Abstract
Slime expelled by velvet worms entraps prey insects within seconds in a hardened biopolymer network that matches the mechanical strength of industrial polymers. While the mechanic stimuli-responsive nature and building blocks of the polymerization are known, it is still unclear how the velvet worms’ slime hardens so fast. Here, we investigated the slime for the first time, not only after, but also before expulsion. Further, we investigated the slime’s micro- and nanostructures in-depth. Besides the previously reported protein nanoglobules, carbohydrates, and lipids, we discovered abundant encapsulated phosphate and carbonate salts. We also detected CO2 bubbles during the hardening of the slime. These findings, along with further observations, suggest that the encapsulated salts in expelled slime rapidly dissolve and neutralize in a baking-powder-like reaction, which seems to accelerate the drying of the slime. The proteins’ conformation and aggregation are thus influenced by shear stress and the salts’ neutralization reaction, increasing the slime’s pH and ionic strength. These insights into the drying process of the velvet worm’s slime demonstrate how naturally evolved polymerizations can unwind in seconds, and could inspire new polymers that are stimuli-responsive or fast-drying under ambient conditions.
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Introduction
Biomedical adhesives are challenged by the need for significant adhesion to soft tissues, even in wet environments1. Knowledge-based material development can gain inspiration from biological processes and materials from natural sources that allow for tailoring adhesion and, thus, show a potential not only for biomedical but also for technological breakthroughs, e.g. in 3D bioprinting of biomacromolecules applications2,3. In this view, the unique slime secretion used by velvet worms—invertebrates from the phylum Onychophora—for defense, prey capture and parental feeding4,5 is exemplary. The velvet worm Epiperipatus biolleyi, which is found in Central America6, produces a white sticky slime that strongly adheres to a wide variety of materials such as wood, metals, glass, and biological tissues.
The slime-expelling mechanism of velvet worms has been investigated previously using anatomical images and high-speed videography7. The worms possess a syringe–hose system in which the muscles surrounding the slime reservoir are contracted, forcing it through a funnel-shaped duct, at which the fluid velocity is increased. The slime then passes through two oral papillae (i.e. elastic oral tubes) that oscillate at a frequency of ~ 30 Hz, producing two slime jets that form a sticky fiber mesh lined with micrometer-sized liquid droplets. While this process is well known, and the expelled slime has been partially characterized8,9,10,11,12,13,14,15,16, the physicochemical processes that drive the rapid drying of the slime after expulsion and mechanical stimulation are only partially known. The expelled slime remains a viscous liquid after expulsion, and upon mechanical stimuli, for example, due to the movements of an entrapped insect, it transforms within seconds to a highly expandable rubber-like and then stiff glassy material8,9. This liquid–solid transition can occur as fast as within 10 s to 1 min after expulsion and mechanical stimulation8.
An initial study on the slime of Euperipatoides rowelli proposes that velvet worm slime consists of protein nanoglobules, which self-assemble into microfibrils after the application of shear forces9. Baer et al. showed that these fibrils are formed by highly phosphorylated proteins that have a β-crystallite structure in the storage phase14,15. Recently, Lu et al. reported that the most abundant proteins, ES_P1 and ES_P2, form multi-protein complexes and are mostly in random coil conformation in the soluble state. The N-terminus are enriched in Gly and Ser, and they suggested that proteins with this terminus could be responsible for the liquid–liquid phase separation16. Bauer et al. suggested that these proteins forming the β-crystallites suffer conformational changes, or partial protein unfolding, during the stretching produced by the shear forces. When dried, the proteins lose mobility and stay in this conformation, but when rehydrated, they gain mobility, so the nanoglobules are formed again, suggesting that the nanoglobule-to-fiber formation is reversible14,17.
Our previous results showed that the fiber formation process was reversible after dissolving the slime in the same amount of water as the native slime (several hours are necessary) or acetic acid-diluted solutions (almost immediately)8. However, the fast liquid-to-solid transition of the bulk slime cannot be reproduced; the water-reconstituted slime is more elastic and loses its glassy appearance. We reported the presence of nanoglobules in our recent work on solidified expelled slime from a different species (Epiperipatus hilkae) that had not yet experienced an external mechanical stimulus. We also discovered fibers, crystalline domains, and abundant electron-dense micro- and nanostructures with higher metal contents compared to the nanoglobules, and the lipids previously reported8. The electron-dense particles could not be reversibly assembled from the reconstituted hardened slime as it was previously done with the nanoglobules. Due to their abundance, we hypothesized that these electron-dense structures could play a vital role in the slime’s rapid liquid-to-solid transition.
In the present work, we performed an in-depth physicochemical characterization of velvet worm slime’s electron-dense particles and investigated changes in their structure and the properties of the slime. We characterized both the expelled slime (before and after applying external mechanical stimulus) and unexpelled slime (extracted in situ from the reservoir). To rule out artifacts due to contaminations (onychophorans have an open circulatory system18), we also analyzed the hemolymph and nano- and microparticles isolated thereof. The slime and nano- and microparticles were analyzed by cryo-transmission electron microscopy (cryo-TEM), selected area electron diffraction (SAED), scanning transmission electron microscopy (STEM), Energy-dispersive X-ray spectroscopy (EDS), polarized microscopy, Attenuated Fourier-transform Infrared Spectroscopy (ATR-FTIR) and protein and lipid staining. The chemical composition of the slime and hemolymph was compared using EDS and Inductively Coupled Plasma Spectroscopy (ICP). The influence of the salts on the tension pull-off adhesion force between two glass blocks and Young’s modulus of the slime was determined by mechanical dynamical analysis (DMTA) and atomic force microscopy (AFM). Therefore, the influence of the salts and small molecular weight compounds in the Storage G′ and Loss modulus G″ of the slime reconstituted in water at a concentration of 40 mg/mL was analyzed.
Results
Characterization of the bulk slime and hemolymph
We collected slime expelled by velvet worms and characterized it optically and with high-resolution microscopy. Figure 1 compares the liquid expelled slime and the solid slime before and after an external mechanical stimulus.
The liquid expelled slime was white and with no glassy appearance (Fig. 1a, Supplementary Video 1), and hundreds of nanometers particles and fibers were dispersed in the liquid phase before it experienced an external mechanical stimulus (Fig. 1b,c). A white pellet containing micro and nanoparticles was obtained when the slime was allowed to flow slowly into an Eppendorf tube and then centrifugated, Fig. 1d. The slime’s white color and the supernatant’s color after that centrifugation suggest that the slime is an emulsion. The remaining supernatant solution was translucent. The environmentally dried expelled slime is a white solid (Fig. 1e) and contains electron-dense nano and microparticles dispersed in the protein matrix, Fig. 1f,g. Preformed microfibers were also observed, Fig. 1h. The size of the electron-dense particles was similar for each slime sample but differed from one specimen to another. The electron-dense core areas of the particles varied from 50 nm to 3 µm. Figure 1g shows the slime containing the smallest electron-dense particles found among the samples analyzed, confirming that the darkest color is associated with the presence of heavier elements, e.g. carbon, nitrogen, and oxygen and not the particle thickness.
Some worms were dissected to determine if these electron-dense microparticles were also present in the stored slime and not just external contamination. Using a CO2 chamber as the first dissection step, make the specimen calm asleep without slime expulsion before the next dissection steps, which were: introducing them into a chloroform vapor chamber, removing the body impurities using a water bath, opening the dorsal area, and removing the hemolymph surrounding the reservoir, as the velvet worms have an open circulatory system18,19,20,21. Finally, the reservoir was separated and opened by small scissors as fast as possible to collect the slime (Supplementary Fig. 1).
The slime extracted directly from the reservoir showed similar features compared to the expelled slime that didn't experience an external mechanical stimulus: white color, presence of dispersed micro and nanoparticles in suspension, and fibers (Supplementary Fig. 1). These results suggested that the crystalline microparticles are not formed as an artifact of the drying, during the slime expulsion or external contamination. Furthermore, the pellet precipitated from 100 µL was clearly visible at the Eppendorf bottom. The approximate weight of the pellet isolated ranged between 12–6 wt% of the initial mass. As described in the following sections, the cryo-TEM analysis confirms the presence of crystalline nanoparticles and microparticles. To verify that these microparticles and nanoparticles were not vesicles released in hemolymph from apoptotic cells or released by cells in a process that could be similar a the release of polyphosphate for platelets during coagulation22, hemolymph from the dorsal area was analyzed and compared with the slime. Therefore, the presence of cells in the expelled slime was also investigated.
The elemental composition of the expelled slime and the hemolymph obtained from the dorsal area were analyzed by ICP and EDS to determine if the vesicles could be derived from the hemolymph. Both fluids present similar elemental compositions in terms of Na, O, P, N, Ca, Mg, K and Al, but at different concentrations; Na, P, Ca and K are higher metal concentrations for both fluids (Supplementary Fig. 2, Supplementary Table 1). Even though the elemental composition was similar, the electron-dense particles could not be found in the dried hemolymph fluid containing a high amount of cells. Dried hemolymph showed mainly cells, NaCl crystals at the border of the dried fluid, calcium oxygen-based particles with no defined preferential morphology, and roundish micrometer structures with a lower amount of P, Na and O than the crystalline particles (Supplementary Fig. 2). Furthermore, the slime is acellular, as shown by the paraffin negative eosin/hematoxylin staining cross-sections of the paraformaldehyde cross-linked solid slime (Supplementary Fig. 3) and also containing glycans. Masson staining and collagen immunostaining of the expelled slime suggests the presence of collagen fibers dispersed in the slime. Collagen fibers are located between the reservoir muscles and lumen (Supplementary. Fig. 4). Therefore, we cannot discard the mixture with a certain hemolymph amount during the expelling process. Still, the hemolymph is not likely to be the source of the dispersed electron-dense particles, as we did find this type of nanoparticle even in the concentrate suspension as described above. Furthermore, the slime extracted from inside the reservoir after removing the hemolymph from the surrounding organs is white and presents similar electron-dense particles (Supplementary Fig. 1).
The extracted from the reservoir and expelled slime protein matrix before an external mechanical stimulus formed lamellar layers in which preformed fibers appear preferentially aligned (Supplementary Figs. 5,6). The slime birefringence shows that the slime is stored as a liquid crystalline fluid in the reservoir, Fig. 2a. A slime matrix consisting of proteins forming β-crystallites in the storage phase has been suggested by Bauer et al.15, who described interlattice spacings, seem to be consistent with those of the electron-transparent few nm-sized crystallites that we found in the protein matrix. These observations are in line with previously reported birefringence of the fibers and particles composing the expelled slime of Epiperipatus hilkae8. Liquid crystalline ordering has also been suggested as a possible storage condition for silks in other animals, such as spiders23,24, and can occur in a wide variety of other biological molecules, such as DNA, collagen, and cellulose. This fluid state may help to decrease the flow viscosity and, consequently, the energetic cost of its secretion25. Harrington et al. suggested that the slime protein changes from a β-crystallite state to a random coil state when stretched17. When the worm expelled the slime all over a glass slide, it formed transparent threads, as seen in Fig. 1i, upper part. The bottom part, where the liquid slime settled without being stretched, remained white. The transparent threads expelled on a glass slide by the worm show an inner crystalline area surrounded by an amorphous coating (Supplementary Fig. 7a), suggesting a phase separation that started during the expelling process. Micrometric fibers were observed but not microparticles in the transparent areas, Fig. 1j,k. Figure 1h,j show how the bulk material did not exhibit a high amount of particles on the surface or in the inner area. Figure 2b,c shows the loss of crystalline order after applying an external mechanical stimulus to the slime. Only randomly dispersed micron-sized fibers that polarized the light were observed. After experiencing an external mechanical stimulus, the expelled slime had a porous structure that could indicate a discontinuous protein network formation or phase separation due to the mechanical stimulus and CO2 formation (Fig. 1l and supplementary Fig. 7a)26,27. This structure could facilitate water diffusion within/through the fibers and their interface with air. The mechanism and role of this porous network formation remain to be fully understood.
When both dried slime samples, i.e., the one expelled and the one extracted from the reservoir, were rehydrated with the approximate amount of water of the liquid slime, they became transparent after mixing with water (80 wt% water), and elastic-like threads could be spun from the suspensions, but no fast-drying took place in this case (Supplementary video 2).
A comparison of the FTIR spectra of the expelled slime (remaining white) before and after experiencing external mechanical stimulus (transparent) shows a shift in the amide I and amide II bands from 1625 to 1634 cm−1 and from 1533 to 1515 cm−1 (Supplementary Fig. 8a). This shift can be correlated to a change in the protein assembly and interactions with the chemical species surrounding the proteins. The band at 1625 cm−1 indicates the presence of β-sheets in the expelled slime without external mechanical stimulus28. A pronounced peak at 1723 cm−1 could be associated with the concentration of the lipidic fraction surrounding the fibers (FTIR signal is obtained from the outer layers, 2 µm depth). This lipidic coating surrounding the fibers could also help to expel the water from the first contact surface, increase the compatibility with insects' cuticles and protect from early disaggregation29,30.
Dynamic scanning analysis of the expelled slime (Supplementary Fig. 8b), in a range below its degradation temperature (Supplementary Fig. 8c), showed an endothermic event at 53,6 °C that could be correlated to protein active water loss and conformational changes. Lu et al.22 showed that the slime denatured, losing its fiber-forming formation properties at 70 °C16. This event was not detected in the expelled slime that experienced mechanical stimulus, which suggests conformational changes that could enhance the protein–protein interaction and change the mechanical properties31. The crystallization and melting of the lipids in the slime at 89–93 °C. Similar values have been obtained for waxes and lipids extracted from plants and insects32. The higher melting temperature could suggest that the lipids could form solid lipidic particles.
pH value of the expelled slime ranged from 5.0 to 5.5, while that of a transparent solution of rehydrated slime ranged from 6.5 to 7.0. There is a pH increase due to the dissolution of a basic component in the slime, which we report here to be the electron-dense particles shown in Fig. 1, as we will describe in the next sections. We then tested the stability of the dried films in both a neutral PBS buffer and a slightly acidic aqueous solution. Slime was partially stable in the neutral buffer (pH 7.4) but quickly dissolved in acidic media (pH 4.5, Supplementary Fig. 7b,c), suggesting the disassembly of the protein matrix composing the slime at low pH.
Characterization of the electron-dense particles
The presence of electron-dense roundish particles was confirmed to be dispersed in the samples taken from the white freshly liquid unexpelled and expelled slime. Figure 3 a and b show the cryo-TEM micrographs of rounded and angular crystalline particles of 50 to 750 nm in diameter dispersed in the unexpelled slime and expelled before experiencing an external mechanical stimulus. The particles were sometimes freestanding, but more often, an electron-transparent coating interconnected several hundreds of these particles in a spring-like arrangement.
The pellet isolated from the expelled slime (remaining white) using centrifugation was analyzed to determine the chemical composition of the crystals by different electron microscopy techniques. Before centrifugation, we fixed the particles with paraformaldehyde to stabilize them, as the shell most probably contained proteins, and the solubility and chemical composition was analyzed. Particles with diameters between 500 nm–3 µm were isolated from the expelled slime (Fig. 4a and Supplementary Fig. 9) at 5000 rpm. The centrifugation speed was optimized to decrease the precipitation of other globular protein structures found that could be correlated to protein aggregates, coacervates, or empty shells (Fig. 4b,c, Supplementary Fig. 10). The electron-dense particles were surrounded by a shell with different d-spacing than the electron-dense inner material (Supplementary Fig. 11). In general, the electron-dense particles were crystalline (Fig. 3c) with an electron-transparent nm-thick coating. Figure 3d–i are proof that the electron-dense particles encapsulate a higher amount of Na, O, and P than the surrounding areas.
The crystalline particles, cross-linked or not cross-linked, could not be completely dissolved in ethanol or chloroform as would be expected for lipids. But they were unstable and rapidly dissolved in water (Supplementary Figs. 12, 13). Inorganic salts such as carbonates and phosphates are poorly soluble in these solvents, but they do dissolve in water. When the particles were rinsed in water and vortexed, they left the cross-linked lipid-protein shells behind (Fig. 4c). Sodium or phosphorous was not detected (Supplementary Fig. 13).
The FTIR spectra of isolated particles from the expelled slime, Fig. 4d, showed two intense absorption bands at 1631 cm−1 and 1529 cm−1, corresponding to the amide vibrational bands I and II of proteins and peptides33. Furthermore, the band observed at 1400 cm−1 could be associated with carbonates34. Phosphates exhibit absorption bands at 1103 cm−135,36 and silicates at approximately 1016 cm−137. The bands at 2900 and 2990 a cm−1 are associated with C–C and C–H from lipids8. These findings suggest that the pellet contained proteins and/or lipoproteins. Protein and lipid staining of the pellet revealed that the micrometer-sized particles are not protein-based but rather stabilized by a lipid-protein coating, as we can observe in the hollow areas that were not stained inside the particles, as it was expected for protein particles (Fig. 4e). Jehle et al. showed that nitrogen was detected in protein composite particles of hundreds of nanometers within secretory vesicles mussel byssus cuticle using STEM-EDS opposite to the velvet worm vesicles that encapsulate mainly inorganic salts38. We speculate that this lipid-protein coating could serve for lubrication and help to isolate the particles to avoid the early reaction of inorganic cargo with the outer acidic media. To determine the presence of another type of particle, we also analyzed the supernatant solution. TEM grids of the deposited supernatant solution were analyzed before and after staining with osmium tetroxide and uranyl acetate. Supplementary Fig. 14 shows that lipid particles (without a electron-dense core) and protein aggregates that did not precipitate remained in the supernatant.
Detail characterization of the isolated crystalline particles
Elemental mapping of an area with particles showed high relative proportions of O, Na and P and some Ca, Cl and Si. The single, rounded particles mainly contained O, Na and C, while the N signal was barely detectable in the N map (Fig. 5a,b, Supplementary Fig. 15).
STEM-EDS elemental analysis of isolated roundish particles (Fig. 5a-c and Supplementary Figs. 15, 17) suggests, based on the elements’ stoichiometry, primarily sodium carbonates (Na: 20 ± 3 at.%; C: 23 ± 7 at.%; O: 41 ± 9 at.%). The micrometer-sized rounded particles shown in Fig. 5a presented crystalline reflections in the reciprocal space (Fig. 5d) with d-spacings of 3.19 Å, 2.82 Å, 2.00 Å, 1.62 Å, and 1.27 Å, corresponding to the (220), (202), (− 514), (204), (− 441) crystal planes of monoclinic natron (Na2CO3·10H2O39,40) with a matching accuracy of 99.28–99.96% (Fig. 5e, Supplementary Fig. 17 and Table 2). The sodium carbonate particles were preferentially round in shape, but other more angular morphologies were found occasionally within the isolated pellet. It was interesting to note that these carbonate microparticles were highly reactive. Under the electron beam, the carbonate particles degraded rapidly. This degradation could occur due to the low melting point of natron and water release from the crystal. Indeed, SAED reflections corresponding to the d-spacings of thermonatrite (Na2CO3·H2O) and nahcolite (NaHCO3) were also detected (Fig. 5e)41,42. We measured the carbonic acid concentrations of both the expelled and expelled under mechanical stimulus slime using a carbonic anhydrase enzymatic assay that detects dissolved carbonic acid (HCO3−), finding values of 2.8 ± 0.3 and 1.4 ± 0.2 wt% respectively, which confirms the presence of carbonates and suggests the decrease during the expulsion process could be related to CO2 release. The peak at 1400 cm−1 in the expelled slime FTIR spectra ( Supplementary Fig. 8) could be associated with the carbonate functional groups43. Several authors havereported that the spider silk’s pH and CO2 concentration could be part of the processes occurring to drive the protein structural changes30,44. We observed that a similar process occurs in the velvet worm slime as it will be described below.
The second main group of isolated more angular particles was identified analogously to consist of sodium phosphate Na: 29.1 ± 5.3 at.%; P: 19.2 ± 3 at.%; O: 37 ± 8.3 at.%) (Fig. 6a,b and Supplementary Fig. 18). Silicates and sulfates were also isolated though in smaller quantities (Supplementary Fig. 19). The phosphate particles were mainly grouped in larger globular structures with a carbon-rich layer as shown in Fig. 6a,b. The individual phosphate particles gave rise to crystalline reflections in the reciprocal space with d-spacings of 4.84 Å, 4.57 Å, 3.84 Å and 2.41 Å, corresponding to the crystal planes of hydrated nahpoite (Na2HPO4·2H2O) with a matching accuracy of 99.13–99.89% (Fig. 6d)45. Figure 6 f shows that other crystalline phosphate species were also identified, such as CaNaPO4 (e.g. lit. d-spacing of 2.66, 2.75, 3.80 and 3.84 Å), Na5P3O10 (lit. d-spacings between 2.22–2.67 and 1.45–1.66 Å), Na3PO4 (e.g. the d-spacings of 2.62 and 2.64 Å, although the solubility of this salt makes it rather unlikely), and hydroxyapatite Ca5(PO4)3OH (e.g. lit. d-spacings 4.08 and 3.17 Å) (also refer to Supplementary Table 3 and the lit. XRD spectra)46.
The three peaks at 2θ < 20° (5.49, 5.96, 6.26 Å) that did not fit phosphate species could be explained by the fact that the carbon-rich layer on the phosphate particle was partially crystalline. Furthermore, second-order harmonics reflections of the phosphate species could be responsible for the unidentified peaks above 2θ > 50° because the intensity of electron diffractions falls less rapidly with 2θ than the intensity of X-ray diffractions. Moreover, these inorganic species might interact, resulting in other species, such as calcium silicates, apatite, and calcium chloride.
Divalent cations could help to decrease the solubility of phosphate salts in water, as reported by Muller et al. that trigger the coacervate formation of phosphates by adding calcium47. Phosphate salts are kosmotropic salts that could control protein suspensions' phase separation and coacervation48. AFM studies of the slime reconstituted in water, NaCl, Na2CO3 and Na5P3010 at a pH = 7 showed that the protein aggregates’ morphology and size depend on the salts type and the solution pH (Supplementary Fig. 20). The nanoglobules were reversibly formed when NaCl was added to the dialyzed slime solution and tend to aggregate in longer fibers and bigger aggregates when sodium carbonate and tripolyphosphate were added. Bauer et al. showed that the type of salts, ionic concentration and the pH plays a role in the protein aggregation using dynamic light scattering14. These results suggest that the carbonic acid and the polyphosphate influence the protein aggregation process and structure besides the shear forces47,48,49,50. The presence of polyphosphates stored inside vesicles is widely recognized in insects, bacteria, and fungi, among other species51. Liu et al.30 reviewed that for spider silk, the inorganic compositions account for ∼10 − 20% of the total low molecular weight compounds, containing the dihydrogen phosphate ion (H2PO4−), the potassium ion (K+), NO3−), Na+, Cl−, and the calcium ion (Ca2+) and that also the adhesive properties could be affected30.
Solubilized carbonates and phosphates can neutralize each other in an acid–base reaction, commonly known as a baking powder reaction. Interestingly, the simultaneously basic and acidic properties of the expelled slime have already been described as early as 1874 when Moseley et al. noted a “slightly bitter and at the same time somewhat astringent” taste of the slime18. Carbonates, biological buffers that stabilize alkaline conditions, are known for being extremely reactive with water and acidic solutions52. However, further studies are necessary to determine the amount of CO2 formation. As the slime has a pH value of 5 that increases up to approximately 7 after dissolving all the particles and mixing the components, some dissolved species that could be formed in the aqueous solution from the Na2HPO4·2H2O solid crystals at this pH are phosphoric acid (H3PO4 = H+ + NaH2PO4, pKa = 2.14) and sodium dihydrogen phosphate (NaH2PO4 = H+ + Na2HPO4, pKa = 7.20). Therefore, we propose the following reaction mechanism (not considering the protein contributions) for the reaction of the particles within the liquid media:
In this reaction, X has got a nominal charge of + 1 and represents freely dissolved cations that eventually serve as the counterions of the partially insoluble phosphate reaction products. The d-spacings consistent with the reactants and reaction products were found in both carbonate and phosphate particles (Figs. 5, 6).
The release of basic ions accompanies the observed release of CO2 gas from the carbonates and the formation of highly soluble phosphate bases (Na3−nXnPO4, Na2−mXmHPO4), which can explain the observed increase in pH in the slime from five to approximately 7. The solid Ca5(PO4)3OH (apatite) is consistent with the electron-dense structures co-located with Ca, P and O seen mainly in the isolated pellet and likely a reaction side product. The above reaction suggests that excess solid NaCl crystals remain as particles in the dried slime. Indeed, we observed numerous NaCl crystals in TEM-EDS as highly electron-dense, cubic, or angular nanoparticles.
The role of silicate ions in the slime remains less clear than that of carbonates and phosphates, even though it can be hypothesized that the former will likely allow for cross-linking of fibrous proteins in the slime.
Influence of the salt on slime Young’s modulus, tension pull-off adhesion force and rheological properties
The tension adhesion pull-off force of two glass blocks glued with the native, reconstituted, and dialyzed slime was compared. The native slime pull-off force of the sample glued with a slime dried mass of 1.1 mg was 251 kPa, and the material was stretched 20 µm before failure, Fig. 7a. The reconstituted slime pull-off force was 193 kPa, and the dislocation was 7.64 µm before failure, Fig. 7a. The samples glued with the dialyzed slime fell apart immediately, and the adhesion pull-off force could not be measured. The proteins tended to precipitate and separate from the solution after dialysis. The salts and small molecular weight compounds could affect the protein solvation and stabilization in solution affecting the adhesion properties53. We observed that the reconstituted slime did not recover the adhesion and fast drying properties as compared to the native slime, suggesting that the initial crystalline molecular arrangement plays a critical role in the adhesion process and drying.
Young’s modulus of the slime without the salts and low molecular compounds and the expelled slime were measured. The tendency from five independent sample measurements is shown in Fig. 7b,c. The expelled slime (average 315 ± 45 MPa) shows a higher Young Modulus than the matrix without the inorganic fraction (average 272 ± 26 MPa), suggesting the inorganic salts' role in the material's cross-linking and hardening54.
The results of the dynamic oscillation tests gave important information concerning the effect of the salts and low molecular weight compounds on the slime behavior. Strain sweeps confirmed the gel-like character from the native slime reconstituted solution, as the elastic modulus G′ was higher than the viscous modulus G″ in the linear viscoelastic regime (Fig. 7d). The native slime had a higher G′ value, suggesting a stronger gel with a solid-like character that dominates over the viscous portion. The storage modulus increased when the frequency was increased (Fig. 7d). This is associated with the rate of shear increase, which is proportional to the energy input to the biomolecules. The G′ was lower for the dialyzed slime, suggesting that the salts could influence the intermolecular associative interactions55,56,57. Furthermore, the storage modulus continues to dominate the loss modulus, but the difference between them is smaller, suggesting that the salts and small molecular weight compounds may promote the network gel formation, Fig. 7e58.
Conclusions
Our findings achieved by high-resolution and time-dependent physicochemical characterization of the velvet worms’ slime reveal structural and chemical alterations following the impact of mechanical stimuli. Alterations of the visual appearance (turbid to transparent) and the pH value (acidic to neutral or slightly basic) correlate with a microstructural transformation starting from aggregates and globules containing particles high in C, O, P, Na, Ca and Cl before the expulsion, and characterized by the disappearance of the rounded carbonate and angular phosphate particles in the expelled slime. Several independent lines of evidence suggest that during and after the expelling process and mechanical stimulus, micro- and nanoparticles previously stabilized by a lipid or protein coat dissolve and react with each other in the acidic slime matrix. Evaluation of crystal diffraction signals confirmed the chemical identity of natron and nahpoite with excellent matching accuracy. The increase of both ionic strength and pH is known to favor coextensive fibrous protein connections and assembly. The dispersed salts and low molecular weight compounds also enhance the slime’s gel-like behavior and its glassy appearance and increase Young’s modulus and adhesion force.
Overall, these results point toward a multi-stage mechanism for the gelation and hardening of the slime. The slime appears to be stored in a liquid-crystalline state in the reservoir at an acidic pH. During expulsion, the inorganic carbonate and phosphate particles disappeared and thus must have reacted with the liquid slime and with each other. This increased the expelled slime’s pH level, produced CO2, and increased the ionic strength. These changes in the slime could subsequently drive, together with the shear stress, the protein aggregation, phase separation, drying and hardening of the slime and lead to the resulting sturdy composite biopolymer. Further studies are necessary to determine the functions of other observed salts in the velvet worm slime, the underlying mechanism for the particle biomineralization process, and the ways how the worm could store the proteins in a liquid crystalline phase. The roles of the glycoproteins and (lipo) protein nanoparticles as potential natural lubricants within the slime also need further investigation.
The mechanism of the rapid polymer curing presented here through lipid-protein-stabilized carbonate and phosphate microparticles may be used to design new industrial polymerization processes in which aqueous formulations of polymers are, for example, injection-molded, serve as biocompatible chemo-mechano-responsive adhesives, or are used for intravital bioprinting. Another interesting application could be the design of bio-inks that change stiffness as a function of shear forces applied during the printing process.
Methods
Worm and slime collection, specimen dissection
Specimens of the species Epiperipatus biolleyi were collected in Las Nubes de Coronado, Costa Rica, under the permission R-001-2018-OT-CONAGEBIO provided by the Costa Rican authority CONAGEBIO (Comisión Nacional para la Gestión de la Biodiversidad). Ten female velvet worms were dissected. The observation of a placenta confirmed the sex. Before dissection, the worms were anesthetized by placing them into a carbon dioxide chamber for 10 min and then euthanized in a dissection glass Petri dish containing cotton impregnated with chloroform. The slime reservoir was then extracted and opened, allowing the liquid, unexpelled slime to flow out (Supplementary Fig. 1). slime collected following the expulsion from the oral papilla as described by Mora et al.11 and after an external mechanical stimulus is referred to herein as “expelled slime”. Most of the characterization analysis were performed inmediately after collecting the slime to avoid bacterial growth. Even dough, it was previously reported the presence of antimicrobial peptides that protect the slime of bacterial growth10.
Slime water content and slime film stability
The water content of the liquid unexpelled and expelled slime before mechanical stimulus (Fig. 1) was determined by weighing the slime before and after drying using a microbalance (BOECO, Germany). Both liquid and dried unexpelled slime appeared turbid under white light. A pH paper indicator was used to determine the pH of the native expelled slime, and the expelled slime rehydrated to its original volume using ultrapure water (Milli-Q, 18.2 MΩ arium 611 DI, Sartorius Stedim Biotech, Germany).
An enzymatic assay (MaxDiscovery™, Bioo Life Science Products, USA) served to detect carbonic acid (HCO3−) from dissolved carbonate particles within the slime. The carbonic acid was quantified in 2.8 mg of dried expelled without movement and expelled slime dissolved in 60 µL of CO2-free water (supplied in the MaxDiscovery kit). T
We performed stability tests of solidified threads of expelled slime on glass by submerging them in acetic acid (0.1%, pH = 5) and 100 mM PBS (pH = 7.4) for 1 h and then rinsing them with Milli-Q water.
Electron microscopy
Elemental distribution maps were recorded in scanning transmission mode on a Talos F200X (Super-X EDS, 4-detector configuration, FEI, USA) at an accelerating voltage of 200 kV. Samples were mounted on a double-tilt holder and fixed using a brass ring and clamp. The data were processed using the software Velox 2.9 (FEI, USA). For the maps, a minimum of 17 frames was recorded with a dwell time of 10 µs per pixel unless noted otherwise. To minimize electron-beam-induced carbon deposition and beam-induced degradation of the particles that were highly sensitive to beam damage, the sample shown in Figs. 4, 5 were mounted on a liquid nitrogen-cooled TEM holder (Gatan Inc., US).
The samples for elemental analysis and quantification of particles (Supplementary Table 2) by SEM–EDS and elemental quantification were non-sputtered. The SEM images (18 kV) measurements were obtained using a TESCAN Mira 3 LM field emission instrument with an Octane Pro EDS detector (METEK, USA). The slime was deposited on freshly cleaved highly oriented pyrolytic graphite (HOPG) for these measurements.
For cryo-electron microscopy (cryo-TEM), a drop of fresh liquid unexpelled or expelled slime was added directly onto a lacey carbon film (PlanoEM, Jena, Germany). Excess material was blotted with filter paper (Whatman 40, Little Chalfont, United Kingdom) for 5 s. Then, the sample was immediately plunged into a eutectic mixture of propane and ethane (Carbagas, Switzerland) using a home-built guillotine-type cryoplunger. The vitrified sample was then loaded into the cryo-transfer holder (model Gatan 626 single tilt). Cryo-TEM images were obtained using a Tecnai Spirit TEM operating at 120 kV equipped with a bottom-mount Eagle camera (both FEI Thermo Fischer, Hillsboro, Oregon, US) not exceeding a dose of 100 electrons Å−2.
Isolation and characterization of micro- and nanostructures in the unexpelled and expelled slime
The slime was slowly added to a 1.5 mL Eppendorf tube, and the suspension was centrifugated to 5000 rpm. The pellets were redispersed in 10 µL of Milli Q water, respectively. Five µL of the final dispersions were air-dried at room temperature directly on highly oriented pyrolytic graphite substrates for SEM and on TEM grids for STEM. For protein and lipid staining of the micro- and nanostructures from the pristine expelled or unexpelled slime, paraformaldehyde 2 wt% (Sigma-Aldrich, Germany) was added to the liquid slime (5 µL of paraformaldehyde solution: 100 µL of slime volume) and allowed to react for 15 min. The liquid remained white after the addition of the cross-linking solution. The suspension was centrifuged at 5000 rpm for 10 min, and the pellet was separated from the liquid supernatant. The pellets were redispersed in 10 µL of Milli Q water, respectively. Five µL of the final dispersions were air-dried at room temperature directly on freshly cleaved highly oriented pyrolytic graphite substrates for SEM and on TEM grids for STEM. Dried pellets and supernatant solutions were analyzed using Fourier-transform infrared spectroscopy (FTIR). The spectra were measured on a Bruker Vertex 70 with an IR Scope II extension.
Protein staining
Fluorescence staining of micro- and nanostructures was performed within the expelled slime and isolated particles. The micro- and nanostructures in the expelled slime and isolated particles were stained using the following dyes: rhodamine B isothiocyanate (RITC) at 4 µM in 0.1 M PBS (Sigma-Aldrich, Germany) for proteins; the lipids with CellMask™ Deep Red Plasma membrane stain at 10 µM in PBS (Thermo Fisher Scientific, Germany). Brightfield microscopy and fluorescence images were taken using a laser-scanning microscope (LSM 710, Zeiss, Germany).
Attenuated total reflectance- Fourier transform infrared (ATR-FTIR)
FTIR spectra were recorded on a Bruker ALPHA II series spectrometer equipped with an ALPHA’s Platinum ATR single reflection diamond ATR module. Spectra were averaged over 32 scans using a resolution of 2 cm−1 over the IR range of 4000–400 cm−1. The data were analyzed using the software Bruker OPUS (version 8.1).
Amplitude-modulated atomic force microscopy (AFM)
Sample topography was analyzed in the air using an AFM microscope (Asylum Research, Santa Barbara, CA) operated in tapping mode. Silicon probes (model Tap150Al-G), backside with resonance frequencies of 150 kHz and force constant of 5 N/m were used. AFM was operated in contact mode silicon tips with a nominal tip radius of 10 nm and cantilever spring constant k = 13 N/m (VEECO) for obtaining the force curves. The spring constant was calibrated according to the supplier protocol and using the Asylum Research Software version 15.09.112 and the GetReal function. The data was modeled using the Hertz model, assuming a 10 nm silicon (100) tip and a material passion ratio of 0.33 common value for polyacrylamide gels. The area analyzed was 1 µm. The Hertz Model was used to model the data.
Tension pull-off adhesion force of the native and dialyzed slime
The effect of the salt removal on the adhesion pull-off force was determined by gluing the smaller side area of two rectangular glass blocks with 5 cm × 3.5 cm, Fig. 8. Initially, the two glass blocks were pre-weighted and a drop of the native slime was added on top of one of the lower block surface that was previously clamped. The upper glass block was slowly lowered until it made contact. The system was kept for one hour, and then the upper block was pulled away at a constant speed. The dried glass blocks were weighed again to determine the slime mass to prepare the glass block glued with a similar amount of the reconstituted slime and desalted sample. The weighted mass for the three repetitions was 0.7, 1, and 1.1 mg. The load − displacement behavior was recorded every 0.001 s. The force just before the slime released contact between the two glass blocks was recorded. A universal test machine (Discovery HR-3/Hybrid Rheometer, TA Company) with rectangular torsional geometry was used. The pull-off value reported is the pull of force divided by area.
Rheological properties of the slime with remaining salts and dialyzed
Rheological measurements were carried out in a universal test machine (Discovery HR-3/Hybrid Rheometer, TA Company) and using parallel-plate Geometry in a steady and oscillatory shear with plate–plate geometry (25 mm diameter, gap of 0.5 mm) at 20 °C. 500 µL of the samples were carefully pipetted on the lower plate, and the upper cone was then lowered to a 0.052 mm gap distance. Prior to the test, the samples were left to equilibrate for five minutes. Storage (G′) and loss (G″) moduli were recorded as a function of the strain, in a range between 0.1 and 100%, at a constant angular frequency of 1 and 10 rad/s and at a fixed temperature of 20 °C. A solution of 40 mg/mL of the reconstituted slime and the same samples after dialysis with a dialysis tubing cellulose membrane, molecular weight cut-off 12,000–14,000 (Sigma, Germany), was used for the experiments.
Data availability
Correspondence and requests for materials should be addressed to YCU.
References
Yang, S. Y. et al. A bio-inspired swellable microneedle adhesive for mechanical interlocking with tissue. Nat. Commun. 4, 1–10 (2013).
Lutz, T. M., Kimna, C., Casini, A. & Lieleg, O. Bio-based and bio-inspired adhesives from animals and plants for biomedical applications. Mater. Today Bio 13, 100203 (2022).
Aldred, N. et al. Chitin is a functional component of the larval adhesive of barnacles. Commun. Biol. 3, 1–8 (2020).
Pablo Barquero-González, J., Vega-Hidalgo, Á. & Monge-Nájera, J. Feeding behavior of Costa Rican velvet worms: Food hiding, parental feeding investment and ontogenetic diet shift (Onychophora: Peripatidae). Cuad. Investig. UNED 11, 85–88 (2019).
Monge-Nájera, J. Onychophorology, the study of velvet worms, historical trends, landmarks and researchers from 1826 to 2020 (a literature review). Uniciencia 35, 210–230 (2021).
Pablo Barquero-González, J., Alonso Cabrera Alvarado, A., Valle-Cubero, S., Monge-Nájera, J. & Morera-Brenes, B. The geographic distribution of Costa Rican velvet worms (Onychophora: Peripatidae). Rev. Biol. Trop. https://doi.org/10.15517/rbt.v64i4.19486 (2016).
Concha, A. et al. Oscillation of the velvet worm slime jet by passive hydrodynamic instability. Nat. Commun. https://doi.org/10.1038/ncomms7292 (2015).
Corrales-Urena, Y. R. et al. Extracellular micro and nanostructures forming the velvet worm solidified adhesive secretion. Mater. Res. Express 4, 125013 (2017).
Baer, A. et al. Mechanoresponsive lipid-protein nanoglobules facilitate reversible fibre formation in velvet worm slime. Nat. Commun. https://doi.org/10.1038/s41467-017-01142-x (2017).
Haritos, V. S. et al. Harnessing disorder: Onychophorans use highly unstructured proteins, not silks, for prey capture. Proc. R. Soc. B 277, 3255–3263 (2010).
Benkendorff, K., Beardmore, K., Gooley, A. A., Packer, N. H. & Tait, N. N. Characterisation of the slime gland secretion from the peripatus, Euperipatoides kanangrensis (Onychophora: Peripatopsidae). Comp. Biochem. Physiol. Part B 124, 457–465 (1999).
Mora, M., Herrera, A. & León, P. Análisis electroforético de las secreciones adhesivas de onicóforos del género Epiperipatus. Rev Biol Trop 44, 147–152 (1996).
Jerez-Jaimes, J. H. & Catalina Bernal-Pérez, M. Taxonomía de onicóforos de Santander, Colombia y termogravimetría, calorimetría de barrido diferencial y espectroscopía infrarroja de la secreción adhesiva (Onychophora: Peripatidae). Rev. Biol. Trop. 57, 567–588 (2009).
Baer, A., Hänsch, S., Mayer, G., Harrington, M. J. & Schmidt, S. Reversible supramolecular assembly of velvet worm adhesive fibers via electrostatic interactions of charged phosphoproteins. Biomacromolecules 19, 4034–4043 (2018).
Baer, A. et al. Shear-induced β-crystallite unfolding in condensed phase nanodroplets promotes fiber formation in a biological adhesive. ACS Nano 13, 4992–5001 (2019).
Lu, Y. et al. Complete sequences of the velvet worm slime proteins reveal that slime formation is enabled by disulfide bonds and intrinsically disordered regions. Adv. Sci. 9, 353 (2022).
Harrington, M. J. & Fratzl, P. Natural load-bearing protein materials. Prog. Mater. Sci. 120, 100767 (2021).
Robson, E. A., Lockwood, A. P. M., Ralph, R. Composition of the blood in onychophora. Nature 5022, 533 (1966).
Campiglia, S. S. The blood of Peripatus acacioi marcus & marcus (Onychophora). III. The ionic composition of the hemolymph. Comp. Biochem. Physiol. A Comp. Physiol. 54, 129–133 (1976).
Baer, A. & Mayer, G. Comparative anatomy of slime glands in onychophora (velvet worms). J. Morphol. 273, 1079–1088 (2012).
Lavallard, R. & Campiglia, S. Données cytochimiques et ultrastructurales sur les tubes sécréteurs des glandes de la glu chez Peripatus acacioi Marcus et Marcus (Onychophore). Z. Zelforsch. 118, 12–34 (1971).
Verhoef, J. J. F. et al. Polyphosphate nanoparticles on the platelet surface trigger contact system activation. Blood 129, 1707–1717 (2017).
Sutherland, T. D., Young, J. H., Weisman, S., Hayashi, C. Y. & Merritt, D. J. Insect silk: One name, many materials. Annu. Rev. Entomol. 55, 171–188 (2010).
Walker, A. A., Holland, C. & Sutherland, T. D. More than one way to spin a crystallite: Multiple trajectories through liquid crystallinity to solid silk. Proc. R. Soc. B 282, 20150259 (2015).
Sung, B. & Kim, M. H. Liquid-crystalline nanoarchitectures for tissue engineering. Beilstein J. Nanotechnol. 9, 205–215 (2018).
Huang, Z. et al. A general patterning approach by manipulating the evolution of two-dimensional liquid foams. Nat. Commun. https://doi.org/10.1038/ncomms14110 (2017).
Mohammadi, P. et al. Phase transitions as intermediate steps in the formation of molecularly engineered protein fibers. Commun. Biol. https://doi.org/10.1038/s42003-018-0090-y (2018).
Baird, G. et al. FTIR spectroscopy detects intermolecular β-sheet formation above the high temperature Tm for two monoclonal antibodies. Protein J. 39, 318–327 (2020).
He, Y. et al. Lipids as integral components in mussel adhesion. Soft Matter 14, 7145–7154 (2018).
Liu, X. et al. Recent progress of spider-silk-inspired adhesive materials. ACS Mater. Lett. 3, 1453–1467 (2021).
Amarpuri, G., Dhopatkar, N., Blackledge, T. A. & Dhinojwala, A. Molecular Changes in spider viscid glue as a function of relative humidity revealed using infrared spectroscopy. ACS Biomater. Sci. Eng. 8, 3354–3360 (2022).
van Bockstaele, F., Romanus, M., Penagos, I. A. & Dewettinck, K. Chapter 9 Functionality of natural waxes in hybrid fat crystal networks. In Development of Trans-Free Lipid Systems and their use in Food Products (ed. Toro-Vazquez, J. F.) (The Royal Society of Chemistry, 2022).
Yang, H., Yang, S., Kong, J., Dong, A. & Yu, S. Obtaining information about protein secondary structures in aqueous solution using Fourier transform IR spectroscopy. Nat. Protoc. 10, 382–396 (2015).
Vahur, S., Teearu, A., Peets, P., Joosu, L. & Leito, I. ATR-FT-IR spectral collection of conservation materials in the extended region of 4000–80 cm–1. Anal. Bioanal. Chem. 408, 3373–3379 (2016).
Krishnamurthy, R., Rajasekaran, R. & Samuel, B. S. Growth and characterization of KDP crystals doped with l-aspartic acid. Spectrochim. Acta A Mol. Biomol. Spectrosc. 104, 310–314 (2013).
Karthein, R. et al. A Fourier-transform infrared spectroscopic study of the phosphoserine residues in hen egg phosvitin and ovalbumin. Biochem. Biophys. Res. Commun. 27, 41 (1988).
Corrales-Ureña, Y. R. et al. Biogenic silica-based microparticles obtained as a sub-product of the nanocellulose extraction process from pineapple peels. Sci. Rep. https://doi.org/10.1038/s41598-018-28444-4 (2018).
Jehle, F., Macías-Sánchez, E., Fratzl, P., Bertinetti, L. & Harrington, M. J. Hierarchically-structured metalloprotein composite coatings biofabricated from co-existing condensed liquid phases. Nat. Commun. https://doi.org/10.1038/s41467-020-14709-y (2020).
Taga, T. The crystal lattice of sodium bicarbonate, NaHCO3. Acta Crystallogr. B 25, 2656–2658 (1969).
Zachariasen, W. H. The crystal lattice of sodium bicarbonate, NaHCO3. J. Chem. Phys. 1, 634–639 (1933).
Barthelmy, D. Nahcolite Mineral Data. General Nahcolite Information (2019).
Americal Mineralogist Data Dase (2019).
Kiefer, J., Strk, A., Kiefer, A. L. & Glade, H. Infrared spectroscopic analysis of the inorganic deposits from water in domestic and technical heat exchangers. Energies 11, 798 (2018).
Shang, L. et al. Spinning and applications of bioinspired fiber systems. ACS Nano 13, 2749–2772 (2019).
Davies, D. R. & Corbridge, D. E. C. The crystal structure of sodium triphosphate, Na5P3O10, phase II. Acta Crystallogr. 11, 315–319 (1958).
Suchanek, W., Yashima, M., Kakihana, M. & Yoshimura, M. Rhenanite (–NaCaPO4) as weak interphase for hydroxyapatite ceramics. J. Eur. Ceram. Soc. 18, 1923–1929 (1998).
Müller, W. E. G. et al. Nanoparticle-directed and ionically forced polyphosphate coacervation: A versatile and reversible core–shell system for drug delivery. Sci. Rep. https://doi.org/10.1038/s41598-020-73100-5 (2020).
Mohammadi, P. et al. Controllable coacervation of recombinantly produced spider silk protein using kosmotropic salts. J. Colloid Interface Sci. 560, 149–160 (2020).
Bashir, Z. et al. Engineering bio-adhesives based on protein-polysaccharide phase separation. Int. J. Mol. Sci. 23, 9987 (2022).
Blocher McTigue, W. C. & Perry, S. L. Protein encapsulation using complex coacervates: What nature has to teach us. Small 16, 1907671 (2020).
Ramos, I. et al. Acidocalcisomes as calcium- and polyphosphate-storage compartments during embryogenesis of the insect Rhodnius prolixus stahl. PLoS One 6, e27276 (2011).
Joshi, S., Kalyanasundaram, S. & Balasubramanian, V. Quantitative analysis of sodium carbonate and sodium bicarbonate in solid mixtures using Fourier transform infrared spectroscopy (FT-IR). Appl. Spectrosc. 67, 841–845 (2013).
Sahni, V. et al. Direct solvation of glycoproteins by salts in spider silk glues enhances adhesion and helps to explain the evolution of modern spider orb webs. Biomacromolecules 15, 1225–1232 (2014).
Braun, M., Menges, M., Opoku, F. & Smith, A. M. The relative contribution of calcium, zinc and oxidation-based cross-links to the stiffness of Arion subfuscus glue. J. Exp. Biol. 216, 1475–1483 (2013).
Bergonzi, C. et al. Study of 3D-printed chitosan scaffold features after different post-printing gelation processes. Sci. Rep. https://doi.org/10.1038/s41598-018-36613-8 (2019).
Holten-Andersen, N. et al. pH-induced metal-ligand cross-links inspired by mussel yield self-healing polymer networks with near-covalent elastic moduli. PNAS 108, 2651–2655. https://doi.org/10.1073/pnas.1015862108/-/DCSupplemental (2011).
Flammang, P., Lambert, A., Bailly, P. & Hennebert, E. Polyphosphoprotein-containing marine adhesives. J. Adhes. 85, 447–464 (2009).
Curnutt, A., Smith, K., Darrow, E. & Walters, K. B. Chemical and microstructural characterization of pH and [Ca2+] dependent sol-gel transitions in mucin biopolymer. Sci. Rep. https://doi.org/10.1038/s41598-020-65392-4 (2020).
Acknowledgements
We acknowledge the Comisión Nacional de Biodiversidad de Costa Rica and Ministerio de Ambiente y Energía MINAE for the worm export permissions and the Swiss Federal Food Safety and Veterinary Office for the import permission under TRACES CVEDA.CH.2018.0000376-V1. To the Área de Conservación Central (ACC)—SINAC for access to the specimens. We thank ScopeM (ETH Zurich) for access to their microscopes. We are grateful to Dr. Miguel Spuch-Calvar for the artwork and Prof. Marielos Mora from the University of Costa Rica for advising the worms dissection protocol. Thanks to Carlos Villalobos and Camilo Torres from the LANOTEC for their help during the specimen collection. This work was supported by the Swiss National Science Foundation (SNSF) through the National Center of Competence in Research Bio-Inspired Materials. FS was supported by the SNSF grant 168187.
Funding
Open Access funding enabled and organized by Projekt DEAL.
Author information
Authors and Affiliations
Contributions
Y.C.U. and R.P. collected and dissected the specimens. R.P. did the TEM. Y.C.U. prepared all the samples analyzed, did the HR-TEM, TEM-SAED, AFM, SEM, and LSM analysis, and drafted the manuscript. M.B.A. did the reservoir histology, and D.V. analyzed the slime using cryo-TEM. A.G., F.S. and Y.C.U. did the STEM analysis using the TALOS. E.O. did part of the STEM-EDS analysis of the hemolymph. P.L.M.N. and J.R.V.B. contributed to the data interpretation. F.S. contributed to the SAED analysis, derivation of the reaction equation, and drafting of the manuscript. K.R. did the FTIR analysis. B.R.R. and A.P.F. did the critical revision of the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher's note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary Information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Corrales-Ureña, Y.R., Schwab, F., Ochoa-Martínez, E. et al. Encapsulated salts in velvet worm slime drive its hardening. Sci Rep 12, 19261 (2022). https://doi.org/10.1038/s41598-022-23523-z
Received:
Accepted:
Published: