Abstract
We have studied current induced magnetization switching in W/CoFeB/MgO based three terminal magnetic tunnel junctions. The switching driven by spin—orbit torque (SOT) is evaluated in the so-called type-Y structure, in which the magnetic easy-axis of the CoFeB layer lies in the film plane and is orthogonal to the current flow. The effective spin Hall angle estimated from the bias field dependence of critical current (Ic) is ~ 0.07. The field and current dependence of the switching probability are studied. The field and DC current induced switching can be described using a model based on thermally assisted magnetization switching. In contrast, the 50 ns long pulse current dependence of the switching probability shows significant deviation from the model, even if contribution from the field-like torque is included. The deviation is particularly evident when the threshold switching current is larger. These results show that conventional thermally assisted magnetization switching model cannot be used to describe SOT induced switching using short current pulses.
Similar content being viewed by others
Introduction
The spin–orbit torque (SOT) magnetoresistive random access memory (MRAM) is one of the emerging technologies for next generation memory devices1, 2. In SOT-MRAM, current is passed along a channel made of a non-magnetic heavy metal (HM) layer on which a magnetic tunnel junction (MTJ) is placed. The current passed along the HM layer generates spin current via the spin Hall effect that diffuses into the ferromagnetic free layer of the MTJ. Such spin current exerts SOT3,4,5 on the free layer magnetization. With appropriate condition, the SOT can induce magnetization switching depending on the direction to which the current flows within the channel. As the current needed to write information (i.e. switch the magnetization) does not flow across the tunnel barrier, the three terminal SOT-MRAM is considered to possess larger endurance compared to the conventional two terminal STT-MRAM6.
The three terminal SOT-MRAM can be categorized into three types7 depending on the geometry of the MTJs and the SOT channel: type-X, Y, Z refers to, respectively, magnetic easy-axis of the free layer of the MTJ pointing along the current flow direction (type-X), orthogonal to the current flow direction but lies in the film plane (type-Y), and perpendicular to the film plane (type-Z). It is now well understood that the switching dynamics of the three types are different. While types-X and Z allow sub-nanosecond switching of the magnetization7,8,9, type-Y requires nanoseconds long incubation time to cause the switching4, 10, 11. On the other hand, magnetization can be controlled in type-Y12 without any magnetic field, whereas a dc bias magnetic field is needed during the current application process for types-X and Z. The switching scheme of type-Y is close to that of conventional STT-MRAM. As field-free switching schemes for types-X and Z devices are currently being developed, the most straightforward approach to replace STT-MRAM with SOT-MRAM is to use the type-Y device.
Here we study SOT induced magnetization switching probability of type-Y three terminal MTJ. We use tungsten (W) as the channel material and CoFeB/MgO/CoFeB as the base element of the MTJ. The switching probability with DC current and pulse current are investigated and compared to model calculations based on thermally assisted magnetization switching. We include the field-like torque in the model in an attempt to account for the experimental results.
Results and discussion
Device structure and magnetization switching by field and current
Figure 1a shows schematic illustration of the three terminal MTJ13 consisting of a W channel10, 14,15,16 and the elliptical MTJ pillar. The MTJ consists of MgO barrier sandwiched by a CoFeB free layer and a CoFeB-based synthetic-antiferromagnet (SAF) pinned layer. The thickness of the free layer is 2 nm. The coordinate axis is sketched in Fig. 1a. The short and long axes of the elliptical MTJ pillar are 120 nm and 370 nm, respectively. The long axis of the pillar, which corresponds to the magnetic easy-axis of the free layer due to shape anisotropy, is parallel to the \(y\)-axis. The pinned layer magnetization points along \({+y}\). A variable amplitude pulse current (Ip) with duration (\({t}_{\rm{p}}\)) fixed to 50 ns or DC current (IDC) (duration is ~ 1 s) is applied to the W channel to induce magnetization switching of the free layer via SOT. The pulse and DC current sources are different. Note that the rise and fall time of the DC current is significantly larger than those of the pulse current but are sufficiently smaller than the duration of the current (~ 1 s). Current passed along the W channel is parallel to the \(x\)-axis: positive current is defined as current flowing along \(+x\). The geometry of the device used here is referred to as type-Y. To probe the magnetic state of the MTJ free layer, a DC bias voltage of 10 mV is applied to the MTJ. An external field Hy is applied along the \(y\)-axis to reset the magnetic state of the free layer as well as to apply a bias field during the channel current application. We have studied more than 15 devices with nominally the same device structure. Representative results from one device are shown: similar data are obtained for the other devices. All measurements are performed at room temperature.
Figure 1b shows the minor loop of the MTJ resistance (RMTJ) vs. Hy. The high (~ 64 kΩ) and low (~ 36 kΩ) resistance states correspond to antiparallel (AP) and parallel (P) alignment of the free and pinned layers’ magnetization. The tunnel magnetoresistance (TMR) ratio and the resistance-area product are ~ 78% and ~ 1600 Ωμm2, respectively. As Hy is swept, switching from P to AP (AP to P) states are found at Hy ~ \(-\) 100 Oe (~ 210 Oe). The center of the minor loop is shifted to + Hy, which is due to the stray field from the pinned layer and/or the orange peel coupling of the free and pinned layers. The shift field, defined as Hs, is ~ 54 Oe.
Figure 1c shows the RMTJ-Ip loop measured with a constant bias field Hy ~ 54 Oe. We pass a current pulse (50 ns long) through the W channel and measure the MTJ resistance while Hy is applied. The amplitude of the current pulse is varied from Ip = + 550 μA to \(-\) 550 μA and then reversed. The SOT switching from P to AP (AP to P) is observed at Ip ~ 390 μA (~ \(-\)380 μA). The change in the MTJ resistance RMTJ is consistent with the R difference of the P and AP magnetic states. We define \({I}_{\mathrm{c}}^{\mathrm{P}(\mathrm{AP})}\) as the switching current when the initial state is the P (AP) state.
Evaluation of the effective spin Hall angle
Figure 2 displays \({I}_{\mathrm{c}}^{\mathrm{P}(\mathrm{AP})}\) as a function of Hy. The solid circles and triangles show \({I}_{\mathrm{c}}^{\mathrm{P}}\) and \({I}_{\mathrm{c}}^{\mathrm{AP}}\), respectively, using 50 ns long pulse current. We find \({|I}_{\mathrm{c}}^{\mathrm{P}(\mathrm{AP})}|\) increases when Hy increases the barrier height of the switching. For example, the lower energy state is the AP (P) state when Hy < Hs (Hy > Hs). \({|I}_{\mathrm{c}}^{\mathrm{AP}}|\) is therefore larger than \({|I}_{\mathrm{c}}^{\mathrm{P}}|\) when Hy < Hs. This is consistent with STT induced magnetization switching. The switching current \({I}_{\mathrm{c}}^{\mathrm{P}(\mathrm{AP})}\) when the pulse current is replaced with a DC current (duration 1 s) is shown by the open symbols in Fig. 2. We fit the data with a linear function to compare the slopes for pulse and DC current. The solid lines in Fig. 2 represent the least square fitting results. The estimated slopes are − 1.18 (solid triangles) and − 0.63 μA/Oe (solid circles) for the pulse current. In the case of DC current, we obtain − 0.44 (open triangles) and − 0.33 μA/Oe (open circles), which are smaller than those for the pulse current.
The inverse of the slope in Fig. 2 corresponds to the damping-like spin orbit effective field (\({h}_{\mathrm{DL}}\)) per unit current acting on the magnetization divided by the Gilbert damping constant \(\alpha\) (see Methods). We find that the averaged \({h}_{\mathrm{DL}}/\alpha\) is ~ − 12.3 Oe (− 29.0 Oe) at a channel current density (j) of 106 A/cm2 for pulse (DC) current. (The current density is estimated by assuming a uniform current flow within the channel.) We infer that difference in \({h}_{\mathrm{DL}}/\alpha\) estimated using the pulse and DC current measurements may be caused by difference in the switching regime (e.g. dynamical switching vs. thermally activated switching17). \({h}_{\mathrm{DL}}\) per current density is related to the effective spin Hall angle \(\xi\) via \({h}_{\mathrm{DL} / j}\sim \hslash \xi /(2e{M}_{s}d)\), where \({M}_{s}\) and \(d\) are the saturation magnetization and thickness of the free layer4. Substituting \({M}_{s}\cong 1200\) emu/cm3 and \(\alpha \cong 0.04\) estimated in a similar system12 and \(d=2\) nm, we find \(\xi \cong -0.03 (-0.07)\) for the pulse (DC) current induced switching. We consider \(\xi\) estimated from DC current induced switching is more accurate due to the smaller \({|I}_{\mathrm{c}}^{\mathrm{P}(\mathrm{AP})}|\); see Methods for the details. Note that \(\xi\) is smaller than that estimated in previous works10, 14, 18 likely due to damages caused by device fabrication processes (e.g. Ar ion etching of the CoFeB free layer that needs to be stopped right above the W layer).
Current and field dependence of the switching probability
The switching probability of the free layer is obtained using the following process: (1) Reset the free layer magnetization direction to either P or AP state using Hy ~ \(\pm\) 1000 Oe. (2) Measure the MTJ resistance at Hy ~ 0. (3) Apply a bias field Hy. For field-induced switching, we vary the amplitude and length of the bias field. To study current-induced switching, a pulse or DC current with variable amplitude is applied subsequently. (4) Measure the MTJ resistance at Hy ~ 0. The difference of the MTJ resistance acquired in processes (2) and (4) provides information on the magnetic state of the free layer. Processes (1)-(4) are repeated 20–50 times to obtain the switching probability.
Figure 3a,b show the probability of field-driven magnetization switching plotted as a function of Hy. The duration of Hy in process (3), denoted as t, is varied. The switching probability changes from 0 to 1 as the magnitude of Hy is increased. The transition of the switching probability from 0 to 1 is relatively sharp and shows little dependence on t. The switching characteristics of DC and pulse current induced magnetization switching are shown in Figs. 4 and 5, respectively. The duration of the pulse current is fixed to 50 ns (DC current is applied for ~ 1 s) and the bias field Hy is varied. Note that Hy < Hs (Hy > Hs) favors the AP (P) state (Hs ~ 54 Oe). The transition of the switching probability, from 0 to 1, is sharp and nearly independent of Hy for the DC current induced switching. For Hy ~ Hs, the transition shows a slight broadening when P approaches 1, a feature that is enhanced for pulse current induced switching.
In contrast, the transition shows a strong dependence on Hy for pulse current induced switching. First, for Hy ~ Hs, we find a tail in the transition from 0 to 1 near P ~ 1, which was also apparent in the DC current switching. Although one may infer that such reduction in the switching probability at near zero (net) magnetic field is associated with magnetization switching processes that involve motion of domain walls, we do not find evidence of intermediate resistance states that correspond to domain walls remaining in the element after application of the current pulse. In addition, we find the transition width for which P varies from 0 to 1 depends on Hy. The transition width tends to increase when \({H}_{y}\) is varied in a way to increase the barrier height for switching. This is not in line with the conventional view of thermally activated magnetization switching.
To show this discrepancy, the switching probability is calculated using a model based on thermally activated magnetization switching, given by19
where \({\tau }_{0}\), \(t\), and \({H}_{\mathrm{K}}\) represent the inverse of the attempt frequency, the duration of the driving force (current or bias field \({H}_{y}\)), and the in-plane magnetic shape anisotropy field, respectively. \({\tau }_{0}\) is fixed to 1 ns here for simplicity. \({\Delta }_{\mathrm{P}(\mathrm{AP})}\) and \({I}_{\mathrm{C}}^{\mathrm{P}(\mathrm{AP})}\) are, respectively, the thermal stability factor and the switching current when the initial state is the P (AP) state. I is the current passed along the W channel: we substitute Ip and IDC into I when pulse current and DC current, respectively, are applied. We also add an effective field that arises due to the field-like SOT (\({h}_{\mathrm{FL}}\)) that scales with \(I\). The direction of the fields (\({H}_{y}, {H}_{\mathrm{S}}, {h}_{\mathrm{FL}}\)) and current are in accordance with the definitions shown in Fig. 1.
First, we study the switching characteristics of field induced magnetization switching (Fig. 3). We fit the data with Eq. (1) using \({\Delta }_{\mathrm{P}(\mathrm{AP})}\) and HK as the fitting parameters and set \(I=0\). The results, shown by the red solid lines in Fig. 3, are in good agreement with the data. We obtain \({\Delta }_{\mathrm{P}}\sim {\Delta }_{\mathrm{AP}}\sim 85\) and HK ~ 300 Oe for all data measured. The size of HK is in good agreement with the shape anisotropy field: from the dimension of the ellipse (370 nm \(\times\) 120 nm \(\times\) 2 nm) and the saturation magnetization of CoFeB (Ms ~ 1200 emu/cm3), HK ~ 396 Oe. The difference of \({\Delta }_{\mathrm{P}}\) and \({\Delta }_{\mathrm{AP}}\) is negligible.
Next, we fit the data from current induced magnetization switching using Eq. (1) with HK = 300 Oe, \({\Delta }_{\mathrm{P}(\mathrm{AP})}\)= 85 (obtained from the results shown in Fig. 2) and Hs = 54 Oe. \({I}_{\mathrm{c}}^{\mathrm{P}(\mathrm{AP})}\) and \({h}_{\mathrm{FL}}\) are used as the fitting parameters. The fitted curves for DC current induced switching are shown by solid lines in Fig. 4a–c. The fitted curves show good agreement with the data. The slight broadening of transition near P ~ 1 for \({|H}_{y}-{H}_{\mathrm{S}}|\) ~ 0, however, cannot be reproduced. We note that \({h}_{\mathrm{FL}}\) does not significantly influence the fitting since \({h}_{\mathrm{FL}}I\) is small compared to \({H}_{y}-{H}_{\mathrm{S}}\). Parameters that provide best fit to the data are summarized in Table 1.
The fitting results of pulse current induced switching are shown in Fig. 5a–c. The parameters used in the calculations are summarized in Table 2. We find that the Hy dependence of the transition width cannot be accounted for by even when the field-like SOT is introduced. The solid, dashed and dotted lines in Fig. 5b show the switching probability calculated using Eq. (1) with different \({h}_{\mathrm{FL}}\). Since \({h}_{\mathrm{FL}}I\) scales with current, its effect on P is different from the external field \({H}_{y}\). We find that positive \({h}_{\mathrm{FL}}\) tends to broaden the transition. Note, however, that the sign of the field-like SOT in similar heterostructures have been found to be either negative or relatively small20. Moreover, the model calculations show significant deviation from the data, in particular, when \(|{H}_{y}-{H}_{\mathrm{S}}|\) ~ 0. This is largely due to the broadening of transition near P ~ 1 for \(|{H}_{y}-{H}_{\mathrm{S}}|\) ~ 0, which is larger than that of DC current induced switching.
We briefly comment on the reason behind the change in the transition width with respect to \({h}_{\mathrm{FL}}\) in the model calculations (i.e. Equation (1)). First, \({h}_{\mathrm{FL}}\) influences \({I}_{\mathrm{c}}^{\mathrm{P}(\mathrm{AP})}\). With the current setting (when current is passed along \(+x\), electrons with spin polarization along \(+y\) diffuses in from the W layer to the CoFeB layer), positive \({h}_{\mathrm{FL}}\) increases \({|I}_{\mathrm{c}}^{\mathrm{P}(\mathrm{AP})}|\) (negative \({h}_{\mathrm{FL}}\) decreases \({|I}_{\mathrm{c}}^{\mathrm{P}(\mathrm{AP})}|\))21, 22. This is evident from the plots shown in Fig. 5b. Increase in \({|I}_{\mathrm{c}}^{\mathrm{P}(\mathrm{AP})}|\) indicates larger barrier height for thermally activated switching. In general, larger barrier height leads to smaller transition width for such switching process. Here, however, the field-like SOT scales with the current. Therefore, increase in current leads to further increase in the barrier height via the field-like SOT, which causes the transition broadening. Thus positive \({h}_{\mathrm{FL}}\) tends to increase the transition width.
Discussion
Finally, we discuss possible mechanisms that cause the anomalous \({H}_{y}\) dependence of the transition width of the pulse current induced magnetization switching probability. First, it is possible that incoherent magnetization switching that involves nucleation and subsequent motion of domain walls can cause such broadening of the switching probability. However, we do not find intermediate resistance states (after application of current pulses) that suggest presence of domain walls in the free layer. The broadening is thus not caused by simple domain wall pinning effects. Current induced Joule heating may also play role in the switching process. For this purpose, we analyzed the data using a modified Eq. (1) that takes into account Joule heating. Here we assumed the barrier height (\({\Delta }_{\mathrm{AP}(\mathrm{P})}\)) decreases with increasing current: \({\Delta }_{\mathrm{AP}(\mathrm{P})}\) in Eq. (1) is replaced by \(\frac{{\Delta }_{\mathrm{AP}(\mathrm{P})}}{1+{aI}^{2}}\), where \(a\) is a fitting constant. We find that such modification cannot describe the \({H}_{y}\) dependence of the transition width of the pulse current induced switching. The nonuniformity of the stray field from the SAF pinned layer, if it were to play a role, will influence the switching probability of both pulse and DC current induced switching. Since the transition width is significantly larger for the pulse current induced switching, we consider its effect is negligible. We infer that the current amplitude required to induce switching plays a role23, 24. If the current amplitude exceeds a threshold above which the so-called dynamic switching occurs (thermally activated switching takes place below the threshold current), the transition width cannot be accounted for using Eq. (1) which is based on thermally activated switching. Further studies are required to clarify the mechanism of the transition width broadening of the pulse current induced switching.
In summary, we have studied SOT switching of a three terminal MTJ that consists of W channel, a CoFeB free layer, MgO barrier and a CoFeB synthetic antiferromagnetic pinned layer. The probability of current induced magnetization switching, as a function of easy axis bias magnetic field, are evaluated and compared to calculations based on thermally activated switching. From the dependence of the switching current on the bias magnetic field, the effective spin Hall angle is estimated to be − 0.07. We find the model can account for the field-induced switching and, to a lesser degree, DC current induced switching. In contrast, the change in the switching probability with pulse current cannot be described even when contribution from the field-like torque is included. We infer that the current amplitude that determines the switching mode (dynamical switching vs. thermally activated switching) plays a role.
Methods
The damping-like spin orbit effective field (\({h}_{\mathrm{DL}}\)) relates to the effective spin Hall angle \(\theta\) via
where \(j\) is the current density flowing in the W channel along the \(x\) direction, \({M}_{s}\) and \(d\) are the saturation magnetization and thickness of the free layer. The critical current density of in-plane magnetized free layer at zero temperature is given by25
where \(\alpha\), \({H}_{\mathrm{K}}\), and \({H}_{\mathrm{demag}}\) are the Gilbert damping constant, in-plane magnetic anisotropy field, and perpendicular magnetic anisotropy field, respectively. The in-plane magnetic anisotropy field originates from the shape anisotropy12, and is primarily determined by the demagnetization coefficients \({N}_{i}\) (\(i=x,y,z)\) via \({H}_{\mathrm{K}}=4\pi M\left({N}_{x}-{N}_{y}\right)\). The perpendicular magnetic anisotropy field is given by \({H}_{\mathrm{demag}}=4\pi M\left({N}_{z}-{N}_{x}\right)-{H}_{\mathrm{K}\perp }\), where \({H}_{\mathrm{K}\perp }\) represents the interfacial perpendicular magnetic anisotropy field26,27,28. Equations (1) and (3) are commonly used to analyze the probability of spin-transfer torque switching29, where it is often assumed that the effective switching barrier height linearly depends on the current when the current pulse-width is sufficiently long30,31,32. When the pulse width of the current is narrow, a large current will be necessary to induce a fast switching. A large current suppresses the effective switching barrier significantly, and as a result, the high energy-barrier assumption33 used in the derivation of Eq. (1) becomes no longer applicable. Therefore, the DC current induced switching measurement provides more accurate value of the effective spin Hall angle compared to that estimated by using the pulse current. From Eqs. (2) and (3), \({h}_{\mathrm{DL}}\) per current density can be estimated as \({\mathrm{d}j}_{\mathrm{c}}/\mathrm{d}{H}_{\mathrm{y}}=\alpha j/{h}_{\mathrm{DL}}\).
Data availability
The data that support the findings of this study are available from the corresponding author upon reasonable request.
References
Garello, K., Yasin, F., Couet, S., Souriau, L., Swerts, J., Rao, S., Beek, S. V., Kim, W., Liu, E., Kundu, S., Tsvetanova, D., Croes, K., Jossart, N., Grimaldi, E., Baumgartner, M., Crotti, D., Fumémont, A., Gambardella, P. & Kar, G. S. SOT-MRAM 300mm integration for low power and ultrafast embedded memories. 2018 IEEE Symposium on VLSI Circuits, 81–82 (2018).
Cubukcu, M. et al. Ultra-fast perpendicular spin–orbit torque MRAM. IEEE Trans. Magn. 54, 9300204 (2018).
Miron, I. M. et al. Perpendicular switching of a single ferromagnetic layer induced by in-plane current injection. Nature 476, 189–193 (2011).
Liu, L. et al. Spin-torque switching with the giant spin Hall effect of tantalum. Science 336, 555–558 (2012).
Manchon, A., Koo, H. C., Nitta, J., Frolov, S. M. & Duine, R. A. New perspectives for Rashba spin–orbit coupling. Nat. Mater. 14, 871–882 (2015).
Thomas, L. et al. Perpendicular spin transfer torque magnetic random access memories with high spin torque efficiency and thermal stability for embedded applications. J. Appl. Phys. 115, 172615 (2014).
Fukami, S., Anekawa, T., Zhang, C. & Ohno, H. A spin–orbit torque switching scheme with collinear magnetic easy axis and current configuration. Nat Nano 11, 621 (2016).
Garello, K. et al. Ultrafast magnetization switching by spin-orbit torques. Appl. Phys. Lett. 105, 212402 (2014).
Cubukcu, M. et al. Spin-orbit torque magnetization switching of a three-terminal perpendicular magnetic tunnel junction. Appl. Phys. Lett. 104, 042406 (2014).
Pai, C. F. et al. Spin transfer torque devices utilizing the giant spin Hall effect of tungsten. Appl. Phys. Lett. 101, 122404 (2012).
Yamanouchi, M. et al. Three terminal magnetic tunnel junction utilizing the spin Hall effect of iridium-doped copper. Appl. Phys. Lett. 102, 212408 (2013).
Shiokawa, Y. et al. Dependency of high-speed write properties on external magnetic field in spin–orbit torque in-plane magnetoresistance devices. Appl. Phys. Express 14, 013001 (2021).
Shiokawa, Y. et al. High write endurance up to 1012 cycles in a spin current-type magnetic memory array. AIP Adv. 9, 035236 (2019).
Hao, Q., Chen, W. Z. & Xiao, G. Beta (β) tungsten thin films: structure, electron transport, and giant spin Hall effect. Appl. Phys. Lett. 106, 182403 (2015).
Kim, J., Sheng, P., Takahashi, S., Mitani, S. & Hayashi, M. Spin Hall magnetoresistance in metallic bilayers. Phys. Rev. Lett. 116, 097201 (2016).
Zhang, C. et al. Critical role of W deposition condition on spin-orbit torque induced magnetization switching in nanoscale W/CoFeB/MgO. Appl. Phys. Lett. 109, 192405 (2016).
Braganca, P. M. et al. Reducing the critical current for short-pulse spin-transfer switching of nanomagnets. Appl. Phys. Lett. 87, 112507 (2005).
Liu, J., Ohkubo, T., Mitani, S., Hono, K. & Hayashi, M. Correlation between the spin Hall angle and the structural phases of early 5d transition metals. Appl. Phys. Lett. 107, 232408 (2015).
Taniguchi, T., Utsumi, Y. & Imamura, H. Thermally activated switching rate of a nanomagnet in the presence of spin torque. Phys. Rev. B 88, 214414 (2013).
Lau, Y. C. & Hayashi, M. Spin torque efficiency of Ta, W, and Pt in metallic bilayers evaluated by harmonic Hall and spin Hall magnetoresistance measurements. Jpn. J. Appl. Phys. 56, 0802B5 (2017).
Taniguchi, T., Mitani, S. & Hayashi, M. Critical current destabilizing perpendicular magnetization by the spin Hall effect. Phys. Rev. B 92, 024428 (2015).
Legrand, W., Ramaswamy, R., Mishra, R. & Yang, H. Coherent subnanosecond switching of perpendicular magnetization by the fieldlike spin-orbit torque without an external Magnetic field. Phys. Rev. Appl. 3, 064012 (2015).
Tomita, H. et al. High-speed spin-transfer switching in GMR nano-pillars with perpendicular anisotropy. IEEE Trans. Mag. 47, 1599 (2011).
Tomita, H., Maehara, H., Nozaki, T. & Suzuki, Y. Negative Dynamic Resistance and RF amplification in magnetic tunnel junctions. J. Mag. 16, 140–144 (2011).
Grollier, J. et al. Field dependence of magnetization reversal by spin transfer. Phys. Rev. B 67, 174402 (2003).
Ikeda, S. et al. A perpendicular-anisotropy CoFeB–MgO magnetic tunnel junction. Nature Mater. 9, 721–724 (2010).
Yakata, S. et al. Influence of perpendicular magnetic anisotropy on spin-transfer switching current in magnetic tunnel junctions. J. Appl. Phys. 105, 07D131 (2009).
Kubota, H., Ishibashi, S., Saruya, T., Nozaki, T. & Fukushima, A. Enhancement of perpendicular magnetic anisotropy in FeB free layers using a thin MgO cap layer. J. Appl. Phys. 111, 07C723 (2012).
Koch, R. H., Katine, J. A. & Sun, J. Z. Time-resolved reversal of spin-transfer switching in a nanomagnet. Phys. Rev. Lett. 92, 088302 (2004).
Taniguchi, T., Utsumi, Y., Marthaler, M., Golubev, D. & Imamura, H. Spin torque switching of an in-plane magnetized system in a thermally activated region. Phys. Rev. B 87, 054406 (2013).
Taniguchi, T., Shibata, M., Marthaler, M., Utsumi, Y. & Imamura, H. Numerical study on spin torque switching in thermally activated region. Appl. Phys. Express 5, 063009 (2012).
Taniguchi, T. & Imamura, H. Current dependence of spin torque switching barrier. Appl. Phys. Express 6, 103005 (2013).
Brown, W. F. Jr. Thermal fluctuations of a single-domain particles. Phys. Rev. 130, 1677 (1963).
Acknowledgements
T. T. is grateful to Takehiko Yorozu for valuable discussions.
Author information
Authors and Affiliations
Contributions
S. I. performed experiments based on discussion with Y. S., T. T., S. M., T. S., and M. H. The samples were fabricated by Y. S., A. T., E. K., Y. I., K. H., and T. S. All authors discussed the results, and S. I., T. T., and M. H. wrote the manuscript.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher's note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Isogami, S., Shiokawa, Y., Tsumita, A. et al. Spin–orbit torque driven magnetization switching in W/CoFeB/MgO-based type-Y three terminal magnetic tunnel junctions. Sci Rep 11, 16676 (2021). https://doi.org/10.1038/s41598-021-95422-8
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-021-95422-8
- Springer Nature Limited