Abstract
Recently, layered two-dimensional ferromagnetic materials (2D FMs) have attracted a great deal of interest for developing low-dimensional magnetic and spintronic devices. Mechanically exfoliated 2D FMs were discovered to possess ferromagnetism down to monolayer. It is therefore of great importance to investigate the distinct magnetic properties at low dimensionality. Here, we report the wafer-scale growth of 2D ferromagnetic thin films of Fe3GeTe2 via molecular beam epitaxy, and their exotic magnetic properties can be manipulated via the Fe composition and the interface coupling with antiferromagnetic MnTe. A 2D layer-by-layer growth mode has been achieved by in situ reflection high-energy electron diffraction oscillations, yielding a well-defined interlayer distance of 0.82 nm along {002} surface. The magnetic easy axis is oriented along c-axis with a Curie temperature of 216.4 K. Remarkably, the Curie temperature can be enhanced when raising the Fe composition. Upon coupling with MnTe, the coercive field dramatically increases 50% from 0.65 to 0.94 Tesla. The large-scale layer-by-layer growth and controllable magnetic properties make Fe3GeTe2 a promising candidate for spintronic applications. It also opens up unprecedented opportunities to explore rich physics when coupled with other 2D superconductors and topological matters.
Similar content being viewed by others
Introduction
With the discovery of graphene and its astonishing physical properties,1 a new class of two-dimensional (2D) materials, ascribed to the dimensionality effect and modulation in their band structures, has become the focus of intense research which ranges from 2D semiconductors, like black phosphorous,2 MoS2,3 and WSe2,4,5,6 to 2D superconductors, for example, NbSe2,7, 8 and FeSe.9,10,11 The 2D ferromagnetic materials (2D FMs),12 were predicted to have promising spintronic applications13,14,15,16 with stable storage, faster response and low-power dissipation.12, 17 To this end, two approaches are currently adopted involving the introduction of defects or adatoms into parent materials or the proximity effect with ferromagnetic materials,18 for instance, the ferromagnetism in NbSe2 through hydrogen absorbed on the surface,19 and the search for the intrinsic magnetic materials. However, the resulting ferromagnetic materials by the former method significantly suffer from the undesired stability and limited controllability. To date, the predicted possible categories of 2D intrinsic FMs are mainly made up of Fe3GeTe2 20, 21 and CrXTe3 (X = Si, Sn, Ge)22,23,24 with the calculated Curie temperature of 220 K (bulk),25, 26 90 K (monolayer),24 170 K (monolayer),22 and 130 K (monolayer).24
Experimentally, some progress has been made. By reducing the sample thickness,18 V5S8 changes from antiferromagnetic to ferromagnetic states. Through previous ferromagnetic resonance (FMR) study,17 the exfoliated CrGeTe3 exhibits a Curie temperature around 61 K with an uniaxial magnetic property which can be tuned by external magnetic field.27 Even down to bilayer and monolayer, CrGeTe3, and CrI3 are still in the ferromagnetic state with a Curie temperature of 30 27 and 45 K,28 respectively, which is much lower than their bulk counterparts. Recently, the reported field-effect transistors based on ferromagnetic semiconductor C3N quantum dots (QDs)29 show an on–off ratio around 1010 with the tunable bandgap ranging from visible to infrared light for different-size QDs. However, the experimental progress in producing large-scale 2D FM thin films remains an obstacle. So far, the ferromagnetic single crystals such as Fe3GeTe2 and CrGeTe3 were mainly developed by chemical vapor transport (CVT).17, 25 Due to the van der Waals interaction between layers, these materials can be easily exfoliated by the Scotch-tape method, but yet, the resultant nano-devices are largely restricted by the sample size.30 Thus, the successful growth of large-scale 2D FM thin films becomes a thrust theme as it not only boosts the rapid exploration of physics but also renders the possibility to investigate various heterojunctions.12 For instance, by coupling with topological insulators, it is possible to probe quantized anomalous Hall effect and magnetic monopoles.31, 32 With superconductors, Andreev reflection effect7, 33 and the super-exchange interaction34, 35 can be investigated through the proximity effect. Besides the exotic physics, the molecular beam epitaxy (MBE) is well established in growing highly uniform and crystalline quality films. For the 2D materials, the thickness can be well controlled through the in situ reflection high-energy electron diffraction (RHEED) oscillations. These outstanding superiorities make MBE a desirable technique for producing wafer-scale-size films with well-defined thickness controllability.
Compared with other ferromagnetic materials such as CrSiTe3 and CrGeTe3, Fe3GeTe2 possesses outstanding properties. First, its superior stability is confirmed by the non-imaginary frequencies in phonon spectrum calculations.20 Indeed, the oxidation process of Fe3GeTe2 in our experiments is slower in comparison with CrGeTe3. Second, it is predicted to be an itinerant ferromagnet with a relatively high-Curie temperature around 220 K.26 Essentially, this becomes a very important figure of merit for spin-based technology architecture. Third, the anisotropy energy of Fe3GeTe2 around 107 erg/cm3 determined by magnetic force microscope36 is much larger than that of CrGeTe3 with 105 erg/cm3 measured with FMR,17 which is critical for magnetic tunnel junctions and magnetic random access memory devices. All of them require a large difference between anisotropy energy and thermal activation energy k B T for stable storage.20 In addition, the perpendicular magnetic anisotropy provides lower switching current in comparison with the in-plane one.37, 38
Here, we investigate 2D FM Fe3GeTe2 thin films grown on sapphire and GaAs by MBE. Periodic in situ RHEED oscillations clearly demonstrate the 2D growth mode through which the thickness of Fe3GeTe2 films can be precisely determined. Our low-temperature transport experiments unveil the out-of-plane easy axis along c direction with the Curie temperature of 216.4 K. And importantly, the Curie temperature is found to vary systematically with the Fe composition. By constructing a superlattice-like structure of (Fe3GeTe2/MnTe)3, where the subscript 3 means three periods of Fe3GeTe2/MnTe, the coercive field of Fe3GeTe2 increases 50%, exhibiting a tunable magnetic states.
Results and discussion
Two-inch high-crystalline-quality Fe3GeTe2 films were grown in a high-vacuum MBE system. Figure 1a shows the crystal structure geometry, which belongs to a space group P63/mmc. Each layer consists of five sublayers with sandwich-like stacking order. The lattice constants are a = b = 3.9536(7) Å and c = 16.396(2) Å. The top view displays a hexagonal distribution of atoms, as shown in the top panel of Fig. 1a. The inset of Fig. 1b exhibits a typical RHEED pattern obtained during the growth, where the streaky stripes suggest the atomically smooth surface and indicate the high-crystalline quality. These properties are further demonstrated by X-ray diffraction (XRD) and high-resolution transmission electron microscope (HRTEM). Figure 1b shows in situ RHEED oscillations and the equal periodicity provides a strong evidence of 2D growth mode. We note that it typically takes 111 s to complete one layer growth, suggesting that the thickness of Fe3GeTe2 films can be well controlled. Due to the low XRD intensity of 8 nm film, a thicker sample on sapphire under the same growth condition is used for the XRD measurements, as shown in Fig. 1c. According to PDF Card #75-5620 and the published XRD data of single crystals,26 peaks marked in red can be ascribed to a series of {002} planes—(002), (004), (008), (0010), and (0014), suggesting that Fe3GeTe2 is single crystalline and the growth is along c axis. Other peaks marked in blue are originated from the sapphire substrate. HRTEM experiments were further carried out to determine the layered structure of the Fe3GeTe2 film on (111) GaAs (Fig. 1d). The upper inset of Fig. 1d is the HRTEM taken from the Fe3GeTe2 region in which a van der Waals gap of 0.82 nm can be observed, corresponding to the (0002) displacing of Fe3GeTe2.20 Figure 1d shows the HRTEM image taken from the interface region between Fe3GeTe2 film and GaAs substrate, taken from GaAs {110} axis. The corresponding selected area electron diffraction (SAED) taken from the interface region is presented in Fig. 1e, from which the crystallographic relationship between the Fe3GeTe2 film and GaAs can be determined as {0001}Fe3GeTe2//{111}GaAs. Energy-dispersive X-ray spectroscopy (EDS) maps taken from the film region confirms the uniform elemental distribution of Fe, Ge, and Te in the film, as shown in Fig. 1f. With all the above characterizations, the Fe3GeTe2 thin films are found to grow uniformly on the substrate, and have a high-crystalline quality.
To explore low-temperature electrical properties, two-inch Fe3GeTe2 films were cut into small pieces and fabricated into a Hall-bar structure (Fig. 2a inset). Figure 2a shows the temperature-dependent resistance (R-T) data of 8 nm Fe3GeTe2 on Al2O3. Consistent with the theoretical predictions,21 with decreasing temperature the resistance decreases, showing a metallic behavior. However, upon reaching ~ 40 K, the R-T curve exhibits an upward increase. The inset shows a fit to the Mott’s variable range hopping (VRH) model yielding ln(R xx ) ~ T −1/3, where 1/3 is characteristic for 2D materials and it would be 1/4 for 3D materials, which means that at low temperatures the localized carriers hop to the lowest activation energy states other than the nearest-neighboring states. A similar transport behavior was also observed in other material systems.39,40,41
To investigate the ferromagnetic properties, a magnetic field up to ±9 T is scanned back and forth. Generally, the Hall effect of ferromagnetic materials can be described by42 R xy = R H B + R AH M, where R H stands for the normal Hall contribution, and R AH comes from the magnetization contribution. Subtracting the normal Hall slopes from the raw data yields the anomalous Hall signals that are also dependent on the angle between magnetic field (B) and the normal vector of the sample surface (Fig. 2b and inset). It is evident that the easy axis of Fe3GeTe2 is along c-axis (out-of-plane) as the coercive field (H c) increases simultaneously with the angle. When raising the temperature, H c decreases and will reach zero at the Curie temperature, as shown in Fig. 2c and e, respectively. Based on that, the Curie temperature can be roughly estimated. More precise determination of Curie temperature can be achieved by the Arrott-plot, as described later. At 2 K, the hole carrier density and mobility were extracted to be 1.2 × 1019 cm−3 and 54.9 cm2 V− 1 s− 1, respectively, as displayed in Fig. 2d.
To estimate the Curie temperature and compare it with that of the bulk crystal counterpart, the method of the Arrott-plot has been adopted.41 First (R xy /R xx 2)2 is plotted against B/(R xy /R xx 2). It is well known that the intercept is positive for ferromagnetic and negative for paramagnetic state.43 Then, the Curie temperature T c can be extracted when the intercept on the (R xy /R xx 2)2 axis goes to zero. Figure 3a shows (R xy /R xx 2)2 ~ B/(R xy /R xx 2) curves of 70, 100, 125, 150, 180, and 200 K, and the intercept, determined from these linear fittings (Fig. 3b), decreases when the temperature increases. Using a liner fit, the Curie temperature is determined to be 216.4 ± 0.4 K.
Superconducting quantum interference device (SQUID) was used to measure the magnetic properties. Since the easy axis of Fe3GeTe2 films is out-of-plane, the magnetic field is set to be perpendicular to the sample surface (perpendicular geometry). Figure 3c displays the Zero-field-cooling (ZFC) and field-cooling (FC) curves under 100 Oe for 8-nm Fe3GeTe2 grown on sapphire substrate. With decreasing the temperature, the magnetization under field-cooling process increases, showing an opposite trend to the ZFC curve. The Curie temperature can be roughly determined to be ~ 212.8 K, comparable to 216.4 K determined by transport Hall results. Magnetization hysteresis was achieved by scanning magnetic field back and forth in the region of ±3 Tesla at 10 K (Fig. 3d). Large diamagnetic background from Al2O3 can be clearly seen and subsequently subtracted to produce the net magnetization of Fe3GeTe2 thin films as displayed in Fig. 3d inset, with the saturation magnetization of 1.23 μB per Fe ion, smaller than that of bulk sample21, 25 ~ 1.6 μB. The shrinking behavior in the center region suggests the mixture signals from a harder magnetic phase and a slightly softer magnetic phase similar to that occurs in MnGe44 and [Co/Pd]IrMn,45 which were further proved by our Kerr microscope measurements. The detailed discussions and experimental results are provided in Supplementary information I and II.
Next, we attempt to manipulate the magnetic properties of Fe3GeTe2 thin films by systematically altering the Fe composition (Fe3+δ GeTe2) and by coupling with antiferromagnetic layer MnTe. As shown in Fig. 4, with increasing the Fe composition, the Curie temperature, extracted from the Arrott-plots (Supplementary Figs. 3–7), dramatically increases. Such a trend was also observed in Fe3+δ GeTe2 single crystals grown by self-flux reaction method,26 where the additional Fe doping decreases the lattice constant c while increases a.
Besides the control of the Fe composition, the heterostructure of Fe3GeTe2/MnTe was produced to enhance the magnetic properties via the exchange interaction from the FM/AFM interface. The detailed growth conditions and characterizations of MnTe itself are presented in Supplementary Fig. 9. The structure of MnTe is hexagonal NiAs-type46 with the lattice constants a = b = 4.158 Å and c = 6.726 Å. The matching of the crystal structures enables the possibility of in situ growing MnTe directly on Fe3GeTe2. More importantly, the magnetic structure of MnTe is featured by the Mn stacking antiferromagnetically along c-axis46 that is perfectly aligned with the easy axis of Fe3GeTe2. Given the fact that the Neel temperature of MnTe is 310 K, higher than the Curie temperature of Fe3GeTe2, we have designed several periods of Fe3GeTe2/MnTe and achieved such superlattices with atomically smooth interface using MBE (see the streaky RHEED patterns in Supplementary Fig. 10). From XRD, different sets of peaks from Fe3GeTe2, MnTe and substrate Al2O3 can be observed (Fig. 5a). Figure 5b shows the R-T curve of 3-period Fe3GeTe2/MnTe with a metallic R-T behavior. Then, the angle-dependent anomalous Hall effect measurements were measured to probe the easy axis (Supplementary Fig. 11(a)) which is found to be out-of-plane. Note that hereafter the ferromagnetism measurements were always taken under the perpendicular geometry. Figure 5c displays anomalous Hall data at different temperatures. The temperature dependence of the coercive field is similar to that from the pure Fe3GeTe2. However, remarkably the coercive field is significantly enhanced (Fig. 5d). The inset of Fig. 5d are the absolute difference and increment ratios which are all above 50 % at different temperatures. At 10 K, the difference of the coercive field is as high as 50 % from 0.65 to 0.94 Tesla.
Conventionally, when FM and AFM are coupled, the interface interaction can induce the exchange bias and the enhanced coercive field. For the exchange bias,47, 48 unlike the pure Fe3GeTe2 there will exist a shift of anomalous Hall data along x axis. To detect whether the exchange bias exists or not, we measured anomalous Hall data in the range of ±4 Tesla before which the sample is initially cooled down under ±5 Tesla from 350 K, well above the Neel temperature of MnTe. As shown in Figure S11(b)–S11(d), there is no signature of exchange bias at 10, 130, and 180 K, analogous to that occurred in Cr-(Bi,Sb)2Te3/CrSb superlattices,49 where the antiferromagnetic CrSb is magnetically ordered with spin texture altering from the bulk due to the interlay exchange coupling but without the interface exchange bias. Comparing these two systems, namely Fe3GeTe2/MnTe and Cr-(Bi,Sb)2Te3/CrSb, it is possible that the absence of the exchange bias in Fe3GeTe2/MnTe is associated with the magnetic order of MnTe (similar to CrSb), instead of antiferromagnetic state. However, such a detailed study requires neutron spectroscopy and polarized neutron reflectometry measurements that are beyond the current scope of the work.
In summary, with MBE we successfully grew wafer-scale 8 nm 2D ferromagnetic Fe3GeTe2 films. Anomalous Hall effect and butterfly-like magnetoresistance verify that the easy axis is out-of-plane. The Curie temperature of the thin film is 216.4 ± 0.4 K. Through Fe doping, the Curie temperature can be adjusted. Further combined with antiferromagnetic MnTe, the coercive field increases 50% at 10 K. With distinct magnetic properties, wafer-scale and tunable high-Curie temperature 2D FMs are promising for spintronic devices and for the study of the proximity effect when coupling with other 2D materials.
Methods
Thin film synthesis
Fe3GeTe2 thin films were grown on (0001) sapphire and (111) GaAs in a Perkin Elmer 430 MBE system with the base vacuum of 2.5 × 10−9 Torr. The substrates were cleaned using a general process before loaded into the chamber. The substrates were annealed at 600 °C for 30 min, and then decreased to the growth temperature of 340 °C. High-purity Fe (99.99%), Ge (99.999%), and Te (99.999%) at the temperature of 1165 °C, 1020 °C, and 285 °C, respectively, were co-evaporated from standard Knudsen cells. MnTe films were grown at the temperature of 320 °C with the Mn (99.99%) and Te (99.999%) cell temperature of 710 and 280 °C, respectively. The flux of each material is calibrated by the crystal oscillator. The MBE system is equipped with an in situ RHEED system.
Thin film characterizations
Structural characterizations of Fe3GeTe2 and MnTe thin films were carried out by X-ray diffraction (Bruker D8 Discover, Bruker Inc., Billerica, MA, USA) and TEM (FEI Tecnai F20) equipped with EDS. Sample composition and concentration were determined by EDS. Cross-section TEM sample was prepared by FIB (FEI Scios DualBeam).
Electrical and magnetization characterizations
The magneto-transport measurements were performed in physical properties measurement system (PPMS) by Quantum Design with a 9 T magnetic field. The devices were confined to the six-Hall-bar geometry. The data were collected using lock-in amplifiers (Stanford Research 830, Stanford Research Systems, Sunnyvale, CA, USA) in low frequency (<20 Hz). The magnetization measurements were accomplished in DC-superconducting quantum interface devices (SQUID) by quantum design with magnetic field up to 9 T.
Data availability
The authors declare that all the relevant data are available within the paper and its Supplementary Information file or from the corresponding author upon reasonable request.
Change history
25 October 2017
A correction to this article has been published and is linked from the HTML version of this article.
References
Zhang, Y., Tan, Y.-W., Stormer, H. L. & Kim, P. Experimental observation of the quantum Hall effect and Berry’s phase in graphene. Nature 438, 201–204 (2005).
Li, L. et al. Black phosphorus field-effect transistors. Nat. Nanotechnol. 9, 372–377 (2014).
Radisavljevic, B., Radenovic, A., Brivio, J., Giacometti, V. & Kis, A. Single-layer MoS2 transistors. Nat. Nanotechnol. 6, 147–150 (2011).
Jones, A. M. et al. Optical generation of excitonic valley coherence in monolayer WSe2. Nat. Nanotechnol. 8, 634–638 (2013).
Ross, J. S. et al. Electrically tunable excitonic light-emitting diodes based on monolayer WSe2 p-n junctions. Nat. Nanotechnol. 9, 268–272 (2014).
Wang, Z., Shan, J. & Mak, K. F. Valley- and spin-polarized Landau levels in monolayer WSe2. Nat. Nanotechnol. 12, 144–149 (2016).
Efetov, D. K. et al. Specular interband Andreev reflections at van der Waals interfaces between graphene and NbSe2. Nat. Phys. 12, 328–332 (2016).
Yokoya, T. et al. Fermi surface sheet-dependent superconductivity in 2H-NbSe2. Science 294, 2518–2520 (2001).
Hsu, F.-C. et al. Superconductivity in the PbO-type structure α-FeSe. Proc. Natl Acad. Sci. 105, 14262–14264 (2008).
Peng, R. et al. Tuning the band structure and superconductivity in single-layer FeSe by interface engineering. Nat. Commun. 5, 5044 (2014).
Qing-Yan, W. et al. Interface-Induced high-temperature superconductivity in single unit-cell FeSe films on SrTiO3. Chin. Phys. Lett. 29, 037402 (2012).
Park, J.-G. Viewpoint: opportunities and challenges of two-dimensional magnetic van der Waals materials: magnetic graphene? J. Phys. Condens. Matter 28, 301001 (2016).
Jongh, L. J. de. Magnetic properties of layered transition metal compounds. in Magnetic Properties of Layered Transition Metal Compounds (ed. Jongh, L. J. de) 1–51 (Springer Netherlands, 1990).
Wolf, S. A. et al. Spintronics: a spin-based electronics vision for the future. Science 294, 1488–1495 (2001).
Žutić, I., Fabian, J. & Das Sarma, S. Spintronics: fundamentals and applications. Rev. Mod. Phys. 76, 323–410 (2004).
Barnaś, J., Fuss, A., Camley, R. E., Grünberg, P. & Zinn, W. Novel magnetoresistance effect in layered magnetic structures: theory and experiment. Phys. Rev. B 42, 8110–8120 (1990).
Zhang, X. et al. Magnetic anisotropy of the single-crystalline ferromagnetic insulator Cr2Ge2Te6. Jpn. J. Appl. Phys. 55, 033001 (2016).
Niu, J. et al. Anomalous Hall effect and magnetic orderings in nano-thick V5S8. ArXiv161100584 Cond-Mat (2016).
Zhu, X. et al. Signature of coexistence of superconductivity and ferromagnetism in two-dimensional NbSe2 triggered by surface molecular adsorption. Nat. Commun. 7, 11210 (2016).
Zhuang, H. L., Kent, P. R. C. & Hennig, R. G. Strong anisotropy and magnetostriction in the two-dimensional Stoner ferromagnet Fe3GeTe2. Phys. Rev. B 93, 134407 (2016).
Zhu, J.-X. et al. Electronic correlation and magnetism in the ferromagnetic metal Fe3GeTe2. Phys. Rev. B 93, 144404 (2016).
Zhuang, H. L., Xie, Y., Kent, P. R. C. & Ganesh, P. Computational discovery of ferromagnetic semiconducting single-layer CrSnTe3. Phys. Rev. B 92, 035407 (2015).
Siberchicot, B., Jobic, S., Carteaux, V., Gressier, P. & Ouvrard, G. Band structure calculations of ferromagnetic chromium tellurides CrSiTe3 and CrGeTe3. J. Phys. Chem. 100, 5863–5867 (1996).
Li, X. & Yang, J. CrXTe 3 (X = Si, Ge) nanosheets: two dimensional intrinsic ferromagnetic semiconductors. J. Mater. Chem. C 2, 7071–7076 (2014).
Chen, B. et al. Magnetic properties of layered itinerant electron ferromagnet Fe3GeTe2. J. Phys. Soc. Jpn. 82, 124711 (2013).
May, A. F., Calder, S., Cantoni, C., Cao, H. & McGuire, M. A. Magnetic structure and phase stability of the van der Waals bonded ferromagnet Fe3-xGeTe2. Phys. Rev. B 93, 014411 (2016).
Gong, C. et al. Discovery of intrinsic ferromagnetism in 2D van der Waals crystals. ArXiv170305753 Cond-Mat (2017).
Huang, B. et al. Layer-dependent ferromagnetism in a van der Waals crystal down to the monolayer limit. ArXiv170305892 Cond-Mat (2017).
Yang, S. et al. C3N—A 2D crystalline, hole-free, tunable-narrow-bandgap semiconductor with ferromagnetic properties. Adv. Mater. n/a-n/a (2017). doi:10.1002/adma.201605625.
Song, X., Hu, J. & Zeng, H. Two-dimensional semiconductors: recent progress and future perspectives. J. Mater. Chem. C. 1, 2952–2969 (2013).
Yu, R. et al. Quantized anomalous hall effect in magnetic topological insulators. Science 329, 61–64 (2010).
Liu, M. et al. Crossover between weak antilocalization and weak localization in a magnetically doped topological insulator. Phys. Rev. Lett. 108, 036805 (2012).
Li, H. et al. The origin of bias independent conductance plateaus and zero bias conductance peaks in Bi2Se3/NbSe2 hybrid structures. ArXiv160707731 Cond-Mat (2016).
Hauser, J. J., Theuerer, H. C. & Werthamer, N. R. Proximity effects between superconducting and magnetic films. Phys. Rev. 142, 118–126 (1966).
Zhu, Y., Pal, A., Blamire, M. G. & Barber, Z. H. Superconducting exchange coupling between ferromagnets. Nat. Mater. 16, 195–199 (2016).
León-Brito, N., Bauer, E. D., Ronning, F., Thompson, J. D. & Movshovich, R. Magnetic microstructure and magnetic properties of uniaxial itinerant ferromagnet Fe3GeTe2. J. Appl. Phys. 120, 083903 (2016).
Sbiaa, R., Law, R., Tan, Ei-Leen. & Liew, T. Spin transfer switching enhancement in perpendicular anisotropy magnetic tunnel junctions with a canted in-plane spin polarizer. J. Appl. Phys. 105, 013910 (2009).
Sbiaa, R., Meng, H. & Piramanayagam, S. N. Materials with perpendicular magnetic anisotropy for magnetic random access memory. Phys. Status Solidi RRL 5, 413–419 (2011).
Ziqan, A. M., Qasrawi, A. F., Mohammad, A. H. & Gasanly, N. M. Thermally assisted variable range hopping in Tl4S3Se crystal. Bull. Mater. Sci. 38, 593–598 (2015).
Roy, A. et al. Structural and electrical properties of MoTe2 and MoSe2 grown by molecular beam epitaxy. ACS Appl. Mater. Interfaces 8, 7396–7402 (2016).
Bao, L. et al. Quantum corrections crossover and ferromagnetism in magnetic topological insulators. Sci. Rep. 3, 2391 (2013).
Nagaosa, N., Sinova, J., Onoda, S., MacDonald, A. H. & Ong, N. P. Anomalous hall effect. Rev. Mod. Phys. 82, 1539–1592 (2010).
Stolichnov, I. et al. Non-volatile ferroelectric control of ferromagnetism in (Ga,Mn)As. Nat. Mater. 7, 464–467 (2008).
Xiu, F. et al. Electric-field-controlled ferromagnetism in high-Curie-temperature Mn0.05Ge0.95 quantum dots. Nat. Mater. 9, 337–344 (2010).
Chesnel, K., Wilcken, B., Rytting, M., Kevan, S. D. & Fullerton, E. E. Field mapping and temperature dependence of magnetic domain memory induced by exchange couplings. New J. Phys. 15, 023016 (2013).
Kriegner, D. et al. Multiple-stable anisotropic magnetoresistance memory in antiferromagnetic MnTe. Nat. Commun. 7, 11623 (2016).
Nogués, J. & Schuller, I. K. Exchange bias. J. Magn. Magn. Mater. 192, 203–232 (1999).
Brown, H., Dahlberg, E. D. & Hou, C. Exchange bias measurements of CoFe/IrMn. J. Appl. Phys. 89, 7543–7545 (2001).
He, Q. L. et al. Tailoring exchange couplings in magnetic topological insulator/antiferromagnet heterostructures. Nat. Mater. 16, 94–100 (2016).
Acknowledgments
This work was supported by the National Key Basic Research Program (2017YFA0303302) and National Natural Science Foundation of China (61322407, 11474058, 61674040), as well as Australian Research Council. We thank Professor Yizheng Wu and Lu Sun for kind helps in Kerr microscope measurements. Part of the sample fabrication was performed at Fudan Nano-fabrication Laboratory.
Author information
Authors and Affiliations
Contributions
F.X. conceived the ideas and supervised the overall research. S.L. and X.Y. synthetized high-quality Fe3GeTe2 thin films. S.L. and W.W. fabricated the devices. S.L., C.H., E.Z., J.L., Y.L., and C.Z. carried out the PPMS measurement. S.L., Y.S., and K.W. analyzed the transport data. Y.Z. and J.Z. did the TEM characterization. S.L. and F.X. wrote the paper with assistance from all other authors.
Corresponding authors
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Change History:A correction to this article has been published and is linked from the HTML version of this article.
A correction to this article is available online at https://doi.org/10.1038/s41699-017-0039-x.
Electronic supplementary material
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Liu, S., Yuan, X., Zou, Y. et al. Wafer-scale two-dimensional ferromagnetic Fe3GeTe2 thin films grown by molecular beam epitaxy. npj 2D Mater Appl 1, 30 (2017). https://doi.org/10.1038/s41699-017-0033-3
Received:
Revised:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41699-017-0033-3
- Springer Nature Limited
This article is cited by
-
Interfacial magnetic spin Hall effect in van der Waals Fe3GeTe2/MoTe2 heterostructure
Nature Communications (2024)
-
Hard ferromagnetism in van der Waals Fe3GaTe2 nanoflake down to monolayer
npj 2D Materials and Applications (2024)
-
Two-dimensional magnetic materials for spintronic applications
Nano Research (2024)
-
Progress in the preparation and physical properties of two-dimensional Cr-based chalcogenide materials and heterojunctions
Frontiers of Physics (2024)
-
Interfacial engineering of ferromagnetism in wafer-scale van der Waals Fe4GeTe2 far above room temperature
Nature Communications (2023)