Abstract
Recent developments of high-entropy alloys with high strength and high ductility draw attention to the metastability-engineering strategy. Using first-principle theory, here we demonstrate that reducing the Ta level in the refractory TiZrHfTax system destabilizes the body-centered cubic (bcc) phase and leads to the appearance of the hexagonal close-packed (hcp) phase embedded in the bcc matrix. The alloying-induced features of the elastic parameters for the cubic and hexagonal structures are mapped out in details, and strong sensitivity to the crystal lattice and chemistry is revealed. Results show softening of the bcc matrix with decreasing Ta concentration which ensures ductile behavior. However, the elastically nearly isotropic hcp precipitates possess enhanced resistance against shear which promotes strengthening of the TiZrHfTax dual-phase system. The present atomic-level insight provides strong evidence to the experimental observation, and emphasizes the significance of quantum-design for advanced multi-phase high-entropy alloys with excellent strength-ductility combinations.
Similar content being viewed by others
Introduction
The development of metallic materials with high strength and at the same time enhanced ductility has never faded for scientific interests and technological applications. Over the past years, high-entropy alloys (HEAs) have drawn significant attention as they open up a near-infinite compositional space for designing materials with exceptional properties1,2,3,4,5,6,7,8,9,10. In general, HEAs are composed of multi-principal elements with equal or near-equal molar ratios, and most of them show preference to stabilize in simple solid-solution phases with face-centered cubic (fcc), body-centered cubic (bcc), or hexagonal close-packed (hcp) underlying lattices11. Particularly, the bcc HEAs based on refractory elements usually possess good phase stability and mechanical strength12,13,14, which makes them potential high-temperature structural materials. However, the low ductility observed for several typical system (e.g., NbMoTaW shows compressive plasticity of ~2% at room temperature12) hinders their applications.
Recently, a metastable transformation-induced plasticity effect was introduced in the case of HEAs15,16,17,18. These alloys consist of multiple phases (i.e., fcc and hcp phases), and show improved strength and ductility as compared to many single-phase HEAs. Similar phenomenon was revealed in the refractory TiZrHfTax HEAs that consist of bcc and hcp phases19. Understanding the intrinsic elastic properties of individual structures is critical for optimizing the mechanical performance of such dual-phase HEAs. Unfortunately, today very limited information is available for HEAs with hcp structure, which can be attributed to the complexity of the problem related to the chemical and magnetic disorder in connection with the multicomponent nature of the HEAs. In this work, we employ first-principle theory to bring to light the elastic behavior of the refractory TiZrHfTax HEAs adopting bcc single-phase or bcc/hcp dual-phase with varying Ta fraction from 0 to 2.
Results and Discussion
It is known that the refractory elements Ti, Zr and Hf are stable in the hcp phase at ambient conditions. In Fig. 1a, we present the total energy of TiZrHf for the hcp structure as a function of the Wigner-Seitz radius w and the hexagonal axial ratio c/a. There is a local minimum in the configurational space with w and c/a values around 3.255 bohr and 1.614, respectively. These optimized w and c/a values are slightly larger than 3.234 bohr and 1.587 determined from the linear rule of mixture based on the corresponding experimental data of the alloy components20. Extending this study to TiZrHfTax (Fig. 1b,c) shows that Ta addition gradually decreases w and increases c/a of the host alloy. This trend can be attributed to the smaller atomic radius of the bcc stabilizer elemental Ta as compared to those of the other components. Regarding the Ta concentration dependence of the volume, in Fig. 1c, we compare the present hcp volumes with those obtained using bcc and fcc underlying lattices. It is found that the volume of the bcc phase is always lower than that of the hcp phase irrespective of the composition. We notice that the denser bcc lattice is in line with the experimentally observed volume collapse (observed, e.g., for Zr) at the hcp to bcc phase transition21.
Figure 2a shows the composition-dependent equilibrium total energies of TiZrHfTax for the bcc and fcc structures relative to that of the hcp structure. It is found that for the equiatomic TiZrHf, the structures follow the hcp, fcc and bcc sequence. The same trend was reported in pure Ti, Zr, and Hf metals22. The present theoretical results indicate that the hcp phase is energetically stable in the low-Ta region, and the bcc phase becomes favorable in the upper part of the actual concentration range. At the same time, the fcc phase is always less stable with respect to the hcp phase for all compositions considered here. These theoretical predictions for TiZrHfTax are in line with the experimental observation19, and are consistent with the previous theoretical results for the alloy components23.
Further insight into the phase stability can be gained by considering the electronic density of state (DOS). In Fig. 2, we present the partial and total DOS of TiZrHfTax for the bcc and hcp structures, respectively. The zero of the energy axis is at the Fermi level (EF). It is clear that for the equiatomic TiZrHf, the bottom of the pseudo-gap is located near EF in the hcp phase, whereas EF lies in a region of high DOS in the bcc phase. This implies that the hcp phase has smaller kinetic energy and thus it is more stable than the bcc phase. From Fig. 2c (upper panel), we find that EF is shifted towards the upper part of the bcc peak with increasing x, which is due to the more d-valence electrons of Ta as compared to the other alloy components. On the other hand, the small decrease of the bcc DOS near EF is likely to be associated with the decrease of the hcp-stabilizing elements and the addition of Ta which in pure bcc phase has a pseudo-gap slightly above EF. The pseudo-gap is clearly visible in the bcc partial DOS of alloy components as shown in Fig. 2b (upper four panels). However, due to the hybridization with the so-called hcp-type TiZrHf matrix, Ta loses electrons and thus EF is shifted towards the peak below the bcc pseudo-gap. In contrast, as shown in Fig. 2b (lower four panels) and Fig. 2c (lower panel), for the hcp lattice EF shifts towards the ascending zone (i.e., towards the peak above the hcp pseudo-gap in the Ta-free alloy) when Ta is added, indicating a clear destabilization of the hcp phase. This explains the relative stability of the bcc phase over hcp with increasing Ta content. We notice that the steep negative DOS slope around EF in high-Ta system (not shown) is similar to that of pure V and Nb metals24,25,26. Namely, anomalous temperature dependence may also occur in these HEAs, which could be verified by further theoretical and experimental analysis.
The mechanical stability criteria can be formulated in terms of single-crystal elastic constants. In Fig. 3, we present the complete set of elastic constants of TiZrHfTax for the bcc, fcc and hcp structures, respectively. It is found that in the high-Ta region, the fcc phase loses mechanical stability, as one of the stability criteria for cubic crystal, namely \({C}_{11} > |{C}_{12}|\), is broken, but the other two restrictions, \({C}_{44} > 0\) and \({C}_{11}+2{C}_{12} > 0\), remain valid over the whole composition range. On the other hand, the bcc phase always satisfies the above conditions. The hcp phase is also predicted to be mechanically stable, since the requirements27 \({C}_{11} > |{C}_{12}|\), \({C}_{44} > 0\), \({C}_{11}{C}_{33} > {C}_{13}^{2}\) and \({C}_{33}({C}_{11}+{C}_{12}) > 2{C}_{13}^{2}\) are fulfilled for all compositions. Taking into account the mechanical stability results and those found for the thermodynamic stability, below we discuss the elastic behavior of TiZrHfTax in the bcc and hcp phases only.
For the bcc phase of TiZrHfTax, as shown in Fig. 3a, \({C}_{11}\) and \({C}_{12}\) increase almost linearly with increasing Ta content, while \({C}_{44}\) is much less sensitive to the change of the composition. The three cubic elastic constants calculated for the equiatomic TiZrHfTa are \({C}_{11}\) = 135.6 GPa, \({C}_{12}\) = 97.4 GPa, \({C}_{44}\) = 88.6 GPa, which yield 19.1 GPa for the tetragonal elastic constant \(C^{\prime} =({C}_{11}-{C}_{12})/2\). For reference, pure Ta in the bcc phase has \(C^{\prime} \) around 53 GPa28. Hence, this alloys is predicted to show much weaker dynamical stability against tetragonal deformation as compared to pure Ta. With decreasing Ta, the bcc phase is destabilized as \(C^{\prime} \) decreases. On the other hand, for the hcp phase (Fig. 3c), we find that \({C}_{11}\), \({C}_{12}\), \({C}_{13}\) and \({C}_{33}\) decrease with decreasing Ta content whereas \({C}_{44}\) and \({C}_{66}=({C}_{11}-{C}_{12})/2\) remarkably increase. This feature confirms the stabilization of the hcp phase in the low-Ta region.
Using the single-crystal elastic constants, one can estimate the elastic properties of polycrystalline alloys. Figure 4a shows the ratio \({A}_{{\rm{VR}}}=({G}_{{\rm{V}}}-{G}_{{\rm{R}}})/({G}_{{\rm{V}}}+{G}_{{\rm{R}}})\) of TiZrHfTax for the bcc and hcp structures, where \({G}_{{\rm{V}}}\) and \({G}_{{\rm{R}}}\) are the Voigt and Reuss bounds for the shear modulus, respectively29. We mention that AVR is independent of the crystal structure, and thus it can be used as a measure of the elastic anisotropy of various structures (for isotropic crystals AVR is zero). It is found that AVR increases from 0.02 at x = 0 to 0.17 at x = 2 in the hcp phase, whereas in the bcc phase it varies from 0.68 to 0.16 when x changes from 0 to 2. Previous work reported that most of the cubic and low symmetry crystals have AVR below 0.2120,27,30. On this scale, the elastic anisotropy of hcp TiZrHfTax can be considered small, however, the bcc elastic anisotropy in the low-Ta region is large, which indicates large uncertainties in the predicted average bcc shear modulus. In the following, we make use of the particular shear moduli defined for selected crystal planes.
We consider the \(\{110\}\langle 111\rangle \) slip system for the bcc lattice due to its special role in the plastic deformation. The associated shear modulus can be written as \(G\{110\}\langle 111\rangle =3{C}^{{\rm{^{\prime} }}}{C}_{44}/({C}^{{\rm{^{\prime} }}}+2{C}_{44})\). We notice that this modulus in fact expresses the shear for any possible shear plane \(\{lmn\}\) which contains the 〈111〉 shear direction. Figure 4b shows the alloying-induced changes of \(G\{110\}\langle 111\rangle \) of TiZrHfTax for the bcc structure, and the inset shows the orientation dependence of the shear modulus in the first quadrants of the \(\{110\}\) plane31. The shear modulus in the \(\{110\}\) plane is found to decrease with decreasing Ta for all directions. Meanwhile, there are clear differences between various directions, which emerge for highly anisotropic systems (\({A}_{{\rm{Z}}}={C}_{44}/C^{\prime} > 3\)) as indicated from Fig. 3a. Furthermore, the equiatomic bcc TiZrHfTa has \(G\{110\}\langle 111\rangle \) = 25.9 GPa, which is about four times larger than that of the Ta-free alloy. The corresponding experimental value for pure bcc Ta is around 60.2 GPa28. The sharp decrease of the shear modulus is a consequence of the decreased mechanical stability marked by the change of \(C^{\prime} \) (Fig. 3a). It is known that the shear modulus represents the resistance to reversible deformations upon shear stress, and the reduction of Ta substantially softens the elastic modulus associated with the \(\{110\}\langle 111\rangle \) shear. This elastic softening promotes dislocation mobility and thus it is crucial for the ductile behavior.
Considering the relatively low elastic anisotropy of hcp TiZrHfTax, in Fig. 4c, we plot the average shear modulus on the basal and primary prismatic planes as a function of Ta content. The inset of Fig. 4c presents the effect of differently oriented planes on the values of shear modulus in hexagonal crystals32. As a general observation, all of the alloys considered here show a pronounced minimum value of shear modulus on the \(\{001\}\) basal plane, for which θ is zero, and a tendency to exhibit a maximum between 0° < θ < 90°. This behavior is similar to that of some pure hcp metals like Mg, Sc, and Zr32. Moreover, the shear modulus of TiZrHfTax varies with the amount of Ta from ~52–72 GPa at x = 0, to ~31–55 GPa at x = 1 and to ~18–43 GPa at x = 2. The trends are almost parallel to each other, and thus a direct comparison of alloying-induced changes may be appropriate. Particularly, it is clear from Fig. 4c that the shear modulus increases when Ta is reduced, in contrast to the trend obtained for the bcc phase (Fig. 4b). This suggests that the appearance of the hcp crystallites (in the low-Ta region) should promote strengthening. We mention that the bulk moduli in the bcc and hcp phases are close to each other for all considered compositions (not shown), and thus the markedly different shear moduli control the ductile-brittle behavior of the present alloys.
In summary, we put forward a systematic study of the phase stability and elastic behavior of the refractory TiZrHfTax (0 ≤ x ≤ 2) HEAs by using first-principle alloy theory. The total-energy and electronic structure calculations predict that the hcp phase remains stable in the low-Ta region, whereas Ta addition makes the bcc phase thermodynamically favorable. This trend is in line with the experimental observation. Analysis of the elastic parameters of the bcc phase shows that a relatively soft shear system \(\{110\}\langle 111\rangle \) exists, and the resolved shear modulus decrease rapidly when Ta is gradually reduced, which plays an important role in the enhanced ductility of the dual-phase system. On the other hand, the hcp phase turns out to be elastically nearly isotropic, and the average shear modulus increases with decreasing Ta concentration, which implies that the emerging hcp precipitates promotes strengthening. We propose that the significantly different elastic behavior of the considered alloy phases can serve as a guide for the development of multi-phase HEAs with adjustable mechanical performance.
Methods
The present ab initio calculations were based on the exact muffin-tin orbitals (EMTO) method20, in combination with the coherent potential approximation (CPA)33,34,35. Details about the EMTO-CPA approach and its self-consistent implementation can be found in previous work20. The one-electron Kohn-Shan equations were solved within the scalar-relativistic approximation and soft-core scheme. The muffin-tin basis set included s, p, d and f orbitals. The exchange-correlation effects were treated within the generalized gradient approximation in the form of Perdew-Burke-Ernzerhof (PBE)36. The equilibrium volume and bulk modulus were extracted from the equation of state fitted to the ab initio total energies for a series of different volumes. The single-crystal elastic constants were obtained by straining the lattice and evaluating the energy changes due to the strain as a function of its magnitude at equilibrium volume20,37,38. All calculations were performed for static lattice and for completely disordered solid solutions. The chemical disorder for both lattices was treated by CPA. The present approach was proved to have the necessary accuracy and predictive power to reveal various parameters and mechanisms for complex multicomponent alloys39,40,41,42,43,44,45.
References
Yeh, J. W. et al. Nanostructured high-entropy alloys with multiple principal elements: novel alloy design concepts and outcomes. Adv. Eng. Mater. 6, 299–303 (2004).
Cantor, B., Chang, I. T. H., Knight, P. & Vincent, A. J. B. Microstructural development in equiatomic multicomponent alloys. Mater. Sci. Eng. A 375–377, 213–218 (2004).
Zhang, Y. et al. Microstructures and properties of high-entropy alloys. Prog. Mater. Sci. 61, 1–93 (2014).
Tsai, M. H. & Yeh, J. W. High-entropy alloys: a critical review. Mater. Res. Lett. 2, 107–123 (2014).
Gludovatz, B. et al. A fracture-resistant high-entropy alloy for cryogenic applications. Science 345, 1153–1158 (2014).
Miracle, D. B. & Senkov, O. N. A critical review of high entropy alloys and related concepts. Acta Mater. 122, 448–511 (2017).
Ye, Y. F., Wang, Q., Lu, J., Liu, C. T. & Yang, Y. High-entropy alloy: challenges and prospects. Mater. Today 19, 349–362 (2016).
Zhang, F. et al. Polymorphism in a high-entropy alloy. Nat. Commun. 8, 15687 (2017).
Fan, Z., Wang, H., Wu, Y., Liu, X. & Lu, Z. Thermoelectric performance of PbSnTeSe high-entropy alloys. Mater. Res. Lett. 5, 187–194 (2017).
Yuan, Y. et al. Rare-earth high-entropy alloys with giant magnetocaloric effect. Acta Mater. 125, 481–489 (2017).
Gao, M. C., Yeh, J. W., Liaw, P. K. & Zhang, Y. High-entropy alloys: fundamentals and applications (Springer, Switzerland, 2016).
Senkov, O. N., Wilks, G. B. & Scott, J. M. & Miracle, D. B. Mechanical properties of Nb25Mo25Ta25W25 and V20Nb20Mo20Ta20W20 refractory high entropy alloys. Intermetallics 19, 698–706 (2011).
Zou, Y., Maiti, S., Steurer, W. & Spolenak, R. Size-dependent plasticity in an Nb25Mo25Ta25W25 refractory high-entropy alloy. Acta Mater. 65, 85–97 (2014).
Han, Z. D. et al. Effect of Ti additions on mechanical properties of NbMoTaW and VNbMoTaW refractory high entropy alloys. Intermetallics 84, 153–157 (2017).
Li, Z., Pradeep, K. G., Deng, Y., Raabe, D. & Tasan, C. C. Metastable high-entropy dual-phase alloys overcome the strength-ductility trade-off. Nature 534, 227–230 (2016).
Li, Z., Tasan, C. C., Pradeep, K. G. & Raabe, D. A TRIP-assisted dual-phase high-entropy alloy: grain size and phase fraction effects on deformation behavior. Acta Mater. 131, 323–335 (2017).
Li, Z., Tasan, C. C., Springer, H., Gault, B. & Raabe, D. Interstitial atoms enable joint twinning and transformation induced plasticity in strong and ductile high-entropy alloys. Sci. Rep. 7, 40704 (2017).
Li, Z., Körmann, F., Grabowski, B., Neugebauer, J. & Raabe, D. Ab initio assisted design of quinary dual-phase high-entropy alloys with transformation-induced plasticity. Acta Mater. 136, 262–270 (2017).
Huang, H. et al. Phase-transformation ductilization of brittle high-entropy alloys via metastability engineering. Adv. Mater. 29, 1701678 (2017).
Vitos, L. Computational quantum mechanics for materials engineers (Springer, London, 2007).
Young, D. A. Phase diagrams of the elements (University of California Press, Berkeley, 1991).
Aguayo, A., Murrieta, G. & de Coss, R. Elastic stability and electronic structure of fcc Ti, Zr, and Hf: A first-principles study. Phys. Rev. B 65, 092106 (2002).
Schonecker, S. et al. Metastable cubic and tetragonal phases of transition metals predicted by density-functional theory. RSC Advances 5, 69680–69689 (2015).
Huang, L., Vitos, L., Kwon, S. K., Johansson, B. & Ahuja, R. Thermoelastic properties of random alloys from first-principles theory. Phys. Rev. B 73, 104203 (2006).
Huang, L., Ramzan, M., Vitos, L., Johansson, B. & Ahuja, R. Anomalous temperature dependence of elastic constant C 44 in V, Nb, Ta, Pd, and Pt. J. Phys. Chem. Solids 71, 1065–1068 (2010).
Tian, F., Varga, L. K., Chen, N., Shen, J. & Vitos, L. Ab initio design of elastically isotropic TiZrNbMoVx high-entropy alloys. J. Alloys Compd. 599, 19–25 (2014).
Grimvall, G. Thermophysical properties of materials (North-Holland, Amsterdam, 1999).
Bolef, D. I. Elastic constants of single crystals of the bcc transition elements V, Nb, and Ta. J. Appl. Phys. 32, 100–105 (1961).
Hill, R. The elastic behaviour of a crystalline aggregate. Proc. Phys. Soc. Sect. A 65, 349–354 (1952).
Chung, D. H. & Buessem, W. R. The elastic anisotropy of crystals. J. Appl. Phys. 38, 2010–2012 (1967).
Wortman, J. J. & Evans, R. A. Young’s modulus, shear modulus, and Poisson’s ratio in silicon and germanium. J. Appl. Phys. 36, 153–156 (1965).
Tromans, D. Elastic anisotropy of hcp metal crystals and polycrystals. Int. J. Res. Rev. Appl. Sci. 6, 462–483 (2011).
Soven, P. Coherent-potential model of substitutional disordered alloys. Phys. Rev. 156, 809–813 (1967).
Győrffy, B. L. Coherent-potential approximation for a nonoverlapping-muffin-tin-potential model of random substitutional alloys. Phys. Rev. B 5, 2382–2384 (1972).
Vitos, L., Abrikosov, I. A. & Johansson, B. Anisotropic lattice distortions in random alloys from first-principles theory. Phys. Rev. Lett. 87, 156401 (2001).
Perdew, J. P., Burke, K. & Ernzerhof, M. Generalized gradient approximation made simple. Phys. Rev. Lett. 77, 3865–3868 (1996).
Steinle-Neumann, G., Stixrude, L. & Cohen, R. E. First-principles elastic constants for the hcp transition metals Fe, Co, and Re at high pressure. Phys. Rev. B 60, 791–799 (1999).
Fast, L., Wills, J. M., Johansson, B. & Eriksson, O. Elastic constants of hexagonal transition metals: theory. Phys. Rev. B 51, 17431–17438 (1995).
Huang, S. et al. Thermal expansion in FeCrCoNiGa high-entropy alloy from theory and experiment. Appl. Phys. Lett. 110, 241902 (2017).
Huang, S., Vida, Á., Heczel, A., Holmström, E. & Vitos, L. Thermal expansion, elastic and magnetic properties of FeCoNiCu-based high-entropy alloys using first-principle theory. JOM 69, 2107–2112 (2017).
Huang, S. et al. Mechanism of magnetic transition in FeCrCoNi-based high entropy alloys. Mater. Des. 103, 71–74 (2016).
Huang, S. et al. Phase stability and magnetic behavior of FeCrCoNiGe high-entropy alloy. Appl. Phys. Lett. 107, 251906 (2015).
Huang, S. et al. Temperature dependent stacking fault energy of FeCrCoNiMn high entropy alloy. Scr. Mater. 108, 44–47 (2015).
Huang, S., Holmström, E., Eriksson, O. & Vitos, L. Mapping the magnetic transition temperatures for medium- and high-entropy alloys. Intermetallics 95, 80–84 (2018).
Huang, S. et al. Twinning in metastable high-entropy alloys. Nat. Commun. 9, 2381 (2018).
Acknowledgements
This work was supported by the Swedish Research Council, the Swedish Foundation for Strategic Research, the Swedish Foundation for International Cooperation in Research and Higher Education, the Carl Tryggers Foundation, the Sweden’s Innovation Agency (VINNOVA Grant No. 2014-03374), the Swedish Energy Agency, the China Scholarship Council and the Hungarian Scientific Research Fund (OTKA 109570). We acknowledge the Swedish National Supercomputer Centre in Linköping and Stockholm for computer resources.
Author information
Authors and Affiliations
Contributions
S.H. and L.V. initiated the research; S.H. and W.L. performed the calculations; S.H., E.H. and L.V. analyzed the data. S.H. and L.V. wrote the paper. All authors participated in the discussion and interpretation of the results.
Corresponding authors
Ethics declarations
Competing Interests
The authors declare no competing interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Huang, S., Li, W., Holmström, E. et al. Phase-transition assisted mechanical behavior of TiZrHfTax high-entropy alloys. Sci Rep 8, 12576 (2018). https://doi.org/10.1038/s41598-018-30892-x
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-018-30892-x
- Springer Nature Limited
This article is cited by
-
Chemically induced local lattice distortions versus structural phase transformations in compositionally complex alloys
npj Computational Materials (2021)