Abstract
Micromechanical resonators with ultra-low energy dissipation are essential for a wide range of applications, such as navigation in GPS-denied environments. Routinely implemented in silicon (Si), their energy dissipation often reaches the quantum limits of Si, which can be surpassed by using materials with lower intrinsic loss. This paper explores dissipation limits in 4H monocrystalline silicon carbide-on-insulator (4H-SiCOI) mechanical resonators fabricated at wafer-level, and reports on ultra-high quality-factors (Q) in gyroscopic-mode disk resonators. The SiC disk resonators are anchored upon an acoustically-engineered Si substrate containing a phononic crystal which suppresses anchor loss and promises QANCHOR near 1 Billion by design. Operating deep in the adiabatic regime, the bulk acoustic wave (BAW) modes of solid SiC disks are mostly free of bulk thermoelastic damping. Capacitively-transduced SiC BAW disk resonators consistently display gyroscopic m = 3 modes with Q-factors above 2 Million (M) at 6.29 MHz, limited by surface TED due to microscale roughness along the disk sidewalls. The surface TED limit is revealed by optical measurements on a SiC disk, with nanoscale smooth sidewalls, exhibiting Q = 18 M at 5.3 MHz, corresponding to f · Q = 9 · 1013 Hz, a 5-fold improvement over the Akhiezer limit of Si. Our results pave the path for integrated SiC resonators and resonant gyroscopes with Q-factors beyond the reach of Si.
Similar content being viewed by others
Introduction
Resonant microelectromechanical systems (MEMS) have permeated a wide range of applications, from consumer electronics to precision robotics and inertial navigation on chip1, using at their heart resonators as mass sensors, pressure sensors, clocks, accelerometers and gyroscopes2. The resolution of MEMS resonators and resonant gyroscopes in particular is limited by electrical and Brownian mechanical noise3, which can be reduced by minimizing energy dissipation to the surroundings4. Specifically, the Brownian mechanical noise scales as Q−1/2 where Q or Q-factor is inversely proportional to energy dissipation. To achieve the lowest possible Brownian mechanical noise and high signal-to-noise ratio, advanced structural designs have been developed in silicon (Si) resonators to minimize energy dissipation and bind Q to intrinsic quantum-based losses combining bulk thermoelastic damping (QTED) and Akhiezer damping (QAKHIEZER) in the megahertz frequency range5,6. For example, energy dissipation in substrate-decoupled gyroscopic-mode silicon (Si) disk resonators approaches the overall quantum limit7,8 while TED-free Lamé resonators cooled down to 120 K have reached the Akhiezer limit of Si9.
Due to ease of fabrication and wafer-level patterning with nanoscale precision, Si has been the prominent structural material for MEMS resonators and resonant gyroscopes. To further improve Q beyond the quantum limits of Si, materials that exhibit lower intrinsic dissipation are under active investigation3. Chief among those is monocrystalline silicon carbide (SiC), an appealing substrate due to its record-low Akhiezer damping compared to all other commonly micro-machinable substrates such as diamond10 and SiN11 and availability of 4” monocrystalline on-axis 4H-SiC wafers. Recent theoretical studies show that Akhiezer damping in SiC can be 30X lower than in Si in the megahertz frequency spectrum3,12. Furthermore, SiC electronics can operate at temperatures exceeding 800 °C, drastically improving the near-150 °C limit of Si electronics and conferring high-temperature robustness to an all-SiC MEMS and Electronics approach13. An all-SiC platform could demonstrate navigation-grade bulk acoustic wave (BAW) gyroscopes that can be deployed in harsh environments such as underground drilling bits.
The cost of production-grade monocrystalline SiC substrates, the restricted deployment of dedicated dry etchers, and the chemical inertness of monocrystalline SiC have tremendously obstructed the realization of SiC resonators with ultra-low dissipation. Through fabrication of fusion-bonded SiC-on-Insulator (SiCOI) substrates, implementation of a substrate-decoupling approach robust to fabrication inaccuracies and the development of nanoscale-precision deep reactive ion etching (DRIE) of SiCOI substrates, this paper lifts some of these limitations and explores the suitability of thick on-axis monocrystalline 4H-SiCOI substrates for mode-matched resonant BAW disk gyroscopes. Advanced processing techniques critical to circumvent extrinsic losses are successfully demonstrated in SiCOI substrates, including forming polycrystalline silicon plugs and defining phononic crystals in the Si handle layer. For the first time, centrally-supported and completely solid SiC disk resonators demonstrate f · Q products near 9.5 · 1013 Hz, well beyond the reach of Si in the megahertz frequency range.
Results
Design of ultra-low dissipation SiC disk resonators with gyroscopic modes
Figure 1a reveals that SiC benefits from an extraordinary low phonon-phonon dissipation limit owing in part to its high Debye average velocity and low Grüneisen parameter, which prevent normal and Umklapp scattering with thermal phonons from siphoning energy when the phonon distribution is perturbed from its equilibrium distribution by the strain produced by acoustic waves14. These pristine material properties concur to reduce the amplitude of lattice thermal vibrations, limit scattering opportunities and restrict anharmonic phonon-phonon scattering in the Akhiezer regime. In practice, multiple extrinsic dissipation mechanisms overshadow intrinsic losses in SiC micromechanical resonators:
Equation (1) guides our design approach to suppress extrinsic loss mechanisms and bind dissipation to intrinsic loss mechanisms. The approach consists in removing anchor loss (QANCHOR) using a non-coplanar 2.5 dimensional (2.5 D) substrate decoupling approach without loading QTED and in operating bulk modes under vacuum to elude air damping (QAIR). Concentrating the energy far from the dissipative surfaces of BAW resonators and taking advantage of the high Young’s modulus of SiC reduces the contribution of surface effects (QSURFACE) to energy dissipation15,16.
Although multiple advanced designs enabling complete substrate deafness (QANCHOR near 1B) have been successfully implemented in center-supported Si BAW resonant gyroscopes7,8, these designs cannot be applied in practice to ultra-high Q SiC resonators and resonant gyroscopes. Using disks with substrate-decoupling structures5,17, instead of completely-solid disks, introduces additional dissipation pathways, severely degrading QTED and negating the benefits of record-high QAKHIEZER. Decreasing the ratio of the SiO2 pedestal’s diameter to the SiC disk’s diameter to below 5% and increasing the height of the SiO2 pedestal to above 200 μm completely circumvent anchor loss while severely compromising structural integrity and resilience to shocks and vibrations. In this work, the anchor loss of centrally-anchored SiC BAW disk resonators is suppressed and both structural integrity and QTED are preserved. Defined in the Si handle layer, an enhanced phononic crystal (PnC)14,18 localizes acoustic energy in the SiC disk resonator through the suppression of acoustic waves travelling in any arbitrary direction in Si under the condition their frequencies are sufficiently close to the target disk’s resonance frequency. By placing the substrate-decoupling PnC and the mechanical resonators in separate planes, the acoustically-deaf Si handle layer can support an array of ultra-high Q SiC resonators while maintaining the die’s footprint. Navigation-grade inertial measurement units (IMUs) contain multiple ultra-high Q gyroscopes, accelerometers and clocks1 and will directly benefit from the demonstration of this non-coplanar 2.5D substrate-decoupling approach which is applied to a single gyroscopic-mode disk resonator in this work. The design details of this 2.5 D frequency-dependent decoupling approach have been published elsewhere14. Matching the bandgap center frequency of the Si PnC and the resonance frequency of the SiC BAW disk resonator prevents in-plane waves from travelling in the Si handle layer. Similarly, out-of-plane waves travelling in the Si handle layer are suppressed by quarter-wavelength-matching the thickness of the Si handle layer to the resonance frequency. Through quarter-wavelength matching, the thickness and acoustic properties of the handle layer set the optimal target resonance frequency and define the frequency-setting dimensions of the SiC resonators; any frequency mismatch reduces the efficiency of this frequency-dependent decoupling approach and loads QANCHOR (see Supplementary Note 1). The QANCHOR of 6.29 MHz m = 3 elliptical modes in 1.4 mm-wide and 55 μm-thick SiC disks on a suspended 380 μm-thick Si honeycomb PnC approaches 1B across all simulated process corners, including thickness variations of the Si handle layer as well as design and fabrication inaccuracies of the PnC (Fig. 1b). Suspending the PnC prevents any physical contact and preserves an effective decoupling approach.
The quarter-wavelength-matching condition for SiCOI wafers with 100s- μm-thick Si handle layer places the optimized resonance frequencies at megahertz range, which is also favorable for achieving high QTED in SiC resonators19. Megahertz BAW disk resonators with frequency-setting dimensions in the millimeter range operate in the deep adiabatic regime. Because thermo-mechanical couplings are suppressed in the adiabatic regime, high QTED significantly above 1 M can be reached in mm-scale BAW disk resonators, despite the relatively high coefficient of thermal expansion (CTE) of SiC. Perforations or micro-scale sidewall roughness permit additional thermo-mechanical couplings to severely degrade QTED17, making a perforation-free design and sidewalls with nanoscale smoothness critical characteristics of micromechanical resonators with ultra-high QTED. For example, Fig. 1c shows that microscale sidewall roughness along the sidewall of completely-solid millimeter-wide SiC disks substantially drops QTED from 36 M to 3 M, making surface TED20 the main damping mechanism in this work. Figure 1d shows dissipation in solid SiC disk resonators operating in the secondary elliptical mode (m = 3) is bound by Akhiezer (f · Q = 6 · 1014 Hz) and bulk TED (f · Q = 1.2 · 1014 Hz), with a combined theoretical f · Q limit of 1 · 1014 Hz. The theoretical limit of SiC surpasses the intrinsic limits of Si, reached recently by Lamé resonators cooled down at 120 K (f · Q = 2 · 1013 Hz)9, revealing the benefits of on-axis 4H-SiC as a substrate for resonators with ultra-low dissipation.
The m = 3 elliptical modes implemented in on-axis 4H-SiCOI substrates are suitable candidates for integrated resonant gyroscopes, owing to the excellent isoelasticity of 4H-SiC21. Moreover, a polycrystalline silicon (polySi) plug is introduced to reduce any alignment inaccuracies between the SiC disk and the SiO2 pedestal to below 500 nm, preserving critical frequency and dissipation degeneracies of Coriolis-coupled modes5. Introducing an n-doped polySi plug obviates directly wire bonding the SiC disk to electrically bias it, avoiding disk tilting and preserving QANCHOR, leaving surface TED as the dominant loss mechanism. The tessellation layout encompasses sufficient area to anchor the electrodes. Figure 1e shows a schematic of the electrically-transduced disk design. Since the presence of electrodes surrounding the SiC disk restricts SEM-based sidewall observations and accurate surface TED numerical simulations, optically-interrogated 100 m-thick SiC disks without electrodes and with relaxed fabrication constraints have been also designed, fabricated and tested (Fig. 1f). Hereinafter, SiC disks with electrodes are referred to as capacitive disks and disks without electrodes as optical disks. To observe the true color of surface TED loss, the optical disks operate the more forgiving m = 8 modes at 5.3 MHz (Fig. 1b).
Fabrication
As shown in the Design section, etching SiC trenches with nanoscale roughness is critical in fabricating SiC resonators with dissipation solely bound by Akhiezer damping and bulk TED. Unlike laser machining, dry etching using high-density plasma holds the promise of nanoscale precision micromachining of monocrystalline SiCOI wafers with vertical and smooth sidewall profiles. The main challenge in SiCOI DRIE stems from the chemical inertness of SiC which mandates elevated DC self-bias voltages to generate reasonable etch rates on the order of 300 to 700 nm/min22,23. Electroplated Ni is preferred as a hard mask for its 30 to 100:1 selectivity over SiC and for its smooth and vertical sidewall profiles via LIGA patterning which are prerequisites for SiC DRIE with nanoscale precision. Like other metal hard masks, Ni tends to sputter and generates microscale particles that fall into the SiC trenches, locally masking the etch and generating columnar etch defects known as micropillars24. The generation of micropillars is disastrous and is bypassed by etching sufficiently narrow trenches at low pressure levels and by flowing an optimized gas composition in the DRIE chamber. Figure 2a–f shows perforation-free solid 4H-SiC disks anchored upon acoustically-deaf Si handle layers with and without surrounding electrodes (see Supplementary Note 2 for fabrication details).
Characterization
The details of the apparatus to measure electrostatically-transduced SiC BAW disk resonators are given in the Methods section. Six SiC BAW capacitive disk resonators were fabricated in parallel on a quarter SiCOI wafer and individually tested. The Q-factors of the m = 3 modes in these SiC disks are consistently measured above 2 M. Figure 3a–c show the electrostatic measurements of an average capacitive SiC BAW disk resonator with ultra-low energy dissipation. The highest Q measured in a capacitive disk is 3.8 M. The m = 3 resonance frequency variations are within ±40 ppm across devices, demonstrating that the frequencies are remarkably robust to process variations. The average m = 3 frequency split is 26 ppm. The smallest measured as-born m = 3 frequency split is 13 ppm. These as-fabricated m = 3 frequency splits result from symmetry-breaking fabrication imperfections and confirm 4H-SiCOI substrates support degenerate Coriolis-coupled secondary elliptical modes in center-supported disk resonators. The 5.5 MHz radial mode is also measured with Qs approaching 750 k, lower than the m = 3 modes due to the resonance frequency laying outside the 1.5 MHz-wide PnC bandgap centered on 6.29 MHz. The mode-shape-specific electrode configuration and the relatively large 4.2 μm-wide transduction gap prevent the electrostatic measurement of other in-plane modes.
The details of the apparatus to measure optically-transduced SiC BAW disk resonators are given in the Methods section. The measurements of 4 mm-diameter optical SiC disk resonators reveal Q-factors as high as 18 M at 5.3 MHz for the m = 8 elliptical modes (Fig. 3d,e), close to the simulated surface TED limit as well as as-born m = 9 frequency splits as small as 3 ppm (Fig. 3f). These larger SiC BAW disk resonators exhibit an astonishing f · Q = 9.5 · 1013 Hz, which is approximately 5-fold over the absolute quantum limit of Si. Moreover, all the in-plane elliptical modes from 2 MHz to 7 MHz can be measured with this apparatus and compared with simulations. Figure 3e displays the effectiveness of the enhanced PnC for modes which satisfy the frequency requirements of the 2.5 D substrate-decoupling approach. Multiple modes exhibit Qs beyond 1 M; however, Qs beyond 10 M are achieved only by modes with frequencies in the PnC bandgap and quarter-wavelength matched with the Si handle layer. These measurements validate that quarter-wavelength-matching sets stringent requirements; the acoustic properties and the thickness of the Si handle layer set the optimal resonance frequency of SiC micromechanical resonators to exhibit ultra-low dissipation. For the first time, Qs beyond the reach of Si have been demonstrated in SiC micromechanical resonators. The extraordinary low intrinsic losses of monocrystalline SiC may be revealed and show its advantages in BAW resonators that are completely substrate-decoupled, operating in the deep adiabatic regime and possess deep sub-micron level roughness, breaking through the barriers in prior efforts on SiC resonators (Fig. 4).
Discussion
SiC is a promising material for integrated micromechanical resonators and resonant gyroscopes with ultra-low dissipation. The measurement results suggest centrally-supported and perforation-free 4H-SiC BAW disk resonators are ideally poised to support gyroscopic modes with ultra-high Q beyond the range available to Si. Measurements validate that the 2.5 D non-coplanar substrate decoupling approach is sensitive to frequency inaccuracies (see Supplementary Note 1). Modes with frequencies that do not fulfill the quarter-wavelength-matching requirements or that are not within the acoustic bandgap of the PnC consistently exhibit low Qs14, showing that both conditions must be met simultaneously to completely circumvent anchor loss in centrally-supported and perforation-free 4H-SiC BAW disk resonators with ultra-high Q-factors limited by quantum loss mechanisms. Extrapolation based on TED simulations and on measurements of both optical and capacitive disks reveal the gyroscopic m = 3 modes of the 6.29 MHz SiC BAW disk resonators may achieve Qs beyond 25 M if the sidewall roughness is trimmed from 2.5 µm to below 500 nm. Achieving even higher Qs to enable navigation-grade SiC gyroscopes will require pushing the m = 3 modes further in the adiabatic regime. For example, the Q-factor of an m = 3 mode at 2.5 MHz will be surface TED limited to 100 M assuming 500 nm-wide striations.
Akin to (100) Si, n-doped monocrystalline on-axis 4H-SiC substrates support degenerate BAW gyroscopic m = 3 modes in disk resonators. As demonstrated in this paper, the m = 3 elliptical modes implemented in 4H-SiC exhibit both ultra-high Qs near 3.8 M and low as-born frequency splits Δf/f near 13 ppm. The measurement of higher Qs beyond 18 M and smaller frequency splits near 3 ppm in optically-interrogated disks suggest SiC resonant BAW gyroscopes may demonstrate sensitivities unknown to their (100) Si counterparts. Bulk micromachining with nanoscale precision is a critical step in demonstrating SiC gyroscopes with ultra-low dissipation. Etching SiC trenches with nanoscale smoothness is required both to implement advanced deep reactive ion etching processes compatible with a modified version of the HARPSS process but also to reach the Akhiezer limit of SiC and take the full advantage of the material capability. Advanced bulk micromachining processing often involve high temperature steps to anneal, oxidize or deposit materials such as polySi (see Supplementary Note 2). The CTE-mismatch between SiC and Si limit the thermal budget; temperatures greater than 900 °C warp the SiCOI substrates, making these additional processing steps challenging to implement. Current efforts aim to reduce the thermal budget of these processing steps or to manufacture SiC-on-SiC substrates, free of CTE-mismatch issues. With evidence of ultra-high Q-factors exceeding 18 M, electrostatic transduction, and as-fabricated frequency splits as low as 3 ppm, 4H-SiC is a promising substrate for robust BAW gyroscopes with ultra-high sensitivity and stability for high-end industrial and navigation applications.
Methods
Test apparatus to measure electrostatically-transduced and centrally-supported SiC BAW disk resonators
A schematic of the test apparatus is shown in Fig. 1e. The capacitive SiC BAW disk resonators are wire bonded to a simple PCB board with transimpedance amplifiers (TIAs) and placed in a vacuum chamber with Torr levels pressure. Due to the high stiffness of BAW modes, air damping is negligible below 100 mTorr, a pressure range greatly exceeding our pressure set-point. After 30 minutes of settling time to allow the device and PCB board to reach thermal equilibrium, the resonators are biased at 25Vp and their frequency characteristics are recorded with a network analyzer that is calibrated to remove feedthrough. There are 12 electrodes that surround the SiC disks: 3 pairs of electrodes, coinciding with the maximum deformation of one of the m = 3 modes are used to actuate and readout the motion of that mode, while the remaining 3 pairs are used to drive and sense the other m = 3 mode with a mode shape orthogonal to the first m = 3 mode.
The characteristics of electrostatically-transduced disks are as follow: SiC device layer thickness: 55 μm, Si handle layer thickness: 380 μm, disk diameter: 1440 μm, pedestal diameter to disk diameter ratio: near 5%, BOX thickness: 6 μm, transduction gap width: 4.2 μm, maximum surface roughness: 1–2 μm, mode of interest: m = 3 in-plane elliptical modes, resonance frequency: 6.29 MHz, maximum Q: 3.8 M corresponding to f · Q = 2.4 · 1013 Hz, minimum frequency split Δf/f: 13 ppm.
Test apparatus to measure optically-transduced and centrally-supported SiC BAW disk resonators
A schematic of the test apparatus is shown in Fig. 1f. The die containing the optically-transduced 4 mm wide SiC BAW disk resonators is glued with crystal bond to a 5 MHz shear piezoelectric actuator from Boston Piezo-Optics® and is placed in a vacuum chamber with optical and electrical access. The die is glued to a 5 MHz piezoelectric shear actuator to facilitate the transfer of energy from the actuator to the die. A firm and practically permanent adhesion is mandated by the 5 MHz resonance frequency. The piezoelectric actuators are controlled by an Agilent Network® analyzer via an RF amplifier. The motion of the disks is sensed by a 1D laser Doppler vibrometer (LDV) from Polytec® using a 20X magnification lens. The LDV is placed on an xyz stage with micrometric control to precisely align the laser head with the sidewall of the SiC disk. The glass window allowing for optical access is optically-rated to minimize absorption at the laser’s wavelength (633 nm). Further, the direction of the LDV head is about 5° off the normal direction of the glass window to prevent receiving undesirable reflected light.
The characteristics of optically-interrogated SiC BAW disks are as follow: SiC device layer thickness: 100 μm, Si handle layer thickness: 450 µm, disk diameter: 4 mm, pedestal diameter to disk diameter ratio: 5%, BOX thickness: 4 μm, maximum surface roughness: 500 nm, mode of interest: m = 8 and m = 9 in-plane elliptical modes, resonance frequency: 5.3 MHz, maximum Q: 18 M corresponding to f · Q = 9.5 · 1013 Hz, minimum frequency split Δf/f: 3 ppm for the m = 9 mode.
References
Wen, H. et al. A high-performance single-chip timing and inertial measurement unit with robust mode-matched gyroscopes. Proc. IEEE Int. Conf. Micro Electro Mech. Syst. 105–108, https://doi.org/10.1109/MEMSYS.2018.8346494 (2018).
Ayazi, F. Multi-DOF inertial MEMS: From gaming to dead reckoning. 16th Int. Solid-State Sensors, Actuators Microsystems Conf. TRANSDUCERS’11 2805–2808, https://doi.org/10.1109/TRANSDUCERS.2011.5969885 (2011).
Ayazi, F., Sorenson, L. & Tabrizian, R. Energy dissipation in micromechanical resonators. Proc. SPIE Micro- Nanotechnol. Sensors, Syst. Appl. III 8031, 803119, https://doi.org/10.1117/12.884731 (2011).
Braginsky, V., Mitrofanov, V., Panov, V. & Krotkov, R. Systems with Small Dissipation. Am. J. Phys. 55, 1153–1154, https://doi.org/10.1119/1.15272 (2005).
Serrano, D. E. et al. Substrate-decoupled, bulk-acoustic wave gyroscopes: Design and evaluation of next-generation environmentally robust devices. Microsystems Nanoeng. 2, 16015, https://doi.org/10.1038/micronano.2016.15 (2016).
Wen, H., Daruwalla, A. & Ayazi, F. Resonant pitch and roll silicon gyroscopes with sub-micron-gap slanted electrodes: Breaking the barrier toward high-performance monolithic inertial measurement units. Microsystems Nanoeng. 3, 16092, https://doi.org/10.1038/micronano.2016.92 (2017).
Mirjalili, R., Wen, H., Serrano, D. E. & Ayazi, F. Substrate-decoupled silicon disk resonators having degenerate gyroscopic modes with Q in excess of 1-million. 18th Int. Conf. Solid-State Sensors, Actuators Microsystems, TRANSDUCERS 2015 15–18, https://doi.org/10.1109/TRANSDUCERS.2015.7180849 (2015).
Daruwalla, A., Wen, H., Mirjalili, R. & Ayazi, F. Epitaxially-grown thick polysilicon for BAW disk resonator gyroscopes with very low dissipation. Proc. IEEE Int. Conf. Micro Electro Mech. Syst. 1008–1011, https://doi.org/10.1109/MEMSYS.2018.8346729 (2018).
Rodriguez, J. et al. Direct Detection of Akhiezer Damping in a Silicon MEMS Resonator. Sci. Rep. 9, 2244–2253, https://doi.org/10.1038/s41598-019-38847-6 (2019).
Abdolvand, R., Ho, G. K., Butler, J. & Ayazi, F. ZNO-on-nanocrystalline diamond lateral bulk acoustic resonators. 795–798, https://doi.org/10.1109/memsys.2007.4433131 (2008).
Tsaturyan, Y., Barg, A., Polzik, E. S. & Schliesser, A. Ultracoherent nanomechanical resonators via soft clamping and dissipation dilution. Nat. Nanotechnol. 12, 776–783, https://doi.org/10.1038/nnano.2017.101 (2017).
Ghaffari, S. et al. Quantum limit of quality factor in silicon micro and nano mechanical resonators. Sci. Rep. 3, 3244, https://doi.org/10.1038/srep03244 (2013).
Neudeck, P. G., Spry, D. J., Chen, L., Prokop, N. F. & Krasowski, M. J. Demonstration of 4H-SiC Digital Integrated Circuits above 800 °C. IEEE Electron Device Lett. 38, 1082–1085, https://doi.org/10.1109/LED.2017.2719280 (2017).
Yang, J., Hamelin, B., Ko, S. & Ayazi, F. Ultra-High Q Monocrystalline Silicon Carbide disk Resonators Anchored Upon a Phononic Crystal. In 2018 Solid State Sensor, Actuator Microsystems Work, 83–86, https://doi.org/10.31438/trf.hh2018.22 (2018).
Yasumura, K. Y. et al. Quality factors in micron- and submicron-thick cantilevers. J. Microelectromechanical Syst. 9, 117–125, https://doi.org/10.1109/84.825786 (2000).
Hamelin, B., Tavassoli, V. & Ayazi, F. Microscale pierced shallow shell resonators: A test vehicle to study surface loss. In Proc. IEEE Int. Conf. Micro Electro Mech. Syst., https://doi.org/10.1109/MEMSYS.2017.7863614 (2017).
Ko, S.-D., Hamelin, B., Yang, J. & Ayazi, F. High-Q monocrystalline silicon carbide disk resonators fabricated using DRIE of thick SiC-on-insulator substrates. In Proc. IEEE Int. Conf. Micro Electro Mech. Syst., https://doi.org/10.1109/MEMSYS.2018.8346726 (2018).
Maldovan, M. Sound and heat revolutions in phononics. Nature 503, 209–217, https://doi.org/10.1038/nature12608 (2013).
Chandorkar, S. A. et al. Multimode thermoelastic dissipation. J. Appl. Phys. 105, https://doi.org/10.1063/1.3072682 (2009).
Sorenson, L., Shao, P. & Ayazi, F. Bulk and surface thermoelastic dissipation in micro-hemispherical shell resonators. J. Microelectromechanical Syst. 24, 486–502, https://doi.org/10.1109/JMEMS.2014.2333528 (2015).
Cook, E. et al. A High-Mass, Eight-Fold Symmetric Silicon Carbide MEMS Gyroscope. In 2018 Solid State Sensor, Actuator Microsystems Work, 364–365, https://doi.org/10.31438/trf.hh2018.102 (2018).
Luna, L. et al. SiC Wafer Bonding and Deep Reactive Ion Etching Towards High-Aspect Ratio SiC MEMS Fabrication. ECS Trans. 86, 105–110, https://doi.org/10.1149/08605.0105ecst (2018).
Dowling, K. M., Ransom, E. H. & Senesky, D. G. Profile evolution of high aspect ratio silicon carbide trenches by inductive coupled plasma etching. J. Microelectromechanical Syst. 26, 135–142, https://doi.org/10.1109/JMEMS.2016.2621131 (2017).
Kuah, S. H. & Wood, P. C. Inductively coupled plasma etching of poly-SiC in SF6 chemistries. J. Vac. Sci. Technol. A Vacuum, Surfaces, Film. 23, 947–952, https://doi.org/10.1116/1.1913682 (2005).
Kermany, A. R. et al. Microresonators with Q-factors over a million from highly stressed epitaxial silicon carbide on silicon. Appl. Phys. Lett. 104, https://doi.org/10.1063/1.4866268 (2014).
Wang, Z., Lee, J. & Feng, P. X. Spatial mapping of multimode Brownian motions in high-frequency silicon carbide microdisk resonators. Nat. Commun. 5, 5158–5168, https://doi.org/10.1038/ncomms6158 (2014).
Ziaei-Moayyed, M., Habermehl, S. D., Branch, D. W., Clews, P. J. & Olsson, R. H. Silicon carbide lateral overtone bulk acoustic resonator with ultrahigh quality factor. In Proc. IEEE Int. Conf. Micro Electro Mech. Syst., 788–792, https://doi.org/10.1109/MEMSYS.2011.5734543 (IEEE, 2011).
Lu, X., Lee, J. Y. & Lin, Q. High-frequency and high-quality silicon carbide optomechanical microresonators. Sci. Rep. 5, 17005, https://doi.org/10.1038/srep17005 (2015).
Acknowledgements
This work is supported by the Defense Advanced Research Projects Agency Microsystems Technology Office, Advanced Inertial Micro Sensors (AIMS) program and U.S. Navy (SPAWAR) under grant N66001-16-1-4027. This work was performed in part at the Georgia Tech Institute for Electronics and Nanotechnology (IEN), a member of the National Nanotechnology Coordinated Infrastructure (NNCI), which is supported by the National Science Foundation (ECCS-1542174). The authors thank the cleanroom staff at IEN, Georgia Institute of Technology for their assistance and Dr. Mohammad J. Moghimi for valuable discussions.
Author information
Authors and Affiliations
Contributions
B.H. developed the key fabrication steps. B.H. and J.Y. conceived the design. B.H., J.Y., A.D. and H.W. analyzed test results. F.A., principal investigator, conceived the study and coordinated the experiments. All authors reviewed the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Hamelin, B., Yang, J., Daruwalla, A. et al. Monocrystalline Silicon Carbide Disk Resonators on Phononic Crystals with Ultra-Low Dissipation Bulk Acoustic Wave Modes. Sci Rep 9, 18698 (2019). https://doi.org/10.1038/s41598-019-54278-9
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-019-54278-9
- Springer Nature Limited
This article is cited by
-
4H silicon carbide bulk acoustic wave gyroscope with ultra-high Q-factor for on-chip inertial navigation
Communications Engineering (2024)
-
Electrochemical etching strategy for shaping monolithic 3D structures from 4H-SiC wafers
Scientific Reports (2023)
-
Spin-acoustic control of silicon vacancies in 4H silicon carbide
Nature Electronics (2023)
-
A novel progressive wave gyroscope based on acousto-optic effects
Microsystems & Nanoengineering (2022)