Abstract
Many-body effects produce deviations from the predictions of conventional band theory in quantum materials, leading to strongly correlated phases with insulating or bad metallic behavior. One example is the rare-earth nickelates RNiO3, which undergo metal-to-insulator transitions (MITs) whose origin is debated. Here, we combine total neutron scattering and broadband dielectric spectroscopy experiments to study and compare carrier dynamics and local crystal structure in LaNiO3 and NdNiO3. We find that the local crystal structure of both materials is distorted in the metallic phase, with slow, thermally activated carrier dynamics at high temperature. We further observe a sharp change in conductivity across the MIT in NdNiO3, accompanied by slight differences in the carrier hopping time. These results suggest that changes in carrier concentration drive the MIT through a polaronic mechanism, where the (bi)polaron liquid freezes into the insulating phase across the MIT temperature.
Similar content being viewed by others
Introduction
Metal-to-insulator transitions (MITs) driven by many-body effects such as strong electron correlations1 or electron–phonon (e–ph) interactions2 have attracted considerable attention. In this context, the perovskite rare-earth-element nickelates RNiO3 (R=La, Pr, Nd, etc.)3, 4 have emerged as an important material family in recent years3,4,5,6,7,8,9,10,11,12,13,14. This family of materials exhibits a high-temperature MIT whose transition temperature TMIT can be tuned continuously by varying the radius of the rare-earth ion3, 4, or through external factors such as strain5,6, reduced dimensionality15,16, and heterostructure design15,16,17,18,19. This electronic transition is concomitant with a long-range structural change, whereby each O6 octahedra expands and contracts around alternating Ni sites following a breathing-type displacement pattern. The RNiO3 systems are therefore ideal candidates for studying MITs and the ways in which they couple to the lattice or vice versa.
One proposal for the MIT is motivated by formal valence counting, which predicts a d7 valence state for the Ni ion, with a single electron occupying the degenerate Ni 3d e g orbitals in the (nearly) cubic metallic phase. This configuration, however, is unstable towards Jahn–Teller distortions or the formation of a mixed Ni valence state, where alternative Ni atoms acquire d7+δ and d7−δ valences for sufficiently large Hund’s coupling7. This charge disproportionation scenario provides one possible mechanism for the MIT7,8,20, where the breathing lattice distortion reflects the Ni–O bond distances expected for the different Ni valence states.
An alternative view for the MIT is rooted in the fact that the nickelates likely belong to a wider class of “negative charge transfer” materials10,12,13,21,22,23,24. In such systems, it is energetically favorable for a Ni hole to move to the surrounding ligand oxygen orbitals. The electronic wave function is then best described as a \(\alpha \left| {d^7} \right\rangle + \beta \left| {d^8\underline{\mathrm L }} \right\rangle\) state10, where \(\beta ^2 \gg \alpha ^2\) and \(\underline{\mathrm L}\) denotes a hole occupying a molecular orbital formed from the surrounding ligand oxygen 2p σ orbitals with an e g symmetry. The fact that \(\beta ^2 \gg \alpha ^2\) implies that the \(d^8\underline{\mathrm L}\) configuration is lower in energy than the d7 in the atomic picture, and thus the system is in the negative charge transfer regime of the Zaanen–Sawatzky–Allen classification scheme22.
The idea that holes occupy ligand molecular orbitals is important, because this charge configuration couples strongly to the breathing motion of the oxygen atoms, which can result in a sizable e–ph interaction. Several theoretical studies have shown that this can drive a MIT through bond disproportionation10,11,12,13. In this scenario, the MIT occurs when pairs of ligand holes occupy alternating O6 octahedra, which then compress to maximize (minimize) the hole’s delocalization (kinetic energy) between the O and Ni orbitals. The insulating phase corresponds to a crystal structure where the oxygen sublattice has expanded and contracted around alternating Ni sites along the three crystallographic axes, creating two inequivalent Ni sites and a monoclinic phase, consistent with experiments. The Ni site surrounded by the compressed oxygen octahedron has a (\(d^8\underline{\mathrm L^2}\)) charge configuration, while the Ni at the center of the expanded octahedron has a (3d8) configuration10.
The bond-disproportionation mechanism and negative charge transfer classification of the nickelates has gained significant theoretical10,11,12 and experimental support in recent years13,21,24. However, an unresolved question concerns the nature of the carriers in the bad metallic phase. The key factor in the bond-disproportionation scenario is the strong coupling between the ligand holes and the bond-stretching motion of the oxygen atoms. If such coupling is present, it should also be active in the metallic phase. It is then natural to wonder how these interactions might affect the properties of the carriers in the metallic state, or if they can produce a polaronic charge carrier. For example, one might expect that the e–ph interaction could generate a local octahedral compression that binds to the ligand hole. Indeed, such a scenario was evidenced in a recent neutron scattering study25, as well as prior x-ray absorption26 and μSR studies27, which all find indications of two different Ni sites in the metallic phase.
In the following, we performed neutron total scattering and broadband dielectric spectroscopy (BDS) measurements to study the local crystal structure in LaNiO3 and NdNiO3 and its relationship with charge dynamics as a function of temperature. These samples were chosen to contrast LaNiO3, which does not undergo an MIT and remains in a high-symmetry rhombohedral phase down to 0 K, with NdNiO3, which has a phase transition from an orthorhombic to a monoclinic phase that coincides with the MIT at T ≈ 200 K25. Our results provide direct evidence that carriers in both materials are indeed small lattice (bi)polarons, where the local breathing distortions bind with the ligand holes, creating a composite quasiparticle with slow dynamics. These results provide a picture of the nickelates where the bad metallic behavior emerges from a polaronic liquid, which freezes into a charge-ordered state at sufficiently low temperatures.
Results
Neutron scattering
To analyze local distortions to the crystal structure, we first converted our neutron total scattering data for LaNiO3 and NdNiO3 into pair distribution functions (PDFs) as shown in Fig. 1. We initially modeled the data for LaNiO3 with the high-symmetry rhombohedral structure (Fig. 1a) with a single Ni site, rather than the lower-symmetry orthorhombic (Fig. 1b) or monoclinic (Fig. 1c) structure, which is characteristic of other rare-earth nickelates. Although this model fits the average structure well (assessed with diffraction, see supplementary Note 1), the poor quality of fit of the small-box refinement in Fig. 1d (blue line, with a weighted residual of Rw = 0.186) indicates that this structure is not consistent with the local atomic arrangement in LaNiO3 at any measured temperature (refinement is only shown at 300 K for clarity). The fit is dramatically improved by using the orthorhombic model (Pnma space group) with distorted NiO6 octahedra; however, some peaks are still modeled poorly (green line, Rw = 0.098). Further agreement between the refinement and the data is achieved by lowering the symmetry to the monoclinic model, which allows for two distinct Ni sites (magenta line, Rw = 0.044). This improvement in the description of the structure is consistent among all temperatures measured (only data at 300 and 100 K are shown).
While both the orthorhombic and monoclinic structures reproduce the local structure reasonably well, the primary discrepancy between the two pertains to the first peak of the PDF, which represents the nearest-neighbor \(\left\langle {{\rm {Ni - O}}} \right\rangle\) bond (Fig. 1e): the width of this peak is better reproduced when we allow for at least two inequivalent Ni sites. These results indicate that the structure of LaNiO3 has a high degree of symmetry when viewed on long length scales, but also has at least two different types of Ni sites when viewed locally. These two Ni sites reflect the different environments surrounding the Ni atoms once local octahedral distortions form in agreement with ref. 25.
Our results for NdNiO3 show qualitatively similar behavior; however, the difference in fit between the orthorhombic and monoclinic models are much more subtle (Fig. 1f). Although the PDF for metallic NdNiO3 is reproduced reasonably well with the orthorhombic model (blue line, Rw = 0.095), the position and intensity of the \(\left\langle {{\rm {Ni - O}}} \right\rangle\) bond are slightly misrepresented (blue line, Fig. 1d). Correlated thermal motion of the Ni and O atoms might explain this mismatch; however, such motion should have no impact on the position of the peak. Instead, lowering the symmetry to the monoclinic model significantly improves the overall fit (green line in Fig. 1e, Rw = 0.053). Although the differences are very slight, this improvement suggests that compressed NiO6 is present in the metallic phase, creating a distribution of long and short Ni–O bonds and the monoclinic model accounts for the inequivalent Ni environments. As expected, the monoclinic model (cyan line, Rw = 0.0380) outperforms the orthorhombic model (magenta, Rw = 0.067) in NdNiO3 below TMIT, with the same improvement occurring in the region of the NiO6 octahedra (Fig. 1c, d).
Although the monoclinic model describes the data better for both samples at all temperatures, we also find clear evidence of a structural transition in NdNiO3 that is present at both short and long length-scales (Fig. 2). Consistent with previous studies3, our data show that NdNiO3 has an abrupt volumetric expansion at TMIT that is absent in metallic LaNiO3 (T ≈ 195 K, Fig. 2a). This change is also apparent in the peak intensity of the PDF describing the local structure. As the temperature is lowered from 295 to 195 K in the metallic phase of NdNiO3, the \(\left\langle {\rm {{Ni - O}}} \right\rangle\) peak height continually grows, as is typical for decreasing thermal motion of the ions (the Debye–Waller effect). However, an apparent discontinuity occurs at TMIT, where the peak broadens, and the intensity suddenly decreases. This non-Debye–Waller-like behavior is evidence for a local structural transition concomitant with the average structural response, where expanded and contracted O6 appear along alternating Ni sites across the entire crystal. In contrast, LaNiO3 displays no such transition and the general trend of increasing peak height with decreasing T persists across the entire measured range (except for two outliers at 140 and 260 K). We observe similar contrasting behavior between NdNiO3 and LaNiO3 in other small-box refinement procedures with an expanded fit range (Supplementary Note 1).
Our neutron data and PDF analysis indicate that the NiO6 octahedra are compressed to varying degrees in both LaNiO3 and NdNiO3 at all temperatures, even in their metallic phases. However, when viewed on long length scales, these distortions are less apparent and the structures are well described by a high-symmetry model. These observations can be reconciled if the lattice distortions are disordered and/or dynamic at high temperatures but “freeze” into a periodic structure below TMIT. This suggests a polaronic picture, where the disordered NiO6 octahedra are dynamic quasiparticles, which form a liquid or gas in the metallic phase. Given that the differences in refinements in Fig. 1c, d are tiny, we have employed BDS as a function of temperature to glean further insight into possible dynamic processes that should be present if this picture holds.
Broadband dielectric spectroscopy
The frequency range available to the BDS technique (up to 10−3–1010 Hz) provides a competitive advantage to more traditional optical spectroscopies by granting more direct access to the low-frequency processes (e.g., lattice process) that control conduction in a material. The real part of the complex-valued ac conductivity σ′(ν) + iσ″(ν) is plotted in Fig. 3a, b for LaNiO3 and NdNiO3, respectively. At all temperatures, σ′(ν) is constant over a broad frequency range extending up to \(\nu \sim 10^5\) Hz and monotonically increases above this range. The frequency-independent portion of the spectrum represents the dc conduction while ν = 1/2πτ e represents a shift from dc to ac behavior.
The data at all measured temperatures can be described well (only the fit at 150 K is shown for clarity) using a continuous-time random walk (CTRW) model \(\sigma ^ \ast \left( v \right) = \sigma _{{\rm dc}}\left[ {\frac{{2\pi {\mathrm{i}}v\tau _e}}{{{\rm ln}\left( {1 + 2\pi {\mathrm{i}}v\tau _e} \right)}}} \right]\), where v is the frequency of the ac electric field, σdc is the dc conductivity, and τ e is the characteristic carrier hopping time28. This model describes the motion of carries hopping in a landscape of randomly varying potential barriers. We have in mind polaronic conduction, where the ligand holes are bound to the local breathing distortion such that coherent motion only occurs when the two move together. In this case, the varying potential barrier arises from variations in the local structural environment, where the barrier height depends on whether or not the neighboring Ni site also hosts a (\(d^8\underline{\mathrm L}\)) polaron or a (\(d^8\underline{\mathrm L^2}\)) bipolaron, as well as the thermal fluctuations in the lattice distortions. It is important to stress that τ e in this model is not the same as the scattering time τ of the Drude model. In particular, a larger τ e describes decreased carrier mobility whereas a larger τ in the Drude model enhances it. The fact that this model fits our data well in both the metallic and insulating phases indicates similar hopping processes are governing carrier dynamics in both phases.
Using the CTRW model, we extracted the temperature dependence of σdc (Fig. 3c) and τ e (Fig. 3d). The dc conductivity for NdNiO3 varies very little at high T but sharply decreases below 195 K. This temperature corresponds to the onset of long-range structural distortions described in Fig. 2 and the MIT reported in previous studies. Conversely, LaNiO3 does not display such a transition as expected. Our BDS experiments are performed on pressed powders and in an air gap geometry (Methods). This setup can produce a value of the conductivity that is reduced by as much as eight orders of magnitude compared with traditional four-probe conductivity measurements29. This decrease occurs because no electrical conduction can proceed through the air gap and instead only electrical displacements induced by the alternating electric field are measured. This also results in some sample variation in the overall magnitude of conductivity (Supplementary Notes 2 and 3). We stress, however, that this does not affect the relative trends in conductivity (as evidenced by the clear transition for NdNiO3) or the measured frequency of dynamic processes responding to the applied fields (discussed below). To support this, we have provided a second data set obtained using a different set of samples and varying air gap thicknesses (Supplementary Note 4).
The extracted τ e ranges from ≈0.1 to 0.4 μs for NdNiO3 and 0.3 to 0.6 μs for LaNiO3 (Fig. 3c), which are orders of magnitude slower than expected for mobile electrons or holes. We believe that this observation is the consequence of the presence of lattice polarons, where the lattice distortions significantly retard carrier hopping. The T-dependence of τ e further supports this interpretation. Here, τ e (T) varies smoothly for LaNiO3 while there is an abrupt change in slope at TMIT for NdNiO3. More importantly, τ e continually decreases with increasing temperature across all regimes in both samples. In general, the dc conductivity is σdc = neμ e , where n is the charge carrier concentration, e is the effective charge, and μ e is the carrier mobility. The latter is inversely related to the carrier hopping time \(\mu _e = \frac{a}{{\tau _eE}}\), where a is the jump distance and E is the electric field strength. Conductivity is therefore affected equally by the number of charge carriers as well as their mobility. A decrease in dc conductivity with decreasing temperature in the insulating phase of NdNiO3 is consistent with the observed increase in τ e (decrease in μ e ). It is surprising, however, that this thermally activated hopping also persists in the metallic phases of both samples. We also note that we can convert our τ e values to carrier mobilities with knowledge of the jump distance using Eq. (8). While this value is not straight forward to determine, we can obtain a rough estimate by using the Ni–Ni distance in a back of the envelope calculation. This assumption gives a mobility \(\sim 0.05\) cm2/V s, which is an order of magnitude smaller than the Hall mobility reported in ref. 30 for SmNiO3 thin films. This value is not unphysically small, and may be due to differences in the samples (e.g., Sm vs. Nd/La or powders vs. films).
The behavior of σdc and τ e is in stark contrast to the Drude picture of metallic conduction, where conductivity decreases as T increases due to thermally excited lattice vibrations and the carrier mobility subsequently decreases. Our data show that increasing T instead enhances the carrier mobility in the nickelate metallic phase. This puzzling observation can be understood if the carriers are lattice polarons, as implied by the PDF data in Fig. 1. In this case, thermal excitations of the lattice make it easier to transfer the phonon cloud between neighboring sites and thus facilitate hopping.
The fact that the mobility in the metallic nickelates is enhanced with increasing T means that carrier concentration must change with temperature to explain the apparent trends in conductivity. This is most evident when examining a plot of σdcτ e (proportional to n) or \(\tau _e^{ - 1}\) (proportional to μ e ) vs. T (Fig. 4). Conventional thought is that metals have a constant n, and the decrease in conductivity with temperature is caused instead by decreased mobility. We have shown that in both metallic NdNiO3 (Fig. 4a) as well as LaNiO3 (Fig. 4b), μ e continually increases with temperature and it is instead n that is decreasing. This result is in agreement with a recent optical spectroscopy study by Jaramillo et al.31, which suggested that changes in carrier concentration are the origin of the bad metal behavior in the nickelates. This result can be understood in the framework of polaronic charge carriers proposed here, where the coherence between the phonon cloud and the holes becomes damped with increased temperature.
Interestingly, although μ e does display a change of slope, the most profound feature of the MIT is the thermal behavior of n, which shows a maximum at the MIT and rapidly falls off at lower temperatures (Fig. 4a). This observation can be explained if there exists a highly disordered “liquid” of polaronic charge carriers in the metallic state that “freeze” into a periodic array in the insulating state, thus resulting in the dramatic decrease in the concentration of mobile charge carriers (Fig. 4c). This interpretation is in full agreement with the PDF data shown earlier, which revealed a sudden broadening of the Ni–O bond peak that was concomitant with the MIT.
Discussion
In light of our results, it is interesting to speculate as to why LaNiO3 does not undergo a MIT, while the remaining nickelates do. We believe that this is due to differences in the Ni–O–Ni bond angle θ produced by the variation on the R ion’s radius. In LaNiO3, which has the largest R ion, this angle is greatest (\(\theta \sim 165^ \circ\)), while it becomes smaller as R decreases in size. (For example, in NdNiO3 it is \(\theta \sim 157^ \circ\) while for the end member LuNiO3 it is estimated to be \(\theta \sim 132.5^ \circ\)3.) Decreasing the bond angle has two important effects in the context of polarons. First, it narrows the electronic bandwidth thus enhancing polaronic effects. Second, it controls the strength of the linear e–ph coupling. In a perfectly cubic structure, with a 180° Ni–O–Ni bond angle, the first order coupling to the oxygen displacement should vanish by symmetry. Thus, decreasing the bond angle from 180° will increase overall strength of the linear e–ph coupling. When combined with the reduced bandwidth, this effect should enhance the formation and localization of small polarons. A combination of these two effects may explain why LaNiO3 does not undergo an MIT; however, further theoretical modeling will be necessary to determine which effect, if any, is dominant.
In summary, we have presented detailed neutron and broadband dielectric spectroscopy measurements on the rare-earth nickelates LaNiO3 and NdNiO3. Our results reveal evidence for distorted NiO6 octahedra in the metallic phase of both materials, with only a minor change in carrier dynamics across the MIT. Our results provide a way to view the metallic state of the nickelates that differs somewhat from the previously proposed bond-disproportionation scenario. These results demonstrate that the \(d^8\underline{\mathrm L^2}\) complexes are pre-formed in the metallic state, forming a disordered (bi)polaronic liquid, with a bad metallic state driven by thermally activated transport properties at high temperature. Across the MIT, the compressed \(d^8\underline{\mathrm L^2}\) bipolarons condense into a charge-ordered lattice, as sketched in Fig. 4c. This understanding of the MIT in the rare-earth nickelates likely has analogies in other systems of negative charge transfer materials such as the high-temperature superconducting bismuthates and related systems32,33. This picture also provides natural explanations for both the observation of an isotope effect for TMIT14 and Curie–Weiss behavior in non-magnetic LaNiO334. In the latter case, the Ni 3d8 ions in the expanded O6 octahedra act as free S = 1 ions in the metallic phase.
Methods
Neutron total scattering experiments
Polycrystalline LaNiO3 and NdNiO3 polycrystalline samples were prepared from citrate precursors obtained by a soft chemistry procedure. Stoichiometric amounts of analytical grade La2O3 or Nd2O3 and Ni(NO3)2⋅6H2O were dissolved in a saturated acid citric solution containing some droplets of HNO3. The citrate solution was slowly evaporated, leading to an organic resin that was dried at 120 °C and slowly decomposed at temperatures up to 600 °C. The products underwent a subsequent treatment in air at 800 °C for 2 h to eliminate all the organic materials and nitrates. The black precursor powders were heated under 200 bar of oxygen pressure for 12 h at 900 °C. Then, the samples were slowly cooled down to room temperature.
Neutron total scattering experiments were performed at the nanoscale ordered materials diffractometer (NOMAD) beamline at the Spallation Neutron Source at Oak Ridge National Laboratory35. Polycrystalline LaNiO3 and NdNiO3 samples were loaded into 2 mm diameter quartz capillaries to a height of ~1 cm. The samples were exposed to the neutron beam for ~1 h per measurement. An identical empty capillary was also measured for 1 h to correct for the background contribution to the data. LaNiO3 was measured at 11 temperatures from 300 to 100 K, while NdNiO3 was measured at nine temperatures from 295 to 95 K.
The total scattering structure function S(Q)−1 was obtained by normalizing scattering intensity from the sample (after the background was subtracted using the empty quartz capillary measurement) to that of a vanadium standard. The reduced PDF was calculated using the Fourier transform of S(Q)−1
where Q is the scattering vector and is defined as Q = 4π/λ sin θ. Here, λ and θ are the neutron wavelength and scattering angle, respectively. A value of 0.1 and 31.4 Å−1 was used for Qmin and Qmax, respectively, in the Fourier transform. The measured S(Q)−1 was multiplied by a Lorch function36 before the transformation to exclude the effects of artificial ripples on data analysis.
Unit cell volumes were determined using Rietveld refinement of the highest Q-resolution backscattering bank of diffraction data with GSAS software37. PDFgui38 was used for real-space refinement of PDF data, while PDF peak heights were determined using peak fitting in OriginPro with a Gaussian function after subtracting a linear baseline.
Broadband dielectric spectroscopy measurements
Broadband dielectric spectroscopy measurements were performed using a Novocontrol Alpha Analyzer with a frequency range of 103–107 Hz. The temperature was varied from 300 to 150 K using a QUATRO liquid nitrogen controller with a stability limit of ±0.1 K. Powder samples were hot pressed at 150 °C into aluminum foil to a thickness of 50 μm. The aluminum foil served as the bottom electrode while a 6 mm diameter brass electrode was used for the top. Teflon spacers were used to create a gap of 100 μm between the sample and top electrode. Complex conductivity (σ′ + iσ′′) was calculated from the measured impedance data using WinDeta software from Novocontrol.
Data availability
The data that support the findings of this study are available from the corresponding author upon reasonable request.
References
Imada, M., Fujimori, A. & Takura, Y. Metal-insulator transitions. Rev. Mod. Phys. 70, 1039–1263 (1998).
Grüner, G. The dynamics of charge-density waves. Rev. Mod. Phys. 60, 1129–1181 (1988).
Medarde, M. L. Structural, magnetic and electronic properties of RNiO3 perovskites (R=rare earth). J. Phys. Condens. Matter 9, 1679–1707 (1997).
Torrance, J. B., Lacorre, P., Nazzal, A. L., Ansaldo, E. J. & Niedermayer, C. Systematic study of insulator-metal transitions in perovskites RniO3 (R=Pr, Nd, Sm, Eu) due to closing of charge-transfer gap. Phys. Rev. B 45, 8209–8212 (1992).
Liu, J. et al Heterointerface engineered electronic and magnetic phases of NdNiO3 thin films. Nat. Commun. 4, 2714 (2013).
Scherwitzl, R. et al Metal-insulator transition in ultrathin LaNiO3 films. Phys. Rev. Lett. 106, 246403 (2011).
Mazin, I. I. et al Charge ordering as alternative to Jahn-Teller distortion. Phys. Rev. Lett. 98, 176406 (2007).
Medarde, M. L. et al Charge disproportionation in RniO3 perovskites (R=rare earth) from high-resolution X-ray absorption spectroscopy. Phys. Rev. B 80, 245105 (2009).
Mizokawa, T. et al Electronic structure of PrNiO3 studied by photoemission and X-ray-absorption spectroscopy: band gap and orbital ordering. Phys. Rev. B 52, 13865–13873 (1995).
Park, H., Millis, A. J. & Marianetti, C. A. Site-selective Mott transition in rare-earth-element nickelates. Phys. Rev. Lett. 109, 156402 (2012).
Lau, B. & Millis, A. J. Theory of the magnetic and metal-insulator transitions in RNiO3 bulk and layered structures. Phys. Rev. Lett. 110, 126404 (2013).
Johnston, S., Mukherjee, A., Elfimov, I., Berciu, M. & Sawatzky, G. A. Charge disproportionation without charge-transfer in the rare-earth-element nickelates as a possible mechanism for the metal-insulator transition. Phys. Rev. Lett. 112, 106404 (2014).
Green, R. J., Haverkort, M. W. & Sawatzky, G. A. Bond disproportionation and dynamical charge fluctuations in the perovskite rare-earth nickelates. Phys. Rev. B 94, 195127 (2016).
Medarde, M., Lacorre, P., Conder, K., Fauth, F. & Furrer, A. Giant 16O-18O isotope effect on the metal-insulator transition of RNiO3 perovskites (R=rare earth). Phys. Rev. Lett. 80, 2397–2400 (1998).
Boris, A. V. et al Dimensionality control of electronic phase transitions in nickel-oxide superlattices. Science 332, 937–940 (2011).
Hepting, M. et al Tunable charge and spin order in PrNiO3 thin films and superlattices. Phys. Rev. Lett. 113, 227206 (2014).
Kim, T. H. et al Polar metals by geometric design. Nature 533, 68–72 (2016).
Benckiser, E. et al Orbital reflectometry of oxide heterostructures. Nat. Mater. 10, 189–193 (2011).
Middey, S. et al Physics of ultrathin films and heterostructures of rare-earth nickelates. Annu. Rev. Mater. Res. 46, 305–334 (2016).
Alonso, J. A., Martinez-Lope, M. J., Casais, M. T., García-Muñoza, J. L. & Fernandez-Diaz, M. T. Room-temperature monoclinic distortion due to charge disproportionation in RNiO3 perovskites with small rare-earth cations (R=Ho, Y, Er, Tm, Yb, and Lu): a neutron diffraction study. Phys. Rev. B 61, 1756–1763 (2000).
Bisogni, V. et al Ground-state oxygen holes and the metal-insulator transition in the negative charge-transfer rare-earth nickelates. Nat. Commun. 7, 13017 (2016).
Zaanen, J., Sawatzky, G. A. & Allen, J. W. Band gaps and electronic structure of transition-metal compounds. Phys. Rev. Lett. 55, 418–421 (1985).
Khomskii, D. I. Unusual valence, negative charge-transfer gaps and self-doping in transition-metal compounds. Lith. J. Phys. 37, 65 (1997).
Mizokawa, T. et al Origin of the band gap in the negative charge-transfer energy compound NaCuO2. Phys. Rev. Lett. 67, 1638–1641 (1991).
Li, B. et al Insulating pockets in metallic LaNiO3. Adv. Electron. Mater. 2, 1500261 (2016).
Piamonteze, C. et al Short-range charge order in RNiO3 perovskites (R=Pr, Nd, Eu, Y) probed by x-ray-absorption spectroscopy. Phys. Rev. B 71, 012104 (2005).
García-Muñoza, J. L. et al. μSR study of short-range charge order in YNiO3 above the monoclinic-orthorhombic transition. Physica B 374, 87–90 (2006).
Dyre, J. C. The random free-energy barrier model for ac conduction in disordered solids. J. Appl. Phys. 64, 2456 (1988).
Heres, M., Cosby, T., Mapesa, E. U. & Sangoro, J. Probing nanoscale ion dynamics in ultrathin films of polymerized ionic liquids by broadband dielectric spectroscopy. ACS Macro Lett. 5, 1065–1069 (2016).
Ha Sieu, D. et al Hall effect measurements on epitaxial SmNiO3 thin films and implications for antiferromagnetism. Phys. Rev. B 87, 125150 (2013).
Jaramillo, R., Ha, S. D., Silevitch, D. M. & Ramanathan, S. Origins of bad-metal conductivity and the insulator-metal transition in the rare-earth nickelates. Nat. Phys. 10, 304–307 (2014).
Foyevtsova, K., Khazraie, A., Elfimov, I. & Sawatzky, G. A. Hybridization effects and bond disproportionation in the bismuth perovskites. Phys. Rev. B 91, 121114 (2015).
Plumb, N. C. et al Momentum-resolved electronic structure of the high-Tc superconductor parent compound BaBiO3. Phys. Rev. Lett. 117, 037002 (2016).
Sreedhar, K. et al Electronic properties of the metallic perovskite LaNiO3: correlated behavior of 3d electrons. Phys. Rev. B 46, 6382–6386 (1992).
Neuefeind, J., Feygenson, M., Carruth, J., Hoffmann, R. & Chipley, K. K. The nanoscale ordered materials diffractometer NOMAD at the spallation neutron source SNS. Nucl. Instrum. Methods Phys. Res. Sect. B-Beam Interact. Mater. At. 287, 68–75 (2012).
Soper, A. K. & Barney, E. R. On the use of modification functions when Fourier transforming total scattering data. J. Appl. Crystallogr. 45, 1314–1317 (2012).
Toby, B. H. EXPGUI, a graphical user interface for GSAS. J. Appl. Crystallogr. 34, 210–213 (2001).
Farrow, C. L. et al PDFfit2 and PDFgui: computer programs for studying nanostructure in crystals. J. Phys.: Condens. Matter 19, 335219 (2007).
Acknowledgements
The authors thank M. Berciu, N. C. Plumb, G. Sawatzky, and M. Fitzsimmons for stimulating discussions. This work was supported by University of Tennessee’s Office of Research & Engagements Organized Research Unit program. A portion of this research used resources at the Spallation Neutron Source, a DOE Office of Science User Facility operated by the Oak Ridge National Laboratory. H.Z. acknowledges support from NSF-DMR-1350002. J.A.A. acknowledges the Spanish MINECO for granting the project MAT2013-41099-R. Collection and interpretation of PDF was supported as part of the Materials Science of Actinides, an Energy Frontier Research Center funded by the US Department of Energy, Office of Science, Basic Energy Sciences under Award # DE-SC0001089.
Author information
Authors and Affiliations
Contributions
J. Shamblin led the experimental effort and analyzed all of the data. J. Shamblin, J.N., and M.L. performed the neutron scattering experiments. J. Shamblin, M.H., and J. Sangoro performed the broadband dielectric spectroscopy experiments. J.A.A. and H.Z. were responsible for sample preparation and characterization. S.J. conceived of the project and was responsible for project management. J. Shamblin and S.J. wrote the paper with input from all authors.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Shamblin, J., Heres, M., Zhou, H. et al. Experimental evidence for bipolaron condensation as a mechanism for the metal-insulator transition in rare-earth nickelates. Nat Commun 9, 86 (2018). https://doi.org/10.1038/s41467-017-02561-6
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-017-02561-6
- Springer Nature Limited
This article is cited by
-
Small-polaron transport in perovskite nickelates
Scientific Reports (2023)
-
Quantifying the role of the lattice in metal–insulator phase transitions
Communications Physics (2022)
-
Tunable resistivity exponents in the metallic phase of epitaxial nickelates
Nature Communications (2020)
-
Quantum Monte Carlo study of lattice polarons in the two-dimensional three-orbital Su–Schrieffer–Heeger model
npj Quantum Materials (2020)