrid composite was investigated. Then the worn surface and lubricant mechanism were analyzed and discussed in the last section.
2 Materials and experimentation
2.1 Material
h-BN nanosheets (50 nm) were purchased from Shanghai Chaowei nano technology Co., Ltd. (Shanghai, China). Dopamine hydrochloride and CuO(40nm) were provided by Mclin Chemical reagent Co., Ltd. (Shanghai, China) and the absolute ethanol were obtained by Tianjin Oubokai Chemical Reagent Co., Ltd. (Tianjin, China). The liquid paraffin was supplied by Yantai Shuangshuang Chemical Co., Ltd. (Yantai, China). Silane coupling agent (KH550) was supplied by Runxiang Chemical Co., Ltd. (Chengdu, China).
2.2 Preparation of h-BN nano sheet (BNNS)
BNNS was prepared by ultrasonic exfoliation of pristine h-BN powder with the help of ultrasonic disrupter. In the experiment, 2 g of pristine h-BN was added in 100 mL isopropanol, followed by sonication at the power of 550 W for 6 h at 10 ℃. Then, the emulsion was settled down for 2 h. After stratification of emulsion, the upper is centrifugated at 4000 r/min. Then the upper system become slightly transparent and precipitate at the bottom are multilayer h-BN. The upper system is poured into suitable amount of water and frozen to dry.
2.3 Preparation of PDA-BNNS
The synthesis of PDA-BNNS was performed with dopamine as described in reference [34]. Following dopamine hydrochloride added to the tris solution, BNNS powder was added quickly to the mixed solution with stirring (10 min). The final mixture was ultrasonically treated for 3 h and equilibrated at 60 ℃ for 24 h. The mixture was filtered with microfiltration membrane and washed with deionized water several times. Finally, the grey powder was frozen to dry.
2.4 Preparation CuO@BNNS hybrid nanocomposites
The CuO@BNNS hybrid was prepared with the similar method in the reference [34]. 0.3 g PDA-BNNS was added into to 50 mL of DMF utilizing ultrasonic treatment for 2 h. After that 0.1 g f-CuO (modified with KH550) was added. Finally, the suspension stirs for another 6 h at 100 ℃. The mixture was filtrated and washed with deionized water and anhydrous ethanol several times, and the products were treated with filtration and then frozen to dry. The whole preparation process was illustrated in Fig. 1.
2.5 Preparation of lubricant oil samples
A certain amount of the obtained modified CuO, PDA-BNNS and CuO@BNNS was poured into paraffin liquid. Then the mixture stirs violently. And then oil mixtures are mixed well under with sonic water bath for 2 h under 25 ℃ to form the homogenous oil system before tribo-test. The weight concentrations of additives in the oils were 0.05 wt% compared to paraffin liquid.
2.6 Tribological property test
The tribological properties of the lubricant oils were conducted on a four-ball tribo-test machine MMW1 (Jinan Shidai assay instrument machine Co., Ltd). Due to put focus on the effect of nanocomposites on extreme pressure property, the tribological test condition was set as following. The rotation speed was 1200 r/min, the load was 100, 200, 300 and 392 N, the test duration time is 60 min. The balls used in the test was made of GCr15 bearing steel with a hardness of 62 HRC and a diameter of 12.7 mm. Each sample was repeated at least for 3 times. Before ever test, the steel ball should be clean with petroleum ether and acetone.
2.7 Characterization
Fourier transform infrared spectra (FT-IR) was performance on FT-IR-650(Guangdong, China) spectrometer in wavenumber range of 400–4000 cm−1. The X-ray diffraction (XRD) pattern was performance on a Bruker D2 phaser machine (30 kV, 10 mA) with a 2θ angle ranging from 5° to 60° and a scan rate of 5° min−1 with Cu Ka radiation (k = 0.154 nm) (Bruker, Germany). The topography and composition of nano composites was probed using a SU8020 scanning electron microscopy (SEM) with 3 kV acceleration voltage (Hitachi, Japan). Thermogravimetric analysis (TGA) was conducted on a Netzsch-TG209F3(Netzsch, Germany) thermogravimetric analyzer under nitrogen atmosphere from 50 to 900 ℃ with a heating range of 10 ℃.min−1. The worn wear scars were measured with Olympus optical DSX-CB microscope and Zeiss Ultra-55 SEM with 20 kV acceleration voltage (Olympus, Japan).
3 Results and discussion
3.1 FT-IR analysis
FT-IR was used to investigate the modification of f-CuO, PDA-BNNS and the hybridization between f-CuO with PDA-BNNS. FT-IR spectrum of PDA-BNNS, f-CuO and CuO@BNNS are depicted in Fig. 2. As drawn in the picture, the obviously characteristic are easy to distinguish. The prominent absorption peak at about 483 cm−1 and 532 cm−1, can be attributed to the characteristic peak of the stretching vibrations along (101) plane of f-CuO. The peak at 2849 cm−1 and 2923 cm−1 can be attributed to the vibration of C=C in the benzene ring structure, which demonstrates the successful preparation of the PDA-BNNS. Similar to peak of f-CuO, the peak at 483 cm−1 and 532 cm−1 of CuO@BNNS is the direct proof for the successful hybridization. Meanwhile, the peak at 817 cm−1 and 1371 cm−1 can be attributed to the B-N stretch movement. And the peak at 3401 cm−1 vest in the movement of -OH bond.
3.2 TGA analysis
TGA was used to confirm the modification of pristine h-BN, f-CuO, PDA-BNNS and CuO@BNNS. As plotted in Fig. 3, there is no distinctive weight loss of pristine h-BN and BNNS under N2 atmosphere, which correspond to its good heat-resistance properties. However, PDA-BNNS and CuO@BNNS present weight loss about 5% and 9% under 900 ℃. According to the TGA curve of PDA-BNNS, the weight loss of 5% can be ascribed to the degradation of PDA. In contrast, the mass loss of CuO@BNNS is higher than PDA-BNNS, due to the decomposition of coupling agent KH550 grafted on nano f-CuO at about 300 ℃. Thus, the modification of CuO nano particle with KH550 and the successful preparation of hybridization of CuO@BNNS are confirmed, combined with the FT-IR spectrum.
3.3 XRD analysis
X-ray diffraction (XRD) curves of the pristine h-BN, f-CuO, PDA-BNNS and CuO@BNNS composites are plotted in Fig. 4. In order to analysis the variation, the intensity of the Y value is normalized. As depicted in Fig. 4, it is clear that the obtained PDA-BNNS and CuO@BNNS present the similar peaks with the raw material at 26.7° and 41.6°, which can be attributed to (002) and (100) planes of hexagonal crystal structure of h-BN according to the standard card of JCPDS card 34–042. The dramatical peak narrowing at 26.7° can be attributed to the sonic effect during the preparation of BNNS nano sheet, which means the obtain of few-layered structure compared to the raw h-BN. And the weaken of the intensity for CuO@BNNS maybe resulted from the surface modified with nano f-CuO [13]. Meanwhile, the peak at 32.6°, 35.6°, 38.8°, 49.02° in pattern of CuO@BNNS are totally aligned with peaks in pattern of f-CuO. This indicates the CuO@BNNS nanocomposite is synthesized.
3.4 SEM analysis
Morphological characteristics of the prepared hybrid composite were characterized by SEM. As depicted in Fig. 5, the bulk CuO is consist of many nanoparticles with diameter obout 40 nm. And the morphology of h-BN displays lumpy and multi-layer stacking structure. Compared to h-BN drawn in Fig. 5c, d, BNNS shows few-layered structure in Fig. 5f. This can be ascribed to the effect of exfoliation during ultrasonic treatment. And the exfoliation happens along (002) face, based on the XRD analysis. According to images of CuO@BNNS in Fig. 5g, h, the rough surface of BNNS exactly illustrated the nanoparticle decoration on BNNS. To further identify the homogeneity of nanocomposite, element distribution of composite analysis was carried out through EDS mapping image corresponding to the area in red rectangle, as presented in Fig. 6. The element dispersion results show that copper, oxygen, boron and nitrogen elements evenly distributed in the composite, which demonstrated that the homogenous nano CuO@BNNS composites are obtained.
3.5 Dispersibility and tribological performance of oil
The lubricating oil is fabricated with 0.05% additives and 99.5% amount of paraffin liquid in ultrasound bath. Preventing from agglomeration of additives, the temperature of ultrasound bath was controlled below 20 ℃. Before the tribological test, all lubricating suspensions based on paraffin liquid with 0.05% additives were sonicated for 30 min. As depicted in Fig. 7, the additives can disperse well in liquid paraffin after sonication. And there is no obvious sedimentation in 3 days. The obvious sedimentation occurs after 5 days. And all the oil become transparent after 7 days. The tribological tests were conducted according to the conditons mentioned in 2.6 (tribological property test).
Figure 8 presents the average coefficient of friction and diameter of wear scar under different conditions. And Fig. 9 depicts the friction coefficient curves with the increasing of sliding time. As shown in Fig. 8, the friction coefficients climb up with the increase of load for each kind of lubricant oil system. Meantime, the oil containing CuO@BNNS presents the lowest friction coefficient, varying from 0.017 to 0.050. And friction coefficient displays more stable with small fluctuations as increasing sliding time for oil with CuO@BNNS, as presented in Fig. 9. By contrast, paraffin liquid without any additive shows the highest friction coefficient, varying from 0.038 to 0.083. In addition, friction coefficient of oil containing PDA-BNNS shows lower value than paraffin liquid, followed by that of f-CuO.
Figure 8 presents the average diameter of wear scar on the steel ball of different systems for reflection of wear rate. As expected, oil containing additive can work on friction coefficient reduction and anti-wear property. Oil containing CuO@BNNS exhibits the lowest average friction coefficient and diameter of wear spot on the steel ball, followed by f-CuO and PDA-BNNS. Statistically, compared with paraffin liquid, the average friction coefficient of oil containing CuO@BNNS, f-CuO and PDA-BNNS were reduced by 53%, 31% and 7% respectively under applied load of 100 N, reduced by 43%, 23% and 12% respectively under applied load of 200 N, reduced by 43%, 29% and 27% respectively under applied load of 300 N and reduced by 39%, 23% and 23% respectively under applied load of 392 N. And the lubricant abilities of PAD-BNNS can result in the few-layered structure exfoliated by sonification and functionalization of BNNS nanosheets.
As illustrated in Fig. 8, the diameter of wear spot becomes larger, as the increase of load, for different lubricant oils. The scar diameter of paraffin liquid shows the highest diameter value under different load condition, followed by PDA-BNNS and f-CuO according to the decreasing order. In summary, contrast to paraffin liquid, oil containing CuO@BNNS presents the best anti-wear properties with the smallest scar diameter on the steel ball. Meanwhile, the optical graphs of wear scar are presented in Fig. 1s (additional data are given in Online Resource ESM_1). On the whole, as the load increasing, the worn surfaces gradually become rougher. And the wear scars diameter become larger. For paraffin liquid, the clear rises and falls can be found on the ball under the condition of load 392 N, compared to the morphologies under other lower load. For oil containing PDA-BNNS or f-CuO, the worn surface appears lack of smoothness especially under higher load. The distinctive grooves in Fig. 1s can be easily distinguished under loads of 200 N, 300 N and 392 N, combined with the higher resolution image in Fig. 10. By contrast, the smooth worn surface of oil containing CuO@BNNS demonstrates the better anti-wear property. It is clear that worn surface of paraffin liquid presents lots of grooves and deep scrapes on the ball, as shown in Fig. 10. By comparison, oils containing additives present relatively smooth worn surface, especially for oil containing CuO@BNNS. From the worn surface in Fig. 10d, the worn surface of oil containing CuO@BNNS presents more smoother morphology than other oil system in generally. This can be result in the lubricant effect of nano f-CuO and PDA-BNNS in the oil. From the 3D profile image in Fig. 11, it is clear that the worn surface of oil containing CuO@BNNS present smaller and more smooth morphology, which is corresponding to the excellent friction reduction and anti-wear effect of CuO@BNNS.
3.6 Surface analysis
SEM pictures of worn surfaces after tribological test for these four kinds of oil are presented in Fig. 12. It is clear that worn surfaces of the four kinds of lubricant oil demonstrate different surface morphologies. As shown in Fig. 12a, there are remarkable lumpy transfer film and deep grooves on the surface for paraffin liquid. By contrast, the worn surfaces with nano additives present different topographies. There is no conspicuous large piece transformation of material on the ball. For worn surface of oil containing CuO@BNNS, there is no obvious scrapes on the surface. The smooth worn surface indicates the superior lubricant and anti-wear properties. And this can be resulted from the synergetic effect of nano f-CuO and PAD-BNNS in the sliding surface during tribological test. However, for worn surfaces of oil containing PDA-BNNS, the deep groove implies the wear and friction direction. For oil containing f-CuO, there only exist some particles and shallow scratch on the surface.
In order to analyze the synergetic effect and lubricant mechanism of oil with CuO@BNNS, the distribution of different elements on the worn surface were detected. The selected area was marked with rectangle shape, as shown in Fig. 12 D. As depicted in Fig. 13, the EDS mapping result implies that the element distribution of copper and boron demonstrate uniform on the worn surface, which exactly accounts for the smooth worn surface. And this also indicates that the nano f-CuO and PDA-BNNS play an important role on the tribological properties, during sliding process.
It is well known that the nanoparticle dispersibility in oil plays a great role on tribological performance. During sliding progress, nanoparticle dispersed in oil penetrates into the friction interface, which can improve the lubrication and anti-wear performance of lubricant oil. To further explore the lubricant mechanism, the schematic diagram of friction process is depicted in Fig. 14. During this test, the well-dispersed CuO@BNNS can easily penetrate into the sliding interface as illustrated in Fig. 14. In the sliding interface, the combined nanocomposites can effectively act as lubricant additive. By comparison, the rough worn surface is obtained for pure oil, as presented in Fig. 12a. Due to the easy shear property of PDA-BNNS, a lower coefficient of friction displays in the test as displayed in Figs. 8 and 12. With the friction proceeding, the CuO@BNN in the oil will fill up the grooves on the sliding interface due to the physical adsorption [34]. And then the nanocomposites act effectively. The nano BNNS arrays under the shear force along the friction interface. Thus, the friction pairs are separated by nano composites from direct contact during the friction process. Meanwhile, nano f-CuO can act as tiny bearing proposed by wang’ group between contact interfaces [35]. Therefore, CuO@BNNS plays a positive role on friction reduction and anti-wear, as illustrated in the SEM images. Simultaneously, the uniformly dispersed f-CuO nanoparticle can enhance the load carrying capacity of PDA-BNNS. In summary, the two aspect endow CuO@BNNS the significantly synergistic effect on tribological performance between f-CuO and PDA-BNNS.
4 Conclusion
Compared to the study on the effect of CuO, h-BN or BNNS on tribological property respectively [12, 13, 27,28,29], this paper aims at investigating the tribological performance of cooperation effect of f-CuO and PDA-BNNS used as lubrication oil additive. A synthesis route of CuO@BNNS was proposed, in this paper. From the tribological results, it is can be concluded that the synergistic effect happened during sliding, contrast to f-CuO or PDA-BNNS, respectively. The tribo-film present smooth morphology and uniform element distribution on the worn surface. And these conclusions can be drawn as following. Compared to h-BN, PDA-BNNS presents better dispersion property in paraffin oil, which plays important role on the tribological property. Oil containing with PDA-BNNS can effectively enhance the property of friction reduction. However, the worn surface still demonstrates deep grooves. For oil containing with f-CuO, the abrasion diameter and friction coefficient decreased compared to paraffin liquid. However, there exists distinctive aggregation on the worn surface. Due to the synergistic effect of f-CuO and PDA-BNNS, oil containing with CuO@BNNS presents outstanding anti-wear and friction reduction properties. The worn surface presents smooth morphology. Meantime, distribution of Cu, O, B and N on the worn surface are really uniform, which results in the above excellent tribological performance. And the lubrication mechanism was proposed to illustrate the excellent tribological process. In summary, the CuO@BNNS nanocomposite can be an appropriate candidate as an effective lubricating oil additive with good anti-friction and anti-wear properties in tribological applications. However, the dispersibility of nanocomposites should be enhanced to meet the demand of real application. And the surface modification by chemical bonding should be developed further.
Data availability statements
All data generated or analyzed during this study are included in this published article and its supplementary information files. The data used to support the findings of this study are available from the corresponding author upon request.
References
Zhu C, Yan Y, Wang F, Cui J, Zhao S, Gao A (2019) Facile fabrication of long-chain alkyl functionalized ultrafine reduced graphene oxide nanocomposites for enhanced tribological performance. RSC Adv 9:7324–7333
Xu Z, Lou W, Zhao G, Zheng D, Hao J, Wang X (2019) Cu nanoparticles decorated WS2 nanosheets as a lubricant additive for enhanced tribological performance. RSC Adv 9:7786–7794
Xie H, Dang S, Jiang B, Xiang L, Zhou S, Sheng H (2019) Tribological performances of SiO2/graphene combinations as water-based lubricant additives for magnesium alloy rolling. Appl Surf Sci 475:847–856
Song W, Yan J, Ji H (2019) Fabrication of GNS/MoS2 composite with different morphology and its tribological performance as a lubricant additive. Appl Surf Sci 469:226–235
White D, Chen M, Xiao C, Huang W, Sundararajan S (2018) Microtribological behavior of Mo and W nanoparticle/graphene composites. Wear 414:310–316
Rosenkranz A, Liu Y, Chen L (2020) 2D nano-materials beyond graphene: from synthesis to tribological studies. Appl Nanosci 10:3353–3388
Ankush R (2017) Tribological investigation of diamond nanoparticles for steel/steel contacts in boundary lubrication regime. Appl Nanosci 7:371–388
Huang Z, Zhao W, Zhao W, Ci X, Li W (2021) Tribological and anti-corrosion performance of epoxy resin composite coatings reinforced with differently sized cubic boron nitride (CBN) particles. Friction 9:104–118
Ye X, Wang M, Huang J, Ma Q, Jin Z (2020) Enhancing the tribological properties of boron nitride by bioinspired polydopamine modification. Appl Surf Sci 529:147054
Kuang W, Zhao B, Yang C, Ding W (2020) Effects of h-BN particles on the microstructure and tribological property of self-lubrication CBN abrasive composites. Cera Int 46:2457–2464
Chen W, Wang Z, Liu X, Jia J, Hua Y (2020) Effect of load on the friction and wear characteristics of Si3N4-hBN ceramic composites sliding against PEEK in artificial seawater. Tribol Int 141:4379–4389
Liu C, Tang G, Su F, Xu X, Li Z (2020) Functionalised h-BN as an effective lubricant additive in PAO oil for MoN coating sliding against Si3N4ball. Lubr Sci 1–10
Wu H, Yin S, Du Y, Wang L, Yang Y, Wang H (2020) Alkyl-functionalized boron nitride nanosheets as lubricant additives. ACS Appl Nano Mater 3:9108–9116
Ao X, Kong D, Zhang Z, Xiao X (2020) Enhancing recovery speed and anti-wear capability of high-temperature shape memory polymer with modified boron nitride nanoparticles. J Mater Sci 55:4292–4302
Zhao W, Zhao W, Huang Z, Liu G, Wu B (2019) Tribological performances of epoxy resin composite coatings using hexagonal boron nitride and cubic boron nitride nanoparticles as additives. Chem Phys Lett 732:136646136656
Bondarev A, Kovalskii A, Firestein K, Loginov P, Sidorenko D, Shvindina N (2018) Hollow spherical and nanosheet-base BN nanoparticles as perspective additives to oil lubricants: correlation between large-scale friction behavior and in situ TEM compression testing. Cera Int 44:6801–6809
Reyes L, Loganathan A, Boesl B, Agarwal A (2016) Effect of 2D boron nitride nanoplate additive on tribological properties of natural oils. Tribo Lett 64:41–48
Wu H, Yin S, Du Y, Wang L, Wang H (2020) An investigation on the lubrication effectiveness of MoS2 and BN layered materials as oil additives using block-on-ring tests. Tribol Int 151:106516–106525
Gong K, Wu X, Zhao G, Wang X (2017) Nanosized MoS2 deposited on graphene as lubricant additive in polyalkylene glycol for steel/steel contact at elevated temperature. Tribol Int 110:1–7
Liu Y, Mateti S, Li C, Liu X, Glushenkov A, Liu D (2018) Synthesis of composite nanosheets of graphene and boron nitride and their lubrication application in oil. Adv Eng Mater 20:1700488–1700494
Zhao J, Chen G, He Y, Li S, Duan Z, Li Y (2019) A novel route to the synthesis of an Fe3O4/h-BN 2D nanocomposite as a lubricant additive. RSC Adv 9:6583–6538
Min C, He Z, Song H, Liu D, Jia W, Qian J (2019) Fabrication of Novel CeO2/GO/CNTs ternary nanocomposites with enhanced tribological performance. Appl Sci 9:170–181
Samanta S, Sahoo R (2020) Covalently linked hexagonal boron nitride-graphene oxide nanocomposites as high-perforance oil-dispersible lubricant additives. ACS App Nano Mater 3:10941–10953
Nasser K, Lineiradel R, Lopez E, Fernandez J (2020) Synergistic effects of hexagonal boron nitride nanoparticles and phosphonium ionic liquids as hybrid lubricant additives. J Mol Liq 311:588–594
Min C, Jia W, He Z, Zhang K, Yang Y, Dong C (2020) Biomimetic synthesis of copper/polydopamine-functionalized oxygenated carbon nitride composites and their application as lubricants. Chem Sel 5:4839–4847
Zhang Y, Tang H, Ji X, Chen LC, Zhang LD (2013) Synthesis of reduced graphene oxide/Cu nanoparticle composites and their tribological properties. RSC Adv 3:26086–26093
Song H, Wang Z, Yang J, Jia X, Zhang Z (2017) Facile synthesis of copper/polydopamine functionalized graphene oxide nanocomposites with enhanced tribological performance. Chem Eng J 324:51–62
Gocman K, Kaldonski T, Kaldonski T, Pawlak Z (2020) An evaluation of lubricating properties of CuO and h-boron nitride (h-BN). Tribol Online 15:374–379
Vijay K, Anil D, Garg HC, Gitesh K (2020) Improving the tribological performance of canola oil by adding CuO nanoadditives for steel/steel contact. Mater Today Proc 28:1392–1396
Gitesh K, Hem CG, Ajay G (2019) Experimental investigation of tribological effect on vegetable oil with CuO nanoparticles and ZDDP additives. Ind Lubr Tribol 71:499–508
Wu L, Zhang Z, Yang M, Yuan J, Li P, Guo F (2019) Facile synthesis of CuO/g-C3N4 hybrids for enhancing the wear resistance of polyimide composite. Eur Polym J 116:463–470
Wen D, Xiao C, Kun Y, Lin A, Andrei V, Grzegorz L, Chao H, Lim T (2020) Enhanced activation of peroxydisulfate by CuO decorated on hexagonal boron nitride for bisphenol A removal. Chem Eng J 393:124714–124722
Sundramoorthy R (2020) Preparation of stable CuO/boron nitride nanocomposite modified electrode for selective electrochemical detection of L-cysteine. ChemistrySelect 5:9111–9118
Wan P, Zhao N, Qi F, Zhang B, Xiong H, Yuan H (2020) Synthesis of PDA-BN@f-Al2O3 hybrid for nanocomposite epoxy coating with superior corrosion protective properties. Prog Org Coat 146:105713–205726
Xue Q, Wang Q (1997) Wear mechanisms of polyetheretherketone composites filled with various kinds of SiC. Wear 213:54–58
Funding
This work was supported by the National Natural Science Foundation of China (No. 51805140, No. 21466009), the central government guides local science and technology development fund (No.216Z1202G, No. 206Z1201), Natural Science Foundation of Hebei Province. (E2018042121, E2020402009), Handan Municipal Science and Technology Bureau (19,422,111,008–26, 19,422,111,008–22).
Author information
Authors and Affiliations
Contributions
Writing-original draft, X. G., F.L., Y.W., Z.L., Y.W., Y.W.; Writing-review & editing, Y.W., Z.Z., H.F., Y.W.; Funding acquisition, Y.W., H.F., X.Z., P.L.; Investigation, X.G.; Validation, X.G.; Supervision, Y.W., H.F.
Corresponding authors
Ethics declarations
Conflict of interest
The authors declare no conflict of interest.
Consent for publication
The authors hereby consent to publication of this article in SN Applied Sciences.
Ethical approval
This article does not contain any studies with human participants performed by any of the authors.
Additional information
Publisher's Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary Information
Below is the link to the electronic supplementary material.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Gao, X., Wang, Y., Wang, Y. et al. Effect of copper oxide@boron nitride nanosheet hybrid nanocomposite on tribological properties of paraffin liquid. SN Appl. Sci. 4, 212 (2022). https://doi.org/10.1007/s42452-022-05094-w
Received:
Accepted:
Published:
DOI: https://doi.org/10.1007/s42452-022-05094-w