Abstract
The high elastic modulus and interlayer strengths of graphite flakes make them a durable solid superlubricant. Apart from this, they have configurable electrical properties, exhibit quantum Hall effects, and possess a myriad of useful photonic properties. The self-retraction behavior of graphite flakes can have significant impact on the creation of ordered stacks for various applications because any accidental or intentional displacement of the top flake over the stacks below may result in a misalignment of the carbon-carbon atomic arrangement which, in turn, can have influence over the electrical and photonic properties. It has also been revealed that there was a tendency of the displaced microflake to fail at times to return to its original starting position and orientation. Here, we elucidate this behavior by considering the influence of the interlayer potential forces based on minimal potential energy seeking. The maps of the parameters interrogated here provide the ability for precautions to be undertaken. They also potentially permit the creation of an array of microflake stacks in which the metastable states permit different information to be encoded by virtue of the differentiated photonic or electrical characteristics readable from each array site.
Avoid common mistakes on your manuscript.
Introduction
The many favorable mechanical, electrical, thermal, and biocompatible properties of graphite render it as an important material. Much work has been expended to investigate the superlubricity [1, 2] between graphite layers where the high elastic moduli and interlayer strengths make it a durable solid lubricant. It also has configurable electrical properties [3–5], exhibits quantum Hall effects [6], and possesses a myriad of useful photonic properties [7–10]. Digressing to the mechanical property aspect of a closely related structure, the ability of nested shells in individual multi-walled carbon nanotubes (MWCNTs) to slide has been known for some time [11, 12]. These MWCNTs have comparable superlubricity as graphite, in which the interwall shear strength against sliding ranges from 0.08 to 0.3 MPa. An interesting behavior of these extracted inner shells is in their ability to self-retract into the outer shells when the extracting force is removed [11]. This has been attributed to the action of van der Waals (vdW) interaction forces [11, 12]. Such a feature has led to the conception of MWCNT-based actuator bearings [13] as well as nanoelectromechanical oscillators which offer the possibility of operating at frequencies in the gigahertz range [14, 15]. More recently, a similar self-retraction capability was demonstrated on two graphite microflakes [16] of equal sizes. Although not mentioned previously, such a behavior can have significant impact in the creation of ordered graphene stacks for various applications. This is because any inadvertent or intentional displacement of the top flake over the stacks below may result in a misalignment of the carbon-carbon atomic arrangement which, in turn, can have influence over the electrical and photonic properties. It has also been revealed that there was a tendency of the displaced microflake to fail at times to return to its original starting position and orientation [16] unlike the MWCNT. Here, we attempt to elucidate this behavior by considering the influence of the interlayer potential forces.
Method
The interlayer interaction between graphite layers has been investigated on perfect sheets [17–19] and on sheets with defects [20]. One method to model the interlayer interaction between graphite layers is to use a Leonard-Jones type of potential. However, such a model may not be sensitive enough to account for the registry of the honeycomb structures and its layers. It is generally accepted that the interlayer interactions are dominated by long-ranged vdW interactions. A registry dependent interlayer interaction potential can be parameterized (see Figure 1a) for layered carbon structures using [21, 22]
where V is registry dependent interlayer potential, subscript i indicates any atom on bottom flake, subscript j indicates any atom on top flake, r ij is distance between atom i and atom j, n is normal vector of corresponding flake, ρ ij is transverse distance between two atoms, f is a function to estimate rapid decay of interlayer potential energy, z0 = 3.34 Å is equilibrium interlayer spacing, λ = 3.629 Å-1, C = 3.03, A = 10.238, δ = 0.578, C0 = 15.71, C2 = 12.29, and C4 = 4.933. The inter-atomic distance of carbon, a = 142 nm, provides a convenient depiction of geometrical size. In our simulations we apply a flake size of 11a and 6a in the × and y axis, respectively (see Figure 1b). Figure 2 traces the potential variations as one perfect graphite layer over one of the same size as a function of the sliding distances in the xy-plane. It can be seen that there is a general increase in potential (more positive indicating less attraction) with sliding distance, thus, accounting for the tendency of the moving flake to self-retract when the motive force to slide is removed. However, the profile contains local potential peaks and troughs. Hence, while the motive force is strong enough to surmount these valleys in the process of moving the flakes apart, the retraction process may engender the flake ceasing to move at the first local trough encountered in the return trip. If we assume the mass of the flake to be small, it is possible to depict the retraction process as a series of quasi-static steps. In each of these steps, which should be small enough, the nearby landscape is interrogated in six ways δ x = δ y = ± 0.01 Å, δφ = ± 0.5° to yield six potentials. In order to arrive at these values, we selected a few displaced positions and orientations and reduced the values until no changes in the return path. The flake can then be taken to advance to the incremental position or orientation based on the lowest of these potentials found if its value is lower than the current potential. Otherwise, the flake is assumed to have arrived at its final retracted state.
In order to characterize the movement more systematically, we adopt the following approach (see Figure 3 in which the distances apart are exaggerated for clarity). The top flake is originally at position I. It is then moved to position II some x-y distance away and rotated by an angle φ to the x-axis. The flake is allowed to perform a series of potential searches at the vicinity of the center of the flake about ± δ x, ± δ y, and δφ to seek for the next position and orientation to retract to. This proceeds sequentially until the flake moves to a rest position III.
Results and discussion
The parameters tracked are (a) the center-to-center distance between positions I and III (AC in Figure 3, (b) the angular displacement of the center-to-center positions of I and III (α in Figure 4), (c) the center-to-center displacement between II and III (BC in Figure 5), and (d) the angular displacement at position III relative to the horizontal (θ in Figure 6). These parameters were traced in relation to × and y distance as well as φ introduced. Only one quadrant of possible movement was explored due to symmetry.
In the plot of distributions of AC using φ = 0° in Figure 4, we find that there is an ability for the top flake center to self-retract to a high degree back to its original position center (e.g. <a). There is a somewhat reducing ability to do this when × and y are increased. This is logical as there is a greater opportunity for the flake to encounter more local minima during retraction even though the overall potential difference is higher with greater displacement. Nevertheless, one finds an easier capability to self -retract fully when displaced in the y as opposed to the × direction. This demeanor is rather preserved despite the angle φ changing, as seen in the other plots with values ranging from 15° to 90° at intervals of 15°. Overall, however, one finds that there are a myriad of states with which the top flake is able to stop at, depending on the displacing positions and orientations. The plot of distributions of α with φ in Figure 5 essentially tells of the quadrant the flake returns to. There were cases wherein if AC was small, the flake may move into other quadrants. Nevertheless, we did not find unexpected cases in which the flake could move to another quadrant when AC was large.
From the plot of distributions of BC with φ = 0° in Figure 6, we find general rings which typically indicate that a flake that is pulled further apart will travel further to try to restore its original position. This is consistent with the potential map shown in Figure 2. Nevertheless one finds that there are islands when the flake is pulled more in the x-direction where BC is zero. This trend mirrors the finding given in Figure 4. From the plot of distributions of θ with φ = 0° in Figure 7, we find that there will generally be large islands of non-rotated states (i.e. θ θ 0°). The other plots indicate that the top flake to mostly θ to mostly rest at the angles with which φ is used. This result infers that the retraction process overall appears to seldom find δφ as the next lower potential step to advance to. However, the map also indicates that there are exceptions to this. We suspect that such cases should closely correspond when the top flake encounters a peak in its path and, thus, undergoes rotation more in order to find the next potential minima.
The landscape maps of Figures 4 to 7 provide us with the ability to analyze the trajectories of certain selected starting conditions. If we consider the case in which the top flake was moved initially to (x = 0.7a, y = 0.2a, φ = 0°), we see from Figures 8 and 9 that it took slightly more than 50 steps before the flake became immobile over a short distance (about 0.2a). From Figure 10, the flake moved towards the x-axis (resulting in α = 0°) when this occurred. Figure 11 informs us that the flake rotated when it encountered the local minima and then restored to its original orientation when it finally came to rest. The situation when the top flake was moved initially to (x = 0.4a, y = 0.2a, φ = 0°) is slightly different. While the flake encountered a local minimum to reside in, this happened at a longer distance away (about 3a) from Figures 8 and 9. The trajectories for α (Figure 10) and θ (Figure 11) were nonetheless unchanged. A significantly larger behavior change occurred when the top flake was moved initially to (x = 7a, y = 0.2a, φ = 30°). With this, the movement trajectory for AC and BC were gradual before the flake eventually came to a rest. The interesting behavior is denoted in Figure 11 wherein the flake is seen to rotate in order to overcome the potential barriers in the way of motion. This is the basis of lubricity as noted previously [17]. When the top flake was moved initially to (x = 0.2a, y = 3a, φ = 0°), a significant degree of self-retraction was achieved (Figures 8 and 9). It is noted that the flake moved slightly towards the right (see Figure 10) in the process but exhibited little rotation (Figure 11).
We highlight certain caveats to the results provided here. The position and orientation tracing approach here assumes that there is no defect in either of the interacting flakes. The ability for graphite layers to be deform has been studied [23], and it is possible that such defects may strongly affect the self-retraction behavior [24]. This will be more evident for micron-scale flakes where the creation of entire interacting regions with perfect lattices is understandably more difficult. Such lattices should, however, be more achievable if the dimensions of the flakes are smaller. It is also important to note that the model here assumes that the force to move the top flake does not comprise an axial component that deforms the lattice. In previous demonstrations of self-retraction behavior, a mechanical probe that depressed and pulled the top flake laterally was utilized [16, 24] in which such an effect cannot be ruled out. The measure of moving the flake with minimal axial deformation will most likely be accomplished using either optical [25], magnetic [26], electrical quadruple ions [27], or vibration [28] that have recently been reported with graphene sheets. The vibration of graphene nanostrips, it appears, offers the possibility of creating bending resonators with high sensitivity to environmental change [28]. It is conceivable, based on the findings here, for metastable misaligned states to appear with each cycle of actuation, to the extent of leaving a wrinkling effect on the sheets [29]. It is also noteworthy that long strips can result in gravity causing the structure to flop downwards. Remedy, however, is available by adopting a dangling arrangement, which has been demonstrated workable in applications associated with wetting monitoring [30, 31].
Conclusions
In summary, we have investigated the self-retraction of a graphite flake over another flake of the same size. This was done using a registry dependent interlayer interaction potential previously reported that is sensitive enough to account for the registry of the honeycomb structures and its layers. Under the assumption that the mass of the flake is small, the retraction process can be depicted as a series of quasi-static steps that seek the lowest potential. The results show that while there is an overall impetus to retract to the original position and orientation to restore to the lowest potential, there is a possibility for the return trajectory to encounter local potential minima that prevents the top flake from restoring fully. Essentially, this means that the graphite flake is able to assume meta-stable states.
Such a behavior can have significant impact in the creation of ordered graphene stacks for various applications. The maps of the parameters that we interrogated here provide the ability for precautions to be undertaken. For instance, any movement in the y direction keeping × and φ constrained will generally result in total retraction. Alternatively, it might be desirable to attain the meta-stable positions and orientations in order to obtain a different photonic or electrical behavior from an aligned stack. The maps then provide a road map to accomplish this. Such a behavior allows one to contemplate the creation of an array of microflake stacks in which the metastable states permit different information to be encoded by virtue of the differentiated photonic or electrical characteristics readable from each array site. Using the maps, these metastable states may be altered to or 'erased' using the retraction behavior to the original stable state. This portends the possibility of high density data recording and retrieval at the nanometer scale. The understanding of the metastable states may also shed light into the wrinkling behavior of graphene sheets, particularly if strips of them are to be used as resonators.
References
Socoliuc A, Bennewitz R, Gnecco E, Meyer E: Transition from stick-slip to continuous sliding in atomic friction: Entering a new regime of ultraflow friction. Phys Rev Lett 2004, 92: 134301.
Dienwiebel M, Verhoeven GS, Pradeep N, Frenken JWM: Superlubricity of graphite. Phys Rev Lett 2004, 92: 126101.
Novoselov KS, Geim AK, Morozov SV, Jiang D, Zhang Y, Dubonos SV, Grigorieva IV, Firsov AA: Electric field effect in atomically thin carbon films. Science 2004, 306: 666–669. 10.1126/science.1102896
Dean CR, Young AF, Meric I, Lee C, Wang L, Sorgenfrei S, Watanabe K, Taniguchi T, Kim P, Shepard KL, Hone J: Boron nitride substrate for high-quality graphene electronics. Nat Nanotechnol 2000, 5: 722–726.
Zhao S, Lv Y, Yang X: Layer independent nanoscale electrical properties of graphene studied by conductive scanning probe microscopy. Nanoscale Res Lett 2011, 6: 498. 10.1186/1556-276X-6-498
Novoselov KS, Jiang Z, Zhang Y, Morozov SV, Stormer HL, Zeitler U, Maan JC, Boebinger GS, Kim P, Geim AK: Room-temperature quantum Hall effect in graphene. Science 2007, 315: 1379. 10.1126/science.1137201
Zhang Y, Tan YW, Stormer HL, Kim P: Experimental observation of the quantum Hall effect and Berry's phase in graphene. Nature 2005, 438: 201–204. 10.1038/nature04235
Liu M, Yin X, Ulin-Avila E, Geng B, Zentgraf T, Ju L, Wang F, Zhang X: A graphene-based broadband optical modulator. Nature 2011, 474: 64. 10.1038/nature10067
Vakil A, Engheta N: Transformation optics using graphene. Science 2011, 332: 1291. 10.1126/science.1202691
Jablan M, Buljan H, Soljacic M: Plasmonics in graphene at infrared frequencies. Phys Rev B 2009, 80: 245435.
Cumings J, Zettl A: Low-friction nanoscale linear bearing realized from multiwall carbon nanotubes. Science 2000, 289: 602–604. 10.1126/science.289.5479.602
Zheng QS, Jiang Q: Multiwalled carbon nanotubes as giga-hertz oscillators. Phys Rev Lett 2002, 88: 045503.
Fennimore AM, Yuzvinsky TD, Han W-Q, Fuhrer MS, Cumings J, Zettl A: Rotational actuators based on carbon nanotubes. Nature 2003, 424: 408–410. 10.1038/nature01823
Guo WL, Guo YF, Gao HJ, Zheng QS, Zhong WY: Energy dissipation in gigahertz oscillators from multiwalled carbon nanotubes. Phys Rev Lett 2003, 91: 125501.
Neild A, Ng TW, Zheng Q: Controlled driven oscillations of double-walled carbon nanotubes. Europhys Lett 2009, 87: 16002. 10.1209/0295-5075/87/16002
Zheng QS, Jiang B, Liu S, Weng Y, Lu L, Xue Q, Zhu J, Jiang Q, Wang S, Peng L: Multiwalled carbon nanotubes as gigahertz oscillators. Phys Rev Lett 2002, 88: 045503.
Verhoeven GS, Dienwiebel M, Frenken JWM: Model calculations of superlubricity of graphite. Phys Rev Lett B 2004, 70: 165418.
Sasaki N, Kobayashi K, Tsukada M: Atomic-scale friction image of graphite in atomic-force microscopy. Phys Rev B 1996, 54: 2138–2149. 10.1103/PhysRevB.54.2138
Sasaki N, Tsukada M, Fujisawa S, Sugawara Y, Morita S, Kobayashi K: Load dependence of the frictional-force microscopy image pattern of the graphite surface. Phys Rev B 1998, 57: 3785–3786. 10.1103/PhysRevB.57.3785
Guo Y, Guo W, Chen C: Modifying atomic scale friction between two graphene sheets: a molecular force-field study. Phys Rev B 2007, 76: 155429.
Kolmogorov AN, Crespi VH: The smoothest bearings: interlayer sliding in multiwalled carbon nanotubes. Phys Rev Lett 2000, 85: 4727. 10.1103/PhysRevLett.85.4727
Kolmogorov AN, Crespi VH: Registry-dependent interlayer potential for graphitic systems. Phys Rev B 2005, 71: 235415.
Fang T-H, Wang T, Yang J-C, Hsiao Y-J: Mechanical characterization of nanoindented graphene via molecular dynamics simulations. Nanoscale Res Lett 2011, 6: 481. 10.1186/1556-276X-6-481
Liu Z, Liu JZ, Yang J, Liu Y, Wang Y, Yang Y, Zheng Q: Self-retracting motion of graphite micro-flakes: superlubricity in micrometer scale. arXiv: 1104.3320 arXiv: 1104.3320
Maragó OM, Bonaccorso F, Saija R, Privitera G, Gucciardi PG, Iat MA, Calogero G, Jones PH, Borghese F, Denti P, Nicolosi V, Ferrari AC: Brownian motion of graphene. ACS Nano 2010, 4: 7515. 10.1021/nn1018126
Simon MD, Geim AK: Diamagnetic levitation: flying frogs and floating magnets (invited). J Appl Phys 2000, 87: 6200. 10.1063/1.372654
Kane BE: Levitated spinning graphene flakes in an electric quadrupole ion trap. Phys Rev B 2010, 82: 115441.
Liu Y, Xu Z, Zheng Q: The interlayer shear effect on graphene multilayer resonators. J MechPhys Solids 2011, 59: 1613–1622. 10.1016/j.jmps.2011.04.014
Wang CY, Mylvaganam K, Zhang LC: Wrinkling of monolayer graphene: a study by molecular dynamics and continuum plate theory. Phys Rev B 2009, 80: 155445.
Panduputra Y, Ng TW, Neild A, Ling WYL: Adhesion force studies using a dangling optical lever with variable sensitivity. Opt Lett 2011, 36: 175–177. 10.1364/OL.36.000175
Ng TW, Panduputra Y: Dynamical force and imaging characterization of superhydrophobic surfaces. Langmuir 2012, 28: 453–458. 10.1021/la203732g
Acknowledgements
Parts of this work were made possible by the support from Australian Research Council Discovery project grant DP0878454. Preliminary discussions with A. Neild are noted.
Author information
Authors and Affiliations
Corresponding author
Additional information
Competing interests
The authors declare that they have no competing interests.
Authors' contributions
TWN directed and provided the critical analysis of the work, CYL, EBC, and NT performed the simulations and refined various implementations of them. JLZ provided critique to the analysis results and developed some numerical checking simulations. JS provided logistical critique to the work. All authors read and approved the final manuscript.
Authors’ original submitted files for images
Below are the links to the authors’ original submitted files for images.
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 2.0 International License (https://creativecommons.org/licenses/by/2.0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly cited.
About this article
Cite this article
Ng, T.W., Lau, C.Y., Bernados-Chamagne, E. et al. Graphite flake self-retraction response based on potential seeking. Nanoscale Res Lett 7, 185 (2012). https://doi.org/10.1186/1556-276X-7-185
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/1556-276X-7-185