Abstract
Memory effect of electric-field control on magnetic behavior in magnetoelectric composite heterostructures has been a topic of interest for a long time. Although the piezostrain and its transfer across the interface of ferroelectric/ferromagnetic films are known to be important in realizing magnetoelectric coupling, the underlying mechanism for nonvolatile modulation of magnetic behaviors remains a challenge. Here, we report on the electric-field control of magnetic properties in wide-band (011)-Pr0.7Sr0.3MnO3/0.7Pb(Mg1/3Nb2/3)O3-0.3PbTiO3 heterostructures. By introducing an electric-field-induced in-plane anisotropic strain field during the cooling process from room temperature, we observe an in-plane anisotropic, nonvolatile modulation of magnetic properties in a wide-band Pr0.7Sr0.3MnO3 film at low temperatures. We attribute this anisotropic memory effect to the preferential seeding and growth of ferromagnetic (FM) domains under the anisotropic strain field. In addition, we find that the anisotropic, nonvolatile modulation of magnetic properties gradually diminishes as the temperature approaches FM transition, indicating that the nonvolatile memory effect is temperature dependent. By taking into account the competition between thermal energy and the potential barrier of the metastable magnetic state induced by the anisotropic strain field, this distinct memory effect is well explained, which provides a promising approach for designing novel electric-writing magnetic memories.
Similar content being viewed by others
Introduction
With the rapid increasing requirements for information storage, developing compact, innovative devices that offer fast, energy-efficient nonvolatile random access memory is becoming a significant and challenging task. To meet this challenge, a new way to control magnetism via electric fields1,2,3, using the converse magnetoelectric (ME) effect, rather than electric currents or magnetic fields, is attracting tremendous attention. Initial research suggests that the top candidates for realizing electric-field control of magnetism are single-phase multiferroic materials with simultaneous magnetic and ferroelectric orders; however, more recent experiments show that these materials have small converse ME effects and are unsuited to practical application4. As an alternative, artificial multiphase systems that consist of both ferromagnetic (FM) and ferroelectric (FE) materials are receiving more attention in recent years1,2,3. Coupling of the two ferroic phases suggests that an electric field may be able to control magnetic properties. Previous experimental work has demonstrated that an electric field can control magnetic anisotropy and remnant magnetization by using strain-mediated ME coupling in heterostructures with FM films grown on FE substrates such as epitaxial La0.67Sr0.33MnO3/BiTiO34, La2/3Sr1/3MnO3/PMN-PT5, polycrystalline Ni/PMN-PT, Fe3O4/PZNPT, CoFe2O4/PMN-PT and CoFe/BiFeO36,7,8,9. For the most part, these studies used the linear-converse piezoelectric response to induce changes in magnetic anisotropy and remnant magnetization, which typically return to their initial state once the driving electric field is removed. However, a nonvolatile tuning of the magnetic state by the electric field, namely the memory effect, is required for information storage.
Perovskite manganites contain rich physical phenomena: the Jahn-Teller (JT) distortion, double-exchange coupling, metal-insulator transition and phase separation due to the strong interplay among lattice, charge, spin and orbital degrees of freedom. Meanwhile, the lattice strain can modulate most of these properties by modifying MnO6-octahedron distortion and thus the strength of the double-exchange interaction and the JT coupling10,11. Especially, due to the strong coupling between lattice and spin, an electric field is able to control the magnetic properties of manganite films through the converse piezoelectric effect or the polarizing effect of the FE substrate2. It is well accepted that heterostructures composed of piezoelectric oxide and manganite film are a promising platform for studying strain-mediated ME coupling, either for revealing fundamental principles or for exploring new functional devices. Recently, Chen et. al12 observed a nonvolatile memory effect of ME coupling/strain in narrow-band, phase-separated Pr0.6Ca0.4MnO3(PCMO)/PMN-PT heterostructures and demonstrated that the electric-field control of magnetization is dominated by the change of phase separation in PCMO, which is nonvolatile and manifests a memory effect of ME coupling. It was assumed that such a nonvolatile magnetic memory effect was due to the modulated energy balance between coexisting FM and charge-ordered antiferromagnetic (COAFM) phases in the phase-separated manganite system.
Here, we report a memory effect of ME coupling in the heterostructure composed of a wide-band Pr0.7Sr0.3MnO3 (PSMO) manganite film grown on (011)-oriented 0.7Pb(Mg1/3Nb2/3)O3-0.3PbTiO3 (PMN-PT) substrate. Heterostructures were fabricated by using the pulsed-laser deposition (PLD) technique. The PSMO thin film was used as a model system because of its relatively large eg bandwidth with trivial phase separation and optimized metal-insulator/ferromagnetism-paramagnetism transition temperature16. In the absence of Sr doping, the Pr0.7Ca0.3MnO3 system has a narrow, one-electron eg bandwidth and exhibits strong COAFM13. When Ca is successively substituted by Sr, the average ion radius is altered14 because Sr ions are larger, leading to an increase in electron bandwidth (W) and hence the hopping amplitude for electrons in the eg band. Such an increase in W stabilizes the FM state by enhancing the double-exchange (DE) interaction and hence favors the FM-metallic state over the COAFM state. As a result, the system behaves strong phase-separation when Ca is partially substituted by Sr. However, in the case of a full substitution (i.e. Pr0.7Sr0.3MnO3), the COAFM state and phase separation become trivial while the FM-metallic state due to DE interaction dominates the transport process15. The (011)-oriented PMN-PT single crystal was chosen as the substrate because of its perovskite-cubic structure (aPMN-PT = 4.017 Å) and excellent anisotropic transverse piezoelectric effect17,18,19. The (011)-cut PMN-PT single-crystal slab behaves opposite piezoelectric behavior in the in-plane [100] and directions when an electric field is applied along the out-plane [011] crystalline direction, which could generate in-plane compressive stress along [100] and tensile stress along 18 This strong in-plane anisotropic piezoelectric effect provides an exceptional opportunity for generating a large in-plane anisotropic strain in the epitaxially grown PSMO film on the PMN-PT substrate. Thus, a different electric-field-tuning magnetic memory effect due to the large in-plane anisotropic strains may be expected in the two in-plane directions.
In this study, by introducing an in-plane anisotropic strain field using the converse piezoelectric effect of the substrate, we observed an in-plane anisotropic, nonvolatile change of magnetization in the low-temperature FM states. More interestingly, these anisotropic modulations of magnetization persisted after the removal of the electric field (anisotropic strain-field) at low temperatures, indicating a nonvolatile magnetic memory effect in the wide-band PSMO film. Our analysis reveals that the preferential seeding and growth of FM domains, driven by the anisotropic strain field during the formation of FM ordering, lead to an induced-magnetic anisotropy in the FM film. After the electric filed is removed, this induced-anisotropy field results in a metastable magnetic state, which accounts for the nonvolatile memory effect in the wide-band PSMO film. Furthermore, we found that this anisotropic memory effect of ME coupling gradually disappears when the temperature approaches the metal-insulator transition, which can be ascribed to the collapse of the metastable magnetic state caused by increasing thermal energy. Our results clearly evidence that an electric-field-induced anisotropic strain can lead to a nonvolatile magnetic memory effect by forming a metastable magnetic state in a wide-band manganite, where phase separation is trivial. The competition between the barrier energy of the metastable magnetic state and the thermal energy is responsible for the observed temperature-dependent memory effect of ME coupling.
Results
The out-of-plane interplanar distance and hence the out-of-plane epitaxial strain of the film were determined by means of x-ray diffraction (XRD) using Cu-Kα radiation. The XRD θ-2θ scan of the (011)-PSMO/PMN-PT heterostructure shows that the film is highly oriented along the [011] direction in the absence of any other impurity phases or textures (Fig. 1(a)). The out-of-plane interplanar distance was found to be ~2.727 Å, which is smaller than the bulk value20, indicating an out-of-plane compressive strain (~−0.3%). X-ray reciprocal space maps (RSMs) around asymmetric reflections were collected by a four-circle diffractometer to determine in-plane epitaxial strains of the film. Fig. 1(b) and (c) display the RSMs around (013) and (222) reflections. The extracted in-plane lattice constants of d100 and d01-1 for the film were 3.874 Å and 2.745 Å, respectively, which is slightly larger than those of bulk PSMO (3.857 and 2.735 Å, Ref. 20). The corresponding in-plane strains are tensile: 0.44% and 0.36% for [100] and directions, respectively. We examined the performance of the PMN-PT substrate and found that applying an electric bias of ±6 kV/cm along [011] can induce a large compressive strain (~−0.31%) along in-plane [100] and a very small tensile strain (~0.018%) along in-plane due to the large anisotropic piezoelectric effect of (011)-cut PMN-PT21, which can transfer to the overlying PSMO film19. The superimposed effect of lattice strains from both the epitaxial growth and the inverse piezoelectric effect cause the PSMO film to undergo a strong anisotropic tensile strain field along the two in-plane directions under ±6 kV/cm bias (i.e., ~0.13% for [100] and ~0.38% for ). Under such in-plane anisotropic tensile strain, a considerable and different bending condition of Mn-O-Mn bonds along two in-plane directions is expected, which will cause anisotropic response in magnetic properties.
We firstly measured the temperature-dependent resistance for PSMO bulk (Fig. 2 (a)) and 100-nm film (Fig. 2 (b)) on PMN-PT (along two perpendicular in-plane directions) in the absence of magnetic or electric fields. Fig. 2(a) shows that PSMO bulk exhibits zero thermal hysteresis around the metal-insulator transition, indicating that the double-exchange interaction dominates the transport process while phase separation behaves trivial, in accordance with previous reports13,14,15. Meanwhile, Fig. 2 (b) shows that the 100-nm film maintains the same features for both in-plane directions. However, the metal-insulator transition temperature (TMI) of the film decreased by ~24 K and ~29 K for in-plane [100] and directions, respectively, in comparison with that in the bulk PSMO. This decrease can be attributed to an introduced epitaxial tensile strain in the film that could enhance the JT electron-phonon coupling and consequently favors the formation of a small polaron10,11. Furthermore, a small but distinct difference in the in-plane magnetic states is also observed in the two in-plane directions. The inset of Fig. 2(b) displays the magnetic hysteresis loops of the film measured along both in-plane directions at 100 K. Both the remnant magnetization (Mr) and coercive field (HC) in the [100] direction are larger than those in the direction, indicating that magnetization prefers to align in the [100] direction. This magnetic anisotropy should be induced by the small anisotropic epitaxial strain22.
The influence of the electric field, piezoelectric strain on magnetic hysteresis (M-H) loops of the film was further investigated for both in-plane [100] and directions at different temperatures (Fig. 3). The samples were first cooled down to the target temperatures with a +7.8 kV/cm electric field and a zero magnetic field, then the M-H loops were measured under the same E-field (+7.8 kV/cm) (red curve) and zero E-field (green curve). To clearly demonstrate the effect of the strain or E-field, the M-H loops were also measured under zero electric field at the same temperatures after the sample was cooled under zero electrical and magnetic fields (black curve). Fig. 3(a) and (b) show the results measured at 100 K for [100] and directions, respectively. Clearly, the modulation of magnetization behaves very differently under the same electric field for the two perpendicular in-plane directions at 100 K. In comparison with the zero field pre-cooling loop (black curve), the saturation magnetization, coercivity and remanence of the +7.8 kV/cm electric field pre-cooling loop reduced significantly in the [100] direction. More importantly, the overall behavior of the loop also changed dramatically by becoming less square (red curve). Whereas for the direction, the opposite trend was observed (the loop becomes more square). The modulation effect in magnetic properties can be partially reflected by the ratio of remnance, denoted as (Mr(E)-Mr(0))/Mr(0), for both in-plane directions. Under a +7.8 kV/cm electric field, the ratios are about -54.9% and 23.3% for [100] and , respectively. The coercivity in the two directions also behaves differently with an applied electric field (it decreases by 100Oe at [100] and increases by 46Oe at , respectively). Such an anisotropic control of the magnetic properties is likely related to the efficient magnetic anisotropy induced by the electric bias. Considering that a relatively large tensile strain in the direction is induced by the applied electric field, as we mentioned above, to reduce the total energy, the FM domains prefer to grow along the direction during the formation of magnetic ordering in the cooling process from the PM state. Therefore, the elongated FM-metallic domains are formed with magnetization along 22,23, which generates an effective in-plane magnetic anisotropy and consequently reorients the easy axis towards the direction. This induced magnetic anisotropy increases both the remnant magnetization and coercivity in the direction but reduces them in the [100] direction as shown in Fig. 3(a) and (b), respectively. It should be noted that the in-plane anisotropic strain field causes different bending of Mn-O-Mn bonds along the two in-plane directions. As a result, a strong overlap of the electronic clouds may occur in the direction with relatively large tensile strain (i.e. ), which will strengthen the FM double-exchange interaction along direction and contribute to the in-plane magnetic anisotropy.
Interestingly, the M-H loops behaved similarly after the removal of the electric field at 100 K for both in-plane directions (the green and red curves overlap). This observation indicates that the modulation of the magnetic properties by the electric-field-induced in-plane anisotropic strain is nonvolatile at 100 K, a temperature far below the TMI/TC transition (see Fig. 2(b)). In other words, the film remembers the effect of the anisotropic strain on the magnetic properties and maintains the states even after the large in-plane anisotropic strain disappears along with the removal of the electric field. Such a nonvolatile modulation of magnetization in a wide-band manganite has not yet been reported and, therefore, deserves further investigation.
Fig. 3(c) and (d) show the M-H loops measured at 200 K approaching the TMI/TC. A similar but much less pronounced effect are observed in comparison with the data obtained at 100 K. With an applied electric field of +7.8 kV/cm, the ratio of (Mr(E)-Mr(0))/Mr(0) are −41.9% and 22.7% for the [100] and directions, respectively, whereas the coercivity decreases by 27Oe at [100] and increases by 32Oe at . The less pronounced effect may be explained by the fact that at 200 K, the spins are not fully ordered ferromagnetically due to strong thermal agitation (see Fig. 4). More interestingly, the modulation of both the remnant magnetization and coercivity caused by the in-plane anisotropic strain disappears after the electric field is removed and hysteresis loops restore their original behavior—that measured at zero electric field upon pre-cooling without any electric or magnetic fields (green and black curves nearly coincide). This indicates that the electric field control on the magnetic properties at 200 K is volatile (i.e. the memory effect observed at low temperatures disappears as the temperature approaches TMI/TC). Such a temperature-dependent memory effect seems similar to that reported in the phase-separated (001)-Pr0.6Ca0.4MnO3/PMN-PT heterostructure12, in which the energy landscape of the phase-separation states plays a dominating role in the memory effect. However, here the wide-band PSMO film shows only trivial phase separation, indicating that an alternative mechanism must be invoked for the observed memory effect.
To better understand the role of temperature in electric field control of magnetic properties; in particular to explore the underlying mechanism of the memory effect in the strain-mediated ME coupling of the wide-band (011)-PSMO/PMN-PT heterostructure, we measured the temperature dependent magnetization (M-T) curves along both [100] and directions (Fig. 4 (a) and (b)). To this end, the sample was first cooled to 10 K in a +7.8 kV/cm electric field and a 0.02T magnetic field from room temperature, then the M-T curves were measured in the warming process and followed by the cooling process without changing either field (red curves in Fig. 4). Then, at 10 K, the electric field was removed and the magnetic field remained unchanged (0.02T), the M-T curves were measured again in the warming process and followed by the cooling process (blue curves in Fig. 4).
Several interesting features are apparent from Fig. 4. First, when the temperature was below the FM transition temperature (230 K), removing the electric field (+7.8 kV/cm) causes completely opposite changes to magnetization during the cooling process for two directions. The maximumal relative changes, defined by ΔM/M(0) = (M(0)-M(E))/M(0), were up to 57.7% and −26.3% in the [100] and directions, respectively. Interestingly, the changes decrease with increasing temperature and vanish at the temperatures above the FM transition point, as shown in the insets to Fig. 4(a) and (b). These anisotropic magnetic responses to the external electric field are consistent with the results shown in Fig. 3 and should be ascribed to the in-plane anisotropic strain field induced by the electric field as discussed above. In fact, the cooling curves measured after the removal of the electric field are the same as the curves measured in a normally magnetic-field cooling process; this is because the magnetic state at 300 K becomes paramagnetic.
Second, during the heating process, the two M-T curves were nearly identical (red and blue curves) despite the application of an electric field (+7.8 or 0 kV/cm), providing more support for a nonvolatile control of magnetization by electric fields. Considering that the measurements of the both M-T curves are performed upon same pre-cooling process with joint applications of +7.8 kV/cm electric field and 0.02T magnetic field, this non-volatile control of magnetization can be certainly ascribed to the memory effect of the strain-mediated ME coupling2. It is important to note here that results from both Fig. 3 and 4 demonstrate that such a memory effect of ME coupling can only be observed in ferromagnically ordered states.
Discussion
Previous studies have shown that in-plane strain can lead to local lattice distortions and make the large-scale electronic phase separation self-organize into elongated domains in the narrow-band phase-separated manganite system22,24. Specially, our recent studies on phase-separated Pr0.7(Ca0.6Sr0.4)03MnO3 films revealed that the in-plane anisotropic strain can be a driving force for the correlated occupation of metallic sites and the preferential formation of elongated FM metallic clusters, which leads to an abnormal thermal hysteresis21. Furthermore, studies based on the effect of electron-lattice coupling indicate that the in-plane strain field not only influences the formation of an electronic phase separation in narrow-band manganite films, but also couples to the spin and orbital degrees of freedom22,25 in wide-band manganite films, strongly affecting DE ferromagnetism. In addition, direct experimental observations have shown that the in-plane anisotropic stress from the lattice mismatch can lead to stripe domains in wide-band La0.7Sr0.3MnO3 films23.
In the present wide-band (011)-PSMO/PMN-PT heterostructured system, the electric field induces a small tensile strain (~0.018%) along the direction and a large compressive strain (~−0.31%) along the [100] direction. This anisotropic strain may then transfer to the PSMO film18,19 through the interface, which produces an anisotropic tensile strain field in the PSMO film. Such an anisotropic tensile strain-field may promote the distortion of the MnO6 octahedra and elongation of the Mn-O-Mn bond along the direction with a higher tensile strain field. As a result, the overlapping of electron clouds between adjacent atoms and the occupation of 3d orbitals appear preferential orientation, which appends an extra magnetic anisotropy to the double-exchange ferromagnetism. Accordingly, the FM domains in the PSMO film form and grow preferentially along the direction to reduce the energy required during the pre-cooling process with an electric field, consequently forming metastable magnetic states. Fig. 5(a) and (b) schematically illustrate the domain distribution in the PSMO film at ground and metastable states, respectively, showing how the FM domains grow preferentially along the direction driven by the anisotropic strain field. With the electric-field tuning on, the state with the especially elongated FM domains has a lower energy than the ground state, making it thermodynamically stable (Fig. 5, upper left). Whereas removal of the applied pre-cooling electric field at 10 K causes the state to reach a higher local minimum energy (metastable) than the ground state (Fig. 5, upper right). These elongated domains in the metastable state bring about an additional magnetic anisotropy, which is responsible for the anisotropic modulation of magnetic behaviors of the film (Fig. 3 and 4). At low temperatures, the energy barrier (ΔE), produced by the shape anisotropic energy of elongate FM domains, blocked the system from recovering to a ground state at a zero electric field, due to the relatively small thermal energy in comparison with ΔE (Fig. 5, upper right). Until the amount of thermal energy is large enough to overcome the ΔE, as we observed in Fig. 3 (c) and (d), or to destroy the FM ordering, the material will continue staying in this metastable state. This explains why, below a certain temperature, the temperature-dependent magnetization of the film remains unchanged after the removal of the E-field and we observe the memory effect of ME coupling from anisotropic stain.
Previous researches investigating the strain-mediated magnetoelectric coupling in FM/FE heterostructures6,12,26 show that nonvolatile magnetic control was implemented by an electric-field induced remnant strain or an irreversible ferroelectric domain effect. However, a pre-established specific remnant strain state and a specific value or range of electric field to reset the strain are required to induce such effects in these systems6,26. Our results reveal that the nonvolatile magnetic memory effect could be simply realized by inducing a metastable magnetic state in the wide-band manganite layer using the electric-field induced anisotropic strain-field, demonstrating a new mechanism for the magnetoelectric memory effect. This unique magnetoelectric memory approach provides a promising technology for new design of spintronics devices such as the thermal-assisted electric-write magnetic memory.
Methods
Heterostructure fabrication
PSMO thin film was deposited on a (011)-oriented PMN-PT single crystal using the pulsed laser deposition (PLD) technique. The PSMO target was prepared by conventional solid reaction methods and the commercial (011)-oriented PMN-PT single crystal was chosen as the substrate because of its perovskite-cubic structure (aPMN-PT = 4.017 Å) and excellent anisotropic transverse piezoelectric effect. The strong in-plane anisotropic piezoelectric effect of PMN-PT provides an exceptional opportunity for generating a large in-plane anisotropic strain in the coherently grown PSMO film. During deposition, the temperature of the substrate was kept at 670°C and the oxygen pressure at 100 Pa. After deposition, the approximately 100-nm-thick film was cooled to room temperature in 1 atm of oxygen.
Characterizations and measurements
The out-of-plane interplanar distance and hence the out-of-plane epitaxial strain of the film were determined by x-ray diffraction (XRD) using Cu-Kα radiation (Fig. 1(a)). In-plane epitaxial strains of the film were determined from X-ray reciprocal space maps (RSMs) around asymmetric reflections that were collected using a four-circle diffractometer (Bruker AXS D8-Discover). Au layers were vapor deposited on both the top and bottom of the PSMO/PMN-PT heterostructure as electrodes. The magnetic properties of the samples were measured using a superconducting quantum interference device (SQUID–MPMS) with in situ electric fields applied across the PSMO/PMN-PT structure by a Keithley 6517A electrometer. The leakage current was below 5nA under a 7.8 KV/cm electric field. A detailed circuit diagram is represented in the inset of Fig. 1(a).
References
Bibes, M. & Barthelemy, A. Multiferroics. Towards a magnetoelectric memory. Nat. Mater. 7, 425 (2008).
Ma, J., Hu, J. M., Li, Z. & Nan, C. W. Recent Progress in Multiferroic Magnetoelectric Composites: from Bulk to Thin Films. Adv. Mater. 23, 1062 (2011).
Lou, J., Liu, M., Reed, D., Ren, Y. H. & Sun, N. X. Giant Electric Field Tuning of Magnetism in Novel Multiferroic FeGaB/Lead Zinc Niobate-Lead Titanate (PZN-PT) Heterostructures. Adv. Mater. 21, 4711 (2009).
Eerenstein, W., Wiora, M., Prieto, J. L., Scott, J. F. & Mathur, N. D. Giant sharp and persistent converse magnetoelectric effects in multiferroic epitaxial heterostructures. Nat. Mater. 6, 348(2007).
Yang, Y. J. et al. Large anisotropic remnant magnetization tunability in (011)-La2/3Sr1/3MnO3/0.7Pb(Mg2/3Nb1/3)O3-0.3PbTiO3 multiferroic epitaxial heterostructures. Appl. Phys. Lett. 100, 043506 (2012).
Wu, T. et al. Giant electric-field-induced reversible and permanent magnetization reorientation on magnetoelectric Ni/(011) [Pb(Mg1/3Nb2/3)O3]1-x-[PbTiO3]x heterostructure. Appl. Phys. Lett. 98, 012504 (2011).
Chu, Y. H. et al. Electric-field control of local ferromagnetism using a magnetoelectric multiferroic. Nat. Mater. 7, 478 (2008).
Liu, M. et al. Giant Electric Field Tuning of Magnetic Properties in Multiferroic Ferrite/Ferroelectric Heterostructures. Adv. Funct. Mater. 19, 1826 (2009).
Yang, J. J. et al. Electric field manipulation of magnetization at room temperature in multiferroic CoFe2O4/Pb(Mg1/3Nb2/3)0.7Ti0.3O3 heterostructures. Appl. Phys. Lett. 94, 212504 (2009).
Millis, A. J., Shraiman, B. I. & Mueller, R. Dynamic Jahn-Teller effect and colossal magnetoresistance in La1-xSrxMnO3 . Phys. Rev. Lett. 77, 175 (1996).
Millis, A. J. Lattice effects in magnetoresistive manganese perovskites. Nature 392, 147 (1998).
Chen, Q. P. et al. Electric-field control of phase separation and memory effect in Pr0.6Ca0.4MnO3/Pb(Mg1/3Nb2/3)0.7Ti0.3O3 heterostructures. Appl. Phys. Lett. 98, 172507 (2011).
Tomioka, Y. & Tokura, Y. Bicritical features of the metal-insulator transition in bandwidth-controlled manganites: Single crystals of Pr1-x(Ca1-ySry)xMnO3 . Phys. Rev. B 66, 104416 (2002).
Tomioka, Y., Asamitsu, A., Kuwahara, H. & Tokura, Y. Reentrant transition of the charge-ordered state in perovskite manganites. J. Phys. Soc. Jpn. 66, 302 (1997).
Tokura, Y. Colossal Magnetoresistive Oxides [ Tokura Y., ed. (ed.)] (Gordon and Breach, London, 1999).
Coey, J. M. D., Viret, M. & von Molnár, S. Mixed-valence manganites. Advances in Physics 58, 571 (2009).
Wang, J., Hu, F. X., Li, R. W., Sun, J. R. & Shen, B. G. Strong tensile strain induced charge/orbital ordering in (001)-La7/8Sr1/8MnO3 thin film on 0.7Pb(Mg1/3Nb2/3)O30.3PbTiO3 . Appl. Phys. Lett. 96, 052501 (2010).
Shanthi, M., Lim, L. C., Rajan, K. K. & Jin, J. Complete sets of elastic, dielectric and piezoelectric properties of flux-grown [011]-poled Pb(Mg1/3Nb2/3)O3-(28-32)% PbTiO3 single crystals. Appl. Phys. Lett. 92, 142906 (2008).
Biegalski, M. D., Dorr, K., Kim, D. H. & Christen, H. M. Applying uniform reversible strain to epitaxial oxide films. Appl. Phys. Lett. 96, 151905 (2010).
Agarwal, S. K. et al. Structural, electrical and thermal studies of Nb-doped Pr0.7Sr0.3Mn1-xNbxO3 (0 < x < 0.05) manganites. Solid Stat. Comm. 150, 684–688 (2010).
Zhao, Y. Y. et al. Abnormal percolative transport and colossal electroresistance induced by anisotropic strain in (011)-Pr0.7(Ca0.6Sr0.4)0.3MnO3/PMN-PT heterostructure. Sci. Rep. 4, 7075 (2014).
Ward, T. Z. et al. Elastically driven anisotropic percolation in electronic phase-separated manganites. Nature Phys. 5, 885–888 (2009).
Dho, J., Kim, Y. N., Hwang, Y. S., Kim, J. C. & Hur, N. H. Strain-induced magnetic stripe domains in La0.7Sr0.3MnO3 thin films. Appl. Phys. Lett. 82, 1434–1436 (2003).
Ahn, K. H., Lookman, T. & Bishop, A. R. Strain-induced metal-insulator phase coexistence in perovskite manganites. Nature (London) 428, 401 (2004).
Lu, C. L. et al. Giant in-plane anisotropy in manganite thin films driven by strain-engineered double exchange interaction and electronic phase separation. Appl. Phys. Lett. 99, 122510 (2011)
Geprags, S., Brandlmaier, A., Opel, M., Gross, R. & Goennenwein, S. T. B. Electric field controlled manipulation of the magnetization in Ni/BaTiO3 hybrid structures. Appl. Phys. Lett. 96, 142509 (2010).
Acknowledgements
This work was supported by the National Basic Research of China (Grant Nos. 2012CB933001, 2014CB643702 and 2013CB921700), the National Natural Science Foundation of China with Grant Nos. 11174345, 11474341, 51271196, 11134007 and 11374348 and the Key Research Program of the Chinese Academy of Sciences.
Author information
Authors and Affiliations
Contributions
J.W. and F.X.H. planned and supervised the experiments. Y.Y.Z. prepared the samples and performed X-ray diffraction and magnetic transport measurements. Y.Y.Z. and H.K. performed the dynamic strain measurements and analyzed the strain data, Y.L. and R.R.W. assisted in the magnetic and transport measurements. X.X.Z. helped with analyses of the results. J.R.S. and B.G.S. made scientific comment on the results. J.W. and F.X.H wrote the paper, which all authors reviewed and refined.
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article's Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder in order to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Zhao, YY., Wang, J., Kuang, H. et al. Anisotropic modulation of magnetic properties and the memory effect in a wide-band (011)-Pr0.7Sr0.3MnO3/PMN-PT heterostructure. Sci Rep 5, 9668 (2015). https://doi.org/10.1038/srep09668
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep09668
- Springer Nature Limited
This article is cited by
-
Electric-field control of nonlinear THz spintronic emitters
Nature Communications (2022)
-
Correlation between spin–phonon coupling and magneto-electric effects in CoFe2O4/PMN-PT nanocomposite: Raman spectroscopy and XMCD study
Journal of Materials Science: Materials in Electronics (2022)