Abstract
Currently available anti-erosive agents only provide partial protection, emphasizing the need to enhance their performance. By characterizing erosive enamel wear at the nanoscale, the aim of this in vitro study was to assess the anti-erosive effects of SnF2 and CPP-ACP both individually and synergistically. Erosion depths were assessed longitudinally on 40 polished human enamel specimens after 1, 5, and 10 erosion cycles. Each cycle comprised one-min erosion in citric acid (pH 3.0) and one-min treatment in whole saliva (control group) or a slurry of one of the three anti-erosive pastes (10% CPP-ACP; 0.45% SnF2 (1100 ppm F); or SnF2/CPP-ACP (10% CPP-ACP + 0.45% SnF2)) (n = 10 per group). Scratch depths were assessed longitudinally in separate experiments using a similar protocol after 1, 5, and 10 cycles. Compared with the control groups, all slurries reduced erosion depths after 1 cycle (p ≤ 0.004) and scratch depths after 5 cycles (p ≤ 0.012). The order of anti-erosive potential was SnF2/CPP-ACP > SnF2 > CPP-ACP > control for erosion depth analysis, and SnF2/CPP-ACP > (SnF2 = CPP-ACP) > control for scratch depth analysis. These data provide ‘proof of concept’ evidence that SnF2/CPP-ACP has superior anti-erosive potential compared to SnF2 or CPP-ACP alone.
Similar content being viewed by others
Introduction
Dental erosion refers to the irreversible loss of tooth structure from acids without bacterial involvement1. Its causes include both extrinsic factors (e.g., acidic beverages around pH of 2.5–4.0)2,3 and intrinsic factors (e.g., gastric regurgitation at around pH of 1.2–3.0)4 that can be exacerbated by mechanical wear (e.g., tooth grinding and toothbrush abrasion)5. Erosive wear refers to the wear process in which dental erosion is the primary aetiological factor6, and it is a condition of growing concern in both children and young adults because of increasing trends of acidic beverage consumption in recent years7. Erosive wear is cumulative over the lifetime and can result in heavily worn, debilitating dentition8. Therefore, clinical management should focus on early detection, prevention, stabilization, and minimally invasive approaches for aesthetic and functional rehabilitation as required9.
There is a consensus that surface protection plays a larger role in erosion inhibition than remineralization, given that remineralization only repairs the eroded ends of hydroxyapatite crystals rather than promoting true crystal growth10. Conventional fluorides, such as sodium fluoride (NaF) and amine fluoride, are commonly used in commercially available anti-erosive agents in various formulations11. Several alternative agents are also available in the form of calcium phosphate-based systems, polyvalent metals (e.g., Sn2+ and Ti4+), polymers (e.g., chitosan), adhesives (e.g., sealants), and protease inhibitors (e.g., chlorhexidine)12.
Conventional fluorides form a CaF2-like layer on the tooth surface and offer partial protection from dental erosion13, but polyvalent metal ions (e.g., Sn2+) have the added advantage of being incorporated into the demineralized tooth structure14 as well as forming a protective coating14,15. Fluoride alone may become insufficient in protecting teeth from demineralization under xerostomic conditions because of the low availability of Ca2+ and PO4–3 ions16. In comparison, calcium phosphate supplements, e.g., casein phosphopeptide-amorphous calcium phosphate (CPP-ACP), can replenish the depleted Ca2+ and PO4–3 ions17 in addition to forming a protective nanofilm against erosive tooth wear18,19,20. Limited evidence suggests that fluoride has a greater anti-erosive potential than calcium and phosphate13 and that the combination of CPP-ACP and NaF is more effective than the individual components21. However, currently available commercial products have limited anti-erosive potential that fall short of providing population-level benefits22.
Recently, SnF2 and CPP-ACP have been combined to form a stable paste composition that has been shown to enhance the protective effects of SnF2 in preventing demineralization and promoting remineralization of subsurface enamel (carious) lesions in vitro and in situ23,24. The inclusion of CPP-ACP with SnF2 was reported to enhance the uptake of Sn and F into the enamel compared with SnF2 alone24. These results suggest that SnF2 and CPP-ACP combined may also exhibit superior anti-erosive properties; however, to date, this has not been studied.
By using a novel technique for bioceramic wear characterization at the nanoscale, the aim of this in vitro study was to assess the anti-erosive effects of SnF2 and CPP-ACP both individually and synergistically at pH 3.0. The null hypothesis was that the combination of CPP-ACP with SnF2 would not significantly enhance protection against enamel erosion.
Results
Quantitative assessment
The changes in erosion and scratch depths in different groups from baseline to Stages 1, 2 and 3 are shown in Figs. 1 and 2, and their statistical outputs are shown in Table 1. The raw data are presented in Supplementary Table S1. The mean erosion depths in the control group (Group 0) were 69.4 nm after 1 min, 252.4 nm after 5 min, and 518 nm after 10 min, and the corresponding scratch depths were 29.4 nm, 207.0 nm, and 449.8 nm, respectively.
Linear mixed-effects modeling showed significant interactions between Group and Stage for erosion depth (p < 0.001), indicating that the associations between erosion depth and Group were dependent on Stage and vice versa. Post hoc pairwise comparisons for stages (baseline, S1, S2 and S3) showed the following trends: (i) between baseline and other stages (12 comparisons): significant increases from baseline to other stages (p ≤ 0.029), except one comparison of baseline vs Stage 1 in Group 3 (p = 0.105); and (ii) between S1 vs S2 vs S3 (12 comparisons): significant increases at later stages (p ≤ 0.017), except two comparisons of Stage 1 versus Stage 2 (p = 0.122) and Stage 2 vs Stage 3 (p = 0.117), in Group 3. Post hoc pairwise comparisons between groups (control group vs Group 1 vs Group 2 vs Group 3) at S1, S2 and S3 stages (excluding baseline data) showed the following trends: (i) between control and other groups (9 comparisons): data for Groups 1, 2 and 3 were significantly smaller than that of the control group (p ≤ 0.004); and (ii) between Groups 1, 2 and 3 (9 comparisons): only three comparisons were significantly different at S3 (Group 3 < Group 2, p = 0.029; Group 3 < Group 1, p < 0.001; Group 2 < Group 1, p = 0.030). The overall trend of the anti-erosive potential of the slurries (i.e., the reverse of erosion depth progression) was Group 3 < Group 2 < Group 1 < control group. Compared with the control group, the mean erosion depths for Groups 3, 2 and 1 (after Stage 3) were smaller by 93%, 84% and 75%, respectively.
Linear mixed-effects modeling showed significant interactions between Group and Stage for scratch depth (p ≤ 0.027), except Group 2 × Stage 1 (p = 0.060), indicating that the associations between scratch depth and Group were dependent on Stage and vice versa. Post hoc pairwise comparisons for stages (baseline, S1, S2 and S3) showed the following trends: (i) between baseline and other stages (12 comparisons): significant increases from baseline to other stages (p ≤ 0.034), except one comparison of baseline vs Stage 1 in Group 3 (p = 0.412); and (ii) between S1 versus S2 versus S3 (12 comparisons): significant increases at later stages (p ≤ 0.006), except two comparisons of Stage 1 versus Stage 2 (p = 0.056) and Stage 2 versus Stage 3 (p = 0.085), in Group 3. Post hoc pairwise comparisons between groups (control group vs Group 1 vs Group 2 vs Group 3) for S1, S2 and S3 stages, excluding baseline data, showed the following trends: (i) between control and other groups (9 comparisons): all six comparisons for Groups 1, 2, and 3 were significantly smaller at S2 and S3 stages (p ≤ 0.012); (ii) between Groups 1, 2 and 3 (9 comparisons): two significantly different comparisons between Group 3 versus Group 1 at S2 and S3 stages (Group 3 < Group 1, p < 0.001 for each comparison) and two significantly different comparisons between Group 3 vs Group 2 at S2 and S3 stages (Group 3 < Group 2, p < 0.001 for each comparison). The overall trend of the anti-erosive potential of the slurries (i.e., the reverse of scratch depth progression) was Group 3 < (Group 2 = Group 1) < control group. Compared with the control group, the overall mean scratch depths for Groups 3, 2 and 1 (after Stage S3) were smaller by 91%, 29%, and 31%, respectively.
Qualitative assessment
Figure 3 shows confocal and SEM images of flat, polished surfaces of control enamel specimens. After Stage 3, all enamel surfaces treated with anti-erosive slurries showed surface deposits in both types of micrographs. The size of these deposits observed in SEM images fell into this order: Group 2 (fine SnF2 particles) < Group 1 (small CPP-ACP globules) < Group 3 (larger SnF2/CPP-ACP agglomerates).
Discussion
Both CPP-ACP and SnF2 applied alone provided protection against erosion, but they were less effective against surface softening (approximately 30% reduction in scratch depth) than against surface loss (approximately 75–80% reduction in erosion depth). In comparison, SnF2/CPP-ACP provided consistently higher levels of protection under both conditions. Although stannous fluoride is one of the most effective anti-erosive agents available25, the current data show even greater anti-erosive potential of SnF2/CPP-ACP (×1.3 for surface softening and ×2.0 for surface loss) (Figs. 1 and 2). These findings led to rejection of the null hypothesis that combining CPP-ACP with SnF2 would not significantly enhance protection against erosive enamel wear. The quantitative data were supported by both confocal and SEM images showing protective surface coatings by all three anti-erosive agents. Furthermore, the current data on the synergistic anti-erosive effects of SnF2 and CPP-ACP in SnF2/CPP-ACP are consistent with its anticariogenic potential24, but the anticariogenic and anti-erosive mechanisms are fundamentally different.
When CPP-ACP is combined with 900 ppm NaF, it forms casein phosphopeptide-amorphous calcium fluoride phosphate (CPP-ACFP) with a 25% greater anti-erosive potential than CPP-ACP alone26. In comparison, SnF2/CPP-ACP exceeds the anti-erosive potential of CPP-ACP by approximately 70% (current data). The key anti-erosive mechanisms of the tested slurries in the present study appear to have involved surface protection from CPP-ACP nanofilms in Group 1, Sn salts in Group 2, and Sn-peptide crosslinking in Group 3. Furthermore, the anti-erosive agents also lubricate the wear interface27,28, which could have partly contributed to wear reduction during scratch testing. Overall, the lowest rates of erosive wear for Sn/CPP-ACP also imply enhanced bonding of this anti-erosive paste to the enamel surfaces compared with Sn or CPP-ACP separately.
The mechanism of crosslinking between SnF2 and CPP-ACP and bonding with the tooth structure has been described by Fernando et al.24. Electron-dense Sn2+ binds CPP-ACFP to form a larger complex (up to 2 µm in diameter). When the Sn/CPP-ACFP complex comes into contact with the tooth surface, the positively charged Sn2+ and the negatively charged CPP residues adsorb to the oppositely charged ions in hydroxyapatite. Subsequently, the CPP complex undergoes a conformational change, releasing a cargo of calcium, phosphate and fluoride ions. The CPP residues also crosslink with each other to form CPP-nanofilaments. Overall, the adsorption of Sn and CPP is likely to be the main contributor to the anti-erosive properties of the SnF2/CPP-ACP complex, with relatively minor effects of buffering and remineralization from calcium, phosphate and fluoride release.
The present data support the notion that both surface loss and softening occur concurrently and that loss of tooth structure occurs immediately29,30, which differs from the view that enamel softening precedes surface loss31. Furthermore, the current study presents novel data for early enamel erosion, e.g., 69.4 nm in the first minute in control specimens, which could be useful for understanding the kinetics of demineralization of the hydroxyapatite crystal (width along a-axis 35.7 nm; height along c-axis 43.1 nm)32. The current erosion depth data of approximately 70 nm after 1 min and approximately 250 nm after 5 min are smaller than those detected by optical coherence tomography at pH 3.2 (240 nm after 1 min and 2010 nm after 5 min)30, but the confocal profiler has a higher resolution than optical coherence tomography.
The variation in baseline erosion data simply reflects the varying thickness of the photoresist polymer coating, ranging from 0.7 to 3.9 μm, and the variation in baseline scratch depths probably reflects the site-specific random differences in the biomechanical properties of enamel. The baseline data were adjusted during statistical analyses to improve data quality, without which the signal/noise ratio would have been too low to yield a meaningful outcome. The present approach of studying enamel erosion is also an advance over existing methods for the following reasons: (i) This is the first study demonstrating the effectiveness of anti-erosive agents in reducing erosion depth as early as 1 min (at nanoscale) compared to longer detection limits in other studies21,33,34, (ii) The automated calculations of erosion and scratch depths reduced operator bias, as evidenced by low technical error of blinded measurements, and (iii) The use of photolithography (nanopatterning technique) enabled longitudinal assessment of erosion depth to be made on the same spots of each specimen, removing intraspecimen variability (error) when compared to cross-sectional design in most previous studies33,35. Human saliva was used in the present study because of relatively large measurement errors at the nanoscale introduced by the mineral precipitates from artificial saliva. This is consistent with an earlier report that artificial saliva is not a true substitute for human saliva36, although it appears to be more appropriate for erosive wear testing at the microscale37.
The present study has the limitations of in vitro design that does not replicate the complexity of the intraoral environment. It is also possible that the physical and structural properties of the enamel were altered during sample preparation, including photolithography, although no obvious structural alteration was noted on baseline micrographs (Fig. 3). Extended periods of saliva treatment were not included between erosion cycles, in contrast to some erosive wear models simulating the complex intraoral conditions during sleep and awake stages38,39. While this could have overestimated the anti-erosive potential of the agents tested in the present study, a simplistic design was deemed suitable for the current ‘proof of concept’ evaluation. The promising findings now call for testing in more realistic future in vitro models, as well as appropriate in situ and in vivo models. A similar approach has been used to validate the use of surface roughness as a measure of early erosive wear in vitro30,40, followed by subsequent testing in situ41. Continued technological advances in 3D imaging and analytical technology42 hold promise to enable the development of precise in situ or in vivo models, potentially minimizing overreliance on complex in vitro models.
Future studies are also needed to determine the optimum dose and frequency of application of SnF2/CPP-ACP in both enamel and dentine and to better understand its protective effects under erosive conditions involving tooth grinding and toothbrush abrasion. Knowledge can be advanced by integrating various direct and indirect methods to elucidate the structural, biomechanical, and chemical (compositional) changes associated with erosive wear43,44,45. Continued effort is required to provide research thrust into translatory applications of novel materials, e.g., novel hydroxyapatite nanoparticles46 and calcium phosphate nanoparticles47, and novel techniques, e.g., sustained release of anti-erosive agents (using nanoimplants and nanoparticles)48, improved adhesion of the salivary biofilm35, electrophoresis-aided remineralization49, and non-thermal plasma-induced remineralization50,51.
Conclusion
The current study provides ‘proof of concept’ evidence for the anti-erosive potential of SnF2/CPP-ACP during the early stages of erosive enamel wear. SnF2/CPP-ACP provided better protection against both surface loss and surface softening than CPP-ACP or SnF2 alone. Surface protection is likely to be the key mechanisms responsible for the anti-erosive effects of the tested materials. Overall, these findings highlight the potential role of SnF2/CPP-ACP in the management of enamel erosion, but further testing is required under more realistic in vitro conditions and precise in situ and in vivo situations.
Methods
Sample preparation
Fifty-three extracted sound human third molar teeth were collected as part of routine dental treatment in the Adelaide Dental Hospital and stored in a 0.5% thymol solution. The Human Research Ethics Committee of the University of Adelaide (H/27/90) approved the study and exempted the requirement for informed consent to collect extracted teeth. All methods were performed in accordance with the relevant guidelines and regulations. The mesiobuccal and distobuccal enamel sections from 40 teeth (n = 80 specimens) were allocated to the first part of the study, with mesiobuccal specimens (n = 40) being used for erosion testing and distobuccal specimens (n = 40) for scratch testing. The mesiobuccal enamel specimens from an additional 13 teeth (n = 13) were allocated to the second part of the study (Fig. 4). This distribution ensured that multiple specimens from the same teeth were not clustered into the same groups. All enamel sections were embedded in epoxy resin and ground flat to 0.25 µm such that approximately 2 mm × 2 mm of enamel surface was exposed in an epoxy cylinder (1.2 cm height × 1.0 cm diameter), as described previously29.
Study design
A novel technique was developed to assess bioceramic wear at the nanoscale. The first part of the study involved longitudinal quantitative and qualitative assessments of erosion on 80 enamel specimens by using three-dimensional (3D) confocal microscopy (LEXT OLS5000 3D Laser Scanning Microscope; Olympus, Tokyo, Japan) with the following parameters: optical resolution X–Y 0.25 µm, Z 0.149 nm; field of view 257.678 μm × 257.410 μm; magnification × 1130. Erosive wear was quantified by measuring (i) erosion depth, a direct measure of surface loss (40 mesiobuccal specimens), and (ii) scratch depth, an indirect measure of surface softening (40 distobuccal specimens). Preliminary experiments showed that a standard artificial saliva formulation52 was unsuitable for nanoscale wear assessment. It caused precipitation of mineral (crystal) aggregates that could not be washed off easily, and ultrasonication only transported those deposits to new reference areas (photoresist deposits) and previously clean enamel surfaces, introducing relatively large measurement errors. In contrast, human saliva did not create such precipitates and was deemed suitable for further experimentation. The second part of the study involved a cross-sectional qualitative assessment of the eroded surfaces using scanning electron microscopy (SEM) (Quanta 450 FEG Environmental Scanning Electron Microscope; FEI Europe B.V., Eindhoven, the Netherlands) on the remaining mesiobuccal specimens (n = 13) (Fig. 4).
Only one specimen was processed at a time from start to finish rather than processing multiple specimens in the same container. Prior to experimentation, all specimens were cleaned in an ultrasonic water bath for 10 min and then treated with human whole saliva for 1 h. Stimulated saliva was collected from a healthy donor after 2-h of fasting at 09.00 h and 12.00 h, and anti-erosive slurries were prepared and used within 3 h of saliva collection. The salivary parameters that were collected using a saliva kit (GC Saliva-Check Buffer Kit; GC Corporation, Tokyo, Japan) on 20 occasions over a 10-month period were pH 6.8–7.8; stimulated saliva flow rate > 5.0 ml at 5 min; and buffering capacity 10–12. The anti-erosive slurries were prepared for the experimental groups by mixing one of the three anti-erosive agents in whole saliva (1 g per 20 ml): (i) Group 1 (CPP-ACP): 10% CPP-ACP (Tooth Mousse; GC Corporation, Tokyo, Japan); (ii) Group 2 (SnF2): 0.45% SnF2 (3440 ppm Sn + 1100 ppm fluoride) (Test product 1; GC Corporation, Tokyo, Japan); and (iii) Group 3 (SnF2/CPP-ACP): 0.45% SnF2 (3440 ppm Sn + 1100 ppm fluoride) enriched 10% CPP-ACP (Test product 2; GC Corporation, Tokyo, Japan). The final concentrations of anti-erosive slurries were 0.5% CPP-ACP and 0.0225% (555 ppm) SnF2 (420 ppm Sn and 135 ppm F). Only whole saliva (without anti-erosive agent) was applied in the control group.
In the first part of the study, enamel specimens were assigned randomly to 3 experimental groups (Groups 1 to 3) and a control group (n = 10 per group). All specimens were subjected to 10 erosion cycles, with each cycle comprising 1 min erosion (0.3% citric acid, pH adjusted to 3.0) and 1 min treatment in whole saliva or the anti-erosive slurry. Erosion was carried out by applying 0.5 ml of citric acid to wash off the enamel surface, and then by leaving it undisturbed for the remainder of the erosion phase. Then, 0.5 ml of whole saliva was applied on the enamel surface for 2 s to rinse off citric acid, and copious amounts of saliva were used to wash off the wall and the base of each epoxy disc. The treatment phase of the erosion cycle was carried out by immersing the whole epoxy discs into 20 ml of whole saliva or anti-erosive slurry. The quantitative and qualitative assessments were performed at 4 stages: baseline (Stage 0; before the 1st erosion cycle) and at the end of the 1st, 5th and 10th erosion cycles (Stages 1, 2 and 3, respectively) corresponding to cumulative erosion for 1 min, 5 min and 10 min, respectively. At Stages 1, 2 and 3, the erosion cycles were stopped, and the specimens were gently dried with air for 5 s before erosion and scratch depths were assessed at room temperature (approximately 40 min per stage). At the completion of assessments at baseline, Stage 1, and Stage 2, the specimens were subjected to precycling with saliva or anti-erosive slurry for 1 min before the next erosion cycle began.
For erosion depth analysis, photolithography was used for deposition (microfabrication) of acid-resistant ‘photoresist’ polymer (resin) on the enamel surface. This deposit was used as a reference plane for longitudinal assessment of erosion on the same surface in subsequent stages. Photolithography is commonly used for surface patterning in microelectronic fabrication by selectively etching a thin film or silicon wafer to create a specific geometric pattern53,54. A pattern with 8 U-shaped arms (Fig. 5) was formed on the enamel surface via a 4-step process: (i) spin-coating a thin, uniform layer of ‘positive’ photoresist resin (Photoresist AZ 1518; Telic Company, Valencia, CA, USA) on the enamel surface, (ii) heating the base of the epoxy disc with a hot plate at 100 °C for 5 min (approximately 38 °C on the exposed enamel surface) to promote adhesion, (iii) applying a photolithographic mask (transparent ‘soda-lime glass’ covered with areas of opaque chrome coating) on the resin before exposing it to ultraviolet light for 5 s, after which the exposed polymer disintegrated and the unexposed polymer (covered by the chrome) remained intact, and (iv) removing the disintegrated resin by applying an alkaline developer (AZ 726 MIF; AZ Electronic Materials USA Corp.70, Somerville, NJ, USA) for 30 s and washing with water for 30 s, followed by gentle air-drying. The entire process resulted in the deposition of a photoresist resin reference plane with a thickness of 0.7 to 3.9 µm.
Nanoscratches were placed with a 20-µm radius spherical diamond tip in a nanoindenter (Ultra-Micro Indentation System – 2000; The Commonwealth Scientific and Industrial Research Organisation (CSIRO), Sydney, Australia) under a load of 100 mN (Fig. 5). Nanoscratch testing is a valid and essential component of studying the tribological (wear) behavior of both thin coatings and bulk materials55,56, including tooth enamel45,57,58,59. The scratch parameters for erosive wear testing were adopted from a previous study, as they provided an adequate signal-to-noise ratio for the detection of enamel softening without bulk failure60. The microscope optics attached to the nanoindenter helped to locate the correct areas for scratch placement. Four sets of three parallel 500-µm-long nano-scratches were placed on the enamel surface at least 400 µm away from the epoxy border and away from obvious cracks or defects. Specifically, these scratches were placed on the top-left corner at baseline, the middle-right region at Stage 1, the middle-left region at Stage 2, and the bottom-right region at Stage 3. The scratches were separated at least 50 μm apart to prevent microcracks and plastic deformation from one scratch affecting others.
For the second part of the study involving SEM analysis, the same experimental protocol for erosion testing was used but without depositing the photoresist resin reference plane. The 13 specimens were divided into 4 groups: Group 1 (n = 3), Group 2 (n = 3), Group 3 (n = 3) and the control group (n = 4). One control specimen was subjected to SEM analysis at baseline, and the rest (n = 12) were subjected to 10 erosion cycles.
Assessment of erosive wear
Changes in both scratch and erosion depths were assessed from baseline to Stages 1, 2 and 3 using 3D topographical analysis software (LEXT OLS 5100; Olympus, Tokyo, Japan) (Fig. 5). All scans were corrected for tilt prior to analysis. The erosion depth was measured along the upper region of the U-shaped arm, so that the middle of the scanned pitch (approximately 50 µm long) was separated by at least 30 µm from the photoresist border. The same surface was located for longitudinal assessment at subsequent stages with the aid of microscope optics. Erosion depth was calculated from the reference plane (photoresist resin) to the enamel surface by averaging all the vertical distances (spaced at 0.25 µm) across the entire scanned pitch. The scratch depth was measured only on freshly placed scratches towards the middle-third (150 µm) of the scanned pitch. Older scratches placed from earlier stages were not used for analysis. Scratch depth was calculated by averaging the vertical distances from the reference plane fitted over the enamel edges onto the body of the scratch (spaced at 0.25 µm) across the 150-µm long pitch. The data for the 3 scratches were averaged to determine the mean scratch depth for each specimen at each stage. For SEM analysis, the specimens were carbon-coated after being air-dried and dehydrated with silica gel for 72 h.
Statistical analysis
Statistical analysis was performed by using a statistical package (Stata 15.1; StataCorp; College Station, TX, USA). Power calculations showed that a sample size of 9 to 10 specimens was required in each group, assuming an effect size of 0.6, type I error probability (α) of 0.05, and power (1-β) of 0.80 for comparison of mean values between the four groups displaying intermediate dispersion of individual values. This conforms to previous studies conducted using similar testing methods29,60. Linear mixed-effects regression models were performed to determine whether the mean erosion depths and scratch depths (dependent variables) were significantly different between Group and Stage (fixed factors). The analyses were controlled for random errors from individual specimens and adjusted for baseline erosion and scratch depths (confounders). Significance was set at the 0.05 level.
Error testing
The method of double determination was used to test for systematic and random errors when calculating erosion and scratch depths at baseline and Stage 3 in 24 randomly selected scans (4 groups × 3 specimens per group × 2 stages for each parameter). The same examiner (DL) collected the data under blinded conditions 2-weeks apart. Paired t-tests showed no significant systematic errors between the repeated measurements (erosion depth, n = 24; t statistic = − 1.09, degrees of freedom = 23, p = 0.285; scratch depth, n = 24; t statistic = − 0.17, degrees of freedom = 23, p = 0.866), and Dahlberg’s technical error of measurements was low (< 3%).
Data availability
The datasets generated and/or analysed during the current study are available from the corresponding author on reasonable request.
References
Ganss, C. Is erosive tooth wear an oral disease?. Monogr. Oral Sci. 25, 16–21. https://doi.org/10.1159/000359931 (2014).
Mitic, A. D. et al. Ultrastructural changes in the cemento-enamel junction caused by acidic beverages: An in vitro study. Microsc. Res. Tech. 83, 91–98. https://doi.org/10.1002/jemt.23392 (2020).
Schmidt, J. & Huang, B. The pH of bottled water commercially available in Australia and its implications for oral health. J. Water Health. 20, 871–876. https://doi.org/10.2166/wh.2022.070 (2022).
Bartlett, D. W. & Coward, P. Y. Comparison of the erosive potential of gastric juice and a carbonated drink in vitro. J. Oral Rehabil. 28, 1045–1047. https://doi.org/10.1046/j.1365-2842.2001.00780.x (2001).
Shellis, R. P. & Addy, M. The interactions between attrition, abrasion and erosion in tooth wear. Monogr. Oral Sci. 25, 32–45. https://doi.org/10.1159/000359936 (2014).
Schlueter, N. et al. Terminology of erosive tooth wear: Consensus report of a workshop organized by the ORCA and the Cariology Research Group of the IADR. Caries Res. 54, 2–6. https://doi.org/10.1159/000503308 (2020).
Lussi, A. & Carvalho, T. S. Erosive tooth wear - a multifactorial condition of growing concern and increasing knowledge. Monogr. Oral Sci. 25, 1–15. https://doi.org/10.1159/000360380 (2014).
Sivasithamparam, K., Harbrow, D., Vinczer, E. & Young, W. G. Endodontic sequelae of dental erosion. Aust. Dent. J. 48, 97–101. https://doi.org/10.1111/j.1834-7819.2003.tb00016.x (2003).
Meyers, I. A. Minimum intervention dentistry and the management of tooth wear in general practice. Aust. Dent. J. 58(1 Suppl), 60–65. https://doi.org/10.1111/adj.12050 (2013).
Buzalaf, M. A., Magalhaes, A. C. & Wiegand, A. Alternatives to fluoride in the prevention and treatment of dental erosion. Monogr. Oral Sci. 25, 244–252. https://doi.org/10.1159/000360557 (2014).
Huysmans, M. C., Young, A. & Ganss, C. The role of fluoride in erosion therapy. Monogr. Oral Sci. 25, 230–243. https://doi.org/10.1159/000360555 (2014).
Buzalaf, M. A. R., Magalhães, A. C. & Wiegand, A. Alternatives to fluoride in the prevention and treatment of dental erosion. Monogr. Oral Sci. 25, 244–252. https://doi.org/10.1159/000360557 (2014).
Lussi, A. et al. The use of fluoride for the prevention of dental erosion and erosive tooth wear in children and adolescents. Eur. Arch. Paediatr. Dent. 20, 517–527. https://doi.org/10.1007/s40368-019-00420-0 (2019).
Kielbassa, A. M., Tschoppe, P., Hellwig, E. & Wrbas, K. T. Effects of regular and whitening dentifrices on remineralization of bovine enamel in vitro. Quintessence Int. 40, 103–112 (2009).
Rakhmatullina, E., Beyeler, B. & Lussi, A. Inhibition of enamel erosion by stannous and fluoride containing rinsing solutions. Schweiz. Monatsschr. Zahnmed. 123, 192–198 (2013).
Deng, J., Jackson, L., Epstein, J. B., Migliorati, C. A. & Murphy, B. A. Dental demineralization and caries in patients with head and neck cancer. Oral Oncol. 51, 824–831. https://doi.org/10.1016/j.oraloncology.2015.06.009 (2015).
Peric, T. et al. Efficacy of pastes containing CPP-ACP and CPP-ACFP in patients with Sjogren’s syndrome. Clin. Oral Investig. 19, 2153–2165. https://doi.org/10.1007/s00784-015-1444-1 (2015).
de Oliveira, A. F. et al. In situ effect of a CPP-ACP chewing gum on enamel erosion associated or not with abrasion. Clin. Oral Investig. 21, 339–346. https://doi.org/10.1007/s00784-016-1796-1 (2017).
Yu, H. et al. In situ effect of Tooth Mousse containing CPP-ACP on human enamel subjected to in vivo acid attacks. J. Dent. 76, 40–45. https://doi.org/10.1016/j.jdent.2018.05.021 (2018).
Reynolds, E. C. Anticariogenic complexes of amorphous calcium phosphate stabilized by casein phosphopeptides: A review. Spec. Care Dent. 18, 8–16. https://doi.org/10.1111/j.1754-4505.1998.tb01353.x (1998).
Gokkaya, B. et al. Effect of a single application of CPP-ACPF varnish on the prevention of erosive tooth wear: An AAS, AFM and SMH Study. Oral Health Prev. Dent. 18, 311–318. https://doi.org/10.3290/j.ohpd.a43365 (2020).
Lussi, A. & Carvalho, T. S. The future of fluorides and other protective agents in erosion prevention. Caries Res. 49(Suppl 1), 18–29. https://doi.org/10.1159/000380886 (2015).
Dashper, S. G. et al. CPP-ACP promotes SnF2 efficacy in a polymicrobial caries model. J. Dent. Res. 98, 218–224. https://doi.org/10.1177/0022034518809088 (2019).
Fernando, J. R. et al. Self-assembly of dental surface nanofilaments and remineralisation by SnF2 and CPP-ACP nanocomplexes. Sci. Rep. 9, 1285. https://doi.org/10.1038/s41598-018-37580-w (2019).
Ganss, C., Neutard, L., von Hinckeldey, J., Klimek, J. & Schlueter, N. Efficacy of a tin/fluoride rinse: A randomized in situ trial on erosion. J. Dent. Res. 89, 1214–1218. https://doi.org/10.1177/0022034510375291 (2010).
Canto, F. M. T. et al. Comparative effect of calcium mesoporous silica versus calcium and/or fluoride products against dental erosion. Braz. Dent. J. 31, 164–170. https://doi.org/10.1590/0103-6440202002557 (2020).
Ranjitkar, S., Kaidonis, J. A., Richards, L. C. & Townsend, G. C. The effect of CPP-ACP on enamel wear under severe erosive conditions. Arch. Oral Biol. 54, 527–532. https://doi.org/10.1016/j.archoralbio.2009.03.006 (2009).
Ranjitkar, S. et al. The effect of casein phosphopeptide-amorphous calcium phosphate on erosive dentine wear. Aust. Dent. J. 54, 101–107. https://doi.org/10.1111/j.1834-7819.2009.01101.x (2009).
Mann, C. et al. Three-dimensional profilometric assessment of early enamel erosion simulating gastric regurgitation. J. Dent. 42, 1411–1421. https://doi.org/10.1016/j.jdent.2014.06.011 (2014).
Mylonas, P., Austin, R. S., Moazzez, R., Joiner, A. & Bartlett, D. W. In vitro evaluation of the early erosive lesion in polished and natural human enamel. Dent. Mater. 34, 1391–1400. https://doi.org/10.1016/j.dental.2018.06.018 (2018).
Lussi, A., Schlueter, N., Rakhmatullina, E. & Ganss, C. Dental erosion - an overview with emphasis on chemical and histopathological aspects. Caries Res. 45(Suppl 1), 2–12. https://doi.org/10.1159/000325915 (2011).
Ortiz-Ruiz, A. J. et al. Structural differences in enamel and dentin in human, bovine, porcine, and ovine teeth. Ann. Anat. 218, 7–17. https://doi.org/10.1016/j.aanat.2017.12.012 (2018).
Sakae, L. O. et al. An in vitro study on the influence of viscosity and frequency of application of fluoride/tin solutions on the progression of erosion of bovine enamel. Arch. Oral Biol. 89, 26–30. https://doi.org/10.1016/j.archoralbio.2018.01.017 (2018).
Zanatta, R. F., Avila, D., Miyamoto, K. M., Torres, C. R. G. & Borges, A. B. Influence of surfactants and fluoride against enamel erosion. Caries Res. 53, 1–9. https://doi.org/10.1159/000488207 (2019).
Viana, I. E. L. et al. Novel fluoride and stannous -functionalized β-tricalcium phosphate nanoparticles for the management of dental erosion. J. Dent. 92, 103263. https://doi.org/10.1016/j.jdent.2019.103263 (2020).
Kielbassa, A. M., Shohadai, S. P. & Schulte-Mönting, J. Effect of saliva substitutes on mineral content of demineralized and sound dental enamel. Support. Care Cancer. 9, 40–47. https://doi.org/10.1007/s005200000148 (2001).
Baumann, T., Kozik, J., Lussi, A. & Carvalho, T. S. Erosion protection conferred by whole human saliva, dialysed saliva, and artificial saliva. Sci. Rep. 6, 34760. https://doi.org/10.1038/srep34760 (2016).
Qutieshat, A. S., Mason, A. G. & Chadwick, R. G. In vitro simulation of erosive challenges to human enamel using a novel artificial mouth. Clin. Exp. Dent. Res. 4, 105–112. https://doi.org/10.1002/cre2.111 (2018).
Pini, N. I. P., Lima, D., Luka, B., Ganss, C. & Schlueter, N. Viscosity of chitosan impacts the efficacy of F/Sn containing toothpastes against erosive/abrasive wear in enamel. J. Dent. 92, 103247. https://doi.org/10.1016/j.jdent.2019.103247 (2020).
Mullan, F., Austin, R. S., Parkinson, C. R., Hasan, A. & Bartlett, D. W. Measurement of surface roughness changes of unpolished and polished enamel following erosion. PLoS ONE 12, e0182406. https://doi.org/10.1371/journal.pone.0182406 (2017).
Mullan, F., Austin, R. S., Parkinson, C. R. & Bartlett, D. W. An in-situ pilot study to investigate the native clinical resistance of enamel to erosion. J. Dent. 70, 124–128. https://doi.org/10.1016/j.jdent.2018.01.005 (2018).
Ranjitkar, S. et al. Surface-sensitive microwear texture analysis of attrition and erosion. J. Dent. Res. 96, 300–307. https://doi.org/10.1177/0022034516680585 (2017).
Chen, X. et al. Three-dimensional visualization of dentine occlusion based on FIB-SEM tomography. Sci. Rep. 13, 2270. https://doi.org/10.1038/s41598-023-29155-1 (2023).
Ionescu, A. C., Esposti, L. D., Iafisco, M. & Brambilla, E. Dental tissue remineralization by bioactive calcium phosphate nanoparticles formulations. Sci. Rep. 12, 5994. https://doi.org/10.1038/s41598-022-09787-5 (2022).
Min, J. et al. Investigation on the gradient nanomechanical behavior of dental fluorosis enamel. Nanoscale Res. Lett. 13, 347. https://doi.org/10.1186/s11671-018-2768-y (2018).
Rodemer, T., Pütz, N. & Hannig, M. Influence of hydroxyapatite nanoparticles on the formation of calcium fluoride surface layer on enamel and dentine in vitro. Sci Rep. 12, 17612. https://doi.org/10.1038/s41598-022-21545-1 (2022).
Iafisco, M. et al. Fluoride-doped amorphous calcium phosphate nanoparticles as a promising biomimetic material for dental remineralization. Sci. Rep. 8, 17016. https://doi.org/10.1038/s41598-018-35258-x (2018).
Bariana, M., Kaidonis, J. A., Losic, D., Ranjitkar, S. & Anderson, P. J. Titania nanotube-based protein delivery system to inhibit cranial bone regeneration in Crouzon model of craniosynostosis. Int. J. Nanomed. 14, 6313–6324. https://doi.org/10.2147/IJN.S202090 (2019).
Zhang, Y. Y., Wong, H. M., McGrath, C. P. J. & Li, Q. L. In vitro and in vivo evaluation of electrophoresis-aided casein phosphopeptide-amorphous calcium phosphate remineralisation system on pH-cycling and acid-etching demineralised enamel. Sci. Rep. 8, 8904. https://doi.org/10.1038/s41598-018-27304-5 (2018).
Awad, M. M. et al. Effect of non-thermal atmospheric plasma on micro-tensile bond strength at adhesive/dentin interface: A systematic review. Materials (Basel). 14, 1026. https://doi.org/10.3390/ma14041026 (2021).
Fathollah, S., Abbasi, H., Akhoundi, S., Naeimabadi, A. & Emamjome, S. Cold plasma enamel surface treatment to increase fluoride varnish uptake. Sci. Rep. 12, 4657. https://doi.org/10.1038/s41598-022-08069-4 (2022).
Ranjitkar, S. et al. The effect of casein phosphopeptide-amorphous calcium phosphate on erosive enamel and dentine wear by toothbrush abrasion. J. Dent. 37, 250–254. https://doi.org/10.1016/j.jdent.2008.11.013 (2009).
Garcia, A., Polesel-Maris, J., Viel, P., Palacin, S. & Berthelot, T. Localized ligand induced electroless plating (LIEP) process for the fabrication of copper patterns onto flexible polymer substrates. Adv. Funct. Mater. 21, 2096–2102. https://doi.org/10.1002/adfm.201100041 (2011).
Yang, D. & Priest, C. Microfluidic platform for high-throughput screening of leach chemistry. Anal. Chem. 90, 8517–8522. https://doi.org/10.1021/acs.analchem.8b01413 (2018).
Jacobs, T. & Carpick, R. Nanoscale wear as a stress-assisted chemical reaction. Nat. Nanotech. 8, 108–112. https://doi.org/10.1038/nnano.2012.255 (2013).
Suh, A. & Yoon, D. I. Nanoscratching technique for highly oriented liquid crystal materials. Sci. Rep. 8, 9460. https://doi.org/10.1038/s41598-018-27887-z (2018).
Guidoni, G. M., Swain, M. V. & Jager, I. Wear behaviour of dental enamel at the nanoscale with a sharp and blunt indenter tip. Wear 266, 60–68. https://doi.org/10.1016/j.wear.2008.05.007 (2009).
Qing, P. et al. Characterization of the nanoscratch, microstructure, and composition in hypoplastic amelogenesis imperfecta. Adv. Mech. Eng. 7, 1–8. https://doi.org/10.1177/1687814015595597 (2015).
Xia, J. et al. Enamel crystallite strength and wear: nanoscale responses of teeth to chewing loads. J. R. Soc. Interface. 14, 20170456. https://doi.org/10.1098/rsif.2017.0456 (2017).
Kwek, S. X. et al. Nanoscratch testing for the assessment of enamel demineralization under conditions simulating wine erosion. Aust. Dent. J. 60, 12–17. https://doi.org/10.1111/adj.12277 (2015).
Acknowledgements
We are grateful to G C Corporation, Tokyo, Japan, for supplying consumables (remineralizing pastes and salivary kits) and funding the microscopy work. This research was supported by a research grant from the Australian Dental Research Foundation Inc. The experimental work was performed at the South Australian node of the Australian National Fabrication Facility under the National Collaborative Research Infrastructure Strategy to provide nano and microfabrication facilities for Australia’s researchers. We acknowledge the instruments and scientific and technical assistance of Microscopy Australia at the University of South Australia, a facility that is funded by the University and State and Federal Governments. We thank Mr Ken Neubauer from Adelaide Microscopy for assistance with scanning electron microscopy work and Dr Robin Yong from Adelaide Dental School for sample collection.
Author information
Authors and Affiliations
Contributions
C.H., E.C.R., L.C.R., and S.R conceived the work. D.A.S. performed in vitro experiments with input from other authors. S.E. and S.R. performed statistical analyses. D.A.S. and S.R. prepared and edited figures. D.A.S., S.E., L.C.R. and S.R. wrote the manuscript. D.A.S. and S.R. revised the manuscript. All authors reviewed the manuscript.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing interests.
Additional information
Publisher's note
Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Supplementary Information
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons licence, and indicate if changes were made. The images or other third party material in this article are included in the article's Creative Commons licence, unless indicated otherwise in a credit line to the material. If material is not included in the article's Creative Commons licence and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this licence, visit http://creativecommons.org/licenses/by/4.0/.
About this article
Cite this article
Al Saady, D., Hall, C., Edwards, S. et al. Erosion-inhibiting potential of the stannous fluoride-enriched CPP-ACP complex in vitro. Sci Rep 13, 7940 (2023). https://doi.org/10.1038/s41598-023-34884-4
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41598-023-34884-4
- Springer Nature Limited