Abstract
Lightweight sheet alloys with superior mechanical performance such as high strength, ductility and formability at room temperature (RT) are desirable for high volume automotive applications. However, ductility or formability of metallic alloys at RT are generally inversely related to strength, thereby making it difficult to optimize all three simultaneously. Here we design a new magnesium sheet alloy-ZAXME11100 (Mg-1.0Zn-1.0Al-0.5Ca-0.4Mn-0.2Ce, wt. pct.) via CALPHAD (CALculation of PHAse Diagram) modeling and experimental validation. This new sheet alloy offers an excellent RT formability with a high Index Erichsen (I.E.) value of 7.8 mm in a solution-treated condition (T4), due to its weak and split basal texture and fine grain structure. The new ZAXME 11100 alloy also shows a rapid age-hardening response during post-forming artificial aging treatment at 210 °C for 1 hour (T6), resulting in a significant increase of yield strength from 159 MPa (T4) to 270 MPa (T6). The excellent combination of T4 ductility (31%), T4 formability (7.8 mm) and T6 yield strength (270 MPa) in this new magnesium alloy is comparable to that of common 6xxx series aluminum sheet alloys. Thus, this new magnesium sheet alloy is highly attractive for sheet applications in automotive and other industries.
Similar content being viewed by others
Introduction
Steels and 6xxx series aluminum (Al-Mg-Si) alloys are mostly used for automotive body panels due to their excellent formability and subsequent bake hardenability1,2. In order to meet the ever-increasing demand for vehicle weight reduction, the use of lighter structural materials has become inevitable in the automotive industry. Magnesium (Mg), the lightest structural metal, has thus attracted considerable attention for applications in automotive and other transportation industries3,4. However, compared to 6xxx series aluminum alloys5,6 or steels7, inferior mechanical properties at RT and high processing cost limit wider applications of commercial Mg sheet alloys such as AZ31 (Mg-3Al-1Zn-0.3Mn) and ZE10 (Mg-1Zn-0.2Ce)8,9. This is the well-known issue of the “strength-formability trade-off dilemma” in Mg and other sheet alloys. Thus, it is of great importance to challenge this dilemma and develop a low-cost Mg alloy with both high tensile properties and RT formability.
Magnesium sheet alloys generally have better formability in solution-treated conditions if their annealed texture is weakened; however, they would exhibit low yield strength due to the recovery and recrystallization of their plastically deformed microstructures10. Until recently, only a limited number of solution-treated Mg sheet alloys can be substantially strengthened via a bake-hardening treatment (2% pre-strain and aging for 20 min at 170 °C11). Such strengthening is attributed to the segregation of solutes to dislocations, as well as the formation of co-clusters of solutes11,12 during baking. However, no research has been reported for developing good RT-formable Mg sheet alloys which may be strengthened rapidly and substantially via a low-cost artificial aging treatment rather than via a bake-hardening treatment. The development of heat-treatable Mg sheet alloys with excellent RT-formability and subsequently rapid age-hardenability is therefore a promising approach to overcome the strength and formability trade-off dilemma13. The Mg-Al-Zn-Mn-Ca system11,12,14 is a promising alloy system to overcome this strength-formability trade-off. Also, trace additions of rare-earth elements like yttrium (Y), neodymium (Nd) and cerium (Ce) can significantly modify the texture and refine grain size to enhance the ductility and formability of wrought Mg alloys. The improvement could be attributed to decreasing the intrinsic stacking fault energy (I1 SFE)15 to generate <c + a> dislocations, decreasing critical resolved shear stress (CRSS) of pyramidal <c + a > slip16, or providing the randomized texture17. Thus, the Mg-Zn-Al-Ca-Mn-Ce system is studied with a trace addition of Ce in this work, based on our earlier work18.
Extensive research has been reported on discovering mechanical behaviors and improving alloy performance via optimizing alloy composition and thermomechanical processing (TMP)18,19,20,21,22,23. CALPHAD (CALculation of Phase Diagrams) modeling24,25,26,27, as a part of Integrated Computational Materials Engineering (ICME)28 framework, has been successfully applied to study the alloying-processing-structure-property relationships in multicomponent alloy systems. Therefore, CALPHAD simulation is used to design a new Mg-1Zn-1Al-0.5Ca-0.4Mn-0.2Ce alloy (hereafter designed as ZAXME11100) and its optimal TMP to obtain more balanced strength, ductility and formability in this study. TMP (including homogenization, rolling and annealing) is critically important in optimizing the alloying effects for the final mechanical properties of the alloy. For example, conventional homogenization process (at below solidus temperature of the alloy to avoid incipient melting) is inefficient in dissolving second phases from the as-cast microstructure and maximizing the solute concentrations in the Mg matrix, thus achieving the overall alloying effects.
In this paper, CALPHAD simulation is used to design a new homogenization process (with multiple isothermal stages including final stages at temperatures higher than the alloy solidus18) for the new alloy, achieving maximum dissolution of alloying elements without incipient melting. The combination of the new alloy design and the multi-stage TMP process leads to the optimum combination of strength, ductility and formability of the new alloy.
Results and discussions
CALPHAD software Thermo-Calc and TCMG5 and MOBMG1 databases29 was used to perform the thermodynamic and kinetic modeling of ZAXME11100 alloy. Figure 1(a) shows the solidification path of ZAXME11100 alloy using the classical Scheil model, and an enlarged region near the end of solidification is shown in Fig. 1(b). The results show that HCP (hexagonal closed packed) Mg phase will form as a primary phase at 638 °C, followed by the formation of Al8Mn5, Mg12Ce, Al2Ca, Ca2Mg5Zn5, Ce2Mg53Zn45, Al11Mn4 and Ca2Mg5Zn13 phases at 628 °C, 546 °C, 488 °C, 368 °C, 357 °C, 329 °C and 325 °C, respectively. Figure 1(c) is the equilibrium phase fraction vs. temperature calculation for ZAXME11100 alloy, and the solidus temperature of ZAXME11100 alloy is shown as 450 °C. The calculated formation temperatures of Al8Mn5 and Mg12Ce are 632 °C and 548 °C, respectively, in Fig. 1(c), which are slightly higher than those (628 °C and 546 °C, respectively) of the same phases during cooling (solidification) in Fig. 1(a,b). Similarly, the formation of Al2Ca, Ca2Mg5Zn5 and Al11Mn4 is at 430 °C, 172 °C, and 208 °C, respectively, which is considerably lower than their temperatures (488 °C, 368 °C, and 329 °C) of formation during solidification in Fig. 1(a,b). On the other hand, Ce2Mg53Zn45 and Ca2Mg5Zn13 phases formed during solidification in Fig. 1(b) are not shown in the equilibrium calculation in Fig. 1(c), thus they are assumed to be metastable phases.
Based on these results, a new homogenization profile (designated as H480, thereafter) was designed with four isothermal stages (320 °C for 4 h, 360 °C for 4 h, 440 °C for 52 h and 480 °C for 1 h) to sequentially dissolve the intermetallic phases while avoiding incipient melting. The first stage was designed as 320 °C between the formation temperatures of stable phases (Ca2Mg5Zn5 at 172 °C; and Al11Mn4 at 208 °C) in Fig. 1(c) and the solidified phases (Ca2Mg5Zn5 at 368 °C; and Al11Mn4 at 329 °C) in Fig. 1(b), to initially dissolve the stable phases (Ca2Mg5Zn5 and Al11Mn4) and the metastable phases (Ce2Mg53Zn45 and Ca2Mg5Zn13). The second stage was done at 360 °C for 4 h to further dissolve the phases with higher melting temperatures, such as Ca2Mg5Zn5 phase (368 °C) in Fig. 1(b) and also reduce the micro-segregation of alloying elements.
The third stage was carried out at 440 °C for 52 h between the formation temperature of Al2Ca (430 °C) in Fig. 1(c) and (488 °C) in Fig. 1(b), to dissolve Al2Ca phase and further homogenize the alloying elements. Figure 1(c) shows a small fraction of liquid at temperatures above the solidus 450 °C. Also, a new phase AlCaMg would possibly form during this stage since it is thermodynamically stable between 430 °C and 478 °C in Fig. 1(c). Thus, the fourth stage was chosen as 480 °C for 1 h to dissolve AlCaMg and potentially Mg12Ce and Al8Mn5 phases with higher thermal stability up to 548 °C and 632 °C, respectively. However, the liquid phase was not experimentally observed during the fourth stage (480 °C, 1 h). The reason could be: (1) the homogenization time was not long enough for the liquid phase to form; or (2) the amount of the liquid phase formed was too small (<~1%, 480 °C in Fig. 1(c)). Thus, the multi-stage homogenization profile (H480) and rolling process (R450) used in producing the ZAXME 11100 alloy sheet are summarized in Fig. 1(d).
Diffusion-controlled distribution of solutes Al, Zn, Ca, Ce and Mn in Mg matrix was studied using DICTRA29 simulation, and Fig. 2(a) plots the calculated solute distributions in both the as-cast (AC) condition and the new H480-homogenized condition. The results demonstrate that the new multi-stage treatment is very effective in dissolving solute elements in Mg grain interiors. Figure 2(b) shows that the diffusion coefficients of Al, Zn, Ca, Mn and Ce solutes in ZAXME11100 alloy are exponentially related to temperature. For example, the diffusion coefficients of the solutes at 480 °C are about 10 times higher than those at 400 °C close to the solidus temperature (450 °C), suggesting that significantly faster homogenization is possible at 480 °C compared to 400 °C (which is below the 450 °C solidus temperature). It is also noted that Al and Mn have the lowest diffusion coefficients among all alloying elements in Mg, which also explains that Al8Mn5 is the most difficult phase to be dissolved during solution treatment.
Microstructures of ZAXME11100 alloy after as-cast condition and the new homogenization treatment (H480) were observed via optical microscopy and shown in Fig. 2(c,d), respectively. The results showed that the second phase particles near and along the grain boundaries have been essentially dissolved after the new homogenization profile (H480). However, a small amount of residual particles, mostly Al8Mn5 and a very few Al2Ca as identified in TEM, are still visible in Fig. 2(d).
The new Mg alloy solutionized at H480 heat treatment has been rolled following the designed rolling process (R450) in Fig. 1(d). The grain size of microstructure from as-cast (AC), H480 and as-rolled (AR) conditions is shown in Fig. 3. It should be noted that (1) the grain size at H480 solution treatment has slightly grown to 312.3 μm, which could be attributed to the inhibition of thermally stable Al8Mn5 and Al2Ca particles formed during the solidification; and (2) the grain size has been significantly decreased to 4.7 μm at as-rolled condition due to recrystallization of the deformed microstructure.
The EBSD inverse pole figure (IPF) map overlaid by large angle grain boundaries with misorientation angles larger than 15 degrees in Fig. 4(a) shows the microstructure of ZAXME11100 alloy after rolling process (R450) followed by the post-forming solution treatment (T4) and water quenching from Fig. 1(d). The average grain size of ZAXME11100 alloy determined via EBSD is about 9.6 μm. It can be seen that the combination of rolling (R450) with the post-forming solution-treatment (T4) yields significant grain refinement in ZAXME11100 alloy. The texture pole figures of solution-treated (T4) microstructure are shown in Fig. 4(b). The microstructure has a weak split basal texture with a maximum intensity of 3.3 mrd. The maximum intensity of basal poles is also tilted by about ±40 degrees away from the normal direction (ND) and toward the transverse direction (TD). Such fine grain size and weakened texture of solution-treated (T4) ZAXME11100 sheet alloy contribute to both high ductility and formability11,14.
The high-angle annular dark-field (HAADF) STEM image in Fig. 5(a) shows a high density of intermetallic particles in the post-forming T4 microstructure. STEM energy dispersive spectroscopy (EDS) elemental maps were collected from the region showing in Fig. 5(a). The STEM-EDS elemental maps in Fig. 5(b–f) show that the nano-scale rod precipitates are enriched with Al and Mn elements. Elements Zn, Ca and Ce (not shown in Fig. 5 due to small amount) are homogeneously distributed in the grain interior, suggesting that those alloying elements are dissolved in Mg matrix, hypothesized to form solute co-clusters11,12 during subsequent aging heat treatments and thereby contribute to strengthening of the ZAXME11100 alloy.
Bright-field (BF) STEM image in Fig. 6(a) reveals that the T4 microstructure consists of a high density of uniformly distributed nano-size rod precipitates randomly distributed both within grain interior and at grain boundaries. Bright field (BF) TEM image with an inset selected diffraction patter in Fig. 6(b) shows that the rod precipitates are Al8Mn5 phase. As shown in Fig. 1(b,c), Al8Mn5 starts to form at 628 °C during solidification and melt at 632 °C under the post-heat treatment. It cannot be dissolved during solution treatment at 480 °C. Therefore, Al8Mn5 can retard grain growth through Zener pinning during annealing at 480 °C, thus contributing to grain refinement. High density and uniformly distributed Al8Mn5 phase also contribute to the strength of T4 microstructure.
Figure 7(a) shows the variation in the Vickers hardness of solution-treated (T4) ZAXME11100 sheet alloy under the artificial aging at 210 °C. The ZAXME11100 sheet alloy has a hardness value of 56.0 ± 2.1 HV in the solution treated condition (T4) from Fig. 1(d) and exhibits a rapid age-hardening to a peak hardness of 70.8 ± 1.5 HV for 1 h. The tensile curves obtained from solution-treated (T4) and peak-aged (T6) samples are shown in Fig. 7(b). The mechanical properties of these samples are summarized in Table 1. The T4 treated ZAXME11100 sheet alloy exhibits a moderate yield strength (Y.S.) of 159 MPa and an ultimate tensile strength (U.T.S.) of 253 MPa with an extraordinarily high elongation of 31% and Index Erichsen (I.E.) value of 7.8 mm. After the T6 heat-treatment, the yield strength (Y.S.) and ultimate tensile strength (U.T.S.) have been significantly improved to 270 MPa and 332 MPa with a high elongation of 26%. Figure 7(c,d), respectively, summary the engineering stress as a function of I.E. values as well as engineering strain for various Mg8,11,12,14,30,31,32,33,34 and Al35,36 sheet alloys. As can been seen, the ZAXME11100 sheet alloy shows good stretch formability in T4 condition, which is close to that reported for 6000 series Al alloy35,36. Subsequently the artificial aging (T6) treatment substantially increases the engineering stress with less reduction of ductility, enabling this alloy to have a well-balanced high strength, ductility and formability at room temperature.
The preliminary STEM imaging in Fig. 8(a,b) for the T6 microstructure of ZAXME11100 alloy did not reveal the formation of crystalline precipitate phases, except for the nano-size Al8Mn5 rods which were seen previously in the solution-treated samples (Fig. 6). This suggests that solutes Al and Mn have the strongest affinity in the ZAXME11100 alloy and that other solutes may not have enough strong affinity to form crystalline phases during aging. Figure 8(c) shows the enthalpy of mixing values of various atomic pairs in the ZAXME11100 system. The calculated result shows that the enthalpies of mixing of Al-Mn (−23289.8 J/mol), Al-Zn-Ca-Mn (−15520 J/mol), Al-Ca-Mn (−15523.8 J/mol), Al-Ce-Mn (−15519.2 J/mol), Al-Zn-Mn (−15527.5 J/mol), and Mg-Al-Mn (−15521.2 J/mol) pairs are significantly negative. Therefore, thermodynamically, there is a strong affinity between the corresponding solutes to form solute clusters or crystalline phases. It should be noted that the Al-Mn pair has the most negative enthalpy of mixing, suggesting that solute pair Al and Mn has a much stronger affinity than other solute pairs, and therefore is most likely to form crystalline precipitates.
Based on results from Fig. 8(a–c), the Al-Mn atomic pair with strongest affinity would form crystalline Al8Mn5 phase. Other atomic pairs with negative mixing enthalpies may form some clusters11,12 without forming distinct observable precipitates during the ageing treatment. Further characterization work is on-going to investigate the strengthening mechanism involved in T6 treatment. Therefore, the significant enhancement of engineering strength after T6 treatment would be attributed to the formation of solute clusters11,12 in Fig. 8(d), which should provide a string pinning effect on the basal <a> dislocations. These dislocations need a larger force to break away from the solute atmosphere after aging (T6). Therefore, the combination of designing new alloy and optimizing TMP with CALPHAD methodology has led to a heat-treatable magnesium sheet alloy (ZAXME11100) with excellent RT-formability and high strength, which has overcome the well-known strength-formability dilemma.
Conclusions
In summary, a new Mg sheet alloy (ZAXME11100: Mg-1Zn-1Al-0.5Ca-0.4Mn-0.2Ce) and a novel thermomechanical process have been developed based on CALPHAD and diffusion modeling in combination with experimental investigation. The new Mg sheet alloy produced via low-cost rolling followed by a multi-stage solution treatment (T4) and conventional aging treatment (T6) has a superior combination of high strength (270 MPa in T6), ductility (31% in T4) and formability (Erichsen Index of 7.8 mm in T4) at room temperature. Microstructure characterization and thermodynamic/kinetic calculations suggest that the following factors contribute to the excellent properties: (1) weak and split basal texture; (2) fine grain structure (average 9.6 μm); and (3) possible formation of solute clusters after a short-time aging treatment (T6) due to the negative mixing enthalpy of various solute pairs. The new ZAXME11100 sheet alloy has successfully overcome the common trade-off relationship between formability/ductility and strength, promising high-volume automotive applications of magnesium sheet components.
Materials and methods
Magnesium sheet alloy preparation method was reported in a previous publication18. Mg-1Zn-1Al-0.5Ca-0.4Mn-0.2Ce (ZAXME11100) alloy was prepared in a steel crucible under a protective gas mixture of CO2 and SF6, then cast at 750 °C into a steel mold pre-heated to 400 °C to produce 110 × 114 × 18 mm plates. The cast plates were machined into 20 × 28 × 7 mm samples which were homogenized (multi-stage H480) and water-quenched. The homogenized samples were cold-rolled initially to ~3 mm with about 0.25 to 0.5 mm thickness reduction per pass, and then rolled to ~1 mm with 30% thickness reduction per pass. Except for the final rolling pass, the samples were pre-heated at 450 °C for 5 min prior to each pass. Longitudinal tensile samples with a gauge length of 12.5 mm, a width of 5 mm, and a thickness of 1 mm were machined from the as-rolled sheets. Some as-rolled tensile samples were solution-treated at 480 °C for 1 h (T4) followed by water-quenching and then artificial aging at 210 °C for 100 hours in an oil bath. Age hardening responses of the solution-treated samples were measured using a Vickers hardness tester. Tensile tests were conducted at RT on the solution-treated (T4) and peak-aged (T6) samples at a strain rate of 1.8 × 10−4 s−1. At least three specimens were tested at RT for each temper condition to ensure repeatability. To evaluate the stretch formability of the solution-treated (T4) sheets, Erichsen cupping tests were performed at RT on 60 × 60 mm rectangular samples with a thickness of 1 mm using an Erichsen sheet metal testing machine with a 20 mm diameter hemispherical punch. The punch speed and blank-clamping force were around 6 mm/min and 10 kN, respectively. Graphite lubrication was used on the tool.
The microstructure of the new alloy was characterized using optical microscopy, scanning electron microscopy (SEM), transmission electron microscopy (TEM) and scanning transmission electron microscopy (STEM). The SEM study and electron backscatter diffraction (EBSD) mapping were conducted using a FEI Apreo SEM equipped with a EDAX OIM system. Specimens for TEM analysis were mechanically ground to ~40 μm using a Fischione model 100 dimpler. Perforation of thin TEM foils were conducted in a Fischione model 1010 ion mill operating at a voltage of 5 keV. TEM and STEM investigations were carried out on a FEI Tecnai F20 TEM/STEM microscope operating at 200 kV. STEM-EDS elemental maps were collected using a FEI G2 60-300 TEM/STEM microscope equipped with a Super-X/ChemiSTEM) EDS system operating at 300 kV.
References
Baker, L. J., Daniel, S. R. & Parker, J. D. Metallurgy and processing of ultralow carbon bake hardening steels. Mater. Sci. Technol. 18, 355–368 (2002).
Birol, Y. Pre-aging to improve bake hardening in a twin-roll cast Al-Mg-Si alloy. Mater. Sci. Eng. A. 391, 175–180 (2005).
Pollock, T. M. Weight loss with magnesium alloys. Science. 328, 986–987 (2010).
Lu, K. The future of metals. Science. 328, 319–320 (2010).
Chino, Y., Sassa, K. & Mabuchi, M. Tensile properties and stretch formability of Mg-1.5 mass%- 0.2 mass% Ce sheet rolled at 723 K. Mater. Trans. 49, 1710–1712 (2008).
Chino, Y., Huang, X., Suzuki, K. & Mabuchi, M. Enhancement of stretch formability at room temperature by addition of Ca in Mg-Zn alloy. Mater. Trans. 51, 818–821 (2010).
Jiang, S. et al. Ultrastrong steel via minimal lattice misfit and high-density nanoprecipitation. Nature. 544, 460–464 (2017).
Suh, B. C., Shim, M. S., Shin, K. S. & Kim, N. J. Current issues in magnesium sheet alloys: where do we go from here? Scr. Mater. 84-85, 1–6 (2014).
Joost, W. J. & Krajewski, P. E. Towards magnesium alloys for high-volume automotive applications. Scr. Mater. 128, 107–112 (2017).
Chino, Y. et al. Influence of Zn concentration on stretch formability at room temperature of Mg-Zn-Ce alloy. Mater. Sci. Eng. A. 528, 566–572 (2010).
Bian, M. Z. et al. Bake-hardenable Mg-Al-Zn-Mn-Ca sheet alloy processed by twin-roll casting. Acta Mater. 158, 278–288 (2018).
Bian, M. Z. et al. A heat-treatable Mg-Al-Ca-Mn-Zn sheet alloy with good room temperature formability. Scr. Mater. 138, 151–155 (2017).
Hono, K., Mendis, C. L., Sasaki, T. T. & Oh-ishi, K. Towards the development of heat treatable high-strength wrought Mg alloys. Scr. Mater. 63, 710–715 (2010).
Trang, T. T. T. et al. Designing a magnesium alloy with high strength and high formability. Nat. Commun. 9, 2522 (2018).
Sandlo¨bes, S. et al. The relation between ductility and stacking fault energies in Mg and Mg–Y alloys. Acta Mater. 60, 3011–3021 (2012).
Liu, G. et al. Designing Mg alloys with high ductility: Reducing the strength discrepancies between soft deformation modes and hard deformation modes. Acta Mater. 141, 1–9 (2017).
Luo, A. A., Mishra, R. K. & Sachdev, A. K. High-ductility magnesium–zinc–cerium extrusion alloys. Scr. Mater. 64, 410–413 (2011).
Shi, R., Miao, J. & Luo, A. A. A new magnesium sheet alloy and its multi-stage homogenization for simultaneously improved ductility and strength at room temperature. Scr. Mater. 171, 92–97 (2019).
Shi, R., Zhu, Z. & Luo, A. A. Assessing phase equilibria and atomic mobility of intermetallic compounds in aluminum-magnesium alloy system. J. Alloys. Compd. 825, 153962 (2020).
Su, C. et al. Enhanced ductility in high-pressure die casting Mg-4Ce-xAl-0.5Mn alloys via modifying second phase. Mater. Sci. Eng. A. 773, 138870 (2020).
Shi, R., Meier, J. & Luo, A. A. Controlling particle/metal interactions in metal matrix composites during solidification: the role of melt viscosity and cooling rate. Metall. Mater. Trans. A. 50, 3736 (2019).
Mishra, A. et al. Theoretical Investigations on Structural Stability and Elastic Properties of MoNbTaW-X (=Ti/V) High Entropy Alloys. J. Mater. Sci. Res. and Rev. 4(2), 1–9 (2019).
Shi, R., Avey, T. & Luo, A. A. A CALPHAD (CALculation of PHAse Diagrams)-based viscosity model for Al-Ni-Fe-Co melt system. J. Mol. Liq. 291, 111271 (2019).
Shi, R., Chandra, D., Chien, W. & Wang, J. High-throughput thermodynamic computation and experimental study of solid-state phase transitions in organic multicomponent orientationally disordered phase change materials for thermal energy storage. CALPHAD. 64, 66–77 (2019).
Luo, A. A. Material design and development: From classical thermodynamics to CALPHAD and ICME approaches. CALPHAD. 50, 6–22 (2015).
Shi, R. & Luo, A. Applications of CALPHAD modeling and databases in advanced lightweight metallic materials. CALPHAD. 62, 1–17 (2018).
Shi, R. Applications of CALPHAD (CALculation of PHAse Diagram) modeling in organic orientationally disordered phase change materials for thermal energy storage. Thermochim. acta. 683, 178461 (2020).
Pollock, TM. et al. Integrated Computational Materials Engineering: A Transformational Discipline for Improved Competitiveness and National Security, The National Academies Press, 500 Fifth Street, N.W. Washington, DC 20001, 2008.
Huang, X. S., Suzuki, K., Chino, Y. & Mabuchi, M. Texture and stretch formability of AZ61 and AM60 magnesium alloy sheets processed by high-temperature rolling. J. Alloys. Compd. 632, 94–102 (2015).
Huang, X. S., Suzuki, K., Chino, Y. & Mabuchi, M. Influence of aluminum content on the texture and sheet formability of AM series magnesium alloys. Mater. Sci. Eng. A. 633, 144–153 (2015).
Bhattacharjeea, T. et al. High strength and formable Mg–6.2 Zn–0.5 Zr– 0.2Ca alloy sheet processed by twin roll casting. Mater. Sci. Eng. A. 609, 154–160 (2014).
Yuasa, M. et al. Effects of group II elements on the cold stretch formability of Mg–Zn alloys. Acta Mater. 83, 294–303 (2015).
Chino, Y., Huang, X. S. & Suzuki, K. J. Development of Room Temperature Formability of Rolled Magnesium Alloy Sheets by Texture Control. Jpn. Met. 81(2), 49–54 (2017).
Hirth, S. M., Marshall, G. J., Court, S. A. & Lloyd, D. J. Effects of Si on the aging behaviour and formability of aluminium alloys based on AA6016. Mater. Sci. Eng. A. 319–321, 452–456 (2001).
Ozturk, F., Esener, E., Toros, S. & Picu, C. R. Effects of aging parameters on formability of 6061-O alloy. Mater. Des. 31, 4847–4852 (2010).
Acknowledgements
The authors acknowledge Dr. Tracy D. Berman and Prof. John E. Allison of University of Michigan for conducting Erichsen cupping test, Randy Gerken of FiatChrysler, Bita Ghaffari of Ford Motor Company, Anil Sachdev and Jon Carter of General Motors and entire USAMP project team for many helpful discussions. This work is partially supported by the United States Automotive Materials Partnership (USAMP) and by the U.S. Department of Energy (DOE) National Energy Technology Laboratory under Award Number DE-EE0007756. This report was prepared as an account of work sponsored by an agency of the United States Government. Neither the United States Government nor any agency thereof, nor any of their employees, makes any warranty, express or implied, or assumes any legal liability or responsibility for the accuracy, completeness, or usefulness of any information, apparatus, product, or process disclosed, or represents that its use would not infringe privately owned rights. Reference herein to any specific commercial product, process, or service by trade name, trademark, manufacturer, or otherwise does not necessarily constitute or imply its endorsement, recommendation, or favoring by the United States Government or any agency thereof. The views and opinions of authors expressed herein do not necessarily state or reflect those of the United States Government or any agency thereof.
Author information
Authors and Affiliations
Contributions
A.A. Luo supervised the research in this paper. A.A. Luo and R. Shi conceived alloy design and TMP processing. R. Shi and T. Avey prepared materials by casting and TMP, examined the optical microstructure and mechanical properties. R. Shi performed CALPHAD/kinetic simulation. J. Miao characterized the microstructure via SEM, EBSD and TEM techniques. All authors analyzed, discussed the results, and then wrote the paper.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher’s note Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Shi, R., Miao, J., Avey, T. et al. A new magnesium sheet alloy with high tensile properties and room-temperature formability. Sci Rep 10, 10044 (2020). https://doi.org/10.1038/s41598-020-67161-9
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-020-67161-9
- Springer Nature Limited
This article is cited by
-
Sampling Procedure, Characterization, and Quantitative Analyses of Industrial Aluminum White Dross
Journal of Sustainable Metallurgy (2023)
-
Toward Development of Strong and Formable Magnesium Alloy Sheets with Bake-Hardenability
JOM (2021)