Abstract
Cubic materials host high crystal symmetry and hence are not expected to support anisotropy in transport phenomena. In contrast to this common expectation, here we report an anomalous anisotropy of spin current can emerge in the (001) film of Mn3Pt, a noncollinear antiferromagnetic spin source with face-centered cubic structure. Such spin current anisotropy originates from the intertwined time reversal-odd (\({{{{{\mathscr{T}}}}}}\)-odd) and time reversal-even (\({{{{{\mathscr{T}}}}}}\)-even) spin Hall effects. Based on symmetry analyses and experimental characterizations of the current-induced spin torques in Mn3Pt-based heterostructures, we find that the spin current generated by Mn3Pt (001) exhibits exotic dependences on the current direction for all the spin components, deviating from that in conventional cubic systems. We also demonstrate that such an anisotropic spin current can be used to realize low-power spintronic applications such as the efficient field-free switching of the perpendicular magnetizations.
Introduction
The anisotropy of transport phenomena is determined by the group symmetry and hence emerges in materials with low symmetry1,2,3,4,5,6. The high-sy6mmetry cubic materials widely used in electronic devices are usually not expected to host a strong transport anisotropy. A typical example is the widely used cubic structured spin source materials such as Pt, which hosts the isotropic spin Hall effect (SHE) to generate an out-of-plane spin current and the associated spin-orbit torque (SOT) for the manipulation of the magnetizations in spintronic devices7. The performance of such a device is independent of the current direction since the spin Hall conductivity (SHC) \({\sigma }_{{zx}}^{y}\) (in the form of \({\sigma }_{{ij}}^{p}\), where \(i\), \(j\), and \(p\) are the generated spin-current, the driven charge-current, and spin polarization directions, respectively) is invariant under rotation transformations of the coordinate system8,9. It would be interesting from the fundamental point of view and desirable for spintronic applications to find a new mechanism for the emergence of the anisotropic spin current in cubic spin sources even with the high symmetry film directions.
Here we demonstrate that an anomalous anisotropy of the spin current can be generated in noncolinear antiferromagnetic Mn3Y (Y= Pt, Ir, or Rh, to be distinguished from Mn3X, X= Sn, Ge, or Ga) family with face-centered cubic structure even for the high symmetric (001) film, due to the noncolinear antiferromagnetism and hence the intertwined time-reversal-even (\({{{{{\mathscr{T}}}}}}-{{{{{\rm{even}}}}}}\)) and time-reversal-odd (\({{{{{\mathscr{T}}}}}}-{{{{{\rm{odd}}}}}}\)) parts of SHE. The noncollinear magnetic configuration of Mn3Y allows not only conventional SHC \({\sigma }_{{zx}}^{y}\) but also unconventional \({\sigma }_{{zx}}^{x}\), \({\sigma }_{{zx}}^{z}\), and all of them exhibit exotic dependence on the current direction. Using Mn3Pt as a representative example, we confirm the anisotropic \({\sigma }_{{zx}}^{p}\) by the measurements of the current-induced spin-torque ferromagnetic resonance (ST-FMR) and the anomalous Hall effect (AHE) loop shift of the ferromagnetic layers adjacent to the Mn3Pt layer in a SOT device. We also show this spin current can realize efficient field-free switching of the perpendicular magnetizations in ferromagnets, and the switching performances can be optimized according to such an anomalous anisotropy.
Results
Symmetry analyses
Mn3Y (Y = Pt, Ir or Rh) is a material family that crystallizes in a cubic Cu3Au-type structure10,11. As depicted in Fig. 1, the Mn atoms form kagome-type lattice planes stacked along the [111] direction. In its paramagnetic phase at high temperatures (Fig. 1a), the preserved time-reversal symmetry (\({{{{{\mathscr{T}}}}}}\)) only allows the \({{{{{\mathscr{T}}}}}}\)-even SHE12,13, and the space group \({Pm}\bar{3m}\) enforces the isotropic \({\sigma }_{{zx}}^{y,{{{{{\rm{even}}}}}}}\), i.e., \({\sigma }_{{zx}}^{y,{{{{{\rm{even}}}}}}}({\phi }_{{{{{{\rm{E}}}}}}}=0^\circ )={\sigma }_{{zx}}^{y,{{{{{\rm{even}}}}}}}({\phi }_{{{{{{\rm{E}}}}}}}\, \ne\, 0^\circ )\), where \({\phi }_{{{{{{\rm{E}}}}}}}\) is used to denote the in-plane current direction with respect to an in-plane reference direction [100]. In an SOT device where a ferromagnetic layer with a perpendicular magnetization is deposited on the Mn3Y (001) film (Fig. 1b), an out-of-plane y-polarized spin current independent of the in-plane charge current direction can be generated in Mn3Y, which enters the top ferromagnetic layer and exert a damping-like torque \(\sim {{{{{\bf{m}}}}}}\times ({{{{{\bf{m}}}}}}\times {{{{{\bf{y}}}}}})\) to switch the ferromagnetic magnetization12,13,14. Such a switching requires a high current density and an external assisting magnetic field for deterministic switching and hence is inefficient for realistic applications15,16,17,18,19,20,21,22,23.
Below the Néel temperature (\({T}_{{{{{{\rm{N}}}}}}}\)), Mn3Y is antiferromagnetic with a noncollinear “head-to-head” or “tail-to-tail” alignments of Mn moments in the kagome planes (Fig. 1c). Its magnetic space group \(R\bar{3}{m^{\prime}}\) allows not only the conventional \({\sigma }_{{zx}}^{y,{{{{{\rm{even}}}}}}}\) but also the unconventional \({\sigma }_{{zx}}^{x,{{{{{\rm{even}}}}}}}\) and \({\sigma }_{{zx}}^{z,{{{{{\rm{even}}}}}}}\). These SHC are dependent on the current direction as:
Therefore, the magnitudes of the \({{{{{\mathscr{T}}}}}}-{{{{{\rm{even}}}}}}\) SHC are the same for currents along the primary directions [100] (\({\phi }_{{{{{{\rm{E}}}}}}}=0^\circ\)) and [010] (\({\phi }_{{{{{{\rm{E}}}}}}}=90^\circ\)). On the other hand, the noncollinear antiferromagnetism breaks \({{{{{\mathscr{T}}}}}}\) symmetry and introduces non-spin-degenerate Fermi surfaces in Mn3Y, which contribute to the \({{{{{\mathscr{T}}}}}}\)-odd SHE (also termed as magnetic SHE, MSHE)24 with the SHC:
These \({{{{{\mathscr{T}}}}}}-{{{{{\rm{odd}}}}}}\) SHC for currents along the primary directions [100] (\({\phi }_{{{{{{\rm{E}}}}}}}=0^\circ\)) and [010] (\({\phi }_{{{{{{\rm{E}}}}}}}=90^\circ\)) also have the same magnitudes. However, the net SHC contributed by the intertwined \({{{{{\mathscr{T}}}}}}\)-even and \({{{{{\mathscr{T}}}}}}-{{{{{\rm{odd}}}}}}\) SHE has a more complicated anisotropy:
where \({\lambda }_{i}\) and \({\mu }_{i}\) are constants and can be used to estimate the relative strength of \({{{{{\mathscr{T}}}}}}\)-even and \({{{{{\mathscr{T}}}}}}\)-odd SHE. Figure 1e schematically show the \({\phi }_{{{{{{\rm{E}}}}}}}\) dependence of \({\sigma }_{{zx}}^{p}\) and its decomposition into the \({{{{{\mathscr{T}}}}}}\)-even and \({{{{{\mathscr{T}}}}}}\)-odd components using arbitrary parameters (see discussion in Supplementary Note 1). Such anisotropy is anomalous for cubic systems, and particularly unexpected for the high symmetric (001) plane. Figure 1d illustrates the SOT exerted by the anisotropic spin current in Mn3Y. The existence of an unconventional torque component \(\sim {{{{{\bf{m}}}}}}\times ({{{{{\bf{m}}}}}}\times {{{{{\bf{z}}}}}})\) can directly change the effective damping and allows the efficient field-free switching of perpendicular magnetization with a small current25,26,27,28,29. One can further design the in-plane current direction for a maximum \(z\)-polarization in the out-of-plane spin current to optimize the performance of the SOT device.
Characterization of the SOT associated with \({\sigma }_{{ij}}^{p}\) (p = x, y, z) by ST-FMR
Here, we use Mn3Pt to demonstrate the anomalous anisotropy of spin current in Mn3Y, which has a \({T}_{{{{{{\rm{N}}}}}}}\) of ~475 K10,11,30,31. We first investigate the current-induced SOT in (001)-oriented Mn3Pt/permalloy (Py) heterostructures by the ST-FMR technique. More details about the sample preparation and characterization are provided in Methods and Supplementary Note 2. The Mn3Pt/Py heterostructure is patterned with microwave-compatible contacts whose orientation is varied to study the SOT anisotropy as a function of the azimuthal angle \({\phi }_{{{{{{\rm{E}}}}}}}\), i.e., the angle between the microwave current \({I}_{{{{{{\rm{rf}}}}}}}\) and the \([100]\) direction of Mn3Pt, as illustrated in Fig. 2a. Here the x, y, z axes form local frames that change with the direction of \({I}_{{{{{{\rm{rf}}}}}}}\), i.e., \({I}_{{{{{{\rm{rf}}}}}}}\) is always along x. For each device with a fixed \({\phi }_{{{{{{\rm{E}}}}}}}\), an in-plane external magnetic field \({H}_{{{{{{\rm{ext}}}}}}}^{\parallel }\) is swept at an angle \({\phi }_{{{{{{\rm{H}}}}}}}\) with respect to \({I}_{{{{{{\rm{rf}}}}}}}\) (Fig. 2a). The ST-FMR signal is a rectified voltage \({V}_{{{{{{\rm{mix}}}}}}}\), whose lineshape can be decomposed into a symmetric component \({V}_{{{{{{\rm{s}}}}}}}\) and an antisymmetric component \({V}_{{{{{{\rm{a}}}}}}}\) near the resonant condition32, characterizing the in-plane SOT \({\tau }_{\parallel }\) and out-of-plane SOT \({\tau }_{\perp }\), respectively, allowing the full determination of the damping-like and field-like SOT from all possible spin polarizations (Supplementary Note 3)33,34. For the in-plane \({{{{{\bf{m}}}}}}\) of Py, \({\tau }_{\perp }\) may come from the damping-like SOT associated with \({\sigma }_{{zx}}^{z}\), while it also includes the field-like contribution from \({\sigma }_{{zx}}^{y}\), \({\sigma }_{{zx}}^{x}\), and the Oersted field.
In our Pt/Py reference sample, \({V}_{{{{{{\rm{mix}}}}}}}\) is symmetric about \({H}_{{{{{{\rm{ext}}}}}}}^{{||}}\), since the spin current is generated solely from the conventional SHE and Oersted field (Supplementary Note 3). In Mn3Pt, however, the measured \({V}_{{{{{{\rm{mix}}}}}}}\) (\({\phi }_{{{{{{\rm{H}}}}}}}=\) 10°) does not overlap with \({-V}_{{{{{{\rm{mix}}}}}}}\) (\({\phi }_{{{{{{\rm{H}}}}}}}=\) 190°), i.e., \({V}_{{{{{{\rm{mix}}}}}}}\) does not exhibit a perfect inversion with the reversal of \({H}_{{{{{{\rm{ext}}}}}}}^{{||}}\), indicating the presence of unconventional SOT associated with the SHC other than \({\sigma }_{{zx}}^{y}\) (Supplementary Note 3)1,35,36,37,38,39,40.
For further investigation, we measure the \({\phi }_{{{{{{\rm{H}}}}}}}\) dependence of \({V}_{{{{{{\rm{a}}}}}}}\) and \({V}_{{{{{{\rm{s}}}}}}}\) at various \({\phi }_{{{{{{\rm{E}}}}}}}\) (Supplementary Note 4). The \({\phi }_{{{{{{\rm{H}}}}}}}\) dependence can be fitted by1,32,36,41:
where \({S}_{{{{{{\rm{DL}}}}}}}^{y}\), \({S}_{{{{{{\rm{DL}}}}}}}^{x}\), and \({A}_{{{{{{\rm{DL}}}}}}}^{z}\) are coefficients for the damping-like SOT associated with \({\sigma }_{{zx}}^{y}\), \({\sigma }_{{zx}}^{x}\), and \({\sigma }_{{zx}}^{z}\), respectively, while \({A}_{{{{{{\rm{FL}}}}}}}^{y}\), \({A}_{{{{{{\rm{FL}}}}}}}^{x}\), and \({S}_{{{{{{\rm{FL}}}}}}}^{z}\) correspond to the field-like counterparts. Note that the contribution of the field-like SOT from the Oersted field is included in \({A}_{{{{{{\rm{FL}}}}}}}^{y}\). We show in Fig. 2b how \({V}_{{{{{{\rm{s}}}}}}}\) (\({\phi }_{{{{{{\rm{E}}}}}}}=45^\circ\)) is decomposed into the contributions from \({\sigma }_{{zx}}^{p}\) (see Supplementary Note 4 for \({V}_{{{{{{\rm{a}}}}}}}\) and \({V}_{{{{{{\rm{s}}}}}}}\) at \({\phi }_{{{{{{\rm{E}}}}}}}\) = 0°, 45°, and 90°). Important observations can be made: (i) Despite a subdominant contribution, the presence of nonzero \({\sigma }_{{zx}}^{x}\) and \({\sigma }_{{zx}}^{z}\) is evident, consistent with the asymmetric \({V}_{{{{{{\rm{mix}}}}}}}({H}_{{{{{{\rm{ext}}}}}}}^{{||}})\) mentioned above. (ii) Compared to the case of \({\phi }_{{{{{{\rm{E}}}}}}}=\) 0°, the \({\sigma }_{{zx}}^{z}\) contribution is enhanced for \({\phi }_{{{{{{\rm{E}}}}}}}=\) 45° (Supplementary Note 4), consistent with the previous observation of a stronger (weaker) \({\sigma }_{{zx}}^{z}\) for \({I}_{{{{{{\rm{rf}}}}}}}\) applied parallel (perpendicular) to the magnetic mirror plane of Mn3Pt38. (iii) A notable discrepancy can be seen between the cases of \({\phi }_{{{{{{\rm{E}}}}}}}=\) 0° and \({\phi }_{{{{{{\rm{E}}}}}}}=\) 90°, which is unexpected considering their equivalency in both the crystal and magnetic structures. This is different to previous reports in cubic systems where the anisotropic spin currents have never been observed in (001) films with the highest crystal symmetry37,42.
To better visualize the SOT anisotropy, we show in Fig. 2c–e the \({\phi }_{{{{{{\rm{E}}}}}}}\) dependence of the damping-like SOT efficiency per unit current density \({\xi }_{{{{{{\rm{DL}}}}}},j}^{p}\), which can be estimated by32,39:
where \(e\), \(\hslash\), \({t}_{{{{{{\rm{HM}}}}}}}\), \({t}_{{{{{{\rm{FM}}}}}}}\), and \({M}_{{{{{{\rm{s}}}}}}}\) represent the elementary charge, the reduced Planck constant, the thickness of the heavy metal (HM, Mn3Pt) and ferromagnetic (FM, Py) layer, and the saturation magnetization of the FM layer, respectively. The effective magnetization \({M}_{{{{{{\rm{eff}}}}}}}\) can be obtained from ST-FMR measurements performed at a sequence of microwave frequencies \(f\) following the Kittel relation. Note that in our samples \({A}_{{{{{{\rm{FL}}}}}}}^{y}\) is dominated by the Oersted field (Supplementary Note 5), making \({A}_{{{{{{\rm{FL}}}}}}}^{y}\) a good measure of the current density in the Mn3Pt layer. In principle, one can derive the relative magnitudes of \({\sigma }_{{zx}}^{y}\), \({\sigma }_{{zx}}^{x}\), and \({\sigma }_{{zx}}^{z}\) by fitting the \({\phi }_{{{{{{\rm{E}}}}}}}\) dependence of \({\xi }_{{{{{{\rm{DL}}}}}},j}^{p}\) using Eq. (3). The fitting yields nonzero values of \({\lambda }_{y}\,\)= 0.04359, \({\mu }_{y}\) = 0.01126, \({\lambda }_{x}\) = 0.00328, \({\mu }_{x}\) = 0.02038, \({\lambda }_{z}\) = 0.02049, and \({\mu }_{z}\) = 0.03176. The values of \(\left|{\lambda }_{i}/{\mu }_{i}\right|\) deviating from 1 is clear evidence of the intertwined \({{{{{\mathscr{T}}}}}}\)-even and \({{{{{\mathscr{T}}}}}}\)-odd SHE, resulting in a discrepancy between the signal at \({\phi }_{{{{{{\rm{E}}}}}}}=\) 0° and \({\phi }_{{{{{{\rm{E}}}}}}}=\) 90°, manifested as the different values of \({\xi }_{{{{{{\rm{DL}}}}}},j}^{i}\) (\({\phi }_{{{{{{\rm{E}}}}}}}=\) 0°) and \({\xi }_{{{{{{\rm{DL}}}}}},j}^{i}\) (\({\phi }_{{{{{{\rm{E}}}}}}}=90^\circ\)). Such an anomalous anisotropy between the spin current polarization and the associated SOT along two orthogonal cubic directions is the main experimental finding of this work.
AHE loop shift with a threshold current
Since the unconventional z-polarized spin current is important for low-power switching of high-density spintronic devices with perpendicular magnetizations, we build Mn3Pt(5)/Ti(3)/CoFeB(1)/MgO(2)/SiO2(2) heterostructures (numbers in parentheses indicate layer thickness in nanometers) with perpendicular magnetic anisotropy (PMA) to further quantify \({\sigma }_{{zx}}^{z}\) (Fig. 3a). The nonmagnetic interlayer Ti was used to provide the PMA of CoFeB and magnetically decouple the Mn3Pt and CoFeB layers43, and hence it does not contribute to the magnetization switching (Supplementary Note 6). The SOT contribution from the Ti layer is negligible due to the extremely small spin Hall angle of Ti43,44. The PMA of this heterostructure is confirmed by the square hysteresis loop in the Hall resistance \({R}_{{xy}}\) as a function of the out-of-plane magnetic field \({H}_{{{{{{\rm{ext}}}}}}}^{z}\) (Supplementary Note 7).
We first perform the AHE loop shift measurement on the PMA heterostructures45. As shown in Fig. 3b, the AHE loop under an out-of-plane magnetic field \({H}_{{{{{{\rm{ext}}}}}}}^{z}\) and I = 1 mA along \([110]\) (i.e., \({\phi }_{{{{{{\rm{E}}}}}}}=45^\circ\)) almost overlaps with the loop under I = −1 mA. However, as shown in Fig. 3c, when I is increased to ±16 mA, considerable AHE loop shift occurs, i.e., the center of the loop is shifted to positive (negative) field values for positive (negative) I. Such a shift is indicative of an effective field \({H}_{{{{{{\rm{eff}}}}}}}^{z}\) acting in conjunction with the external \({H}_{{{{{{\rm{ext}}}}}}}^{z}\) (see also Supplementary Note 8 and Note 9). Figure 3d depicts the I dependence of \({H}_{{{{{{\rm{eff}}}}}}}^{z}\) (see “Methods”) for selected \({\phi }_{{{{{{\rm{E}}}}}}}\) of 0°, 45°, and 90°. Echoing the qualitatively different behavior between I = ±1 and ±16 mA, a clear threshold current effect is evident: \({H}_{{{{{{\rm{eff}}}}}}}^{z}\) abruptly increases from near zero when I is greater than a threshold value45, characteristic of a damping-like \({\tau }_{\perp }\) originating from \({\sigma }_{{zx}}^{z}\)6,29,43,45.
To better visualize the anisotropy of \({H}_{{{{{{\rm{eff}}}}}}}^{z}\) which characterizes the anisotropy of \({\sigma }_{{zx}}^{z}\) and the associated \({\tau }_{\perp }\), we plot in Fig. 3e the \({\phi }_{{{{{{\rm{E}}}}}}}\) dependence of the \({H}_{{{{{{\rm{eff}}}}}}}^{z}/J\), where \(J\) is the applied in-plane current density. With increasing \({\phi }_{{{{{{\rm{E}}}}}}}\), \({H}_{{{{{{\rm{eff}}}}}}}^{z}/J\) first increases to a maximum for \({\phi }_{{{{{{\rm{E}}}}}}}=\) 45°, and then decreases and changes the sign around \({\phi }_{{{{{{\rm{E}}}}}}}=135^\circ\). The \({H}_{{{{{{\rm{eff}}}}}}}^{z}/J\) for \({\phi }_{{{{{{\rm{E}}}}}}}=\) 0° is about a half of that for \({\phi }_{{{{{{\rm{E}}}}}}}=\) 90°. This behavior is consistent with the \({\phi }_{{{{{{\rm{E}}}}}}}\) dependence of \({\xi }_{{{{{{\rm{DL}}}}}},j}^{z}\) measured by ST-FMR (Fig. 2e). Therefore, based on the similar results from two different measurements, we confirm the anomalous anisotropy of the spin current in Mn3Pt which is not expected by the cubic crystal symmetry. The \({\phi }_{{{{{{\rm{E}}}}}}}\) dependence of \({H}_{{{{{{\rm{eff}}}}}}}^{z}/J\) can be well fitted using Eq. (3) (Fig. 3e), yielding parameters \({\lambda }_{z}\) = 3.48 and \({\mu }_{z}\) = 9.59. \({\lambda }_{z}/{\mu }_{z}=0.36\) indicates that such an anomalous anisotropy is originated from the coexistence of \({{{{{\mathscr{T}}}}}}\)-odd and \({{{{{\mathscr{T}}}}}}\)-even SHE in Mn3Pt, where \({{{{{\mathscr{T}}}}}}\)-odd SHE is predominating. We have estimated the actual device temperature to be ~331 K for the maximum current in the AHE loop shift measurement (Supplementary Note 10), which is well below the TN of Mn3Pt (~475 K). Therefore, the AFM spin texture and the associated spin current largely remain unaffected by the Joule heating effects.
Field-free deterministic magnetization switching
The existence of \({\sigma }_{{zx}}^{z}\) allows the field-free deterministic switching of the perpendicular magnetization in the CoFeB layer adjacent to Mn3Pt. However, such switching has not been achieved in Mn3Pt by previous efforts. As will be shown below, our efforts in doing so not only end in success, but also provide solid evidence for the predominating role of the \({{{{{\mathscr{T}}}}}}\)-odd SHE which, in turn, supports the mechanism proposed above for the anomalous anisotropy.
As shown in Fig. 4a, the injected pulse current, when above a threshold value, is able to change the sign of \({R}_{{xy}}\) for various \({\phi }_{{{{{{\rm{E}}}}}}}\), indicating that deterministic magnetization switching of the PMA CoFeB layer has been realized without an in-plane assistant field (see “Methods” and Supplementary Note 11 for more details). The change of the switching Hall resistance is represented by \(\triangle {R}_{{xy}}\), which is the half of the difference between \({R}_{{xy}}\) at zero current after the application of the positive and negative current pulses. We find that the \({\phi }_{{{{{{\rm{E}}}}}}}\) dependence of \(\triangle {R}_{{xy}}\) is consistent with that of \({H}_{{{{{{\rm{eff}}}}}}}^{z}/J\) (Fig. 4b). The largest \(\triangle {R}_{{xy}}\) corresponding to a switching ratio of ≈77% is achieved when \({H}_{{{{{{\rm{eff}}}}}}}^{z}/J\) is maximum around \({\phi }_{{{{{{\rm{E}}}}}}}=\) 45°, indicating the optimal current direction for designing SOT devices based on Mn3Pt. It is note that the actual device temperature is ~356 K for the maximum current in the magnetization switching measurement (Supplementary Note 10), and this temperature is well below the TN of Mn3Pt.
The magnetic space group \(R\bar{3}{m^{\prime}}\) supports a small but nonvanishing net magnetization in Mn3Pt. The presence of such a net magnetization allows the switching of the magnetic order parameter by a small magnetic field, which is equivalent to the \({{{{{\mathscr{T}}}}}}\)-operation which changes the sign of the \({{{{{\mathscr{T}}}}}}\)-odd SHC but does not influence the \({{{{{\mathscr{T}}}}}}\)-even SHC29,46. This property can be used to verify whether \({{{{{\mathscr{T}}}}}}\)-odd SHE dominates the anisotropic spin current in Mn3Pt and hence the field-free switching of the perpendicular magnetization. Here we perform the current-induced magnetization switching measurements for \({\phi }_{{{{{{\rm{E}}}}}}}=0^\circ\) with the application of a premagnetization field \({H}_{{{{{{\rm{pre}}}}}}}\) of 8 T along the \([001]\) direction, which aligns the magnetic order parameter of Mn3Pt as depicted in the inset of Fig. 4c. The polarity of the field-free switching is anticlockwise in this case (Fig. 4d). Applying the \({H}_{{{{{{\rm{pre}}}}}}}\) to the \([00\bar{1}]\) direction reverses the magnetic order parameter of Mn3Pt and changes the switching polarity to clockwise. This clearly proves the predominating role of the \({{{{{\mathscr{T}}}}}}\)-odd SHE47 for the spin current in Mn3Pt and hence the field-free switching of the perpendicular magnetization. We have performed additional AHE loop shift measurements following similar procedures to that adopted in the magnetization switching measurements (Supplementary Note 12). As shown in Fig. S12, the loop shifts for an \({H}_{{{{{{\rm{pre}}}}}}}\) of 8 T along the [001] and [\(00\bar{1}\)] directions are opposite, consistent with the reversal of the switching polarity.
Discussion
We have demonstrated, via the measurements of ST-FMR, AHE loop shift, and current-induced magnetization switching, the existence of an anomalous anisotropy of the spin current generated by the spin source Mn3Pt with a cubic crystal structure and a noncollinear antiferromagnetic order. While the observation of a spin polarization and the associated SOT along the out-of-plane direction able to induce field-free deterministic magnetization switching in a neighboring FM layer is interesting in itself, the most significant finding of our work is the anisotropy of the SOT when the electrical current is injected along orthogonal cubic directions.
Unlike the AHE, the intrinsic contribution to the conventional \({{{{{\mathscr{T}}}}}}\)-even SHE is expected to be isotropic in a nonmagnetic cubic spin source, i.e., it exhibits an isotropic SHC7,8,9. Anisotropic behavior of the conventional SHE in cubic spin sources has only been previously demonstrated in certain Pt-based heterostructures. For example, the spin Hall angle \({\theta }_{{{{{{\rm{SH}}}}}}}\) determined from the spin Hall magnetoresistance and the damping-like SOT were both found to be different between \(I\) // \([001]\) and \(I\) // \([1\bar{1}0]\)42 or between \(I\) // \([1\bar{1}0]\) and \(I\) // \([11\bar{2}]\)38 in these heterostructures. However, the two sets of orthogonal directions involved are not perfectly equivalent even from the crystallographic point of view, providing the opportunity for factors like the anisotropy in the resistivity \(\rho\) and the spin diffusion length to impact the observed anisotropy via, e.g., \({\theta }_{{{{{{\rm{SH}}}}}}}\) ~ \(\rho {\sigma }_{{ij}}^{p,{{{{{\rm{even}}}}}}}\)48,49, although interfacial Rashba-Edelstein effect was also argued to contribute. In sharp contrast, the \([100]\) and \([010]\) directions of Mn3Pt, along which we identify an anisotropy, are perfectly equivalent in the crystal structure. This equivalency is not affected even when the magnetic structure is taken into account. The \({{{{{\mathscr{T}}}}}}\)-odd MSHE evidenced by the polarity reversal in the PMA magnetization switching justifies our proposal of the \({{{{{\mathscr{T}}}}}}\)-odd MSHE and the \({{{{{\mathscr{T}}}}}}\)-even conventional SHE combined to give rise to the anomalous anisotropy, a scenario that captures all the experimental observations, including specifically how the SOT efficiency extracted from ST-FMR, the out-of-plane effective field estimated from the AHE loop shift, and the current-induced magnetization switching ratio, vary with changing the injected current direction with respect to the crystal axes.
To our knowledge, our work presents the first observation—in a single material—of the coexistence of \({{{{{\mathscr{T}}}}}}\)-even12,13,50,51 and \({{{{{\mathscr{T}}}}}}\)-odd SHE24,29,39,40,47,52,53,54,55,56,57,58, which usually exist solely or independently in distinct material systems and do not show an intertwinement. The cooperation of the \({{{{{\mathscr{T}}}}}}\)-even and \({{{{{\mathscr{T}}}}}}\)-odd SHE offers anomalous transport anisotropy and useful functionality. The anomalous anisotropy uncovered here adds a new tuning knob to spintronic devices utilizing SOT: one could envision devices based on a cubic spin source, whose ability and efficiency in controlling the magnetization of the FM layer can be modified simply by changing the direction of the injected electrical current from one principle cubic axis to its orthogonal counterpart; meanwhile, most other properties are kept identical in this process due to the high cubic symmetry.
There are many other cubic kagome noncollinear antiferromagnets, such as Mn3Ir36, and Mn3AN (A = Ga, Sn, Ni, etc.)35,37,59 hosting a noncollinear magnetic order and a magnetic group symmetry similar to Mn3Pt discussed in this work, which may also support the anisotropic spin currents. The strength of such anisotropy can be further enhanced by the exotic electronic structures in these materials. For example, the bulk Weyl cones and associated surface Fermi arcs have been observed in some kagome noncollinear antiferromagnets60,61, which may strongly enhance the transport anisotropy. Moreover, in the cubic kagome noncollinear antiferromagnets, the strong correlation effect may occur61,62, which may further enhance the transport anisotropy. We thus believe that cubic kagome noncollinear antiferromagnets are ideal material platforms for investigation of the anomalous transport anisotropy and realization of the efficient spintronic applications.
In summary, we observed an unexpected anisotropy of spin current in Mn3Pt, a cubic structured spin source with noncollinear antiferromagnetism due to the intertwined \({{{{{\mathscr{T}}}}}}\)-odd and \({{{{{\mathscr{T}}}}}}\)-even SHE. We also show the spin current generated in Mn3Pt can be used to realize efficient field-free SOT switching of ferromagnets PMA and the anomalous anisotropy can be used to optimize the switching performance. Our work offers a new route to introduce transport anisotropy in materials with high crystal symmetry, which is beneficial for designing and engineering of low-power and high-performance electronic devices.
Methods
Sample preparation
Samples of Mn3Pt, Mn3Pt/Ti/CoFeB/MgO/SiO2, Mn3Pt/Py, and Pt/Py bilayers were deposited on MgO(001) substrates by DC/RF magnetron sputtering with a base pressure of 1 × 10–7 Torr. Note that the metallic and oxide films were deposited by using DC and RF magnetron sputtering, respectively. For the deposition of Mn3Pt, the MgO(001) substrate was pre-annealed for 1 h at 700 °C before deposition to obtain a smooth and clean substrate. The deposition was performed at 500 °C. The Ar gas pressure and sputtering power were 2 mTorr and 40 W, respectively. After deposition, the Mn3Pt film was heated to 550 °C for 1.5 h to improve the crystalline quality. After cooling down to room temperature, the Ti/CoFeB/MgO/SiO2 multilayer or the Py layer were deposited onto the Mn3Pt film, respectively. The Mn3Pt/Ti/CoFeB/MgO/SiO2 heterostructure was in situ annealed at 200 °C for 30 min under vacuum conditions to promote PMA. A 2 nm SiO2 capping layer was used to protect its underlayers. For the Mn3Pt(12 nm)/Py (Ni80Fe20, 13 nm) bilayer used in the ST-FMR measurements, the Py film was prepared at room temperature, with the Ar gas pressure and sputtering power being 2 mTorr and 40 W, respectively. The control sample Pt/Py bilayers used for the ST-FMR measurements were deposited at room temperature and the Ar gas pressure and sputtering power for the Pt film were 2 mTorr and 20 W, respectively. The film thicknesses were controlled by the deposition time with a pre-calibrated deposition rate as determined by X-ray reflectivity measurements.
Device fabrication
In order to investigate the anisotropy of the spin-orbit torque of cubic Mn3Pt, samples of Mn3Pt/Ti/CoFeB/MgO and Mn3Pt (Pt)/Py were patterned into Hall bars (10 µm × 50 µm) and microstrip devices (20 µm × 50 µm), respectively, using a combination of photolithography and ion beam etching. Then, a top electrode of Ti(5 nm)/Cu(100 nm) was deposited by DC magnetron sputtering. For devices with different current directions in the sample plane, \({\phi }_{{{{{{\rm{E}}}}}}}\) ranges from 0° to 180° with a step of 15°.
Sample characterization
The thickness and crystal structure were characterized by X-ray reflectivity and high-resolution X-ray diffraction techniques with a Bruker D8 Discover diffractometer using Cu Kα radiation (λ = 0.15419 nm). The cross-sectional crystalline structure was imaged by AC-STEM (FEI Titan Themis 200) operated at 200 kV. The atomic ratio of our sample has been checked by energy-dispersive X-ray spectroscopy (EDS). The magnetic and electrical properties were measured in a magnetic property measurement system (MPMS, Quantum Design) and physical property measurement system (PPMS, Quantum Design), respectively.
ST-FMR measurements
The ST-FMR signals (\({V}_{{{{{{\rm{mix}}}}}}}\)) were measured by a Stanford Research SR830 lock-in amplifier. In the angular-dependent ST-FMR measurements, the applied microwave current with frequency and nominal power were 7 GHz and 18 dBm, respectively.
AHE loop shift measurements
The existence of \({H}_{{{{{{\rm{eff}}}}}}}^{z}\) was verified by the AHE loop shift measurements with different pulse currents, where \({H}_{{{{{{\rm{eff}}}}}}}^{z}\) is defined as the shift of the loop \({H}_{{{{{{\rm{eff}}}}}}}^{z}\left(I\right)=[|{H}_{{{{{{\rm{rev}}}}}}}^{+}\left(I\right)|-|{H}_{{{{{{\rm{rev}}}}}}}^{-}\left(I\right)|]/2\), with \({H}_{{{{{{\rm{rev}}}}}}}^{\pm }\left(I\right)\) being the positive and negative magnetization-reversal fields.
Current-induced magnetization switching measurements
The current-induced magnetization measurements were conducted by utilizing a Keithley 6221 current source and a 2182 nano voltmeter. For each experimental data point in the \({R}_{{xy}}\)-I loop, a pulse d.c. current \({I}_{{{{{{\rm{p}}}}}}}\) with a duration of 200 μs was applied to the Hall bar device as the write current. Then, a small probe pulse current of 0.1 mA with a duration of 2 ms was applied to monitor the \({R}_{{xy}}\). The amplitude of the write pulse current was varied to obtain a complete \({R}_{{xy}}\)-I loop.
Data availability
The data that support the findings of this study are available from the corresponding authors upon reasonable request.
References
MacNeill, D. et al. Control of spin–orbit torques through crystal symmetry in WTe2/ferromagnet bilayers. Nat. Phys. 13, 300–305 (2016).
MacNeill, D. et al. Thickness dependence of spin-orbit torques generated by WTe2. Phys. Rev. B 96, 054450 (2017).
Guimaraes, M. H. D. et al. Spin-orbit torques in NbSe2/permalloy bilayers. Nano Lett. 18, 1311–1316 (2018).
Stiehl, G. M. et al. Current-induced torques with Dresselhaus symmetry due to resistance anisotropy in 2D materials. ACS Nano 13, 2599–2605 (2019).
Song, P. et al. Coexistence of large conventional and planar spin Hall effect with long spin diffusion length in a low-symmetry semimetal at room temperature. Nat. Mater. 19, 292–298 (2020).
Liu, L. et al. Symmetry-dependent field-free switching of perpendicular magnetization. Nat. Nanotechnol. 16, 277–282 (2021).
Ikebuchi, T. et al. Crystal orientation dependence of spin Hall angle in epitaxial Pt/FeNi systems. Appl. Phys. Lett. 120, 072406 (2022).
Chudnovsky, E. M. Intrinsic spin Hall effect in noncubic crystals. Phys. Rev. B 80, 153105 (2009).
Freimuth, F., Blugel, S. & Mokrousov, Y. Anisotropic spin Hall effect from first principles. Phys. Rev. Lett. 105, 246602 (2010).
Krén, E. et al. Magnetic structures and magnetic transformations in ordered Mn3(Rh, Pt) alloys. Phys. Lett. 20, 331–332 (1966).
Krén, E. et al. Magnetic structures and exchange interactions in the Mn-Pt system. Phys. Rev. 171, 574 (1968).
Liu, L. et al. Current-induced switching of perpendicularly magnetized magnetic layers using spin torque from the spin Hall effect. Phys. Rev. Lett. 109, 096602 (2012).
Liu, L. et al. Spin-torque switching with the giant spin Hall effect of tantalum. Science 336, 555–558 (2012).
Miron, I. M. et al. Perpendicular switching of a single ferromagnetic layer induced by in-plane current injection. Nature 476, 189–193 (2011).
Yu, G. et al. Switching of perpendicular magnetization by spin–orbit torques in the absence of external magnetic fields. Nat. Nanotechnol. 9, 548–554 (2014).
You, L. et al. Switching of perpendicularly polarized nanomagnets with spin orbit torque without an external magnetic field by engineering a tilted anisotropy. Proc. Natl Acad. Sci. USA 112, 10310–10315 (2015).
Fukami, S., Anekawa, T., Zhang, C. & Ohno, H. A spin-orbit torque switching scheme with collinear magnetic easy axis and current configuration. Nat. Nanotechnol. 11, 621–625 (2016).
Oh, Y.-W. et al. Field-free switching of perpendicular magnetization through spin–orbit torque in antiferromagnet/ferromagnet/oxide structures. Nat. Nanotechnol. 11, 878–884 (2016).
Fukami, S. et al. Magnetization switching by spin-orbit torque in an antiferromagnet-ferromagnet bilayer system. Nat. Mater. 15, 535–541 (2016).
Lau, Y. C. et al. Spin-orbit torque switching without an external field using interlayer exchange coupling. Nat. Nanotechnol. 11, 758–762 (2016).
Cai, K. et al. Electric field control of deterministic current-induced magnetization switching in a hybrid ferromagnetic/ferroelectric structure. Nat. Mater. 16, 712–716 (2017).
Wang, M. et al. Field-free switching of a perpendicular magnetic tunnel junction through the interplay of spin–orbit and spin-transfer torques. Nat. Electron. 1, 582–588 (2018).
Liu, L. et al. Current-induced magnetization switching in all-oxide heterostructures. Nat. Nanotechnol. 14, 939–944 (2019).
Zelezny, J., Zhang, Y., Felser, C. & Yan, B. Spin-polarized current in noncollinear antiferromagnets. Phys. Rev. Lett. 119, 187204 (2017).
Slonczewski, J. C. Current-driven excitation of magnetic multilayers. J. Magn. Magn. Mater. 159, L1 (1996).
Sun, J. Z. Spin-current interaction with a monodomain magnetic body: a model study. Phys. Rev. B 62, 570 (2000).
Lee, K.-S., Lee, S.-W., Min, B.-C. & Lee, K.-J. Threshold current for switching of a perpendicular magnetic layer induced by spin Hall effect. Appl. Phys. Lett. 102, 112410 (2013).
Lee, D.-K. & Lee, K.-J. Spin-orbit torque switching of perpendicular magnetization in ferromagnetic trilayers. Sci. Rep. 10, 1–7 (2020).
Hu, S. et al. Efficient perpendicular magnetization switching by a magnetic spin Hall effect in a noncollinear antiferromagnet. Nat. Commun. 13, 4447 (2022).
Krén, E., Kádár, G., Pál, L. & Szabó, P. Investigation of the first‐order magnetic transformation in Mn3Pt. J. Appl. Phys. 38, 1265–1266 (1967).
Liu, Z. Q. et al. Electrical switching of the topological anomalous Hall effect in a non-collinear antiferromagnet above room temperature. Nat. Electron. 1, 172–177 (2018).
Liu, L., Moriyama, T., Ralph, D. C. & Buhrman, R. A. Spin-torque ferromagnetic resonance induced by the spin Hall effect. Phys. Rev. Lett. 106, 036601 (2011).
Sankey, J. C. et al. Measurement of the spin-transfer-torque vector in magnetic tunnel junctions. Nat. Phys. 4, 67–71 (2008).
Garello, K. et al. Symmetry and magnitude of spin–orbit torques in ferromagnetic heterostructures. Nat. Nanotechnol. 8, 587–593 (2013).
Nan, T. et al. Controlling spin current polarization through non-collinear antiferromagnetism. Nat. Commun. 11, 4671 (2020).
Zhou, J. et al. Magnetic asymmetry induced anomalous spin-orbit torque in IrMn. Phys. Rev. B 101, 184403 (2020).
You, Y. et al. Cluster magnetic octupole induced out-of-plane spin polarization in antiperovskite antiferromagnet. Nat. Commun. 12, 6524 (2021).
Bai, H. et al. Control of spin-orbit torques through magnetic symmetry in differently oriented noncollinear antiferromagnetic Mn3Pt. Phys. Rev. B 104, 104401 (2021).
Bose, A. et al. Tilted spin current generated by the collinear antiferromagnet ruthenium dioxide. Nat. Electron. 5, 267–274 (2022).
Bai, H. et al. Observation of spin splitting torque in a collinear antiferromagnet RuO2. Phys. Rev. Lett. 128, 197202 (2022).
Fang, D. et al. Spin–orbit-driven ferromagnetic resonance. Nat. Nanotechnol. 6, 413–417 (2011).
Thompson, R. et al. Anisotropic spin-orbit torque through crystal-orientation engineering in epitaxial Pt. Phys. Rev. Appl. 15, 014055 (2021).
Cao, C. et al. Efficient tuning of the spin-orbit torque via the magnetic phase transition of FeRh. ACS Nano 16, 12727 (2022).
Du, C., Wang, H., Yang, F. & Hammel, P. C. Systematic variation of spin-orbit coupling withd-orbital filling: large inverse spin Hall effect in 3d transition metals. Phys. Rev. B 90, 140407 (2014).
Baek, S. C. et al. Spin currents and spin-orbit torques in ferromagnetic trilayers. Nat. Mater. 17, 509 (2018).
Pal, B. et al. Setting of the magnetic structure of chiral kagome antiferromagnets by a seeded spin-orbit torque. Sci. Adv. 8, eabo5930 (2022).
Kimata, M. et al. Magnetic and magnetic inverse spin Hall effects in a non-collinear antiferromagnet. Nature 565, 627–630 (2019).
Zhang, W. et al. Role of transparency of platinum–ferromagnet interfaces in determining the intrinsic magnitude of the spin Hall effect. Nat. Phys. 11, 496–502 (2015).
Zhu, L. et al. Strong damping‐like spin‐orbit torque and tunable Dzyaloshinskii–Moriya interaction generated by low‐resistivity Pd1−xPtx alloys. Adv. Funct. Mater. 29, 1805822 (2019).
Sinova, J. et al. Spin Hall effects. Rev. Mod. Phys. 87, 1213–1260 (2015).
Cao, C. et al. Spin-orbit torque and Dzyaloshinskii–Moriya interaction in 4d metal Rh-based magnetic heterostructures. Appl. Phys. Lett. 118, 112402 (2021).
Zhang, Y. et al. Strong anisotropic anomalous Hall effect and spin Hall effect in the chiral antiferromagnetic compounds Mn3X (X = Ge, Sn, Ga, Ir, Rh, and Pt). Phys. Rev. B 95, 075128 (2017).
Zhang, Y. et al. Spin Hall effect emerging from a noncollinear magnetic lattice without spin–orbit coupling. N. J. Phys. 20, 073028 (2018).
Hayami, S., Yanagi, Y. & Kusunose, H. Momentum-dependent spin splitting by collinear antiferromagnetic ordering. J. Phys. Soc. Jpn. 88, 123702 (2019).
Mook, A. et al. Origin of the magnetic spin Hall effect: spin current vorticity in the Fermi sea. Phys. Rev. Res. 2, 023065 (2020).
Yuan, L.-D. et al. Giant momentum-dependent spin splitting in centrosymmetric low-Z antiferromagnets. Phys. Rev. B 102, 014422 (2020).
Chen, X. et al. Observation of the antiferromagnetic spin Hall effect. Nat. Mater. 20, 800–804 (2021).
Gonzalez-Hernandez, R. et al. Efficient electrical spin splitter based on nonrelativistic collinear antiferromagnetism. Phys. Rev. Lett. 126, 127701 (2021).
Boldrin, D. et al. Giant Piezomagnetism in Mn3NiN. ACS Appl. Mater. Interfaces 10, 18863–18868 (2018).
Yin, J. X., Lian, B. & Hasan, M. Z. Topological kagome magnets and superconductors. Nature 612, 647–657 (2022).
Kuroda, K. et al. Evidence for magnetic Weyl fermions in a correlated metal. Nat. Mater. 16, 1090–1095 (2017).
Zhang, S. S. et al. Many-body resonance in a correlated topological kagome antiferromagnet. Phys. Rev. Lett. 125, 046401 (2020).
Acknowledgements
This work was supported by the National Key Research and Development Program of China (Grant Nos. 2021YFA1600200), the National Natural Science Foundation of China (Grant Nos. 12174103, 12274411, 12274125, 12241405, 12274411 and 52250418), the Natural Science Foundation of Shanghai (Grant Nos. 21ZR1420500 and 21JC1402300), the Shanghai Pujiang Program (Grant No. 21PJ1403100), the CAS Project for Young Scientists in Basic Research (Grant No. YSBR-084), and the Natural Science Foundation of Anhui Province (Grant No. 2208085QA08).
Author information
Authors and Affiliations
Contributions
C.C. and S.C. conceived the idea and designed the experiment. D.F.S., Y.X., J.C., and Q.Z. supervised the project. C.C. and Y.W. grew the samples and performed the structural characterizations. S.C. fabricated the devices. C.C. and S.C. performed electrical transport measurements and analyzed the results together with X.Q. Z.Z. and G.Y. performed the ST-FMR measurements. L.L., T.Z., and J.C. gave suggestions on the experiments. R.C.X. and D.F.S. performed the theoretical analyses. All authors contributed to discussions. C.C., S.C., D.F.S., and Y.X. wrote the manuscript with input from all authors.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Peer review
Peer review information
Nature Communications thanks the anonymous reviewers for their contribution to the peer review of this work. A peer review file is available.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Cao, C., Chen, S., Xiao, RC. et al. Anomalous spin current anisotropy in a noncollinear antiferromagnet. Nat Commun 14, 5873 (2023). https://doi.org/10.1038/s41467-023-41568-0
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-023-41568-0
- Springer Nature Limited