Abstract
The electric field manipulation of magnetic properties is currently of great interest for the opportunities provided in low-energy-consuming spintronics devices. Here, we report the effect of electric field on magnetic and transport properties of the ferromagnetic SrRuO3 film which is epitaxially grown on Pb(Mg1/3Nb2/3)O3-PbTiO3 ferroelectric substrate. With the application of electric field on the substrate, the magnetization, Curie temperature and resistivity of SrRuO3 are effectively modified. The mechanism of the electric field manipulation of these properties is ascribed to the rotations of RuO6 oxygen octahedra caused by the electric-field-induced strain, which changes the overlap and hybridization between the Ru 4d orbitals and O 2p orbitals, resulting in the modification of the magnetic and electronic properties.
Similar content being viewed by others
Introduction
Magnetoelectric (ME) heterostructures consisting of ferromagnetic and ferroelectric elements have aroused great interest in recent years for their rich coupling mechanisms and promising applications in next-generation electronic devices1,2,3,4,5,6. The ME effects can be classified as direct ME (DME) and converse ME (CME), which are characterized as magnetic-field-induced polarization and electric-field-induced magnetization, respectively. The CME effect, i.e. electric field control of magnetism, is now a research focus, since it can provide a low-consuming method to manipulate the magnetization1,3,4. Up to now, the most used CME mode is the strain-mediated coupling1,7. By depositing the ferromagnetic component on ferroelectric/piezoelectric substrate, the electric-field-induced strain can remarkably manipulate magnetization, giving rise to large ME effects8,9,10. Pb(Mg1/3Nb2/3)O3–PbTiO3(PMN-PT) and PbZrxTi1-xO3(PZT) are frequently selected as the ferroelectric/piezoelectric substrates due to their excellent piezoelectric and ferroelectric performance. As for the ferromagnetic components, magnetic perovskites are ideal candidates because they exhibit abundant physical properties and are easy to grow epitaxially on the ferroelectric substrates10,11,12,13. In magnetic-perovskite-based ME heterostructures, the magnetism can be manipulated by means of altering the magnetic anisotropy10, affecting the phase separation11,12, or adjusting the spin state of magnetic ions13 through the electric-field-induced strain. In addition to strain-mediated mechanism, ferroelectric field-effect14 may also plays a role in tuning magnetic and transport properties of magnetic perovskites in those ME heterostructures due to the accumulation or depletion of charge carries at interface through ferroelectric polarization reversal15,16,17. It is known that networks of corner-sharing oxygen octahedra play an important role in determining the magnetic and electronic properties of the perovskite through its deformations, rotations or tilts18,19,20. Recently, theoretical results based on the first-principles calculation point out that the magnetization can be controlled via octahedral rotations in a perovskite related oxide21. Since the oxygen octahedral rotations in perovskites can be manipulated by applying stress18, it may provide an opportunity to achieve CME effect in magnetic perovskites.
SrRuO3 (SRO) is a moderately correlated material and the only known 4d transition metal oxide with ferromagnetic order and metallic behavior, which has attracted an enormous amount of investigation for its intriguing magnetic and electronic properties22. The perovskite structure of SRO crystallizes in orthorhombic symmetry, exhibiting a GdFeO3-kind of distortion associated with rotation and tilt of RuO6 octahedra22. The manipulation of resistivity by ferroelectric field-effect has been reported in a SRO/PZT heterostructure, in which a 9% change of the resistivity upon reversing the ferroelectric polarization is observed23. However, there are few reports about the electric-field control of magnetization or resistivity in SRO film using strain-mediated mechanism. As we know, density-functional theory calculations have predicted that the magnetic moment is suppressed under compressive strain and enhanced with tensile strain for (001)-epitaxial SRO films due to the strain-induced oxygen octahedral rotations24. As for the experimental results, Gan et.al reported that, compared with the strain relaxed film, the saturation magnetic moment can be suppressed in the compressive SRO film25. Moreover, Terai et.al found that the Curie temperature (TC) of SRO is enhanced under tensile strain26. Up to now, most of the studies about the strain dependent of magnetic properties for SRO are focused on the films deposited on various substrates, in which the different strain states are attributed to the mismatch of lattice parameters27,28,29. Since the magnetic properties of these films are entangled with other factors such as non-stoichiometry, defects, impurities, interdiffusion with the substrate or surface morphology, it is not strict to isolate strain effects by comparing with each other22,30. However, depositing SRO film on the piezoelectric substrate can neglect these intricacies and provide an electric-field-controlled strain state in-situ, which is helpful to gain more insight on the strain impact on the magnetic properties of the film. In this paper, we deposit SRO film on PMN-PT substrate and investigate the electric field manipulation of magnetization and resistivity by applying an electric field on the piezoelectric single crystal. The experimental results show that not only the saturation magnetization but also TC can be affected by the electric field, showing an intrinsic CME effect. The effect of electric field on the resistivity further demonstrates the correlation between magnetic and electric properties of SRO film.
Results
The XRD θ-2θ scan of SRO/PMN-PT heterostructure is shown in Fig. 1(a). Obviously, only the diffraction peaks of substrate and film can be observed, suggesting the single phase and highly (001)-oriented nature of the film. Although the structure of PMN-PT crystal and bulk SRO are rhombohedral and orthorhombic respectively, they can be regarded as the pseudocubic structures with lattice parameters of aPMN-PT = 4.02 Å and aSRO = 3.93 Å. Due to the lattice mismatch (~2.3%) between SRO and PMN-PT, the SRO film is under the substrate-induced tensile strain along the in-plane direction. Besides the epitaxial growth, the surface morphology of the film is also important for the efficiency of strain transferred from the substrate to the film in strain-mediated ME heterostructures17. The AFM image exhibited in Fig. 1(b) with an area of 2 × 2 µm2 shows a rather smooth surface with the root mean square roughness about 0.4 nm. Therefore, the structural and morphological features of SRO film demonstrate a favorable condition for the following CME coupling measurements.
For investigating the effect of electric field on the magnetism, we measure the thermomagnetic curves for SRO film with or without electric field, where the applying magnetic field and electric field are 500 Oe and 8 kV/cm, respectively. As shown in Fig. 2, SRO film shows a typical ferromagnetic transition and the value of TC under zero electric field is around 117 K. With the application of electric field, an obvious suppression of the magnetization and a shift of TC are observed simultaneously. The upper inset of Fig. 2 shows the temperature dependence of the relative change of magnetization ΔM/M (ΔM/M = [M(E) − M(0)]/M(0), where M(E) and M(0) are the magnetization with and without electric field, respectively.). A negative CME effect with a peak value of −26.8% near 117 K is observed in SRO film by applying an electric field on the PMN-PT substrate. To further determine the variation of TC caused by the electric field, we extract TC from extrapolating the linear part of M2-T curve to M = 0 in a temperature range below TC31. As shown in the bottom inset of Fig. 2, TC shifts from 117 K to 115 K with an electric field of 8 kV/cm. According to the earlier reports8,9,10, the magnetization of the strain-mediated ME system is usually modified by altering the magnetic anisotropy, giving rise to an extrinsic CME effect. However, in the case of SRO/PMN-PT heterostructure, not only the magnetization but also TC varies with the electric field, suggesting that the CME effect in SRO film may have other coupling mechanism.
Figure 3 shows the magnetic hysteresis loops (M-H) at 115 K under the electric fields of zero and 12 kV/cm with the magnetic field parallel to the film surface and the schematic diagram of laminate structure and magnetic measurement is shown in the inset. It is obvious that both M-H curves show typical ferromagnetic character and are almost saturated under the magnetic field of 5 kOe. With the application of electric field, a noticeable separation of magnetization can be observed. The value of ΔM/M under the magnetic field of 5 kOe is about −8.6%. As we know, the modification of magnetic anisotropy can affect the magnetization, but cannot change the saturation magnetization. Therefore, the electric field would have an intrinsic effect on the magnetism of SRO film due to the change of saturation magnetization.
To further explore the origin of electric field control of magnetism in SRO/PMN-PT heterostructure, the relative change of magnetization ΔM/M as a function of bipolar electric field with a bias magnetic field of 500 Oe is measured at 115 K. As shown in Fig. 4(a), a hysteresis loop with a rather symmetric butterfly shape is observed, which is consistent with the shape of strain vs electric field hysteresis loop and different from that of polarization vs electric field hysteresis loop of the PMN-PT substrate17. Thus the observed electric field manipulation of magnetization in SRO/PMN-PT heterostructure would be ascribed to the electric-field-induced strain. When an electric field is applied on PMN-PT with the direction parallel to the polarization, the substrate would contract along the in-plane direction which causes the reduction of magnetization of the upper SRO layer about 9.2% under an electric field of 20 kV/cm. As the electric field reverse its direction, a tensile strain is produced, which leads to the enhancement of magnetization with a maximum value of about 6.7% at the coercivity field of 10.8 kV/cm. Compared with the earlier report about depositing SRO film on different substrates29, this method of controlling magnetism in SRO is adjustable and scalable, since the applying electric field can be continuously tuned and the value of generated stress is also countable32. After the substrate is poled with a positive electric field, the time dependence of magnetization and electric field is measured with a bias magnetic field of 500 Oe. As shown in Fig. 4(b), when an electric field of 12 kV/cm is applied, SRO film exhibits a low magnetization state of 0.139 μB/Ru. While the electric field turns off, it subsequently transforms into a high magnetization state of 0.149 μB/Ru. Furthermore, the magnetization of SRO film shows almost stable change after several cycles with the electric field switching on and off alternatively, suggesting that the magnetization of this heterostructure can be reversibly and reproducibly controlled by the electric field.
As mentioned above, SRO is a kind of moderately correlated material, in which the transport and magnetism are related with the conduction d band, leading to an intrinsic coupling between the magnetic and transport properties22. Therefore, the electric field would have influence on the transport properties of SRO film as well. Figure 5(a) shows the temperature dependence of resistivity for SRO film with and without electric fields and the schematic image of electric measurement is shown in the inset. Under zero electric field, the resistivity decreases almost linearly with the temperature cooling down from room temperature, exhibiting a typical behavior of “bad metal”33. When the temperature further decreases, a kink is observed around TC and the resistivity decreases rapidly below this temperature due to the loss of spin disorder scattering34. It is obvious that the resistivity of SRO film decreases in the measured temperature regions with the application of an electric field on PMN-PT substrate. We also measure the hysteresis loop of the relative change of resistivity ΔR/R (ΔR/R = [R(E) − R(0)]/R(0)) as a function of bipolar electric field at 115 K. As demonstrated in Fig. 5(b), ΔR/R exhibits a nearly symmetric butterfly shape with the variation of electric field, which is similar with the ΔM/M -E hysteresis loop, further suggesting that the electric field modulation of the resistivity stems from the electric-field-induced strain as well. Under the compressive strain, the resistivity of SRO film decreases about 1.3% at an electric field of 20 kV/cm. While the tensile strain is found to increase the resistivity with a maximum value about 1.1% at the coercivity field of 10 kV/cm. The resistivity response to the variation of electric field as a function of time for SRO film is also measured at 115 K with the substrate poled under a positive electric field. As shown in Fig. 5 (c), the resistivity reduces with the electric field switching on and restores its initial state immediately with the electric field switching off, showing a same behavior with that of magnetization. The reversible modulation of the resistivity ΔR/R is about −0.5% with an applied field of 6 kV/cm.
Discussion
It is well accepted that there is a rather strong hybridization between the Ru 4d orbitals and O 2p orbitals of SRO, leading to a ferromagnetic ground state35,36. However, in the case of CaRuO3, it possesses the same structure as that of SrRuO3, but has larger rotations of the RO6 oxygen octahedra, which results in a paramagnetic ground state37. This fact suggests that the octahedral rotations and tilts play a key role in determining the magnetic state of ARuO3 (A = Ca, Sr) system and the magnetic properties of them can be adjusted through modulation of the hybridization between the Ru 4d and O 2p states by structural distortions19. In SRO/PMN-PT heterostructure, when an electric field is applied with the direction parallel to the polarization, the PMN-PT substrate would contract along in-plane direction and weaken the as-grown tensile strain. As illustrated in Fig. 6, in order to adapt this contraction, the RuO6 octahedral rotation angle of SRO film would enlarge correspondingly, giving rise to the enhancement of the overlap and hybridization between the Ru 4d orbitals and O 2p orbitals18,19,38. Therefore, the magnetic interaction would reduce36,39, which leads to the decrease of magnetization and TC, showing an intrinsic CME effect.
Since the strain, ΔM/M and ΔR/R have the similar electric-field dependence, we can assume that the magnetization and resistivity change linearly with the strain. When an electric field of 8 kV/cm is applied, an in-plane compression of about 0.1% is generated11, leading to the decrease of TC of SRO film for about 2 K, as shown in Fig. 2. This result is comparable with that reported by Terai et.al26, where the strain of 0.25% results in the variation of TC for about 4 K for SRO film grown on Ba1-xSrxTiO3/BaTiO3 buffer layers. As for the magnetization, the saturation magnetization of SRO film decreases about 8.6% near TC under an electric field of 12 kV/cm (about 0.12% compressive strain32), corresponding to about 71.7% reduction of magnetization under 1% compressive strain. This result is dramatically larger than that reported by Gan et.al25, in which the saturation magnetization of SRO decreases about 20% under a 0.67% compressive strain at 10 K. The larger effect of elastic strain on saturation magnetization in our sample reflects that the magnetism of SRO film responds more sensitive to the strain near TC, as revealed in the upper inset of Fig. 2.
The electric field manipulation of resistivity can also be attributed to the oxygen octahedral rotations caused by the strain. In order to accommodate the electric-field-induced strain, the Ru-O-Ru bond angles, which is determined by the rotation of the oxygen octahedra, would change and the overlap between the Ru 4d states and O 2p states would enhance correspondingly18,40. As a result, the variation of the Ru-O-Ru bond angles affects the electron hopping matrix elements while the enhanced orbital overlap broadens the electron bandwidth and reduces the correlation effect, leading to the decrease of resistivity36,40,41.
In conclusion, the electric field control of magnetic and transport properties of SRO/PMN-PT heterostructure have been investigated. We demonstrate that the saturation magnetization, TC and resistivity of SRO film can be manipulated with the application of electric field. Moreover, the magnetization and resistivity can be controlled reversibly and reproducibly with in situ electric field. The observed CME effect in SRO/PMN-PT heterostructure can be understood in the scenario of electric-field-induce strain modulates the hybridization between the Ru 4d orbitals and O 2p orbitals through altering the octahedral rotations. This result suggests an alternative mechanism for intrinsic CME effect in perovskite films through controlling octahedral rotations. The electric field control of magnetic and transport properties in SRO/PMN-PT heterostructure provide a potential application in low-energy-consuming spintronics devices.
Methods
SRO film with thickness about 300 nm was deposited on polished (001)-oriented PMN-PT substrate with dimensions of 5 × 5 × 0.5 mm3 by pulsed laser deposition method with a 248 nm KrF excimer laser. During the growth, the substrate temperature was 700°C and the background oxygen pressure was 13 Pa. After deposition, the film was cooled down in oxygen of 2 × 104 Pa. X-ray diffraction (XRD) and atomic force microscopy (AFM) measurements were performed to characterize the structure and surface topography of the film. To conduct the investigation of electric field on magnetic and transport properties in situ, Au layer was sputtered on the backside of the PMN-PT substrate as bottom electrode while the conducting SRO layer acts as top electrode. The PMN-PT substrate was poled at 350 K under an electric field of 8 kV/cm for 30 min. before measuring the CME effect. The magnetic properties were measured with a magnetic property measurement system (MPMS, Quantum Design) and the transport properties were measured by four probes method with a physical property measurement system (PPMS, Quantum Design). Electric voltage was applied in situ by a source meter (Keithley, model 2410).
References
Ma, J., Hu, J. M., Li, Z. & Nan, C. W. Recent Progress in Multiferroic Magnetoelectric Composites: from Bulk to Thin Films. Adv. Mater. 23, 1062–1087 (2011).
Eerenstein, W., Mathur, N. D. & Scott, J. F. Multiferroic and magnetoelectric materials. Nature 442, 759–765 (2006).
Wu, S. et al. Reversible electric control of exchange bias in a multiferroic field-effect device. Nature Mater. 9, 756–761 (2010).
Bibes, M. & Barthélémy, A. Towards a magnetoelectric memory. Nature Mater. 7, 425–426 (2008).
Wang, Y. et al. An extremely low equivalent magnetic noise magnetoelectric sensor. Adv. Mater. 23, 4111–4114 (2011).
Nan, C.-W., Bichurin, M., Dong, S., Viehland, D. & Srinivasan, G. Multiferroic magnetoelectric composites: historical perspective, status and future directions. J. Appl. Phys. 103, 031101 (2008).
Vaz, C. A. F. Electric field control of magnetism in multiferroic heterostructures. J. Phys.: Condens. Matter. 24, 333201 (2012).
Liu, M. et al. Giant electric field tuning of magnetic properties in multiferroic ferrite/ferroelectric heterostructures. Adv. Funct. Mater. 19, 1826–1831 (2009).
Buzzi, M. et al. Single domain spin manipulation by electric fields in strain coupled artificial multiferroic nanostructures. Phys. Rev. Lett. 111, 027204 (2013).
Yang, Y. et al. Large anisotropic remnant magnetization tunability in (011)-La2/3Sr1/3MnO3/0.7Pb(Mg2/3Nb1/3)O3-0.3PbTiO3 multiferroic epitaxial heterostructures. Appl. Phys. Lett. 100, 043506 (2012).
Chen, Q. et al. Electric-field control of phase separation and memory effect in Pr0.6Ca0.4MnO3/Pb(Mg1/3Nb2/3)0.7Ti0.3O3 heterostructures. Appl. Phys. Lett. 98, 172507 (2011).
Zheng, M. et al. Coupling of magnetic field and lattice strain and its impact on electronic phase separation in La0.335Pr0.335Ca0.33MnO3/ferroelectric crystal heterostructures. Appl. Phys. Lett. 103, 263507 (2013).
Zhang, Q. M. et al. The electric field manipulation of magnetization in La1−xSrxCoO3/Pb(Mg1/3Nb2/3)O3-PbTiO3 heterostructures. Appl. Phys. Lett. 104, 142409 (2014).
Ahn, C. H., Triscone, J.-M. & Mannhart, J. Electric field effect in correlated oxide systems. Nature 424, 1015–1018 (2003).
Molegraaf, H. J. A. et al. Magnetoelectric effects in complex oxides with competing ground states. Adv. Mater. 21, 3470–3474 (2009).
Zhu, Q. X. et al. Coaction and competition between the ferroelectric field effect and the strain effect in Pr0.5Ca0.5MnO3 film/0.67Pb(Mg1/3Nb2/3)O3-0.33PbTiO3 crystal heterostructures. Appl. Phys. Lett. 101, 172906 (2012).
Jiang, T. et al. Coaction and distinguishment of converse piezoelectric and field effects in La0.7Ca0.3MnO3/SrTiO3/0.68Pb(Mg1/3Nb2/3)O3-0.32PbTiO3 heterostructures. Appl. Phys. Lett. 103, 053504 (2013).
Vailionis, A. et al. Misfit strain accommodation in epitaxial ABO3 perovskites: Lattice rotations and lattice modulations. Phys. Rev. B 83, 064101 (2011).
He, J., Borisevich, A., Kalinin, S. V., Pennycook, S. J. & Pantelides, S. T. Control of octahedral tilts and magnetic properties of perovskite oxide heterostructures by substrate symmetry. Phys. Rev. Lett. 105, 227203 (2010).
Lu, W., Yang, P., Song, W. D., Chow, G. M. & Chen, J. S. Control of oxygen octahedral rotations and physical properties in SrRuO3 films. Phys. Rev. B 88, 214115 (2013).
Benedek, N. A. & Fennie, C. J. Hybrid improper ferroelectricity: a mechanism for controllable polarization-magnetization coupling. Phys. Rev. Lett. 106, 107204 (2011).
Koster, G. et al. Structure, physical properties and applications of SrRuO3 thin films. Rev. Mod. Phys. 84, 253 (2012).
Ahn, C. H. et al. Ferroelectric field effect in ultrathin SrRuO3 films. Appl. Phys. Lett. 70, 206–208 (1997).
Zayak, A., Huang, X., Neaton, J. & Rabe, K. M. Structural, electronic and magnetic properties of SrRuO3 under epitaxial strain. Phys. Rev. B 74, 094104 (2006).
Gan, Q., Rao, R., Eom, C., Garrett, J. & Lee, M. Direct measurement of strain effects on magnetic and electrical properties of epitaxial SrRuO3 thin films. Appl. Phys. Lett. 72, 978–980 (1998).
Terai, K., Ohnishi, T., Lippmaa, M., Koinuma, H. & Kawasaki, M. Magnetic properties of strain-controlled SrRuO3 thin films. Jpn. J. Appl. Phys. 43, L227 (2004).
Wang, X. et al. Magnetic anisotropy and transport properties of 70 nm SrRuO3 films grown on different substrates. J. Appl. Phys. 109, 07D707 (2011).
Gu, M. et al. Magnetic Ordering and Structural Phase Transitions in a Strained Ultrathin SrRuO3/SrTiO3 Superlattice. Phys. Rev. Lett. 109, 157003 (2012).
Grutter, A., Wong, F., Arenholz, E., Liberati, M. & Suzuki, Y. Enhanced magnetization in epitaxial SrRuO3 thin films via substrate-induced strain. J. Appl. Phys. 107, 09E138 (2010).
Siemons, W. et al. Dependence of the electronic structure of SrRuO3 and its degree of correlation on cation off-stoichiometry. Phys. Rev. B 76, 075126 (2007).
Thiele, C., Dörr, K., Bilani, O., Rödel, J. & Schultz, L. Influence of strain on the magnetization and magnetoelectric effect in La0.7A0.3MnO3/PMN-PT (001)(A = Sr, Ca). Phys. Rev. B 75, 054408 (2007).
Biegalski, M. D., Doerr, K., Kim, D. H. & Christen, H. M. Applying uniform reversible strain to epitaxial oxide films. Appl. Phys. Lett. 96, 151905 (2010).
Klein, L. et al. Anomalous spin scattering effects in the badly metallic itinerant ferromagnet SrRuO3 . Phys. Rev. Lett. 77, 2774 (1996).
Wu, X., Foltyn, S., Dye, R., Coulter, Y. & Muenchausen, R. Properties of epitaxial SrRuO3 thin films. Appl. Phys. Lett. 62, 2434–2436 (1993).
Singh, D. J. Electronic and magnetic properties of the 4d itinerant ferromagnet SrRuO3 . J. Appl. Phys. 79, 4818–4820 (1996).
Mazin, I. & Singh, D. J. Electronic structure and magnetism in Ru-based perovskites. Phys. Rev. B 56, 2556 (1997).
Khalifah, P., Ohkubo, I., Christen, H. M. & Mandrus, D. Evolution of transport and magnetic properties near the ferromagnetic quantum critical point in the series CaxSr1− xRuO3 . Phys. Rev. B 70, 134426 (2004).
Grutter, A., Wong, F., Arenholz, E., Vailionis, A. & Suzuki, Y. Evidence of high-spin Ru and universal magnetic anisotropy in SrRuO3 thin films. Phys. Rev. B 85, 134429 (2012).
Middey, S., Mahadevan, P. & Sarma, D. Dependence of magnetism on GdFeO3 distortion in the t2g system ARuO3 (A = Sr, Ca). Phys. Rev. B 83, 014416 (2011).
Vailionis, A., Siemons, W. & Koster, G. Room temperature epitaxial stabilization of a tetragonal phase in ARuO3 (A = Ca and Sr) thin films. Appl. Phys. Lett. 93, 051909 (2008).
Lu, W. et al. Effect of oxygen vacancies on the electronic structure and transport properties of SrRuO3 thin films. J. Appl. Phys. 113, 17E125 (2013).
Acknowledgements
This work was supported by the National Basic Research Program of China (Nos. 2012CB932304 and 2014AA032904) and National Natural Science Foundation of China (Grant Nos. 11174130 and U1232210).
Author information
Authors and Affiliations
Contributions
W.P.Z. and D.H.W. designed the experiments. W.P.Z., Q.L., Y.Q.X., Q.M.Z. and L.Y.L. carried out the magnetic and transport measurements. The date were collected by W.P.Z. Results were analyzed and interpreted by W.P.Z., D.H.W., Q.Q.C. and Y.W.D. The manuscript was written by W.P.Z. and D.H.W.
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Rights and permissions
This work is licensed under a Creative Commons Attribution-NonCommercial-NoDerivs 4.0 International License. The images or other third party material in this article are included in the article's Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder in order to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by-nc-nd/4.0/
About this article
Cite this article
Zhou, W., Li, Q., Xiong, Y. et al. Electric field manipulation of magnetic and transport properties in SrRuO3/Pb(Mg1/3Nb2/3)O3-PbTiO3 heterostructure. Sci Rep 4, 6991 (2014). https://doi.org/10.1038/srep06991
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep06991
- Springer Nature Limited
This article is cited by
-
Large magnetoelectric coupling in multiferroic oxide heterostructures assembled via epitaxial lift-off
Nature Communications (2020)
-
Reversible manipulation of the magnetic state in SrRuO3 through electric-field controlled proton evolution
Nature Communications (2020)
-
Photostriction of strontium ruthenate
Nature Communications (2017)
-
Electrical modulation of magnetism in multiferroic heterostructures at room temperature
Journal of Materials Science (2017)
-
Modulation of metal-insulator transitions by field-controlled strain in NdNiO3/SrTiO3/PMN-PT (001) heterostructures
Scientific Reports (2016)