Abstract
The AlOx-based resistive switching memory device is fabricated by an oxidation diffusion process that involves depositing an Al film on an ITO substrate and annealing at 400 °C in a vacuum. An AlOx interface layer with a thickness of ~ 20 nm is formed as a resistance switching layer. Bipolar and unipolar resistive switching (RS) behaviours are obtained when the compliance current is limited (≥ 1 mA). In the unipolar RS behaviour, the devices fail to perform set/reset cycles at a low temperature (40 K), which suggests that Joule heating is essential for the unipolar RS behaviour. In the bipolar RS behaviour, the abrupt reset transforms into a gradual reset with decreasing temperature, which suggests that Joule heating affects the rupture of the conductive filament. In addition, the conductive mechanisms in the high-resistance state and low-resistance state are revealed by the temperature dependence of the I-V curves. For the low-resistance state, the conduction mechanism is due to the electron hopping mechanism, with a hopping activation energy of 9.93 meV. For the high-resistance state, transport mechanism is dominated by the space-charge-limited conduction (SCLC) mechanism.
Avoid common mistakes on your manuscript.
Background
Resistive switching random access memory (RRAM) has attracted extensive attention as one of the most promising candidates for next-generation non-volatile memory [1,2,3,4]. Compared with traditional commercialized flash memory and other emerging non-volatile memories, the RRAM device has a simple structure (MIM), fast write/erase speed and excellent endurance and retention performance [5,6,7,8]. As one of the resistive switching materials compatible with conventional complementary metal-oxide semiconductor technology, AlOx-based RRAM has also been extensively studied, having more attractive application potential due to its multilevel storage capability and self-rectification [9, 10]. Generally, two switching types are observed in metal-oxide devices: (1) unipolar switching, which is not dependent on the polarity of the applied voltage and (2) bipolar switching, which relies on the polarity of the applied voltage. Their inherent switching mechanisms are different. Many factors can affect the type of resistive switching, such as the device structure, electrode materials and programming current [11]. The coexistence of unipolar and bipolar switching has been reported in some metal-oxide materials, such as HfO2, NiO and ZnO [12,13,14,15,16]. The bipolar resistive switching (RS) behaviour is related to the formation/rupture of conductive filaments composed of oxygen vacancies. The unipolar RS behaviour is often due to a thermal damage conductive filament or phase structure transition. The bipolar RS behaviour is usually observed in AlOx-based RRAM. The coexistence of unipolar and bipolar behaviours in AlOx RRAM has rarely been reported, and the physical switching mechanism in the unipolar RS behaviour has still not been clarified.
In this paper, we report the coexistence of the unipolar and bipolar RS behaviours in AlOx-based RRAM. By studying the resistive switching characteristics of unipolar and bipolar switching for different compliance currents, Joule heating is used to explain the rupture conductive filaments in the reset process of the unipolar RS behaviour. When the local temperature inside conductive filaments reaches the critical temperature, the conductive filaments are broken, and the unipolar RS behaviour occurs. Moreover, the use of Joule heating to assist in rupturing conductive filaments in the reset process is proposed for the bipolar RS behaviour. The effect of Joule heating is well verified by placing the device at different temperatures. Meanwhile, the performance effect at different temperatures for AlOx RRAM is also investigated. The stability and controllability of the RS behaviour is essential for applying RRAM arrays in the future. A deeper understanding of the effect of Joule heating in the resistive switching process is important and necessary. Moreover, we investigate the conductive mechanism by the temperature dependence of the current for high-resistance state (HRS) and low-resistance state (LRS).
Methods
The resistive switching memory devices based on AlOx are fabricated by the following process. The schematic diagram is shown in Fig. 1(a)–(d). The Al and Pt are sputtered on the surface of the ITO glass substrate in sequence with a shadow mask to form circular spots with a 200-μm diameter. The Pt layer covering the Al can be used to avoid oxidation of the Al surface during the following annealing process. The device is annealed at 400 °C for 4 h in a vacuum. An unannealed sample is used for reference. The cross-section scanning electron microscope (SEM) photograph reveals the structure of the device. A three-layer structure of the annealed Pt/Al/ITO device is shown in the inset of Fig. 1(e). The top layer is a Pt electrode (~ 66 nm). The middle layer is an annealed Al layer (~ 256 nm). The bottom layer is an ITO electrode (~ 161 nm). The microstructure of the device is analysed by high-resolution transmission electron microscopy (HRTEM). The distribution of elements is obtained by using energy dispersive X-ray (EDX) spectroscopy on the same equipment. The I-V test is carried out using the Agilent B1500A semiconductor parameter analyser in dc sweep mode at room temperature. The temperature dependence of the I-V characteristic is detected in the Lake Shore CRX-4K system under a vacuum of 5 × 10−5 Torr.
Results and Discussion
To check the microstructure changes after annealing the Pt/Al/ITO devices, HRTEM is used to check the region between the Al and ITO glass substrates. Figures 2a and b show the unannealed and annealed samples, respectively. Compared to the unannealed sample, an obvious interface layer is found in the annealed sample after 4 h. The thickness of the interface layer is ~ 20 nm. The EDX spectra are used to identify the element distribution between Al and ITO, as shown in Fig. 2c. An obvious diffusion of oxygen atoms occurred at the interface of the Al/ITO interface during the annealing process. Other elements (In, Sn) do not display significant diffusion in the EDX spectra. Compared to other metals, Al has a lower standard Gibbs free energy (− 1582.9 KJ/mol) to form the corresponding metal oxides [17]. We infer that the interface AlOx layer formed during the annealing process.
Figure 3a shows the unannealed sample current-voltage (I-V) characteristic. No resistive switching behaviour is observed, which is consistent with the unannealed TEM results. No AlOx resistive switching layer is formed. The inset shows a schematic diagram of the electrical measurement. During the I-V measurement, the voltage is applied to the top electrode (Pt), and the bottom electrode (ITO) is grounded. The annealed devices are also measured under the same conditions. The annealed device shows the coexistence of the unipolar and bipolar RS behaviours. The two RS behaviours can be activated independently. Figure 3b shows 50-cycle sweep curves of the unipolar RS behaviour. The compliance current is set to 10 mA to avoid hard breakdown of devices during the set process. The arrows indicate the voltage sweeping direction. A positive voltage sweep (0 V → 3.5 V) is applied to the Pt electrode. The device switches from a high-resistance state to a low-resistance state (set process or programming process). Afterward, another voltage sweep (0 V → 1 V) causes an abrupt current reduction with the compliance current removed. The device switches to the HRS (reset process or erasing process). No obvious larger forming voltage is required to activate the device. The inset displays the 80-cycle endurance characteristics, and the ratio of Ron/Roff is approximately 103 using a read voltage of 0.1 V. Figure 3c shows the bipolar RS behaviour. The RS behaviour is observed in the opposite voltage polarity. The set and reset sweeping voltages follow the sequence of 0 V → +3.4 V → 0 V → − 2.5 V → 0 V. The device switches from the HRS to the LRS when a positive bias voltage is applied to the Pt top electrode. Then, it is switched back to the HRS under a negative bias voltage. Similar to the unipolar case, no obvious electroforming process is observed. The inset shows the endurance characteristics for 150 cycles. The ratio of Ron/Roff is approximately 103 using a read voltage of 0.1 V.
Generally, the bipolar RS behaviour is often observed in AlOx-based RRAM devices. The bipolar switching mechanism is due to forming/rupturing conductive filaments composed of oxygen vacancies [11, 16]. When a positive voltage is applied to the top electrode, the oxygen ions (O2−) migrate to the top electrode, leaving oxygen vacancies. Oxygen vacancies are accumulated to form the conductive filaments. The device switches to the LRS. When a negative voltage is applied to the top electrode, the oxygen ions are extracted back to AlOx and the conductive filaments rupture. The bipolar switching mechanism is related to the electrochemical mechanism. However, the set process and reset process occur with the same voltage polarity for the unipolar switching behaviour. The unipolar resistive switching is triggered by conductive filament thermal breakdown. The switching mechanism is explained by a thermal-based mechanism in other RRAM devices [16]. To verify that the Joule heating accounts for the unipolar switching behaviour in AlOx RRAM, a different compliance current is used to control the current flow through the device.
Figure 4a shows the I-V characteristic of the bipolar switching behaviour for different compliance currents. The conductive filament resistance can be controlled by the setting compliance current. A lower resistance of the LRS (Icc = 10 mA, RLRS ~ 40 Ω; Icc =1 mA, RLRS ~ 300 Ω; Icc = 100 uA, RLRS ~ 8 KΩ) can be obtained by increasing the compliance current. The resistance in the LRS (RLRS) varies from tens of ohms to thousands of ohms under different compliance currents. The different RLRS values are related to the formation of different conductive filament sizes under different compliance currents. Joule heating decreases with decreasing filament size [18]. Notably, when the compliance current Icc = 100 uA and Icc = 1 mA, a gradual reset process is observed during the reset process in the bipolar RS behaviour, which is different from the abrupt reset at Icc = 10 mA. The gradual reset is explained by the progressive rupture of the conductive filament [19]. The abrupt reset is related to Joule heating assistance rupture [20]. The influence of Joule heating on the bipolar RS behaviour is reflected in the abrupt reset process. The bipolar RS behaviour can be considered a combination of an electrochemical mechanism and Joule heating at high programming currents [13, 21].
Figure 4b shows the unipolar characteristics under different compliance currents (Icc = 10 mA, Icc = 1 mA and Icc = 100 uA). The unipolar switching is observed only at a compliance current Icc = 10 mA and 1 mA. Compared to the reset voltage of the compliance current Icc = 10 mA within 1 V, the reset voltage (Icc = 1 mA) is obviously increased over 1.5 V and the reset current decreases by approximately two orders of magnitude (~ 724 uA) after the reset operation. The current value after the reset process approximates the compliance current. The device cannot reset to the initial state (~ 100 KΩ). Russo et al. proposed the critical temperature (Tcrit) for the unipolar reset process in the self-accelerated thermal dissolution model [22]. When the temperature inside the conductive filament reaches the critical value under an applied reset voltage between the two electrodes, the conductive filament is dissolved and broken in the reset state. The function relationship among the critical temperature, voltage, current and resistance can be described as follows:
T0 is room temperature, Rth is the effective thermal resistance of the conductive filament, which has a weaker size dependence, and the electric power can be written asPreset = Vreset · Ireset. For the lower compliance current Icc = 1 mA, a larger reset voltage is needed. When the hottest point of the conductive filament reaches the critical temperature, the thermal stability of the conductive filament worsens. The conductive filaments subsequently rupture. The unipolar RS behaviour then occurs. However, the LRS current is smaller for compliance current Icc = 100 uA. Even if the reset voltage increases, the current value faces difficulty in reaching the current level at the larger compliance current (Icc = 1 mA and Icc = 10 mA). The Joule heating generated is not sufficient to reach the critical temperature. Thus, no unipolar RS behaviour is observed. If the reset voltage is increased further, the device may break. Therefore, the unipolar RS behaviour is driven by Joule heating in AlOx RRAM.
For further research on the influence of Joule heating on the RS behaviour, the devices are placed at different temperatures. During the set process, the compliance current Icc = 10 mA is used. The I-V curves of the bipolar behaviour are shown in Fig. 5a. It is worth noting that the abrupt reset process transforms into a gradual reset process with decreasing temperature down to 40 K. Compared to 300 K and 340 K, the Joule heating can be well dispersed at 40 K. The effect of the Joule heating can be reduced to a minimum. Thus, the electrochemical mechanism plays a major role during the reset process in the bipolar switching behaviour. The gradual reset process is explained by a partially ruptured conductive filament. The device cannot be reset to the initial state at the same reset voltage. This phenomenon is also observed in other metal-oxide materials [23]. Figures 5b and c show the statistical distribution of the operating current (HRS, LRS) and voltage (SET, RESET) in bipolar switching at different temperatures. Clearly, the HRS current decreases with increasing temperature. In addition, the SET voltage increases with increasing temperature. These observations suggest that the Joule heating affects the breakage of the conductive filaments. When the temperature is raised, fewer conductive filaments remain in the AlOx resistive switching layer during the reset process. More insulating high-resistance states are obtained. The SET voltage obviously increases. The LRS current slightly increases with increasing temperature, which corresponds to the characteristic transport of a semiconductor. Figure 5d shows the I-V characteristic of the unipolar behaviour at different temperatures. Compared to 300 K and 340 K, the device cannot reset to the initial state at 40 K, which is due to thermal dissipation. The temperature inside the conductive filament does not reach the critical temperature. The conductive filament cannot be completely ruptured. The device cannot switch to the LRS again at the compliance current Icc = 10 mA (the blue dotted line). Figures 5e and f show the statistical distribution of the operating current (HRS, LRS) and voltage (SET, RESET) under unipolar switching at different temperatures. Similarly, a higher HRS current and a larger SET voltage with increasing temperature are observed. Thus, Joule heating is considered essential for the unipolar RS behaviour.
For a better study of the conduction mechanism, we preliminarily estimate the switching mechanism by fitting the I-V curve. The I-V curve is re-plotted in a double-logarithmic plot, as shown in Fig. 6a. The LRS shows an Ohmic conducting behaviour with a slope close to 1, which is probably caused by the formation of conductive filaments [24]. The HRS can be divided into two regions: in the low-voltage area (< 0.4 V, region 1), the Ohmic conduction behaviour is observed, whereas in the high-voltage area (> 0.4 V, region 2), the slope is close to 2. The transport behaviour is consistent with the space-charge-limited conduction (SCLC) [25]. In the SCLC model, the current density J for trap-controlled SCLC emissions can be described as
where q is the elementary charge, n0 is the thermally generated free carriers, μ is the electron mobility, εr is the static dielectric constant, ε0 is the permittivity of the space, θ is the ratio of the free carrier density to total carrier density, V is the applied voltage and d is the film thickness. In region 1 (low applied voltage), corresponding to Ohm’s law (I ∝ V1), a small number of carriers may be generated due to thermal excitation and excited to the conduction band from the valence band or the impurity level in this region. When the applied voltage increases, the injected carriers become trapped. The conduction becomes space-charge-limited. The current of the HRS follows a square law (I ∝ V2) in region 2. Figure 6b shows the temperature dependence of the HRS current. The current increases with increasing temperature, which suggests a semiconductor-like conducting behaviour [26, 27]. From the slopes of Arrhenius-type plots of the data (the inset of Fig. 6c), the activation energy (Eα) from 0.01 V to 2 V is as summarized in Fig. 6c. The results indicate that Eα is relatively high (~ 0.15 eV) in the low-voltage region and shows Ohmic conduction behaviour. As the voltage increases, Eα decreases, which is a characteristic feature of SCLC [28]. The temperature-dependent I-V analyses clearly support the SCLC conduction mechanism in the HRS.
Figure 6d shows that the current of the LRS slightly increases with increasing temperature, showing a semiconductor-like conducting behaviour. Metal conductive filaments are excluded. Figure 6e shows a linear relationship between ln (I) and T−1/4, which suggests that the mechanism of the LRS obeys Mott’s variable range hopping model [29, 30]. If the energy levels of two localized states are close enough and the wave functions overlap, electrons can hop between the two sites, assisted by thermal energy. The value of activation energy Eα is 9.93 meV for the LRS, as shown in Fig. 6f, which is smaller than 26 meV (the activation energy at room temperature). This value ensures the variable range hopping of the electrons at room temperature. In other metal-oxide semiconductors, the hopping mechanism is also observed in the LRS, and the I-V curve fitting shows the Ohmic conductive behaviour at room temperature [31]. Thus, the resistive switching mechanism in the LRS is related to oxygen vacancies in the conductive filaments.
Figure 7 illustrates the unipolar and bipolar resistive switching models. For the unipolar and bipolar RS behaviours in the set process, oxygen ions migrate towards the top electrode under an electric field. Finally, the oxygen ions are reduced, leaving oxygen vacancies in the AlOx resistive switching layer. A large accumulation of oxygen vacancies forms oxygen conductive filaments between the ITO and unoxidized Al layers. The device is set to the LRS. The electrons hop through the conductive filament composed of oxygen vacancies, as shown in Fig. 7(a) and (c). For the unipolar RS behaviour in the reset process, the compliance current is removed. The positive bias is applied again, and the current increases with increasing voltage. When the highest temperature point inside the conductive filament reaches the critical temperature, the stability of the conductive filament becomes worse and is easily broken. The device switches to the HRS after the conductive filament is destroyed, as shown in Fig. 7(b). In the bipolar RS behaviour, a negative bias is applied to the top electrode. Oxygen ions are extracted back to the AlOx interface layer. The conductive filaments rupture, as shown in Fig. 7(d). The device is reset to the HRS. When the reset current is relatively larger, Joule heating enhances the conductive filament rupture process. An abrupt transition in the reset process appears. The electron transport mechanism in the HRS is dominated by the SCLC mechanism in both RS behaviours.
Conclusions
In this paper, the coexistence of the unipolar and bipolar resistive switching behaviours is observed in AlOx-based RRAM. By researching the current-voltage characteristics of the unipolar and bipolar switching at different compliance currents and varying work temperatures, we propose that Joule heating is essential for the unipolar resistive switching behaviour in AlOx-based RRAM. When a high programming current flows through the conductive filament in the reset process, the local temperature in the conductive filaments reaches the critical temperature, and the conductive filaments rupture. Unipolar RS behaviour occurs. In the bipolar resistive switching behaviour, the reset process is attributed not only to the electrochemical mechanism but also to the Joule heating. Thermal prompts rupture of the conductive filament when the device has a high erase current, which results in higher resistance of the HRS and a larger SET operating voltage in AlOx-based RRAM. Thus, Joule heating is a non-negligible factor of the RS performance. These results will help us deeply understand the influence of Joule heating on the resistive switching behaviour in AlOx-based RRAM. Furthermore, the conductive mechanism is studied. The conductive mechanism for the LRS is due to the electrons hopping through conductive paths. For the HRS, the conductive mechanism is dominated by the SCLC mechanism.
Availability of Data and Materials
All data and materials are available without restriction.
Abbreviations
- RS:
-
Resistive switching
- SCLC:
-
Space-charge-limited conduction
- RRAM:
-
Resistive switching random access memory
- HRS:
-
High-resistance state
- LRS:
-
Low-resistance state
- SEM:
-
Scanning electron microscope
- HRTEM:
-
High-resolution transmission electron microscopy
- EDX:
-
Energy dispersive X-ray spectroscopy
References
Wedig A, Luebben M, Cho D-Y, Moors M, Skaja K, Rana V, Hasegawa T, Adepalli KK, Yildiz B, Waser R and Valov I: Nanoscale cation motion in TaOx, HfOx and TiOx memristive systems. Nat. Nano. 2016, 11:67.
Zhou YX, Li Y, Su YT, Wang ZR, Shih LY, Chang TC, Chang KC, Long SB (2017) Sze SM and Miao: nonvolatile reconfigurable sequential logic in a HfO2 resistive random access memory array. Nanoscale 9:6649
Leiwen G, Yanhuai L, Qin L, Zhongxiao S, Fei M (2017) Enhanced resistive switching characteristics in Al2O3 memory devices by embedded Ag nanoparticles. Nanotechnology 28:215201
Yoon JH, Song SJ, Yoo IH, Seok JY, Yoon KJ, Kwon DE, Hwang CS (2014) Highly uniform, electroforming-free, and self-rectifying resistive memory in the Pt/Ta2O5/HfO2-x/TiN structure. Adv. Funct. Mater. 24:5086
Writam B, Xumeng Z, Qing L, Hangbing L, Qi L, Shibing L, Ming L (2018) Design of CMOS compatible, high-speed, highly-stable complementary switching with multilevel operation in 3D vertically stacked novel HfO2/Al2O3/TiOx (HAT) RRAM. Adv. Electron. Mater. 4:1700561
Kim KH, JoS H, Gaba S, Lu W (2010) Nanoscale resistive memory with intrinsic diode characteristics and long endurance. Appl. Phys. Lett 96:053106
Lee MJ, Lee CB, Lee D, Chang M, Hur JH, Kim YB, Kim CJ, Seo DH, Seo S, Chung UI, Yoo IK, Kim K (2011) A fast, high-endurance and scalable non-volatile memory device made from asymmetric Ta2O5-x/TaO2-x bilayer structures. Nat. Mater. 10:625
Wang M, Cai S, Pan C, Wang CY, Lian XJ, Zhuo Y, Xu K, Cao TJ, Pan XQ, Wang BG, Liang SJ, Yang JJ, Wang P, Miao F (2018) Robust memristors based on layered two-dimensional materials. Nature Electronics 9:1822
Yuan F, Wang JC, Zhang Z, Ye YR, Pan L, Xu J, Lai CS (2014) Hybrid aluminum and indium conducting filaments for nonpolar resistive switching of Al/AlOx/indium tin oxide flexible device. Applied Physics Express 7:024204
Tran XA, Zhu W, Liu WJ, Yeo YC, Nguyen BY and Yu HY: A self-rectifying AlOy bipolar RRAM with sub-50-μA set/reset current for cross-bar architecture 2012 IEEE Electron Device Lett. 2012, 33:1402.
Waser R, Dittmann R, Staikov G, Szot K (2009) Redox-based resistive switching memories–nanoionic mechanisms, prospects, and challenges. Adv. Mater. 8:418
Goux, L., Chen, Y. Y., Pantisano, L., Wang, X. P., Groeseneken, G., Jurczak, M., & Wouters, D. J : On the gradual unipolar and bipolar resistive switching of TiN\HfO2\Pt memory systems. Electrochem. Solid-State Lett. 2010, 13: G54.
Gou L, Lisoni JG, Jurczak M, Wouters DJ, Courtade L, Muller C (2010) Coexistence of the bipolar and unipolar resistive-switching modes in NiO cells made by thermal oxidation of Ni layers. J. Appl. Phys. 107:024512
Lee S, Kim H, Park J (2010) Yong, K: Coexistence of unipolar and bipolar resistive switching characteristics in ZnO thin films. J. Appl. Phys. 108:076101
Chen, J. Y., Hsin, C. L., Huang, C. W., Chiu, C. H., Huang, Y. T., Lin, S. J., Chen, L. J: Dynamic evolution of conducting nanofilament in resistive switching memories. Nano lett. 2013, r: 3671-3677.
Yang Y (2013) Lu, W: Nanoscale resistive switching devices: mechanisms and modeling. Nanoscale 5:10076
Li Q, Qiu L, Wei X, Dai B, Zeng H (2016) Point contact resistive switching memory based on self-formed interface of Al/ITO. Sci. Rep. 6:29347
Ielmini D, Nardi F, Cagli C (2011) Physical models of size-dependent nanofilament formation and rupture in NiO resistive switching memories. Nanotechnology 22:254022
Wu Y, Yu S, Lee B, Wong P (2011) Low-power TiN/Al2O3/Pt resistive switching device with sub-20 μA switching current and gradual resistance modulation. J. Appl. Phys. 110:094104
Zhou P, Ye L, Sun QQ, Wang PF, Jiang AQ, Ding SJ, Zhang DW (2013) Effect of concurrent joule heat and charge trapping on RESET for NbAlO fabricated by atomic layer deposition. Nanoscale research letters 8:91
Chang SH, Lee JS, Chae SC, Lee SB, Liu C, Kahng B, Noh TW (2009) Occurrence of both unipolar memory and threshold resistance switching in a NiO film. Phys. Rev. Lett. 102:026801
Russo U, Ielmini D, Cagli C, Lacaita AL (2009) Self-accelerated thermal dissolution model for reset programming in unipolar resistive-switching memory (RRAM) devices. IEEE Transactions on Electron Devices 56:193
Chen YS, Lee HY, Chen PS, Wu TY, Wang CC, Tzeng PJ (2010) Lien, C: An ultrathin forming-free HfOx resistance memory with excellent electrical performance. IEEE Electron Device Lett. 31:1473
Chiu FC: A review on conduction mechanisms in dielectric films. Advances in Materials Science and Engineering, 2014.
Kim KM, Choi BJ, Lee MH, Kim GH, Song SJ, Seok JY, Hwang CS (2011) A detailed understanding of the electronic bipolar resistance switching behavior in Pt/TiO2/Pt structure. Nanotechnology 22:254010
Yang YC, Pan F, Liu Q, Liu M, Zeng F (2009) Fully room-temperature-fabricated nonvolatile resistive memory for ultrafast and high-density memory application. Nano Lett. 9:1636
Leiwen G, Yanhuai L, Qin L, Zhongxiao S, Fei M (2017) Enhanced resistive switching characteristics in Al2O3 memory devices by embedded Ag nanoparticles. Nanotechnology 28:215201
Shao XL, Zhou LW, Yoon KJ, Jiang H, Zhao JS, Zhang KL, Yoo S, Hwang C (2015) Electronic resistance switching in the Al/TiOx/Al structure for forming-free and area-scalable memory. Nanoscale 7:11063
Choi S, Yang Y, Lu W (2014) Random telegraph noise and resistance switching analysis of oxide based resistive memory. Nanoscale 6:400
Zhang Y, Deng N, Wu H, Yu Z, Zhang J, Qian H (2014) Metallic to hopping conduction transition in Ta2O5− x/TaOy resistive switching device. Appl. Phys. Lett. 105:063508
Yan P, Li Y, Hui YJ, Zhong SJ, Zhou YX, Xu L, Liu N, Qian H, Sun HJ, Miao XS (2015) Conducting mechanisms of forming-free TiW/Cu2O/Cu memristive devices. Appl. Phys. Lett. 107:083501
Acknowledgements
The authors gratefully acknowledge the financial support for this work by National Nature Science Foundation of China. The experiment equipment was supported by Nation Laboratory of Solid State Microstructures in Nanjing University.
Funding
This study was supported by the National Nature Science Foundation of China (grant nos. 61071008, 61634003, 61376004 and 11374153.
Author information
Authors and Affiliations
Contributions
WL carried out the sample fabrication. LX, ZM, HZ, JL, DT and LC participated in the manuscript discussion of results. All authors read and approved the final manuscript.
Corresponding author
Ethics declarations
Competing Interest
The authors declare that they have no competing interests.
Additional information
Publisher’s Note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Rights and permissions
Open Access This article is distributed under the terms of the Creative Commons Attribution 4.0 International License (http://creativecommons.org/licenses/by/4.0/), which permits unrestricted use, distribution, and reproduction in any medium, provided you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made.
About this article
Cite this article
Zhang, X., Xu, L., Zhang, H. et al. Effect of Joule Heating on Resistive Switching Characteristic in AlOx Cells Made by Thermal Oxidation Formation. Nanoscale Res Lett 15, 11 (2020). https://doi.org/10.1186/s11671-019-3229-y
Received:
Accepted:
Published:
DOI: https://doi.org/10.1186/s11671-019-3229-y