Abstract
We explore the contributions to the electrical resistance of monolayer and bilayer graphene, revealing transitions between different regimes of charge carrier scattering. In monolayer graphene at low densities, a nonmonotonic variation of the resistance is observed as a function of temperature. Such behaviour is consistent with the influence of scattering from screened Coulomb impurities. At higher densities, the resistance instead varies in a manner consistent with the influence of scattering from acoustic and optical phonons. The crossover from phonon-, to charged-impurity, limited conduction occurs once the concentration of gate-induced carriers is reduced below that of the residual carriers. In bilayer graphene, the resistance exhibits a monotonic decrease with increasing temperature for all densities, with the importance of short-range impurity scattering resulting in a “universal” density-independent (scaled) conductivity at high densities. At lower densities, the conductivity deviates from this universal curve, pointing to the importance of thermal activation of carriers out of charge puddles. These various assignments, in both systems, are made possible by an approach of “differential-conductance mapping”, which allows us to suppress quantum corrections to reveal the underlying mechanisms governing the resistivity.
Similar content being viewed by others
Introduction
In spite of the interest that graphene has attracted over the past decade1, the manner in which different scattering processes combine to determine its electrical resistance remains a topic of investigation. The reason for this may be traced to the ultrathin structure of this material, which allows its conduction to be influenced by a variety of different scattering mechanisms1,2,3,4,5,6,7,8,9,10,11,12,13,14,15,16,17,18,19,20,21,22,23. Phonon-mediated scattering, for example, can be generated by graphene’s intrinsic modes2,3,4,5,6,7,8,9, but can also be due to rippling4, 10, 11 or the underlying substrate5, 12, 13. Impurity scattering, on the other hand, is usually attributed to the presence of long-range charged impurities in the dielectric substrate13,14,15,16,17,18,19, and of short-range neutral defects in the graphene itself15, 16, 18, 20, 22. Collectively, these mechanisms may combine to yield complicated variations of the resistance as a function of both temperature (T) and carrier density (n & p for electrons and holes, respectively). A problematic task in experiment is that of separating out the different contributions, a job that is made all the more challenging at low temperatures by the emergence of quantum corrections24,25,26,27,28,29. Most notable of these are those arising from weak (anti) localization24,25,26,27 and electron-electron scattering28, 29, although Kondo physics has also been invoked to account for the behaviour observed in this regime30,31,32,33,34.
In conventional semiconductors near room temperature, and with modest levels of doping, phonon scattering is typically the dominant process limiting carrier mobility (µ). The situation in graphene is more complicated, however, not only for the reasons identified above. Electrons and holes reside on a two-dimensional Dirac cone, placing significant phase-space restrictions on electron-phonon scattering7, 35,36,37. The large (>160 meV) energy of the graphene optical modes is additionally understood to suppress their importance, and the overall message is that phonon scattering is weak35,36,37. Room temperature mobility as large as ∼20,000 cm2/Vs is therefore expected for graphene on SiO2 17, 19, while experiment has demonstrated values an order of magnitude larger for suspended layers4, 6. In many other experiments (performed with graphene on SiO2), however, observed mobility values may be smaller than 1000 cm2/Vs38, 39, suggesting that the contribution to the resistivity from impurity scattering can be much more important than in conventional semiconductors.
In this article, we study the resistance of graphene/SiO2 transistors over a wide range of temperature (3–300 K), and for densities spanning the electron and hole branches of the Dirac cone. Due to their different energy dispersions, the importance of Coulomb and short-range impurities is expected to be very different in monolayer and bilayer graphene22. We therefore perform a comparative study of transistors fabricated with these materials. While prior work has largely focused on the resistance variations exhibited by graphene under linear transport2,3,4,5,6,7,8,9,10,11,12,13,14,15,16,17,18,19,20,21,22,23, far fewer studies40,41,42,43,44 have applied differential-conductance measurements to this problem. Here we use measurements of differential-conductance, performed as a function of temperature, density and drain bias, to identify the different contributions to graphene’s resistance. Crucially, this allows us to identify resistivity contributions, free of the influence of quantum corrections. Our findings in both the monolayer and bilayer systems are in good agreement with the theories1, 20, 22, 23, 45 proposed by Das Sarma and his colleagues.
Results
Linear Conductance of Monolayer and Bilayer Graphene
We begin our discussion by first of all addressing the temperature dependence of graphene’s linear transport, a problem that has previously been widely investigated2,3,4,5,6,7,8,9,10,11,12,13,14,15,16,17,18,19,20,21,22,23. To make a direct connection to these earlier works, in Fig. 1 we plot the variation of the conductivity, as a function of gate-voltage (V g ) and temperature. In Fig. 1a we show that the conductivity of monolayer graphene is only weakly dependent on temperature, while in Fig. 1b the bilayer shows a much stronger variation. The weak temperature dependence observed in the monolayer indicates that the dominant source of resistivity in this material, at all densities, is long-range Coulomb disorder. According to ref. 4, the contribution to the resistivity due to this mechanism should not depend on temperature below 300 K. This is in contrast with our results for the bilayer system, which shows a pronounced increase in overall conductivity with increasing temperature. The reason for this much stronger temperature dependence may be attributed to two factors, the first of which is that the thermal carrier concentrations increases much more strongly with increasing temperature in the bilayer. Secondly, due to the very different nature of screening in the two materials, scattering from short range defects, rather than Coulomb impurities, is expected to dominate in the bilayer, and is characterized by a strongly temperature-dependent nature20, 22.
As a final comment, we note that Fig. 1 shows that, away from the Dirac point, the conductivity in both devices varies linearly with gate voltage (and so with n or p). While these variations might appear to suggest a common origin, in both materials, this, in fact, is not the case. Rather, the observed behaviour is completely consistent with what one expects when scattering in the monolayer is dominated by screened Coulomb impurities4, 17,18,19,20,21,22, and that in the bilayer is governed by unscreened short-range disorder22.
Differential-Conductance Mapping of Monolayer and Bilayer Graphene
While linear transport provides a useful tool to reveal the role of different scattering mechanisms, for a more complete picture, offering energy resolution, it is necessary to make use of nonequilibrium studies. It is this approach that we apply here, where we perform differential-conductance mapping of graphene, as a function of drain bias, gate voltage, and temperature. The value of this approach is highlighted in Fig. 2, where we show contour plots of differential conductance (g d ) as a function of these parameters. (More precisely, the plots show differential resistance g d −1, since it is more easy to resolve the different features of the resulting contours in this case.) Fig. 2a,b are for monolayer and bilayer graphene, respectively. While their left panels plot (at the lowest temperature of 3 K) the variation of g d −1 as a function of V d and V g , the right-hand panels plot the differential resistance at fixed density (see figure caption) and as a function of temperature. The Dirac point is identified as a pronounced peak at V g = 14 and V g = −5 V, for monolayer and bilayer graphene, respectively, as indicated by the dotted lines in the left-hand panels. The main features of these contours are: (1) The zero-bias peak in differential resistance that is strongly suppressed with increasing temperature, washing out around 40–50 K; (2) The pronounced temperature-dependent variations of g d −1, away from the zero-bias peak, which appear to be of opposite sign for the monolayer and bilayer systems.
Zero-Bias Resistance Peak Due to Quantum Corrections
The zero-bias peak (Fig. 2) in the low-temperature differential resistance (g d −1) is consistent with the influence of quantum corrections, most notably weak localization and electron interactions46. As can be seen in the data of Fig. 2, the peak washes out around 40 K or so (this can be seen more clearly in the right panel of Fig. 2c), consistent with its origins in a quantum-coherent effect46. Furthermore, in the upper inset to Fig. 1a, we plot the differential conductance of the monolayer device at three magnetic fields. While the largest of these (0.4 T) should be sufficient to fully quench weak localization28, the amplitude of the zero bias peak is only reduced by ∼50% compared to its size at zero magnetic field. This indicates that this feature arises from a combination of weak localization and electron interactions, both of which become increasingly important as the temperature is lowered and carrier coherence is enhanced46 (see Section S5 of the Supplementary Information).
To observe how the resistance is influenced by semiclassical contributions such as phonon, and charged-impurity, scattering, it is necessary to suppress the quantum corrections by suitable means. We achieve this here by measuring the variation of resistance in the presence of non-zero DC bias, as we demonstrate in Figs 3 & 4. The essential observation here is that, for V d = 0, the resistance of both monolayer (Fig. 3a,b) and bilayer (Fig. 4a,b) graphene increases as a logarithmic function of decreasing temperature below ∼40 K. This behavior is well known46 for quantum corrections and can be quenched by measuring the temperature dependence of the resistance under non-zero DC bias. In Fig. 3a, for example, the zero-bias resistance measured (near the Dirac point) in monolayer graphene shows its logarithmic upturn below 50 K (also see the inset to the main panel). With a DC bias of 10 mV, however, the logarithmic upturn is completely suppressed and the resistance decreases continuously down to 3 K. A similar suppression is apparent for electron and hole densities far from the Dirac point (Fig. 3b, main panel and insets), as well as in bilayer graphene (Fig. 4a,b), and should result from the suppression of carrier phase coherence as the DC bias is increased. The essential point for the study here is that, by suppressing the influence of the quantum corrections, we are able to investigate the underlying sources of graphene’s resistance.
Resistance Variations in Monolayer and Bilayer Graphene
Having described how the quantum corrections may be suppressed in our studies, in this section we focus in more detail on the resistance variations exhibited by the monolayer (Fig. 3) and bilayer (Fig. 4) devices. The most striking feature of Fig. 3a, in which we plot the results of measurements obtained with the Fermi level close to the Dirac point, is a nonmonotonic variation of the resistance (also see the contour in the left panel of Fig. 2c). Even with the quantum corrections suppressed at V d = 10 mV, the resistance still exhibits this nonmonotonic character; increasing first as the temperature is lowered below 300 K, before crossing over to a metallic-like variation for which the resistance decreases below 150–200 K. A similar variation is apparent for larger voltages (V d > 10 mV) but the resistance no longer drops at low temperatures, instead showing a tendency to saturation. This is presumably due to self-heating of the graphene carriers under the strongly nonequilibrium voltage47; the voltage of 20 mV, for example, corresponds to an equivalent temperature of 200 K, consistent with the temperature below which the resistance saturates in Fig. 3a.
In Fig. 3b we show the corresponding variations of the resistance, exhibited by the monolayer system once the hole concentration has been adjusted to n g = 1.7 × 1012 cm−2. With the quantum corrections suppressed by the application of the DC bias, the resistance at higher temperatures is characterized by a monotonically-increasing (metallic) variation. Similar behaviour is apparent, also, in the lower inset to Fig. 3b, where we plot the corresponding results obtained for an electron density of 1.9 × 1012 cm−2.
While we have focused thus far on the behaviour exhibited by monolayer graphene, in panels (a) & (b) of Fig. 4 we plot a series of graphs that are the bilayer counterparts of Fig. 3a,b, respectively. Comparing the monolayer and bilayer devices, we immediately note that (with quantum corrections suppressed) the latter exhibits a much simpler, monotonic, decrease of resistance with increasing temperature. This insulator-like behaviour is observed both close to (Fig. 4a), and away from (Fig. 4b), the Dirac point. Similar results, obtained for another bilayer device, are presented in Section S6 of the Supplementary Information. Critically, the continuous increase of conductance with increasing temperature cannot be explained within any model of phonon-limited conduction in this material.
Discussion
Before discussing the implications of our experimental results it will be helpful to first of all summarize some of the theoretical predictions regarding the sources of resistivity in graphene. Phonons should always give rise to an increasing (metallic) resistivity with increasing temperature, with acoustic phonons providing a linear-in-T contribution over the range of interest here3, 5, 7. With regards to scattering from optical phonons, the large energies associated with these modes is often thought to render them unimportant at or below room temperature. However, recent first-principles calculations8, 9 based on density-functional theory suggest that, above ∼200 K, optical-phonon scattering may actually become stronger than that due to the acoustic modes, resulting in a metallic resistivity that shows a more rapid increase than linear-in-T.
Impurity scattering in graphene is typically attributed to Coulombic impurities in the SiO2 substrate and to neutral defects in the graphene layer. With regards to charged impurities, the influence of these is strongly dependent on the screening generated by carriers in the graphene. Screening enters the matrix element for the scattering process via the dielectric function, which in turn depends upon the polarizability of the material. The key point here is that the dependence of this function on temperature and scattering wavevector is very different in monolayer and bilayer graphene, resulting in very distinct screening properties in these materials20, 22. Most notably, in monolayer graphene the polarizability shows a nonmonotonic dependence on temperature, which should give rise to a similarly nonmonotonic variation of the resistivity. Hwang and Das Sarma20 have calculated this behaviour analytically, accounting for the influence of thermal carriers via usual Fermi-Dirac statistics, obtaining asymptotic expressions for the monolayer conductivity:
where σ 0 = σ(T = 0), T F is the Fermi temperature, r s is the Wigner-Seitz radius and:
When the explicit temperature dependence of the finite energy averaging of the scattering time is considered, and by taking r s = 0.88 (for graphene on SiO2), equation (1) is slightly modified to20:
Das Sarma et al. have also considered22 the influence of temperature-dependent screening in bilayer graphene, and predict a metallic resistivity contribution at low temperatures (T/T F ≪ 1). A critical difference with the monolayer, however, is that scattering from short-range impurities is expected to be much more important in bilayer material. The short-range scatterers give rise to a strong insulating temperature dependence of the resistivity in this system, which can overwhelm any signature from charged impurities. (This is to be contrasted with monolayer graphene, in which the influence of short-ranged scatterers is only expected20, 22 to be significant at very-high densities – ∼1013 cm−2 – once screening of the Coulomb impurities become fully effective.) While the resistivity correction arising from short-range scatterers can only be evaluated numerically, the authors of ref. 22. showed that this mechanism should give rise to an insulating variation of the scaled conductivity (σ(T/T F )/σ 0) that is independent of density.
In later work23, 45 by the Maryland group, the authors addressed explicitly the thermal activation of carriers out of localized puddles arising from the disorder background. Here the authors discussed the puddles as giving rise to a “two-component” model of transport; the first involving usual diffusive transport in the graphene layer, while the second involves the thermal activation of carriers out of the puddles. The activated transport is predicted23, 45 to give rise to an insulating conductivity near the Dirac point in both monolayer and bilayer graphene systems (equations (5) & (6), respectively, valid when k B T < s):
where s is the strength of the potential fluctuations in graphene and is typically expected to be in the range of 10–100 meV. The thermal activation is expected to be most significant in the bilayer system, in which the extent of puddle formation should be much stronger, leading to larger characteristic values of s 23, 45. Nonetheless, evidence for the activation has been found in disordered, CVD-grown, monolayer graphene48. Here, the competition between thermal activation, temperature-dependent screening, and phonon scattering was found to result in a nonmonotonic variation of the conductivity, in the crossover regime between insulating and metallic states.
The presence of puddling in typical experiments usually obscures the intrinsic variations of the conductivity that are expected for graphene. Here, the conductivity near its Dirac point is predicted to follow the semiclassical transport theory proposed in ref. 49. According to this theory, which accounts for the influence of thermal excitation, screening, and scattering, the conductivity should be insulating in character, and follow a power-law variation as a function of temperature. While this behaviour is not observed in most experiments, such as those performed here where the graphene is supported on an SiO2 substrate, there is evidence to suggest that it can be observed at sufficiently low densities in clean, suspended material6, 50,51,52,53.
With this understanding, we now consider the implications of our experimental results in the light of the predictions above. We begin, in Fig. 5, by performing an analysis of the resistance variations observed in monolayer graphene, with a non-zero DC bias (V d = 10 mV) applied to suppress its quantum-corrections. In the inset to Fig. 5a, we plot resistance as a function of temperature for a number of gate voltages on the hole side of the Dirac curve (V g ≤ 14 V). These data are re-plotted in the main panel of the figure, by rescaling them relative to their low-temperature resistance (at 3 K). Starting from a gate voltage of −10 V, the Fermi level lies well within the valence band (see Fig. 1a) and the resistance exhibits a metallic variation over the entire temperature range. As the gate voltage is increased towards the Dirac point (at V g = 14 V), however, the resistance develops a nonmonotonic character, the onset of which appears at progressively lower temperatures for larger gate voltages. For V g = 6 V, for example, the crossover to an insulating resistance occurs around 250–300 K; by the time the Dirac point is reached, however, the onset has shifted down to ∼150 K.
The data of Fig. 5a support a scenario involving a crossover from phonon-dominated conduction, when the Fermi level lies far from the Dirac point, to one in which transport is governed by scattering from screened Coulomb impurities when the Fermi level is near to this special point. In Section S4 of the Supplementary Information, we include a table relating the different gate voltages to the corresponding electrostatically-induced concentrations (n g ) that they imply. From this table, we see that the data in this figure span a wide range of carrier density, from n g ∼ 2 × 1012 cm−2 in the highest case to almost n g ∼ 0 near the Dirac point (at V g = 14 V). In Fig. 5b, we then address the origins of the resistance variations observed well away from the Dirac point, by plotting the temperature-dependent change of resistivity (relative to its value at 3 K). At these hole concentrations (>7 × 1011 cm−2), the gate-induced carrier density is larger than that due to both residual impurities (n*) and thermal carriers (n th ), even at room temperature. (For a further discussion of this point see Section S4 of the Supplementary Information, where we also show how consistent estimates for the residual impurity density can be obtained from a Raman analysis – see Fig. S1 – or from the features of the Dirac curve – see Fig. S4). In this limit we find that the resistance shows purely metallic behaviour, increasing monotonically with increasing temperature. At the same time, as n g is increased through variation of the gate bias in this figure, the overall resistance level systematically decreases. The dotted line included in the figure represents an extrapolation of the data of Park et al., who have calculated the phonon-limited resistivity for graphene by first-principles methods8, 9. Their calculations employ both density-functional theory, and density-functional perturbation theory, to compute all electronic and phononic properties, including the influence of resultant electron-phonon coupling. The dotted line in Fig. 5b clearly agrees well with our experimental data for the gate voltage of −10 V (corresponding to a hole density of n g = 1.7 × 1012 cm−2). According to Park et al., the phonon-limited resistivity is governed by acoustic modes at low temperatures, whereas at temperatures above ∼150 K the role of optical phonons becomes more important. It is this crossover in scattering that we attribute to the rapid upturn of the resistivity seen in experiment beyond 150 K. From this analysis we therefore conclude that, when the concentration is dominated by the influence of gate-induced carriers, the resistivity of graphene is essentially determined by phonon scattering. This situation changes when the gate-induced concentration of carriers decreases, however, as we now discuss.
As the gate voltage is increased beyond 6 V in Fig. 5a, the hole concentration drops below n g = 5 × 1011 cm−2 and it is clear that the scaled resistance deviates from a purely metallic variation that is the signature of electron-phonon scattering and develops, instead, a nonmonotonic dependence on temperature. The onset of this behaviour initially occurs near room temperature, but decreases to ∼150 K as n g → 0. A clue as to the origins of this nonmonotonicity, is provided again in Section S4 of the Supplementary Information. This figure shows that, for n g < 5 × 1011 cm−2, one enters a new regime where the full carrier concentration is strongly modified by the contribution from charged-impurity induced residual carriers. On the basis of these observations, we attribute the nonmonotonic variations seen in Fig. 5a to the role of scattering from screened Coulomb impurities, as predicted by Hwang and Das Sarma20. To establish this point, in Fig. 5c we have rescaled the data from Fig. 5a to reveal a connection to equation (4). The graph focuses on the low-temperature limit (T << T F ), where the prediction of equation (4) is expected to be valid20, and the dotted line in the figure represents the universal variation this describes (for r s = 0.88). It is clear that good agreement with this line is obtained for the lowest density studied, where the gate-induced concentration (n g = 1.4 × 1011 cm−2) is in fact smaller than that (∼2 × 1011 cm−2) due to the Coulomb impurities. As the gate voltage is used to produce heavier hole doping, however, the conductance rises rapidly above the dotted line in Fig. 5c. The suggestion of these results is therefore as follows. At the lowest density that we study (n g < 5 × 1011 cm−2), the resistivity data closely follow the universal variation expected20 for scattering from screened Coulomb impurities, indicating that this mechanism dominates over phonon scattering in this limit. As the density is increased, however, the data in Fig. 5c rise above the universal curve, indicating that an additional mechanism is contributing significantly to the resistivity. This mechanism is presumably due to phonon scattering, which grows to eventually dominate the measured resistance once the density becomes sufficiently large (n g > 1012 cm−2).
While in the above discussion we have characterized our results in terms of “metallic” and “insulating” resistivity variations, it must be emphasized that this has nothing to do with a metal-insulator transition. Indeed, even with the nonmonotonic character of the resistance manifested most strongly near the Dirac point, the minimum conductivity achieved in the monolayer is ∼20 e 2/h per square (see Sections S1 & S3 of the Supplementary Information). The graphene is therefore metallic at all densities studied, and the observation of “metal-like” and “insulator-like” resistance variations simply reflects the competition between the different scattering mechanisms noted above.
Turning to the variations exhibited by bilayer graphene, these are somewhat easier to analyse since they show no evidence of any metallic variation that would provide a signature of electron-phonon scattering. The first point we note from Fig. 1 is that the overall conductivity in bilayer material is much lower than that in the monolayer, a difference that is commonly observed in experiment and which is attributed to differences in the density of states and screening properties of these materials54. The different density of states is also responsible54 for the increased importance of thermal carriers in the bilayer system, relative to the monolayer (see Section S3 of the Supplementary Information). As we indicate in Fig. 6a, where we plot the variation of resistance with temperature for electrons, the resistance of this material therefore shows insulating variations for all temperatures and densities. This appears consistent with the predictions for scattering from short-range defects in bilayer material22. As described above, the signature of such scattering in the bilayer should be a density-independent variation of the scaled conductivity (σ(T/T F )/σ 0). This behaviour can be clearly seen in the main panel of Fig. 6b, where we plot rescaled differential conductance as a function of T/T F for a number of electron densities in the range of n g = 1.2 – 2.9 × 1012 cm−2 (see the table included in Section S4 of the Supplementary Information for the correspondence of V g to n g for the bilayer). Over this density range, where the contribution from gate-induced carriers dominates the total electron or hole density (see Section S4 of the Supplementary Information), the data clearly fall on a common curve expected for short-range scatterers22. This is obviously very different to the behaviour discussed for monolayer graphene, in which the resistivity at higher densities was instead dominated by electron-phonon scattering (Fig. 5b). This may be understood in terms of the different screening properties of monolayer and bilayer graphene22. In the inset to Fig. 6b, we extend our analysis by including data for lower electron densities (n g = 0.1–1.2 × 1012 cm−2) than those in the main panel. Here it is clear that the data progressively deviate from the density-independent curve, as n g is reduced to 1.0 × 1011 cm−2. Since this concentration corresponds to the situation where n g < n *, one might expect that the transport should be increasingly limited by puddling behaviour associated with charged background impurities. Consistent with this, in this regime, we find that the temperature dependence of the conductance is well described by the prediction of equation (6) for two-component transport23, 45. This is shown in Fig. 6c, where we are able to fit the data near the Dirac point with a reasonable23, 45 estimate (s = 35 meV) for the potential-fluctuation strength.
In conclusion, in this article we have explored the contributions to the resistance of monolayer and bilayer graphene transistors. Our studies have revealed transitions between different regimes of scattering, as a function of density, temperature, and of the material system, the details of which appear consistent with the predictions of theory1, 20, 22, 23, 45. In monolayer graphene, the temperature dependence of the resistivity near the Dirac point appears to arise predominately from scattering from screened Coulomb impurities, whereas at higher densities it shows signatures of acoustic and optical phonons. In bilayer graphene, short-range impurities dominate the temperature-dependence of the resistivity for nearly all densities. The exception to this behaviour arises near the Dirac point, where thermal activation out of charge puddles becomes significant. A key approach here has been the application of differential-conductance measurements to suppress the influence of quantum corrections, which has allowed us to identify the various transport regimes relevant to these materials. This approach is expected to be broadly applicable to other low-dimensional materials, and should find application, for example, in the study of transition-metal dichalcogenides and topological insulators.
Methods
Graphene devices were fabricated by exfoliating Kish graphite onto a doped Si substrate with a 300-nm SiO2 cap layer, and an underlying, heavily-doped, Si layer that served as a back gate47. Individual graphene flakes were then contacted with Cr/Au (3-/50-nm) electrodes, defined by electron-beam lithography and lift-off. Layer identification was achieved through a combination of optical microscopy and Raman imaging (see Section S2 of the Supplementary Information). Various devices were fabricated, and characterized electrically, and in the Supplementary Information we show how these exhibited similar and consistent characteristics, independent of the contact configuration used (see Section S1 of the Supplementary Information). In this report, we focus on a detailed study of the differential conductance exhibited by two representative devices, one monolayer and the other bilayer. Optical micrographs of these devices can be seen in the insets to Fig. 1. The various measurements reported here were performed in a four-terminal geometry, thereby eliminating the influence of any contact resistance. In the micrographs of Fig. 1 we indicate how this was achieved, by denoting the two contacts that were used to apply an external (AC and/or DC) voltage(s), and the two internal probes that were then used to measure the resulting voltage drop (v) across a region that then served as our channel. Two different kinds of measurement were made in this study; linear conductance (or resistance) was determined by a low-frequency (13-Hz) AC technique, using a small AC signal (v d = 100-μV RMS) as the externally-applied voltage. For measurements of differential conductance (g d ), a DC voltage (V d ) of varying amplitude was applied on top of this AC component, allowing us to perform differential-conductance spectroscopy as a function of both V d and gate voltage (V g ). An important point that must be emphasized here is that, in all figures and associated text, indicated values of V d are those applied directly to the graphene region under study. These values are determined by utilising the small-signal AC measurements as a calibration; with a knowledge of v d , the external-circuit components, and our measurement of the actual AC voltage drop (v) across the graphene channel, we define a ratio (v/v d ) that we use to determine the actual DC voltage drop across the channel (V d = V d appl × (v/v d )). In this expression, V d appl is the DC voltage applied to the outer contacts of the device. Finally, to suppress the influence of quantum corrections, the differential conductance or resistance (g d −1) was measured by applying a small, but fixed, value of V d and subsequently determining the variation of g d (T)| Vd or g d −1(T)| Vd .
References
Das Sarma, S., Adam, S., Hwang, E. H. & Rossi, E. Electronic transport in two-dimensional graphene. Rev. Mod. Phys. 83, 407 (2011).
Stauber, T., Peres, N. M. R. & Guinea, F. Electronic Transport in Graphene: A Semiclassical Approach Including Midgap States. Phys. Rev. B 76, 205423 (2007).
Hwang, E. H. & Das Sarma, S. Acoustic Phonon Scattering Limited Carrier Mobility in Two-Dimensional Extrinsic Graphene. Phys. Rev. B 77, 115449 (2008).
Morozov, S. V. et al. Giant Intrinsic Carrier Mobilities in Graphene and its Bilayer. Phys. Rev. Lett. 100, 016602 (2008).
Chen, J. H., Jang, C., Xiao, S., Ishigami, M. & Fuhrer, M. S. Intrinsic and Extrinsic Performance Limits of Graphene Devices on SiO2. Nat. Nanotechnol. 3, 206–209 (2008).
Bolotin, K. I., Sikes, K. J., Hone, J., Stormer, H. L. & Kim, P. Temperature-Dependent Transport in Suspended Graphene. Phys. Rev. Lett. 101, 096802 (2008).
Efetov, D. K. & Kim, P. Controlling Electron-Phonon Interactions in Graphene at Ultrahigh Carrier Densities. Phys. Rev. Lett. 105, 256805 (2010).
Park, C.-H. et al. Electron−Phonon Interactions and the Intrinsic Electrical Resistivity of Graphene. Nano Lett. 14, 1113–1119 (2014).
Sohier, T. et al. Phonon-Limited Resistivity of Graphene by First-Principles Calculations: Electron-Phonon Interactions, Strain-Induced Gauge Field, and Boltzmann Equation. Phys. Rev. B 90, 125414 (2014).
Mariani, E. & von Oppen, F. Flexural Phonons in Free-Standing Graphene. Phys. Rev. Lett. 100, 076801 (2008).
Castro, E. V. et al. Limits on Charge Carrier Mobility in Suspended Graphene due to Flexural Phonons. Phys. Rev. Lett. 105, 266601 (2010).
Fratini, S. & Guinea, F. Substrate-Limited Electron Dynamics in Graphene. Phys. Rev. B 77, 195415 (2008).
Zou, K., Hong, X., Keefer, D. & Zhu, J. Deposition of High-Quality HfO2 on Graphene and the Effect of Remote Oxide Phonon Scattering. Phys. Rev. Lett. 105, 126601 (2010).
Cheianov, V. V. & Fal’ko, V. I. Friedel Oscillations, Impurity Scattering, and Temperature Dependence of Resistivity in Graphene. Phys. Rev. Lett. 97, 226801 (2006).
Ando, T. Screening Effect and Impurity Scattering in Monolayer graphene. J. Phys. Soc. Jpn 75, 074716 (2006).
Nomura, K. & MacDonald, A. H. Quantum Transport of Massless Dirac Fermions. Phys. Rev. Lett. 98, 076602 (2007).
Tan, Y.-W. et al. Measurement of Scattering Rate and Minimum Conductivity in Graphene. Phys. Rev. Lett. 99, 246803 (2007).
Hwang, E. H., Adam, S. & Das Sarma, S. Carrier Transport in Two-Dimensional Graphene Layers. Phys. Rev. Lett. 98, 186806 (2007).
Chen, J. H., Jang, C., Fuhrer, M. S., Williams, E. D. & Ishigami, M. Charged-Impurity Scattering in Graphene. Nat. Phys. 4, 377–381 (2008).
Hwang, E. H. & Das Sarma, S. Screening-Induced Temperature-Dependent Transport in Two-Dimensional Graphene. Phys. Rev. B 79, 165404 (2009).
Katsnelson, M. I. Scattering of Charge Carriers by Point Defects in Bilayer Graphene. Phys. Rev. B 76, 073411 (2007).
Das Sarma, S., Hwang, E. H. & Rossi, E. Theory of Carrier Transport in Bilayer Graphene. Phys. Rev. B 81, 161407(R) (2010).
Li, Q., Hwang, E. H. & Das Sarma, S. Disorder-induced temperature-dependent transport in graphene: Puddles, impurities, activation, and diffusion. Phys. Rev. B 84, 115442 (2011).
McCann, E. et al. Weak-Localization Magnetoresistance and Valley Symmetry in Graphene. Phys. Rev. Lett. 97, 146805 (2006).
Wu, X., Li, X., Song, Z., Berger, C. & de Heer, W. A. Weak Antilocalization in Epitaxial Graphene: Evidence for Chiral Electrons. Phys. Rev. Lett. 98, 136801 (2007).
Gorbachev, R. V., Tikhonenko, F. V., Mayorov, A. S., Horsell, D. W. & Savchenko, A. K. Weak Localization in Bilayer Graphene. Phys. Rev. Lett. 98, 176805 (2007).
Tikhonenko, F. V., Horsell, D. W., Gorbachev, R. V. & Savchenko, A. K. Weak Localization in Graphene Flakes. Phys. Rev. Lett. 100, 056802 (2008).
Kozikov, A. A., Savchenko, A. K., Narozhny, B. N. & Shytov, A. V. Electron-Electron Interactions in the Conductivity of Graphene. Phys. Rev. B 82, 075424 (2010).
Jouault, B. et al. Interplay between Interferences and Electron-Electron Interactions in Epitaxial Graphene. Phys. Rev. B 83, 195417 (2011).
Hentschel, M. & Guinea, F. Orthogonality Catastrophe and Kondo Effect in Graphene. Phys. Rev. B 76, 115407 (2007).
Sengupta, K. & Baskaran, G. Tuning Kondo Physics in Graphene with Gate Voltage. Phys. Rev. B 77, 045417 (2008).
Cornaglia, P. S., Usaj, G. & Balseiro, C. A. Localized Spins on Graphene. Phys. Rev. Lett. 102, 046801 (2009).
Chen, J. H., Li, L., Cullen, W. G., Williams, E. D. & Fuhrer, M. H. Tunable Kondo Effect in Graphene with Defects. Nat. Phys. 7, 535–538 (2011).
Gopinadhan, K., Shin, Y. J. & Yang, H. Universal Scaling of Resistivity in Bilayer Graphene. Appl. Phys. Lett. 101, 223111 (2012).
Bistritzer, R. & MacDonald, A. H. Electronic Cooling in Graphene. Phys. Rev. Lett. 102, 206410 (2009).
Tse, W.-K. & Das Sarma, S. Energy relaxation of Hot Dirac Fermions in Graphene. Phys. Rev. B 79, 235406 (2009).
Song, J. C. W., Reizer, M. Y. & Levitov, L. S. Disorder-Assisted Electron-Phonon Scattering and Cooling Pathways in Graphene. Phys. Rev. Lett. 109, 106602 (2012).
Bohra, G. et al. Nonergodicity and Microscopic Symmetry Breaking of the Conductance Fluctuations in Disordered Mesoscopic Graphene. Phys. Rev. B 86, 161405(R) (2012).
Bohra, G. et al. Robust Mesoscopic Fluctuations in Disordered Graphene. Appl. Phys. Lett. 101, 093110 (2012).
Vandecasteele, N., Barreiro, A., Lazzeri, M., Bachtold, A. & Mauri, F. Current-Voltage Characteristics of Graphene Devices: Interplay Between Zener-Klein Tunneling and Defects. Phys. Rev. B 82, 045416 (2010).
Viljas, J. K., Fay, A., Wiesner, M. & Hakonen, P. J. Self-Heating and Nonlinear Current-Voltage Characteristics in Bilayer Graphene. Phys. Rev. B 83, 205421 (2011).
Fay, A. et al. Shot Noise and Conductivity at High Bias in Bilayer Graphene: Signatures of Electron-Optical Phonon Coupling. Phys. Rev. B 84, 245427 (2011).
Price, A. S., Hornett, S. M., Shytov, A. V., Hendry, E. & Horsella, D. W. Nonlinear Resistivity and Heat Dissipation in Monolayer Graphene. Phys. Rev. B 85, 161411(R) (2012).
Han, Q. et al. Highly Sensitive Hot-Electron Bolometer Based on Disordered Graphene. Sci. Rep. 3, 3533 (2013).
Hwang, E. H. & Das Sarma, S. Insulating behavior in metallic bilayer graphene: Interplay between density inhomogeneity and temperature. Phys. Rev. B 82, 081409(R) (2010).
Lin, J. J. & Bird, J. P. Recent Experimental Studies of Electron Dephasing in Metal and Semiconductor Mesoscopic Structures. J. Phys.: Cond. Matt. 14, R501–R596 (2002).
Somphonsane, R. et al. Fast Energy Relaxation of Hot Carriers Near the Dirac Point of Graphene. Nano Lett. 13, 4305–4310 (2013).
Heo, J. et al. Nonmonotonic temperature dependent transport in graphene grown by chemical vapor deposition. Phys. Rev. B 84, 035421 (2011).
Das Sarma, S. & Hwang, E. H. Density-dependent electrical conductivity in suspended graphene: Approaching the Dirac point in transport. Phys. Rev. B 87, 035415 (2013).
Das Sarma, S., Hwang, E. H. & Li, Q. Disorder by order in graphene. Phys. Rev. B 85, 195451 (2012).
Du, X., Skachko, I., Duerr, F., Luican, A. & Andrei, E. Y. Fractional quantum Hall effect and insulating phase of Dirac electrons in graphene. Nature 462, 192 (2009).
Bolotin, K. I. et al. Ultrahigh electron mobility in suspended graphene. Solid State Commun. 146, 351 (2008).
Mayorov, A. S. et al. How Close Can One Approach the Dirac Point in Graphene experimentally? Nano Lett. 12, 4629 (2012).
Zhu, W., Perebeinos, V., Freitag, M. & Avouris, P. Carrier scattering, mobilities, and electrostatic potential in monolayer, bilayer, and trilayer graphene. Phys. Rev. B 80, 235402 (2009).
Acknowledgements
This work was supported by the U.S. Department of Energy, Office of Basic Energy Sciences, Division of Materials Sciences and Engineering under Award DE-FG02–04ER46180. RS acknowledges support from the Thailand Research Fund (TRG5880012), King Mongkut’s Institute of Technology Ladkrabang Research Fund (TRG5880012 & KREF015802), and a research fellowship from the National Science Foundation (OISE0968405). HR and JN acknowledge support of the National Science Foundation (ECCS-1509221).
Author information
Authors and Affiliations
Contributions
R.S., H.R., and G.H. fabricated the graphene transistors, and R.S., H.R., J.N. and C.-P.K. measured their temperature-dependent electrical characteristics. J.N. and N.A. performed Raman microscopy of the devices. R.S., H.R., G.H., J.N., C.-P.K., Y.-H.L., and J.P.B. collaborated on the design of the experiments. R.S., H.R., J.F. and J.B.P. analysed the data and collaborated on the writing of the manuscript.
Corresponding author
Ethics declarations
Competing Interests
The authors declare that they have no competing interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Somphonsane, R., Ramamoorthy, H., He, G. et al. Evaluating the Sources of Graphene’s Resistivity Using Differential Conductance. Sci Rep 7, 10317 (2017). https://doi.org/10.1038/s41598-017-10367-1
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-017-10367-1
- Springer Nature Limited
This article is cited by
-
Electron scattering by Friedel oscillations in carbon nanotubes
Nano Research (2022)
-
Universal scaling of weak localization in graphene due to bias-induced dispersion decoherence
Scientific Reports (2020)