Abstract
Phase change memory (PCM) is a promising nonvolatile memory to reform current commercial computing system. Inhibiting face-centered cubic (f-) to hexagonal (h-) phase transition of Ge2Sb2Te5 (GST) thin film is essential for realizing high-density, high-speed, and low-power PCM. Although the atomic configurations of f- and h-lattices of GST alloy and the transition mechanisms have been extensively studied, the real transition process should be more complex than previous explanations, e.g. vacancy-ordering model for f-to-h transition. In this study, dynamic crystallization procedure of GST thin film was directly characterized by in situ heating transmission electron microscopy. We reveal that the equilibrium to h-phase is more like an abnormal grain growth process driven by surface energy anisotropy. More specifically, [0001]-oriented h-grains with the lowest surface energy grow much faster by consuming surrounding small grains, no matter what the crystallographic reconfigurations would be on the frontier grain-growth boundaries. We argue the widely accepted vacancy-ordering mechanism may not be indispensable for the large-scale f-to-h grain growth procedure. The real-time observations in this work contribute to a more comprehensive understanding of the crystallization behavior of GST thin film and can be essential for guiding its optimization to achieve high-performance PCM applications.
Similar content being viewed by others
Introduction
As a promising candidate for storage-class memory1 to mitigate the performance gap between dynamic random access memory (DRAM) and NAND Flash memory2, phase change memory (PCM) bears excellent properties including sub 10 ns switching speed3, 4, scalability to sub 10 nm dimension5, 6, more than 1011 cyclability6, and up to 220 °C 10-year data retention ability7. In commercialized PCM devices, the reversible transitions between amorphous (a-) and crystalline (c-) phases of Ge2Sb2Te5 (GST) material are utilized to store “0” and “1” data states. The RESET operation refers to an amorphization procedure which melts the c-phase and subsequently quenches it to a-phase by applying a short intense electrical pulse on PCM device. Conversely, a longer pulse of lower intensity for SET operation can heat the a-phase to a temperature between crystallization and melting points to obtain c-structure.
The a-GST material firstly crystallizes into a metastable face-centered-cubic (f-) lattice structure at ~150 °C8, and subsequently transforms into equilibrium hexagonal (h-) structure at 300~350 °C9. In f-GST lattice, Te atoms occupy well-defined anionic sites, while Ge/Sb atoms and vacancies randomly occupy the cationic sites10; that is, the atomic stacking sequence along [111] direction of f-lattice ([0001] direction of h-lattice) is –(Te–Ge/Sb/Vacancy)n–10,11,12,13,14. While in h-GST, along the [0001] direction, the stacking feature of nine-layered building block can be described as –(Te–Ge/Sb–Te–Ge/Sb–Te–Te–Ge/Sb–Te–Ge/Sb)n–14. Avoiding f-to-h phase transition of GST alloy has always been a key issue in PCM technology field, since in a real PCM device, the h-GST phase is deemed to be a black sheep incurring larger RESET current, slower SET speed, severe composition drift, bigger volume shrinkage upon re-crystallization, and large void formation after high temperature (~400 °C) back-end of line process15, 16.
Recently, an intermediate state of f-GST, namely vacancy-ordering cubic (VOC) phase, was theoretically17 and experimentally11, 12 demonstrated to play a key role during the f-to-h transition. Once 100% vacancy-aggregation into {111} planes achieves and forms non-atomic layers in f-GST resembling the Van der Waals interaction gaps in h-GST, the system energy is as small as the equilibrium h-phase17. In view of the similar configuration and minor energy discrepancy between the 100% VOC- and h-GST lattices, a non-diffusion controlled slide of the building blocks was proposed to understand the f-to-h transformation18. Analogous research achievement stated that a shearing martensitic transformation from {200} planes of f-GST to {\(10\bar{1}3\)} planes of h-GST should be energetically favorable during f-to-h transition19, 20. In addition, the discovery of twin crystals consisted by one f- and one h-grain led to an “epitaxial growth model” to interpret the structure evolution manner as f-GST approaching the h-phase21, 22. One can find that previous studies inclined to utilize transformation between similarly structured f- and h-lattices (often from specific crystal orientations under static observation) to conjecture the dynamic atomic rearrangements for the whole f-to-h transition, which would inevitably be neither comprehensive nor precise enough.
In this report, in situ heating transmission electron microscopy (TEM) was utilized to characterize the dynamic crystallization procedure of GST thin films. We note previous literature23 mainly concentrated on the phase transformation procedure and electronic structure of GST films upon in situ annealing, while no vacancy ordering process or h-grain growth mechanism was discussed. Here, we reveal that the rapid growth behavior of h-grains for GST thin film resembles an “abnormal” type24, 25, which is driven by surface energy anisotropy. In contrast to the “normal” case in which grains get larger in a uniform manner, the abnormal growth of h-grains can be characterized by a subset of h-grains (mainly [0001]-oriented) growing bigger at a high rate and at the expense of their multifarious neighboring (small) grains. Such swift expansion of the big h-grain was usually named as the “growth-dominated crystallization” for f-to-h transition of GST16, 21, no matter what crystallographic configurations the small grains would have. We also speculate that the vacancy-ordering process into {111} planes11, 12, 17 may or may not occur in every f-grain, or to say, it is not an indispensable way for f-grains evolving into h-ones especially in the growth period. The adjustments by sliding the building blocks between similar f- and h-atomic configurations17, 19, 21 would be more likely to involve the incubation of h-seeds from the f-matrix. The present scenarios may offer a more comprehensive perspective to understand the phase transition physics of this key material, and be essential for optimizing GST-based commercialized phase change materials to boost the performances of high density PCM device.
Results
In situ heating crystallization of Ge2Sb2Te5 thin film
Figure 1 exhibits in situ heating crystallization process of GST thin film at different temperatures in TEM. The as-deposited GST thin film (Fig. 1a) shows typical a-phase at room temperature. It crystallizes into f-phase with uniformly distributed (randomly oriented) nano-crystals (<~15 nm in average grain size) at 150 °C (Fig. 1b) with calculated lattice parameter of a = 6.01 Å16, 26. When temperature increases to 210 °C (Fig. 1c) and 270 °C (Fig. 1d), f-grains continuously grow larger as the average grain size reaching ~20 and ~30 nm, respectively. The corresponding selected area electron diffraction (SAED) rings in Fig. 1c,d are of a little discontinuity as compared to that in Fig. 1b, denoting the gradual enlargements of the f-grains at higher temperatures. The transient moment at 320 °C (Fig. 1e) shows that GST film has small grains (mixture of evenly distributed small f- and h-grains as also proved in Supplementary Fig. 1) bordering a large h-grain. The dominant h-grain quickly swallows (with ~6.7 nm/s growing speed) adjacent small grains like flood and grows into a larger one, as clearly recorded in Supplementary Movie 1 (with the observation area ~2 × 2 μm2). The large h-grain with μm size, as illustrated from the SAED pattern in Fig. 1f, is of single-crystal type showing strong [0001]-oriented texture. Since we also found tiny h-grains can be incubated from f-matrix at pretty low temperature (~210 °C) (Supplementary Fig. 2), it is reasonable to deduce that, under the circumstance of favorable energy level and similar atomic configuration17,18,19,20,21,22, some of them may act as seeds for quickly growing up into the dominant [0001]-oriented h-grains.
Unnecessity of vacancy-ordering mechanism at fast growth stage of hexagonal grain
In Fig. 2, we reveal the in situ heating vacancy aggregation on {111} planes in a [011]-oriented f-grain, and finally being swallowed by an adjacent large h-grain. At 150 °C (Fig. 2a), the observed grain shows typical f-lattice structure with randomly distributed vacancies. When temperature reaches 210 °C (Fig. 2b), some intersecting (parquet-like) defect layers26 paralleling to {111} planes emerge, causing weak scattered streaks in the inserted corresponding fast-Fourier transform (FFT) pattern. These defect layers should be ascribed to the ordering of randomly distributed vacancies in f-lattice27, 28. In the case of 250~290 °C (Fig. 2c,d), further vacancy ordering leads to gradually clearer and longer defect layers (marked by arrows) in the f-grain. The brighter super-lattice reflection spots in corresponding FFT pattern represent a long-period ordered structure separated by the defect layers. At this period, the f-grain corresponds to an incomplete vacancy-ordering status, and there are still plenty of (Ge/Sb) atoms resided in the van der Waals-like gaps11. At 310 °C (Fig. 2e), the f-grain becomes a little larger, while its high resolution transmission electron microscopy (HRTEM) and FFT images become a bit blurred, which may be originated from a slight grain rotation, resulting in the deviation of [011] zone axis from the incident direction of the electron beam.
As heating temperature increases to 320 °C (Fig. 2f), the [011]-oriented f-grain is about to be eaten by an adjacent big [0001]-oriented h-grain. It is worth pointing out that the non-diffusion controlled slide of building blocks between similar f- and h- atomic configurations requires parallelism between 〈111〉f and 〈0001〉h directions17, 18. Nevertheless in current case the [011]-oriented f-grain deviates ~35.3° (inter-axial angle) with 〈111〉f direction29 (standing for 〈0001〉h direction). Obviously, the non-diffusion controlled slide model is invalid here for the largely misaligned structure rearrangement.
Transient growth state on hexagonal grain boundary
On the boundary of a dominant [0001]-oriented h-grain (see Fig. 3a and zooming image of region ① in Fig. 3b), there reside some small grains corresponding to selected regions ②~④ (see Fig. 3a and zooming images in Fig. 3c to e respectively), which was captured at room temperature from an annealed sample heated up to 320 °C in TEM. Through indexing, the small grains in regions ②~④ are [011]-oriented f-grain, [001]-oriented f-grain, and \([\bar{5}503]\)-oriented h-grain, respectively. In contrast to the vacancy-ordered f-grain (in Fig. 2f), f-grain in region ② has not undergone obvious vacancy-ordering process, but it still cannot escape being annexed by the dominant h-grain as heating continues. The complexities are also produced by f-grain in region ③ and h-grain in region ④. For the [001]-oriented f-grain in region ③ which is unparallel to the 〈0001〉h direction, whether or not the vacancy-ordered layers exist, it could not be transformed into h-phase via a simple building-block sliding procedure. The \([\bar{5}503]\)-oriented h-grain in region ④ also misaligns with the dominant [0001]-oriented h-grain, and the calculated inter-axial angle between \(\langle \bar{5}503\rangle \) and 〈0001〉 orientations is about 35 6° (ref. 29). In addition, a well-resolved video in Supplementary Movie 2 (with the observation area ~20 × 20 nm2) shows the quick expansion (in a few seconds) of a [0001]-oriented h-grain from the upper part by consuming a subjacent grain (without any grain-rotation). The consumed grain obviously does not belong to the vacancy-ordered type. These results further prove that vacancy-ordering into {111} planes of the f-grain may or may not happen especially at the stage of fast h-grain growth. We thus believe the VOC-to-h rearranging model is not enough to describe the f-to-h transition image, and it would be more or less only related to the stochastic (energetically favorable) h-nucleation from f-matrix.
Discussion
Given this, we summarize the crystallization process of GST thin film in Fig. 4. The a-GST (Fig. 4a) firstly crystallizes into small f-grains with randomly distributed vacancies at ~150 °C (Fig. 4b). Then, some randomly oriented VOC-grains and small h-grains are formed from the f-matrix at ~210 °C (Fig. 4c). By further heating up to ~320 °C (Fig. 4d), a dominant (large) [0001]-oriented h-grain appears and grows up quickly to accomplish the f-to-h transformation. The enlarged sketch (Fig. 4e) illustrates the transient growth state on the boundary of the dominant h-grain. Since the concentration of adatoms on the grain boundary is a function of its curvature30, usually atoms from the convex side tend to increase their coordination number via migrating to the concave side so as to lower down the system free energy. This is also valid here when low-coordinated atoms in f-GST lattice with large portion of vacancies confront the compact h-lattice. They diffuse to the boundary and reconstruct into the high-coordinated configuration. The arrows marked in Fig. 4e denote the concave-to-convex expansion (growth) directions for the dominant h-grain.
In theory, the grain growth rate V can be expressed as:
where M is the average grain boundary mobility and F is the combined driving force25, 31. The latter can be qualitatively divided into three categories: surface energy, grain boundary energy, and free energy from f-to-h phase transformation.
To model the abnormal h-grain growth in f-GST thin film of thickness D (Fig. 5), we examine the case that an initial h-GST grain of radius r h is incubated from the f-GST matrix with uniform f-grain radius r f (Fig. 5a), and grows into a bigger one of radius r (Fig. 5b). The starting h-grain can be characterized by a surface energy per unit area Γ s , h and an interphase boundary energy between the h- and f-phases per unit area Γ f/h . The f-grains are characterized by an average grain boundary energy per unit area \({{\rm{\Gamma }}}_{gb,f}^{\ast }\) and average surface energy per unit area \({{\rm{\Gamma }}}_{s,f}^{\ast }\). Note that \({{\rm{\Gamma }}}_{s,h}\), Γ f/h , \({{\rm{\Gamma }}}_{s,f}^{\ast }\), and \({{\rm{\Gamma }}}_{gb,f}^{\ast }\) all have positive values and obviously \({{\rm{\Gamma }}}_{s,f}^{\ast } > {{\rm{\Gamma }}}_{s,h}\).
For the h-grain of radius r h to annex its surrounding f-grains contained in an area of \(\pi {r}^{2}-\pi {r}_{h}^{2}\), the energy per unit volume of this region before the subsequent grain growth is:
where \(\,N=1/(\pi {r}_{f}^{2}D)\) is the total number of f-grains per unit volume, \({A}_{gb}=\pi {r}_{f}D\) is the grain boundary area associated with an average f-grain, and ΔG h and ΔG f are the free energies of formation per unit volume of h- and f-GST respectively. Apparently, ΔG h and ΔG f are both negative, and ΔG f > ΔG h . After transformation, the fast growth of the dominant h-grain achieves significant reduction of the total energy, and the energy at this time of this region can be described as:
The driving force for the transformation from the higher energy state E B to the lower one E A can therefore be expressed as:
In equation (4), the first, second, and the third terms represent the contributions from surface energy, grain-boundary energy, and free energy change from f-to-h transformation respectively.
At the initial heating stage of transforming a f-grain into a small h-grain, when r h ≈ 0 and r ≈ r f , the driving force can be roughly described as:
From equation (5), we notice that the surface energy anisotropy and Gibbs free energy change upon f-to-h phase transition represent the positive momentums. As for the interphase boundary energy, no doubt it would act as a barrier to h-grain growth at the initial stage and represent the negative momentum, especially when the average f-grain size r f is pretty small. It has been demonstrated that the modified GST materials, eg., after Ge15, 32, C16, or N32, 33 doping, all have diminished f-grains. According to equation (5), when the grain size is pretty small, we can roughly regard the surface energy anisotropy as a constant parameter, and a smaller r f of f-grain in modified GST films would make the interphase boundary energy become dominant as transforming to h-grain. Not surprisingly, the transformation to h-phase thus can be postponed to higher temperature. In addition, the formation of segregated Ge, C, or GeNx phases on the grain boundaries can significantly inhibit the h-grain boundary migration (M being lowered), leading to the slow grain growth rate of h-phase.
On the other hand, for the fast growth period of the dominant h-grain, consuming surrounding small f-grains, the driving force, by assuming r ≈ r h + r f and r ≈ r h (>2 μm) ≫ \({r}_{f}\) (~20 nm), then can be rewritten into:
According to equation (6), one can qualitatively conclude that, for the ultra-thin GST film (D being quite small), the contribution of surface energy anisotropy (the first item) becomes extremely dominant as the average grain size is greater than the film thickness31. In fact, at higher temperature with larger r f grain size, the contribution of surface anisotropy would be more dominant, which in turn increases driving force and prompts the h-grain growth. In this case, grains with orientation of low surface energy will preferentially grow faster than those with other orientations. The abnormal grain growth thus prevails until the orientation-favored grains impinge on grains with similar surface energy. Eventually, most of the grains surviving abnormal grain growth would be orientated with the minimum surface energy. In c-materials, the minimum surface energy planes usually are the closest-packed atomic ones31, eg., (0001) plane of h-GST grain. The easier formation of h-phase for thin GST film is indeed a critical issue that should be avoided in manufacturing high density (giga-bit) PCM devices as the sectional size of vertical (dash-typed) phase change film being shrunk to 7.5 nm × 17 nm (ref. 6). Also note that the f-to-h transition becomes much easier when the thickness of GST film sandwiched between ZnS-SiO2 cladding films is further scaled from 6 to 2 nm (ref. 34), because the transition temperature is significantly reduced, as well as the energy barrier. Introducing compressive stress to the ultra-thin GST film by encapsulating with suitable dielectric films34 or doping with high glass-transition temperature elements15, 16, 32, 33 would be helpful for suppressing the formation of the h-phase for high density PCM application.
Conclusion
In summary, with the aid of in situ TEM heating technique, we describe a more comprehensive characterization of the crystallization process of GST thin film. We believe that vacancy ordering phenomenon in f-phase is just a specific fragment of the whole f-to-h transition process. It would be more or less related to the stochastic h-nucleation from f-phase occurred at energetically favorable areas. The abnormal growth of large h-grain at high temperature is mainly driven by surface energy anisotropy. The closest-packed (0001) atomic plane of h-GST grain has the smallest surface energy than those of diversely-oriented f- or h-grains. This driving force would be particularly prominent as the film thickness being greatly diminished and smaller than the average grain size. Thus no matter how complicated the grain boundary would be, the [0001]-oriented h-grain can achieve overall growth. The present results mainly concentrate on the h-grain growth stage, and further study on initially stochastic h-nucleation process will be a great help to more comprehensively understanding the crystallization mechanism of the GST alloy.
Methods
GST films (~15 nm in thickness) were directly deposited on TEM grids coated with ultra-thin carbon film at room temperature by sputtering GST alloy target. Amorphous SiO2 film (~5 nm in thickness), as the anti-oxidation layer, was successively deposited on top of GST films. By using energy-dispersive spectroscopy equipped on the TEM and X-ray fluorescence spectroscopy, the average concentrations of Ge, Sb, and Te elements of the GST films were determined to be 21.4 at.%, 22.6 at.%, and 56.0 at.%. The microstructures of the GST films were characterized by bright-field TEM, SAED, and HRTEM via using JEOL 2100 F TEM under 200 kV. The in situ heating crystallization of a-GST film was carried out in a heating holder (Gatan 628) at heating rate of 10 °C/min. During the whole heating process, electron beam was shut off to avoid irradiation effects and only turned on for capturing images35.
References
Lam, C. H. Storage Class Memory. Solid-State and Integrated Circuit Technology (ICSICT), 10th IEEE International Conference on. 1080–1083 (2010).
Wong, H.-S. P. & Salahuddin, S. Memory leads the way to better computing. Nat. Nanotech. 10, 191–194 (2015).
Loke, D. et al. Breaking the Speed Limits of Phase-Change Memory. Science 336, 1566–1569 (2012).
Zhu, M. et al. One order of magnitude faster phase change at reduced power in Ti-Sb-Te. Nat. Commun. 5, 4086 (2014).
Giusca, C. E. et al. Confined crystals of the smallest phase-change material. Nano Lett. 13, 4020–4027 (2013).
Kim, I. S. et al. High performance PRAM cell scalable to sub-20nm technology with below 4F2 cell size, extendable to DRAM applications. Symp. on VLSI Tech. Dig. 203–204 (2010).
Cheng, H. Y. et al. Novel Fast-switching and High-data Retention Phase-change Memory Based on New Ga-Sb-Ge Material. IEDM Tech. Dig. 3.5.1–3.5.4 (2015).
Yamada, N. et al. Rapid-phase transitions of GeTe-Sb2Te3 pseudobinary amorphous thin films for an optical disk memory. J. Appl. Phys. 65, 2849–2856 (1991).
Friedrich, I. et al. Structural transformations of Ge2Sb2Te5 films studied by electrical resistance measurements. J. Appl. Phys. 87, 4130–4134 (2000).
Yamada, N. & Matsunaga, T. Structure of laser-crystallize Ge2Sb2+xTe5 sputtered thin films for use in optical memory. J. Appl. Phys. 88, 7020–7028 (2000).
Zhang, B. et al. Element-resolved atomic structure imaging of rocksalt Ge2Sb2Te5 phase-change material. Appl. Phys. Lett. 108, 191902 (2016).
Zhang, B. et al. Vacancy structures and melting behavior in rock-salt GeSbTe. Sci. Rep. 6, 25453 (2016).
Lotnyk, A. et al. Real-space imaging of atomic arrangement and vacancy layers ordering in laser crystallised Ge2Sb2Te5 phase change thin films. Acta Materialia 105, 1–8 (2016).
Matsunaga, T. et al. Structures of stable and metastable Ge2Sb2Te5, an intermetallic compound in GeTe-Sb2Te3 pseudo-binary systems. Acta Crystallogr. Section B. B60, 685–691 (2004).
Cheng, H. Y. et al. A High Performance Phase Change Memory with Fast Switching Speed and High Temperature Retention by Engineering the GexSbyTez Phase Change Material. IEDM Tech. Dig. 3.4.1−3.4.4 (2011).
Zhou, X. et al. Understanding Phase-Change Behaviors of Carbon-Doped Ge2Sb2Te5 for Phase-Change Memory Application. ACS Appl. Mater. Interfaces 6, 14207–14214 (2014).
Zhang, W. et al. Role of vacancies in metal–insulator transitions of crystalline phase-change materials. Nature Mater. 11, 952–956 (2012).
Sun, Z. et al. Structure of phase change materials for data storage. Phys. Rev. Lett. 96, 055507 (2006).
Zhang, W. et al. Martensitic transformation in Ge2Sb2Te5 alloy. Adv. Eng. Mater. 10, 67–72 (2008).
Zhang, W. et al. How important is the {103} plane of stable Ge2Sb2Te5 for phase-change memory? Journal of Microscopy 259, 10–15 (2015).
Park, Y. J. et al. In situ transmission electron microscopy study of the nucleation and grain growth of Ge2Sb2Te5 thin films. Appl. Surf. Sci. 252, 8102–8106 (2006).
Kim, E. T. et al. Investigation of the structural transformation behavior of Ge2Sb2Te5 thin films using high resolution electron microscopy. Appl. Phys. Lett. 91, 101909 (2007).
Song, S. A. et al. In situ dynamic HR-TEM and EELS study on phase transitions of Ge2Sb2Te5 chalcogenides. Ultramicroscopy 108, 1408–1419 (2008).
Thompson, C. V. Grain growth in polycrystalline thin films of semiconductors. Interface Sci. 6, 85–93 (1998).
Chou, T. C. & Nieh, T. G. Interface-controlled phase transformation and abnormal grain growth of α-Al2O3 in thin γ-alumina films. Thin Solid Films 221, 89–97 (1992).
Lankhorst, M. H. R. et al. Low-cost and nanoscale non-volatile memory concept for future silicon chips. Nat. Mater. 4, 347–352 (2005).
Rosenthal, T. et al. Real structure and thermoelectric properties of GeTe-rich germanium antimony tellurides. Chem. Mater. 23, 4349–4356 (2011).
Ross, U. et al. Direct imaging of crystal structure and defects in metastable Ge2Sb2Te5 by quantitative aberration-corrected scanning transmission electron microscopy. Appl. Phys. Lett. 104, 121904 (2014).
Williams, D. B. & Carter, C. B. Transmission Electron Microscopy: A Textbook for Materials Science, 2nd ed. (Springer: New York, 2009).
Mullins, W. W. Two-dimensional motion of idealized grain boundaries. J. Appl. Phys. 27, 900 (1956).
Thompson, C. V. Secondary grain growth in thin films of semiconductors: theoretical aspects. J. Appl. Phys. 58, 763–772 (1985).
Cheng, H. Y. et al. A thermally robust phase change memory by engineering the Ge/N concentration in (Ge, N)xSbyTez phase change material. IEDM Tech. Dig. 31.1.1−31.1.4 (2012).
Lee, T. H. et al. Microscopic mechanism of doping-induced kinetically constrained crystallization in phase change materials. Adv. Mater. 27, 5477–5483 (2015).
Simpson, R. E. et al. Toward the ultimate limit of phase change in Ge2Sb2Te5. Nano Lett. 10, 414–419 (2010).
Kooi, B. J. et al. In situ transmission electron microscopy study of the crystallization of Ge2Sb2Te5. J. Appl. Phys. 95, 924–932 (2004).
Acknowledgements
This work was supported by Strategic Priority Research Program of Chinese Academy of Sciences (XDA09020402), National Natural Science Foundation of China (61106001, 61261160500, 61376006, 61622408), Science and Technology Council of Shanghai (13ZR1447200, 13DZ2295700). Many thanks for the support from Oxford Company in SEM-TKD experiment.
Author information
Authors and Affiliations
Contributions
Y.Z. and K.D. prepared the film samples. Y.Z., Y.C., R.H. and Q.J. carried out the transmission electron microscopy experiments. W.Y. and S.S. contributed with helpful discussions. F.R. and Y.C. carried out theoretical analysis and together wrote this paper with contributions from all co-authors. The project was initiated and conceptualized by W.L., Z.S. and S.F.
Corresponding authors
Ethics declarations
Competing Interests
The authors declare that they have no competing interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Zheng, Y., Cheng, Y., Huang, R. et al. Surface Energy Driven Cubic-to-Hexagonal Grain Growth of Ge2Sb2Te5 Thin Film. Sci Rep 7, 5915 (2017). https://doi.org/10.1038/s41598-017-06426-2
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-017-06426-2
- Springer Nature Limited
This article is cited by
-
The effect of thickness on texture of Ge2Sb2Te5 phase-change films
Journal of Materials Science: Materials in Electronics (2020)
-
Scandium doping brings speed improvement in Sb2Te alloy for phase change random access memory application
Scientific Reports (2018)
-
Improvement of thermal stability of antimony film by cerium addition for phase change memory application
Journal of Materials Science: Materials in Electronics (2018)