Abstract
Bioactive glasses convert to a biomimetic apatite when in contact with physiological solutions; however, the number and type of phases precipitating depends on glass composition and reactivity. This process is typically followed by X-ray diffraction and infrared spectroscopy. Here, we visualise surface mineralisation in a series of sodium-free bioactive glasses, using transmission electron microscopy (TEM) with energy-dispersive X-ray spectroscopy (EDXS) and X-ray nano-computed tomography (nano-CT). In the glasses, the phosphate content was increased while adding stoichiometric amounts of calcium to maintain phosphate in an orthophosphate environment in the glass. Calcium fluoride was added to keep the melting temperature low. TEM brought to light the presence of phosphate clustering and nearly crystalline calcium fluoride environments in the glasses. A combination of analytical methods, including solid-state NMR, shows how with increasing phosphate content in the glass, precipitation of calcium fluoride during immersion is superseded by fluorapatite precipitation. Nano-CT gives insight into bioactive glass particle morphology after immersion, while TEM illustrates how compositional changes in the glass affect microstructure at a sub-micron to nanometre-level.
Similar content being viewed by others
Introduction
Bioactive glasses are used clinically as granules for bone regeneration, such as in periodontal disease, for filling of alveolar sockets or for treating chronic bone infections1,2. Two clinically approved compositions are phospho-silicate glasses 45S5 and S53P4, commercialised as NovaBone® and Bonalive®, respectively. Such bioactive glass compositions usually contain sodium, which was initially added for lowering the melting temperature and long considered the reason for fast glass degradation in contact with aqueous solutions3. However, it was later shown that the rapid pH increase caused by large sodium concentrations in a bioactive glass has adverse effects in cell culture testing even in a buffered solution such as cell culture medium4. Also, acellular immersion experiments showed that sodium is not really necessary for making glasses degrade, release ions or form an apatite surface layer5,6, and that ion release and apatite formation can be maintained in calcium phospho-silicate glasses if the phosphate content is increased without increasing the silicate network polymerisation7,8,9. As removing sodium from a bioactive glass and replacing it with calcium increases the melting temperature, fluoride may be added to the glass, as it effectively lowers the melting temperature10, to compensate for the traditional fluxing agent Na2O. Besides, fluoride accelerates apatite precipitation by lowering apatite solubility11, and fluoride release from bioactive glasses was shown to promote osteoblast proliferation, differentiation and mineralisation in vitro12.
Here, we investigate a series of sodium-free glasses with varying phosphate/silicate ratio and reactions. The study of the influence of this compositional ratio is interesting mainly for two reasons: (1) during immersion it may help to tailor the precipitation of fluoride and/or phosphate phases and, thus, ion concentrations in solution13, and (2) the phosphate/silicate ratio is strongly related with phase separation phenomena, not only in bioactive glasses but in glasses in general14,15. Phase separation may also determine the precipitation of crystalline phases upon immersion in biological solutions16,17,18. We aim not only to systematically investigate the effect of phosphate/silicate ratio in Na2O-free bioactive glasses on in vitro ion release and apatite precipitation upon immersion in Tris buffer, but to further visualise apatite mineralisation using transmission electron microscopy (TEM) with energy-dispersive X-ray spectroscopy (EDXS) and X-ray nano-computed tomography (nano-CT).
Results and discussion
Glasses before immersion in Tris buffer solution
Analysed fluoride contents have already been reported in our previous publication19, and phosphate/silicate ratio strongly influenced fluorine retention in the glass melts. The P2O5-free glass showed the lowest fluoride loss (13 ± 3%), which was associated with HF volatilization. Glasses P2, P3 and P5 lost 42 ± 19, 26 ± 7 and 55 ± 24% of fluoride, respectively. This difference we associated with an additional mechanism of fluoride loss in phosphate-containing compositions, involving the volatilization of phosphorus-containing fluoride compounds, e.g. POF319.
All glasses were amorphous according to X-ray diffraction (XRD) patterns (Fig. 1) showing the characteristic amorphous halo centred at approximately 30°2θ. Fourier-transformed infrared spectroscopy (FTIR) spectra (Fig. 2) show a broad band visible between 600 and 450 cm−1, which has been assigned to P-O and Si–O–Si bending vibrations20. The bands between 850 and 940 cm−1 (B,C in Fig. 2) correspond to Q2 groups with two non-bridging-oxygen atoms (NBO; ≡Si–O−), while the one positioned at about 1000 cm−1 (A) corresponds to Q3 (one NBO)20. No marked differences were observed with composition. The phosphate content in the present glass system was increased while adding stoichiometric amounts of calcium oxide, which maintains the number of NBO attached to phosphorus21. Therefore, the number of NBO attached to silicon and the silicon network connectivity remained constant throughout the series.
Magic angle spinning nuclear magnetic resonance (MAS NMR) peaks observed for the untreated glasses (Fig. 3) are broad, in agreement with the low level of structural order typical of glasses. 31P MAS NMR spectra of untreated samples P2, P3 and P5 show a single peak at 2.5 to 2.8 ppm (Fig. 3a, Table 1), corresponding to orthophosphate (QP0) groups charge-balanced by calcium ions, in agreement with other Na-free glasses reported in the literature10. The presence of a symmetric orthophosphate signal suggests absence or very low concentrations of Si–O–P bonds. Such direct chemical bonds between the silicate and the phosphate part of the glass structure are typically detected in molecular dynamics simulations16; however, the experimental side is less clear. While it might be possible that the concentration of Si–O-P bonds is too low to be detected by conventional 1D MAS NMR spectra, very detailed solid-state NMR studies on a 29Si and 17O-enriched sample of Bioglass 45S5 did not detect any Si–O–P bonds either22. By contrast, solid-state NMR studies on a calcium-free version of Bioglass 45S5 not only detected phosphate clustering but also found indications for the presence of Si–O–P bonds23. The occurrence of phase separation or clustering, such as presence of phosphate-enriched domains, in bioactive glasses has also been a matter of debate. Molecular dynamics simulations16 only found pronounced phosphate clustering for compositions much higher in phosphate content than 45S5, while a more recent study using dielectric measurements found two different sodium-hopping domains and interpreted this as caused by phase separation, most likely into a phosphate-rich and a silicate-rich phase24. TEM results can give insight into possible phase separation here, discussed further below.
19F MAS NMR spectra (Fig. 3b) also show single peaks only for untreated glasses, with chemical shifts varying between −93.8 (P0) and −96.4 ppm (P5), corresponding to an F-Ca(n) calcium fluoride-like environment. A single peak at −89 ppm was reported in a Na-free glasses of a similar composition5,10. It would be unlikely to have Si–F bonds, e.g., FCa2Si units, present, since their signals were reported to be positioned at −113.1 ppm25. It has been widely described that in bioactive glasses fluoride complexes modifier cations such as Ca2+ by ionic interaction and does not form Si–F bonds, as confirmed by 19F and 29Si MAS NMR spectroscopy10,26,27, X-ray photoelectron spectroscopy26,28, molecular dynamics simulation25,29 and other methods26,30. We thus expect fluoride here to be coordinated by calcium ions. Molecular dynamics simulations further suggested the formation or Ca-F rich clusters26, where calcium and fluoride species interact ionically, resulting in areas of low viscosity, prone to crystallisation.
Glasses P0, P2 and P5 were further investigated using TEM-based techniques. Glasses P0 and P2 were imaged as bulk samples, while glass P5 was characterized in its powder form. In general, powder particles present an inhomogeneous thickness, and they are usually not electron transparent, which makes TEM interpretation difficult. This issue is overcome by bulk sample preparation for TEM analyses. Figure 4a shows the P0 microstructure before immersion. The larger roundish regions (white arrows in Fig. 4a) could correspond to electron radiation damage from the TEM. The dark areas of a few nanometres in diameter (black arrows in Fig. 4a) could be attributed to immiscibility phases or phase separation droplets (PSD). Since calcium is the highest atomic number element in these glasses, the dark colour in bright field images suggests that those PSD are enriched in Ca2+. This agrees with studies showing that fluorides can induce phase separation, in which the nucleation and crystallization takes place in the volume of the PSD14,31,32,33,34,35. Larger PSD were also observed in the phosphate-containing glasses (Fig. 4b–d), with those in glass P2 having irregular morphology. In glass P5, round features were observed at the thinnest part of the powder particles (Fig. 4c,d). In some areas, crystalline planes were discerned (black arrow and inset in Fig. 4d). However, these crystalline areas did not seem sufficient to be detected by XRD (Fig. 1, 2). Besides CaF2, it is known that P2O5 may induce phase separation15,17, and nanometre-sized Ca-P-rich clusters have been observed by TEM18. Based on this, the droplet phase in Fig. 4 is likely to be enriched in P, Ca, and F, while the matrix phase is rich in silicon.
EDXS analysis was performed on glass P2 (2.4 mol% P2O5). In the HAADF image (Fig. 4e) irregular areas are observed as bright contrast, which indicates an enrichment in the element of highest atomic number (Z-contrast), which is Ca. Figure 4h displays EDXS results of one of those bright areas and of the matrix. Both show very similar elemental concentrations, with only slightly higher calcium concentrations in the bright droplet. This similarity in chemical composition suggests that the bright contrast in the micrograph (Fig. 4g) may have a second contribution from diffraction contrast in addition to the Z-contrast. Diffraction contrast originates from differences in the orientation of the atomic layers rather than density or chemical composition (similar to what we observed previously for Bioglass 45S536). Both contrast contributions can be explained as very early stages of crystallisation, i.e. precursors of crystalline phases with an atomic medium-range order, possibly involving calcium fluoride-like areas10,37, owing to the slightly higher concentration in calcium. Pre-ordered fluoride bonds have been determined by 19F MAS NMR in glasses containing BaF2 (Ba-F bonds38) and LaF3 (La–F bonds39). The phosphorus distribution mapping is superimposed in yellow (Fig. 4f). P is heterogeneously distributed, but clear enrichment areas are not observed for this glass. This suggests clustering rather than phase separation, despite molecular dynamics simulations predicting phosphate clustering for higher concentrations of phosphate only16.
Changes during immersion in Tris buffer solution
All glasses caused an increase in the pH of the Tris buffer solution (Fig. 5a), which is characteristic for bioactive phospho-silicate glasses and is caused by a rapid ion exchange between modifier cations (here, Ca2+ only) attached to NBO and protons from the solution17. This pH increase is very fast at early time points and slows down with time, particularly for glass P0, which seems to give a constant pH from day 3 (the slight pH decrease observed mirrors that of the glass-free control). At 14 days, pH values in solution seem to decrease with phosphate/silicate ratio in the glass (Fig. 5a,c), an effect which has been reported earlier9. This relationship between pH rise in solution and phosphate content in the glass can be explained with the pH rise originating from the ion exchange between the silicate part of the glass, as modifier cations (ionically connected to NBO) are released in exchange for protons. By contrast, orthophosphate groups and calcium ions charge balancing them are released together7. Phosphate-free composition P0 is showing the lowest pH rise and the lowest relative calcium concentration in solution. A possible explanation may be less water intrusion in this composition, owing to the absence of phosphate groups and, as a result, a more densely packed glass network. The release of calcium and fluoride ions from the Ca-F environment in the glass does not affect the pH either37,40. The less prominent increase in pH from day 7 could be associated with the decrease in ion release, which would be obtained by depletion of the ions and the formation of a passivating apatite layer as discussed below.
A common feature in all glasses here is that ion release is fastest within the first 3 days. Such rapid release is typical for bioactive glasses, has been observed in dynamic ion release studies at very early time points41, and it is explained by a highly disrupted silicate network allowing for fast water intrusion and ion exchange to happen42,43. To facilitate comparison between glass compositions, calcium and silicon ion concentrations in solution were normalised to the content of the respective ion in the glass, i.e., they are shown as relative concentrations in percentages. Curves of calcium concentrations in Tris buffer over time mirror the pH curves. pH changes during immersion of bioactive glasses can be described as a summation of all ion exchange occurring between modifiers attached to NBO and the solution44, and calcium ions are the only modifier ions in the present glass system. However, ion concentrations detected in solution depend on both ion release from the glass and precipitation of solid phases from the solution and, as discussed below, precipitation of two calcium-containing phases occurs in the present system. A likely explanation for the matching trends in pH and calcium concentrations is that precipitation consumes stoichiometric amounts of calcium associated with phosphate and fluoride in the glass, while calcium ions remaining in solution correspond roughly to the stoichiometric amounts of modifiers attached to NBO. Silica-species have a low solubility in aqueous solutions of the physiological pH conditions studied here, with the actual solubility showing pH dependence45. Except for composition P0, concentration of silica species (Fig. 5d) shows an inverse relationship with pH, which may simply reflect this relationship of silica solubility with pH in this range.
Besides pH trends and ion concentrations, ion exchange is also reflected in FTIR spectra and XRD patterns46. The intensity of bands B and C corresponding to NBO (ca. 850 to 940 cm−1) decreases drastically at early time points (Fig. 2). For P0, this effect is apparent from 1 day of immersion, while for the other glasses the bands have virtually disappeared at 6 h. The corresponding appearance of an additional amorphous halo in XRD patterns (Fig. 1) at lower 2θ values illustrates the formation of an ion-depleted layer, typically referred to as silica gel layer47,48. FTIR band J appearing at 790 cm−1 also reflects silica gel formation, corresponding between vibrations between SiO4 tetrahedra20. Besides the formation of an ion-depleted glass layer, precipitation of crystalline phases has been observed with apatite being of particular interest. Phosphate is typically the limiting factor for apatite formation, which the present results confirm (Fig. 5b). As immersion experiments here were performed in a medium free of phosphate (as well as calcium and fluoride) ions, phosphate content in and release from the glasses directly influences precipitation. FTIR spectra of P0 (Fig. 2a) show no indication of precipitation apart from silica gel formation; XRD patterns (Fig. 1a), by contrast, show precipitation of calcium fluoride (CaF2, ID 00-035-0816) from 2 days of immersion, which is also reflected in 19F MAS NMR spectra (7 and 14 days, Fig. 3b) showing narrow peaks positioned at about −108 ppm (Table 1)49,50. The broad feature still present at about −94 ppm indicates that there is still a contribution from amorphous F-Ca(n) species in the glass5,10.
It is interesting to note that the split FTIR band between 560, 580 and 600 cm−1 (K) appears at early time points, with spectra showing no indication of amorphous CaP being present (except maybe for P2 at 6 h, Fig. 2b). A possible explanation is the relatively simple glass composition, containing only calcium ions as modifiers, and the effect of fluoride ions accelerating apatite precipitation51 by preventing the formation of octacalcium phosphate as an intermediate step52. This early apatite formation is also reflected in results on ion concentrations in solution. Phosphate concentrations from 6 h in solution were very low in agreement with previous studies6,53, and this result has been associated with a rapid phosphorus release before the first time point of analysis causing early apatite precipitation which subsequently resulted in the solution being depleted in phosphate species53. In the present study, phosphorus concentrations were around the detection limit except for glasses P3 to P5 at 6 h and 1 day (Fig. 5b). These slightly higher concentrations for P3 to P5 suggest that phosphate availability was not yet the limiting factor for apatite formation here, and that depletion occurred later.
The apatite formed on bioactive glasses is often described as biomimetic owing to its nano crystallinity54 and its carbonate substitution. Presence of carbonate substitution is indicated by the band at about 870 cm−1 (band H in Fig. 2b–d; C–O stretch) as well as broad bands between 1400 and 1600 cm−1 (F), with the position of the latter indicating B-type substitution, i.e. carbonate replacing a phosphate band55.
Micro- and nano-structural changes during immersion in Tris buffer solution
Figure 6a,b shows sub-micron scale TEM micrographs of the P0 powder microstructure at 7 days of immersion in Tris buffer solution. In addition to homogeneous areas, agglomerates of smaller particles were also observed. Crystalline planes were clearly visible at higher magnification, which according to the XRD results (Fig. 1) can be attributed to CaF2. At 14 days of immersion, the coarse morphology of the powder particles does not change significantly. However, the crystalline area covers a more extensive area (black arrows in Fig. 6c,d). Owing to the absence of phosphate ions in glass and immersion medium, no precipitation of calcium phosphate (CaP) species can possibly occur for composition P0.
With increasing phosphate content in the glass, the situation changes. From 1 day of immersion, FTIR spectra of immersed P2 (Fig. 2b) show a split band (K) at 560, 580 and 600 cm−1, which is characteristic for apatitic orthophosphate groups55. Concomitant appearance of the narrow P—O stretch band positioned at 1030 cm−1 (G) further confirms the beginning of apatite crystallisation. For glasses P3 and P5 (Fig. 2c,d) these bands are visible from 6 h of immersion already, showing that the higher phosphate content in the glass caused larger or faster phosphate release (further discussed below) and, subsequently, faster apatite precipitation. For glasses P2 to P5, XRD patterns (Fig. 1b–d) show appearance of apatite formation later than FTIR spectra (which is not surprising as ATR-FTIR is more surface sensitive than XRD), but they confirm that, indeed, apatite forms (e.g. fluorapatite, Ca3(PO4)F, ID 01-071-0880, or a partially fluoride-substituted apatite). In addition, they show reflections corresponding to calcium fluoride for P2 and P3. 31P MAS NMR spectra (Fig. 3a) further confirm apatite formation: while the peak positions before and after immersion (Table 1) have changed slightly only, the linewidth has narrowed drastically for spectra after immersion, indicating a more ordered structure around phosphorus atoms, i.e. a crystalline calcium orthophosphate environment. 19F MAS NMR spectra of glasses P2 to P5 at 7 days' immersion (Fig. 3b) show a signal at −101 to −102 ppm, associated with fluorapatite56, which was weak only for P2 but increased in intensity with phosphate content in the glass. This signal appeared as a dominant feature for P5, confirming that the apatite formed is fluorapatite.
Using nano-CT, we investigated whether changes in glass morphology had occurred during immersion in Tris buffer. The three-dimensional nano-CT images of P0 and P2 powder samples at 14 days of immersion in Tris buffer (Fig. 7) show the morphology of the samples and the distribution in space of various particles with irregular shapes and different sizes, ranging from some tens of micrometres to hundreds of nanometres. The larger and rather edgy particles also show different surface textures, appearing either smooth or rough due to the presence of pores of some hundreds of nanometres (Fig. 7a, blue arrows). Although we imaged the samples by Zernike phase-contrast, the grey level distribution of the images also carries some absorption-contrast information, and the pixel grey level and the electronic density of the chemical elements in the sample are related. Therefore, the domains below 5 µm in size, which are smaller and more rounded and show a different grey level than the matrix (which is mainly composed of silicon) could be related to the presence of calcium. Indeed, the crystallisation of CaF2 in P0 (Fig. 7a, bottom) and CaF2 and fluorapatite in P2 (Fig. 7b, bottom) correlate well with the presence of these brighter particles in nano-CT images and also support the results obtained by EDX.
Figure 8 shows the micro- and nanostructure of P2 powder at 7 and 14 days of immersion, showing similarities to those seen for P0 (Fig. 6a,b). At higher magnifications, small crystalline areas are densely distributed in the matrix (Fig. 8b). Moreover, from the HRTEM image (Fig. 8c) a power spectrum analysis and fast Fourier transform (FFT) of the crystalline area (Fig. 8d,e) show distinctive spots r1 and r2 which can be correlated with the r(−220) and r(11–1) positions of the calculated electron diffraction pattern based on CaF2 (ICSD 28,730), confirming crystallization of CaF2 in that particular area of sample P2 at 7 days. EDXS analysis performed at 14 days of immersion (Fig. 8f,g) shows the following composition (in at%): 37.4 Si, 38.0 Ca, 8.6 F and 16.0 P, which matches that of fluorapatite (with ratio Ca:F being nearly 5:1 and Ca:P nearly 5:3). Figure 6e-i shows P5 powder microstructure at 7 and 14 days of immersion. Crystalline planes are observed at 7 days (Fig. 6f,g), and crystalline areas are located at the edges of the powder particles (Fig. 6e), which corresponds to the crystalline phases detected by XRD analysis.
Taken together, TEM highlights the presence of phosphate clustering and nearly crystalline calcium fluoride environments in SiO2-P2O5-CaO-CaF2 glasses, which are likely to affect not only ion release and precipitation but possibly also crystallisation at elevated temperatures. By using a combination of various analytical methods, we can illustrate how ion release is followed by surface precipitation, and how this process changes if the phosphate/silicate ratio in the glass increases. Nano-CT and TEM made it possible to visualise how these changes affect the bioactive glass morphology and microstructure at a sub-micron to nanometre-level after mineralisation.
Methods
Glass design and preparation
Glasses in the system SiO2-P2O5-CaO-CaF2 (Table 2) were designed by increasing the phosphate/silicate ratio while maintaining the silicate network polymerisation (network connectivity, NC = 2.11)7,17 comparable to that of Bioglass 45S5. Glasses were named based on their P2O5 content.
Glasses were melted in platinum–rhodium crucibles; 150 g batches contained mixtures of analytical grade SiO2 (99.0%, Carl Roth, Germany), Ca(H2PO4)2·2H2O (Budenheim KG, Germany), CaF2 (Chemiewerk Nünchritz, Germany), and CaCO3 (≥ 99.0% Merck, Germany). The raw materials were melted in an induction furnace (in-house built) at temperatures of up to 1550 °C. Glasses P0-P3 were cast into brass moulds. Glass transition temperatures (Tg) were determined by differential scanning calorimetry (STA 449 F1 Jupiter, NETZSCH-Gerätebau, Germany) at 10 K/min heating rate. Based on the Tg values around 653 °C the glasses were annealed at 670 °C (± 5 K) for 2 h. Compositions P4 and P5 had a high tendency to devitrify and were therefore quenched only without subsequent annealing. The glasses were crushed using a metallic mortar, sieved (125 to 250 µm) and stored in a desiccator. Glasses P0, P2 and P5 were chosen for imaging characterisation. Bulk pieces of P0 and P2 were prepared by drilling rods (5 mm in diameter) from the annealed glass blocks and subsequently cutting into 5 mm thick pieces with a low-speed diamond saw (Struers Minitom, Denmark) and low viscosity oil. Glass P5 was only characterized as powder since it was not possible to obtain bulk pieces owing to its inherent devitrification tendency. Fluoride quantification was carried out by Laser-induced breakdown spectroscopy as detailed previously19.
Immersion experiments
For in vitro dissolution tests, 75 mg of glass powder (125 to 250 µm particle size range) was immersed in 50 mL of 0.062 mol L−1 Tris buffer solution (pH 7.4) following a previously described protocol46. Samples were placed in an orbital shaker at 37 °C and 100 rpm for 6, 24, 48, 72 h, 7 or 14 days. Experiments were performed in triplicates. At each time point, the pH was measured using a pH electrode and meter (S40 SevenMulti™, Mettler Toledo) and samples were filtered; leachates were acidified using 1 M HNO3 solution and analysed by inductively-coupled plasma optical-emission spectroscopy (ICP-OES; 5110, Agilent Technologies, Germany). Glass powders were analysed as described in the following.
Powder characterisation
Samples before and after immersion in Tris buffer solution were characterised by X-ray diffraction (Rigaku Miniflex 300, Cu Kα, 15 kV and 40 mA). The powders were milled finely for analysis, and patterns were recorded with a scan range between 10 and 60°2θ and a 0.02° step size. Phase identification was carried out using PDXL software together with the ICDD PDF-2 database.
Attenuated total reflectance Fourier transformed infrared spectroscopy (ATR-FTIR; Cary 630, Agilent Technologies, Germany) in absorbance mode was used to further examine the powders. For analysis, powders were ground with an agate pestle and mortar, and spectra were collected between 4000 and 400 cm−1 with a resolution of 4 cm−1 and 16 scans per measurement. An initial background scan was carried out before each set of samples.
Magic angle spinning nuclear magnetic resonance spectroscopy was used to study the phosphorus (31P) and fluorine (19F) chemical environment in the glasses before and after immersion. These analyses were performed on a Bruker Avance 400 Ultrashield spectrometer (Bruker BioSpin) operating at a 14.1 T magnetic field, and data processing was carried out using TopSpin. Glass powders were packed in a 2.5 mm rotor and rotated at 12 kHz and 22 kHz for 31P and 19F, respectively, with 32 scans per analysis. 19F chemical shift was referenced using the −120 ppm peak of 1 M NaF aqueous solution as a secondary reference against CFCl3; 31P chemical shift was referenced to 85% H3PO4 solution (0 ppm).
Imaging techniques
Transmission electron microscopy was employed to characterize samples P0, P2 and P5 before and after immersion in Tris buffer solution. Bulk sample preparation (P0 and P2) was carried out by wedge-polishing (Allied High Tech MultiPrep, USA), followed by double-sided ion-beam milling using low-energy (2.5 keV) argon ions under a small angle of incidence (6°) until grinding and polishing artefacts were removed (precision ion-polishing system, PIPS + II, Gatan, Inc.). Electron-transparent areas of the sample were selectively coated with carbon using a special coating mask57 prior to TEM investigation to reduce charging effects resulting from interaction with the electron beam. TEM powder samples (P5 before immersion, and P0, P2 and P5 glasses after immersion) were suspended in ethanol. A droplet of the dispersion was dried on a carbon-coated copper grid and mounted in the TEM sample holder. High resolution (HR) bright field images and scanning transmission electron microscopy (STEM) images were recorded in a TEM microscope (FEI Tecnai G2 F20, Thermo Fisher Scientific, Netherlands) operating at 200 kV and camera length 200 mm.
Energy dispersive X-ray spectroscopy (EDXS) area analyses of Si (K-line), P (K-line), Ca (K-line) and F (K-line) were recorded in the same microscope (percentage of oxygen was calculated as difference to 100%). The bulk TEM sample of glass P2 before immersion was additionally investigated in a more advanced TEM microscope (FEI Titan 80–300, Thermo Fisher Scientific, Netherlands) with spherical aberration corrector and high-brightness gun at 80 kV acceleration voltage and 70 mm camera length. High-angle annular dark field (HAADF) images and EDXS elemental distribution mappings were obtained to gain information about elemental distribution. The EDXS detector (Super X, Thermo Fisher Scientific, Netherlands) consists of four silicon drift detectors, offering a maximum collection angle of 0.8 sr. The analytical accuracy of the EDXS measurement was assessed to be around 2%.
In the powder sample of sample P2 at 7 days of immersion in Tris buffer solution, fast Fourier transformation (FFT) of HRTEM images (also called a power spectrum) was obtained (Digital Micrograph software, Gatan). Measured d-spacings calculated from the power spectra were compared with reference d-spacings of specific candidates (Ca,F) preselected by XRD evaluation. Structural data, i.e. atomic positions of the references, were taken from the Inorganic Crystal Structure Database (ICSD, Fachinformationszentrum Karlsruhe, Germany, and the National Institute of Standards and Technology, USA). The structures were then rebuilt using CaRIne Software (CaRIne Crystallography 3.1) to generate d-spacing lists and simulate the electron diffraction pattern (EDP).
Samples P0 and P2 were imaged using a Carl Zeiss Xradia 810 Ultra X-ray microscope equipped with a chromium source (5.4 keV). The powdered samples were imaged inside a polyimide tube (Goodfellow Cambridge Ltd., LS522958) glued onto the tip of a metallic pin that was inserted in the sample holder. The samples were scanned using Zernike phase contrast, a field-of-view of 64 µm2 with a detector binning of 2 (isotropic pixel size 128 nm2) and a total of 901 projection images, each one with an exposure time of 50 to 60 s. These were acquired by rotating the sample 180° and the drift was corrected using the adaptive motion compensation from the software. Image reconstruction for obtaining the X-ray nano-computed tomography (nano-CT) dataset was performed by a filtered back-projection algorithm using XMReconstructor software. The tomograms obtained were then exported as a stack of 16-bit TIFF images. Vision4D software (arivis AG) was used for the volumetric visualisation.
References
Hench, L. Chronology of bioactive glass development and clinical applications. New J. Glass Ceram. 3, 66–73. https://doi.org/10.4236/njgc.2013.32011 (2013).
Lindfors, N. C. et al. Bioactive glass S53P4 as bone graft substitute in treatment of osteomyelitis. Bone 47, 212–218. https://doi.org/10.1016/j.bone.2010.05.030 (2010).
Hench, L. L. The story of Bioglass®. J. Mater. Sci. Mater. Med. 17, 967–978. https://doi.org/10.1007/s10856-006-0432-z (2006).
Wallace, K. E., Hill, R. G., Pembroke, J. T., Brown, C. J. & Hatton, P. V. Influence of sodium oxide content on bioactive glass properties. J. Mater. Sci. Mater. Med. 10, 697–701. https://doi.org/10.1023/A:1008910718446 (1999).
Chen, X. et al. Sodium is not essential for high bioactivity of glasses. Int. J. Appl. Glass Sci. 8, 428–437. https://doi.org/10.1111/ijag.12323 (2017).
Chen, X. et al. Bioactivity of sodium free fluoride containing glasses and glass-ceramics. Materials 7, 5470–5487. https://doi.org/10.3390/ma7085470 (2014).
Hill, R. G. & Brauer, D. S. Predicting the bioactivity of glasses using the network connectivity or split network models. J. Non-Cryst. Solids 357, 3884–3887. https://doi.org/10.1016/j.jnoncrysol.2011.07.025 (2011).
Eden, M., Sundberg, P. & Stalhandske, C. The split network analysis for exploring composition-structure correlations in multi-component glasses: II. Multinuclear NMR studies of alumino-borosilicates and glass-wool fibers. J. Non-Cryst. Solids 357, 1587–1594. https://doi.org/10.1016/j.jnoncrysol.2010.11.101 (2011).
O’Donnell, M. D., Watts, S. J., Law, R. V. & Hill, R. G. Effect of P2O5 content in two series of soda lime phosphosilicate glasses on structure and properties—Part II: Physical properties. J. Non-Cryst. Solids 354, 3561–3566. https://doi.org/10.1016/j.jnoncrysol.2008.03.035 (2008).
Brauer, D. S., Karpukhina, N., Law, R. V. & Hill, R. G. Structure of fluoride-containing bioactive glasses. J. Mater. Chem. 19, 5629–5636. https://doi.org/10.1039/b900956f (2009).
Cate, J. M. & Featherstone, J. D. B. Mechanistic aspects of the interactions between fluoride and dental enamel. Crit. Rev. Oral Biol. Med. 2, 283–296. https://doi.org/10.1177/10454411910020030101 (1991).
Gentleman, E., Stevens, M. M., Hill, R. G. & Brauer, D. S. Surface properties and ion release from fluoride-containing bioactive glasses promote osteoblast differentiation and mineralization in vitro. Acta Biomater. 9, 5771–5779. https://doi.org/10.1016/j.actbio.2012.10.043 (2013).
Łukowicz, K. et al. The role of CaO/SiO2 ratio and P2O5 content in gel-derived bioactive glass-polymer composites in the modulation of their bioactivity and osteoinductivity in human BMSCs. Mater. Sci. Eng. C. 109, 110535. https://doi.org/10.1016/j.msec.2019.110535 (2020).
Deng, W., Gong, Y. & Cheng, J.-S. Liquid-phase separation and crystallization of high silicon canasite-based glass ceramic. J. Non-Cryst. Solids 385, 47–54. https://doi.org/10.1016/j.jnoncrysol.2013.11.006 (2014).
Glatz, P. et al. Different roles of phosphorus in the nucleation of lithium aluminosilicate glasses. J. Non-Cryst. Solids 493, 48–56. https://doi.org/10.1016/j.jnoncrysol.2018.04.021 (2018).
Tilocca, A. & Cormack, A. N. Structural effects of phosphorus inclusion in bioactive silicate glasses. J. Phys. Chem. B 111, 14256–14264. https://doi.org/10.1021/jp075677o (2007).
Brauer, D. S. Bioactive glasses: Structure and properties. Angew. Chem. Int. Edit. 54, 4160–4181. https://doi.org/10.1002/anie.201405310 (2015).
Fábián, M. et al. Network structure and thermal properties of bioactive (SiO2–CaO–Na2O–P2O5) glasses. J. Mater. Sci 55, 2303–2320. https://doi.org/10.1007/s10853-019-04206-z (2020).
Pablos-Martín, A., Contreras Jaimes, A. T., Wahl, S., Meyer, S. & Brauer, D. S. Fluorine loss determination in bioactive glasses by laser-induced breakdown spectroscopy (LIBS). Int. J. Appl. Glass Sci. 12, 213–221. https://doi.org/10.1111/ijag.15867 (2021).
Kim, C. Y., Clark, A. E. & Hench, L. L. Early stages of calcium-phosphate layer formation in bioglasses. J. Non-Cryst. Solids 113, 195–202. https://doi.org/10.1016/0022-3093(89)90011-2 (1989).
O’Donnell, M. D., Watts, S. J., Law, R. V. & Hill, R. G. Effect of P2O5 content in two series of soda lime phosphosilicate glasses on structure and properties—Part I: NMR. J. Non-Cryst. Solids 354, 3554–3560. https://doi.org/10.1016/j.jnoncrysol.2008.03.034 (2008).
Pedone, A., Charpentier, T., Malavasi, G. & Menziani, M. C. New insights into the atomic structure of 45S5 Bioglass by means of solid-state NMR spectroscopy and accurate first-principles simulations. Chem. Mater. 22, 5644–5652. https://doi.org/10.1021/cm102089c (2010).
Fayon, F., Duée, C., Poumeyrol, T., Allix, M. & Massiot, D. Evidence of nanometric-sized phosphate clusters in bioactive glasses as revealed by solid-state 31P NMR. J. Phys. Chem. C 117, 2283–2288. https://doi.org/10.1021/jp312263j (2013).
Elgayar, I., Hill, R., Chen, X., Bubb, N. & Wood, D. Dielectric spectroscopy and dissolution studies of bioactive glasses. Int. J. Appl. Glass Sci. 8, 418–427. https://doi.org/10.1111/ijag.12324 (2017).
Pedone, A., Charpentier, T. & Menziani, M. C. The structure of fluoride-containing bioactive glasses: new insights from first-principles calculations and solid state NMR spectroscopy. J. Mater. Chem. 22, 12599–12608. https://doi.org/10.1039/C2JM30890H (2012).
Chungong, L. F. et al. Insight into the atomic scale structure of CaF2-CaO-SiO2 glasses using a combination of neutron diffraction, 29Si solid state NMR, high energy X-ray diffraction, FTIR, and XPS. Biomed. Glass. 5(1), 112–123 (2019).
Hayashi, M., Watanabe, T., Nagata, K. & Hayashi, S. Coordination environment of fluorine in the CaO-SiO2-CaF2 glasses bearing Na2O: A solid-state 19F MAS NMR study. ISIJ Int. 44, 1527–1533. https://doi.org/10.2355/isijinternational.44.1527 (2004).
Hayashi, M., Nabeshima, N., Fukuyama, H. & Nagata, K. Effect of fluorine on silicate network for CaO-CaF2-SiO2 and CaO-CaF2-SiO2-FeO2 glasses. ISIJ Int. 42, 352–358. https://doi.org/10.2355/isijinternational.42.352 (2002).
Christie, J. K., Pedone, A., Menziani, M. C. & Tilocca, A. Fluorine environment in bioactive glasses: Ab initio molecular dynamics simulations. J. Phys. Chem. B 115, 2038–2045. https://doi.org/10.1021/jp110788h (2011).
Hill, R., Wood, D. & Thomas, M. Trimethylsilylation analysis of the silicate structure of fluoro-alumino-silicate glasses and the structural role of fluorine. J. Mater. Sci 34, 1767–1774. https://doi.org/10.1023/A:1004550907134 (1999).
Hoell, A. et al. Crystallization of BaF2 from droplets of phase separated glass: Evidence of a core–shell structure by ASAXS. CrystEngComm 22, 5031–5039. https://doi.org/10.1039/C9CE02003A (2020).
Lin, C., Bocker, C. & Rüssel, C. Nanocrystallization in oxyfluoride glasses controlled by amorphous phase separation. Nano Lett. 15, 6764–6769. https://doi.org/10.1021/acs.nanolett.5b02605 (2015).
Rodríguez Chialanza, M. et al. Structural analysis of oxyfluoride borate glass and BaF2 crystallization from phase separation. J. Am. Ceram. Soc. 103, 3126–3137. https://doi.org/10.1111/jace.17022 (2020).
de Pablos-Martin, A., Patzig, C., Hohe, T., Duran, A. & Pascual, M. J. Distribution of thulium in Tm3+-doped oxyfluoride glasses and glass-ceramics. CrystEngComm 15, 6979–6985. https://doi.org/10.1039/C3ce40731d (2013).
Imanieh, M. H., Yekta, B. E., Marghussian, V., Shakhesi, S. & Martín, I. R. Crystallization of nano calcium fluoride in CaF2–Al2O3–SiO2 system. Solid State Sci. 17, 76–82. https://doi.org/10.1016/j.solidstatesciences.2012.11.008 (2013).
Contreras Jaimes, A. T. et al. Deepening our understanding of bioactive glass crystallization using TEM and 3D nano-CT. J. Eur. Ceram. Soc. https://doi.org/10.1016/j.jeurceramsoc.2021.1002.1051 (2021).
Christie, J. K. & Brauer, D. S. The role of fluoride in the nanoheterogeneity of bioactive glasses. Phys. Chem. Glasses-B 58, 180–186. https://doi.org/10.13036/17533562.58.4.180 (2017).
Bocker, C., Muñoz, F., Duran, A. & Rüssel, C. Fluorine sites in glasses and transparent glass-ceramics of the system Na2O/K2O/Al2O3/SiO2/BaF2. J. Solid State Chem. 184, 405–410. https://doi.org/10.1016/j.jssc.2010.12.001 (2011).
Munoz, F. et al. NMR investigation of the crystallization mechanism of LaF3 and NaLaF4 phases in aluminosilicate glasses. J. Non-Cryst. Solids 357, 1463–1468. https://doi.org/10.1016/j.jnoncrysol.2010.11.024 (2011).
Lusvardi, G. et al. Quantitative structure−property relationships of potentially bioactive fluoro phospho-silicat glasses. J. Phys. Chem. B 113, 10331–10338. https://doi.org/10.1021/jp809805z (2009).
Fagerlund, S., Hupa, L. & Hupa, M. Dissolution patterns of biocompatible glasses in 2-amino-2-hydroxymethyl-propane-1,3-diol (Tris) buffer. Acta Biomater. 9, 5400–5410. https://doi.org/10.1016/j.actbio.2012.08.051 (2013).
Tilocca, A. & Cormack, A. N. Exploring the surface of bioactive glasses: Water adsorption and reactivity. J. Phys. Chem. C 112, 11936–11945. https://doi.org/10.1021/jp803541j (2008).
Tilocca, A. & Cormack, A. N. Modeling the water−bioglass interface by ab initio molecular dynamics simulations. ACS Appl. Mater. Interfaces 1, 1324–1333. https://doi.org/10.1021/am900198t (2009).
Bingel, L., Groh, D., Karpukhina, N. & Brauer, D. S. Influence of dissolution medium pH on ion release and apatite formation of Bioglass® 45S5. Mater. Lett. 143, 279–282. https://doi.org/10.1016/j.matlet.2014.12.124 (2015).
Iler, R. K. The Chemistry of Silica: Solubility, Polymerization, Colloid and Surface properties and Biochemistry of Silica (Wiley, 1979).
Kirste, G. et al. Effect of chloride ions in Tris buffer solution on bioactive glass apatite mineralization. Int. J. Appl. Glass Sci. 8, 438–449. https://doi.org/10.1111/ijag.12288 (2017).
Abu Tahari, M. N., Hakim, A., Marliza, T. S., Mohd, N. H. & Yarmo, M. A. XRD and CO2 adsorption studies of modified silica gel with octadecylamine. Mater. Sci. Forum 888, 529–533 (2017).
Biswas, R. K. et al. Study of short range structure of amorphous Silica from PDF using Ag radiation in laboratory XRD system RAMAN and NEXAFS. J Non-Cryst Solids 488, 1–9. https://doi.org/10.1016/j.jnoncrysol.2018.02.037 (2018).
Schmedtauf der Günne, J., Mangstl, M. & Kraus, F. Occurrence of difluorine F2 in nature: In situ proof and quantification by NMR spectroscopy. Angew. Chem. Int. Ed. 51, 7847–7849. https://doi.org/10.1002/anie.201203515 (2012).
Hill, R. G. et al. Characterisation of fluorine containing glasses and glass-ceramics by 19F magic angle spinning nuclear magnetic resonance spectroscopy. J. Eur. Ceram. Soc. 29, 2185–2191. https://doi.org/10.1016/j.jeurceramsoc.2009.01.009 (2009).
Mneimne, M., Hill, R. G., Bushby, A. J. & Brauer, D. S. High phosphate content significantly increases apatite formation of fluoride-containing bioactive glasses. Acta Biomater. 7, 1827–1834. https://doi.org/10.1016/j.actbio.2010.11.037 (2011).
Iijima, M. & Onuma, K. Roles of fluoride on octacalcium phosphate and apatite formation on amorphous calcium phosphate substrate. Cryst. Growth Des. 18, 2279–2288. https://doi.org/10.1021/acs.cgd.7b01717 (2018).
Brauer, D. S., Mneimne, M. & Hill, R. G. Fluoride-containing bioactive glasses: Fluoride loss during melting and ion release in tris buffer solution. J. Non-Cryst. Solids 357, 3328–3333. https://doi.org/10.1016/j.jnoncrysol.2011.05.031 (2011).
O’Donnell, M. D., Watts, S. J., Hill, R. G. & Law, R. V. The effect of phosphate content on the bioactivity of soda-lime-phosphosilicate glasses. J. Mater. Sci. Mater. Med. 20, 1611–1618. https://doi.org/10.1007/s10856-009-3732-2 (2009).
LeGeros, R. Z., Trautz, O. R., Klein, E. & LeGeros, J. P. Two types of carbonate substitution in the apatite structure. Experientia 25, 5–7. https://doi.org/10.1007/bf01903856 (1969).
Yi, H. et al. A carbonate-fluoride defect model for carbonate-rich fluorapatite. Am. Mineral. 98, 1066–1069. https://doi.org/10.2138/am.2013.4445 (2013).
Höche, T., Gerlach, J. W. & Petsch, T. Static-charging mitigation and contamination avoidance by selective carbon coating of TEM samples. Ultramicroscopy 106, 981–985. https://doi.org/10.1016/j.ultramic.2006.05.007 (2006).
Acknowledgements
D.S.B., A.P.M. and J.M.S.S. acknowledge funding by the German Research Foundation (DFG; grant numbers BR 4608/7-1, PA 3095/1-1 and WE 4051/21-1). D.S.B. and J.M. acknowledge funding for a bilateral exchange programme by the German Academic Exchange Service (DAAD) and the Academy of Finland. The authors thank Steffi Ebbinghaus, Gabi Möller and Lutz Preißer (Otto Schott Institute of Materials Research) for XRD measurements and sample preparation, respectively, Julia Prechtl and Andrea Böbenroth (Fraunhofer IMWS) for TEM and nano-CT sample preparation, Dr Harold Toms (Queen Mary University of London) for assistance with MAS NMR experiments and Lutz Berthold (Fraunhofer IMWS) for EDXS mappings.
Funding
Open Access funding enabled and organized by Projekt DEAL.
Author information
Authors and Affiliations
Contributions
All experiments were performed by A.T.C.J., G.K., A.P.M., S.S. and J.M.S.S. and designed by J.M., N.K., R.G.H. and D.S.B. A.T.C.J., G.K., A.P.M. and D.S.B wrote the main manuscript text. All authors discussed the results and reviewed the manuscript.
Corresponding authors
Ethics declarations
Competing interests
A.T.C.J., G.K., A.P.M., S.S. and J.M.S.S and J.M declare no competing interests. R.G.H. is on the Board of Directors of BioMin Technologies Ltd., a company selling bioactive glass-containing dentifrices. D.S.B., N.K. and R.G.H. own shares in the company.
Additional information
Publisher's note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Jaimes, A.T.C., Kirste, G., de Pablos-Martín, A. et al. Nano-imaging confirms improved apatite precipitation for high phosphate/silicate ratio bioactive glasses. Sci Rep 11, 19464 (2021). https://doi.org/10.1038/s41598-021-98863-3
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-021-98863-3
- Springer Nature Limited