Abstract
This work reports the preparation and characterization of silver nanoparticles synthesized through wet chemical solution method and of silver films deposited by dip-coating method. X-ray diffraction (XRD), field emission scanning electron microscopy (FESEM), field emission transmission electron microscopy (FETEM), high-resolution transmission electron microscopy (HRTEM), selected area electron diffraction (SAED), and energy dispersive spectroscopy (EDX) have been used to characterize the prepared silver nanoparticles and thin film. The morphology and crystal structure of silver nanoparticles have been determined by FESEM, HRTEM, and FETEM. The average grain size of silver nanoparticles is found to be 17.5 nm. The peaks in XRD pattern are in good agreement with that of face-centered-cubic form of metallic silver. TGA/DTA results confirmed the weight loss and the exothermic reaction due to desorption of chemisorbed water. The temperature dependence of resistivity of silver thin film, determined in the temperature range of 100-300 K, exhibit semiconducting behavior of the sample. The sample shows the activated variable range hopping in the localized states near the Fermi level.
Avoid common mistakes on your manuscript.
Introduction
Metal nanoparticles with at least one dimension approximately 1-100 nm have received considerable attention in both scientific and technological areas due to their unique and unusual physico-chemical properties compared with that of bulk materials [1]. Phenomena at the nanoscale are likely to be a completely new world, where properties may not be predictable from those observed at large size scales, on account of quantum size effect and surface effects. Synthesis of nanoparticles has been a rapidly growing field in solid state chemistry [2]. Metal nanoparticles are particularly interesting because they can easily be synthesized and modified chemically as well as can suitably be applied for device fabrication [3–5]. Due to the specific size, shape, and distribution, nanoparticles are used in the production of novel systems such as nanosensors [6], nanoresonators [7], nanoactuators [8], nanoreactors [9], single electron tunneling devices [10], plasmonics [11], and nanowire based devices [12] etc.
Among the various metal nanostructures, noble metal nanoparticles have attracted much attention, due to their superior physical and chemical properties. Nowadays, a lot of researches have been focused on silver nanoparticles because of their important scientific and technological applications in color filters [13, 14], optical switching [15], optical sensors [16, 17], and especially in surface-enhanced Raman scattering [18–20]. Such properties and applications strongly depend on the morphology, crystal structure, and dimensions of silver nanostructures. Over recent years, silver thin films have been a subject of intensive investigations because of excellent optical, electrical, catalytic, sensing, and antibacterial properties [21, 22] and subsequent applications. The synthesis of silver nanoparticles with controlled morphology is important for uncovering their specific properties and for achieving their practical applications.
Silver nanoparticles are of current importance because of its easy preparation process and unique optical, electrical, and thermal properties. The electrical conductivity of polyaniline-silver nanocomposite increases with increase in silver nanoparticles content than that of pure polyaniline [23, 24]. Pillai et al. [25] demonstrated that solar cells employing metallic nanoparticles can dramatically enhance the near infrared absorption due to the presence of surface plasmons. The excited surface plasmons can eject electrons into a surrounding conductive medium resulting in effective charge separation. D. Basak et al. [26] observed significant modifications in the electrical properties of poly (methyl methacrylate) thin films upon dispersion of silver nanoparticles. So far as the electrical properties are concerned, it is necessary to throw some light on the structural and morphological characteristics of silver nanoparticles.
In the synthesis of nanoparticles, it is very important to control not only the particle size but also the particle shape and particle size distribution as well. In the present investigation, the synthesis of silver nanoparticles and thin films by wet chemical solution route [27] has been discussed. The prepared silver nanoparticles have been examined using X-ray diffraction (XRD), field emission transmission scanning electron microscope (FESEM), field emission transmission electron microscope (FETEM), high-resolution transmission electron microscope (HRTEM), two-probe direct-current (dc) resistivity measurement and thermogravimetric analysis/differential thermal analysis (TGA/DTA) thermal system.
Experimental details
All the chemicals employed in the synthesis have been of analytical reagent grade. We used them without further purification. The nanoparticles of silver have been prepared according to the conventional procedure [28]. The aqueous solution (20 ml) containing glucose (9 mmol), polyvinylpyrrolidone (12 mmol), and sodium hydroxide (7 mmol) has been heated at 60°C for 30 min under vigorous stirring at 3,000 rpm. After that, 10 ml aqueous solution of AgNO3 (1 mol/l) has been dropped in the previous solution. After refluxing for 60 min, the colloidal solution has been allowed to cool slowly to room temperature. The resultant solution has been undertaken to centrifugation at 8,000 rpm for 90 min. After filtration, the precipitate so obtained has been washed many times with deionized water using centrifugation for 15 min each time. Finally, the precipitate has been collected and powdered finely, and identified as silver nanoparticles using characterization tools. These silver nanoparticles have been re-dispersed in ethanol for the preparation of silver film. The films have been deposited on ultra-clean quartz substrates using dip-coating method. The quartz substrate has been immersed vertically into the ethanol solution of silver nanoparticles (25 mg/ml). After that, the container has been placed in a vacuum chamber (10-3 torr) at room temperature for 24 h; the smooth, uniform, and bright silver film has been obtained on the quartz substrate due to the evaporation of the solvent (ethanol) under reduced pressure. The film shows good adhesion to the substrate. Prior to the deposition of silver film, the quartz slide has been immersed in chromic-sulfuric acid for a day in order to clean the surface and to enhance its hydrophilicity; and then rinsed many times with deionized water and dried in air.
The morphology and crystal structure of silver nanoparticles powder has been evaluated by FESEM, FETEM, HRTEM, SAED, energy dispersive spectroscopy (EDX), and XRD. SEM images were obtained using a field emission scanning electron microscope (JSM-7600F, JEOL, Tokyo Japan) at an accelerating voltage of 15 kV. The fine powder of silver nanoparticles has been dispersed in ethanol on a carbon coated copper grid and TEM images were obtained with ultra-high resolution FETEM (JEOL, JEM-2100F) at an accelerating voltage of 200 kV. The reaction type and weight loss have been confirmed using TGA/DTA thermal system (DTG-60, Shimadzu, Kyoto, Japan). The XRD pattern was recorded by X-ray diffractometer (PANalytical X'Pert, Almelo, The Netherlands) equipped with Ni filter and CuKα (λ = 1.54056 Å) radiation source. For dc resistivity measurements, silver film with deposited contacts has been mounted in a specially designed metallic sample holder where a vacuum of about 10-3 torr could be maintained throughout the measurements. A voltage (1.5 V, DC) was applied across the film and the resulting current was measured by a digital electrometer (Keithley 617, Keithley Instruments, Inc., Cleveland OH, USA). The temperature was measured by mounting a calibrated copper-constantan thermocouple near the sample.
Results and discussion
Structural properties
Figure 1 shows the XRD pattern of powder silver nanoparticles. The presence of peaks at 2θ values 38.1°, 44.09°, 64.36°, 77.29°, 81.31°, 97.92°, 110.81° and 114.61° corresponds to (111), (200), (220), (311), (222), (400), (331), and (420) planes of silver, respectively. Thus, the XRD spectrum confirmed the crystalline structure of silver nanoparticles. No peaks of other impurity crystalline phases have been detected. All the peaks in XRD pattern can be readily indexed to a face-centered cubic structure of silver as per available literature (JCPDS, File No. 4-0783). The lattice constant calculated from this pattern has been found to be a = 0.4085 nm, which is consistent with the standard value a = 0.4086 nm. The crystallite size (L) of the material of thin film has been evaluated by Scherrer's formula [29]
where λ is wavelength (0.15418 Å) of X-rays used, β is broadening of diffraction line measured at half of its maximum intensity (in radian), and θ is Bragg's diffraction angle (in degree). The crystallite size of silver nanoparticles has been found to be 16.37 nm. In order to distinguish the effect of crystallite size induced broadening and strain induced broadening at FWHM of XRD profile, Williamson-Hall plot [30] has been drawn which is shown in inset of Figure 1. The crystallite size and strain can be obtained from the intercept at y-axis and the slope of line, respectively.
where β is FWHM in radian, t is the grain size in nm, ε is the strain, λ is X-ray wavelength in nanometers, and C is a correction factor taken as 0.94. The grain size and strain of the sample have been found to be 16.37 nm and 3.98 × 10-3, respectively.
The intrinsic stress (σ s) developed in nanoparticles due to the deviation of measured lattice constant of silver nanoparticles over the bulk has been calculated using the relation [31]
Here, Y is the Young's modulus of Ag (83 GPa), a is the lattice constant (in nanometers) measured from XRD data, a 0 is the bulk lattice constant (0.5406 nm) and γ is the Poisson's ratio (0.37) for Ag.
The dislocation density (δ) in the nanoparticles has been determined using expression [32]
The X-ray line profile analysis has been was used to determine the intrinsic stress and dislocation density of silver nanoparticles and found to be as 0.275 GPa and 7.0 × -14 m-2 respectively.
Figure 2 shows the FESEM image of silver nanoparticles. It exhibits that almost all the nanoparticles are of spherical shape with no agglomeration. FETEM and HRTEM images of the same sample are shown in Figure 3a, b, respectively. Figure 3a shows that silver nanoparticles are spherical in shape having smooth surface and are well dispersed. The average diameter of silver nanoparticles is found to be approximately 35 nm. TEM image also shows that the produced nanoparticles have more or less narrow size distribution. HRTEM image (Figure 3b) has given us further insight into the microstructure and crystallinity of as-prepared silver nanoparticles. The clear and uniform lattice fringes confirmed that the spherical particles are highly crystallized. The lattice spacing of 0.232 nm corresponds to (111) planes of silver. The results show that the dominant faces of silver spheres are (111). The SAED pattern has been obtained by directing the electron beam perpendicular to one of the spheres. The hexagonal symmetry of diffraction spots pattern shown in the inset of Figure 3b confirmed that the spherical particles are well crystalline, and its face is indexed to (111) planes. Both HRTEM image and SAED pattern confirmed that the prepared spherical silver nanoparticles are single crystals.
The elemental analysis of sample has been performed using EDX spectroscopy. Inset of Figure 2 shows EDX spectrum of silver nanoparticles. The peaks observed at 3.0, 3.2, and 3.4 keV correspond to the binding energies of Ag L α , Ag L β , and Ag L β 2respectively; while the peaks situated at the binding energies of 0.85, 1.0, 8.05, and 8.95 keV belong to CuL 1, CuL α , CuK α , and CuK β , respectively. In addition, a peak at 0.25 keV corresponding to carbon (CK α ) has been observed. The copper and the carbon peaks correspond to the carbon coated copper grid of TEM. No peaks of other impurity have been detected. Therefore, the EDX profile of sample (inset of Figure 2) indicates that the silver nanoparticles sample contain pure silver, with no oxide.
Thermal properties
TGA and DTA spectra have been recorded in temperature range from room temperature to 700°C using simultaneous thermal system (Shimadzu, DTG-60). A ceramic (Al2O3) crucible was used for heating and measurements were carried out in nitrogen atmosphere at the heating rate of 10°C/min. TGA and DTA curves of powder silver nanoparticles are given in Figure 4. It is observed from TGA curve that dominant weight loss of the sample occurred in temperature region between 200 and 300°C. There is almost no weight loss below 200°C and above 300°C. It can be generally attributed to the evaporation of water and organic components. Overall, TGA results show a loss of 14.58% upto 300°C. DTA plot displays an intense exothermic peak between 200°C and 300°C which mainly attributed to crystallization of silver nanoparticles. DTA profiles show that complete thermal decomposition and crystallization of the sample occur simultaneously.
Electrical properties
The temperature dependence of dc electrical resistivity of thin films of silver nanoparticles in the temperature range 100-300 K has been shown in Figure 5. It is evident from the figure that the resistivity decreases with increase in temperature, which shows the semiconducting nature of the sample. In these semiconductors, there are additional energy levels in the band gap, which are localized and close to either the conduction or the valence band. Since the energy difference between these levels and band edges is very small, a slight thermal excitation is sufficient to accept or donate electrons; thereby the electrical resistivity decreases with increase in temperature. Electron transport in the nanocrystalline silver thin film at relatively low temperature could be explained by thermally activated hopping between localized states near the Fermi level. In the variable range hopping (VRH) process [33], it becomes favorable for an electron to jump from one localized state to another where the overlapping of wave functions exists. The difference in corresponding eigen energies is compensated by the absorption or emission of phonons. Thus, the variation of electrical resistivity with temperature can be described by three-dimensional Mott's variable range hopping model [34],
where ρo is the high temperature limit of resistivity (in Ω-m)and T o is Mott's characteristic temperature (in kelvin) associated with the degree of localization of the electronic wave function.
The Mott's characteristic temperature T o for three-dimensional hopping transport is given by,
where k B is the Boltzmann constant (in electronvolt per kelvin), N(E F) is the density of states (in per electron volt per cubic meter), 1/γ is the decay length of electronic wave function which typically varies in the range 3-30 Å and C o is a dimensionless constant, which has a value in the range 16-310 [35]. It is clear from Figure 5 and its inset that the sample exhibits a good fitting over the entire temperature range 100-300 K. Here, we have taken the localization length γ = 3 Å as reported by Maddison et al. [36]. From the fitted values of T o, we have found the value of density of states at the Fermi level N(E F) approximately 3.732 × 1024 eV-1 m-3 for silver nanoparticles.
Conclusions
The present wet chemical solution method for the preparation of silver nanoparticles and their thin films is simple, convenient, and viable which allows nanocrystalline silver particles of spherical shape and almost narrow size distribution. The x-ray diffraction pattern of sample shows a face-centered cubic crystalline phase of silver with lattice constant 0.4085 nm. The average particle size, as obtained from FETEM analysis, is 17.5 nm that agreed with XRD results. TGA/DTA study shows that the dominant weight loss occurs between 200°C and 300°C; and the reaction is of exothermic type. The temperature dependence of resistivity of silver film exhibits semiconducting behavior of the sample. The electrical conduction is due to the activated VRH in the localized states near the Fermi level.
References
Schmid G, ed: Nanoparticles: from theory to application. Weinheim:Wiley-VCH; 2004.
Petit C, Lixon P, Pelini MP: In situ synthesis of silver nanocluster in AOT reverse mic. J Phys Chem 1993, 97: 12974. 10.1021/j100151a054
Collier CP, Saykally RJ, Shiang JJ, Henrichs SE, Heath JR: Reversible Tuning of Silver Quantum Dot Monolayers Through the Metal-Insulator Transition. Science 1997, 277: 1978. 10.1126/science.277.5334.1978
Klein DL, Roth R, Lim AKL, Alivwasatos AP, McEuen PL: A single-electron transistor made from a cadmium selenide nanocrystal. Nature 1997, 389: 699. 10.1038/39535
Sastry M, Gole A, Sainkar SR: Formation of patterened, Heterocolloidal nanoparticles thin films. Langmuir 2000, 16: 3553. 10.1021/la990948a
Velev OD, Kaler EW: In Situ Assembly of Colloidal Particles into Miniaturized Biosensors. Langmuir 1999, 15: 3693. 10.1021/la981729c
Ekinci KL, Huang XMH, Roukes ML: Ultrasensitive nanoelectromechanical mass detection. Appl Phys Lett 2004, 84: 4469. 10.1063/1.1755417
Lee WC, Cho YH: Bio-inspired digital nanoactuators for photon and biomaterial Manipulation. Curr Appl Phys 2007, 7: 139. 10.1016/j.cap.2006.03.001
Roos C, Schmidt M, Ebenhoch J, Baumann F, Deubzer B, Weis J: Design and Synthesis of Molecular Reactors for the Preparation of Topologically Trapped Gold Cluster. Adv Mat 1999, 11: 761. 10.1002/(SICI)1521-4095(199906)11:9<761::AID-ADMA761>3.0.CO;2-D
Hong SH, Kim HK, Cho KH, Hwang SW, Hwang JS, Ahn D: Fabrication of single electron transistors with molecular tunnel barriers using ac dielectrophoresis technique. J Vac Sci Technol B 2006, 24: 136. 10.1116/1.2150227
Krenn JR, Weeber JC, Dereux A, Bourillot E, Goudonnet JP, Schider G, Leitner AR, Aussenegg F: Direct observation of localized surface plasmon coupling. Phys Rev B 1999, 60: 5029. 10.1103/PhysRevB.60.5029
Huang Y, Duan X, Wei Q, Lieber CM: Directed Assembly of One Dimensional Nanostructures into Functional Networks. Science 2001, 291: 630. 10.1126/science.291.5504.630
Biswas A, Aktas OC, Schurmann U, Saeed U, Zaporojtchenko V, Faupel F, Strunskus T: Tunable multiple plasmon resonance wavelengths response from multicomponent polymer-metal nanocomposite systems. Appl Phys Lett 2004, 84: 2655. 10.1063/1.1697626
Quinten M: The color of finely dispersed nanoparticles. Appl Phys B Lasers Opt 2001, 73: 317. 10.1007/s003400100666
Stegeman GI, Wright EM: All-optical waveguide switching. Opt. ... Opt Quantum Electron 1999, 22: 95.
Biswas A, Eilers H, Hidden F, Aktas OC, Kiran CVS: Large broadband visible to infrared plasmonic absorption from Ag nanoparticles with a fractal structure embedded in a Teflon AF (R) matrix. Appl Phys Lett 2006, 88: 13103. 10.1063/1.2161401
Wei H, Eilers H: From silver nanoparticles to thin films: Evolution of microstructure and electrical conductionon glass substrates. Journal of Physics and Chemistry of Solids 2009, 70: 459. 10.1016/j.jpcs.2008.11.012
Talley CE, Jackson JB, Oubre C, Grady NK, Hollars C, Lane SM, Huser TR, Nordlander P, Halas NJ: Surface-Enhanced Raman Scattering from Individual Au Nanoparticles and Nanoparticle Dimer Substrates. Nano Lett 2005, 5: 1569. 10.1021/nl050928v
Braun G, Pavel I, Morrill AR, Seferos DS, Bazan GC, Reich NO, Moskovits MJ: Chemically Patterned Microspheres for Controlled Nanoparticle Assembly in the Construction of SERS Hot Spots. Am Chem Soc 2007, 129: 7760. 10.1021/ja072533e
Shegai T, Li Z, Dadosh T, Zhang Z, Xu HX, Haran G: Managing light polarization via plasmon-molecule interactions within an asymmetric metal nanoparticle trimer. Proc Natl Acad Sci USA 2008, 105: 16448. 10.1073/pnas.0808365105
Saito Y, Wang JJ, Smith DA, Batchelder DN: A Simple Chemical Method for the Preparation of Silver Surfaces for Efficient SERS. Langmuir 2002, 18: 2959. 10.1021/la011554y
Lee D, Cohen RE, Rubner MF: Antibacterial Properties of Ag Nanoparticle Loaded Multilayers and Formation of Magnetically Directed Antibacterial Microparticles. Langmuir 2005, 21: 9651. 10.1021/la0513306
Gupta K, Jana PC, Meikap AK: Optical and electrical transport properties of polyaniline-silver nanocomposite. Synthetic Metals 2010, 160: 1566. 10.1016/j.synthmet.2010.05.026
Barnes WL, Dereux A, Ebbesen TW: Surface plasmon subwavelength optics. Nature 2003, 424: 824. 10.1038/nature01937
Pillai S, Catchpole KR, Trupke T, Green MA: Surface plasmon enhanced silicon solar cells. Appl Phys 2007, 101: 93105. 10.1063/1.2734885
Basak D, Karan S, Mallik B: Significant modifications in the electrical properties of poly(methyl methacrylate) thin films upon dispersion of silver nanoparticles. Solid State Commun 2007, 141: 483. 10.1016/j.ssc.2006.12.014
Wang X, Zhuang J, Peng Q, Li Y: A general strategy for nanocrystal synthesis. Nature 2005, 431: 3968.
Wang SH, Qiao XL, Chen JG, Ding SY: Preperation of silver nanoparticles by chemical reduction method. Coll Surf A 2005, 256: 111. 10.1016/j.colsurfa.2004.12.058
Klug HP, Alexander LE: X-ray diffraction procedures for polycrystalline and amorphous materials. New York: Wiley; 1954:491.
Williamson GK, Hall WH: X-ray line broadening from filed aluminium and wolfram L'elargissement des raies de rayons × obtenues des limailles d'aluminium et de tungsteneDie verbreiterung der roentgeninterferenzlinien von aluminium-und wolframspaenen. Acta Metall 1953, 1: 22. 10.1016/0001-6160(53)90006-6
Eckertova L: Physics of thin films. New York: Plenum press; 1984:204.
Venkata Subbaiah YP, Prathap P, Ramakrishna Reddy KT: Structural, electrical and optical properties of ZnS films deposited by close-spaced evaporation. Appl Surf Sci 2006, 253: 2409. 10.1016/j.apsusc.2006.04.063
Demichelis F, Pirri CF, Tresso E: Degree of crystallinity and electrical transport properties of microcrystalline silicon-carbon alloys. Phil Mag B 1993, 67: 331. 10.1080/13642819308220136
Khan MW, Kumar R, Choudhary RJ, Srivastava JP, Patil SI, Choi WK: Electrical transport and 1/f noise properties of LaFe1-xNixO3 (x = 0.3, 0.4 and 0.5) thin films. J Phys D 2008, 41: 175409. 10.1088/0022-3727/41/17/175409
Godet C: Variable range hopping revisited: the case of an exponential distribution of localized states. J Non-Cryst Solids 2002, 333: 299.
Maddison DS, Tansley TL: Variable range hopping in polypyrrole films of a range of conductivities and preparation methods. J Appl Phys 1992, 72: 4677. 10.1063/1.352073
Acknowledgements
Thanks are due to King Abdul Aziz City for Science and Technology (KAACST), Riyadh, Saudi Arabia (Grant No.: 10-NAN1001-02) for providing financial assistance in the form of major research project.
Author information
Authors and Affiliations
Corresponding author
Additional information
Competing interests
The authors declare that they have no competing interests.
Authors' contributions
MAMK participated in the design of the study and performed the electrical studies. SK and MA carried out the structural studies. SAA and MSA performed the thermal studies. MAMK and MA also involved in writing of the manuscript. All authors read and approved the final manuscript.
Authors’ original submitted files for images
Below are the links to the authors’ original submitted files for images.
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 2.0 International License (https://creativecommons.org/licenses/by/2.0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.
About this article
Cite this article
Majeed Khan, M.A., Kumar, S., Ahamed, M. et al. Structural and thermal studies of silver nanoparticles and electrical transport study of their thin films. Nanoscale Res Lett 6, 434 (2011). https://doi.org/10.1186/1556-276X-6-434
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/1556-276X-6-434