Abstract
Resistive random access memory (RRAM) characteristics using a new Cr/GdOx/TiN structure with different device sizes ranging from 0.4 × 0.4 to 8 × 8 μm2 have been reported in this study. Polycrystalline GdOx film with a thickness of 17 nm and a small via-hole size of 0.4 μm are observed by a transmission electron microscope (TEM) image. All elements and GdOx film are confirmed by energy dispersive X-ray spectroscopy and X-ray photoelectron spectroscopy analyses. Repeatable resistive switching characteristics at a current compliance (CC) of 300 μA and low operating voltage of ±4 V are observed. The switching mechanism is based on the oxygen vacancy filament formation/rupture through GdOx grain boundaries under external bias. After measuring 50 RRAM devices randomly, the 8-μm devices exhibit superior resistive switching characteristics than those of the 0.4-μm devices owing to higher recombination rate of oxygen with remaining conducting filament in the GdOx film as well as larger interface area, even with a thinner GdOx film of 9 nm. The GdOx film thickness dependence RRAM characteristics have been discussed also. Memory device shows repeatable 100 switching cycles, good device-to-device uniformity with a switching yield of approximately 80%, long read endurance of >105 cycles, and good data retention of >3 × 104 s at a CC of 300 μA.
Avoid common mistakes on your manuscript.
Background
Recently, resistive random access memory (RRAM) is one of the most potential candidates for future nanoscale non-volatile memory application [1–4]. Under external bias, the resistive switching phenomena have been observed in various types of materials including HfOx[5–10], TaOx[11–16], AlOx[17–20], and so on. Besides binary oxides, some rare-earth materials such as yttrium-oxide (Yb2O3) [21] and gadolinium-oxide (Gd2O3) [22–27] also attract to the researchers for high-performance RRAM application. However, the Gd2O3 is one of the promising materials because of its higher energy bandgap 5.4 eV [28], higher dielectric constant 14 to 20 [28, 29], and good chemical and thermal stability [24]. Most importantly, this can form Gd:Gd2O3 film [22] as well as polycrystalline [22], which will help to have controllable oxygen vacancy filament formation/rupture under external bias. Although, the Gd2O3 material is useful, however, RRAM properties have been reported infrequently. Aratani et al. [23] have reported the conductive bridging RRAM using Cu or a Ag/CuTe/Gd2O3/W structure with an operating current of 100 μA. Cao et al. [24] have reported unipolar resistive switching using a Pt/Gd2O3/Pt structure at high RESET current of approximately 35 mA. Zhou et al. [25] have reported bipolar resistive switching phenomena using a Pt/GdOx/TaNx structure at high current compliance (CC) of 1 mA, and high forming voltage is required to switch the device initially. Wang et al. [26] have also reported resistive switching using a Pt-Al/Gd2O3/W structure at a high CC of 1 mA. Yoon et al. [27] have reported Cu doped MoOx/GdOx bilayer resistive switching characteristics with a CC of 300 μA. In our previous study [22], we have reported self-compliance resistive switching phenomena using IrOx/GdOx/W cross-point structure at a CC of >300 μA. The resistive switching phenomena using a IrOx/GdOx/W via-hole structure at a high CC of >1 mA have also been reported [30]. Generally, resistive switching characteristics of other RRAMs using binary oxides show high current operation [6, 13, 18], and it is reported rare at low current operation [7, 8, 14]. Further, many electrodes such as TiN, Pt, Ir, IrO2, W, Cu, and so on have been also used and known to have high-performance RRAMs; however, the chromium (Cr) in a Cr/Gd2O3/TiN structure has not been reported yet. The work function of Cr is 4.5 eV [31], which is larger than Al of 4.28 eV [31]. Gibbs free energies of Cr2O3 and Gd2O3 are reported -694.88 [32, 33] and -1,730 [34] kJ/mole respectively at 300 K. Therefore, the Cr will not be oxidized easily with respect to Gd2O3 switching material. This is benefited of Cr in the Cr/Gd2O3/TiN structure.
In this study, repeatable bipolar resistive switching characteristics of the Cr/GdOx/TiN RRAM devices at a CC of 300 μA and low operating voltage of ±4 V have been investigated for the first time. Polycrystalline GdOx film and a via-hole size of 0.4 μm are observed by both the transmission electron microscope (TEM) and energy-dispersive X-ray spectroscopy (EDS) analysis. The resistive switching phenomena with variation of device sizes ranging from 0.4 × 0.4 to 8 × 8 μm2 have been discussed. More than 50 randomly picked devices are measured. Large size devices (8 μm) show superior resistive switching characteristics as compared to those of the small size devices (0.4 μm) at a CC of 300 μA. Memory device shows good 100 switching cycles, device-to-device uniformity, program/erase (P/E) endurance of >100 cycles, and long read endurance of >105 cycles. Memory device also shows excellent data retention of more than 3 × 104 s with a large resistance ratio of >70.
Methods
The Cr/GdOx/TiN RRAM devices were fabricated as follows. First, the SiO2 layer with a thickness of 200 nm was deposited on an 8-in Si substrate. Then, TiN as a bottom electrode (BE) was deposited on an SiO2/Si substrate. The thickness of TiN BE was approximately 200 nm. In next step, an SiO2 layer with a thickness of 150 nm was deposited on TiN BE. Then, the via-holes with different sizes ranging from 0.4 × 0.4 to 8 × 8 μm2 and BE contacts were designed and etched. Photo-resist was coated and patterned for switching material and the top electrode (TE) contacts. Therefore, another lithography step was used to pattern the devices for lift-off. After that, a small piece of approximately 1 × 1 in2 was cut from the 8-in patterned wafer and deposited consecutive switching material and the top electrode. The Gd2O3 as a resistive switching material was deposited by an electron-beam evaporation method. Pure Gd2O3 shots were used during evaporation. The deposition rate of Gd2O3 was 0.2 Å/s, and the power was 400 W. After deposition, the Gd2O3 material was a Gd-rich Gd2O3 film which was confirmed by X-ray photo-electron spectroscopy (XPS) analysis [22]. Broad scan of XP spectra is shown in Figure 1a. The Gd (3d, 4 s, 4p, and 4d), O1s, and C1s peaks are also observed. XPS spectra of Gd 3d5/2 and Gd2O3 3d5/2 peaks were located at 1186.73 eV and 1,189 eV, respectively, which confirmed a Gd-rich Gd2O3 film, i.e., GdOx (Figure 1b). The area ratio in between Gd and Gd2O3 is 1:0.89. This suggests that the as-deposited Gd2O3 film is a Gd-rich GdOx film. Then, the Cr TE was deposited by rf sputtering process. Argon (Ar) gas flow rate was 10 sccm during deposition. The deposition power and chamber pressure were 100 W and 6 mTorr, respectively. Finally, a lift-off process was performed to get the final RRAM device. The thickness of the GdOx film was 17 nm. For comparison, the thickness of the GdOx film was also 9 nm. Microstructure of a Gd2O3 film in the RRAM devices was carried out by using TEM-JEOL 2100 F system (JEOL Ltd., Akishima-shi, Japan) with energy of 200 keV and resolution of 0.2 nm. Memory characteristics were performed by using HP 4156C precision parameter analyzer system (Agilent Technologies, Inc., Santa Clara, CA, USA). During electrical measurement of the memory devices, the BE was grounded and the sweeping bias was applied on the TE. All measurements were characterized inside the black box on an 8-in chuck.
Results and discussion
Figure 2a shows the TEM image of the Cr/GdOx/TiN RRAM device. Device size is approximately 0.4 × 0.4 μm2. High-resolution TEM (HRTEM) images at the outside and inside of the via-hole regions are shown in Figure 2b,c, respectively. It is observed that the thickness of the GdOx layer is higher at the outside as compared to the inside regions (23 vs. 17 nm). This occurs owing to the physical vapor deposition method. The thickness of Cr is approximately 70 nm inside the via-hole region. Another layer of TiOx (i.e., TiOxNy) with a thickness of approximately 3 nm inside the via-hole region is observed, as shown in Figure 2c. This is due to the fact that Ti is more reactive with O2 (-888 kJ/mole at 300 K [35]), which results in formation of TiOxNy layer at the GdOx/TiN interface. Figure 2d represents EDS spectra of the Cr/GdOx/TiN RRAM device. The EDS spectra correlates with positions 1, 2, 3, 4, and 5, as shown in Figure 2c, which confirms the presence of Cr, Gd, Ti, O, and N elements in the respective layers. The kinetic energy values of Cr, Gd, Ti, O, and N at maximum peak positions are found to be 5.42, 8.04, 4.52, 0.26, and 0.28 eV, respectively, which are similar to the reported energy values [36–38]. The weight and atomic percentages of each element in each position of Figure 2c have been described in Table 1. From positions 2 and 3, it is observed that the GdOx layer is separated into two sub-layers. The values of weight percentage of O in positions 2 and 3 are 13.3% and 11.2% whereas atomic percentages are 53.1% and 51.6%, respectively. Therefore, the oxygen content is slightly lower at position 3 than that at position 2. This represents that the ‘oxygen-rich’ GdOx layer with a thickness approximately 3 nm is formed at the TE/GdOx interface (i.e., white region at the TE side). It is known that Gibbs free energy of Cr2O3 and Gd2O3 are -694.88 [32, 33] and -1,730 [34] kJ/mole, respectively. During Cr deposition by a sputtering process, it might be possible that few oxygen ions (O2-) from the Gd2O3 film move towards TE to form Cr2O3. According to lower Gibbs free energy of Cr2O3 comparing with Gd2O3, Cr might not be oxidized and O2- ions accumulate at the TE/GdOx interface having formation of oxygen-rich and oxygen-deficient GdOx layers, respectively, as shown in Figure 2c. It is observed that the thickness of GdOx layer at the outside via region is approximately 23 nm (Figure 2b), which is higher than the thickness of GdOx layer at the inside via-hole region (Figure 2c). Therefore, the crystallinity of the GdOx film at the outside region will be more as well as different crystal orientation could be observed, which results to another layer being observed at the Gd2O3/SiO2 interface. The calculated d spacing is 2.695(d200), 2.779(d101), or 3.052 Å (d100) which confirms the GdOx film being polycrystalline, as shown clearly in Figure 3. Crystal grains in the GdOx films are also reported previously [22]. Li et al. [28] also reported the polycrystalline Gd2O3 film deposited by sputtering. This suggests that the Gd2O3 film is polycrystalline in nature, which will have weak bonds on the grain boundary sites and lead to the repeatable resistive switching memory characteristics.
Figure 4 exhibits typical bipolar current-voltage (I-V) characteristics of the Cr/GdOx/TiN RRAM device with a size of 8 × 8 μm2. The thickness of the GdOx film is 17 nm. The sweeping voltage is shown, as indicated by 1 to 5 inside the figure. This RRAM device is operated with a CC of 300 μA. First switching cycle of the memory device shows low formation voltage (Vform) +1.5 V. Initially, memory devices show low leakage current, which is controlled by the size of the device, and defects and thickness of the GdOx film. Figure 5a represents cumulative probability of the leakage currents of randomly measured more than 50 RRAM devices with sizes ranging from 0.4 × 0.4 to 8 × 8 μm2. It is observed that the leakage current increases with increasing device sizes from 2 to 8 μm. A large size device has more defects than that of a smaller device. That is why the 8-sμm devices have the highest leakage current. On the other hand, the leakage currents are the same for the 1- and 0.4-μm devices, which is due to the current measurement limitation by our probe station. The leakage current is increased by decreasing the thickness of the switching layer of 9 nm, as shown in Figure 5a. Basically, both the smaller device size and the thicker GdOx film of 17 nm have smaller leakage current. As similar to the device size dependent leakage current, the Vform also decreases with increasing the device sizes. Figure 5b represents the distribution of the formation voltages of more than 50 RRAM devices. The average values of Vform are found to be 3.5 and 1.9 V for the 2- and 8-μm devices, respectively. However, the average SET voltage (VSET) has little changes from 1.27 to 1.12 V for the 2- to 8-μm devices (Figure 5c). Therefore, the VSET is independent of the device sizes from 2 to 8 μm. This indicates that all 50 devices with size of 8 μm can be operated at a low voltage of <4 V, which would be very useful for practical realization. It is also observed that all 8-μm devices show formation (yield of 100%) whereas the 2-μm devices have only 72% yield. Even after formation, the clear SET is observed only 40% of 2-μm devices. Therefore, some devices do not show RESET. However, the clear SET is observed 78% of the 8-μm devices. The 8-μm device shows a typical VSET (1.2 V) from the second cycle, as shown in Figure 4. After that, the memory device shows good bipolar resistive switching phenomena under small RESET voltage (VRESET) of -1.2 V. The average VRESET value of 50 devices is found to be -1.5 V (Figure 5c). The value of average VRESET is similar or higher than the value of VSET, which is useful for better read operation of these RRAM devices. Even this RRAM device can read at negative voltage because of the higher VRESET values. In Figure 4, the RESET current (IRESET) is found to be 320 μA. This suggests that both SET and RESET currents (300 vs. 320 μA) are almost the same which signifies good current clamping between two electrodes and GdOx switching material. Considering 50 RRAM devices with a size of 8 μm (Figure 5d), the average value of IRESET is higher for the first cycle as compared to the second cycle (320 vs. 390 μA), which is owing to a current overshoot effect during the formation or the first cycle of the pristine device at a CC of 300 μA. However, most of the devices show slightly higher IRESET for the first cycle. The current conduction is understood by fitting an I-V curve in a log-log scale, as shown in Figure 6. Slope value of current at a low resistance state (LRS) is 1.1 (IαV1.1) whereas slope values of current at a high resistance state (HRS) are 1.1 (IαV1.1), 1.8 (IαV1.8), 2.8 (IαV2.8), and 3.6 (IαV3.6) at low to high voltage regions, respectively. The slope values of HRS are reported 1, 2, 4, and 6 by Shang et al. [39], 1.1, 1.3, and 8.5 by Rubi et al. [40], and 1.2, 2.2, and 3.9 by us [41]. This represents that the current transport of LRS is dominating by Ohmic whereas HRS follows by trap controlled space charge limited current conduction (TC-SCLC) of our RRAM device. The resistive switching mechanism is based on the formation and rupture of oxygen vacancy conducting filament in the GdOx material depending upon electrical stimulus. When positive bias is applied on the TE, the weak Gd-O bonds on the grain boundaries break and oxygen ions (O2-) migrate towards the TE and leaving behind oxygen vacancy as well as conducting path formed through polycrystalline grain boundary. Then, the memory device triggers from HRS to LRS. Considering the Gibbs free energy of Cr2O3 and Gd2O3, the Cr TE is not oxidized and a part of GdOx is shown to be oxygen-rich (Figure 2). Basically, the oxygen vacancy filament is formed in between the O-rich GdOx and TiOxNy layers. The oxygen vacancy filaments in different switching materials are also reported by other groups [1, 5, 7]. Both O-rich GdOx and TiOxNy interfacial layers will behave as a series of the conducting filaments, and a current overshoot effect is not observed (Figure 5d). When a negative voltage is applied on the TE, O2- ions are driven out from TE/GdOx interface and re-oxidize the conductive path and memory device switch back from LRS to HRS. Therefore, the O2- ions migrate through crystal grain boundaries and will control the SET/RESET of both the resistance states.
It is observed that the 0.4-μm devices with thicker a GdOx film of 17 nm do not show formation as well as resistive switching phenomena owing to thicker switching layer and smaller active area. By reducing thickness of the GdOx film up to 9 nm, the clear formation and SET operation could be observed even at a smallest size of 0.4 μm in our process. Figure 7a illustrates typical bipolar I-V characteristics for a device size of 0.4 × 0.4 μm2. The device performs consecutive 100 dc cycles with less distribution of LRS and HRS under a CC of 300 μA. The values of Vform, VSET, and VRESET are found to be 2 V, 0.7 V, and -0.7 V, respectively. The values of IRESET are found to be 1.8 mA and 375 μA for the first and second cycles, respectively. After measuring 100 RRAM devices, the values of Vform, VSET, VRESET, and IRESET (first/second cycle) at 50% probability are found to be 1.7 V, 0.9 V, and -0.7 V, and 1.07 mA/391 μA for the 8-μm devices, and those values are found to be 2.5 V, 0.7 V, and -0.8 V, and 1.35 mA/370 μA for the 0.4-μm devices, respectively (not shown here). Therefore, the 8-μm devices have lower formation voltage and smaller RESET current at the first cycle as compared to the 0.4-μm devices, which suggests that larger size devices have a better performance even with the thinner GdOx film of 9 nm. To check the uniformity of the resistance states, we have measured randomly >50 devices and studied statistical distribution of HRS and LRS of device-to-device with device sizes of 0.4 and 8 μm, as shown in Figure 7b. The thickness of the GdOx film is 17 nm for the 8-μm devices and 9 nm for the 0.4-μm devices. Except for few devices which have a small resistance ratio (HRS/LRS) of <2, it is found that the 8-μm device shows better device-to-device uniformity with a high yield >78% as compared to the 0.4-μm devices with a yield >72%. The 8-μm device with a 9-nm-thick GdOx film has also a high yield >88% (not shown here). Further, the 0.4-μm devices show SET failure (Figure 7b), which is reported similar in literature [42]. The values of HRS and LRS for the 8-μm devices at 50% probability are 471.6 and 6.6 kΩ, whereas those values are 126.58 and 4.52 kΩ for the 0.4-μm devices, respectively. The value of LRS is lower for the 0.4-μm devices than those of the 8-μm devices, which is due to higher IRESET. Therefore, it is observed that the 8-μm device exhibits better uniformity and resistance ratio as compared to the 0.4-μm device. This suggests that recombination rate of oxygen ion (O2-) with oxygen vacancy filament is less due to a smaller TE/GdOx interface area for the 0.4-μm devices. So dissolution of oxygen vacancy filament is less for the 0.4-μm devices resulting in higher RESET current, lower resistance ratio, and poor device-to-device uniformity. In the case of the 8-μm devices, recombination rate of oxygen ion (O2-) with oxygen vacancy filament is higher due to a larger TE/GdOx interface area, which results in lower RESET current, higher resistance ratio, and better device-to-device uniformity. Chen et al. [43] reported the oxygen recombination rate dependence improved resistive switching characteristics using HfOx-based RRAMs. The larger interface area has better switching characteristics because of a higher oxygen recombination rate. This implies that the TE/GdOx interface area in the Cr/GdOx/TiN structures plays an important role to have superior switching phenomena. Further study is also needed to unravel the effect of switching performance on different thicknesses of the GdOx layer.
Figure 8a represents I-V characteristics of successive 90 cycles with good uniformity for the 8-μm devices with a GdOx film of 17 nm. This is also confirmed by current distribution of HRS and LRS at a read voltage (Vread) of +0.2 V, as shown in Figure 8b. The memory devices show an excellent cycle-to-cycle uniformity. The average value (μ) of current in HRS and LRS at a Vread of +0.2 V are 290 nA and 32.6 μA respectively and standard deviations (σ) are 0.19 and 9.84, respectively. The memory device performs P/E endurance of >100 cycles with a resistance ratio of >5, as shown in Figure 8c. The P/E voltage was +2.5/-2 V and pulse width was 500 μs. The programming and erasing currents were 300 and 500 μA, respectively. Figure 9 shows read endurance and data retention characteristics of the 8-μm devices with a GdOx film of 17 nm. Figure 9a represents long read endurance characteristics of >105 cycles. Stress pulse width was 500 μs. The read pulse width was 10 ms. Both resistance states were read out at +0.2 V. After 105 cycles, good resistance ratio is found to be >100. Figure 9b exhibits good data retention for more than 3 × 104 s with a resistance ratio of >70. Before a data retention test, the device with a size of 8 μm was programmed or erased at a CC of 300 μA. This new RRAM device is very useful for future nanoscale non-volatile memory applications.
Conclusions
RRAM characteristics by measuring more 50 randomly picked devices in a new Cr/GdOx/TiN structure have been investigated. HRTEM images confirm that a GdOx material exists as polycrystalline and thickness of GdOx layer is 17 nm. The GdOx film is also confirmed by EDS and XPS analyses. Large size of the 8-μm devices show better resistive switching characteristics as compared to those small size of the 0.4-μm devices at a CC of 300 μA under low operating voltage of ±4 V, which is due to higher oxygen recombination rate of oxygen with remaining conducting filament in the GdOx film as well as larger TE/GdOx interfacial area. Switching mechanism is based on formation and rupture of the oxygen vacancy conducting filaments through the GdOx grain boundaries. The 8-μm devices show repeatable switching cycles, good device-to-device uniformity, and long read pulse endurance of >105 cycles. Memory device also performs excellent data retention of more than 3 × 104 s with a high resistance ratio of >70. Therefore, the Cr/GdOx/TiN RRAM device shows a great potential for future nanoscale non-volatile memory application.
References
Prakash A, Jana D, Maikap S: TaOx–based resistive switching memories: prospective and challenges. Nanoscale Research Lett 2013, 8: 418. 10.1186/1556-276X-8-418
Torrezan AC, Strachan JP, Medeiros-Ribeiro G, Williams RS: Sub-nanosecond switching of a tantalum oxide memristor. Nanotechnology 2011, 22: 485203. 10.1088/0957-4484/22/48/485203
Ho CH, Hsu CL, Chen CC, Liu JT, Wu CS, Huang CC, Hu C, Fu-Liang Y: 9nm half-pitch functional resistive memory cell with <1μA programming current using thermally oxidized sub-stoichiometric WOx film. San Francisco, CA: Tech Dig - Int Electron Devices Meet. (IEDM); 2010:436.
Park J, Lee W, Choe M, Jung S, Son M, Kim S, Park S, Shin J, Lee D, Siddik M, Woo J, Choi G, Cha E, Lee T, Hwang H: Quantized conductive filament formed by limited Cu source in sub-5nm era. Washington, DC: Tech Dig - Int Electron Devices Meet. (IEDM); 2011.
Panda D, Huang CY, Tseng TY: Resistive switching characteristics of nickel silicide layer embedded HfO2 film. Appl Phys Lett 2012, 100: 112901. 10.1063/1.3694045
Yu S, Gao B, Dai H, Sun B, Liu L, Liu X, Han R, Kang J, Yu B: Improved uniformity of resistive switching behaviors in HfO2 thin films with embedded Al layers. Electrochem Solid-State Lett 2010, 13: H36. 10.1149/1.3267050
Chen YY, Goux L, Clima S, Govoreanu B, Degraeve R, Kar GS, Fantini A, Groeseneken G, Wouters DJ, Jurczak M: Endurance/retention trade-off on HfO2/metal cap 1T1R bipolar RRAM. IEEE Trans Electron Devices 2013, 60: 1114.
Lee HY, Chen PS, Wu TY, Chen YS, Wang CC, Tzeng PJ, Lin CH, Chen F, Lien CH, Tsai MJ: Low power and high speed bipolar switching with a thin reactive Ti buffer layer in robust HfO2 based RRAM. San Francisco, CA: Tech Dig - Int Electron Devices Meet. (IEDM); 2008:1–4.
Bocquet M, Deleruyelle D, Aziza H, Muller C, Portal JM: Compact modeling solutions for OxRAM memories. J Low Power Electron Appl 2014, 4: 1. 10.3390/jlpea4010001
Long S, Perniola L, Cagli C, Buckley J, Lian X, Miranda E, Pan F, Liu M, Suñé J: Voltage and power-controlled regimes in the progressive unipolar RESET transition of HfO2-based RRAM. Sci Rep 2013, 3: 2929.
Ninomiya T, Wei Z, Muraoka S, Yasuhara R, Katayama K, Takagi T: Conductive filament scaling of TaOx bipolar ReRAM for improving data retention under low operation current. IEEE Trans Electron Devices 2013, 60: 1384.
Schmelzer S, Linn E, Bottger U, Waser R: Uniform complementary resistive switching in tantalum oxide using current sweeps. IEEE Electron Device Lett 2013, 34: 114.
Zhang L, Huang R, Zhu M, Qin S, Kuang Y, Gao D, Shi C, Wang Y: Unipolar TaOx-based resistive change memory realized with electrode engineering. IEEE Electron Dev Lett 2010, 31: 966.
Goux L, Fantini A, Redolfi A, Chen CY, Shi FF, Degraeve R, Chen YY, Witters T, Groeseneken G, Jurczak M: Role of the Ta scavenger electrode in the excellent switching control and reliability of a scalable low-current operated TiN/Ta2O5/Ta RRAM device. Honolulu: Symp. on VLSI Technol; 2014:130.
Yang Y, Choi S, Lu W: Oxide heterostructure resistive memory. Nano Lett 2013, 13: 2908. 10.1021/nl401287w
Prakash A, Maikap S, Banerjee W, Jana D, Lai CS: Impact of electrically formed interfacial layer and improved memory characteristics of IrOx/high-κx/W structures containing AlOx, GdOx, HfOx, and TaOx switching materials. Nanoscale Res Lett 2013, 8: 379. 10.1186/1556-276X-8-379
Chen YS, Chen PS, Lee HY, Wu TY, Tsai KH, Chen F, Tsai MJ: Enhanced endurance reliability and low current operation for AlOx/HfOx based unipolar RRAM with Ni electrode. Solid State Electronics 2014, 94: 1.
Lin CY, Wu CY, Wu CY, Hu C, Tseng TY: Bistable resistive switching in Al2O3 memory thin films. J Electrochem Soc 2007, 154: G189. 10.1149/1.2750450
Wu Y, Yu S, Lee B, Wong P: Low-power TiN/Al2O3/Pt resistive switching device with sub-20 μA switching current and gradual resistance modulation. J Appl Phys 2011, 110: 094104. 10.1063/1.3657938
Baik SJ, Lim KS: Bipolar resistance switching driven by tunnel barrier modulation in TiOx/AlOx bilayered structure. Appl Phys Lett 2010, 97: 072109. 10.1063/1.3481076
Tseng HC, Chang TC, Huang JJ, Chen YT, Yang PC, Huang HC, Gan DS, Ho NJ, Sze SM, Tsai MJ: Resistive switching characteristics of ytterbium oxide thin film for nonvolatile memory application. Thin Solid Films 2011.
Jana D, Maikap S, Prakash A, Chen YY, Chiu HC, Yang JR: Enhanced resistive switching phenomena using low-positive-voltage format and self-compliance IrOx/GdOx/W cross-point memories. Nanoscale Res Lett 2014, 9: 12. 10.1186/1556-276X-9-12
Aratani K, Ohba K, Mizuguchi T, Yasuda S, Shiimoto T, Tsushima T, Sone T, Endo K, Kouchiyama A, Sasaki S, Maesaka A, Yamada N, Narisawa H: A novel resistance memory with high scalability and nanosecond switching. Tech Dig - Int Electron Devices Meet 2007, 783.
Cao X, Li X, Gao X, Yu W, Liu X, Zhang Y, Chen L, Cheng X: Forming free colossal resistive switching effect in rare-earth-oxide Gd2O3 films for memristor applications. J Appl Phys 2009, 106: 073723. 10.1063/1.3236573
Zhou Q, Zhai J: Study of the bipolar resistive-switching behaviors in Pt/GdOx/TaNx structure for RRAM application. Phys Status Solidi A 2014, 211: 173. 10.1002/pssa.201330098
Wang JC, Jian DY, Ye YR, Chang LC, Lai CS: Characteristics of gadolinium oxide resistive switching memory with Pt–Al alloy top electrode and post-metallization annealing. J Phys D Appl Phys 2013, 46: 275103. 10.1088/0022-3727/46/27/275103
Yoon J, Choi H, Lee D, Park JB, Lee J, Seong DJ, Ju Y, Chang M, Jung S, Hwang H: Excellent switching uniformity of Cu-doped MoOx/GdOx bilayer for nonvolatile memory application. IEEE Electron Device Lett 2009, 30: 457.
Li YL, Chena NF, Zhoua JP, Songa SL, Liu LF, Yina ZG, Caia CL: Effect of the oxygen concentration on the properties of Gd2O3 thin films. J Cryst Growth 2004, 265: 548. 10.1016/j.jcrysgro.2004.02.095
Kwo J, Hong M, Kortan AR, Queeney KT, Chabal YJ, Mannaerts JP, Boone T, Krajewski JJ, Sergent AM, Rosamilia JM: High-ϵ gate dielectrics Gd2O3 and Y2O3 for silicon. Appl Phys Lett 2000, 77: 130. 10.1063/1.126899
Jana D, Maikap S, Tien TC, Lee HY, Chen WS, Chen FT, Kao MJ, Tsai MJ: Formation-polarity-dependent improved resistive switching memory performance using IrOx/GdOx/WOx/W structure. Jpn J Appl Phys 2012, 51: 04DD17. 10.7567/JJAP.51.04DD17
Michaelson HB: The work function of the elements and its periodicity. J Appl Phys 1977, 48: 4729. 10.1063/1.323539
Chang WY, Huang HW, Wang WT, Hou CH, Chueh YL, He JR: High uniformity of resistive switching characteristics in a Cr/ZnO/Pt device. J Electrochem Soc 2012, 159: G29. 10.1149/2.092203jes
Li H, Selvaduray G: Ellingham diagram web project. 2014.http://www.engr.sjsu.edu/ellingham/
Dean JA: Lange’s handbook of chemistry. Fifteenth edition. New York: MacGRAH HILL INC; 1998.
Birks N, Meier GH, Pettit FS: Introduction to the high-temperature oxidation of metals. Cambridge University Press; 2006. http://www.doitpoms.ac.uk/tlplib/ellingham_diagrams/interactive.php
Tiwary MK, Singh AK, Sawhney KJS: Analysis of stainless steel samples by energy dispersive X-ray fluorescence (EDXRF) spectrometry. Bull Mater Sci 2001, 24: 633. 10.1007/BF02704012
Vinu S, Sarun PM, Shabna R, Biju A, Syamaprasad U: Enhancement of critical current density and flux pinning properties of Gd-doped (Bi, Pb)-2212 superconductor. J Appl Phys 2008, 104: 043905. 10.1063/1.2969048
Dillon M, Franke C: Diagenetic alteration of natural Fe–Ti oxides identified by energy dispersive spectroscopy and low-temperature magnetic remanence and hysteresis measurements. Phys Earth Planet In 2009, 172: 141. 10.1016/j.pepi.2008.08.003
Shang DS, Wang Q, Chen LD, Dong R, Li XM, Zhang WQ: Effect of carrier trapping on the hysteretic current–voltage characteristics in Ag/La0.7Ca0.3MnO3/Pt heterostructures. Phys Rev B 2006, 73: 245427.
Rubi D, Tesler F, Alposta I, Kalstein A, Ghenzi N, Gomez-Marlasca F, Rozenberg M, Levy P: Two resistive switching regimes in thin film manganite memory devices on silicon. Appl Phys Lett 2013, 103: 163506. 10.1063/1.4826484
Prakash A, Maikap S, Chen WS, Lee HY, Chen F, Tien TC, Lai CS: Device size-dependent improved resistive switching performance. IEEE Trans Nanotechnol 2014, 13: 409.
Balatti S, Ambrogio S, Gilmer DC, Ielmini D: Set variability and failure induced by complementary switching in bipolar RRAM. IEEE Electron Device Lett 2013, 34: 861.
Chen YY, Komura M, Degraeve R, Govoreanu B, Goux L, Fantini A, Raghavan N, Clima S, Zhang L, Belmonte A, Redolfi A, Kar GS, Groeseneken G, Wouters DJ, Jurczak M: Improvement of data retention in HfO2/Hf 1T1R RRAM cell under low operating current. Washington, DC: Tech Dig - Int Electron Devices Meet. (IEDM); 2013:252.
Acknowledgements
This work was supported by National Science Council (NSC) Taiwan, under contract no. NSC-102-2221-E-182-057-MY2. The authors are grateful to EOL/ITRI, Hsinchu, Taiwan, for their experimental support.
Author information
Authors and Affiliations
Corresponding author
Additional information
Competing interests
The authors declare that they have no competing interests.
Authors’ contributions
DJ carried out this research work, and MD and SS helped to measure the memory devices under the instruction of SM. All the authors contributed to the revision of the manuscript, and they approved it for publication.
Authors’ original submitted files for images
Below are the links to the authors’ original submitted files for images.
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made.
The images or other third party material in this article are included in the article’s Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder.
To view a copy of this licence, visit https://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Jana, D., Dutta, M., Samanta, S. et al. RRAM characteristics using a new Cr/GdOx/TiN structure. Nanoscale Res Lett 9, 680 (2014). https://doi.org/10.1186/1556-276X-9-680
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/1556-276X-9-680