Abstract
Since the advent of graphene, a variety of studies have been performed to elucidate its fundamental physics, or to explore its practical applications. Gate-tunable resistance is one of the most important properties of graphene and has been studied in 1–3 layer graphene in a number of efforts to control the band gap to obtain a large on-off ratio. On the other hand, the transport property of multilayer graphene with more than three layers is less well understood. Here we show a new aspect of multilayer graphene. We found that four-layer graphene shows intrinsic peak structures in the gate voltage dependence of its resistance at zero magnetic field. Measurement of quantum oscillations in magnetic field confirmed that the peaks originate from the specific band structure of graphene and appear at the carrier density for the bottoms of conduction bands and valence bands. The intrinsic peak structures should generally be observed in AB-stacked multilayer graphene. The present results would be significant for understanding the physics of graphene and making graphene FET devices.
Similar content being viewed by others
Introduction
Graphene is a material with excellent physical properties—its electrical mobility, for example, much higher than that of organic semiconductors1,2—and is a candidate base material for next-generation devices. Controllability of resistance by using gate voltage is one of most significant properties of graphene for practical application in FET devices. It is known that transport property of graphene is highly influenced by the surface environment (e.g., ionized impurity, contamination or ripples, etc.3,4). Gate-voltage dependence of the resistance of such dirty graphene samples often shows multiple-peak structure, which possibly originate from local potential energy differences due to the surface contamination. Placing graphene on high-quality h-BN flakes or using encapsulation techniques drastically improve the electron mobility of graphene samples and enables one to measure intrinsic features of the transport property of graphene5,6,7. In high-mobility graphene, a large resistance peak appears at the charge neutrality point and resistance decreases monotonically with increasing carrier density5,6,7. This would be a natural property of graphene with a single band, such as mono- and bilayer graphene. Although AB-stacked trilayer graphene has a bilayer-like band and a monolayer-like band, the gate voltage dependence of its resistance would be similar to that of the single-band system because the density of states of the bilayer-like band is much larger than that of the monolayer-like band and is dominant7. On the other hand, AB-stacked multilayer graphene with larger number of layers does not necessarily show the above mentioned property because it has more than two bilayer-like bands. In this work, we studied AB-stacked tetralayer graphene, which is the simplest case of multilayer graphene with more than three layers. The band structure of AB-stacked tetralayer graphene is shown schematically in panel i of Fig. 1a. The energy of the bottom of the light-mass bilayer-like band is higher than that of the heavy-mass bilayer-like band, and the density of states of the light-mass bilayer-like band is not negligible with respect to that of the heavy-mass bilayer-like band. This paper will show that this multi-bilayer-like band leads to the phenomenon that gate-voltage dependence of resistance generally shows intrinsic peak structures.
Results
Experimental
We employed a technique to modify electronic band structure by using perpendicular electric field. The method was originally proposed to create an energy gap in the graphene system. Monolayer graphene, where electrons behave like massless Dirac fermions with linear dispersion relation8,9,10, does not have a band gap. Bilayer graphene, where electron bands have massive dispersion relations10,11,12, does not have a band gap either. However, it was predicted that a perpendicular electric field forms an energy gap between the bottoms of conduction and valence bands13,14. The response of AB-stacked graphene’s electronic structure to perpendicular electric fields shows significant layer-number dependence. AB-stacked trilayer graphene, for example, has a bilayer-like band and monolayer-like band. Unlike bilayer graphene, it does not exhibit insulating behavior induced by applying a perpendicular electric field. Its electric resistance instead decreases13,14,15. Electronic band structure in AB-stacked tetralayer graphene in the presence of a perpendicular electric field is schematically described in panel ii in Fig. 1a. An electric field opens an energy gap at the bottoms of each of the bilayer-like bands.
In order to detect electronic structure by using a transport experiment, the quality of the graphene should be sufficiently high. Moreover, top and bottom electrodes are required to apply a perpendicular electric field. This requirement was attained by using the AB-stacked tetralayer graphene device shown in Fig. 1b. AB-stacked tetralayer graphene was encapsulated with h-BN16, and onto the top of the stack was transferred a rather thick graphene flake serving as a top gate electrode. This stack of films was formed on a SiO2/Si substrate, where Si is conducting at low temperatures and served as a bottom gate. Encapsulation of graphene by high-quality h-BN flakes drastically increases the electric mobility of graphene. The high-quality and atomically flat surface of the h-BN flakes reduces scattering due to ionized impurity and surface roughness6,16,17. Mobility of the graphene which was calculated with μ = 1/nep, was more than 40,000 cm2/VS at the high carrier density regime.
Gate voltage dependence of resistivity at zero magnetic field
Figure 2a shows bottom gate voltage Vbg dependence of resistivity for different top gate voltages Vtg measured at T = 4.2 K. In the trace with Vtg = 0V, a slightly complicated peak structures are discernible near the charge neutrality point. The peak structure showed significant variation as top gate voltages was varied. The most prominent variation is enhancement of the peak, which grows with increasing |Vtg| values and appeared roughly symmetric with respect to Vtg = 0V. The enhancement of the resistance by top gate voltage would be qualitatively understood by formation of a band gap by perpendicular electric fields, as in bilayer graphene14. However, the largest peak of Vbg-dependence of resistivity at Vtg = 0V reached to only approximately 250 ohms, and this value was smaller than that in the preceding study in AB-stacked tetralayer graphene that reported insulating behavior18. This indicates that energy gap in tetralayer graphene encapsulated with h-BN would be considerably small (see the Supplementary Information).
Beside the large peak structure there were small peaks as shown in Fig. 2a. These peaks appeared even at Vtg = 0V. As shown in the following discussion, the presence of these peaks is an intrinsic property of AB-stacked tetralayer graphene. In the case of dirty graphene, multiple peaks might be observed because inhomogeneity in the sample or surface contaminations can create locally different electrostatic potentials. However, our samples were encapsulated using a dry process, which ensures clean surfaces. The peaks are reproducibly observed in other samples with the same number of layers. Samples with larger numbers of layers also show different peak structures (see Supplementary Information).
In order to study the peak structure further, we measured resistivity as a function of the top and the bottom gate voltages (Fig. 2b). Gate voltages were converted into carrier densities ntg and nbg, which are induced by top and bottom gate voltage, and were calculated by using calibrated specific capacitance. It is clear that the observed peak in Fig. 2a showed significant dependence on ntg and nbg, and appeared as resistance ridges. By applying both top and bottom gate voltage, total charge density −entot induced in graphene can be expressed by \(-e{n}_{tot}=-\,e({n}_{tg}+{n}_{bg})=\,-\,({C}_{tg}{V}_{tg}+\,{C}_{bg}\,{V}_{bg})\) where Ctg and Cbg are top and bottom gate capacitances, respectively. The white broken line a in the figure that passes through nbg = 0 and ntg = 0 is a resistance ridge that connects two large peaks appearing at ntg = ±0.8 × 1012. On this line, graphene is in a condition of charge neutrality and total carrier density estimated from Hall resistance vanishes. Here, carriers induced by the top gate voltage and bottom gate voltage are compensated, i.e., CtgVtg + CbgVbg = 0. The ratio of capacitances, Cbg/Ctg was calculated to be 0.078. Using calibrated specific bottom gate capacitance, Cbg = 108 aF/μm2, Ctg was calculated to be Ctg = 1385 aF/μm2. On the other hand, D⊥ = −e(nbg − ntg) = CtgVtg − CbgVbg is the difference in charge density induced by top and bottom gate voltages and is proportional to the electric flux density in graphene. D⊥ is proportional to the electric field perpendicular to the surface of graphene. At the charge neutrality point, ridge a appears. In addition, other resistance ridges b, c, and d showed different dependence on gate voltages. In particular ridges b and c are not parallel to the line of charge neutrality point (ridge a), and crossed at approximately \({n}_{bg}=\,{n}_{tg}\approx 0.4\times {10}^{12}\,{{\rm{cm}}}^{-2}\). The ridge d also show a weak dependence as is seen by connecting two largest resistance peaks appearing at ntg = ±0.8 × 1012 cm−2.
In order to inspect the nature of the ridges, we replot it as a function of ntot and electric flux density D⊥ as shown in Fig. 2c. The figure has a few remarkable features. First, ridge structures appear symmetrically about D⊥ = 0, from which one could infer that the ridge structures originated from the intrinsic property of graphene. In particular, ridges b and c overlap at D⊥ = 0, forming a single peak. These ridges possibly originated from bottoms of a conduction band and a valence band of light-mass bilayer-like band. At D⊥ = 0, the conduction band and valence band of the light-mass bilayer-like band contact at their bottoms (see left panel ii in Fig. 2c). The structure of the crossing is reminiscent of the energy gap in the bilayer-like band formed by applying a perpendicular electric field as shown in panel iii in Fig. 2c and is possibly related to the light-mass bilayer-like band. Secondly, ridge d seems to connect large peaks appearing at D⊥≈ ±2× 10−7 cm−2 sA and merge into ridge a. The growing resistivity with increasing |D⊥| at ntot = 0 would result from decreasing semi-metallic carriers. Density of states for electron-like band and hole-like band tends to decrease. Possibly a small energy gap is formed (see the Supplementary Information).
Landau level spectroscopy
Energy band structure can be directly probed by quantum oscillation measurement in magnetic fields at T = 4.2 K. The structure of Landau levels revealed the nature of the resistance ridges at zero magnetic field. Figure 3a displays a map of Rxx as a function of ntot and B. Here Vtg and Vbg were varied so that the condition D⊥ = 0 was satisfied. Figure 3b shows a color map of longitudinal conductivity \({\sigma }_{xx}\,\)which was calculated by using a formula, \({\sigma }_{xx}={\rho }_{xx}/({\rho }_{xx}^{2}+{\rho }_{xy}^{2})\). Before discussing the effect of perpendicular electric fields, here, we briefly explain the fan diagram. Complicated stripes are due to Shubnikov-de Haas oscillation which originated from Landau quantization of two-dimensional electrons. Each stripe is a Landau level of a specific band, and has a specific index. Landau levels of AB-stacked tetralayer graphene basically consist of two sets of Landau levels for bilayer-like bands: one for the light-mass bilayer-like band and the other for the heavy-mass bilayer-like band. Mixing and crossing of these Landau levels make the structure of the fan diagram complicated18,19. Next, we focus on zero-mode Landau levels that appear near the bottoms of bands, and energy gap appearing in the vicinity of charge neutrality points. Arrows β and γ, which grow vertically with increasing magnetic field, are zero-mode Landau levels of the light-mass and the heavy-mass bilayer-like band. These zero-mode Landau levels generally appear at the bottoms of bands in the Dirac fermions9. Analysis of filling factor ν of energy gaps associated with the Landau level crossing indicated that the zero-mode Landau levels have a degeneracy of eight, which is a hallmark of bilayer-like bands.
Now we discuss the relationship between the fan diagram and the ridge structure at zero magnetic field. Ridge structures appear approximately the same values of ntot with those of zero-mode Landau levels. Because zero-mode Landau level is formed near the bottoms of the bands, ntot at which the zero-mode Landau level appears would be a measure of ntot for the bottoms of the bands at zero magnetic field. For D⊥ = 0, the zero-mode Landau level β of light mass bilayer-like band appeared at approximately the same ntot as the crossing point of the ridges b and c in the lower panel in Fig. 3a (the same as Fig. 2c). On the other hand, zero-mode Landau level γ for heavy mass bilayer-like band appeared on ridge d in the vicinity of D⊥ = 0.
A similar correspondence can be found in the case of non-vanishing vertical electric field. Figure 3c,d show results for D⊥ = -2.7 × 10−7 and +2.7 × 10−7 cm−2 sA, respectively. Values of D⊥ are indicated by arrows in lower panels. It is clear that zero-mode Landau level β in Fig. 3a has split into two zero-modes β1 and β2 with four-fold degeneracy. (β2 also showed small splitting into two levels with two-fold degeneracy at high magnetic fields). The zero-mode Landau levels β1 and β2, appeared at approximately the same ntot of that for ridges b and c in zero magnetic field (yellow points). As for the heavy-mass bilayer-like band, splitting is not clearly observed in the fan diagram. However ridge structures similar to a and b are actually observed for heavy mass bilayer-like band in measurement of wider area using a different sample (see the Supplementary Information).
Ridge a, on the other hand, is not relevant to zero-mode Landau levels. As seen in Fig. 3a,b, when at least B > 0.5 T, there was an energy gap at around ntot = 0 (indicated with arrow α). This indicates that carrier density is considerably small in zero magnetic field. The ridge d in Fig. 3 is influenced by growing resistivity of ridge a for |D⊥| > ± 0.8 × 10−7 cm−2 sA.
Behavior of zero-mode Landau levels with respect to D ⊥ at a fixed magnetic field
The origin of the ridge structure was further checked by detailed measurements of Landau levels as a function of ntot and D⊥. Upper panel in Fig. 4 displays a top and bottom gate voltage dependence of longitudinal resistivity measured in a magnetic field of approximately B = 3.3 T. The derivative of longitudinal resistance with respect to total carrier density ntot (dRxx/dntot) is shown to enhance visibility. The step-like structure indicated by β2 corresponds to zero-mode Landau level β2 in Fig. 3c. Two dashed lines of the step shape indicate that Landau level β2 split. Zero-mode Landau level β1 also split into two levels. By comparing with lower panel in Fig. 4, which is results for zero magnetic field, it is clear that zero-mode Landau Levels β1 and β2 follow the ridge structure b and c. This clearly indicates that the ridges b and c originate from bottoms of split light-mass bilayer-like band. The step-like feature originates from crossing of zero-mode with other Landau levels with higher indices. For example, a step appearing at D⊥ ≈ −2 × 10−7 cm−2 sA and ntot ≈ 1.3 × 1012 cm−2 is a crossing with the Landau level labeled as δ. On the other hand, the zero-mode Landau level of the heavy-mass bilayer-like band, is not clearly seen in Fig. 4. This is because at the measured magnetic field, the zero-mode Landau level crosses the Landau levels that appear between gaps with filling factors −12 and −8 at ntot = −0.4 × 1012 cm−2.
Discussion
Origin of resistance ridge structure in zero magnetic field
As seen in the above, the ridges in the carrier density dependence of resistance (or resistance peaks in ntot dependences at fixed values of D⊥) at zero magnetic field reflected electronic band structure. Ridges, which appeared not at the charge neutrality point, are closely related to the bottoms of conduction and valence bands. Conductivity of the samples is contributed by the light-mass bilayer-like band and the heavy-mass bilayer-like band, which are naturally expected to have different mobilities. Therefore, in the frame of two-carrier model conductivity σ is expressed by
Here nL and nH are carrier densities of the light-mass bilayer-like band and heavy-mass bilayer-like band, and μL and μH are their mobilities. Total carrier density is sum of nL and nH, i.e., ntot = nL + nH. The values of the mobility may be different because the band masses of the light-mass bilayer-like band and heavy-mass bilayer-like band should be different. In order to discuss resistance peak structure (or conductance dip structure), one needs to assume ntot dependence of nL or nH. If we assume a semi-metallic band structure consisting of parabolic bands and assume that μL and μH are constant values, ntot dependence of the conductance is simply given by a polygonal line whose vertices are located at ntot for the bottoms of the bands. This results in discontinuous dσ/dntot at the vertices and generally results in a single dip structure in the conductivity (or a single peak in the resistance). To explain resistance peaks at the bottoms of the bands, the mobility for each band would presumably be dependent on the carrier density. Mobility calculated by using μ = σ/entot generally varies with the carrier density. This phenomenon is widely seen in monolayer and bilayer graphene and results from nature of ionized impurity scattering and screening20. Moreover, mobilities would vary at the bottoms of the bands because the band mass would vary near the bottoms of the band owing to mixing of light-mass and heavy-mass bilayer-like bands which is shown in a band calculation considering full Slonczweski-Weiss-McClure (SWMcC) parameters21 (see the Supplementary Information).
On the other hand, ridge structure, which was observed at the vicinity of charge neutrality point, would require a bit different explanation. The observed ridge at the charge neutrality point would be related to the report from ref.18 showing insulating behavior at the charge neutrality point. A small energy gap is possibly formed because of, for example, the staggered potential due to many body interaction of electrons18,22,23. In this paper we tentatively attributed the enhancement of resistance to possible formation of energy gap (see the Supplementary Information). Electronic states near the charge neutrality point in tetralayer graphene is expected to be complicated as compared to graphene with fewer number of layers, and would require further investigation.
Spatial symmetry and energy gap
In case of even-layer graphene, spatial inversion symmetry and time reversal symmetry impose strict conditions on the energy state. A conduction band and a valence bands are degenerated at k = 0. Therefore, bottoms of conduction and valence bands contact at k = 0, and an energy gap does not open23. However if spatial inversion symmetry is broken by the potential due to a perpendicular electric field, an energy gap is allowed to open. This fact could be clearly observed by the crossing of ridges b and c at D⊥ = 0. Simple band calculation indicates that gap magnitude generally differs between light-mass and heavy-mass bilayer-like bands, as was observed in the experiment (see Supplementary Information).
Valley splitting
The broken spatial symmetry caused by the perpendicular electric field is also relevant to the valley splitting of the zero-mode Landau levels. At zero magnetic field, spatial inversion symmetry results in degenerate quantum states for K and K’ points in reciprocal lattice space. Quantum states at K and K’ points are also degenerated in magnetic fields. The eight-fold degenerated zero-mode Landau levels, which were observed in present experiment for D⊥ = 0, are due to inequivalent quantum states for K and K’ points. Zero-mode Landau level splitting due to a perpendicular electric field is a result of breaking of spatial inversion symmetry. Moreover Landau level calculation based on effective mass approximation indicated that the splitting is due to the valley-splitting; quantum states for K and K’ points are no longer equivalent, and the zero-mode Landau levels show large valley splitting while those levels with larger indices show smaller valley-splitting, which is consistent with our observation.
In AB-stacked tetralayer graphene samples with a single gate electrode, the valley split zero-mode Landau levels with degeneracy of four or less are always observed rather than eight-fold degenerate Landau levels even though a perpendicular electric field is not intentionally applied by using top and bottom electrodes. This is because spatial inversion symmetry is broken owing to the electrostatic potential due to gate induced charges which screens gate electric fields24 (see the Supplementary Information).
Multilayer graphene
The multiple-peak structure in Vg dependence of resistance at zero magnetic field would be a general property of multilayer graphene with four or more layers. In six-layer graphene we found ridge structures similar to those in Fig. 2b,c but with more, which reflected three sets of bilayer-like bands (see the Supplementary Information). These properties of multilayer graphene have not been reported previously. This would be because mobility of the samples was not sufficiently high. Indeed, low mobility samples show a broad peak or broad peaks, and it is difficult to discuss electronic band structure.
Summary
We have studied transport property of AB-stacked tetralayer graphene samples which are encapsulated with h-BN flakes and have top and bottom gate electrodes. We found that, at zero magnetic field, the top and bottom gate voltage dependence of resistance shows non-trivial ridge structures which stem from band structures. By analyzing Landau fan diagrams, positions of some ridge structures were verified to correspond to those of the zero-mode Landau levels of bilayer-like bands. They are eight-fold degenerated at zero perpendicular electric field while they split into two four-fold degenerated levels in presence of perpendicular electric field. Correspondingly, the ridge structures crossed at zero electric field. On the other hand resistance increased by applying perpendicular electric field at the charge neutrality point at zero magnetic field, however, strong insulating behavior was not observed. In AB-stacked six-layer graphene we also found similar ridge structures. The ridges that appear in the top and bottom gate voltage dependence would be a common feature of multilayer graphene with number of layers larger than three.
Methods
Graphene was prepared by mechanically exfoliating high-quality Kish graphite using adhesive tape. Graphene was encapsulated with high quality h-BN flakes. The top gate was several-layer graphene that was deposited on top of the encapsulated graphene. Each sample was patterned into a Hall bar using standard electron beam lithography. Electric resistance was measured using the standard lock-in technique with a low-frequency excitation current whose frequency and amplitude were typically 10 Hz and 1 μA. Magnetic fields were applied by using a superconducting solenoid. Transport measurements were performed at temperature of 4.2 K.
References
Geim, A. K. & Novoselov, K. S. The rise of graphene. Nature Mat. 6, 183 (2007).
Castro Neto, A. H., Guinea, F., Peres, N. M. R., Novoselov, K. S. & Geim, A. K. The electronic properties of graphene. Rev. Mod. Phys. 81, 109 (2009).
Das Sarma, S., Adam, S., Hwang, E. H. & Rossi, E. Electronic transport in two-dimensional graphene. Rev. Mod. Phys. 83, 407 (2011).
Martin, J. et al. Observation of electron-hole puddles in graphene using a scanning single-electron transistor. Nature Phys. 4, 144 (2008).
Bolotin, K. I. et al. Ultrahigh electron mobility in suspended graphene. Solid State Commun. 146, 351 (2008).
Dean, C. R. et al. Boron nitride substrates for high-quality graphene electronics. Nature Nanotechnol. 5, 722 (2010).
Taychatanapat, T., Watanabe, K., Taniguchi, T. & Jarillo-Herrero, P. Quantum Hall effect and Landau-level crossing of Dirac fermions in trilayer graphene. Nature Phys. 7, 621 (2011).
Wallace, P. R. The band theory of graphite. Phys. Rev. 71, 622 (1947).
Shon, N. H. & Ando, T. Quantum transport in two-dimensional graphite system. J. Phys. Soc. Jpn. 67, 2421 (1998).
Novoselov, K. S. et al. Two-dimensional gas of massless Dirac fermions in graphene. Nature 438, 197 (2005).
McCann, E. Asymmetry gap in the electronic band structure of bilayer graphene. Phys. Rev. B 74, 161403 (2006).
Koshino, M. & Ando, T. Transport in bilayer graphene. Phys. Rev. B 73, 245403 (2006).
Jhang, S. H. et al. Stacking-order dependent transport properties of trilayer graphene. Phys. Rev. B 84, 161408 (2011).
Zou, K. et al. Transport studies of dual-gated ABC and ABA trilayer graphene. Nano Lett. 13, 369 (2013).
Lui, C. H. et al. Observation of an electrically tunable band gap in trilayer graphene. Nature Phys. 7, 944 (2011).
Wang, L. et al. One-dimensional electrical contact to a two-dimensional material. Science 342, 614 (2013).
Zomer, P. J., Dash, S. P., Tombros, N. & van Wees, B. J. A transfer technique for high mobility graphene devices on commercially available hexagonal boron nitride. Appl. Phys. Lett. 99, 232104 (2011).
Grushina, A. L. et al. Insulating state in tetralayers reveals an even-odd interaction effect in multilayer graphene. Nature Commun. 6, 6419 (2015).
Wu, Z. F. et al. Detection of interlayer interaction in few-layer graphene. Phys. Rev. B 92, 075408 (2015).
Tan, Y. W. et al. Measurement of scattering rate and minimum conductivity in graphene. Phys. Rev. Lett. 99, 246803 (2007).
Koshino, M. & Ando, T. Electronic structures and optical absorption of multilayer graphenes. Solid State Commun. 149, 1123 (2009).
Nam, Y. et al. Interaction-induced insulating state in thick multilayer graphene. 2D Mater. 3, 045014 (2016).
Koshino, M., Sugisawa, K. & McCann, E. Interaction-induced insulating states in multilayer graphenes. Phys. Rev. B 95, 235311 (2017).
Hirahara et al. Magnetoresistance measurements of tetra-layer graphene device with single gate electrode. J. Phys. Conf. Ser. 969, 012150 (2018).
Acknowledgements
This work was supported by KAKENHI No. 25107003 from MEXT Japan. Authors thank M. Koshino at Osaka University and R. Saito at Tohoku University for valuable discussions. They also thank Y. Iye at the University of Tokyo for providing high-quality graphite crystals.
Author information
Authors and Affiliations
Contributions
T.H. and R.Y. conceived the experiments. The samples were made by T.H., T.N., R.E., T.O. and S.T. Measurements were carried out by T.H. and T.N. High quality h-BN crystals were grown by K.W. and T.T. T.H. and R.Y. analyzed data and wrote manuscript.
Corresponding author
Ethics declarations
Competing Interests
The authors declare no competing interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Hirahara, T., Ebisuoka, R., Oka, T. et al. Multilayer graphene shows intrinsic resistance peaks in the carrier density dependence. Sci Rep 8, 13992 (2018). https://doi.org/10.1038/s41598-018-32214-7
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-018-32214-7
- Springer Nature Limited
Keywords
This article is cited by
-
Unconventional satellite resistance peaks in moiré superlattice of h-BN/ AB-stacked tetralayer-graphene heterostructures
Communications Physics (2021)