Abstract
Graphene with ultra-high carrier mobility and ultra-short photoresponse time has shown remarkable potential in ultrafast photodetection. However, the broad and weak optical absorption (∼2.3%) of monolayer graphene hinders its practical application in photodetectors with high responsivity and selectivity. Here we demonstrate that twisted bilayer graphene, a stack of two graphene monolayers with an interlayer twist angle, exhibits a strong light–matter interaction and selectively enhanced photocurrent generation. Such enhancement is attributed to the emergence of unique twist-angle-dependent van Hove singularities, which are directly revealed by spatially resolved angle-resolved photoemission spectroscopy. When the energy interval between the van Hove singularities of the conduction and valance bands matches the energy of incident photons, the photocurrent generated can be significantly enhanced (up to ∼80 times with the integration of plasmonic structures in our devices). These results provide valuable insight for designing graphene photodetectors with enhanced sensitivity for variable wavelength.
Similar content being viewed by others
Introduction
The unique Dirac-cone band structure makes graphene a promising material for photodetection. Its linearly dispersive band structure near Fermi level results in massless Dirac fermion type of carriers, large Fermi velocity (∼1/300 of the speed of light) and surprisingly high carrier mobility1,2,3,4. In graphene device, the photovoltage generation time is shorter than 50 fs, which is associated with the carrier heating time5. In addition, the rapid cooling process of photoexcited carriers (∼picoseconds) in the monolayer graphene results in a quick annihilation of photoelectrical signal in the electric circuit5,6,7,8,9,10,11,12. These advantages of the monolayer graphene facilitate its applications associated with ultrafast photodetection, such as high-speed optical communications13,14,15,16,17 and terahertz oscillators18. However, it remains a great challenge to achieve high photoresponsivity and selectivity in the monolayer-graphene-based detectors due to the weak and broadband absorption (only 2.3%, from the ultraviolet to the infrared)19 and the short photocarrier cooling time (∼picoseconds)5,6,7,8,9,10,11,12.
On the other hand, twisted bilayer graphene (tBLG) is non-AB stacked bilayer graphene in which one graphene monolayer sheet rotates by a certain angle (θ) relative to the other (Fig. 1a). Recent theoretical studies of tBLG have shown that the Dirac band dispersions change dramatically and become strongly warped with small twist angles (θ≤5°)20,21,22,23. Even at relatively large twist angles, the electronic coupling between the two monolayers, albeit weak, can still introduce new band structures20,21,22,23,24,25,26,27. Unlike the parabolic band structure in AB-stacked bilayer graphene28,29,30,31,32,33,34, the band structure of tBLG with large twist angle (typically larger than 5°)20,35 maintains linear near the Dirac point and thus it inherits some unique properties of monolayer graphene36. Away from the Dirac point, Dirac cones of the two individual monolayers intersect and form saddle points in reciprocal space of tBLG24, leading to the formation of van Hove singularities (VHSs) in the density of state (DOS)25,26,35,37,38, which then gives rise to some interesting phenomena such as enhanced optical absorption, Raman G-band resonance and enhanced chemical reactivity of tBLG27,37,39,40,41,42,43,44,45.
In this study, to address the problem of low photoresponsivity and selectivity in the monolayer graphene photodetection, we explore the high-performance photodetector based on tBLG with VHSs. For the first time, we report that the VHSs in tBLG leads to a prominent photocurrent enhancement of tBLG photodetectors with a wavelength selectivity under incident light irradiation.
Results
Structure and Raman spectra
tBLG samples were grown on copper foil via chemical vapour deposition (CVD) method and then transferred to heavily doped Si substrate, which was capped with 90 nm SiO2. As shown in typical optical image and scanning electron microscopy images (Fig. 1b,c), both the overlayer and underlayer in tBLG exhibit hexagonal shapes with sharp edges, which implies highly crystalline qualities of tBLG domains46,47,48. The interlayer twist angle can be measured from the relative misalignment of the straight edges, which is consistent with the observation by transmission electron microscopy (TEM) (Supplementary Fig. 1 and Supplementary Note 1). tBLG domains with different twist angles can be readily obtained in our samples (Fig. 1d), which provide a platform for the study of θ-dependent light–matter interactions. The highly crystalline quality and clean interface between two monolayers of our CVD sample are evidenced by the moiré pattern in high-resolution TEM image (Fig. 1e). This clean interface guarantees the interaction and coupling of electronic states from the over- and underlayer of tBLG. This interlayer electronic coupling is also proved by the enhanced G-band peak in Raman spectra (Fig. 1f). Taking 13° tBLG domain as an example, the Raman G-band intensity displays a tremendous enhancement of ∼20 folds under 532 nm laser (2.33 eV), which is consistent with the previously reported results27,28,39,40,41,42,43. This Raman G-band enhancement implies that an interlayer coupling introduces new band structures in tBLG. In addition, the enhanced G-band intensity of 13° tBLG domain was found to be uniform across the whole domain as shown in the G-band mapping image (Fig. 1f), which further confirms the high quality of our CVD tBLG samples. The Raman G-band enhancement is believed to correlate with the formation of VHSs in tBLG27,37,39,40,41,42,49.
Micro-ARPES spectra of tBLG
To unravel the nature of VHSs, we directly investigate the band structures of CVD-grown tBLG domains using spatially resolved angle-resolved photoemission spectroscopy with submicrometre spatial resolution (micro-ARPES). Owing to the twist angle (θ) between over- and underlayer of tBLG, the two sets of (six) Dirac points originated from each layer are rotated relatively by the angle θ as well (see Fig. 2a), which we mark as the k (left cones) and kθ (right cones) points, respectively. The band structures of a tBLG domain are shown in Fig. 2, where the constant energy contours (Fig. 2b), the band dispersions cutting across (Fig. 2c) and perpendicular (Fig. 2d) to the two adjacent Dirac points are presented, respectively. In Fig. 2b, the stacking plots of the band contours at different binding energies clearly depict the typical two Dirac-cone dispersions of tBLG and each preserves the linear dispersion of monolayer graphene. One of the Dirac cone exhibits a weaker intensity and higher electron doping level, indicating its origin from the underlayer graphene, as the photoelectrons from the bottom layer are screened by the top layer (thus leading to a weaker intensity), and being closer to the Cu substrate also increases its charge transfer50,51.
By measuring the separation between the two Dirac points (Fig. 2b,c), we can determine the twist angle (θ) of this tBLG domain as 19.1° (Supplementary Fig. 2 and Supplementary Note 2). Without interlayer coupling, the two Dirac cones in Fig. 2 shall intersect and cross each other at higher binding energy. Instead, the band structure at Fig. 2b clearly shows fine structures at the intersection (indicated by red arrows in Fig. 2b) and the dispersion in Fig. 2c shows the opening of the gap at the crossing point of the dispersions from the two Dirac cones, which is indicated by the faint intensity in the spectra intensity map (left panel) and the dip in the DOS plot (right panel, indicated by red arrows). This gap opening in the band structure is a typical anticrossing behaviour introduced by interlayer electronic coupling24, which leads to the formation of the VHS (Fig. 1a). In addition, from Fig. 2d, one can see that the anticrossing affects the hyperbolic curve as well and results in split and parallel dispersions.
With the same method, we further studied tBLG domains with various different twist angles and tracked the positions of VHSs with respect to the twist angles, as can be seen in Fig. 2e. At small angles, the value of EVHS increases almost linearly with θ, in consistence with the theoretical prediction (Supplementary Fig. 2). This dependence also helps explain the Raman G-band enhancement at specific twist angle (Fig. 1f) for a given incident laser frequency. If the energy of incident photon matches the energy interval of the two VHSs of tBLG (ℏω≈2EVHS, see Fig. 1a), the electrons are excited and transit between the fine band structure, causing the increase of the intensity of Raman G band peak (see Supplementary Fig. 3 and Supplementary Note 3 for details).
Selectively enhanced photocurrent generation of tBLG
The strong light–matter interaction of tBLG selectively enhanced by the VHSs can also enhance the generation of photocurrent under illumination. As an example, two adjacent tBLG domains with twist angle of 13° and 7° transferred onto SiO2 (90 nm)/Si were etched into a strip and then embedded into two-terminal devices in parallel (Fig. 3a,b). Raman spectroscopy and two-dimensional maps of the two adjacent tBLG domains were first measured under the 532-nm laser (2.33 eV). As expected, the G-band intensity of whole 13° domain exhibits a uniformly 20-fold enhancement as compared with the 7° domain (see Fig. 3c), as the energy interval of the two VHSs in 13° domain matches the energy of incident photon (ℏω≈2EVHS). To generate photocurrent selectively, interfacial junctions of tBLG-metal electrodes were used to separate the photoexcited electrons and holes under illumination52,53. As shown in current–bias voltage curves, both tBLG domains produce pronounced photocurrent shifts (Fig. 3d). Remarkably, the 13° tBLG domain generates a much larger net photocurrent (0.63 μA) at zero bias than that of the 7° domain (0.097 μA), originated from selectively enhanced light–matter interaction of 13° tBLG domain with the 532-nm laser.
We further conducted net photocurrent mapping of the device by using scanning photocurrent microscopy, in which the net photocurrent was recorded while scanning a focused 532-nm laser spot with a diameter of ∼1 μm over the device (Fig. 3e,f). The photocurrent was observed to exhibit contrary directions at the two graphene–metal electrode interfaces in the device. Significantly, the intensity of photocurrent generated at 13° tBLG domain is ∼6.6 times stronger than that at the 7° tBLG domain. This twist angle-related photocurrent enhancement holds great promise in high-selectivity photodetection applications.
To further evaluate the photoresponsivity of tBLG, we performed photocurrent measurements of tBLG devices under different incident power of 532 nm laser illumination, respectively. As shown in Fig. 3g, the photocurrents from 7° and 13° tBLG domains both increase as the incident power rises from ∼1 μW to ∼5 mW. The photoresponsivity of 7° and 13° tBLG domain is measured as ∼0.15 and ∼1 mA W−1, respectively, indicating a robust and strong enhancement in 13° tBLG domain under different incident power of 532 nm laser illumination.
From the unravelling of band structures, the energy interval of the two VHSs (2EVHS) of 13° tBLG domain is ∼2.34 eV, which matches the energy of incident photon (2.33 eV, λ=532 nm) and thus leads to a strong light–matter interaction. When we changed the wavelength of incident laser from 532 to 632.8 nm (1.96 eV), the photocurrent was found to be selectively enhanced in a 10.5° tBLG domain device with 2EVHS of ∼1.89 eV (Supplementary Fig. 4 and Supplementary Note 4). To further investigate the correlation of 2EVHS with ℏω in photocurrent generation of 13° and 10.5° tBLG domains, ℏω was gradually changed from 1.77 to 2.48 eV (500 to 700 nm in wavelength), while the power of incident laser was kept unchanged. As shown in Fig. 4a, the photocurrents of 13° and 10.5° tBLG domains exhibit peaks at ∼2.30 and ∼1.94 eV, agreeing well with 2EVHS values (∼2.34 and ∼1.89 eV), respectively.
Discussion
The origin of the photocurrent enhancement can be understood qualitatively when taking the unique electronic state of tBLG into account. In the photoexcitation process, the interband transition has to satisfy both momentum and energy conservation. For momentum conservation, the electrons are confined to transit between states with the same k value in reciprocal space, owing to the very small momentum of incident photons. As for energy conservation, the energy difference between these two states equals to ℏω. When ℏω≈2EVHS, the initial and final states are both near VHSs (thus with enhanced DOS, see Fig. 1a). Specifically, the effect of VHSs on the photoexcitation process can be evaluated by joint DOS (JDOS), which is defined as:
where EC and EV represent the energies of the conduction and valence bands, respectively. JDOS is associated with the process in which an electron absorbs a photon with energy ℏω=Ec−Ev and then transits from conduction to valence band. A calculated JDOS shows an abrupt increase associated with the VHSs when ℏω≈2EVHS (ref. 40). This leads to an enhanced photoexcitation process, consistent with experimental observations in Raman (Fig. 1f) and absorption spectra27,45. As a result, the intensified photoexcitation process may result in the enhanced photocurrent generation.
Besides the efficient photoexcitation, the improvement of separation efficiency of excited carriers can facilitate the photocurrent generation in tBLG. A gate voltage applied on the tBLG photodetection device can manipulate the doping level of graphene in channel and thus change the value of Seebeck coefficient, which may simultaneously lead to the photocurrent change54,55,56,57. As shown in Fig. 4b, the photocurrent of 13° tBLG domain has a 2.6-fold increase from ∼25 to ∼66 nA when the back-gate voltage decreases from 0 to −20 V. As the back-gate voltage increases from 0 to 20 V, the photocurrent first flips its polarity at 2.5 V and then reaches a value of about −82 nA. The inset in Fig. 4b shows the two band profiles of graphene–metal electrode junctions in the tBLG photodetection device under the applied back-gate voltage. From the transfer curve (Supplementary Fig. 5 and Supplementary Note 5), we believe that the positive gate voltage manipulates the graphene in channel from p- to n-type doping, which gives rise to the change of Seebeck coefficient. In contrast, owing to the Fermi-level pinning of graphene underneath the metal electrodes, its Seebeck coefficient keeps unchanged. Therefore, the difference of these two Seebeck coefficients could be tuned and flipped by gate voltage, which leads to the value and polarity change of photocurrent.
The responsivity of tBLG is measured as ∼1 mA W−1 at the resonance frequency, which is about 20 times enhancement compared with that of mechanically exfoliated monolayer graphene (∼0.05 mA W−1) with similar device configuration (Supplementary Fig. 6). To further improve the responsivity, we have integrated tBLG with plasmonic electrode structures as shown in Fig. 5a. A tBLG domain and an adjacent monolayer domain were embedded into the same two-terminal electrodes. A finger-patterned plasmonic structure (Ti/Au, 5/45 nm in thickness) with 110 nm finger width and 300 nm pitch58 were fabricated on the tBLG domain as shown in Fig. 5b,c. The Raman mapping image in Fig. 5d exhibits uniformly enhanced G-band intensity, which confirms that the interval of two VHSs (2EVHS) of the tBLG domain matches the energy of incident photon (532 nm and 2.33 eV). The scanning photocurrent results of the device (Fig. 5e,f) show that the photocurrents of tBLG and the adjacent monolayer domain are measured as ∼10 and ∼0.95 nA, respectively. The enhancement of about 10.5 times is achieved. Remarkably, the photocurrent generated on tBLG near the finger structure is further enhanced to the value of ∼77 nA, which is ∼80-fold enhancement compared with the photocurrent of adjacent monolayer graphene channel. The mechanism of such strong photoresponsivity enhancements can be ascribed to the combination of the selective resonance enhancement of VHSs in tBLG and plasmonic enhancement of the finger structure.
In summary, we have experimentally demonstrated that the light–matter interaction in tBLG with VHSs is dependent on the interlayer twist angle (θ) and then can lead to a selective enhancement in photocurrent generation. Micro-ARPES was performed to unravel the band structure of CVD-grown tBLG and reveal the emergence of θ-dependent VHSs. The photocurrent of tBLG photodetectors exhibits a ∼6.6-fold enhancement at a suitable θ, when the energy interval of the VHSs (2EVHS) matches the energy of incident photon (ℏω). By integrating plasmonic structures, the responsivity of tBLG photodetector can be significantly enhanced by ∼80 folds compared with the monolayer graphene. Our results open a new route to graphene-based optoelectronic applications.
Methods
tBLG growth and characterization
The tBLG was grown on copper foil in a home-made low-pressure CVD system. The growth was carried out under the flow of H2 and CH4 (600:1 in volume) with a pressure of 600 Pa at 1,030 °C for 40 min. The samples were characterized by Olympus BX51 microscope, scanning electron microscopy (Hitachi S-4800 operated at 2 kV), TEM (FEI Tecnai F30 operated at 300 kV for the diffraction image and FEI 80-300 Cs image-corrected Titan operated at 80 kV for the moiré pattern image) and Raman spectroscopy (Horiba HR800). The micro-ARPES measurements were carried out at the spectromicroscopy beamline at Elettra Synchrotron Radiation lab in Italy, with energy resolution of 50 meV, spatial resolution of 0.8 μm and angle resolution of 0.5°. Before the micro-ARPES measurements, in-situ annealing at 350 °C was carried out to clean the sample surface.
Device fabrication and measurement
tBLG samples on copper were transferred to a highly doped Si substrate with 90 nm SiO2 with the help of poly(methyl methacrylate)59. The Ti/Au (20/30 nm) electrodes and Ti/Au (5/45 nm) figure structures were fabricated by electron-beam lithography and the following electron-beam evaporation. The electrical measurements were performed by Keithley SCS-4200. The photoelectrical measurements were performed by a scanning photocurrent microscopy. In the set-up, 532 and 632.8 nm, and Supercontinuum Laser Sources (NKT Photonic) were used as laser sources. The chopper-modulated (∼1 kHz) laser beams were focused to ∼1 μm on the device using × 100 objective and the short-circuit photocurrents were then measured by pre-amplifier and lock-in amplifier. When scanning the laser spot over the device, the induced photocurrents and beam positions were recorded and displayed simultaneously with the assistance of a computer, which communicated with lock-in amplifier and motorized stage (with device on it). A voltage source (Keithley 2400) was used to supply the gate voltage. All the electrical and photoelectrical measurements were performed in air at room temperature.
Additional information
How to cite this article: Yin, J. et al. Selectively enhanced photocurrent generation in twisted bilayer graphene with van Hove singularity. Nat. Commun. 7:10699 doi: 10.1038/ncomms10699 (2016).
Change history
19 July 2016
A correction has been published and is appended to both the HTML and PDF versions of this paper. The error has not been fixed in the paper.
References
Novoselov, K. S. et al. Two-dimensional gas of massless Dirac fermions in graphene. Nature 438, 197–200 (2005).
Novoselov, K. S. et al. Electric field effect in atomically thin carbon films. Science 306, 666–669 (2004).
Zhang, Y. B. et al. Experimental observation of the quantum Hall effect and Berry’s phase in graphene. Nature 438, 201–204 (2005).
Geim, A. K. & Novoselov, K. S. The rise of graphene. Nat. Mater. 6, 183–191 (2007).
Tielrooij, K. J. et al. Generation of photovoltage in graphene on a femtosecond timescale through efficient carrier heating. Nat. Nanotechnol. 10, 437–443 (2015).
Sun, D. et al. Ultrafast relaxation of excited Dirac fermions in epitaxial graphene using optical differential transmission spectroscopy. Phys. Rev. Lett. 101, 157402 (2008).
George, P. A. et al. Ultrafast optical-pump terahertz-probe spectroscopy of the carrier relaxation and recombination dynamics in epitaxial graphene. Nano Lett. 8, 4248–4251 (2008).
Tani, S. et al. Ultrafast carrier dynamics in graphene under a high electric field. Phys. Rev. Lett. 109, 166603 (2012).
Graham, M. W. et al. Photocurrent measurements of supercollision cooling in graphene. Nat. Phys. 9, 103–108 (2013).
Tielrooij, K. J. et al. Photoexcitation cascade and multiple hot-carrier generation in graphene. Nat. Phys. 9, 248–252 (2013).
Tse, W.-K. & Das Sarma, S. Energy relaxation of hot Dirac fermions in graphene. Phys. Rev. B 79, 235406 (2009).
Bistritzer, R. & MacDonald, A. H. Electronic cooling in graphene. Phys. Rev. Lett. 102, 206410 (2009).
Xia, F. N. et al. Ultrafast graphene photodetector. Nat. Nanotechnol. 4, 839–843 (2009).
Mueller, T. et al. Graphene photodetectors for high-speed optical communications. Nat. Photonics 4, 297–301 (2010).
Gan, X. et al. Chip-integrated ultrafast graphene photodetector with high responsivity. Nat. Photonics 7, 883–887 (2013).
Pospischil, A. et al. CMOS-compatible graphene photodetector covering all optical communication bands. Nat. Photonics 7, 892–896 (2013).
Schall, D. et al. 50 GBit/s photodetectors based on wafer-scale graphene for integrated silicon photonic communication systems. ACS Photonics 1, 781–784 (2014).
Boubanga-Tombet, S. et al. Ultrafast carrier dynamics and terahertz emission in optically pumped graphene at room temperature. Phys. Rev. B 85, 035443 (2012).
Nair, R. R. et al. Fine structure constant defines visual transparency of graphene. Science 320, 1308–1308 (2008).
Shallcross, S. et al. Quantum interference at the twist boundary in graphene. Phys. Rev. Lett. 101, 056803 (2008).
Shallcross, S. et al. Emergent momentum scale, localization, and van Hove singularities in the graphene twist bilayer. Phys. Rev. B 87, 245403 (2013).
Shallcross, S. et al. Electronic structure of turbostratic graphene. Phys. Rev. B 81, 1 (2010).
Landgraf, W. et al. Electronic structure of twisted graphene flakes. Phys. Rev. B 87, 075433 (2013).
Ohta, T. et al. Evidence for interlayer coupling and moire periodic potentials in twisted bilayer graphene. Phys. Rev. Lett. 109, 186807 (2012).
Li, G. H. et al. Observation of Van Hove singularities in twisted graphene layers. Nat. Phys. 6, 109–113 (2010).
Yan, W. et al. Angle-dependent van Hove singularities in a slightly twisted graphene bilayer. Phys. Rev. Lett. 109, 126801 (2012).
Havener, R. W. et al. Angle-resolved Raman imaging of inter layer rotations and interactions in twisted bilayer graphene. Nano Lett. 12, 3162–3167 (2012).
Ohta, T. et al. Controlling the electronic structure of bilayer graphene. Science 313, 951–954 (2006).
McCann, E. Asymmetry gap in the electronic band structure of bilayer graphene. Phys. Rev. B 74, 161403 (2006).
Castro, E. V. et al. Biased bilayer graphene: semiconductor with a gap tunable by the electric field effect. Phys. Rev. Lett. 99, 216802 (2007).
McCann, E. & Fal’ko, V. I. Landau-level degeneracy and quantum hall effect in a graphite bilayer. Phys. Rev. Lett. 96, 086805 (2006).
Guinea, F. et al. Electronic states and Landau levels in graphene stacks. Phys. Rev. B 73, 245426 (2006).
Ohta, T. et al. Interlayer interaction and electronic screening in multilayer graphene investigated with angle-resolved photoemission spectroscopy. Phys. Rev. Lett. 98, 206802 (2007).
Zhang, Y. B. et al. Direct observation of a widely tunable bandgap in bilayer graphene. Nature 459, 820–823 (2009).
Luican, A. et al. Single-layer behavior and its breakdown in twisted graphene layers. Phys. Rev. Lett. 106, 126802 (2011).
dos Santos, J. et al. Graphene bilayer with a twist: electronic structure. Phys. Rev. Lett. 99, 256802 (2007).
Coh, S. et al. Theory of the Raman spectrum of rotated double-layer graphene. Phys. Rev. B 88, 165431 (2013).
Brihuega, I. et al. Unraveling the intrinsic and robust nature of van Hove Singularities in twisted bilayer graphene by scanning tunneling microscopy and theoretical analysis. Phys. Rev. Lett. 109, 196802 (2012).
Kim, K. et al. Raman spectroscopy study of rotated double-layer graphene: misorientation-angle dependence of electronic structure. Phys. Rev. Lett. 108, 246103 (2012).
Sato, K. et al. Zone folding effect in Raman G-band intensity of twisted bilayer graphene. Phys. Rev. B 86, 125414 (2012).
Carozo, V. et al. Resonance effects on the Raman spectra of graphene superlattices. Phys. Rev. B 88, 085401 (2013).
He, R. et al. Observation of low energy Raman modes in twisted bilayer graphene. Nano Lett. 13, 3594–3601 (2013).
Ni, Z. et al. Reduction of Fermi velocity in folded graphene observed by resonance Raman spectroscopy. Phys. Rev. B 77, 235403 (2008).
Liao, L. et al. van Hove singularity enhanced photochemical reactivity of twisted bilayer graphene. Nano Lett. 15, 5585–5589 (2015).
Wang, Y. Y. et al. Stacking-dependent optical conductivity of bilayer graphene. ACS Nano 4, 4074–4080 (2010).
Zhou, H. L. et al. Chemical vapour deposition growth of large single crystals of monolayer and bilayer graphene. Nat. Commun. 4, 2096 (2013).
Yan, Z. et al. Toward the synthesis of wafer-scale single-crystal graphene on copper foils. ACS Nano 6, 9110–9117 (2012).
Ma, T. et al. Repeated growth-etching-regrowth for large-area defect-free single-crystal graphene by chemical vapor deposition. ACS Nano 8, 12806–12813 (2014).
Ni, Z. H. et al. G-band Raman double resonance in twisted bilayer graphene: evidence of band splitting and folding. Phys. Rev. B 80, 125404 (2009).
Giovannetti, G. et al. Doping graphene with metal contacts. Phys. Rev. Lett. 101, 026803 (2008).
Zhou, S. Y. et al. Substrate-induced bandgap opening in epitaxial graphene. Nat. Mater. 6, 770–775 (2007).
Xia, F. N. et al. Photocurrent imaging and efficient photon detection in a graphene transistor. Nano Lett. 9, 1039–1044 (2009).
Mueller, T. et al. Role of contacts in graphene transistors: a scanning photocurrent study. Phys. Rev. B 79, 245430 (2009).
Song, J. C. W. et al. Hot carrier transport and photocurrent response in graphene. Nano Lett. 11, 4688–4692 (2011).
Gabor, N. M. et al. Hot carrier-assisted intrinsic photoresponse in graphene. Science 334, 648–652 (2011).
Xu, X. D. et al. Photo-thermoelectric effect at a graphene interface junction. Nano Lett. 10, 562–566 (2010).
Sun, D. et al. Ultrafast hot-carrier-dominated photocurrent in graphene. Nat. Nanotechnol. 7, 114–118 (2012).
Echtermeyer, T. J. et al. Strong plasmonic enhancement of photovoltage in graphene. Nat. Commun. 2, 458 (2011).
Reina, A. et al. Transferring and identification of single- and few-layer graphene on arbitrary substrates. J. Phys. Chem. C 112, 17741–17744 (2008).
Acknowledgements
We are grateful to Dr Yao Guo and Mr Chen Peng from Department of Electronics, Peking University, for their suggestions in device fabrication, and Mr Ziwei Li from School of Physics, Peking University, for the calculation regarding to plasmonic structures. We acknowledge financial support from the National Basic Research Program of China (numbers 2014CB932500, 2011CB921904 and 2013CB932603), the National Natural Science Foundation of China (numbers 21173004, 21222303, 51121091 and 51362029), the National Program for Support of Top-Notch Young Professionals and Beijing Municipal Science and Technology Commission (Z131100003213016). Part of this work was performed at the Stanford Nano Shared Facilities.
Author information
Authors and Affiliations
Contributions
J.Y. and H.L.P. conceived and designed the experiments. J.Y and H.W. performed the synthesis and structural characterization. J.Y. made the devices and carried out optoelectronic measurements. Z.T., L. Liao, L. Lin and X.S. assisted in experimental work and contributed to the scientific discussions. H.P. and Y.L.C. preformed micro-ARPES. A.L.K. and H.L.P. conducted the TEM, high-resolution TEM and aberration-corrected high-resolution TEM experiments. J.Y., H.L.P. and H.P. wrote the paper. H.L.P., Z.L. and Y.L.C. supervised the project. All the authors discussed the results and commented on the manuscript.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Supplementary information
Supplementary Information
Supplementary Figures 1-6, Supplementary Notes 1-5 and Supplementary References. (PDF 809 kb)
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Yin, J., Wang, H., Peng, H. et al. Selectively enhanced photocurrent generation in twisted bilayer graphene with van Hove singularity. Nat Commun 7, 10699 (2016). https://doi.org/10.1038/ncomms10699
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/ncomms10699
- Springer Nature Limited
This article is cited by
-
Waveguide-integrated twisted bilayer graphene photodetectors
Nature Communications (2024)
-
Moiré superlattice engineering of two-dimensional materials for electrocatalytic hydrogen evolution reaction
Nano Research (2023)
-
Graphene-Enhanced Refractive Index Sensing and Narrow-band Filtering with Crossed Bicircular Resonator Cavity Waveguides
Plasmonics (2023)
-
Advance in two-dimensional twisted moiré materials: Fabrication, properties, and applications
Nano Research (2023)
-
Hetero-site nucleation for growing twisted bilayer graphene with a wide range of twist angles
Nature Communications (2021)