Abstract
Many flexible electronic devices contain metal films on polymer substrates to satisfy requirements for both electrical conductivity and mechanical durability. Despite numerous trials to date, the stretchability of metal interconnects remains an issue. In this paper, we have demonstrated a stretchable metal interconnect through control of the texture of a copper film with columnar grown grains on a polyimide (PI) substrate. The columnar grown copper films (CGC films) were deposited by regulating radio frequency (RF) sputtering powers. CGC films were able to sustain their electrical conductivity at strains above 100%. Instead of ultimate electrical discontinuity by channel crack propagation, CGC films maintained their conductivity by forming ligament structures, or a ‘conductive net,’ through trapped micro-cracks. XRD, AFM and in situ SEM analysis were used to investigate these stretchable conductors.
Similar content being viewed by others
Explore related subjects
Discover the latest articles, news and stories from top researchers in related subjects.Introduction
Flexible electronics are an extremely popular area of technology, as they to exceed spatial limitations of traditional electronics and can interface directly with living organisms. Many applications, including electronic skin or sensors1,2, wearable devices3, transparent speakers4 and flexible and foldable displays5,6, commonly contain stretchable conductors. Conductive interconnects need to satisfy requirements for both electrical conductivity and mechanical properties. Metals such as gold and copper are preferred as interconnects because of their outstanding electrical properties, but their stretchability has been recognized as a weak point. Many geometrical approaches aim to extend the strain limitations of metals by designing wavy serpentines7,8,9,10,11,12 or facilitating the percolation of conductive particles13. In both cases, large stretchability has been demonstrated under uniaxial or multi-axial strain14. However, wavy serpentines need extra space near the interconnects to achieve their stretchability9 and conductive particles such as silver nanowires show steep increase in resistivity at high strains due to the loss of conductive pathways15.
In addition to geometrical approaches, some metallurgical strategies have been studied to enhance the stretchability of conductors. One of these studies demonstrated improved stretchability in copper by annealing and inserting an adhesive layer between a copper film and a polymer substrate16. Less commonly, microstructural approaches have been tried, though failure tends to occur due to stress concentrations. Only research on gold nanocrystals on a PDMS substrate17,18 have been reported, where gold nanocrystals on PDMS substrates endured uniaxial tension up to 30% strain without electrical failures, even as micro-cracks in the gold ligaments developed.
Here, we propose another metallurgical strategy to achieve high stretchability together with high electrical conductivity. We have developed a stretchable copper thin film on a polyimide substrate by controlling its texture. Copper grains were grown in columnar shapes with a particular orientation. The selective grain growth was controlled by changing the radio frequency (RF) sputtering powers. The texture-controlled copper grains were grown in regular arrays with homogeneous diameters and heights above 1 μm, leading to a high aspect ratio. The texture-controlled copper film was stretchable beyond 100% while maintaining its electrical conductivity. Texture-controllable grains were experimentally observable and their grain growth mechanism is described with crystallographic theories.
Results and Discussion
Copper films deposited on polyimide substrates can have different grain growths by varying the radio frequency (RF) sputtering power, e.g., a polycrystalline copper film (Fig. 1a,b) and a columnar grown copper film (CGC film) (Fig. 1c,d). When the polycrystalline film was pulled in uniaxial tension, as shown in Fig. 1, the film failed by channel crack propagation below 10% strain. Buckling in the transverse direction also accompanied deformation, which resulted in delamination and electrical failures in the polycrystalline copper (Fig. 1b). When CGC films were stretched, initial cracks appeared at a strain of 3%; however, these cracks were trapped by surrounding grains instead of propagating, leading to the activation of other cracks. As a result, many short-range cracks developed at low strains and the microstructure preventing the further development of channel cracks with increasing strain. These trapped short-range cracks contributed to building a ligament structure, such that the films could act as a ‘conductive net’; therefore, the CGC film could maintain its electrical conductivity even at larger strains. In Fig. 1d, the CGC film at 106% applied strain is wholly interconnected by netlike ligaments containing short range-cracks. After 106% strain, further deformation was terminated by the rupture of the PI substrate, not by limitations of the CGC film.
A CGC film on a PI substrate deposited at 100 W for 60 minutes was stretched up to 100% and tilted at 52° to examine its grain growth using scanning electron microscopy (SEM) (Fig. 2a,b). The texture-controlled thin films comprised well-aligned, homogenous columns with similar height and diameter. To determine the average size of copper columns and the degree of uniformity in their alignment, the CGC films were studied using atomic force microscope (AFM). The measurements for a CGC film deposited at 100 W for 15 minutes are shown in Fig. 2c. The average grain size was 43.5 nm and the height of the columnar grains varied with sputtering time and power conditions. With longer sputtering times, the grains attained higher aspect ratios. Columnar grains even over 1 μm in height were grown in the film sputtered at 100 W for 60 minutes (Figure S1.a). The root mean square (RMS) roughness of the film was 0.829 nm, which indicates that the height of the columns was nearly constant.
Three different microstructures from various sputtering power conditions were observed using X-ray diffraction (XRD): amorphous, texture-controlled and polycrystalline structures (Fig. 2d). Amorphous copper grains formed at 20 W sputtering power. A (111) texture developed as the power reached 40 W and the texture stabilized up to 100 W. Higher intensity diffraction patterns appeared at higher sputtering powers. The notable peak at (111) indicated that grains grew in a single orientation in the shape of columns. At 200 W and 300 W, additional intensified peaks at (200) and (220) appeared, suggesting the development of polycrystalline structures. Columnar grains in a selective orientation are a result of minimizing the crystallographically anisotropic free energy in the thin film system: surface energy, interfacial energy and strain energy are known to influence selective grain growth19. According to a previous study20, minimization of surface and interface energies are dominant in our experimental range of film thicknesses and sputtering conditions. In particular, with face-centered-cubic materials like copper, the (111) orientation has the minimum surface energy, leading to selective grain growth in this preferable orientation. When copper films are deposited with higher sputtering powers than 100 W, the minimization of strain energy governs the grain growth instead of surface and interfacial energy in the (100) and (110) orientations19,21. Therefore, our results are consistent with a general phenomenon in polycrystalline structures in copper films.
The deposition rates of CGC films are shown in Figure S1, with all thicknesses measured by AFM. The copper films were grown at a rate of 1 μm per hour at a sputtering power of 100 W. There was a linear dependence between deposition time and film thickness (Figure S1.a). In addition, for films deposited for 60 minutes, higher deposition rates were attained at higher sputtering powers, but the relationship was not linear (Figure S1.b).
The stretchability of the CGC films is shown in Fig. 3, determined by measuring the electrical resistance of the films during uniaxial tension. Mechanical straining and electrical measurements were performed on a custom-made stretcher made from anodized alumina for electrical insulation, as shown in Figure S2. The resistances of copper films deposited using different sputtering powers for 60 minutes are shown in Fig. 3a. In the case of the amorphous copper film grown at 20 W, the resistance at 40% strain quadrupled and rapidly increased tenfold at just below 60% applied strain. CGC films with controlled textures at 40 W and 100 W were the most stable, maintaining their electrical conductivities at higher strain levels than in any other cases. In particular, the CGC film deposited at 100 W showed the most similar conductivity-strain behavior to the theoretical prediction. The uniaxial elongation could not continue beyond 100% due to the rupture of the PI substrate, whereas the CGC film would have remained intact. The resistances in polycrystalline copper films deposited at 200 W and 300 W went up nearly tenfold under uniaxial elongation up to maximum strains of 40% and 10%, respectively. The relatively early discrepancy between the measured and the theoretical values in the amorphous and polycrystalline copper films was due to electrical pathway discontinuities originating from channel cracks and their propagations at small applied strain levels. More SEM images regarding on crack morphology under stretching are available in Figure S3 of Supporting information. The thicknesses of the films in Fig. 3a varied due to the different sputtering power conditions. The thickness effect on electrical resistivity was also explored in the Supporting information (Figure S4). While there was a slight dependence between film thickness and resistivity, it was weak relative to the effect of sputtering power.
Figure 3b shows the resistivities of copper films grown at different sputtering powers before tension. At a sputtering power of 20 W, where amorphous copper grains developed, the resistivity was an order of magnitude higher than those of the remaining cases. Grain sizes depending on sputtering powers were investigated in Figure S3. Larger grains were formed at higher sputtering powers. We suspect that the high electrical resistivity of copper films deposited at low sputtering powers may be due to their small grains and large amount of grain boundaries. At a sputtering power of 40 W, the resistivity dropped significantly to 34 μΩ · cm. Resistivities of copper films deposited above 100 W had almost uniform values around 15 μΩ · cm, indicating similar initial conductivity behavior between texture-controlled copper films and polycrystalline copper films. In Fig. 3c, we examined resistivity changes in CGC films during film deposition by measuring the resistivities at different film thicknesses. Deposited at a constant sputtering power of 100 W, the CGC film showed small variations in electrical resistivity, ranging from 10 to 15 μΩ · cm, implying that the resistivities of CGC films prior to straining remain constant during the deposition process. While reported resistivity of copper thin films on polyimide substrates is ranging from 3.8 to 17 μΩ · cm22,23. CGC films have slightly higher resistivity. High resistivity may be due to lots of grain boundaries in CGC films.
We captured in situ SEM images during uniaxial tension of CGC films deposited at 100 W. Strain proceeded up to 60%, with initial cracks generating at 5% strain. These cracks propagated with higher applied strain but were quickly followed by the activation of additional short cracks rather than the aggravation of existing cracks. When the strain reached 10%, the total density of cracks remained constant and further propagations were suppressed. According to the in situ SEM images, the ligaments endured applied stress up to 60% (Fig. 4d–f). A corresponding movie clip is available in Supplementary Movie 1. In Fig. 4g, an activated crack was trapped by other grains nearby and the crack did not propagate with further elongation of the film. The localization of short-range cracks promoted the generation of other cracks at 10% strain through the transfer of load to neighboring grains. When larger strains were applied to the CGC film, grains tended to slide along grain boundaries (Fig. 4h) and some portions of the ligament structure rotated about a reference point (Fig. 4i). Crack trapping, grain boundary sliding and ligament rotations played a key role in maintaining electrical conduction beyond 100% applied strain.
Conclusion
Columnar grown copper films on polyimide substrates were fabricated by controlling sputtering powers and their electrical conductivities were measured during uniaxial tension. At a specific sputtering power condition, homogeneous columnar grains with uniform height and diameter and a selective texture of (111) orientation formed as a crystallographic product of minimizing the free energy of the system. The microstructural phenomena of crack trapping, grain boundary sliding and ligament rotation promoted high stretchability of the CGC films even beyond 100% applied strain and their variation in electrical resistivity under strain approached the theoretically predicted behavior. In addition, with longer deposition times, columnar grains with higher aspect ratios were obtained, some of which were over 1 μm in height.
CGC films will be able to satisfy great demands in both research and industrial sectors for large-scale flexible electronics. The performance of these films can be optimized with the formation of high aspect ratio features modulated by sputtering powers and times. Stretchable interconnects with ligaments made from other metals deposited on other stretchable polymer substrates are also expected to be developed in further studies.
Methods
Fabrication procedure of Cu thin films
Preparation of polyimide (PI) substrate
Cu films were deposited on polyimide foils (Kapton® by DuPont) with dimensions of 5 mm × 40 mm × 125 μm. To improve adhesion, PI foils were sonicated in acetone for 10 minutes and then stored in a vacuum chamber for 2 hours to remove acetone remnants and absorbed water before deposition.
Copper deposition
Copper films were deposited by radio frequency (RF) sputter under various sputtering conditions, with powers ranging from 20 W to 300 W for different sputtering times, which produced copper films with thicknesses ranging from 200 nm to 1000 nm. The base pressure of the RF chamber was less than 10−6 torr. Ar was used as the working gas at a pressure of 2.5 × 10−2 torr. The radio frequency of the power supply was 13.56 MHz.
Resistance measurement with uniaxial tensile tests on Cu films
The uniaxial tensile tests were performed with a custom-made micro tensile testing device (Figure S2). The screw driven stretcher was made of anodized alumina for electrical insulation. The initial length of each specimen was 5.6 mm. All tensile tests were conducted with a constant strain rate of 5 × 10−4 sec−1 at room temperature. The resistance of the films was measured by the 4-point probe method with a multimeter (DMM 2000/E, Keithley). A schematic of the entire experimental set-up is on Figure S2. (d). The microstructures of the copper films were observed in a scanning electron microscope (SEM) with a built-in focused ion beam (FIB) (NOVA200, FEI). In situ observations were also performed using the FIB-SEM system. The maximum applied strain was 100%, which was restricted by the failure of the PI substrates.
AFM and XRD analysis
The average grain size, root mean square of surface roughness and film thickness were measured by atomic force microscopy (AFM, DI-3000, Digital Instrument) in contact mode in air at room temperature. Crystallographic textures of the copper films were examined by X-ray diffraction (XRD, M18XHF-SRA, MAC Science Co.) with Cu Kα radiation. The wavelength was 1.54056 Å and scanning speed was 10.0 degrees per minute. The voltage and current were 50.0 kV and 100.0 mA, respectively.
Additional Information
How to cite this article: Sun, J.-Y. et al. Columnar grown copper films on polyimides strained beyond 100%. Sci. Rep. 5, 13791; doi: 10.1038/srep13791 (2015).
References
Hammock, M. L., Chortos, A., Tee, B. C. K., Tok, J. B. H. & Bao, Z. A. 25th Anniversary Article: The Evolution of Electronic Skin (E-Skin): A Brief History, Design Considerations and Recent Progress. Advanced Materials 25, 5997–6037, 10.1002/adma.201302240 (2013).
Kim, J. et al. Stretchable silicon nanoribbon electronics for skin prosthesis. Nature communications 5, 10.1038/ncomms6747 (2014).
Sun, J. Y., Keplinger, C., Whitesides, G. M. & Suo, Z. G. Ionic Skin. Advanced Materials 26, 7608–7614, 10.1002/adma.201403441 (2014).
Keplinger, C. et al. Stretchable, transparent, ionic conductors. Science 341, 984–987 (2013).
Liang, J. J., Li, L., Niu, X. F., Yu, Z. B. & Pei, Q. B. Elastomeric polymer light-emitting devices and displays. Nat. Photonics 7, 817–824, 10.1038/nphoton.2013.242 (2013).
Ghosh, D. S., Chen, T. L., Mkhitaryan, V. & Pruneri, V. Ultrathin Transparent Conductive Polyimide Foil Embedding Silver Nanowires. ACS Appl. Mater. Interfaces 6, 20943–20948, 10.1021/am505704e (2014).
Kim, D.-H. et al. Materials for multifunctional balloon catheters with capabilities in cardiac electrophysiological mapping and ablation therapy. Nature materials 10, 316–323 (2011).
Gray, D. S., Tien, J. & Chen, C. S. High‐Conductivity Elastomeric Electronics. Advanced Materials 16, 393–397 (2004).
Kim, D. H. et al. Epidermal Electronics. Science 333, 838–843, 10.1126/science.1206157 (2011).
Bossuyt, F., Vervust, T. & Vanfleteren, J. Stretchable Electronics Technology for Large Area Applications: Fabrication and Mechanical Characterization. IEEE Trans. Compon. Pack. Manuf. Technol. 3, 229–235, 10.1109/tcpmt.2012.2185792 (2013).
Lacour, S. P., Jones, J., Wagner, S., Li, T. & Suo, Z. G. Stretchable interconnects for elastic electronic surfaces. Proc. IEEE 93, 1459–1467, 10.1109/jproc.2005.851502 (2005).
Sun, J.-Y., Xia, S., Moon, M.-W., Oh, K. H. & Kim, K.-S. Folding wrinkles of a thin stiff layer on a soft substrate. Proc. R. Soc. A 468, 932–953, 10.1098/rspa.2011.0567 (2011)
Hu, L. B., Yuan, W., Brochu, P., Gruner, G. & Pei, Q. B. Highly stretchable, conductive and transparent nanotube thin films. Applied Physics Letters 94, 3, 10.1063/1.3114463 (2009).
Xu, S. et al. Stretchable batteries with self-similar serpentine interconnects and integrated wireless recharging systems. Nature Communications 4, 8, 10.1038/ncomms2553 (2013).
Hu, W. L. et al. Intrinsically stretchable transparent electrodes based on silver-nanowire-crosslinked-polyacrylate composites. Nanotechnology 23, 9, 10.1088/0957-4484/23/34/344002 (2012).
Lu, N., Wang, X., Suo, Z. & Vlassak, J. Metal films on polymer substrates stretched beyond 50%. Applied Physics Letters 91, 221909 (2007).
Adrega, T. & Lacour, S. Stretchable gold conductors embedded in PDMS and patterned by photolithography: fabrication and electromechanical characterization. Journal of Micromechanics and Microengineering 20, 055025 (2010).
Lacour, S. P., Chan, D., Wagner, S., Li, T. & Suo, Z. G. Mechanisms of reversible stretchability of thin metal films on elastomeric substrates. Applied Physics Letters 88, 3, 10.1063/1.2201874 (2006).
Weihnacht, V. & Brückner, W. Abnormal grain growth in {111} textured Cu thin films. Thin Solid Films 418, 136–144 (2002).
Thompson, C. V. & Carel, R. Stress and grain growth in thin films. Journal of the Mechanics and Physics of Solids 44, 657–673 (1996).
Floro, J., Thompson, C., Carel, R. & Bristowe, P. Competition between strain and interface energy during epitaxial grain growth in Ag films on Ni (001). Journal of materials research 9, 2411–2424 (1994).
Lee, J., Lee, B., Jeong, S., Kim, Y. & Lee, M. Appl. Surf. Sci. 307, 42–45, 10.1016/j.apsusc.2014.03.127 (2014)
Eun, K., Chon, M.-W., Yoo, T.-H., Song, Y.-W. & Choa, S.-H. Micro. Electron. Reliab. 55, 838–845, 10.1016/j.microrel.2014.12.015 (2015)
Acknowledgements
This work was supported by a grant from CAMP funded by the Ministry of Science and Technology (RIAM) and from the Korea Research Foundation. J.-Y. Sun and H.-R. Lee acknowledge support from the Research Resettlement Fund for new faculty at Seoul National University. K.H. Oh thanks support from the SRC/ERC program of MOST/KOSEF (0417-20130128). K.H. Oh acknowledges support from the Fundamental R&D Program for Technology of World Premier Materials funded by the Ministry of Knowledge Economy, Republic of Korea (10037919).
Author information
Authors and Affiliations
Contributions
J.-Y.S., K.H.O designed the study and interpreted the results. J.-Y.S. conducted the experiments with columnar growth of copper films. J.-Y.S., H.-R.L analyzed the failure mechanism of CGC films. J.-Y.S., H.-R.L wrote the manuscript. All authors commented on the manuscript.
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Electronic supplementary material
Rights and permissions
This work is licensed under a Creative Commons Attribution 4.0 International License. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in the credit line; if the material is not included under the Creative Commons license, users will need to obtain permission from the license holder to reproduce the material. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Sun, JY., Lee, HR. & Hwan Oh, K. Columnar grown copper films on polyimides strained beyond 100%. Sci Rep 5, 13791 (2015). https://doi.org/10.1038/srep13791
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/srep13791
- Springer Nature Limited
This article is cited by
-
Silver and epoxy binder-based printed electrodes and the effect of silver nanoparticles on stretchability
Journal of Materials Science: Materials in Electronics (2019)